Made available in DSpace on 2017-07-20T13:42:00Z (GMT). No. of bitstreams: 1 Rafael Jansen Mikami.pdf: 3198153 bytes, checksum: 6a277457317456e313f7f86a96cd4474 (MD5) Previous issue date: 2017-03-31 / The use of recycled aggregates for producing concrete has been studied as a way to reuse construction waste. However, these aggregates may contain contaminants that may cause the leaching of pollutants, especially in open places, such as floors and sidewalks. Thus, the objective of this study was to verify the releasing of sulfates and heavy metals in the water by leaching of pervious concrete made of recycled aggregates. Six types of aggregates were produced with uniform granulometric distribution. One of the aggregates was conventional aggregate and the other ones were recycled aggregates. For each type of aggregate, containing different ceramic contents, concrete specimens were made. To perform the leaching test, pervious concrete specimens were immersed in ultrapure water, which was renewed after 24, 48, 168 and 384 h from the start of the test. The leached water was analyzed for pH, electrical conductivity, alkalinity, chemical oxygen demand (COD), total solids, sulfates and potentially toxic elements (Cr, Cd, Zn, Pb, Cu). It was verified that all concretes produced had a permeability coefficient above the minimum recommended value for use as a pervious pavement, of 0,10 cm.s-1. However, the maximum compressive strength obtained was 10,15 MPa, not reaching the minimum for use in pavements (20 MPa). The incorporation of ceramic material in the aggregate resulted in an increase in water absorption. The leaching tests showed that the pH of the concrete leachate remained alkaline, reaching an overall average value of 11,5. The electrical conductivity throughout the experiment increased, demonstrating that the concrete continued to release ions over the 16 day period. The mean sulfate concentration in the leachate varied between 21,3 and 71,7 mg.L-1 after 24 h of the test, gradually reducing until the last sampling, in which the concentration was between 2,4 and 21,6 mg.L-1. No direct relationship between the sulfate concentration and the ceramic content in the aggregate was observed. However, it was visually verified that a specimen was contaminated with gypsum, implying a sulfate concentration five times higher than the other samples of the same treatment, increasing the mean of the treatment. Significant quantities of chromium were detected in the leachate, mainly of the concrete made with 100% ceramic aggregate, which released 0,083 mg.L-1 of chromium. In all treatments, cadmium concentrations in the leachate were between 0,009 and 0,113 mg.L-1, exceeding the maximum limit of 0,005 mg.L-1, established by Brazilian Standard (NBR) 10004:2004. / O uso de agregados reciclados na confecção de concretos tem sido estudado como uma forma de reutilizar os resíduos da construção civil. Entretanto, esses agregados podem conter contaminantes, havendo o risco da lixiviação de poluentes, principalmente em locais expostos ao ambiente, como pisos e calçadas. Dessa forma, o objetivo deste estudo foi verificar a liberação de sulfatos e metais pesados na água pela lixiviação de concreto permeável confeccionado com agregados graúdos reciclados. Seis tipos de agregados foram produzidos com distribuição granulométrica uniforme, sendo um agregado convencional e os demais agregados reciclados. Para cada tipo de agregado, contendo diferentes teores de cerâmica, foram confeccionados corpos de prova de concreto. Para a realização do teste de lixiviação, corpos de prova de concreto permeável foram imersos em água ultrapura, sendo esta renovada após 24, 48, 168 e 384 h do início do ensaio. A água lixiviada foi analisada quanto ao pH, condutividade elétrica, alcalinidade, a demanda química de oxigênio (DQO), sólidos totais, sulfatos e elementos potencialmente tóxicos (Cr, Cd, Zn, Pb, Cu). Verificou-se que todos os concretos produzidos apresentaram coeficiente de permeabilidade acima do valor mínimo recomendado para uso como pavimento permeável, de 0,10 cm.s-1. No entanto, a resistência à compressão máxima obtida foi de 10,15 MPa, não atingindo o mínimo para utilização em pavimentos (20 MPa). A incorporação de material cerâmico no agregado resultou em um crescente aumento na absorção de água. Os testes de lixiviação demonstraram que o pH do lixiviado de concreto se manteve alcalino, atingindo um valor médio geral de 11,5. A condutividade elétrica ao longo do experimento aumentou, demonstrando que o concreto continuou a liberar íons ao longo do período de 16 dias. A concentração média de sulfato no lixiviado variou entre 21,3 e 71,7 mg.L-1 após 24 h de ensaio, reduzindo gradualmente até a última coleta, na qual a concentração se situou entre 2,4 e 21,6 mg.L-1. Não foi constatada relação direta entre a concentração de sulfato e o teor de material cerâmico no agregado. No entanto, verificou-se visualmente que um corpo de prova estava contaminado com gesso, o que implicou em uma concentração de sulfato cinco vezes superior às demais amostras do mesmo tratamento, elevando a média do tratamento. Foram detectadas quantidades significativas de cromo no lixiviado, principalmente do concreto confeccionado com agregado 100% cerâmico, que liberou 0,083 mg.L-1 de cromo. Em todos os tratamentos verificaram-se concentrações de cádmio no lixiviado entre 0,009 e 0,113 mg.L-1, ultrapassando o limite máximo de 0,005 mg.L-1, estabelecido pela Norma Brasileira (NBR) 10004:2004.

