Zugl.: Dresden, Techn. Universiẗat, Diss. 2008.

Zugl.: Aachen, Univ., Diss., 2008

University, Diss., 2004--Kiel.

The adsorption and organization of reactive microgels has been investigated on technical aluminium. By means of a two-step emulsion polymerisation with phosphate substituted monomer we obtain polymeric nano-particles with phosphate groups on the surface. In a first step cross-linked butyl acrylate/styrene particles were formed. In a second step a mixture of functionalised acrylate and butyl acrylate/styrene was added to the system. In this way, the composite particles were obtained. Particle size and size distribution were measured by F-FFF and light scattering methods. For phosphate functionalised dispersions, it was possible to show the distribution of P-species around particles by energy dispersive TEM easurements. These nano-particles adsorb spontaneously onto aluminium surfaces from aqeous dispersion. They form well packed layers, which have been proved by SEM measurements. The properties of the adsorbed microgel layers were confirmed by industrial linked adhesion and corrosion tests. Panels with adsorbed phosphate funczionalised particles have an excellent corrosion inhibition effect.

The light scattering methods were used for characterization of properties and formation of networks of different dimension, based on N-vinylcaprolactam (VCL). Formation of PVCL microgels in presence of poly(vinyl alcohol) as stabilizer was studied. Size of resulting microgels strongly depends on the temperature and heating rate: interparticle aggregation was observed during slow heating and intraparticle collapse during fast heating. Angular dependence of measured diffusion coefficient on the angle of observation was studied for the microgel in the swollen, shrunken and aggregated states. Thermo-sensitive microgels based on N-vinylcaprolactam and acetoacetoxyethyl methacrylate were prepared under surfactant free conditions. The presence of internal part with low thermo-sensitivity and highly thermo-sensitive outer part of the particle (the core-shell structure of microgel) was deduced from static and dynamic light scattering experiments. Results obtained from combined SLS and DLS show the change of conformation from "swollen" soft sphere to compact shrunken "hard sphere". Thermo-sensitive microgel based on N-vinylcaprolactam and N-vinylpyrrolidone was used for investigation of the internal modes in microgel dispersion in the wide range of qRg values. Two internal motions and translation diffusion were observed in the asymptotic range. Angular dependence of the normalized diffusion coefficient showed power law behavior in this range. The experimentally determined value of exponent n = 0.96 was in good agreement with the value predicted for ZIMM limit for polymer chains with hydrodynamic interaction. The reduced first cumulant Ã*(q) reached a constant value in the range of large qRg values. Appearance of plateau value indicates ZIMM limit of hydrodynamic interaction but experimental value was much lower than the theoretically predicted plateau value for linear chains in good solution. 3,3?-(ethane-1,1-diyl)bis(1-vinyl-2-pyrrolidone) was used as a cross-linker of VCL in solution by radical polymerization. The network formation was investigated by dynamic light scattering. It was shown, that monitoring of the light scattered intensity in all cases is quite sensitive to detect the gelation threshold even in the presence of very low amount of cross-linker. The power law of time correlation function at the gel point is a sufficient but not a necessary condition for critical gelation. The exponent calculated from power law depends on cross-linker concentration and can be attributed to the degree of branching. Critical exponents obtained at the gel point by DLS and rheology for hydrogel system based on VCL and hydroxyethyl methacrylate were compared. The theoretically predicted equality of exponents from these methods was found as not valid at least for this studied system.

The light scattering methods were used for characterization of properties and formation of networks of different dimension, based on N-vinylcaprolactam (VCL). Formation of PVCL microgels in presence of poly(vinyl alcohol) as stabilizer was studied. Size of resulting microgels strongly depends on the temperature and heating rate: interparticle aggregation was observed during slow heating and intraparticle collapse during fast heating. Angular dependence of measured diffusion coefficient on the angle of observation was studied for the microgel in the swollen, shrunken and aggregated states. Thermo-sensitive microgels based on N-vinylcaprolactam and acetoacetoxyethyl methacrylate were prepared under surfactant free conditions. The presence of internal part with low thermo-sensitivity and highly thermo-sensitive outer part of the particle (the core-shell structure of microgel) was deduced from static and dynamic light scattering experiments. Results obtained from combined SLS and DLS show the change of conformation from "swollen" soft sphere to compact shrunken "hard sphere". Thermo-sensitive microgel based on N-vinylcaprolactam and N-vinylpyrrolidone was used for investigation of the internal modes in microgel dispersion in the wide range of qRg values. Two internal motions and translation diffusion were observed in the asymptotic range. Angular dependence of the normalized diffusion coefficient showed power law behavior in this range. The experimentally determined value of exponent n = 0.96 was in good agreement with the value predicted for ZIMM limit for polymer chains with hydrodynamic interaction. The reduced first cumulant Ã*(q) reached a constant value in the range of large qRg values. Appearance of plateau value indicates ZIMM limit of hydrodynamic interaction but experimental value was much lower than the theoretically predicted plateau value for linear chains in good solution. 3,3?-(ethane-1,1-diyl)bis(1-vinyl-2-pyrrolidone) was used as a cross-linker of VCL in solution by radical polymerization. The network formation was investigated by dynamic light scattering. It was shown, that monitoring of the light scattered intensity in all cases is quite sensitive to detect the gelation threshold even in the presence of very low amount of cross-linker. The power law of time correlation function at the gel point is a sufficient but not a necessary condition for critical gelation. The exponent calculated from power law depends on cross-linker concentration and can be attributed to the degree of branching. Critical exponents obtained at the gel point by DLS and rheology for hydrogel system based on VCL and hydroxyethyl methacrylate were compared. The theoretically predicted equality of exponents from these methods was found as not valid at least for this studied system.

