Orientador: Rafael Leonardo Xediek Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:07:37Z (GMT). No. of bitstreams: 1 Naoe_HilkaTiemi_M.pdf: 1024541 bytes, checksum: 92dfb7adacf4acd2b08826fb3278ce7c (MD5) Previous issue date: 2009 / Resumo: O objetivo neste estudo foi verificar a resistência da união ao cisalhamento entre as resinas acrílicas Clássico ou Onda-Cryl e o dente Trubyte-Biotone, sob a influência de diversas formas de retenção, compreendendo nenhum tratamento (controle), perfuração com broca, jateamento com partículas de óxido de alumínio, condicionamento com monômero, condicionamento com primer e interações. Noventa matrizes retangulares, medindo 20mm de largura por 35mm de comprimento, foram confeccionadas com cera utilidade e incluídas na parte inferior de muflas metálicas ou plásticas, com gesso pedra tipo III Herodent. As matrizes retangulares foram removidas depois de plastificadas com água em ebulição e os moldes de gesso revestidos com silicone laboratorial, nos quais foram incluídos um dente molar com a base contendo um cilindro de cera de 6mm de diâmetro por 25mm de comprimento. O conjunto dente-cilindro em cera foi recoberto com uma camada de silicone e a mufla preenchida com gesso pedra. Depois da presa do gesso, o conjunto dente-cilindro em cera foi removido, o bastão em cera retirado, o dente limpo com detergente e as bases submetidas aos tratamentos de acordo com o protocolo e recolocadas nos moldes de silicone. As resinas acrílicas termopolimerizáveis foram proporcionadas na relação volumétrica de 3/1 (polímero/monômero), adaptadas na fase plástica nos moldes de silicone e prensadas em prensa hidráulica de bancada. As muflas metálicas foram levadas à termopolimerizadora automática para polimerização da resina no ciclo em banho de água à temperatura de 74ºC durante 9 horas. As muflas plásticas foram colocadas em forno de microondas para polimerização da resina, calibrado com 900W de potência, para o ciclo de: fase I - 3 minutos com 40% da potência, fase II - 4 minutos com potência 0% e fase III - 3 minutos com 90% da potência e esfriamento das muflas em bancada. Depois da demuflagem, os corpos-de-prova foram armazenados em água destilada à temperatura de 37ºC durante 24 horas. Depois da armazenagem, os corpos-de-prova foram submetidos ao teste de resistência ao cisalhamento na máquina de ensaios universal Instron, com velocidade de 1mm/minuto. Os resultados submetidos à análise de variância e as médias ao teste de Tukey (5%) mostraram que os valores da união entre dentes artificiais e resinas acrílicas não apresentam diferença estatística significativa, quando comparadas independentemente dos tipos de tratamentos. Na análise dos tipos de tratamentos, independentemente da resina acrílica, o grupo que recebeu jateamento+adesivo apresentou média com diferença estatística significativa com o grupo perfurado+adesivo. Os demais grupos não apresentaram diferença estatística significativa. Quando os tratamentos foram considerados em cada resina, na Clássico não houve diferença significativa entre eles e na Onda-Cryl os tratamentos controle e perfurado+adesivo foram diferentes estatisticamente dos grupos jateado+ monômero e jateado+adesivo. Os demais grupos não apresentaram diferenças estatísticas. Na comparação entre resinas, somente o grupo controle apresentou diferença estatística significativa com o maior valor para a resina Onda-Cryl / Abstract: The purpose of this study was to verify the shear bond strength between denture tooth Trubyte-Biotone and the acrylic resins Clássico and Onda-Cryl, under the influence of various forms of treatments, including no treatment (control), retention groove, sandblasting with aluminum oxide particles, monomer application, primer application, and interactions. Ninety wax rectangular mold patterns (20 mm in width and 35 mm in length), were poured into a traditional brass flask or metal with type III dental stone that was proportioned and manipulated following the manufacturer's recommendations. After wax patterns removal, the stone mold was filled with a layer of laboratory silicone putty. Identical model acrylic molar teeth with a wax stick (6mm diameter and 25mm long) attached at the ridge lap surface were partially embedded into the silicone layer. The resultant tooth/wax stick set was then covered with a layer of laboratory silicone putty. After dental stone isolation with petroleum jelly, the flask was completely poured with type III dental stone and pressed in a hydraulic press bench. Following, the tooth/wax stick set was deflasked and the wax stick removed from the tooth ridge lap. The tooth was brushed with a solution of hot water and liquid detergent to eliminate the wax residuos. Heat-cured denture base acrylic resins were prepared using a ratio of volume 3/1(polymer/monomer), adapted on stage in plastic molds made of silicon and pressing into bench hydraulic press. The metal flask were conventional packed, polymerized in a hot water bath at 74oC for 9 hours in polymerizing unit, and deflasked after flask cooling at room temperature. The plastic flask were placed in the microwave oven for curing the acrylic resin, calibrated with 900W of power for the cycle: Phase I - 3 minutes with 40% of the power, phase II - 4 minutes with 0% power and phase III - 3 minutes with 90% of the power and flask cooling at room temperature. After deflasked, all specimens were stored in distilled water at a temperature of 37oC for 24 hours, and they were performed the shear bond testing in an Instron machine, using a cross-speed of 1mm/minuto. The results were submitted to ANOVA and Tukey's test (5%) showed that the values of the shear bond strength between artificial teeth and acrylic resins were not statistically significant when compared regardless of the types of treatments. In the treatment type analysis, regardless of acrylic resin, the sandblasting+adhesive group showed bond strength values with significant statistically difference when compared to groove+adhesive group. The other experimental groups were not statistically different. When the treatments were considered in each resin, in the Classico acrylic resin there was no significant difference between them. In Onda-Cryl, control and groove+adhesive treatments were statistically different of the sandblasting+monomer and sandblasting+adhesive groups, while the other showed no statistical differences. In the comparison between resins, only the control group showed statistically significant differences, with the greatest value for the Onda-Cryl acrylic resin / Mestrado / Mestre em Materiais Dentários