Os resíduos de construção e demolição (RCD) representam cerca de 50% de todo o resíduo sólido gerado, sendo que cerca de 90% deste é de origem mineral e pode ser reciclado através de processos de beneficiamento mineral. Para se atingir a reciclagem massiva torna-se imperativo o desenvolvimento de novos mercados e melhorias de usina capazes de tornar o resíduo uma matéria prima de qualidade adequada. Dessa forma a caracterização tecnológica é imprescindível para obtenção de informações fundamentais sobre o processo de beneficiamento e as especificações para os produtos. O programa experimental foi desenvolvido em três amostras de RCD britados de duas usinas de reciclagem do Estado de São Paulo, Itaquera cinza (IT-C), Itaquera vermelho (IT-V), Vinhedo vermelho (VI-V). As atividades desenvolvidas foram: amostragem, cominuição, determinação das composições químicas e mineralógicas por faixa granulométrica, determinação de propriedades físicas relevantes para reciclagem de RCD como agregados para uso em concreto, determinação das curvas de separabilidade por densidade e análise de sua composição química e mineralógica e estudos microscópicos para avaliação do teor de aglomerantes por faixa densitária. Os resultados de análises químicas mostram que as composições químicas das três amostras são semelhantes; os teores variam com a granulometria, com marcantes diferenças na fração mais fina. A composição mineralógica predominante é de silicatos, provenientes de agregados e rochas naturais, cerâmicas e aglomerantes, com menores teores de alumina e óxido de cálcio; a perda ao fogo está diretamente relacionada ao teor de aglomerantes, uma vez que representa a água combinada e o gás carbônico presente. A separação do RCD em classes de densidade permitiu identificar que os produtos obtidos apresentam composições diferentes e pode ser empregada para se obter agregados de melhor qualidade e, portanto, para aplicações mais nobres, uma vez que se verifica que cerca de 80% em massa dos resíduos possuem densidades superiores a 2,2 g/cm3 com qualidades físicas adequadas para uso em concreto estrutural. Adicionalmente, a massa específica aparente e absorção de água estão diretamente relacionadas com os intervalos de densidade. O teor de aglomerantes aumenta significativamente para os produtos de menor densidade, sendo que as partículas cerâmicas estão isentas de pasta de cimento endurecida e cal. / Construction and demolition waste (CDW) represents around 50% of the total solid waste and are essentially constituted by mineral fraction (>90%); therefore it?s possible to recycle it through mineral processing techniques. The development of different uses and the improvement of the typical technologies applied to CDW recycling are essential to achieve a satisfactory level of recycling. Applied mineralogy tools are fundamental to characterize the studied raw material and support the mineral processing in order to obtain products according to its specifications. This research was carried out in three crushed samples from two different plants close to Sao Paulo; they were named according to its classification: grey Itaquera (IT-C), red Itaquera (IT-V) and red Vinhedo (VI-V). The method involved basically sampling, crushing, characterization of the relevant physical properties for a concrete recycled aggregate approach, evaluation of the specific gravity separability curves and chemical and mineralogical analyses for each grain size fraction and gravity classes, and so microscope analyses to verify the binder contents. The results show that the chemical composition of the three samples is very similar, the grades change according to the grain size fractions, specially for the finest fraction. The mineral composition is also quite akin, it is mostly represented by silicates (mainly aggregates and natural rocks), ceramics and binder; minor amounts of Al2O3 and CaO were also detected. The loss of ignition is directly related to the binder and clay minerals (basically OH and CO2). Specific gravity classes are very different regarding their chemical, mineralogical and physical properties, despite their similarity among the samples. Thus the specific gravity separation is more effective to classify the recycled CD debris than its color and could be applied to obtain high quality recycled aggregates, while a significant amount (80%) is recovered above 2.2 g/cm3 and may be used as high strength concrete aggregates. In addition, the physical properties, like specific gravity and water absorption are strictly related to the specific gravity classes.

