Made available in DSpace on 2013-10-11T13:36:07Z (GMT). No. of bitstreams: 1 000450854-Texto+Completo-0.pdf: 2937082 bytes, checksum: a58744bec268788ef21970b772d8b358 (MD5) Previous issue date: 2013 / Short implants have shown success rates similar to implants of conventional length, and both bone quality and initial stability of the receptor site of the implant may influence prognosis. Therefore, this study aimed to evaluate three methods of measuring implant stability - insertion torque (IT), Periotest (PTV) and Osstell (ISQ) - and the effect of bone quality evaluated during surgery (Leckholm and Zarb, 1985) and at images of multislice computed tomography (CT) or cone beam computed tomography (CBCT), assessed visually and by optical density (8bit grayscale), the primary stability of 45 short implants (Straumann SLActive® RN SP 4. 1 x 6-mm long) placed in 20 patients at a private practice. All implants had screw-retained metaloceramic single crowns planned. One implant that showed ample mobility at the time of placement was not deployed and thus not entered into the statistical analysis. The significance level was set at 5%. Correlation was found (Spearman) between IT PTV x (-0. 686), IT ISQ x (0. 606) x ISQ and PTV (-0. 627). Correlation was found between surgical bone quality and visual evaluation of CT / CBCT, but there was no correlation between surgical bone quality and optical density neither between visual evaluation of CT / CBCT and optical density. Primary stability of bone type 4 (evaluated surgically) was statistically lower when assessed by PTV, where the median for bones types 1-2, type 3 and type 4 were -5. 0 (-6. 0, -2. 5), -3. 0 (- 3. 5, 1. 5) and 2. 5 (0. 8, 5. 3), respectively (p <0. 001); ISQ average was 71. 06 (+ / - 8. 48) the type 1-2, 70. 24 (+ / - 4. 24) and 65. 19 in type 3 (+ / - 8. 38) in the type 4 (p <0. 001) and IT, where 78. 6% of type 4 bone implants placed had IT <15Ncm. Each implant obtained bone healing after 3 months. Thus, these results suggest that a moderate correlation between the measurements methods of primary stability (IT, PTV and ISQ) can be established and that the implants placed in type 4 bone get smaller initial stability than the other bone types. More studies are needed to validate methods for assessing bone for use in CT and CBCT. / Os implantes curtos têm mostrado taxas de sucesso semelhantes às dos implantes de tamanho convencional, sendo que a estabilidade inicial e a qualidade óssea do leito receptor do implante podem influenciar seu prognóstico. Desta forma este estudo teve como objetivo avaliar três métodos de aferição da estabilidade dos implantes - torque de inserção (IT), periotest (PTV) e Osstell (ISQ) - e o efeito da qualidade óssea avaliada no ato da cirurgia (Leckholm e Zarb, 1985) e em imagens de tomografias computadorizadas multislice (CT) ou de tomografias computadorizadas cone beam (CBCT), avaliadas visualmente e por densidade óptica (variação de tons de cinza em 8bits), na estabilidade primária de 45 implantes curtos (Straumann SLActive RN SP 4. 1 x 6mm), colocados em 20 pacientes de clínica privada. Para todos os implantes estavam previstas coroas metalocerâmicas aparafusadas unitárias. Um implante que apresentou ampla mobilidade no momento da colocação não foi implantado e não entrou na análise estatística. O nível de significância foi de 5%. Foi encontrada correlação (Spearman) entre IT x PTV (-0,686), IT x ISQ (0,606) e PTV x ISQ (-0,627). Foi encontrada correlação entre a qualidade óssea cirúrgica e a qualidade óssea visual, contudo não houve correlação entre a qualidade óssea cirúrgica e a densidade óptica nem entre a qualidade óssea visual e densidade óptica.A estabilidade primária em osso tipo 4 (avaliado cirurgicamente) foi estatisticamente menor quando avaliada por PTV, onde a mediana foi -5,0 (-6,0 ; -2,5) no tipo 1-2, -3,0 (-3,5 ; 1,5) no tipo 3 e 2,5 (0,8 ; 5,3) no tipo 4 (p < 0,001); ISQ onde a média foi de 71,06 (+/- 8,48) no tipo 1-2, 70,24 (+/- 4,24) no tipo 3 e 65,19 (+/- 8,38) no tipo 4 (p < 0,001); e IT, onde 78,6% dos implantes colocados osso tipo 4 tiveram IT < 15Ncm. Todos os implantes obtiveram cicatrização óssea após 3 meses. Desta forma, estes resultados sugerem uma correlação moderada entre os métodos de estabilidade primária (IT, PTV e ISQ) e que os implantes colocados em osso tipo 4 obtêm menor estabilidade inicial que nos outros tipos ósseos. Mais estudos são necessários para validar métodos de avaliação óssea para serem utilizados em CT e CBCT.