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-12T19:10:52Z (GMT). No. of bitstreams: 1 Oliveira_KarlaMychellyneCosta_M.pdf: 1881397 bytes, checksum: 97ee455b1517d285dfad583e4a0fe633 (MD5) Previous issue date: 2009 / Resumo: O objetivo deste trabalho foi comparar a tensão de contração de polimerização gerada por compósitos resinosos em diferentes tempos após a fotoativação, por meio de análise fotoelástica. Três compósitos experimentais com diferentes tipos de fotoiniciadores, e dois compósitos comerciais, sendo um à base de monômeros metacrilatos e o outro à base de siloranos foram comparados. Compósitos experimentais foram fabricados com 40% em massa de matriz orgânica e 60% de partículas de carga inorgânica, canforoquinona (CQ) ou fenil propanodiona (PPD) foram adicionados como sistemas fotoiniciadores. Discos deresina fotoelástica (base: Araldite GY 279/ endurecedor: Aradur 2963) foram confeccionados com perfurações de 6mm de diâmetro e 2mm de espessura no centro de cada disco. A superfície interna da resina fotoelástica foi condicionada com agente adesivo. Os compósitos foram separados em 5 grupos, sendo que os grupos 1 e 2 representaram os compósitos comerciais Filtek Silorane e Filtek Z250, respectivamente. Enquanto que os grupos 3, 4 e 5 constituíam os compósitos experimentais com os sistemas iniciadores CQ/Amina, CQ/PPD/Amina e PPD/Amina, respectivamente. O compósito foi inserido em incremento único no preparo da resina fotoelástica e fotoativado com luz LED (LED Ultralume 5) por 60s. As tensões geradas pelos compósitos foram avaliadas logo após a fotoativação, em 24 horas e 7 dias, por meio de análise fotoelástica com polariscópio plano, diretamente sobre luz branca ou com filtro vermelho resultando em imagens coloridas e monocromáticas, respectivamente. A análise qualitativa das imagens fotoelásticas revelaram que o grupo 1 apresentou a menor tensão de contração de polimerização em todos os tempos avaliados. Comparando os grupos das resinas experimentais, notou-se que o grupo 3 gerou maior tensão na resina fotoelástica em relação aos grupos 4 e 5 imediatamente após a fotoativação. Porém, 24 horas e 7 dias após a fotoativação as tensões geradas se equipararam para os grupos das resinas experimentais. A análise quantitativa realizada com avaliação das imagens monocromáticas mostrou que a tensão gerada pelo compósito Filtek Silorane foi similar à do compósito Filtek Z250 imediatamente após a fotoativação; porém, em 24 horas e 7dias o Filtek Z250 apresentou maiores tensões quando comparado ao Filtek Silorane. Os compósitos experimentais não apresentaram diferença estatisticamente significativa entre eles em nenhum dos tempos avaliados. Em geral, as tensões geradas aumentaram com o passar do tempo. Concluiu-se que o PPD não foi efetivo para minimizar as tensões geradas durante o processo de polimerização dos compósitos. Compósitos à base de silorano apresentaram os menores valores de tensão de contração de polimerização. / Abstract: The aim of this study was to compare polymerization shrinkage stresses of dental composites in different moments after light-activation. Three experimental composites with different photoinitiator systems, and two commercial composites, one methacrilate based and the other silorane based were compared. Experimental composites were fabricated with 40% of organic matrix and 60% of inorganic filler, canforoquinone (CQ) or phenyl propanodione (PPD) were added to the resin as photoinitiator systems. Discs of the photoelastic resin (Araltide GY279/Aralur 2963) were prepared with cylindrical cavities (6mm diameter, 2mm thick) in the center of each disc. Internal surfaces of the photoelastic resin were roughened and prepared with adhesive system application. The composites were divided into five groups: groups 1 and 2 represented commercial composites Filtek Silorane and Filtek Z250, respectively; groups 3, 4 and 5 represented experimental composites with CQ/Amine, CQ/PPD/Amine and PPD/Amine as initiator system, respectively. A bulk increment of the composite was inserted into the cavity of photoelastic resin and photo-polymerized with a LED light-cure unit (LED Ultralume 5) for 60s. The stresses created by polymerization shrinkage were analyzed immediately after photopolymerization, in 24 hours and 7 days, by photoelastic analysis with a plane polariscope, with white light, with or without a red filter resulting in color and black and white images, respectively. Qualitative analysis of photoelastic images showed that group 1 had the lowest polymerization shrinkage stress in all times evaluated. Comparing experimental composites, it was observed that group 3 created more stress in photoelastic resin than groups 4 and 5 immediately after light-activation. However, 24 hours and 7 days after photopolymerization the stresses had equalized in resin experimental groups. Quantitative analysis showed that shrinkage strain of Filtek Silorane was similar to that of Filtek Z250 immediately after photopolymerization. In 24 hours and 7 days, the Filtek Z250 showed higher strain than Filtek Silorane. Experimental composites didn't differ statistically between each other in all times evaluated. Generally, the tension increased with the time. It was concluded that PPD wasn't capable of decrease the stresses created during polymerization process of composites. Silorane based composites had the lowest stresses during polymerization shrinkage process. / Mestrado / Mestre em Materiais Dentários

Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T01:34:04Z (GMT). No. of bitstreams: 1 Paes_PaulaNunesGuimaraes_M.pdf: 8634173 bytes, checksum: 841ceeadf71622e4274b862220cdb566 (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi avaliar o efeito dos métodos de ativação e da fadiga mecânica sobre a resistência à tração diametral de cimentos resinosos duais. Pastas base e ativadora do RelyX ARC, Enforce, Nexus 2 e RelyX UNICEM foram manipuladas e inseridas em matrizes cilíndricas de silicona de adição (4 x 2 mm) e distribuídas em grupos de acordo com a técnica de ativação em: 1- Sem fotoativação (ativação química); 2- Fotoativação direta (ativação Dual); 3- Fotoativação através da cerâmica. Após armazenamento por 24 horas em água destilada a 37ºC, metade das amostras de cada grupo (n=10) foram submetidos a 30.000 ciclos mecânicos, com freqüência de 1 Hz e carga de 12 N. As amostras não cicladas permaneceram armazenadas em água destilada em estufa a 37ºC por 32 h após a manipulação, para que fossem testadas com o mesmo intervalo de tempo que as amostras cicladas. Em seguida, todas as amostras foram submetidas ao ensaio de Resistência à Tração Diametral (RTD) em máquina universal de ensaios INSTRON, com velocidade de 0,5 mm/min. Os dados de RTD (MPa) para os modos de ativação química, dual indireta e dual direta foram submetidos à análise de Variância e ao teste de Tukey (5%) e mostraram que apenas os fatores modo de ativação e cimento apresentaram interação significativa. O fator ciclagem