Os resíduos de construção e demolição (RCD) são gerados em quantidades expressivas nas cidades de grande e médio portes no Brasil e são comumente descartados de forma irregular. Para os milhares de quilômetros de vias urbanas não pavimentadas, o agregado reciclado de resíduo sólido da construção civil é uma alternativa aos materiais convencionais de pavimentação. Esta dissertação analisa o comportamento mecânico do agregado reciclado para emprego em camadas de base e sub-base. A pesquisa consiste em ensaios laboratoriais, acompanhados de um estudo de caso - o pavimento do novo campus da Universidade de São Paulo (USP Leste). Um trecho de 1.020 metros de extensão foi utilizado no estudo, de um total de aproximadamente dois quilômetros de vias pavimentadas no campus. O pavimento avaliado possui agregado reciclado em sua estrutura; quatro seções-tipo diferentes foram construídas, variando os materiais, as espessuras, a compactação e o subleito. Propriedades físicas e mecânicas do agregado reciclado foram determinadas em laboratório por meio dos seguintes testes: composição, porcentagem de materiais indesejáveis, massa específica, absorção de água, graduação, forma dos grãos, compactação, influência da compactação, índice de suporte Califórnia, módulo de resiliência e deformação permanente. Os ensaios de campo compreenderam: controle de materiais e de execução, resistência à penetração pelo Dynamic Cone Penetrometer e levantamento deflectométrico com o Falling Weight Deflectometer. Baseado na análise das bacias de deflexão das seções-tipo construídas, o trecho estudado é dividido em quatro comportamentos distintos à deformação. Os resultados mostraram que o comportamento mecânico do agregado reciclado apresenta uma forte dependência da eficiência da compactação. Quando submetido a uma compactação adequada, o material reciclado comporta-se tal qual uma brita graduada simples. / Construction and demolition waste (CDW) is generated in significant amounts in medium and large size cities in Brazil and are usually disposed of illegally. For the thousands of kilometers of unpaved urban roads, the recycled aggregate of CDW is an alternative to conventional paving materials. This dissertation analyses the mechanical behavior of the recycled aggregate for use in base and subbase layers. This research consisted of a series of laboratory tests, followed by a case study - the pavement of the new campus of the University of Sao Paulo (USP Leste). A test track of 1,020 meters of extension was used for the study, from a total of approximately two kilometers of paved roads in the campus. The pavement studied contains recycled aggregate in its structure; four different road sections were constructed, varying the materials, thickness, compaction and subgrade. Physical and mechanical properties of the recycled aggregate were characterized through the following laboratory tests: composition, percentage of impurities, bulk density, water absorption, gradation, grain form, compaction, compaction influence, California Bearing Ratio, resilient modulus and permanent deformation. The field tests covered: materials and construction control, bearing capacity using the Dynamic Cone Penetrometer and deflection measurement using a Falling Weight Deflectometer. Based on the analysis of the deflection basins of the built road sections, the test track is divided according to four different deformation behaviors. The results show that the mechanical behavior of the recycled aggregate presents a strong dependence on the compaction effort. When submitted to proper compaction, the recycled material behaves as a crushed-stone.

