Desenvolvimento de materiais híbridos baseados em poliimida / Development of hybrid materials based on polyimideFerreira, Fábio Augusto de Souza 10 July 2014 (has links)
Nesse trabalho são discutidos os resultados a respeito de materiais híbridos baseados na poliimida, PI, obtida por reações de policondensação entre a diamina 4,4\'-Oxidianilina (ODA) e o dianidrido 4,4\'-Oxidiftálico (ODPA), seguida de imidização térmica. O estudo foca na influência do tempo de tratamento (1, 15 e 60 min) e na temperatura de decomposição térmica (500°C) sobre as propriedades da PI. Os experimentos foram realizados sob fluxo de Argônio e os materiais obtidos apresentam características intermediárias entre PI e materiais carbonáceos. Dados de Nanoindentação (NI) revelaram aumento de até 50% de dureza para os filmes tratados por 60 min. ODPA e ODA serviu ainda de base para a preparação do revestimento híbrido contendo ORMOSIL gerado in situ por catálise ácida via processo sol-gel a partir do (3-aminopropil)trietóxissilano (APTES) e Tetraetil Ortossilicato (TEOS). O revestimento obtido é homogêneo e tem boa interação com o substrato (aço inoxidável 316L). A polarização potenciodinâmica revelou uma proteção elevada tanto em solução de NaCl 3,5% em massa quanto em H2SO4 0,5 mol L-1, em relação ao aço sem revestimento, com densidade de corrente da ordem de 10-9 A cm-2, na faixa de -700 a 500 mV vs Ag/AgCl. Por fim, filmes híbridos baseados em ODPA, ODA, APTES e TEOS, adicionados de Ácido Fosfotungstico (HPW) foram preparados e avaliados por Espectroscopia na região do Infravermelho com Transformada de Fourier e Ressonância Magnética Nuclear de Silício e Fósforo (29Si e 31P MAS NMR) que confirmaram a formação da PI e da rede ORMOSIL, bem como revelam que a estrutura do HPW permaneceu intacta após o processo de síntese. Mapeamentos realizados por Micro-fluorescência de Raios X assistida por Luz Síncrotron (μ-XRF) mostram uma boa dispersão da fase inorgânica (ORMOSIL e HPW) na orgânica (POO), e todos os materiais são termicamente estáveis até aproximadamente 500°C, de acordo com as curvas obtidas por Termogravimetria (TGA). Outras técnicas de caracterização também foram usadas para uma investigação mais detalhada dos materiais. / In this thesis are presented the results and considerations related to several hybrid materials derived from the polyimide, PI, obtained by polycondensation reactions between 4,4\'-Oxydianiline (ODA) and 4,4\'-Oxydiphthalic (ODA), followed by thermal imidization. The study focuses on the effect of thermal treatment time (1, 15 and 60 min) and the temperature of beginning of thermal decomposition (773 K) on the properties of PI. The experiments were performed under Argon flow, and the materials presented intermingled properties of PI and carbonaceous materials. The hardness, evaluated by Nanoindentation (NI), reached an increase of 50% for POO films treated for 60 min. POO was also used for the preparation of the hybrid coating containing ORMOSIL obtained in situ by acid catalysis via sol-gel process from (3-aminopropyl)triethoxysilane (APTES) and Tetraethyl Orthosilicate (TEOS). The coating is homogeneous and present a good interaction with the substrate (316L stainless steel). Data of potendynamic polarization revealed a high protection both under NaCl 3.5 wt% and H2SO4 0.5 mol L-1 solutions related to the neat substrate, with current density of order 10-9 A cm-2, in range potential of -700 to 500 mV vs Ag/AgCl. Finally, hybrid films were prepared based on ODPA, ODA, APTES and TEOS, in addition to Phosphotungstic Acid (HPW). The characteristics of all materials were evaluated by Fourier Transform Infrared Spectroscopy in Middle and Near Infrared region (FTMIR and FTNIR), and Magic Angle Spinning-Nuclear Magnetic Resonance of Silicon 29 and Phosphorus 31 (29Si and 31P MAS NMR) which confirmed the ORMOSIL network formation, as well as revealed that the HPW structure remained intact after the synthesis process. Mapping performed by Assisted Synchrotron Light X-ray Micro Fluorescence (μ-XRF) the good dispersion of the inorganic phase (ORMOSIL and HPW) in the organic phase (POO). All materials are thermally stable up to 773 K, according to Thermogravimetric Analysis (TGA). Other techniques of characterization were also used to further investigation of the materials.