mecânica e a interação tripla não obtiveram interação significativa. Os valores da interação dos fatores cimento e modos de ativação química, dual indireta e dual direta respectivamente foram: RelyX ARC (49,68 ± 8,42; 63,43 ± 6,92 e 55,12 ± 5,16), Enforce (49,12 ± 3,89; 56,96 ± 6,45 e 56,42 ± 8,88), RelyX ARC (28,12 ± 11,21; 40,10 ± 4,39 e 37,44 ± 6,49) e Nexus 2 (61,89 ± 11,21; 62,56 ± 10,93 e 59,26 ± 9,47). A análise dos resultados após o teste de Tukey mostrou que o cimento Nexus 2 não apresentou aumento nos valores de RTD quando ativado pela luz em relação à polimerização química. Os demais cimentos apresentaram valores maiores quando fotoativados de forma direta ou indireta, em relação aos valores alcançados pelo modo de polimerização química, com exceção do cimento RelyX ARC que obteve os mesmos valores quando ativado de forma dual direta e polimerizado quimicamente. A interposição do disco de cerâmica durante a fotoativacão alterou os valores de resistência à tração diametral apenas para o cimento RelyX ARC. A ciclagem mecânica não afetou a resistência à tração diametral de nenhum cimento resinoso dual avaliado e a composição de cada cimento resinoso dual, assim como o seu modo de ativação, foram determinantes para a obtenção da resistência à tração diametral dos mesmos. / Abstract: The aim of this study was to evaluate the effect of the activation methods and the mechanical fatigue on diametral tensile strength of dual resin cements. Base and catalyst pastes of the cements RelyX ARC, Enforce, Nexus 2 and RelyX UNICEM were mixed and inserted into cylindrical silicon moulds (4 x 2 mm) and divided in groups according to their activation methods: 1) without photoactivation (chemical activation); 2) direct curing (dual ativation); 3) light activation through porcelain disk. After being stored for 24 hours in distillated water at 37ºC, half of the samples of each group (n=10) were subjected to 30,000 mechanical cycles at 1 Hz frequency and 12 N load. The samples not cycled remained in distillated water at 37ºC for 32 h after the mixing, so they were tested with the same time that the other fatigued samples did. Then, the samples were subjected to Diametral Tensile Strength (DTS) in Instron universal machine with 0,5 mm/min speed. The data of the Diametral Tensile Strength (MPa) obtained for each cement in chemical, indirect dual and direct dual modes of activation were submeted to three-way analysis of variance and Turkey's Student Range Test (5%) and showed that only the activation methods and the cement type presented significant difference. Mechanical fatigue and triple factors interation didn't present significant difference. The data of the cement factor with chemical activation, indirect curing and direct curing was respectively: RelyX ARC (49.68 ± 8.42; 63.43 ± 6.92 e 55.12 ± 5.16), Enforce (49.12 ± 3.89; 56.96 ± 6.45 and 56.42 ± 8.88), RelyX ARC (28.12 ± 11.21; 40.10 ± 4.39 and 37.44 ± 6.49) and Nexus 2 (61.89 ± 11.21; 62.56 ± 10.93 and 59.26 ± 9.47). After Turkey's test, the data showed that the cement Nexus 2 didn't present increase in the DTS values when it was light actived comparing to chemical curing. The others cement presented higher values when directly or indirectly photoactivated compared with the values obtained with chemical activation mode. The exception was the RelyX ARC cement that obtained the same data when it was direct cured and chemical activated. The interposition of porcelain disk during the photoactivation did alter the DTS values only for the RelyX ARC cement. However, the mechanical fatigue didn't alter the DTS values of any dual resin cement tested. Each dual cement composition, as their activation mode, was fundamental in order to obtain its DTS values. / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientador: Marcelo Giannini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T02:04:38Z (GMT). No. of bitstreams: 1 DiFrancescantonio_Marina_M.pdf: 16720831 bytes, checksum: ce2d1ee161bca05d6b15b3e0a9eaeedd (MD5) Previous issue date: 2009 / Resumo: As propriedades mecânicas dos cimentos resinosos são influenciadas pelo tipo e composição da matriz resinosa, tipo e tamanho das partículas de carga, modo e grau de conversão dos monômeros em polímeros, e a viscosidade é uma propriedade que está intimamente ligada a esses fatores. Os objetivos deste estudo foram avaliar a influência da viscosidade (alta e baixa) e modo de polimerização (polimerização dual e autopolimerizado) de cimentos resinosos duais (Nexus 2/ Kerr, Corp e Variolink II/ Ivoclar-Vivadent): na resistência de união da restauração à dentina (RU), no grau de conversão (GC) e na resistência flexural biaxial (RFB). Para o teste de RU, substratos dentinários de cinqüenta e seis terceiros molares humanos foram utilizados para o ensaio de microtração através da cimentação de uma peça protética do material de resina composta indireta e estes foram foto-ativados ou não segundo cada grupo experimental. Após 24 horas, os dentes foram secionados para obter espécimes em forma de palitos (de área de secção transversal de 1.0 mm²), que foram testados em tração a uma velocidade de 0,5 mm/ mim (4411/Instron). Os resultados foram analisados por ANOVA 3 fatores e teste Tukey (p=0,05). Para a análise do GC, os cimentos foram aplicados na superfície da unidade de reflectância total atenuada acoplada ao espectrômetro infravermelho (Nicolet Instrument Corp, Madson, Wisconsin, EUA) sendo foto-ativados ou não. Espectros foram obtidos após 5 minutos e 24 horas. O cálculo do grau de conversão foi realizado através da análise da mudança na proporção entre as alturas dos picos das ligações duplas de carbono alifática e aromática. Os dados foram submetidos a ANOVA 3 fatores e teste de Tukey (p=0,05). Para o ensaio de RFB, noventa e seis discos de cimentos resinosos (0,5mm de espessura/ 6mm de diâmetro) foram preparados utilizando moldes de silicone de adição (n=12) e foram foto-ativados ou não segundo os grupos experimentais. Após 5 dias, os discos foram testados em dispositivos de ensaio de flexão biaxial em máquina de ensaio universal (1,27 mm/min, Instron 5844) e os dados analisados estatisticamente por ANOVA 3 fatores e teste Tukey(p=0,05). Para a RU, a polimerização dual (foto + autopolimerização) aumentou significantemente os valores médios para os cimentos resinosos em baixa viscosidade para ambos os cimentos resinosos duais utilizados no estudo. Em relação o GC, a foto-ativação e quando o GC foi mensurado após 24 horas, aumentaram significativamente o GC para ambos os cimentos resinosos. A versão em baixa viscosidade apresentou maior GC que os em alta viscosidade, para as duas formas de polimerização. No teste RFB, a foto-ativação aumentou significantemente a resistência e módulo de flexão. A versão em alta viscosidade quando