Submitted by Fabricia Fialho Reginato (fabriciar) on 2015-07-08T22:34:01Z No. of bitstreams: 1 DanieleGugel.pdf: 2874038 bytes, checksum: 4386cae5306c5137fce5e8448d48f6fa (MD5) / Made available in DSpace on 2015-07-08T22:34:01Z (GMT). No. of bitstreams: 1 DanieleGugel.pdf: 2874038 bytes, checksum: 4386cae5306c5137fce5e8448d48f6fa (MD5) Previous issue date: 2014-04-02 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / FINEP - Financiadora de Estudos e Projetos / A construção civil é um setor que causa elevado impacto ambiental devido à geração de resíduos e ao elevado consumo de matérias-primas. Demandas cada vez maiores por áreas a serem destinadas a aterros, aliadas à escassez de recursos naturais, favorecem a utilização de resíduos de construção e demolição como fonte para agregados. Neste contexto, muitos estudos estão sendo feitos a respeito de concretos produzidos com resíduos de construção e demolição, focados principalmente nas propriedades mecânicas de resistência à tração e à compressão. Para aplicação como material estrutural, entretanto, a relação tensão x deformação e, particularmente, o Módulo de Elasticidade são importantes parâmetros a serem analisados, pois são diretamente relacionados com o projeto de estruturas. Frente ao exposto, o presente trabalho utilizou agregado graúdo reciclado de concreto (ARC) na confecção de novos concretos e teve como objetivo analisar o comportamento elástico dos mesmos. Para tanto, foram confeccionados concretos com 0% e 50% de substituição de agregados graúdos naturais (AGN) por ARC. O comportamento elástico foi determinado através de um método destrutivo (Estático) e através de um método não destrutivo (Dinâmico) nas idades de 7, 28 e 63 dias para os níveis de carregamento de 0 (somente Dinâmico), 20, 30, 40, 50, 60, 70 e 80% da resistência do concreto. Os resultados encontrados para o Módulo de Elasticidade foram comparados com estimativas a partir de métodos empíricos previstos nas normas CEB-FIP Model Code 1990, ACI 318 (2011) e NBR 6118 (ABNT, 2007 e 2014). Com isso, visou-se observar a influência do ARC nas propriedades elásticas do concreto, comparar o comportamento elástico dos concretos de referência aos resultados dos concretos com ARC, estudar a correlação entre os dois métodos experimentais (Dinâmico e Estático) e verificar a correspondência entre os resultados experimentais obtidos com os normativos. Como principais conclusões, pôde-se verificar que os concretos com ARC apresentam limite elástico similar aos concretos que utilizam somente AGN (este limite situa-se entre 40 e 50% da ƒc); não foi possível identificar uma relação única entre os valores de módulo obtidos pelo Método Dinâmico e pelo Método Estático para ambos os concretos; não é possível afirmar que concretos de resistências similares, mas idades diferentes apresentaram módulos diferentes; os concretos com e sem ARC estudados apresentaram valores de Módulo de Elasticidade obtidos pelo método Estático bastante inferiores aos previstos pelas normas estudadas; os valores de Módulo de Elasticidade obtidos pelo método Dinâmico, para concretos com e sem ARC, estão contidos na faixa entre a norma mais conservadora e a menos conservadora e as curvas obtidas mostram que os concretos com ARC têm comportamento similar aos concretos sem ARC, mas são menos rígidos (maiores deformações para as mesmas tensões). / The construction industry causes a great environmental impact due to the generation of waste and the high consumption of raw material. Increasing demands for areas to become landfills, as well as shortages of natural resources, have favored the use of construction and demolition waste as a source of aggregate. In this context, many studies have been made regarding concretes produced with the use of demolition and construction waste; mainly focused on the mechanical properties of tensile and compressive strength. However, in order to use concretes produced with waste as a structural material, the stress-strain behavior and, particularly, the elastic modulus are important parameters to be analyzed, once they are directly related to structural design. Based on that, the objective of this project is to analyze the elastic behavior of concretes using coarse natural aggregates (NA) and 50% of substitution of these aggregate by coarse recycled concrete aggregates (RCA). The elastic behavior was determined by both a destructive method (static) and a nondestructive one (dynamic) on the ages of 7, 28 and 63 days for the loading levels of 0 (only dynamic), 20, 30, 40, 50, 60, 70 and 80% of respective concrete strength. The found results for the Modulus of Elasticity have been compared to estimates based on the empirical recommendations by CEB-FIP Model Code 1990, ACI 318 (2011) and NBR 6118 (ABNT, 2007 and 2014) standards. The objectives of this work were to observe the influence of the RCA on the elastic properties of concrete; to compare the elastic behavior between concretes with and without RCA, to study the correlation of both experimental methods (dynamic and static) and finally to check the relation between measured and calculated values of modulus of elasticity. The conclusions indicate that concretes with and without RCA have similar elastic limits (between 40% and 50% of the concrete strength); it is not possible to identify a unique relationship between the values obtained by dynamic and static methods for both concretes; it is not possible to assert that concretes with similar strength, but different ages, have different modulus; the values of modulus of elasticity obtained by the static method for both concretes are significantly below that indicated by the considered standards; the values of modulus of elasticity obtained by the dynamic method for concrete with and without RCA are contained in the range between the more and less conservative standards and concretes with RCA have a similar behavior than concretes without RCA, but are less rigid (larger strain for the same stress).

