Made available in DSpace on 2014-06-12T17:39:53Z (GMT). No. of bitstreams: 2 arquivo7542_1.pdf: 2911934 bytes, checksum: 78998b306d462867774180e86413cfd6 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2007 / Instituto Federal de Educação, Ciência e Tecnologia de Pernambuco / A liga de alumínio utilizada nesse estudo foi catalogada pela Aluminium Association como AA 8023, pertence ao sistema Al-Fe-Mn e possui como principal característica uma elevada resistência associada a uma boa formabilidade, sendo utilizada em aletas de radiadores automotivos e embalagens de alta resistência. Nesse contexto, o estudo da cinética de recristalização assume um papel relevante por possibilitar o controle do estado encruado em função do tempo de tratamento. O objetivo desse trabalho é determinar as cinéticas de recristalização para cada propriedade (tensão de escoamento e alongamento) para melhor entendimento da fenomenologia formabilidade א resistência. Inicialmente foram realizadas análises térmicas diferenciais - ATD para identificação dos domínios de transformação de fase da liga encruada. Em seguida diferentes amostras foram recozidas isotermicamente nas temperaturas de 310°C (pico da curva ATD), 295°C e 325°C em tempos que variaram de 5 min a 120 min. As amostras tratadas foram submetidas a ensaio de tração uniaxial, segundo a norma ASTM-E8M-89B, para levantamento das curvas propriedade versus tempo. Os valores das propriedades mecânicas (tensão de escoamento e alongamento) foram relacionados biunivocamente aos da fração transformada para determinação da cinética de recristalização. Para melhor compreensão da formabilidade א resistência, propriedades conflitantes, também foi feito um estudo do potencial de encruamento onde foram realizados ensaios de tração para determinação da tensão de escoamento para espessuras que variaram de 1,0 mm a 4,0 mm, laminadas até 80%, a uma taxa de deformação de 1,8 s-1 para produzir chapas com espessuras até 1,0mm (80%). Para análise microestrutural foi utilizada microscopia eletrônica de varredura MEV onde os efeitos da recristalização foram observados a partir das fraturas em corpos de prova submetidos a diferentes condições de tratamentos térmicos (recozimento). Os resultados mostraram que a cinética de recristalização descrita utilizando equações, obtidas indiretamente a partir das propriedades mecânicas consideradas, aproximam-se do comportamento sigmoidal proposto por Johnson-Mehl-Avrami

Dissertação (Mestrado em Engenharia Mecânica) - Centro Universitário FEI, 2015

Orientador: Tomaz Manabu Hashimoto / Banca: Marcelo dos Santos Pereira / Banca: Pedro Paulo de Campos / Resumo: A obtenção de microestrutura constituída de ferrita acicular em aços micro-ligados é promissora por apresentar boa combinação de propriedades mecânicas, especialmente pela melhoria da tenacidade, graças a morfologia fina e entrelaçada que dificulta a propagação de trinca. Embora as propriedades mecânicas sejam adequadas para aplicações estruturais, o uso desta microestrutura tem sido um tanto limitado. Sob ponto de vista de mecanismo de nucleação, a causa desta limitação reside na dificuldade de obtenção de ferrita acicular a partir de aços forjados por apresentarem baixa densidade de inclusões não metálicas como óxidos, sulfetos e nitretos que servem como sítios de nucleação intragranular. A proposta deste trabalho é estudar os efeitos das condições de processamentos como temperatura de austenitização e temperatura de transformação isotérmica na formação de grandes frações de ferrita acicular e correlação com as propriedades mecânicas. Os resultados mostraram que é possível obter estruturas multifásicas com grandes frações de ferrita acicular, com excelentes combinações de resistência e ductilidade. / Abstract: Obtaining acicular ferrite structure of low carbon steels is promising because a good mechanical properties combination. The toughness improvement is due the interlaced morphology of the acicular ferrite that promote crack propagation interruption. Although the mechanical are suitable to structural applications, the use of this microstrocture has been limited in view of complicated mechanism of acicular ferrite nucleation. The formation of acicular ferrite in low carbon wrougth steels is limited in view of low density of nonmetallic inclusions those serve as preferential sites of intragrunular nucleation. The purpose of this work is a study of processing conditions effects like austenitizing temperature and isothermal transformation an acicular ferrite formation. The results shown that it's possible to obtain multiphase structures with great fraction of acicular ferrite as well as excellent strength-ductility combination. KEYWORD: Low carbon steels, acicular ferrite, mechanical properties. / Mestre