foto-ativada mostrou maior resistência flexural que em baixa viscosidade, enquanto a viscosidade não alterou os valores médios de módulo flexural. Pode-se concluir que a foto-ativação é necessária durante a cimentação de restaurações indiretas, para garantir adequadas propriedades físico-químicas, e a utilização de cimentos resinosos em diferentes viscosidades pode modificar os valores médios de RFB, GC e RU à dentina. / Abstract: The mechanical properties of resin cements may be influenced by the type and monomer composition, type and filler size, mode, and degree of conversion, which are all associated with resin viscosities. The aim of this study was to evaluate the influence of resin cement viscosity (high and low) (Nexus 2/ Kerr, Corp and Variolink II/ Ivoclar-Vivadent) and the curing mode (dual and chemical activation) on the bond strength to dentin, on the degree of conversion and biaxial flexural strength. For microtensile bond strength test, two bonding agents and their respective resin cement, occlusal dentin surfaces of fifty-six human third molars were used for the testing and the resin cements were applied to pre-cured resin composite discs, which were fixed to dentin surfaces, simulating an indirect restoration. The restored teeth were either light-activated or allowed to self-cure, according to experimental groups. After 24 hs, the teeth were sectioned to obtain bonded beams specimens (1.0 mm²). Each specimen was tested in tension at a crosshead speed of 0.5 mm/min (4411/Instron). Data (MPa) was analyzed by 3- way ANOVA and Tukey's Tukey's test (p=0.05). To evaluate the degree of conversion, the resin cements were applied to surface of a horizontal attenuatedtotal- reflectance unit (Nicolet Instrument Corp, Madson, Wisconsin, EUA) and were polymerized using one of two conditions: self-cure (SC) or direct light exposure (600 mW/cm2, XL3000/3M ESPE) and infrared spectra were obtained after 5 minutes and 24 hours. The degree of conversion was calculated using standard techniques of observing changes in aliphatic-to-aromatic peak ratios pre- and postcuring. Data were analyzed by 3-way repeated measure ANOVA and Tukey's test (p=0.05). For the biaxial flexural strength, forty-eight resin cement discs of each product (0.5 mm thick and 6.0 mm in diameter) were created using silicon impression material molds (n=12) and were either light activated or not, according to experimental groups. After 5 days, the specimens were subjected to the biaxial flexure test in a universal testing machine (1.27 mm/min, Instron 5844) and the data ware statistically analyzed by 3-way ANOVA and Tukey's post-hoc test (p=0.05). For bond strength testing, the dual curing mode increased the bond strength for the low viscosity resin cements for both dual resin cement used in this study. For the degree of conversion, the light activation, after 24h, significantly increased the degree of conversion for both resin cements, and the low viscosity version from dual cure or self-cured groups exhibited higher degree of conversion than high viscosity version. Regarding biaxial flexural strength, the light-activation significantly increased flexural strength and modulus, and the high viscosity versions of dual cure groups exhibited higher flexural strength than their low viscosity versions, while the viscosity of resin cements did not influence the modulus. In conclusion, the light-activation of dual resin cements is required in indirect restorations, to provide proper mechanical and chemical properties, and the use of resin cements with different viscosities may change the bonding biomechanical characteristics of indirect restorations. / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T22:07:09Z (GMT). No. of bitstreams: 1 Humel_MariaMalerbaColombi_M.pdf: 94914593 bytes, checksum: c626dc60328a5176cf526d1c4fa76f3c (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi analisar a resistência a microtração, microdureza Knoop do compósito e formação de fendas em restaurações classe I utilizando três sistemas adesivos: Clearfil S3 Bond (S3), Clearfil Protect Bond (ProtectB) e One-Up Bond F Plus (OneUp); E compósito TPH3, fotoativados por fontes de Luz Emitida por Diodo (LED) ou luz halógena, tendo o ângulo cavosuperficial em esmalte condicionado ou não por ácido fosfórico à 35%. Após o término das restaurações, foram obtidas réplicas em resina epóxica para análise em Microscopia Eletrônica de Varredura (MEV) da adaptação da margem em esmalte antes e após termociclagem (n=6). Através de sorteio, a metade dos 144 dentes restaurados foi utilizada no ensaio de microtração e a outra metade no ensaio de microdureza Knoop em 3 diferentes profundidades (n=6). Uma vez que a análise de variância apontou diferença entre os fatores estudados, o resultado do teste Tukey apontou, para análise de fendas nos grupos sem condicionamento prévio do esmalte cavosuperficial, independente do adesivo aplicado, apresentou diferença estatística significativa após os ciclos, quando comparados aos valores antes da termociclagem. Para o adesivo OneUp, o condicionamento do esmalte cavosuperficial contribuiu na redução de fenda. Para o teste de microtração, a análise de variância demonstrou não haver diferença estatística siginificativa entre os fatores estudados e suas inteirações (p = 0,05). Os adesivos OneUp e S3 apresentaram maiores valores de microdureza Knoop no topo, e o adesivo ProtectB não apresentou diferenças estatísticas entre as três profundidades. O adesivo S3 apresentou os menores valores de dureza nas profundidades de base e intermediária. Os sistemas autocondicionantes não apresentaram diferença na união ao substrato dentário, independente de sua forma de aplicação e do condicionamento prévio do esmalte cavosuperficial. Porém, o condicionamento do esmalte cavosuperficial contribuiu na diminuição da formação de fendas, apenas para o adesivo OneUp se comparados os grupos após termociclagem sem condicionamento e com condicionamento do esmalte cavosuperficial. A composição do adesivo utilizado teve influência na microdureza Knoop do compósito odontológico dependendo da profundidade da cavidade. A luz LED apresentou melhores valores de microdureza quando comparado à luz Halógen / Abstract: The aim of this study was to analyze the microtensile bond strength, Knoop microhardness and gap formation of class I restorations using three different self-etching adhesives: Clearfil S3 Bond (S3), Clearfil Protect Bond (ProtectB) and One-Up Bond F Plus (OneUp). TPH3 restorative composite was used with two different light activation: Light Emitted by Diode or Halogen Lamp and the superficial enamel was etched or not with 35% phosphoric acid. After restorative procedure, epoxy resin replicas were obtained before and after submitted teeth to thermal cycling for gap