The adsorption and organization of reactive microgels has been investigated on technical aluminium. By means of a two-step emulsion polymerisation with phosphate substituted monomer we obtain polymeric nano-particles with phosphate groups on the surface. In a first step cross-linked butyl acrylate/styrene particles were formed. In a second step a mixture of functionalised acrylate and butyl acrylate/styrene was added to the system. In this way, the composite particles were obtained. Particle size and size distribution were measured by F-FFF and light scattering methods. For phosphate functionalised dispersions, it was possible to show the distribution of P-species around particles by energy dispersive TEM easurements. These nano-particles adsorb spontaneously onto aluminium surfaces from aqeous dispersion. They form well packed layers, which have been proved by SEM measurements. The properties of the adsorbed microgel layers were confirmed by industrial linked adhesion and corrosion tests. Panels with adsorbed phosphate funczionalised particles have an excellent corrosion inhibition effect.

Poly(3,4-ethylenedioxythiophene), PEDOT, belongs to the group of conducting polymers and is characterized by its high stability, a moderate band gap and its optical transparency in the conductive state. A large disadvantage of conducting polymers, and also PEDOT, is their poor solubility. One way to achieve processible materials is the synthesis of colloidal particles. Thus, this work focuses on the development of conductive particles by preparing composite structures. Polymeric colloids like latex particles and microgels were used as templates for the oxidative polymerization of EDOT. Depending on template structure completely different composite morphologies with variable properties were obtained. It was found that modification with PEDOT did not only cause conductive particles for application as humidity sensor materials, but also candidates for further functionalization with gold nanoparticles (Au-NPs). Due to a multi-stage synthesis route it was possible to achieve polystyrene(core)-PEDOT(shell)-particles decored with Au-NPs. Microgels acting as “micro reactors” for the incorporation of PEDOT and Au-NPs were also used for preparing multifunctional composites for catalytic applications. / Poly(3,4-ethylendioxythiophen), PEDOT, gehört zur Gruppe der leitfähigen Polymere und zeichnet sich durch seine hohe Stabilität, eine moderate Bandlücke und seine optische Transparenz im dotierten Zustand aus. Ein Nachteil leitfähiger Polymere, wie auch von PEDOT, ist deren schlechte Löslichkeit. Die Synthese kolloidaler Partikel bietet jedoch eine Möglichkeit dieses Problem zu umgehen. In diesem Zusammenhang richtete sich der Fokus dieser Arbeit auf die Darstellung leitfähiger Partikel in Form von Kompositstrukturen. Polymerkolloide, wie Latex- und Mikrogelpartikel, sind als Template eingesetzt worden, in deren Gegenwart PEDOT durch eine oxidative Polymerisation synthetisiert wurde. In Abhängigkeit von der Struktur des Templats sind unterschiedliche Kompositmorphologien mit steuerbaren Eigenschaften erhalten worden. Auf diese Weise wurden neben Materialien für die Feuchtigkeitssensorik leitfähige Kompositpartikel hergestellt, die zusätzlich mit Gold-Nanopartikeln (Au-NP) funktionalisiert werden konnten. Durch ein mehrstufiges Syntheseverfahren sind somit Polystyrol(Kern)-PEDOT(Schale)-Partikel mit Au-NP-funktionalisierter Oberfläche synthetisiert worden. Mikrogelpartikel, die als „Mikroreaktoren“ für die Inkorporation von PEDOT- und Au-NP dienten, wurden ebenfalls eingesetzt, um multifunktionale Komposite mit katalytischen Eigenschaften herzustellen.