O processo de solda por fricção (FSW) é um dos processos inovadores que está sendo apresentado e estudado, na comunidade cientifica e empresas, por propiciar uma união de excelente qualidade. No entanto existem questões ainda a serem resolvidas principalmente nas soldas de materiais dissimilares como é o caso das ligas de cobre e alumínio. O objetivo deste trabalho é produzir uniões da liga de Cobre e Alumínio, pois esses materiais são qualificados como de difícil soldabilidade pelos sistemas convencionais restringindo assim sua aplicação. Este trabalho avaliou a soldagem de juntas sobrepostas de uma liga de alumínio (ASTM 6060 T5) e a liga de cobre (ASTM-B-187, C 110- têmpera meio dura) em que o cobre é posicionado acima do alumínio. As juntas foram soldadas pelo processo de soldagem por fricção e mistura mecânica (FSW) com quatro velocidades de rotação (800, 900, 1000, e 1100 rpm), com a velocidade de avanço mantida em 10 mm/min. foi também avaliada a influência de um avanço contrário ao inicial (ACI) de 2 mm no início da solda. As juntas produzidas foram avaliadas através de ensaios de cisalhamento, fadiga, microestrutura, ultrassom e resistividade elétrica. Não foi observada influência significativa dos parâmetros de processo sobre a resistência mecânica. No entanto, a soldagem com ACI de 1000 rpm foram os parâmetros que apresentaram os melhores resultados e menor dispersão entre as condições avaliadas. A resistência elétrica das juntas soldadas em todas as condições se mostrou muito próxima da média entre as resistências das ligas utilizadas, indicando a viabilidade da aplicação desse processo em conexões elétricas. Em relação à fadiga, ficou evidenciado um aumento em torno de 30% na vida das juntas soldadas com ACI. Os ensaios de ultrassom não mostraram descontinuidades que comprometessem a aplicação de nenhuma das juntas soldadas. / The friction welding process (FSW) is one of the innovative processes being presented and studied, in the scientific community and companies, for providing a union of excellent quality. However, there are still issues to be solved mainly in soldering of dissimilar materials such as copper and aluminum alloys. The objective of this work is to produce copper and aluminum alloy joints, since these materials are classified as difficult solderability by conventional systems, thus restricting their application. This work evaluated the welding of overlapping joints of an aluminum alloy (ASTM 6060 T5) and the copper alloy (ASTM-B-187, C 110-hardened quench) in which the copper is positioned above the aluminum. The joints were welded by the friction welding and mechanical mixing (FSW) process with four rotational speeds (800, 900, 1000, and 1100 rpm), with the feed rate maintained at 10 mm / min. The influence of a non-initial advance (ACI) of 2 mm at the beginning of the weld was evaluated. The joints produced were evaluated through shear, fatigue, microstructure, ultrasonic and electrical resistivity tests. No significant influence of process parameters on mechanical strength was observed. However, the welding with (ACI) of 1000 rpm were the parameters that presented the best results and lower dispersion among the evaluated conditions. The electrical resistance of the welded joints in all conditions was very close to the average between the resistances of the alloys used, indicating the feasibility of the application of this process in electrical connections. In relation to fatigue, an increase of around 30% in the life of welded joints with (ACI) was evidenced. Ultrasound tests showed no discontinuities that would compromise the application of any of the welded joints.