analyzes by Scanning Electronic Microscopy (SEM) of enamel marginal adaptation. Half of teeth were randomly divided to microtensile bond strength test and the other half to microhardness test (n=6). For gap formation, the Tukey's test showed statistical differences before and after thermal-cycling to the groups without enamel etching. For OneUp adhesive, the etched enamel contributed to avoid gap formation when compared groups before thermal-cycling with and without enamel cavosurface etching. OneUp and S3 adhesives showed the highest square means on top surface for Knoop microhardness results, and S3 showed the lowest square means for the middle and base surfaces. ProtectB showed no significant differences for the different surface depth. The self-etching adhesives showed no significant difference to the microtensile Bond strength, irrespective to the different application procedure and previous etching or not of the enamel surface. However, the etched enamel contributed to avoid gap formation when OneUp adhesive system was used when compared groups befoure termocycling with and without enamel cavosurface etching. The adhesive system showed an influence on resin composite to Knoop microhardness test depending on the restoration depth. The LED light activation restorations showed the highest microhardness means when compared with Halogen Lamp. / Mestrado / Dentística / Mestre em Clínica Odontológica

Orientador: Simonides Consani / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T05:29:08Z (GMT). No. of bitstreams: 1 Loureiro_FlaviaHelenFurtado_M.pdf: 641905 bytes, checksum: 2615b8335b9cf2d7b6a766b05792ef4e (MD5) Previous issue date: 2007 / Resumo: O estudo avaliou o efeito de métodos de avaliação sobre as variações térmicas, em função de diferentes tipos de fotoativação do compósito Filtek Z250. Para o método de avaliação pelo dente foram utilizados 50 incisivos bovinos hígidos, nos quais foram feitos preparos cavitários (2x2x2mm) padronizados a 13mm da junção amelo-cementária. Os dentes foram separados aleatoriamente em 5 grupos (n=10), de acordo com o tipo de fotoativação: 1- luz halógena contínua (700 mW/cm2 por 20s); 2- luz halógena com dupla intensidade (inicial de 100 mW/cm2 por 5s obtida com espaçador, seguido de 700 mW/cm2 por 15s, totalizando 20s); 3- luz halógena intermitente (2s de ativação com 700 mW/cm2 seguido do mesmo tempo pela ausência de luz, totalizando 40s); 4- luz emitida por diodo (400 mW/cm2 por 20s); 5- luz emitida por arco de plasma de xenônio (1450 mW/cm2 por 10s). No método de avaliação pela matriz, a resina composta foi inserida num molde cúbico de silicone (2x2x2mm) apoiado numa base de resina acrílica para servir como guia do termopar. Um disco de dentina (1mm) foi colocado entre o termopar e a resina composta para simular a dentina remanescente do preparo cavitário do método de avaliação pelo dente. O protocolo experimental de fotoativação para o método de avaliação pela matriz foi similar ao método de avaliação pelo dente. As restaurações de ambos os métodos foram realizadas em ambiente controlado (37oC e 40±10% UR) e as temperaturas registradas com termômetro digital acoplado ao termopar tipo-K introduzido no canal radicular, de maneira que ficasse, no método dente, em contato com a dentina da câmara pulpar, correspondente à parede axial do preparo e no método matriz, em contato com o disco de dentina. Os dados foram submetidos à analise de variância e ao teste de Tukey em nível de 5% de probabilidade. A média da variação de temperatura registrada pela técnica da matriz (2.56oC) foi maior e com diferença estatisticamente significante quando comparada à média registrada na técnica do dente (1.17 oC), independente dos demais fatores. Houve diferença estatística significativa entre os fotoativadores quando comparados em cada método de avaliação e em todos os tipos de fotoativação quando os métodos de avaliação foram comparados entre si / Abstract: This study evaluated the effect of different methods of thermal evaluation using Filtek Z250 composite resin with different methods of photoativation. In the method of evaluation with tooth it was used 50 incisors where was prepared standardized cavities (2x2x2mm) 13 mm far from amelo-cementary junction. The teeth were randomly assigned into 5 groups (n=10), according to each light-curing method: 1- continue halogen light ( 700mW/cm2 per 20s); 2- halogen light with a soft-start mode (initial intensity of 100mW/cm2 per 5s obtained with a spacer and 700 mW/cm2 per 15s, totaling 20s); 3-intermittent halogen light (2s at 700 mW/cm2, followed by the same time of light absence, totaling 40s); 4- LED (400 mW/cm2 per 20s); PAC (1450 mW/cm2 per 10s). In the method of evaluation with matrix the resin composites were applied into a cubic elastomer mold (2x2x2mm). This mold was positioned under the acrylic resin base that guide the acess of thermocouple. Between the thermocouple and the composite, a 1.0mm dentine disc was positioned to simulated the remaining dentin of the method of evaluation with tooth. The same experimental protocol of photoativation was used for both methods. All experiments were carried out in a controlled environment (37 degree centigrates and 40±10% relative humidity). The variations of temperature(degree centigrates) were obtained using a digital thermometer attached to a type-k thermocouple, which was inserted into the root canal and in contact to the dentine of the pulp chamber (correspondent to the axial wall of the cavity) or in the matrix in contact with the dentine discs. The data were submitted to a two-way ANOVA and the means were compared by the Tukey's test (5%). The variation of temperature with the matrix technique (2.56 degrees centigrates) was higher and with significant different from the tooth technique (1.17 degrees centigrates), independent of the others factors. There was statistical difference among light cure units inside the same evaluation method and when the methods were compared. / Mestrado / Mestre em Materiais Dentários

