Orientador: Roseana da E. Trevisan / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-13T23:31:13Z (GMT). No. of bitstreams: 1 Ventrella_VicenteAfonso_M.pdf: 3636995 bytes, checksum: 7db257d008cb3ca21b4394be2dd489da (MD5) Previous issue date: 1990 / Resumo: Este trabalho descreve o efeito da taxa de resfriamento na microestrutura do cordão de solda de chapas de aço inoxidável austenítico tipo 304, 304 L e 316 , com 3,0 mm de espessura. Foram enfatizados 3 aspectos (a) variação do teor de ferrita delta no cordão de solda em função das diferentes taxas de resfriamento ; (b) variação do teor de cromo e niquel nas fases ferrita e austenita, em função da taxa de resfriamento; (c ) alterações no Diagrama de Schaeffler com as diferentes taxas de resfriamento. O processo de soldagem utilizado foi o SATG Soldagem ao Arco Tungstênio em Atmosfera Gasosa)...Observação: O resumo, na íntegra, poderá ser visualizado no texto completo da tese digital / Abstract: This work describes the effect of cooling weld fillet microstructure of austenitic stainless type 304 , 304L and 316 , with 3,0 mm thickness. Three aspects have been emphasized (a) delta ferrite content variation on the weld fillet as a function of the differents cooling ratesi ( b ) Chromium and Nickel content variation on the ferrite and austenitic phases, as a function of the cooling rate ( c ) Schaeffler Diagram implications with the differents cooling rates. The TIG ( Tungsten Inert Gas ) process of welding was used ...Note: The complete abstract is available with the full electronic digital thesis or dissertations / Mestrado / Mestre em Engenharia Mecânica

Orientador : Kil Jin Park / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agricola / Made available in DSpace on 2018-07-31T16:41:17Z (GMT). No. of bitstreams: 1 Leite_JulianaPiresdeArruda_M.pdf: 2345729 bytes, checksum: a3bd853bbf7cdea9b85070edadc10cec (MD5) Previous issue date: 2001 / Mestrado

Orientador: Irenilza de Alencar Naas / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Agricola / Made available in DSpace on 2018-07-24T01:20:58Z (GMT). No. of bitstreams: 1 Silva_IranJoseOliveirada_D.pdf: 5956166 bytes, checksum: af1089b12544c480ead9889a5108739f (MD5) Previous issue date: 1998 / Doutorado / Construções Rurais e Ambiencia / Doutor em Engenharia Agrícola

Orientadores : Sergio Gama, Judit Zoltan Halasz / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia de Campinas / Made available in DSpace on 2018-07-16T21:38:51Z (GMT). No. of bitstreams: 1 Ordonez_JonhsonFrancisco_M.pdf: 1513568 bytes, checksum: a097d9b06c8f3c771775092a826e387b (MD5) Previous issue date: 1987 / Resumo: Os trocadores de calor criogênicos podem ser usados numa infinidade de sistemas onde devem-se promover trocas térmicas entre dois ou mais fluidos, a citar: Refrigeradores/Liquefatores de nitrogênio, h61io, hidrogênio, oxigênio, etc. Este trabalho consta, essencialmente, do dimensionamento, fabricação e testes de dois tipos de trocadores do calor usados em Refrigeradores/Liquefatores de ciclo Stirling: um trocador de calor compacto tipo casco-tubo o um trocador do calor regenerativo criogênicos. Na apresentação: 1) faz-se um esboço dos principais trocadores de calor usados em processos criogênicos; 2) apresenta-se os Refrigeradores/Liquefatores de ciclo Stirling; 3) finalmente, particulariza-se o dimensionamento, fabricação e tostes de dois tipos específicos de trocadores de calor para refrigeradoes criogênicos do ciclo Stirling: um trocador de calor regenerativo criogênicos, feito com 1g de cobre, e um trocador tipo casco-tubo do 11cm do diâmetro o 251 tubos de O,12cm do diâmetro / Abstract: Not informed / Mestrado / Mestre em Engenharia Mecânica

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Engenharia de Alimentos. / Made available in DSpace on 2012-10-23T01:06:09Z (GMT). No. of bitstreams: 1 242207.pdf: 1853347 bytes, checksum: aa703ff96302014a4ed3bea86a4d856e (MD5) / O resfriamento por imersão é um processo comumente utilizado para reduzir a temperatura de alimentos como carcaças de frango, frutas e hortaliças. Neste trabalho foram estudados alguns fatores que influenciam a evolução temporal da temperatura do centro do produto durante o resfriamento por imersão. Para a realização dos experimentos utilizou-se uma esfera maciça de alumínio como meio modelo. Os parâmetros avaliados foram a homogeneidade da agitação da água e as influências da intensidade (variando a vazão de ar comprimido injetado) e do modo (por bomba ou por bomba e ar, do próprio ambiente, para a recirculação da água) da agitação da água. O coeficiente médio de transferência de calor convectivo foi obtido por diferentes métodos: método da capacitância global, método analítico e método numérico. Também foi analisada a força resultante que age sobre a esfera devido a agitação promovida. Tentou-se correlacionar através de modelos logarítmicos a média e o desvio padrão da curva temporal da força resultante com o coeficiente médio de transferência de calor convectivo a fim de universalizar os resultados. O uso do método da capacitância global não se mostrou apropriado, pois não foi possível desprezar os gradientes internos de temperatura na esfera. Então, foram utilizados os métodos analítico e numérico para a determinação do coeficiente médio de transferência de calor convectivo, sendo que estes métodos não apresentaram diferença entre os resultados. O incremento da vazão de ar comprimido proporcionou menores tempos de resfriamento, ou seja, maior troca térmica entre o fluido e a superfície da esfera. Porém, o aumento da vazão de ar comprimido não é linearmente proporcional ao aumento do coeficiente médio de transferência de calor convectivo. O comportamento da curva de agitação versus h tende a uma assíntota, o que significa que em um determinado momento o aumento da agitação não mais proporcionará um aumento significativo no processo de troca térmica. Comparando as diferentes posições da esfera no tanque de imersão durante o resfriamento observou-se a existência de heterogeneidade na agitação. A generalização dos resultados, através de correlações entre o coeficiente convectivo médio de transferência de calor e valores da média e desvio padrão das curvas de força resultante, é bastante complexa, pois este coeficiente é influenciado por diversos fatores. Entretanto, um sistema de medição de força previamente calibrado pode fornecer bons resultados a respeito do processo de resfriamento sendo uma alternativa prática e rápida para ser utilizada em uma indústria. The immersion chilling is a process usually used to reduce foods temperatures as that of chicken carcasses, fruits and vegetables. In this work some factors that influence the temperature evolution of the product center during the immersion cooling was studied. To perform the experiments a massive aluminum sphere was used as model product. The evaluated parameters were the agitation homogeneity of the water and the influence of the intensity and the agitation mode over this parameter. The intensity was evaluated by varying the injected compressed air and the mode by pumping the water, first recirculating it with a simple pump and second by incorporating air by means of a Venturi device. The average convective heat transfer coefficient was obtained by different methods: lumped method, analytical method and numerical method. Also the resultant force that acts on the sphere due to the promoted agitation was analyzed. It was tried to correlate the average and the standard deviation of the resultant force curve with the average convective heat transfer coefficient through logarithmic models in order to universalize the results. The use of the lumped method was not appropriate, because it was no possible to disdain the internal temperature gradients in the sphere. The analytical and numerical methods were then tried to determine the average convective heat transfer coefficient. These methods had not presented difference between the results. The incrementation of the compressed air flow lead to minors cooling times, or either, greater thermal changes between the fluid and the sphere surface. However, the increase of the compressed air flow is not linearly proportional to the increase of the average convective heat transfer coefficient value. The behavior of the agitation curve versus h tends to an asymptote, which means that in one definite moment the agitation increase will not more provide a significant increase in the thermal exchange process. Comparing the different positions of the sphere in the immersion tank during the cooling it was observed the existence of heterogeneities in the agitation. The generalization of the results, through correlations between the average convective heat transfer coefficient and values of the average and standard deviation of the resultant force curves, is much more complex, because this coefficient is influenced by diverse other factors. However, a previously calibrated system of resultant force measurement can supply good results about the cooling process, being an practical and fast alternative to be used in industry.