Resumo: Os compósitos poliméricos avançados têm sido utilizados como materiais estruturais de elevado desempenho em aplicações aeroespaciais nos últimos 40 anos. No entanto, esses materiais podem apresentar problemas quando expostos à umidade, temperatura, radiação ultravioleta e variação térmica, podendo ocorrer sinergia entre os principais mecanismos de degradação. Entre os compósitos termoplásticos, o laminado processado a partir de fibras de carbono/PEKK (poli(éter-cetona-cetona)) mostra excelente balanço de propriedades, incluindo elevada temperatura de transição vítrea, elevados valores de resistência, rigidez e tenacidade à fratura, baixa absorção de umidade e boa resistência ambiental. O objetivo do presente trabalho é avaliar a influência dos parâmetros de processamento na obtenção do compósito de fibra de carbono/PEKK, via moldagem por compressão a quente, assim como, estudar a influência de diferentes condicionamentos ambientais, como efeito higrotérmico, radiação ultravioleta (UV) e ciclagem térmica nos comportamentos viscoelástico e mecânico do compósito. Neste trabalho, os efeitos da degradação ambiental sobre as propriedades mecânicas e viscoelásticas foram avaliadas por meio de ensaios de compressão, de cisalhamento interlaminar, DMA e vibração livre. O processamento dos compósitos por moldagem por compressão a quente mostrou-se adequado necessitando, porém, da otimização de alguns parâmetros. As análises viscoelásticas das amostras submetidas ao condicionamento por radiação UV mostram que as temperaturas de transição vítrea das amostras não condicionadas e condicionadas encontram-se relativamente próximas (~157°C a 162°C), mas o módulo de armazenamento apresenta uma acentuada degradação, evidenciando o efeito deletério da radiação UV na rigidez do compósito estudado / Abstract: Advanced polymeric composites have been introduced as structural materials for high performance aerospace applications over the last 40 years. However, these materials can present problems when exposed to moisture, temperature, ultraviolet (UV) radiation and thermal cycling, besides it may occur the synergy among the main degradation mechanisms. Among the thermoplastic composite materials, carbon fiber reinforced PEKK (poly(etherketone- ketone)) laminates have shown excellent balance of properties, including high glass transition temperature, high strength, stiffness and fracture toughness values, low moisture absorption and good environmental resistance. The aim of the present work is to evaluate the influence of the processing parameters on the carbon fiber/PEKK composites manufacturing, by hot compression molding, and also the influence of different environmental conditionings as hygrothermal, ultraviolet (UV) radiation and thermal cycling effects on viscoelastic and mechanical behaviors. In this work, the effects of environmental degradation on mechanical and viscoelastic properties were studied by compression, interlaminar shear strengths, DMA and free vibration tests. Hot compression molding showed good to produce the thermoplastic composite, but it need be optimised. The viscoelastic tests of the samples submitted to the UV radiation effects show the glass transition temperatures of non-conditioning and conditioning specimens are near (~157°C to 162°C) when compared between then. On the other hand, the storage modulus presents a significant degradation emphasising the deleterious effect of the UV conditioning on the studied composite stiffness / Orientador: Edson Cocchieri Botelho / Coorientador: Mirabel Cerqueira Rezende / Banca: Michelle Leali Costa / Banca: Lília Muleer Guerrini / Banca: Evandro Luis Nohara / Banca: José Fernandes Maria Marlet / Doutor

Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2014. / Made available in DSpace on 2015-02-05T20:22:02Z (GMT). No. of bitstreams: 1 332260.pdf: 4118348 bytes, checksum: 828e7cdf48de5ec37861ecba66999ec9 (MD5) Previous issue date: 2014 / Como o concreto projetado é normalmente carregado durante as primeiras horas da hidratação, sem nenhum processo de cura úmida para evitar a retração. A fissuração nesta fase pode ser um sério problema, comprometendo o comportamento da estrutura em curto e longo-prazo.O objetivo desta tese é auxiliar na compreensão desta problemática explorando o uso das fibras. Desta forma, são investigadas experimentalmente as propriedades mecânicas durante o processo de hidratação de concretos projetados, reforçados com fibras polipropileno e aço, tipicamente utilizados em túneis, com vistas a prevenir a possibilidade de fissuração. Os dados experimentais também alimentaram um modelo empírico de um elemento teórico, espesso e restringido, de concreto projetado, durante o período mais intenso da hidratação.A pesquisa experimental forneceu dados de velocidade de pulso ultrassônico, teor de umidade, resistência à compressão e