The magnetization damping properties of square permalloy elements were characterized. These 20 nm-thick permalloy squares were deposited by the electron beam evaporation. Time resolved magneto-optic Kerr effect microscopy (TR-MOKE) was used to measure the magnetization evolution in the sample. By curve fitting in Matlab, I obtained the value of damping constant that is consistent with the reference paper. A Landau confi guration in the square permalloy sample leads to the different trends of the damping constant with external bias field. The damping constant in the bottom domain is found to decrease with increasing bias field while the damping constant in the top domain has been saturated into the minimum value. The decreasing tendency of magnetization precession frequencies is consistent with the Kittel equation modi fied with an anisotropic energy term. Additionally, FePt thin films and patterned CoFeB disks were investigated but neither yielded conclusive dynamic data. / Graduate / 0611 / 0607 / 0752 / leizhang.summer@gmail.com

In the present work, the implications of ion irradiation on the magnetostatic and dynamic properties of soft magnetic Py/Ta (Py = Permalloy: Ni80Fe20) single and multilayer films have been investigated with the main objective of finding a way to determine their saturation magnetization. Both polar magneto-optical Kerr effect (MOKE) and vector network analyzer ferromagnetic resonance (VNA-FMR) measurements have proven to be suitable methods to determine µ0MS, circumventing the problem of the unknown effective magnetic volume that causes conventional techniques such as SQUID or VSM to fail. Provided there is no perpendicular anisotropy contribution in the samples, the saturation magnetization can be determined even in the case of strong interfacial mixing due to an inherently high number of Py/Ta interfaces and/or ion irradiation with high fluences. Another integral part of this work has been to construct a VNA-FMR spectrometer capable of performing both azimuthal and polar angle-dependent measurements using a magnet strong enough to saturate samples containing iron. Starting from scratch, this comprised numerous steps such as developing a suitable coplanar waveguide design, and writing the control, evaluation, and fitting software. With both increasing ion fluence and number of Py/Ta interfaces, a decrease of saturation magnetization has been observed. In the case of the 10×Py samples, an immediate decrease of µ0MS already sets in at small ion fluences. However, for the 1×Py and 5×Py samples, the saturation magnetization remains constant up to a certain ion fluence, but then starts to rapidly decrease. Ne ion irradiation causes a mixing and broadening of the interfaces. Thus, the Py/Ta stacks undergo a transition from being polycrystalline to amorphous at a critical fluence depending on the number of interfaces. The saturation magnetization is found to vanish at a Ta concentration of about 10–15 at.% in the Py layers. The samples possess a small uniaxial anisotropy, which remains virtually unaffected by the ion fluence, but slightly reduces with an increasing number of Py/Ta interfaces. In addition to magnetostatics, the dynamic properties of the samples have been investigated as well. The Gilbert damping parameter α increases with both increasing number of Py/Ta interfaces and higher ion fluences, with the former having a stronger influence. The inhomogeneous linewidth broadening ΔB0 increases as well with increasing number of Py/Ta interfaces, but slightly decreases for higher ion fluences. / In dieser Dissertation ist der Einfluss von Ionenbestrahlung auf die magnetostatischen und dynamischen Eigenschaften von weichmagnetischen Py/Ta-Einzel- und Multilagen (Py = Permalloy: Ni80Fe20) untersucht worden, wobei das Hauptziel gewesen ist, eine Methode zur Bestimmung der Sättigungsmagnetisierung zu finden. Sowohl polare magneto-optische Kerr-Effektmessungen (MOKE) als auch ferromagnetische Resonanzmessungen mittels eines Vektornetzwerkanalysators (VNA-FMR) haben sich als geeignet erwiesen, um µ0MS zu bestimmen, wobei das Problem des unbekannten effektiven magnetischen Volumens umgangen wird, welches bei der Verwendung von Techniken wie SQUID oder VSM auftreten würde. Unter der Voraussetzung, dass die Proben keinen senkrechten magnetischen Anisotropiebeitrag besitzen, kann die Sättigungsmagnetisierung selbst im Fall starker Grenzflächendurchmischung infolge einer großen Anzahl an Py/Ta-Grenzflächen und/oder Ionenbestrahlung mit hohen Fluenzen bestimmt werden. Ein weiterer wesentlicher Bestandteil dieser Arbeit ist die Konstruktion eines VNA-FMR-Spektrometers gewesen, welches vollautomatisiert ist, polare und azimutale Winkelabhängigkeiten messen kann und einen Magneten besitzt, der Proben, die Eisen beinhalten, sättigen kann. Von Grund auf beginnend umfasste dies zahlreiche Schritte wie z. B. die Entwicklung eines geeigneten koplanaren Wellenleiterdesigns sowie das Schreiben von Steuerungs-, Auswertungs- und Fitprogrammen. Mit steigender Fluenz und Zahl an Py/Ta-Grenzflächen ist eine Abnahme der Sättigungsmagnetisierung beobachtet worden. Im Fall der 10×Py-Proben findet diese bereits bei kleinen Fluenzen statt. Im Gegensatz dazu bleibt µ0MS der 1×Py- und 5×Py-Proben bis zu einer bestimmten Fluenz konstant, bevor sie sich dann umso schneller verringert. Die Bestrahlung mit Ne-Ionen verursacht eine Durchmischung und Verbreiterung der Grenzflächen. Infolgedessen erfahren die Py/Ta-Proben bei einer kritischen Fluenz, die von der Zahl der Grenzflächen abhängig ist, einen Phasenübergang von polykristallin zu amorph. Die Sättigungsmagnetisierung verschwindet ab einer Ta-Konzentration von etwa 10–15 Atom-% in den Py-Schichten. Die Proben besitzen eine kleine uniaxiale Anisotropie, die praktisch unbeeinflusst von der Fluenz ist, sich jedoch mit steigender Zahl an Py/Ta-Grenzflächen leicht verringert. Neben den statischen sind auch die dynamischen magnetischen Eigenschaften der Proben untersucht worden. Der Gilbert-Dämpfungsparameter α erhöht sich sowohl mit steigender Zahl an Py/Ta-Grenzflächen als auch mit höheren Fluenzen, wobei Erstere einen größeren Einfluss hat. Die inhomogene Linienverbreiterung ΔB0 nimmt ebenfalls mit steigender Zahl an Py/Ta-Grenzflächen zu, verringert sich jedoch bei größeren Fluenzen leicht.