Ce travail de thèse combine des approches expérimentales et théoriques visant à caractériser les propriétés mécaniques et de durabilité des bétons à base de granulats recyclés. La première partie est consacrée à la quantification de l'effet des granulats recyclés sur les propriétés mécaniques et de durabilité de ces bétons. Les résultats montrent que les propriétés mécaniques et de durabilité des bétons à base de granulats recyclés sont sensibles non seulement aux propriétés physiques des granulats recyclés mais aussi à leur quantité au sein de la microstructure. Par ailleurs, une caractérisation des propriétés mécaniques locales grâce aux essais de nano indentation et micro indentation a aussi été entreprise; ce qui a permis d'avoir accès aux propriétés mécaniques des phases telles que les zones d'interface ou encore l'ancien mortier. La deuxième partie est une approche consacrée à l'établissement des modèles multi-échelles en mesure de rendre compte des propriétés macroscopiques (mécanique et de diffusion) des bétons à base de granulats de démolition en tirant profit des informations recueillies sur la microstructure (observation au microscope, nano et micro indentation,...). Une prise en compte du caractère complexe des granulats recyclés a aussi été abordée dans ce développement théorique. Enfin, une comparaison des résultats des modèles avec ceux expérimentaux est présentée puis discutée dans ce travail / This thesis combines experimental and theoretical approaches to characterize the mechanical and durability properties of recycled aggregate concretes (RAC). The first part of the work is devoted to the quantification of the impact of recycled concrete aggregates on the mechanical and durability properties of RAC. The results show that mechanical and durability properties of recycled aggregate concretes depend not only on the physical properties of recycled concrete aggregates but also on their quantity in the microstructure. Furthermore, statistical indentation technique is used to capture the local mechanical properties of phases in the microstructure of RAC such as the interfacial transition zones and the attached mortar. The second part of this study deals with the multi-scale modeling of the mechanical and the durability properties of RAC. The main purpose of this theoretical work is to establish models capable to predict the macroscopic behaviour based on the available information on the microstructure (obtained by optical microscopy or through indentation technique). The established models take into account the complex structure of the recycled concrete aggregates. Finally, the results of the models are compared with experimental data for discussion

O Brasil destaca-se como o sétimo produtor mundial de fundidos, com mais de 30 empresas de microfusão localizadas nas regiões Sul e Sudeste do país eum dos grandes desafios é a gestão dos resíduos, entre eles, a casca cerâmica. Para a mitigação dos seus impactos é necessário o uso de técnicas de reciclagem que combinem desenvolvimento técnico com proteção ao meio ambiente e utilize a construção civil, mais especificamente o concreto, como fonte de incorporação do resíduo de casca cerâmica. Para isso, foi estudado o resíduo como agregado graúdo e miúdo em comparação com a areia e a brita 0. A massa específica do agregado seco e a massa unitária dos agregados foram avaliadas, sendo que o resíduo apresentou uma pequena redução para ambos os casos. A absorção de água foi maior para o agregado reciclado. O agregado miúdo reciclado apresentou resultados maiores para o módulo de finura e a massa específica. O índice de forma do agregado graúdo reciclado apresentou melhores resultados do agregado natural. Para avaliação do comportamento do resíduo no concreto foi utilizado o método de dosagem do IPT EPUSP. A relação água/cimento aumentou com a incorporação do resíduo Ainda, houve redução do consumo de cimento com o resíduo incorporado. As adições com até 75% de substituição do agregado graúdo apresentaram maior resistência à compressão axial comparado ao concreto convencional e, quanto maior a relação a/c menor a resistência à compressão obtida.Para o concreto em estado endurecido a absorção de água aumentou com a adição de resíduo. O índice de vazios do concreto aumenta com a incorporação de resíduo na mistura. A incorporação de resíduo aumenta a massa específica real e da amostra seca das dosagens até a substituição