tração, módulo de elasticidade, temperatura, retração e fluência, bem como alguns parâmetros na pós-fissuração dos traços reforçados com fibras, tais como abertura de fissura e tensão reduzida de tração; desde o tempo de lançamento do concreto até a idade de 28 dias.Os concretos reforçados com fibras tiveram melhor desempenho na fase plástica e na fase pós-fissurada do material. Apresentaram menor retração e perda de água na fase plástica, bem como reduziram a abertura de fissuras na fase pós-fissurada, demonstrando que as fibras são eficazes nestas fases. O concreto reforçado com fibra de polipropileno apresentou desempenho ligeiramente superior nestas fases se comparada ao concreto com fibra de aço.O modelo empírico denominado PEAC- Prediction of Early Age Cracking foi desenvolvido para prever a idade de fissuração do elemento teórico, durante o período de tempo, desde a pega até que o calor de hidratação retorne à temperatura ambiente.Baseando-se em PEAC, os concretos projetados não fissuraram por temperatura, retração e fluência, considerando a pega final como o tempo zero para retração. Se considerarmos o tempo de pega inicial como tempo zero, o concreto sem fibras, de controle, fissurou durante as primeiras 72 horas desde o lançamento do material.<br> / Abstract : As shotcrete is normally loaded during hydration, without any wet curing process to prevent shrinkage, cracking at this stage can be a serious problem affecting the short and long-term performance of the structure.The aim of this thesis is to contribute to better understand of such problem by exploring the potential of fibers. In this way, it was experimentaly investigated the mechanical properties during the hidration process, of shotcretes reinforced with polypropilene and steel fibers, typically used in tunnels; toward the prevention of the possibility of cracking. The experimental data, also fed an empirical model of a thick and restrained, theoretical element made in shotcrete, during the most intense phase of hydration.The experimental work provided data on ultrassonic pulse velocity, moisture content, compressive and tensile strength, modulus of elasticity, temperature, shrinkage and creep, as well as some post-cracking parameters such as crack opening and the reduced tensile stresses of the fiber reinforced mixes; from the time of casting until the 28 days of age.The concretes reinforced with fibers performed better in the plastic and post- cracked phases of the material. They showed lower water loss and shrinkage in the plastic phase, as well as they reduced the crack opening in the post-cracked stage, showing that the fibers are effective in these phases. The concrete reinforced with polypropylene fiber showed slightly better performance in these phases, when compared to concrete with steel fiber.PEAC - Prediction of Early-Age Cracking model was conceived to predict the cracking time, in the theoretical element, from setting until the heat of hydration returns to room temperature.Based on PEAC the shotcrete mixes did not crack when temperature, shrinkage and creep are altogether considering the final setting time as time zero for shrinkage. However, if the initial setting time is considered as time zero, the control mix, without fiber, cracked during the heat of hydration process.

OLIVEIRA, F. J. S. Alívio de tensões residuais em junta soldada com arame de baixa temperatura de transformação martensítica. 114 f. 2015. Dissertação (Mestrado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2015. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2016-02-11T13:28:57Z No. of bitstreams: 1 2015_dis_fjsoliveira.pdf: 7683640 bytes, checksum: 246f11d2265825746ccf246cb9ce15be (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2016-03-15T18:46:31Z (GMT) No. of bitstreams: 1 2015_dis_fjsoliveira.pdf: 7683640 bytes, checksum: 246f11d2265825746ccf246cb9ce15be (MD5) / Made available in DSpace on 2016-03-15T18:46:31Z (GMT). No. of bitstreams: 1 2015_dis_fjsoliveira.pdf: 7683640 bytes, checksum: 246f11d2265825746ccf246cb9ce15be (MD5) Previous issue date: 2015-09-25 / The multi-pass welding of thick plates imposes to the welded joint a state of residual stresses that can be very harmful when they are in service. There are various phenomena that can alter the levels of residual stresses after materials welding; one of them is phase transformation. This work presents a comparative study of the levels of residual stresses in three welded joints, produced with different filler metals by Flux Cored Arc Welding (FCAW). A martensitic stainless steel wire Fe-12% Cr-5% Ni with low transformation temperature was the first to be used. After this an austenitic stainless steel Fe-18.5% Cr-10% Ni was used and finally a low alloy steel Fe -1.25% Cr-0.5% Mo. In the welding process, we used a workbench robot with multiprocess source for making