Made available in DSpace on 2013-10-11T13:36:08Z (GMT). No. of bitstreams: 1 000450848-Texto+Completo-0.pdf: 1608827 bytes, checksum: 3e7ff522aa354768faac74eab4ba6daa (MD5) Previous issue date: 2013 / Clinical evidences suggest that the stability of dental implants plays an important role on the success of osseointegration. However, there is not sufficient information with respect to the stability of short (6-mm long) implants. Thus, the aims of this study were: 1) to assess clinically and longitudinally the stability of short implants in relation to the bone quality, by means of insertion torque, resonance frequency analysis (RFA) (Osstell®) and damping capacity (PTV) (Periotest®); and 2) to evaluate the correlation among these three techniques. Thirty-nine one-stage implants (Straumann®, SLActive, ø4. 1 x 6-mm long) were placed in the posterior region of the maxilla and the mandible in 18 patients with ages ranging between 25 and 76 years old. The bone quality was identified by the surgeon’s tactile sensitivity at the moment of the perforation and classified according to the Lekholm & Zarb classification (1985) (types I-IV). The insertion torque was measured using the manual wrench (Straumann®) and divided into three groups: <15 N. cm, between 15 and 35 N. cm and, finally, >35 N. cm. The PTV values were measured immediately after the manual torque, at the implant assembler level. For the RFA values, a mean was calculated for the mesio-distal and bucco-lingual measurements. The RFA and PTVs assessments were repeated at the moment of the crown installation (3 months later). The results showed a significant effect of bone quality on the stability values of the implant. Insertion torque values were significantly higher for bone types I-II than for bone types III and IV. Statistical difference was found only for PTV values between bone types I and II compared to bone type IV. For the RFA values, implants placed in types I-II and III presented ISQ significantly higher than implants placed in type IV bone. Besides that, regardless of the type of bone, the mean ISQ values were significantly higher after the osseointegration period (mean=79. 36) than that at the moment of the placement of the implant (mean=68. 29). The results of this study showed that bone quality influences on the values of primary and secondary stability, presenting moderate correlation among the three methods of stability assessment. / Evidências clínicas sugerem que a estabilidade dos implantes exerce um papel importante no sucesso da osseointegração. No entanto, não há informações suficientes a respeito da estabilidade de implantes curtos (6-mm). Diante disso, os objetivos deste estudo foram: 1) avaliar clínica e longitudinalmente a estabilidade de implantes curtos em função da qualidade óssea, através do torque de inserção, análise da frequência de ressonância (RFA) (Osstell®) e capacidade de amortecimento (PTV) (Periotest®); e 2) avaliar a correlação entre as três técnicas. Foram instalados 39 implantes (Straumann, SLActive, 4. 1 x 6 mm), de 1 estágio cirúrgico, na região posterior de maxila e mandíbula, em 18 pacientes com idade entre 25 e 76 anos. A qualidade óssea foi identificada pela sensibilidade tátil do cirurgião no momento da perfuração e classificada de acordo com a classificação de Lekholm & Zarb (1985) (tipos I-IV). O torque de inserção foi medido utilizando um torquímetro manual (Straumann®), e dividido em três grupos: < 15 Ncm, entre 15 e 35 Ncm e >35 Ncm. Os valores PTV foram medidos imediatamente após o torque manual, no montador do implante. Para os valores de RFA foi calculada a média das medidas mésio-distal e vestíbulo-lingual. A avaliação de RFA e PTVs foi repetida no momento da instalação da coroa (3 meses mais tarde). Os resultados mostraram efeito significativo da qualidade óssea nos valores de estabilidade do implante. Os valores do torque de inserção foram significativamente maiores no osso tipo 1-2 do que em osso tipo 3 e 4. Para os valores PTV foi encontrada diferença estatística entre o osso 1-2 e 4. Analisando os valores RFA, os implantes instalados em osso tipo 1-2 e 3 apresentaram ISQ significativamente maior do que os implantes instalados em osso tipo 4. Além disso, independente do tipo de osso, as médias dos valores de ISQ foram significativamente maiores após o período de osseointegração (79,36) do que no momento da instalação do implante (68,29). Os resultados demonstraram que a qualidade óssea influencia nos valores de estabilidade primária e secundária, havendo correlação moderada entre os três métodos de avaliação da estabilidade.