Gegenstand dieser Arbeit ist die Herstellung funktioneller Polymerpartikel und deren Nutzung für biomedizinische Applikationen. Die Anwendungsgebiete der resultierenden Hybridmaterialien reichen vom Einsatz als Kontrastmittel in bildgebenden Verfahren der medizinischen Diagnostik über die Verwendung als Antimikrobium bis hin zum Einsatz als „Werkzeug“ zur Zellisolierung und aktivierung. Dazu wurden kompakte Latexpartikel und sensitive, poröse Mikrogelpartikel mittels emulgatorfreier Heterophasenpolymerisation synthetisiert. Als funktionelles Monomer wurde Glycidylmethacrylat verwendet, über dessen reaktive Epoxygruppen anschließend weitere Moleküle angebunden werden können. Die Funktionalisierung der Polymerpartikel erfolgte einerseits mit anorganischen Nanopartikeln (dotierte Lanthanfluorid-Nanopartikel, Gold- und Silbernanopartikel) und andererseits mit Biomolekülen wie Nukleotiden und Antikörpern. Einige Verwendungsgebiete, wie die Stimulierung von Memory-T-Zellen mit Antikörper-Polymer-Konjugaten oder der Einsatz der Silberkomposite aufgrund ihrer antimikrobiellen Wirkung, wurden näher untersucht. / The aim of this work was the synthesis of functional polymeric particles and their use for biomedical purposes. The application areas of the resulting hybrid materials range from contrast agents in medical diagnostics and usage due to antimicrobial properties to “tools” for cell isolation and activation. Compact core-shell particles and porous microgel particles were prepared by surfactant-free heterophase polymerization in water. All particles contain glycidyl methacrylate whose epoxy groups are capable to bind other molecules covalently. On the one hand, polymeric particles were functionalized with inorganic nanoparticles (doped lanthanum fluoride nanoparticles, gold and silver nanopariticles) and on the other hand with biomolecules such as nucleotides and antibodies. Selected application fields like the stimulation of memory T-cells with polymer-antibody-conjugates or the use of the silver composites due to their antimicrobial activity were investigated in detail.

Poly(3,4-ethylenedioxythiophene), PEDOT, belongs to the group of conducting polymers and is characterized by its high stability, a moderate band gap and its optical transparency in the conductive state. A large disadvantage of conducting polymers, and also PEDOT, is their poor solubility. One way to achieve processible materials is the synthesis of colloidal particles. Thus, this work focuses on the development of conductive particles by preparing composite structures. Polymeric colloids like latex particles and microgels were used as templates for the oxidative polymerization of EDOT. Depending on template structure completely different composite morphologies with variable properties were obtained. It was found that modification with PEDOT did not only cause conductive particles for application as humidity sensor materials, but also candidates for further functionalization with gold nanoparticles (Au-NPs). Due to a multi-stage synthesis route it was possible to achieve polystyrene(core)-PEDOT(shell)-particles decored with Au-NPs. Microgels acting as “micro reactors” for the incorporation of PEDOT and Au-NPs were also used for preparing multifunctional composites for catalytic applications. / Poly(3,4-ethylendioxythiophen), PEDOT, gehört zur Gruppe der leitfähigen Polymere und zeichnet sich durch seine hohe Stabilität, eine moderate Bandlücke und seine optische Transparenz im dotierten Zustand aus. Ein Nachteil leitfähiger Polymere, wie auch von PEDOT, ist deren schlechte Löslichkeit. Die Synthese kolloidaler Partikel bietet jedoch eine Möglichkeit dieses Problem zu umgehen. In diesem Zusammenhang richtete sich der Fokus dieser Arbeit auf die Darstellung leitfähiger Partikel in Form von Kompositstrukturen. Polymerkolloide, wie Latex- und Mikrogelpartikel, sind als Template eingesetzt worden, in deren Gegenwart PEDOT durch eine oxidative Polymerisation synthetisiert wurde. In Abhängigkeit von der Struktur des Templats sind unterschiedliche Kompositmorphologien mit steuerbaren Eigenschaften erhalten worden. Auf diese Weise wurden neben Materialien für die Feuchtigkeitssensorik leitfähige Kompositpartikel hergestellt, die zusätzlich mit Gold-Nanopartikeln (Au-NP) funktionalisiert werden konnten. Durch ein mehrstufiges Syntheseverfahren sind somit Polystyrol(Kern)-PEDOT(Schale)-Partikel mit Au-NP-funktionalisierter Oberfläche synthetisiert worden. Mikrogelpartikel, die als „Mikroreaktoren“ für die Inkorporation von PEDOT- und Au-NP dienten, wurden ebenfalls eingesetzt, um multifunktionale Komposite mit katalytischen Eigenschaften herzustellen.