Orientador: Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T10:00:26Z (GMT). No. of bitstreams: 1 Brandt_WilliamCunha_M.pdf: 8253284 bytes, checksum: 5b5866a653bd8e558f3b48364895e2aa (MD5) Previous issue date: 2007 / Resumo: O objetivo do presente estudo foi analisar o grau de conversão (GC) de compósitos experimentais contendo diferentes fotoiniciadores quando fotoativados por diferentes fontes de luz. Um compósito experimental contendo uma mistura de BisGMA, UDMA, BisEMA e TEGDMA foi preparado com o uso dos fotoiniciadores CQ (Canforoquinona) e PPD (1-Fenil-1,2-Propanodiona). Os fotoiniciadores foram usados sozinhos ou em associação. O agente redutor usado foi a amina terciária DMAEMA (dimetil amino etil metacrilato). À mistura, foram acrescentados 65% em massa de partículas de carga silanizadas. As fontes de luz utilizadas para a fotoativação dos compósitos foi uma fonte de luz baseada em lâmpada de halogênio-quartzo-tungstênio - QTH (XL 2500-3M/ESPE) e duas fontes de diodo emissor de luz - LED (UltraBlue IS-DMC e UltraLume LED 5-Ultradent). Os diâmetros das pontas das fontes de luz (cm) foram mensurados para o cálculo da área de emissão de luz de cada aparelho fotoativador, e posterior verificação da irradiância (mW/cm²) através do cálculo potência/área. As fontes de luz foram submetidas à análise de potência (mW), estando o diâmetro da ponta ativa dos fotoativadores padronizado ou não. Após, a análise das fontes de luz foi realizada através de um espectrômetro (USB 2000) e os espectros emitidos pelas fontes de luz foram registrados para a aferição da irradiância em determinados comprimentos de onda. Um espectrofotômetro (Varian Cary 5G) foi utilizado para a análise da curva de absorção dos fotoiniciadores. A análise do GC foi realizada através de Espectroscopia de Infravermelho Transformada de Fourier - FTIR. Os resultados de GC foram submetidos à análise de variância dois fatores (ANOVAtwo way) e teste de Tukey (5%). De acordo com a análise das fontes de luz, o UltraLume 5 apresentou os maiores valores de irradiância (1315 mW/cm²) com pico de emissão de luz em 454nm, enquanto o UltraBlue IS os menores valores (597 mW/cm²) com pico de emissão de luz em 456nm. O aparelho XL 2500 apresentou valores intermediários de irradiância (935 mW/cm²) e pico de emissão de luz em 484nm. A análise da curva de absorção dos fotoiniciadores demonstrou que a CQ possui absorção concentrada na região azul do espectro da luz visível com Absmax em 470nm, enquanto que o PPD inicia a curva na região UV com Absmax em 398nm com término na região visível. Quando os compósitos foram fotoativados pelas fontes de luz LED, não existiu diferença nos valores de GC, independentemente do fotoiniciador usado. Porém, quando a fonte de luz QTH foi utilizada, o compósito contendo PPD mostrou valores de GC estatisticamente menores que os contendo somente CQ. O fotoiniciador PPD mostrou potencial para a iniciação da reação de polimerização de compósitos dentais fotoativados. Um importante fator a ser considerado além da densidade energética total é a correlação entre o espectro de absorção do fotoiniciador e o espectro de emissão da fonte de luz / Abstract: The aim of this study was to evaluate the degree of conversion (DC) of experimental resin composites, with different photoinitiators, activated by different light-curing units (LCUs). A blend of BisGMA, UDMA, BisEMA and TEGDMA with camphorquinone (CQ) and/or 1-phenyl-1,2-propanedione (PPD) was prepared. Dimethylaminoethyl methacrylate (DMAEMA) was used as co-initiator. Each mixture was loaded with 65wt% of silanated filler particles. Quartz-tungstenhalogen â?¿ QTH (XL 2500, 3M ESPE) or light-emitting diode â?¿ LED (UltraBlue ISDMC and UltraLume LED 5-Ultradent) units were used for activation procedures. The diameter of the tip (cm) and the output power (mW) were obtained. The irradiance (mW/cm2) value was calculated by the ratio of the output power by the area of the tip. The light emitted by each unit was analyzed using a spectrometer (USB 2000), and the spectral profile was recorded to assess the irradiance value in different areas of the light spectrum. The absorption curve of each photoinitiator was analyzed using a spectrophotometer (Varian Cary 5G). DC was assessed by Fourier transformed infra-red spectroscopy. Data were submitted to two-way ANOVA and Tukeyâ?¿s test (5%). In the LCUs analysis, UltraLume 5 showed the highest irradiance values (1315 mW/cm²), with peak of emission at 454nm, whereas UltraBlue IS presented the lowest irradiance values (597 mW/cm²), with peak of emission at 456nm. XL 2500 showed intermediary values (935 mW/cm²), with peak of emission at 484nm. The light absorption analysis of dental photoinitiators showed that CQ exhibited an absorption centered in the blue region of the light spectrum, with Absmax at 470nm, while PPD initiates the curve in the UV region, with Absmax at 398nm, your absorption extended to the visible region. For light-activation using the both LED units, no significant difference in DC values was observed, regardless of the photoinitiator agent. However, for activation with the QTH unit, the composite with PPD showed significantly lower DC values than composites with CQ. In summary, PPD showed potential use as initiator agent for polymerization of light-cured dental composites. An important factor which should be considered, besides the radiant exposure, is the correlation between the absorption spectrum of the photoinitiator and the emission spectrum of the LCU / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientadores: Regina Maria Puppin Rontani, Renata de Oliveira Mattos-Graner / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T10:43:29Z (GMT). No. of bitstreams: 1 Fucio_SuzanaBeatrizPortugalde_M.pdf: 1914666 bytes, checksum: 2dbf8bdbcedb3127f232b29d0b441c5b (MD5) Previous issue date: 2007 / Resumo: O desenvolvimento do biofilme de Streptococcus mutans sobre materiais restauradores e a biodegradação destes substratos em função dos metabólitos bacterianos podem ser influenciados pelas propriedades e características do material. A partir de uma revisão sistemática em que se verificou a carrência de estudos a respeito dos efeitos do biofilme na superície de materiais restauradores, foi proposto investigar algumas características quantitativas e qualitativas do biofilme após 30 dias de interação com materiais restauradores, além de analisar propriedades e microestrutura da superfície dos materiais que sofreram tal interação. Para cada material testado (cerâmica - C, resina composta nanoparticulada e cimentos de inúmero de vidro modificado por resina - CIVMR e convencional - CIVC), foram confeccionados 25 discos sob condições assépticas, para distribuição em 3 grupos de estocagem: 1) 100% de umidade relativa a 37ºC (n=5); 2) meio de cultura a 37ºC (BHI + 1% sacarose) (n=5); 3) biofilme de Streptococcus mutans e meio de cultura a 37ºC (n=15). Valores de dureza do grupo 1 (valores imediatos) foram obtidos previamente à estocagem, a fim de se verificar alterações ao longo do tempo quando estocados em umidade relativa apenas. Após 30 dias de estocagem, os discos do grupo 3 foram levados para observação do biofilme corado e hidratado em microscopia de varredura confocal a laser (CLSM). As imagens obtidas auxiliaram na obtenção de valores / Abstract: Streptococcus mutans biofilm development on restorative materials and biodegradation of those materials due to bacterial acids are influenced by material properties and characteristics. Since a systematic review found a deficiency concerning studies related