Made available in DSpace on 2014-12-03T01:01:44Z (GMT). No. of bitstreams: 1 000463068-Texto+Completo-0.pdf: 2847170 bytes, checksum: 24881d931a22a088ffe1f361a64aed3c (MD5) Previous issue date: 2014 / The aim of this study was to make a comparative analysis of aspects related to the osseointegration of titanium implants placed with and without local application of a bisphosphonate, after 4 weeks, in vivo. The study comprised the placement of 50 cp. titanium implants in the middle third of the tibia of 10 rabbits, with the right tibia being used as control, and the left as test site. In the test group, local administration of sodium alendronate gel was instituted, and in the control group, sterile saline solution was used. After euthanasia, 10 implants from each group were analyzed for maximum removal torque. The remainder of the sample was processed to obtain non decalcified slides with approximately 30μm thick, in which histomorphological and histomorphometric analyses of bone-implant contact (%BIC) were performed. Data were analyzed at a level of significance of 5%. The removal torque of the test group, on an average, were half of the values obtained in the control group. The test group showed lower percentage of BIC, and notable changes in bone quality. It was concluded that the initial events of osseointegration of titanium implants are not favored by the local application of sodium alendronate gel in rabbits. / O objetivo deste estudo foi analisar, comparativamente, aspectos relacionados à osseointegração de implantes de titânio, instalados com e sem a aplicação tópica de um bisfosfonato, após 04 semanas in vivo. O estudo compreendeu a colocação de 50 implantes de titânio cp. no terço médio da tíbia de 10 coelhos, sendo a tíbia direita usada como controle e a esquerda como teste. No grupo teste procedeu-se a administração local de gel de alendronato de sódio e no grupo controle foi utilizada solução salina estéril. Após a eutanásia, 10 implantes de cada grupo foram destinados à análise de torque máximo de remoção. O restante da amostra foi processada para obtenção de lâminas não descalcificadas de aproximadamente 30μm de espessura, onde foram realizadas análises histomorfológica e histomorfométrica de contato ossoimplante (%BIC). Os dados foram analisados com nível de significância de 5%. Os valores de torque máximo de remoção do grupo teste foram, em média, metade dos valores do grupo controle. O grupo teste demonstrou menor %BIC, bem como alterações notáveis em qualidade óssea. Conclui-se que os eventos iniciais de osseointegração de implantes de titânio não são favorecidos pela aplicação local de gel de alendronato de sódio em coelhos.

Made available in DSpace on 2011-12-27T14:14:20Z (GMT). No. of bitstreams: 2 000390167-0.pdf: 8479233 bytes, checksum: 78f267d7711851d94f32594d0a86c23d (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The aim of this study was to evaluate the fit between the components UCLA and implant of the same system (Neodent). The comparison was made through an evaluation of the vertical and horizontal gaps present at the interface between implant and UCLA, through scanning electronic microscopy (SEM), measurements in selected locations. Statistical analysis was done through variance analysis procedure (Anova-Oneway) and Tukey´s posterior procedure, with a significance level of 5%. The results pointed the UCLA components present significant differences in many evaluated aspects. Such differences might have some influence in the use of these components, both in clinical results and in its predictability. / O objetivo deste estudo foi avaliar a precisão de adaptação entre componentes UCLA e implante de um mesmo sistema (Neodent). A análise foi através da avaliação da fenda vertical e da discrepância horizontal da interface implante-UCLA por microscopia eletrônica de varredura (MEV), das mensurações em locais indicados. Para a comparação dos resultados, foi utilizado o procedimento de análise de variância (Anova-Oneway) e o procedimento posterior de Tukey, ao nível de significância de 5%. Os resultados mostraram que os componentes UCLA avaliados possuem diferenças significantes em diversos pontos avaliados. Essa variabilidade nos resultados podem interferir na eficácia de uso desses componentes, nos resultados clínicos e na sua previsibilidade.