|
2 |
Desenvolvimento de materiais híbridos baseados em poliimida / Development of hybrid materials based on polyimideFábio Augusto de Souza Ferreira 10 July 2014 (has links)
Nesse trabalho são discutidos os resultados a respeito de materiais híbridos baseados na poliimida, PI, obtida por reações de policondensação entre a diamina 4,4\'-Oxidianilina (ODA) e o dianidrido 4,4\'-Oxidiftálico (ODPA), seguida de imidização térmica. O estudo foca na influência do tempo de tratamento (1, 15 e 60 min) e na temperatura de decomposição térmica (500°C) sobre as propriedades da PI. Os experimentos foram realizados sob fluxo de Argônio e os materiais obtidos apresentam características intermediárias entre PI e materiais carbonáceos. Dados de Nanoindentação (NI) revelaram aumento de até 50% de dureza para os filmes tratados por 60 min. ODPA e ODA serviu ainda de base para a preparação do revestimento híbrido contendo ORMOSIL gerado in situ por catálise ácida via processo sol-gel a partir do (3-aminopropil)trietóxissilano (APTES) e Tetraetil Ortossilicato (TEOS). O revestimento obtido é homogêneo e tem boa interação com o substrato (aço inoxidável 316L). A polarização potenciodinâmica revelou uma proteção elevada tanto em solução de NaCl 3,5% em massa quanto em H2SO4 0,5 mol L-1, em relação ao aço sem revestimento, com densidade de corrente da ordem de 10-9 A cm-2, na faixa de -700 a 500 mV vs Ag/AgCl. Por fim, filmes híbridos baseados em ODPA, ODA, APTES e TEOS, adicionados de Ácido Fosfotungstico (HPW) foram preparados e avaliados por Espectroscopia na região do Infravermelho com Transformada de Fourier e Ressonância Magnética Nuclear de Silício e Fósforo (29Si e 31P MAS NMR) que confirmaram a formação da PI e da rede ORMOSIL, bem como revelam que a estrutura do HPW permaneceu intacta após o processo de síntese. Mapeamentos realizados por Micro-fluorescência de Raios X assistida por Luz Síncrotron (μ-XRF) mostram uma boa dispersão da fase inorgânica (ORMOSIL e HPW) na orgânica (POO), e todos os materiais são termicamente estáveis até aproximadamente 500°C, de acordo com as curvas obtidas por Termogravimetria (TGA). Outras técnicas de caracterização também foram usadas para uma investigação mais detalhada dos materiais. / In this thesis are presented the results and considerations related to several hybrid materials derived from the polyimide, PI, obtained by polycondensation reactions between 4,4\'-Oxydianiline (ODA) and 4,4\'-Oxydiphthalic (ODA), followed by thermal imidization. The study focuses on the effect of thermal treatment time (1, 15 and 60 min) and the temperature of beginning of thermal decomposition (773 K) on the properties of PI. The experiments were performed under Argon flow, and the materials presented intermingled properties of PI and carbonaceous materials. The hardness, evaluated by Nanoindentation (NI), reached an increase of 50% for POO films treated for 60 min. POO was also used for the preparation of the hybrid coating containing ORMOSIL obtained in situ by acid catalysis via sol-gel process from (3-aminopropyl)triethoxysilane (APTES) and Tetraethyl Orthosilicate (TEOS). The coating is homogeneous and present a good interaction with the substrate (316L stainless steel). Data of potendynamic polarization revealed a high protection both under NaCl 3.5 wt% and H2SO4 0.5 mol L-1 solutions related to the neat substrate, with current density of order 10-9 A cm-2, in range potential of -700 to 500 mV vs Ag/AgCl. Finally, hybrid films were prepared based on ODPA, ODA, APTES and TEOS, in addition to Phosphotungstic Acid (HPW). The characteristics of all materials were evaluated by Fourier Transform Infrared Spectroscopy in Middle and Near Infrared region (FTMIR and FTNIR), and Magic Angle Spinning-Nuclear Magnetic Resonance of Silicon 29 and Phosphorus 31 (29Si and 31P MAS NMR) which confirmed the ORMOSIL network formation, as well as revealed that the HPW structure remained intact after the synthesis process. Mapping performed by Assisted Synchrotron Light X-ray Micro Fluorescence (μ-XRF) the good dispersion of the inorganic phase (ORMOSIL and HPW) in the organic phase (POO). All materials are thermally stable up to 773 K, according to Thermogravimetric Analysis (TGA). Other techniques of characterization were also used to further investigation of the materials.