joints, and the AISI 4140 the base metal.. Residual stresses were measured on the surface of welded joints using X-ray diffraction method. Tensile strength, toughness and hardness, as well as the resultant microstructure in weld metal, heat affected zone and base metal were evaluated. The results showed that the joint produced with wire electrode that has undergone low temperature martensitic transformation presents significant levels of compressive residual stress, unlike the other joints which present tensile residual stress at most of the measured points. In tensile tests, the joint of martensitic stainless steel showed high yield limits and tensile strength, and its rupture occurred at the interface between base metal and weld metal. Results of the impact tests of this joint showed relatively low absorbed energy values at the weld metal and heat affected zone. / A soldagem multipasse de chapas grossas impõe à junta soldada um estado de tensões residuais que pode ser muito prejudicial quando estas estão em serviço. Existem vários fenômenos capazes de alterar os níveis de tensões residuais de soldagem nos materiais, um deles é a transformação de fases. Este trabalho apresenta um estudo comparativo dos níveis de tensões residuais em três juntas soldadas, produzidas com metais de adição diferentes pelo processo arame tubular. Um arame eletrodo de aço inoxidável martensítico Fe-12%Cr-5%Ni com baixa temperatura de transformação foi o primeiro a ser utilizado, o segundo, um aço inoxidável austenítico Fe-18,5%Cr-10%Ni, e finalmente, um aço baixa liga Fe-1,25%Cr-0,5%Mo. No processo de soldagem foi utilizada uma bancada robotizada com fonte multiprocesso para confecção das juntas, sendo o aço ABNT 4140 o metal de base. As tensões residuais foram medidas na superfície das juntas soldadas através do método de difração de raios-X. Também foram avaliadas as seguintes propriedades mecânicas; resistência à tração, tenacidade e microdureza, bem como, as microestruturas resultantes na zona fundida, zona afetada pelo calor e metal de base. Os resultados mostraram que a junta produzida com arame eletrodo que sofreu transformação martensítica a baixa temperatura apresentou níveis consideráveis de tensão residual compressiva, ao contrário das demais juntas que apresentaram tensão residual trativa na maioria dos pontos medidos. Nos ensaios de tração, a junta de baixa temperatura de transformação martensítica apresentou elevados limites de escoamento e de resistência à tração, e a sua ruptura ocorreu na interface entre o metal de base e o metal de solda. Nos ensaios de impacto da mesma junta, os valores de energia absorvida no metal de solda e zona termicamente afetada se apresentaram relativamente baixos.

As estruturas sanduíche são formadas por duas faces externas (geralmente feitas com fibra sintética e resina) e um núcleo no meio. Estas estruturas possuem elevada rigidez em flexão, resistência ao cisalhamento e à compressão, e um peso muito baixo. São muitas vezes produzidos por moldagem líquida, como a infusão. Neste trabalho, foi utilizada resina éster‑vinílica, manta e tecido de fibra de vidro e núcleos de PET e PVC, para obter estruturas sanduíche pelo processo de RTM Light. O principal objetivo desta tese é validar a utilização desse processo para a fabricação dessas estruturas utilizando combinações dos núcleos e da manta ou tecido nas faces. Buscou‑se também estudar numericamente, utilizando o software OpenFOAM, o processo de RTM Light para estruturas sanduíches, sobre o qual há pouco estudo na literatura. A resina éster‑vinílica apresentou propriedades adequadas para utilização nestes compósitos, como viscosidade intermediária e tempo de cura apropriado para o processo de RTM Light, sendo que sua pós‑cura teve um efeito importante nas propriedades finais dos compósitos. Os dois núcleos demonstraram propriedades similares, como resistência à compressão transversal e longitudinal, mas o PVC apresentou uma resistência ao cisalhamento superior ao PET. Quanto ao tipo de reforço, também foram obtidos resultados similares, mas o tecido apresentou uma maior resistência à flexão que a manta. A simulação numérica do processo possibilitou prever o comportamento da resina dentro do molde de tal maneira a identificar padrões de preenchimento, bem como regiões mais propícias à formação de vazios. Sendo, portanto, uma ferramenta importante na construção de moldes, definição dos parâmetros de processo e na escolha das matérias‑primas. / The sandwich structures are comprised of two external faces (usually made of synthetic fiber and resin) and a core in between. These structures have high stiffness in bending, shear and compression strength, with a very low weight. They are often produced by liquid molding, such as infusion. In this work, vynil‑ester resin, glass mats and cloths and PET and PVC cores were used to obtain sandwich