Made available in DSpace on 2015-04-30T14:06:27Z (GMT). No. of bitstreams: 1 000467680-Texto+Completo-0.pdf: 13016515 bytes, checksum: e3ef505603c7d5be9a1581e535fd60e2 (MD5) Previous issue date: 2014 / The aim of this study was to evaluate the influence of the number of implants and the distal tilting of posterior implants (27 degrees) on the resulting tensions in periimplant bone, abutment screw and prosthetic screw of mandibular full-arch fixed implant supported prosthesis, using a nonlinear finite element analysis. Six virtual models were created, simulating a mandibular full-arch prosthesis with a metallic framework: models with five parallel implants (5R) and with tilted posterior implants (5I); models with four parallel implants (4R) and tilted posterior ones (4I); and models with three parallel implants (3R) and with tilted posterior implants (3I). The Von Mises tensions were analyzed, on a qualitative aspect, on the three regions of interest. The results showed that tilting the posterior implants resulted in higher tensions on the periimplant bone region. Also, the implant placed adjacent to the loading area presented the higher stress magnitudes on the three regions of interest, during all the simulations. Within the limitations of this study, it's possible to conclude that tilting the posterior implants without distalizing the implants platforms, can represent higher Von Mises tensions on the cortical periimplant bone. Still, that the use of three implants supporting a mandibular full-arch prosthesis generated higher stress values on the analyzed regions, when compared to the models simulating four and five implants. / O objetivo do presente trabalho foi avaliar em reabilitações totais fixas implantossuportadas, através de uma Metodologia de Elementos Finitos não linear, a influência do número e da inclinação dos implantes posteriores em 27 graus para distal nas tensões em osso periimplantar cortical, parafuso do pilar protético e parafuso protético. Seis modelos virtuais foram gerados simulando uma prótese total fixa mandibular, com infraestrutura metálica: modelos com 5 implantes, paralelos entre si (5R) e com dois posteriores inclinados (5I); modelos com 4 implantes, paralelos entre si (4R) e com dois posteriores inclinados (4I); modelos com 3 implantes, paralelos entre si (3R) e com dois posteriores inclinados (3I). Uma força de 100 N foi simulada em região de primeiro molar, no cantilever protético. As tensões Von Mises resultantes foram analisadas de forma qualitativa nas três regiões de interesse. Os resultados mostraram que a utilização de implantes posteriores inclinados resultaram em maiores tensões na região periimplantar. Ainda, que o implante adjacente à carga apresentou os maiores valores de tensão nas três regiões avaliadas em todas as simulações. Dentro das limitações deste trabalho, pode-se concluir que a inclinação de implantes posteriores, sem a distalização das plataformas dos mesmos, mostra-se desfavorável no que diz respeito à incidência de tensões no osso periimplantar cortical. Além disso, a utilização de três implantes suportando uma prótese total fixa mandibular, apresentou maiores valores de tensão se comparado as situações com quatro e cinco implantes.