to effects of biofilm on the surface of restorative materials, the proposition for this investigation was to analyze some quantitative and qualitative biofilm characteristics after 30-days interaction with restorative materials. In addition, it was investigated changes on the surface properties and microstructure of materials after 30-days interaction. Twenty-five disks of each material tested (ceramic - C, nanofill composite - NC, resin-modified glass ionomer - RMGIC and conventional glass ionomer cement - CGIC) were made, at aseptic conditions, and distributed in 3 storage groups: 1) 100% relative humidity at 37ºC (n=5); 2) growth medium at 37ºC (BHI + 1% sucrose) (n=5); 3) Streptococcus mutans biofilm and growth medium at 37ºC (n=15). Vickers hardness values from group 1 were obtained previously storage, in order to observe aging by relative humidity. After 30 days storage, disks were stained, kept hydrated and observed by confocal laser scanning microscopy, whose images supported to acquire values concerning biofilm thickness, bio-volume, roughness coefficient and surface to volume ratio. Qualitative analyses related to viable / non-viable cells distribution and biofilm architecture also were realized. Subsequently, all disks were ultrasonically washed and analyzed to surface roughness, hardness and microstructure. Biofilms presented a progression more viable cells in superficial regions of the biofilm to proportionally more nonviable cells in the deeper regions of the biofilms, near the disk. Besides, cellular aggregates and fluid-filled channels were observed in biofilm developed on all materials. Concerning biofilm quantitative properties, thickness was the unique with difference statistically significant among materials. C and NC accumulated thicker biofilms than RMGIC and CGIC. There was no difference statistically significant among immediate and storage groups related to C and NC surface roughness and hardness. However, group 3 of NC showed surface biodegradation microscopically. Group 1 of RMGIC and CGIC presented higher hardness values than immediate values. Nevertheless, hardness values from RMGIC group 3 decreased compared groups 1 and 2, while surface roughness values of group 3 increased statistically. Group 3 of CGIC showed higher roughness values than other groups and no difference statistically significant among three storage groups concerning hardness values. RMGIC and CGIC micrographs also demonstrated biodegradation on the surface materials. Within this study conditions, it was concluded that there was influence of restorative materials on biofilm development and influence of biofilm on the surface properties and microstructure characteristics of materials tested, being material -dependent / Mestrado / Materiais Dentarios / Doutor em Materiais Dentários

Orientadores: Lourenço Correr Sobrinho, Evandro Piva / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:26:35Z (GMT). No. of bitstreams: 1 Moraes_RafaelRattode_M.pdf: 1004520 bytes, checksum: 0807f001b1199f8774a3942567218dd4 (MD5) Previous issue date: 2007 / Resumo: O objetivo deste estudo foi investigar a influência da adição de Bis-EMA sobre propriedades físicas e mecânicas de cimentos resinosos experimentais à base de Bis- GMA/TEGDMA. A partir da mistura de Bis-GMA e TEGDMA na proporção de 50:50 em peso (R01), o monômero Bis-EMA foi gradualmente incorporado à mistura, 10% em peso por vez, definindo onze formulações adicionais com as seguintes proporções entre Bis- GMA/TEGDMA/Bis-EMA: 50/40/10 (R02), 50/30/20 (R03), 50/20/30 (R04), 50/10/40 (R05), 50/0/50 (R06), 40/10/50 (R07), 30/10/60 (R08), 20/10/70 (R09), 10/10/80 (R10), 0/10/90 (R11) e 0/0/100 (R12). Canforoquinona (0,4%), N,N-dimetil-p-toluidina (0,8%) e hidroquinona (0,2%) foram dissolvidas em cada mistura, às quais foram adicionados 60% em peso de partículas de vidro silanizadas. O grau de conversão foi avaliado por espectroscopia infravermelha em tempo real. A resistência flexural e módulo de elasticidade foram analisados em teste de flexão de três pontos. A espessura de película foi mensurada colocando os materiais entre placas de vidro polidas. A dureza Knoop foi determinada em um microdurômetro, com carga de 50g por 15s. A sorção de água e a solubilidade foram avaliadas por meio de alteração de peso das amostras após imersão em água destilada por sete dias. Os dados foram separadamente submetidos à Análise de Variância e teste de Tukey (a = 0,05). As médias para grau de conversão (%) variaram entre 49,8 (R10) e 65,0 (R06). A substituição de TEGDMA por Bis-EMA aumentou a conversão de ligações duplas, enquanto a substituição de Bis-GMA por Bis-EMA não apresentou influência significativa. No teste de flexão, as médias (MPa) variaram entre 104 (R10) e 131 (R02), mas nenhuma diferença significativa entre os grupos foi detectada. Para o módulo de elasticidade, enquanto a substituição de TEGDMA por Bis-EMA não apresentou influência significativa, a substituição de Bis-GMA por Bis-EMA diminuiu significativamente os valores, com médias (GPa) variando entre 5,41 (R09) e 9,59 (R04). As médias de espessura de película (µm) variaram entre 29,3 (R01) e 66,7 (R06), com a substituição de TEGDMA por Bis-EMA gradualmente aumentando os valores, e R04-06 apresentando películas significativamente mais espessas. Médias para dureza (kg/mm2) variaram entre 35,5 (R01) e 47,9 (R05), com a substituição de TEGDMA por Bis-EMA aumentando gradualmente a dureza, exceto para R06, enquanto a substituição de Bis-GMA por Bis-EMA não apresentou efeito significativo. Uma gradual diminuição na sorção de água foi verificada à medida que TEGDMA e Bis- GMA foram sendo substituídos por Bis-EMA, com médias (µg/mm3) variando entre 48,96 (R01) e 15,68 (R12). Médias para solubilidade variaram entre 4,55 (R04) e 9,77 (R02), sem diferença significativa observada entre os grupos. Em geral, os achados do presente estudo mostram que, dependendo da quantidade de Bis-EMA substituindo Bis-GMA e/ou TEGDMA, maior conversão de monômeros ou menor módulo de elasticidade foram detectados. Por outro lado, a substituição de TEGDMA por Bis-EMA aumentou a dureza e diminuiu a sorção de água, embora um aumento na espessura de película tenha sido detectado para algumas misturas. Além disso, a substituição de Bis-GMA por Bis-EMA apresentou influência significativa na diminuição da sorção de água / Abstract: The aim of this study was to investigate the influence of Bis-EMA addition on physical and mechanical properties of experimental resin luting agents based on Bis- GMA/TEGDMA. Starting from a 50:50 wt:wt ratio blend of Bis-GMA and TEGDMA (R01), the Bis-EMA monomer was gradually added to the mixture, 10wt% at a time, defining eleven additional formulations with the following Bis-GMA/TEGDMA/Bis-EMA ratios: 50/40/10 (R02), 50/30/20 (R03), 50/20/30 (R04), 50/10/40 (R05), 50/0/50 (R06), 40/10/50 (R07), 30/10/60 (R08), 20/10/70 (R09), 10/10/80 (R10), 0/10/90 (R11) and 0/0/100 (R12). Camphorquinone (0.4%), N,N-dimethyl-p-toluidine (0.8%) and hydroquinone (0.2%) were dissolved in each mixture, which were loaded to a constant 60wt% with silanated glass fillers. Degree of conversion was assessed by real-time infrared spectroscopy. Flexural strength and elastic modulus were determined in a three-point bending test. Film thickness was measured by placing the materials between optically flat glass plates. Knoop hardness evaluation was carried out through an indenter, with a load of 50g for 15s. Water sorption and solubility were assessed by weight alteration of samples after storage in distilled water for seven days. Data were separately submitted to Analysis of Variance and Tukey's test (a = 0.05). Means for degree of conversion (%) varied between 49.8 (R10) and 65.0 (R06). Replacing TEGDMA with Bis-EMA caused an increase in conversion of double bonds, while the substitution of Bis-GMA by Bis-EMA had no significant influence. Means for flexural strength (MPa) varied between 104 (R10) and 131 (R02), but no significant difference among groups was detected. For the elastic modulus, while replacing TEGDMA with Bis-EMA had no significant influence, the replacement of Bis-GMA by Bis-EMA significantly decreased the values, with means (GPa) varying between 5.41 (R09) and 9.59 (R04). Film thickness means (µm) varied between 29.3 (R01) and 66.7 (R06), with the substitution of TEGDMA by Bis-EMA gradually increasing the film values, and R04-06 showing significantly thicker films. Hardness means (KHN, kg/mm2) varied between 35.5 (R01) and 47.9 (R05), with the replacement of TEGDMA by Bis-EMA gradually increasing hardness, except for R06, while replacing Bis-GMA with Bis-EMA had no significant effect. A gradual decrease in water sorption was detected as TEGDMA and Bis-GMA were gradually replaced by Bis-EMA, with means (µg/mm3) varying between 48.96 (R01) and 15.68 (R12). Solubility means (µg/mm3) varied between 4.55 (R04) and 9.77 (R02), with no significant differences detected among groups. In general, the present findings show that, depending on the amount of Bis-EMA replacing Bis-GMA and/or TEGDMA, increased monomer conversion or decreased elastic modulus were detected. On the other hand, replacing TEGDMA with Bis-EMA increased hardness and decreased water sorption, although an increase in film thickness has been detected for some mixtures. Also, the substitution of Bis-GMA by Bis-EMA had a significant influence on decreasing water sorption / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários

Orientador: Simonides Consani / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T11:55:44Z (GMT). No. of bitstreams: 1 Lopes_MuriloBaena_D.pdf: 3468611 bytes, checksum: 9606e712f2290f8675f6224ff08a51a6 (MD5) Previous issue date: 2007 / Resumo: O propósito deste estudo foi: 1 - Comparar os valores de resistência de união esmalte e dentina humanos com os valores obtidos em dentes bovinos, utilizando dois sistemas de união com princípios de atuação distintos; 2 -Comparar as dimensões tubulares e distribuição na dentina humana e bovina; 3-Comparar duas técnicas (confocal e microscopia óptica) para determinar a microinfiltração em dentes bovinos e humanos para sistemas adesivos. Para o teste de resistência de união, a dentina e o esmalte humano e bovino apresentaram valores equivalentes para o Clearfil Liner Bond 2V. O Scotchbond Multi-Purpose não mostrou diferença estatística em esmalte, porém em dentina o substrato bovino mostrou maiores valores de união que o humano. Quando analisado o diâmetro tubular, a dentina bovina superficial e média mostrou diâmetros estatisticamente maiores que para a dentina humana superficial e média. Não se encontrou diferença estatística entre o diâmetro tubular em dentina humana e bovina em dentina profunda. A densidade dos túbulos dentinários foi estatisticamente maior em dentina humana que em dentina bovina. No teste de microinflitração, quando dente bovino foi utilizado, o Scotchbond apresentou estatisticamente mais infiltração que o Clearfil. Para o dente humano não foi encontrada diferença estatística. Quando escores foram analisados, o Scotchbond não apresentou diferenças para o Clearfil, entretanto este apresentou estatisticamente menos infiltração em dente bovino que em dente humano quando o microscópio óptico foi utilizado. Microscópio confocal mostrou maior especificidade para o corante e limites de microinfiltração mais nítidos. Com o substrato bovino nem sempre se encontrou resultados equivalentes em teste de união com o dente humano. A estrutura dentinária mostrou-se diferente entre dentes humanos e bovinos. O dente bovino não seria o mais adequado para testes de microinfiltração / Abstract: The purpose of this study was: 1 - To compare shear bond strength values obtained in human enamel and dentin with the values obtained in bovine teeth using two adhesive systems with different actions; 2- To compared the tubular dimensions and distribution of human dentine and bovine dentine; 3 - To compare two techniques (confocal and optical microscopies) for determining microleakage in human and bovine teeth for adhesive bond systems. For shear bond strength, the bovine and the human dentin and enamel had equivalent values for Clearfil Liner Bond 2V. Scotchbond Multi-Purpose had no statistical differences on enamel, but on dentin, the bovine substrate showed higher bond strength values than the human one. Bovine dentine tubular diameter for superficial and middle dentine was significantly greater than for human superficial and middle dentine. There was no significant difference in tubular diameter between human and bovine deep dentine. The density of dentine tubules is significantly greater in human dentine than in bovine dentine. When bovine teeth were used, Scotchbond showed statistically higher mean penetration than Clearfil. When human teeth were used no difference was found. For microleakage test, when bovine teeth were used, Scotchbond showed statistically higher mean penetration than Clearfil. When human teeth were used no difference was found. When scores were analyzed, Scotchbond showed no difference to Clearfil, however Clearfil showed statistically less infiltration in bovine teeth than in human teeth when optical microscopy was used. Confocal microscopy showed higher sensibility for the stain and clearer leakage limits. The bovine teeth not always show the same pattern of results of human teeth in shear bond test. The dentinal structure showed different between human and bovine substrates. Bovine teeth may be not suitable for adhesive microleakage tests / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários