Made available in DSpace on 2014-06-12T18:08:18Z (GMT). No. of bitstreams: 2 arquivo8966_1.pdf: 2111684 bytes, checksum: 8e2c58cfa9b6a98cadc353b1ca613b29 (MD5) license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5) Previous issue date: 2009 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Indústrias químicas, petroquímicas e usinas geradoras de energia são locais altamente favoráveis ao desenvolvimento e proliferação de microrganismos. Quando a corrosão do material metálico se processa sob a influência de microrganismos, ela é denominada biocorrosão ou corrosão microbiologicamente induzida (CMI). Este trabalho teve como principal objetivo avaliar a microbiota marinha da Região de Suape na corrosão de cupons metálicos de Aço Carbono AISI 1005 e SAE 1008. Foram investigados microrganismos responsáveis pelo processo de biocorrosão e avaliado o uso de um revestimento polimérico para proteção da liga aço carbono. O material utilizado foram cupons de aço carbono AISI 1005 e SAE 1008 e o revestimento anticorrosivo a base de resina epóxi. Os cupons com dimensões 1x25x35mm foram previamente jateados, tratados e pesados. Os experimentos foram conduzidos em sistema estático constituídos por biorreatores. As amostras de água foram sempre coletadas no mesmo local, trocadas e analisadas (parâmetros físico-químicos e microbiológicos) a cada 15 dias. As análises para quantificação dos microrganismos planctônicos (bactérias aeróbias e anaeróbias totais, bactérias precipitantes do ferro, bactérias redutoras do sulfato (BRS), Pseudomonas aeruginosa, assim como fungos filamentosos) foram realizadas durante um período entre 60 e 90 dias. Neste mesmo período, também foram retirados cupons para quantificação dos microrganismos sésseis. Também foi realizada uma cinética de crescimento microbiano na formação do biofilme ao longo de 14 dias, com a retirada dos cupons a cada 48 horas para avaliar o comportamento de formação de biofilme em função do tempo. Posteriormente, os cupons foram analisados através de técnicas de caracterização da superfície metálica e taxa de corrosão. Os valores encontrados para as taxas de corrosão referentes aos cupons AISI 1005 sem revestimento, SAE 1008 sem revestimento e SAE 1008 com revestimento foram de 0,04708 mm/ano, 0,0561 mm/ano e 0,0053 mm/ano, respectivamente. Para ambos os cupons sem revestimento (1005 e 1008) o melhor modelo proposto foi um ajuste polinomial de grau três. Para o cupom revestido o modelo que melhor se ajustou foi a equação de decaimento exponencial de grau um. Esse resultado mostra a importância do revestimento no combate à corrosão das ligas metálicas em ambientes fortemente corrosivos

Nesse trabalho são discutidos os resultados a respeito de materiais híbridos baseados na poliimida, PI, obtida por reações de policondensação entre a diamina 4,4\'-Oxidianilina (ODA) e o dianidrido 4,4\'-Oxidiftálico (ODPA), seguida de imidização térmica. O estudo foca na influência do tempo de tratamento (1, 15 e 60 min) e na temperatura de decomposição térmica (500°C) sobre as propriedades da PI. Os experimentos foram realizados sob fluxo de Argônio e os materiais obtidos apresentam características intermediárias entre PI e materiais carbonáceos. Dados de Nanoindentação (NI) revelaram aumento de até 50% de dureza para os filmes tratados por 60 min. ODPA e ODA serviu ainda de base para a preparação do revestimento híbrido contendo ORMOSIL gerado in situ por catálise ácida via processo sol-gel a partir do (3-aminopropil)trietóxissilano (APTES) e Tetraetil Ortossilicato (TEOS). O revestimento obtido é homogêneo e tem boa interação com o substrato (aço inoxidável 316L). A polarização potenciodinâmica revelou uma proteção elevada tanto em solução de NaCl 3,5% em massa quanto em H2SO4 0,5 mol L-1, em relação ao aço sem revestimento, com densidade de corrente da ordem de 10-9 A cm-2, na faixa de -700 a 500 mV vs Ag/AgCl. Por fim, filmes híbridos baseados em ODPA, ODA, APTES e TEOS, adicionados de Ácido Fosfotungstico (HPW) foram preparados e avaliados por Espectroscopia na região do Infravermelho com Transformada de Fourier e Ressonância Magnética Nuclear de Silício e Fósforo (29Si e 31P MAS NMR) que confirmaram a formação da PI e da rede ORMOSIL, bem como revelam que a estrutura do HPW permaneceu intacta após o processo de síntese. Mapeamentos realizados por Micro-fluorescência de Raios X assistida por Luz Síncrotron (μ-XRF) mostram uma boa dispersão da fase inorgânica (ORMOSIL e HPW) na orgânica (POO), e todos os materiais são termicamente estáveis até aproximadamente 500°C, de acordo com as curvas obtidas por Termogravimetria (TGA). Outras técnicas de caracterização também foram usadas para uma investigação mais detalhada dos materiais. / In this thesis are presented the results and considerations related to several hybrid materials derived from the polyimide, PI, obtained by polycondensation reactions between 4,4\'-Oxydianiline (ODA) and 4,4\'-Oxydiphthalic (ODA), followed by thermal imidization. The study focuses on the effect of thermal treatment time (1, 15 and 60 min) and the temperature of beginning of thermal decomposition (773 K) on the properties of PI. The experiments were performed under Argon flow, and the materials presented intermingled properties of PI and carbonaceous materials. The hardness, evaluated by Nanoindentation (NI), reached an increase of 50% for POO films treated for 60 min. POO was also used for the preparation of the hybrid coating containing ORMOSIL obtained in situ by acid catalysis via sol-gel process from (3-aminopropyl)triethoxysilane (APTES) and Tetraethyl Orthosilicate (TEOS). The coating is homogeneous and present a good interaction with the substrate (316L stainless steel). Data of potendynamic polarization revealed a high protection both under NaCl 3.5 wt% and H2SO4 0.5 mol L-1 solutions related to the neat substrate, with current density of order 10-9 A cm-2, in range potential of -700 to 500 mV vs Ag/AgCl. Finally, hybrid films were prepared based on ODPA, ODA, APTES and TEOS, in addition to Phosphotungstic Acid (HPW). The characteristics of all materials were evaluated by Fourier Transform Infrared Spectroscopy in Middle and Near Infrared region (FTMIR and FTNIR), and Magic Angle Spinning-Nuclear Magnetic Resonance of Silicon 29 and Phosphorus 31 (29Si and 31P MAS NMR) which confirmed the ORMOSIL network formation, as well as revealed that the HPW structure remained intact after the synthesis process. Mapping performed by Assisted Synchrotron Light X-ray Micro Fluorescence (μ-XRF) the good dispersion of the inorganic phase (ORMOSIL and HPW) in the organic phase (POO). All materials are thermally stable up to 773 K, according to Thermogravimetric Analysis (TGA). Other techniques of characterization were also used to further investigation of the materials.

Nesse trabalho são discutidos os resultados a respeito de materiais híbridos baseados na poliimida, PI, obtida por reações de policondensação entre a diamina 4,4\'-Oxidianilina (ODA) e o dianidrido 4,4\'-Oxidiftálico (ODPA), seguida de imidização térmica. O estudo foca na influência do tempo de tratamento (1, 15 e 60 min) e na temperatura de decomposição térmica (500°C) sobre as propriedades da PI. Os experimentos foram realizados sob fluxo de Argônio e os materiais obtidos apresentam características intermediárias entre PI e materiais carbonáceos. Dados de Nanoindentação (NI) revelaram aumento de até 50% de dureza para os filmes tratados por 60 min. ODPA e ODA serviu ainda de base para a preparação do revestimento híbrido contendo ORMOSIL gerado in situ por catálise ácida via processo sol-gel a partir do (3-aminopropil)trietóxissilano (APTES) e Tetraetil Ortossilicato (TEOS). O revestimento obtido é homogêneo e tem boa interação com o substrato (aço inoxidável 316L). A polarização potenciodinâmica revelou uma proteção elevada tanto em solução de NaCl 3,5% em massa quanto em H2SO4 0,5 mol L-1, em relação ao aço sem revestimento, com densidade de corrente da ordem de 10-9 A cm-2, na faixa de -700 a 500 mV vs Ag/AgCl. Por fim, filmes híbridos baseados em ODPA, ODA, APTES e TEOS, adicionados de Ácido Fosfotungstico (HPW) foram preparados e avaliados por Espectroscopia na região do Infravermelho com Transformada de Fourier e Ressonância Magnética Nuclear de Silício e Fósforo (29Si e 31P MAS NMR) que confirmaram a formação da PI e da rede ORMOSIL, bem como revelam que a estrutura do HPW permaneceu intacta após o processo de síntese. Mapeamentos realizados por Micro-fluorescência de Raios X assistida por Luz Síncrotron (μ-XRF) mostram uma boa dispersão da fase inorgânica (ORMOSIL e HPW) na orgânica (POO), e todos os materiais são termicamente estáveis até aproximadamente 500°C, de acordo com as curvas obtidas por Termogravimetria (TGA). Outras técnicas de caracterização também foram usadas para uma investigação mais detalhada dos materiais. / In this thesis are presented the results and considerations related to several hybrid materials derived from the polyimide, PI, obtained by polycondensation reactions between 4,4\'-Oxydianiline (ODA) and 4,4\'-Oxydiphthalic (ODA), followed by thermal imidization. The study focuses on the effect of thermal treatment time (1, 15 and 60 min) and the temperature of beginning of thermal decomposition (773 K) on the properties of PI. The experiments were performed under Argon flow, and the materials presented intermingled properties of PI and carbonaceous materials. The hardness, evaluated by Nanoindentation (NI), reached an increase of 50% for POO films treated for 60 min. POO was also used for the preparation of the hybrid coating containing ORMOSIL obtained in situ by acid catalysis via sol-gel process from (3-aminopropyl)triethoxysilane (APTES) and Tetraethyl Orthosilicate (TEOS). The coating is homogeneous and present a good interaction with the substrate (316L stainless steel). Data of potendynamic polarization revealed a high protection both under NaCl 3.5 wt% and H2SO4 0.5 mol L-1 solutions related to the neat substrate, with current density of order 10-9 A cm-2, in range potential of -700 to 500 mV vs Ag/AgCl. Finally, hybrid films were prepared based on ODPA, ODA, APTES and TEOS, in addition to Phosphotungstic Acid (HPW). The characteristics of all materials were evaluated by Fourier Transform Infrared Spectroscopy in Middle and Near Infrared region (FTMIR and FTNIR), and Magic Angle Spinning-Nuclear Magnetic Resonance of Silicon 29 and Phosphorus 31 (29Si and 31P MAS NMR) which confirmed the ORMOSIL network formation, as well as revealed that the HPW structure remained intact after the synthesis process. Mapping performed by Assisted Synchrotron Light X-ray Micro Fluorescence (μ-XRF) the good dispersion of the inorganic phase (ORMOSIL and HPW) in the organic phase (POO). All materials are thermally stable up to 773 K, according to Thermogravimetric Analysis (TGA). Other techniques of characterization were also used to further investigation of the materials.