Made available in DSpace on 2015-05-22T12:38:48Z (GMT). No. of bitstreams: 1 000468625-Texto+Completo-0.pdf: 2863238 bytes, checksum: 3e057c78a6b6e5cfbd0cf6767d59dd26 (MD5) Previous issue date: 2014 / The clinical success of the implant treatment is strongly related with the achievement and maintenance of the stability of the fixture. As the surface topography, roughness and wettability are modifications that can affect the quality of the osseointegration, several studies have analyzed the benefits of these modifications. The histomorphometric analyses of the bone-to-implant contact (BIC) and the resonance frequency analyses (RFA) are commonly used to verify the osseointegration and implant stability.In the present study, 32 implants with two different surfaces treatment were installed in the tibia of 16 New Zealand rabbits and splitted in two groups. The Group I was formed by Neodent Drive implants, with sandblasted, acid etched and hydrophilic surface (Neodent Drive Acqua, Neodent, Curitiba, Brasil). The Group II was formed by Neodent Drive implants, with sandblasted and acid etched surface (Neodent Drive Porous, Neodent, Curitiba, Brasil). The samples were analyzed at 07, 14, 30 and 60 days after the implant placement.The results showed statistically significant differences between the mean values for the BIC at 14 (p=0. 028) and 30 days (p=0. 028). The mean BIC for the Acqua implants (Group I) were 43,32 ± 1,31% and 55,03 ± 5,14%, at 14 and 30 days respectively. The mean BIC in the Porous implants (Group II) were 46,27 ± 0,10% and 47,13 ± 0,67%, at 14 and 30 days, respectively. At 60 days, the mean BIC for the Acqua implants were 54,68 ± 3,51% and for the Porous implants were 50,86 ± 1,03%.There were not statistically significant differences in the implant stability quotient (ISQ) measurements between Acqua and Porous implants, except at 07 days after the implant placement. At day 07, the results of the present study showed higher ISQ values for the Porous implants (68,75 ± 4,16%) than Acqua implants (61,5 ± 8,01%). The follow-up ISQ analyses in the same Group, showed statistically significant increases of the mean values from 7 to 60 days and from 30 to 60 days, for both groups.In conclusion, the sandblasted and acid etched treatment used to create roughness on the Neodent implant surface is reliable and allows bone apposition, as the BIC and ISQ values found were similar or superior than the showed in the literature for similar animal models and similar implant surface. The increase of the BIC and ISQ values on the follow up showed the achievement of the secondary stability and the increase in stiffness between the implant fixture and the surrounding tissues. There were not identified better results with the hydrophilic surface during the early period of healing. Thus, further investigations are necessary to confirm the suggested results in this present study. / A obtenção e a manutenção da estabilidade do implante são pré-requisitos para o sucesso clínico das próteses sobre implantes. Visto que a topografia, a rugosidade e a hidrofilicidade são algumas das alterações da superfície dos implante que podem alterar a resposta do tecido ósseo, diversos estudos tem procurado entender os benefícios que estas modificações podem proporcionar. A quantificação histomorfométrica do contato osso-implante (BIC) e a análise de frequência de ressonância (AFR) são parâmetros frequentemente utilizados na implantodontia para verificar a osseointegração e a estabilidade dos implantes.No presente estudo, foram instalados 32 implantes com duas diferentes superfícies nas tíbias de 16 coelhos, divididos em dois grupos: Grupo I) constituído pelos implantes com superfície tratada por jateamento de areia, ataque ácido, hidrofílica e modificada quimicamente (Neodent Drive Acqua, Neodent, Curitiba, Brasil) e Grupo II) constituído pelos implantes com superfície tratada por jateamento de areia e ataque ácido (Neodent Drive Porous, Neodent, Curitiba, Brasil). As amostras foram analisadas após 7, 14, 30 e 60 dias da colocação dos implantes.Na comparação da média geral do BIC, entre Acqua e Porous, foram observadas diferenças estatisticamente significantes no período de 14 dias (p=0,028) e no período de 30 dias (p=0,028). As medidas médias de BIC obtidas para os implantes Acqua foram 43,32 ± 1,31% e 55,03 ± 5,14%, aos 14 e 30 dias respectivamente. Para os implantes Porous, as medidas de BIC foram 46,27 ± 0,10% e 47,13 ± 0,67%, aos 14 e 30 dias respectivamente. No período de 60 dias, os valores médios de BIC da superfície Acqua foram 54,68 ± 3,51% e da superfície Porous foram 50,86 ± 1,03%.Na comparação da média geral do quociente de estabilidade do implante (QEI), entre Acqua e Porous, não foram observadas diferenças estatisticamente significantes entre os grupos, com exceção no período de 07 dias, no qual os resultados do presente estudo demonstraram maiores valores de QEI para o grupo Porous (68,75 ± 4,16%) do que para o grupo Acqua (61,5 ± 8,01%). A análise do QEI durante os diferentes períodos dentro de um mesmo grupo, demonstrou diferenças estatisticamente significativas entre os períodos de 7 vs 60 dias e 30 vs 60 dias, para a média geral do QEI no grupo Acqua e no grupo dos implantes Porous.As conclusões do presente estudo são que os resultados demonstraram que a modificação da superfície por jateamento de areia e ataque ácido utilizada para produzir as superfícies Acqua e Porous resulta em uma adequada aposição óssea, visto que os valores do BIC e QEI encontrados são similares ou superiores aos resultados encontrados na literatura com modelos experimentais e superfícies similares. Os aumentos dos valores do BIC e QEI durante os períodos pós-operatórios revelaram a obtenção de estabilidade secundária e maior rigidez na ancoragem do implante com o passar do tempo. Não foram identificados melhores resultados com a superfície hidrofílica nos períodos iniciais da osseointegração. Sendo assim, são necessários estudos pré-clínicos e clínicos para confirmar as sugestões que os resultados deste presente estudo revelaram.