de 50% do agregado graúdo e após esta, tem-se uma pequena redução nestes parâmetros. A espessura carbonatada aumentou com a idade e as dosagens até 50% de adição do agregado graúdo apresentaram valores menores do que o concreto convencional. Palavras-chave: Casca cerâmica, concreto, resíduo, agregado reciclado. / Brazil stands out as the seventh world-wide producer of castings, with more than 30 microfusion companies located in the South and Southeast regions of the country and one of the great challenges is waste management, among them the ceramic shell. To mitigate its impacts, it is necessary to use recycling techniques that combine technical development with protection of the environment and use civil construction, specifically concrete, as a source of incorporation of the residue of ceramic shell. For this, the residue was studied as a large aggregate and small compared to sand and gravel 0. The specific mass of the dry aggregate and the unit mass of the aggregates were evaluated, and the residue presented a small reduction for both cases. The water absorption was higher for the recycled aggregate. The recycled kid aggregate presented higher results for the modulus of fineness and the specific mass. The shape index of the recycled aggregate presented better results from the natural aggregate. To evaluate the behavior of the residue in the concrete, the IPT EPUSP dosing method was used The water / cement ratio increased with the incorporation of the residue. Also, there was a reduction of the cement consumption with the incorporated residue. Additions with up to 75% of the large aggregate substitution showed greater resistance to axial compression compared to conventional concrete, and the higher the a / c ratio the lower the compressive strength obtained. For concrete in the hardened state the water absorption increased with the addition of residue. The void content of the concrete increases with the incorporation of residue into the mixture. Residue incorporation increases the actual specific mass and the dry sample of the dosages up to the replacement of 50% of the large aggregate and after this, a small reduction in these parameters is observed. The carbonate thickness increased with age and the dosages up to 50% addition of the coarse aggregate presented lower values than the conventional concrete.

A proposta busca reduzir a absorção de água dos agregados reciclados de Resíduos de Construção e Demolição (RCD), através do tratamento de sua superfície com hidrofugante, de maneira que estes não aumentem o consumo de água tampouco reduzam a resistência mecânica. Os agregados reciclados de RCD foram caracterizados quanto à granulometria, morfologia, porosidade, ângulo de contato aparente, absorção de água, análise de imagem e rugosidade superficial. Em seguida, os mesmos foram tratados superficialmente com dois tipos de hidrofugante: solução de silano e parafina. Todos os tratamentos permitiram reduzir a absorção de água dos agregados reciclados de RCD. O tratamento por imersão foi aquele que permitiu obter os melhores resultados e a menor variabilidade entre as técnicas. Os tratamentos hidrofugam a superfície, apesar da parafina apresentar maior molhabilidade. O tratamento com parafina apresentou, em termos de absorção de água, resultados inferiores e menos variáveis que o silano. Os parâmetros de rugosidade constataram que, ambos os materiais perdem seu perfil topográfico original quando tratados com parafina. Os diferentes agregados reciclados com cada hidrofugante foram aplicados em materiais cimentícios analisados no estado fresco e no estado endurecido. Os tratamentos reduziram a absorção e o consumo de água de mistura, porém afetaram negativamente as propriedades mecânicas, devido nova interface gerada (no caso específica de parafina) e falta de molhabilidade nas superfícies. / The proposal aims to reduce the water absorption of the Construction and Demolition Waste (CDW) recycled aggregates through hydrophobic surface treatment, so that these do not increase the concretes water consumption (nor reduce de mechanical strength). The CDW recycled aggregates were characterized regarding granulometry, morphology, porosity, apparent contact angle, water absorption, image analysis and surface roughness. Then they had their surface treated with two types of water-repellent: silane solution and paraffin. All treatments have reduced water absorption of the CDW recycled aggregate. Immersion treatment was the one that allowed the best results and the lowest variability between techniques. The treatments repel water on surface, despite the paraffin presenting better wettability. Paraffin treatment showed, in terms of water absorption, lower and less variable results than silane did. Roughness parameters found that both materials lose their topographic profile when treating with paraffin. The different recycled aggregates with each repellent were applied in cementitious materials analyzed in fresh and hardened state. The treatments reduced absorption and mixing consumption of water in the mixing, but adversely affect mechanical properties due to the new interface created (paraffin wax in special) and the lack of wettability on surfaces.