Orientador: Roger Josef Zemp / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Química / Made available in DSpace on 2018-08-25T15:18:44Z (GMT). No. of bitstreams: 1 Silva_IgorMacieldeOliveirae_M.pdf: 2922871 bytes, checksum: 4b7ffbcbf31e3be71d4453d00d6c7592 (MD5) Previous issue date: 2014 / Resumo: Sistemas de água de resfriamento são o método mais comum de rejeição de calor na indústria. Sistemas convencionais de água de resfriamento recirculante possuem uma rede de trocadores de calor em uma configuração paralela, demandando grande quantidade de circulação de água e torres de resfriamento. Embora a reutilização de água de resfriamento reduza a quantidade de água que é necessária no sistema e aumente o desempenho e capacidade da torre de resfriamento, a queda de pressão na rede de trocadores de calor pode aumentar devido ao seu arranjo em série-paralelo. Este estudo introduz uma metodologia para projetar diferentes sistemas de água de resfriamento e para analisar os impactos da reutilização de água sobre a queda de pressão na rede de trocadores de calor e sobre a torre de resfriamento. A partir de um modelo de super-estrutura, utiliza-se um algoritmo combinatorial com o auxílio da ferramenta de otimização Solver do Microsoft Excel para resolver um problema não-linear (NLP) de cada estrutura de rede de trocadores de calor. A queda de pressão em redes de trocadores de calor é avaliada por uma metodologia baseada na Teoria dos Grafos e utiliza os algoritmos de ordenação por topologia e de caminho crítico. Utiliza-se o método de Merkel para modelar a altura de uma torre de resfriamento e poder avaliar o volume necessário de uma torre de resfriamento para cada rede de trocadores de calor. Um estudo de caso é utilizado para ilustrar cada passo a medida que a metodologia é desenvolvida, buscando prover fundamentos para um estágio conceitual durante o projeto de um sistema de água de resfriamento / Abstract: Cooling water systems are the most common method of waste heat disposal in industry. Conventional recirculating cooling water systems have a heat exchanger network in a parallel arrangement, demanding not only substantial cooling water flow, but also large cooling towers. Although cooling water reuse reduces the amount of water that is recirculated in the system, thereby increasing the cooling tower capacity and performance, the pressure drop in the heat exchanger network may significantly increase due to series-parallel arrangements. This study introduces a methodology to design different cooling water systems and to analyse the cooling water reuse impacts on the heat exchanger network pressure drop and on the cooling tower size. From a superstructure model, a combinatorial algorithm in conjunction with the optimisation tool Solver in Microsoft Excel is used to solve a non-linear problem for each heat exchanger network structure. Pressure drop in heat exchanger networks is evaluated by a methodology that is based on Graph Theory and that uses topological sorting and critical path algorithms. Merkel's method is used to model the cooling tower height and to assess the required cooling tower volume for each heat exchanger network. A case study is used to illustrate each step as the methodology is developed, aiming to provide a basis for a conceptual stage during the cooling water system design / Mestrado / Engenharia Química / Mestre em Engenharia Química

PINHEIRO, P. H. M. Efeitos da temperatura de interpasse sobre as alterações metalúrgicas e propriedades mecânicas de juntas dissimilares do aço ASTM A182-F22 soldadas com ligas de níquel . 2014. 137 f. Dissertação (Mestrado em Engenharia e Ciências de Materiais) - Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2014. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2015-02-20T17:50:03Z No. of bitstreams: 1 2014_dis_phmpinheiro.pdf: 6606451 bytes, checksum: 27345de923b0a80104c4cb60e1d51768 (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2015-02-24T16:26:23Z (GMT) No. of bitstreams: 1 2014_dis_phmpinheiro.pdf: 6606451 bytes, checksum: 27345de923b0a80104c4cb60e1d51768 (MD5) / Made available in DSpace on 2015-02-24T16:26:23Z (GMT). No. of bitstreams: 1 2014_dis_phmpinheiro.pdf: 6606451 bytes, checksum: 27345de923b0a80104c4cb60e1d51768 (MD5) Previous issue date: 2014-01-30 / Nickel alloys can be used to weld dissimilar joints of low alloy carbon steels. One of the purposes of this union is to avoid the formation of hydrogen induced cracking. According codes and standard there is a limitation that imposes the maximum interpass temperature at 150°C for welding using nickel alloys. However, the low interpass temperature reduces productivity and increases manufacturing costs. A study that evaluates effect of the preheating and interpass temperature of dissimilar welds on the metallurgical changes and mechanical properties is of great relevance. In this way, the general objective of this study is to assess the effect of interpass temperature on metallurgical changes and mechanical properties of dissimilar welded joints among ASTM A182-F22 steel and different nickel-based alloys. GMAW were carried out on joints of steel (ASTM A182-F22) using different nickel-based alloys as filler metal and different interpass temperatures (35°C, 150°C and 350°C). The heat input was kept constant (1.0 kJ/mm). Based on the results obtained it was observed that increasing preheating temperature there is a tends to reduce the precipitates content, because of dilution. The distribution coefficient of Mo and Nb decrease with the increase of iron content in the fusion zone, making stronger the segregation of these elements. Interpass temperature tend to reduce the HAZ hardness, due to the in cooling rate reduction caused by increase interpass temperature. In the tensile tests failure in the base metal. There was a reduction in yield strength for welds produced with 350°C preheat temperature, being a possible cause the precipitation of carbides due to preheating and multipasses. The Charpy-V tests indicated that, generally, the increase in interpass temperature reduced the toughness in the fusion zone. The absorbed energy by the interface dropped when interpass temperature increase. The welding time was considerably reduced with the interpass temperature increase, however, it should be to considerate changes in HAZ and fusion zone. / As ligas de níquel podem ser utilizadas na união de juntas dissimilares de aços carbono baixa liga. Uma das finalidades desta união é evitar a formação de trincas induzidas pelo hidrogênio. Existe uma limitação por norma que impõe a temperatura de interpasse máxima de 150°C para soldagem com ligas de níquel. Contudo, a temperatura de interpasse baixa reduz a produtividade e consequentemente aumenta os custos de fabricação. Um estudo que avalia como a temperatura de preaquecimento/interpasse na soldagem dissimilar influencia as alterações metalúrgicas e propriedades mecânicas é oportuno. Desta forma, o objetivo geral deste trabalho é avaliar o efeito do aumento da temperatura de interpasse nas alterações metalúrgicas e nas propriedades mecânicas de juntas dissimilares soldadas do aço ASTM A182-F22 com diferentes ligas de níquel. Foram realizadas soldagens MIG/MAG automática em juntas do aço (ASTM A182-F22) utilizando diferentes ligas de níquel como metal de adição e diferentes temperaturas de interpasse (35°C, 150°C e 350°C). A energia de soldagem foi mantida constante (1,0 kJ/mm). Baseado nos resultados obtidos o aumento da temperatura de preaquecimento tende a reduzir a fração de precipitados, decorrente do aumento da diluição. O coeficiente de distribuição do Mo e Nb diminuem com o aumento do teor de ferro na solda. Isto, por sua vez, torna mais forte a segregação destes elementos. A temperatura de interpasse tendeu a reduzir a dureza da (ZTA-GG), por conta da redução da velocidade de resfriamento. Nos ensaios de tração os corpos de prova romperam na região referente ao metal de base. Houve uma redução no limite de escoamento nas condições soldadas com temperatura de 350°C, sendo uma possível causa a precipitação de carbonetos devido ao preaquecimento e aos multipasses. Os ensaios de Charpy-V indicaram que, de uma forma geral, o aumento da temperatura de interpasse reduziu a tenacidade na zona fundida. A energia absorvida na interface sofreu redução com o aumento da temperatura de interpasse, decorrente do aumento da descarbonetação. O tempo de soldagem foi reduzido de forma considerável com o aumento de temperatura de interpasse, entretanto, deve-se avaliar as alterações na ZTA e ZF.