structures by Light RTM process. The main objective of this thesis is to validate the use of this process for the manufacture of these structures produced with a combination of cores and mats/clothes on the faces. The study was also based on a numerical study of the RTM Light process using the OpenFOAM software, for sandwiches structures, about which very little is available in the literature. The vinyl ester resin showed suitable properties for use in these composites, such as intermediate viscosity and adequate curing time for the Light RTM process, and its post‑cure had an important effect on the final properties of the composites. Both cores showed similar properties, such as resistance the transverse and longitudinal compression, but PVC showed greater shear strength than PET. The two types of reinforcement also produced similar results, but the use of cloths increased flexural strength. Numerical simulation of the process enabled prediction of the behavior of the resin inside the mold in a way to identify the filling pattern, as well as regions more prone to void formation. Thus, being an important tool for mold construction, definition of process parameters and the selection of raw materials.

O processo de solda por fricção (FSW) é um dos processos inovadores que está sendo apresentado e estudado, na comunidade cientifica e empresas, por propiciar uma união de excelente qualidade. No entanto existem questões ainda a serem resolvidas principalmente nas soldas de materiais dissimilares como é o caso das ligas de cobre e alumínio. O objetivo deste trabalho é produzir uniões da liga de Cobre e Alumínio, pois esses materiais são qualificados como de difícil soldabilidade pelos sistemas convencionais restringindo assim sua aplicação. Este trabalho avaliou a soldagem de juntas sobrepostas de uma liga de alumínio (ASTM 6060 T5) e a liga de cobre (ASTM-B-187, C 110- têmpera meio dura) em que o cobre é posicionado acima do alumínio. As juntas foram soldadas pelo processo de soldagem por fricção e mistura mecânica (FSW) com quatro velocidades de rotação (800, 900, 1000, e 1100 rpm), com a velocidade de avanço mantida em 10 mm/min. foi também avaliada a influência de um avanço contrário ao inicial (ACI) de 2 mm no início da solda. As juntas produzidas foram avaliadas através de ensaios de cisalhamento, fadiga, microestrutura, ultrassom e resistividade elétrica. Não foi observada influência significativa dos parâmetros de processo sobre a resistência mecânica. No entanto, a soldagem com ACI de 1000 rpm foram os parâmetros que apresentaram os melhores resultados e menor dispersão entre as condições avaliadas. A resistência elétrica das juntas soldadas em todas as condições se mostrou muito próxima da média entre as resistências das ligas utilizadas, indicando a viabilidade da aplicação desse processo em conexões elétricas. Em relação à fadiga, ficou evidenciado um aumento em torno de 30% na vida das juntas soldadas com ACI. Os ensaios de ultrassom não mostraram descontinuidades que comprometessem a aplicação de nenhuma das juntas soldadas. / The friction welding process (FSW) is one of the innovative processes being presented and studied, in the scientific community and companies, for providing a union of excellent quality. However, there are still issues to be solved mainly in soldering of dissimilar materials such as copper and aluminum alloys. The objective of this work is to produce copper and aluminum alloy joints, since these materials are classified as difficult solderability by conventional systems, thus restricting their application. This work evaluated the welding of overlapping joints of an aluminum alloy (ASTM 6060 T5) and the copper alloy (ASTM-B-187, C 110-hardened quench) in which the copper is positioned above the aluminum. The joints were welded by the friction welding and mechanical mixing (FSW) process with four rotational speeds (800, 900, 1000, and 1100 rpm), with the feed rate maintained at 10 mm / min. The influence of a non-initial advance (ACI) of 2 mm at the beginning of the weld was evaluated. The joints produced were evaluated through shear, fatigue, microstructure, ultrasonic and electrical resistivity tests. No significant influence of process parameters on mechanical strength was observed. However, the welding with (ACI) of 1000 rpm were the parameters that presented the best results and lower dispersion among the evaluated conditions. The electrical resistance of the welded joints in all conditions was very close to the average between the resistances of the alloys used, indicating the feasibility of the application of this process in electrical connections. In relation to fatigue, an increase of around 30% in the life of welded joints with (ACI) was evidenced. Ultrasound tests showed no discontinuities that would compromise the application of any of the welded joints.