A comparison of concrete containing recycled concrete coarse aggregates and natural coarse aggregates subjected to high strain, low cycle compressive fatigue is presented. Using a strain based feedback control loop, concrete cylinders are compressed at 15µε/s to a specified strain then unloaded to zero stress for 10 cycles. After cycling, all samples are loaded to a strain of 0.008. Direct concrete material variables are the water to cement (w/c) ratio, taken as 0.60, 0.45, and 0.39, and percent coarse recycled concrete aggregate content, varied from zero to 100 percent. The primary testing variable is the specified unloading strain. Unloading strains include 60, 75, 90, 100, and 120 percent of the strain at peak stress. Ten batches of concrete were made, generating a total of 224 samples for testing. Findings confirm previous research showing a reduction in strength with increasing recycled concrete coarse aggregate content, an equivalent concrete with only 25 percent replacement of natural coarse aggregates and an equivalent strength concrete with a decrease in the w/c ratio and 100 percent recycled concrete coarse aggregates. Fatigue testing indicates that each cycle’s maximum stress remains unchanged, but the stiffness degrades more rapidly with increasing recycled aggregate content and a constant w/c ratio.

The purpose of this study is to investigate factors influencing the Thai millennial consumers’ intention to purchase clothing and accessories made from recycled plastic. The research relied on deductive reasoning through hypothesis testing; Statistical measurements were employed. Consequently, a descriptive quantitative research approach was utilized to conduct the study. The data were collected physically and virtually via a web-based survey. A total number of 393 responses from Thai millennial consumers who live in Bangkok and its vicinity were analyzed with the application of structural equation modeling. The result demonstrates that environmental concern, attitude, and perceived behavioral control have a significant relationship on purchase intention of green apparel, shoes, and accessories made from recycled plastic. Environmental concern also positively mediates the green attitude and has a stronger correlation toward attitude than purchase intention. The subjective norm, on the other hand, shows no significance.

Currently in Iowa, the amount of RAP materials allowed for the surface layer is limited to 15% by weight. The objective of this project was to develop quality standards for inclusion of RAP content higher than 15% in asphalt mixtures. To meet Superpave mix design requirements, it was necessary to fractionate the RAP materials. Based on the extensive sieve-by-sieve analysis of RAP materials, the optimum sieve size to fractionate RAP materials was identified. To determine if the higher percentage of RAP materials than 15% can be used in Iowa's state highway, three test sections with 30.0%, 35.5% and 39.2% of RAP materials were constructed on Highway 6 in Iowa City. The construction of the field test sections was monitored and the cores were obtained to measure field densities of test sections. Field mixtures collected from test sections were compacted in the laboratory in order to test the moisture sensitivity using a Hamburg Wheel Tracking Device. The binder was extracted from the field mixtures with varying amounts of RAP materials and tested to determine the effects of RAP materials on the PG grade of a virgin binder. Field cores were taken from the various mix designs to determine the percent density of each test section. A condition survey of the test sections was then performed to evaluate the short-term performance.