Made available in DSpace on 2011-12-27T14:14:05Z (GMT). No. of bitstreams: 2 000422228-0.pdf: 2027786 bytes, checksum: fc45ed715786efb01f83f7fff755ceef (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Nowadays, the focus of many researches in Implant Dentistry is on the modification of the titanium surface in search of alternatives that can provide more quickness and quality to the osseointegration process. Osseointegration is a phenomenon that happens mainly through the interfacial response of bone cells in contact with the titanium surface. There are different treatment methods that can be used to modify the topographic and chemical properties of the titanium surface in order to optimize the tissue-implant reactions. In this study, we evaluated the influence of different titanium surface treatments in the adhesion and proliferation of human osteoblasts by quantitatively analyzing the number of adherent cells in different cell culture periods. Forty level II titanium disks with 15mm diameter and 1mm thickness were divided into four groups according to their surface characterization: G1. machined; G2. acid-etched; G3. with hydroxyapatite coating; and G4. with bisphosphonate immobilized on hydroxyapatite coating. Osteoblast cells derived from human osteosarcoma (SaOS-2) were cultured on the disks and the cell counting was made in 3, 7 and 14 days. To determine the number of cells, a coloring process of the nucleus using propide iodide was carried out and disks were then analyzed in an optical microscope under ultraviolet light. The cell counting in the different experimental groups and culture periods was compared using ANOVA complemented by Tukey’s test. Results of the statistical analysis made it possible to conclude that: (1) the titanium surface and the cell culture period, as well as the interaction of both, significantly affect the cell growth; (2) modifying the titanium surface by acid-etching favors the adhesion and proliferation of human osteoblasts, in vitro. Further researches are necessary to elucidate the immobilized bisphosphonate influence on the titanium surface at the initial osteogenesis events. / Atualmente, o foco de muitas pesquisas científicas em Implantodontia está voltado para a modificação da superfície do titânio na busca de alternativas que proporcionem maior rapidez e qualidade no processo de osseointegração. A osseointegração é um fenômeno que acontece fundamentalmente através da resposta interfacial das células ósseas em contato com a superfície do titânio. Diferentes métodos de tratamento podem ser utilizados para modificar as propriedades topográficas e químicas da superfície do titânio a fim de otimizar as reações tecido-implante. Neste estudo foi avaliada a influência de diferentes tratamentos de superfície do titânio na adesão e proliferação de osteoblastos humanos, através da análise quantitativa do número de células aderidas em diferentes períodos de cultura celular. Para isso, 40 discos de titânio grau II, comercialmente puro, de 15mm de diâmetro e 1mm de espessura, foram divididos em quatro grupos conforme a caracterização de sua superfície: G1. maquinada; G2. ácido-condicionada; G3. com cobertura de hidroxiapatita; e G4. com bisfosfonato imobilizado na cobertura de hidroxiapatita. Células osteoblásticas derivadas de osteossarcoma humano (SaOS-2) foram cultivadas sobre os discos e a contagem celular foi realizada em 3, 7 e 14 dias. Para determinação do número de células, um processo de coloração dos núcleos com Iodeto de Propídio foi realizado, e os discos foram analisados em microscópio óptico sob luz ultravioleta. As contagens celulares nos diferentes grupos experimentais e períodos de cultura foram comparadas por meio de ANOVA, complementado pelo teste de Tukey. Os resultados da análise estatística permitem concluir que: (1) a superfície do titânio e o período de cultura celular, bem como a interação de ambos, significativamente afetam o crescimento celular; (2) a modificação na superfície do titânio através de condicionamento ácido favorece, in vitro, a adesão e proliferação de osteoblastos humanos. Mais pesquisas são necessárias para elucidar a influência do bisfosfonato imobilizado na superfície do titânio nos eventos iniciais da osteogênese.