Made available in DSpace on 2016-08-29T15:36:57Z (GMT). No. of bitstreams: 1 tese_4999_.pdf: 1657727 bytes, checksum: a01030a5e40bb2bca2e3941bc0895770 (MD5) Previous issue date: 2011-07-15 / RESUMO CARDOSO, Ariana de Lima. Desrama artificial em eucalipto e seu efeito na resistência a danos por vento e nós da madeira. 2011. Dissertação (Mestrado em Ciências Florestais) Universidade Federal do Espírito Santo, Jerônimo Monteiro-ES. Orientador: Prof. Dr. Aderbal Gomes da Silva. Coorientadores: Dr. Antônio Marcos Rosado e Prof. Dr. Edvaldo Fialho Reis. O objetivo deste trabalho foi testar a influência de diferentes níveis de desrama em plantios clonais do híbrido Eucalyptus urophylla x Eucalyptus grandis, na região do Vale do Rio Doce, MG, visando à minimização de danos por ventos, bem como estudar a influência da desrama na formação dos nós e no aumento da resistência a quebra por vento. O experimento foi desenvolvido em povoamentos híbridos de Eucalyptus urophylla x Eucalyptus grandis, no espaçamento 3,00 x 3,33 m com os clones A e B, no município de Belo Oriente, MG. Foram utilizados 3 tratamentos de desrama artificial, 4 repetições, em plantas a partir dos 24 meses de idade. Para avaliar a influência dos níveis de desrama na resistência da madeira dos clones A e B, foi empregada a metodologia do teste de resistência. As características dendrométricas avaliadas: altura total, diâmetro a altura do peito, altura comercial e altura de quebra não foram influenciadas pelos níveis de desrama artificial. O clone A mostrou-se mais resistente que o clone B. Em relação à força para tocar o solo, não foi possível identificar uma relação entre os níveis de desrama e um aumento da força para tocar o solo. O nível de desrama artificial D2 foi o que mais contribuiu para o aumento da força para quebrar e que mais contribuiu para a redução das perdas da porcentagem de hectares danificados. A produção dos clones não foi afetada pelos níveis de desrama artificial. Para a classe de diâmetro (<0,50 cm), houve diferença estatística para a posição de avaliação que foi feita até 5m de altura, porém não houve interação significativa entre clone e posição; clone e níveis de desrama artificial. Para a classe de diâmetro (0,50-1,00 cm), a posição de avaliação dos nós (até 5m de altura) ao longo do tronco diferiu significativamente ao nível de 5% pelo teste de Tukey, além disso, o efeito da aplicação dos níveis de desrama artificial foi o mesmo para os clones A e B. O número de nós externos para a classe de diâmetro (> 1,00 cm) nos níveis de desrama de D1 e D2 diferiram da testemunha T1 ao nível de 5% de probabilidade pelo teste de Tukey. Houve interação significativa entre os clones e as posições de avaliação de nós externos para a classe de diâmetro (>1,00 cm). O nível de desrama artificial D2 é o mais indicado para o aumento da resistência da força para tombar, sendo comprovado para o clone A. A aplicação do nível de desrama D2 contribui para o aumento da resistência a quebra pelo vento, implicando diretamente a redução da perda de hectares em florestas clonais de Eucalyptus urophylla x Eucalyptus grandis. A cicatrização e o fechamento dos ferimentos promovidos pelos níveis de desrama artificial contribuíram para o aumento da madeira limpa, redução de nós e melhoria da resistência da madeira. Palavras-chave: Desrama artificial, floresta plantada, qualidade da madeira, vento