|
3 |
Condutividade induzida por radiação ionizante no Mylar (PET) e Kapton (polimiidia). / Radiation-induced conductivity in Mylar (PET) and Kapton (polymide)Gregório Filho, Rinaldo 14 August 1986 (has links)
Este trabalho apresenta uma extensiva série de resultados experimentais da condutividade induzida por radiação X contínua, durante e após a irradiação, em amostras de PET e Kapton. As medidas foram realizadas variando-se uma série de parâmetros, tais como: o campo elétrico aplicado, a taxa de exposição, a espessura da amostra, o tipo de eletrodo, a energia da radiação e as condições ambientes. Foram feitas ainda medidas da corrente termo-estimulada em amostras irradiadas e não irradiadas, que permitiram verificar a presença de armadilhas nos materiais. Medidas da corrente fotônica com diferentes eletrodos e espessuras das amostras, constataram a influência do eletrodo no valor dessa corrente. Finalmente um modelo teórico foi desenvolvido, baseado na teoria de balanço dos portadores generalizada, com a inclusão do efeito do campo elétrico na taxa de geração de portadores (efeito Onsager). O ajuste teórico-experimental permitiu a determinação numérica dos principais parâmetros de condução, tais como, mobilidade dos portadores, coeficiente de recombinação e densidade de armadilhas, para os dois materiais estudados. / In this work we present extensive results of measurements of the prompt and delayed radiation-induced conductivity of samples of PET and Kapton. Experimental parameters, such as the effective energy of the radiation, the exposure rate, the total dose, the value of the applied electric field, the nature of the electrodes, and the ambienta1 conditions were changed within wide limits. We also report measurement of thermally stimulated currents for non-irradiated and for irradiated samples which allowed us to investigate the trap-structure of the materials. Measurements of photo-Compton currents with different electrode materials and sample thicknesses gave information about the relation between the nature of the electrodes and the amplitudes of the currents. Based on the generalized rate theory of radiation-induced conduction we developed a theoretical model which includes the effect of the applied electric field on the carrier generation yield (geminate recombination, Onsager effect). Comparison of experimental and theoretical curves allowed us to determine the values of the main conduction parameters, such as carrier mobility, recombination coefficient, trap densities, for the materials under investigation.
|
4 |
Condutividade induzida por radiação ionizante no Mylar (PET) e Kapton (polimiidia). / Radiation-induced conductivity in Mylar (PET) and Kapton (polymide)Rinaldo Gregório Filho 14 August 1986 (has links)
Este trabalho apresenta uma extensiva série de resultados experimentais da condutividade induzida por radiação X contínua, durante e após a irradiação, em amostras de PET e Kapton. As medidas foram realizadas variando-se uma série de parâmetros, tais como: o campo elétrico aplicado, a taxa de exposição, a espessura da amostra, o tipo de eletrodo, a energia da radiação e as condições ambientes. Foram feitas ainda medidas da corrente termo-estimulada em amostras irradiadas e não irradiadas, que permitiram verificar a presença de armadilhas nos materiais. Medidas da corrente fotônica com diferentes eletrodos e espessuras das amostras, constataram a influência do eletrodo no valor dessa corrente. Finalmente um modelo teórico foi desenvolvido, baseado na teoria de balanço dos portadores generalizada, com a inclusão do efeito do campo elétrico na taxa de geração de portadores (efeito Onsager). O ajuste teórico-experimental permitiu a determinação numérica dos principais parâmetros de condução, tais como, mobilidade dos portadores, coeficiente de recombinação e densidade de armadilhas, para os dois materiais estudados. / In this work we present extensive results of measurements of the prompt and delayed radiation-induced conductivity of samples of PET and Kapton. Experimental parameters, such as the effective energy of the radiation, the exposure rate, the total dose, the value of the applied electric field, the nature of the electrodes, and the ambienta1 conditions were changed within wide limits. We also report measurement of thermally stimulated currents for non-irradiated and for irradiated samples which allowed us to investigate the trap-structure of the materials. Measurements of photo-Compton currents with different electrode materials and sample thicknesses gave information about the relation between the nature of the electrodes and the amplitudes of the currents. Based on the generalized rate theory of radiation-induced conduction we developed a theoretical model which includes the effect of the applied electric field on the carrier generation yield (geminate recombination, Onsager effect). Comparison of experimental and theoretical curves allowed us to determine the values of the main conduction parameters, such as carrier mobility, recombination coefficient, trap densities, for the materials under investigation.
|