Made available in DSpace on 2011-12-27T14:14:07Z (GMT). No. of bitstreams: 2 000417615-0.pdf: 921449 bytes, checksum: b1758518b6fea65cac8a47bf9564b908 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The possibilities of changing implant surface properties are numerous, both in terms of chemical and biological aspects and also of surface morphology and topography. Recent studies have focused on establishing an implant surface with characteristics that optimize osseointegration in sites with low bone density. The aim of the present study was to carry out clinical and histological assessments of the influence of different implant surfaces on the response of peri-implant tissues with low bone density. Eight male New Zealand rabbits were used in the study. The following implant surfaces were assessed: cast titanium (G1), acid-etched titanium (G2), titanium coated with titanium plasma spray (G3), and titanium coated with new acidetched porous titanium coating (G4).Animals were sacrificed 30 days after surgery. Following clinical assessment of implant stability in the alveolar bone, tibia bone fragments containing the implants were prepared and submitted to histological analysis. Clinical assessment results showed that all implants achieved stability in peri-implant tissues. In some specimens, new bone formation was observed, as well as tissue migration to the coronal, non-submerged area of the implant. Our findings suggest that the implant surface G3 was the one that most contributed to bone regeneration, with minimum foreign body reaction observed in peri-implant tissues. / As possibilidades de modificação das propriedades de superfície dos implantes são muito grandes, tanto com relação aos aspectos químico e biológico quanto aos morfológico e topográfico. Pesquisas recentes têm-se dedicado a buscar uma superfície que otimize o processo de osseointegração em regiões com baixa densidade óssea. Assim, o objetivo deste estudo foi avaliar a influência de diferentes superfícies implantares sobre a resposta tecidual em regiões com baixa densidade óssea. Foram utilizados para este estudo 8 coelhos machos da raça Nova Zelândia. Em cada animal foram inseridos, cirurgicamente, 4 implantes cilíndricos, sendo na tíbia direita as amostras dos grupos G1 (superfície usinada) e G2 (tratamento com ataque ácido de rotina) e na tíbia esquerda as amostras dos grupos G3 (superfície com camada porosa de titânio) e G4 (superfície com camada porosa de titânio mais tratamento com ataque ácido inovador) O experimento foi repetido, de forma idêntica, em todos os animais. Durante todo o período de observação (30 dias), os animais permaneceram saudáveis, com cicatrização normal na região operada, sem evidência de infecção ou deiscência de sutura. Todos os implantes obtiveram estabilidade ao tecido perimplantar, mesmo após o processo de descalcificação óssea. Em alguns grupos da amostra a neoformação óssea cobriu a porção coronal não submersa dos implantes. Os resultados da análise histológica evidenciaram que a interface óssea com os implantes dos grupos G1 e G2 foi caracteristicamente linear e regular e com G3 e G4 mais irregular. De modo geral, os implantes do grupo G3 melhor contribuíram para a dinâmica do reparo ósseo.

Made available in DSpace on 2011-12-27T14:14:33Z (GMT). No. of bitstreams: 2 000422969-0.pdf: 4980923 bytes, checksum: 2690ee5096ce9b097a8aa97b37d89ecf (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Studies have showed that roughness surfaces in titanium implants can modulate bones responses. The objective of present study is evaluate the bone implant contact between two types of dentistry implants with differents treatments of surface, Titamax EX Cone Morse® sandblasted/acid-etched and a Titamax EX Cone Morse® with a new proposal surface called nanosurface, in a sheep model, during 30 and 60 days. Two female sheeps received 10 implants each (n=20), five sandblasted/acid etched implants and five with the new surface implant. Implants were inserted in tibia an ulna. After the euthanization, in 30 and 60 days, the specimens were processed and a scanning electron microscopy was used to evaluate the bone contact implant of these two types of dentistry implants in a different time. The software Image J Plus® was used to determine the bone contact implants and SPSS® for statistical analyses. The histomorphology showed bone formation between implants crests in both groups, in 30 days. However, there was a lose in bone contact implant in the nanosurface group, in 60 days. The sandblasted/etched group mantained its measures. These differences were statistically significant. More studies are necessary to improve this new kind of surface a long time to become accceptable to clinical use and bennefit the patients / O objetivo desta pesquisa foi avaliar a ultraestrutura da superfície do implante através da microscopia eletrônica de varredura e a resposta histológica da interface osso-implante através da histomorfometria da osseointegração de duas superfícies de implantes (Titamax EX Cone Morse® jateado + ataque ácido e Titamax EX Cone Morse® desenvolvida com uma nova proposta de tratamento de superfície, ainda não comercializada, intitulada nanosuperfície) em modelo animal, avaliados após um período de 30 e 60 dias. Foram utilizadas duas ovelhas adultas da espécie Ovis aries. As ovelhas foram divididas em dois grupos: uma ovelha pertencente ao grupo 1, com morte prevista após 30 dias da instalação dos implantes e uma ovelha pertencente ao grupo 2, com morte após 60 dias. Cada animal forneceu 10 amostras, sendo 05 amostras compostas por implantes dentários com superfície tratada com jato + ataque ácido e 05 amostras compostas por implantes dentários com superfície tratada com nanopartículas. As amostras foram processadas e avaliadas em microscópio eletrônico de varredura em diferentes magnitudes para avaliar os resultados do contato entre o osso e a superfície dos implantes nos períodos propostos. O programa Image J Plus® foi usado para a avaliação desse contato e o SPSS® para a análise estatística. A histomorfometria mostrou a formação óssea sobre a superfície dos implantes em ambas as amostras no grupo 1, ou seja, no período de 30 dias. Entretanto, apesar da formação óssea também ocorrer sobre a superfície dos implantes em ambas as amostras do grupo 2, ou seja, no período de 60 dias, observou-se uma perda do contato osso-implante na amostra de nanosuperficie ao longo do período da pesquisa. Para se tornar mais aceitável o uso clínico em benefício aos pacientes dos implantes Titamax EX Cone Morse® nanosuperficie, outros estudos se fazem necessários para sugerir melhorias no tratamento de superfície dos implantes e para avaliação por períodos maiores de tempo.

Made available in DSpace on 2011-12-27T14:14:37Z (GMT). No. of bitstreams: 2 000417773-0.pdf: 1138982 bytes, checksum: 03423e2cddaa5a43349be69c0853e615 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / Given that the majority of osseointegrated implants undergo some type of surface conditioning in order to improve osseoitegration and that in vitro differentiation of mesenchymal cells into osteoblasts is a mastered process that has been used for evaluating a given biomaterial with regard to its osteinductive and osteoconductive capabilities, the present work aims to evaluate the adhesion, proliferation and differentiation of human bone marrow cells on titanium implant surfaces that have or have not been treated by discrete calcium phosphate deposition. Human bone marrow cells obtained from a single donor were cultured in media containing 12 titanium discs of one of the following: the Bonelike® (Biomet 3I, Brazil) with a surface treated by double acid etching; the Osseotite™ (Biomet 3I, USA) with similar surface treatment and the Nanotite™(Biomet 3I, USA). After 14 and 21 days of culture, real time PCR and SEM examinations were performed. From the results we concluded that implant surface roughness allows cell adhesion, differentiation and proliferation, the ALP synthesis is higher in Bonelike® and the presence of calcium phosphate nanoparticles on an implant surface leads to enhanced BGLAP synthesis and cell proliferation. / Os implantes osseointegrados, em sua maioria, possuem algum tipo de condicionamento da sua superfície que visa melhorar a osseointegração. O mecanismo de diferenciação celular in vitro de células mesenquimais em osteoblastos já é bastante conhecido e serve para avaliação das propriedades de osteoindução e osteocondução de biomateriais. O presente estudo tem por objetivo avaliar a adesão, proliferação e diferenciação das células da medula óssea humana em superfícies de implantes de titânio com e sem deposição discreta de fosfato de cálcio. As células foram obtidas a partir da medula óssea de um doador humano. Foram selecionados 12 discos de titânio do tipo Bonelike® (Biomet 3I, Brasil) com superfície tratada por duplo ataque ácido; Osseotite™ (Biomet 3I, USA) com superfície tratada por duplo ataque ácido e Nanotite™ (Biomet 3I, USA). Após 14 e 21 dias de cultura foi realizado PCR em tempo real para avaliação da diferenciação celular e microscopia eletrônica de varredura para avaliação da proliferação e adesão celular aos discos de titânio. Os resultados indicaram que a rugosidade da superfície dos discos de titânio possibilita a adesão, diferenciação e proliferação celular, que a síntese de ALP é maior na superfície Bonelike e que as partículas de fosfato de cálcio demonstraram maior grau de síntese de BGLAP e proliferação celular.