Made available in DSpace on 2014-06-11T19:35:41Z (GMT). No. of bitstreams: 0 Previous issue date: 2003Bitstream added on 2014-06-13T19:05:51Z : No. of bitstreams: 1 camargo_jr_dr_guara.pdf: 1019492 bytes, checksum: 2297d5279bcff4ccbedcb325ccb31939 (MD5) / O resfriamento evaporativo consiste na utilização da evaporação da água através da passagem de um fluxo de ar, provocando a redução na temperatura do ar e, apesar de utilizarem tecnologia relativamente simples, ainda são pouco utilizados para o condicionamento de ar em regiões de clima úmido. Este trabalho realiza um estudo dos potenciais e limitações de sistemas de condicionamento de ar por resfriamento evaporativo e evaporativo-adsortivo quando utilizados com o objetivo de propiciar conforto térmico ao homem e reduzir o consumo de energia. Apresenta-se, inicialmente, o princípio de funcionamento de sistemas de resfriamento evaporativo e de desumidificadores por adsorção. A seguir, apresentam-se os resultados dos ensaios de desempenho realizados em um resfriador evaporativo direto e propõe-se um novo sistema a ser utilizado em regiões em que as condições de conforto não podem ser supridas pelo resfriamento evaporativo somente. Estuda-se a aplicação desses sistemas a diversas cidades, caracterizadas por diferentes condições climáticas e conclui-se que os sistemas de resfriamento evaporativo acoplados a um desumidificador adsortivo apresentam perspectivas promissoras, principalmente para aplicação em condicionamento de ar onde existem fontes de calor de baixo custo ou calor residual disponível. A análise das condições do ar de insuflamento demonstra a viabilidade da utilização do sistema proposto para conforto térmico humano em regiões de clima úmido como uma alternativa aos sistemas convencionais de condicionamento de ar, poupando energia e protegendo o meio ambiente. / Evaporative cooling consists in using water evaporation through the passage of an air flow, thus decreasing the air temperature. In spite of using simple technology, it is seldon used for air conditioning in humid climate regions. This thesis develops a methodology that can be used to establish potentials and limitations of air conditioning systems by evaporative and desiccant cooling when used for human thermal comfort and lower power consumption. Firstly, the operational principles of evaporative cooling and dehumidification by adsorption systems are presented. Next, the results of performance tests developed on a direct evaporative cooler are described. Finally, a new system to be used in regions where the thermal comfort conditions cannot be supplied only by evaporative cooling is proposed. The applications of this system in several cities, characterized by different climate conditions are studied. It concluded that evaporative cooling systems coupled to a dehumidification adsorption system present promising perspectives, mainly to low cost air conditioning applications where residual heat sources are available. The analysis of the supply air conditions shows the feasibility of the proposed system for human thermal comfort in humid climates as an alternative to conventional air conditioning systems, saving energy and protecting the environment.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2017. / Submitted by Priscilla Sousa (priscillasousa@bce.unb.br) on 2017-10-06T14:44:17Z No. of bitstreams: 1 2017_AlencarCaldeiraCamposJúnior.pdf: 7370985 bytes, checksum: dda58dedd332ee584f61e054668dea1a (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2017-10-09T10:55:43Z (GMT) No. of bitstreams: 1 2017_AlencarCaldeiraCamposJúnior.pdf: 7370985 bytes, checksum: dda58dedd332ee584f61e054668dea1a (MD5) / Made available in DSpace on 2017-10-09T10:55:43Z (GMT). No. of bitstreams: 1 2017_AlencarCaldeiraCamposJúnior.pdf: 7370985 bytes, checksum: dda58dedd332ee584f61e054668dea1a (MD5) Previous issue date: 2017-10-09 / O presente trabalho, de cunho experimental, tem como objetivo investigar o processo de resfriamento em um componente eletrônico (célula Peltier) utilizando convecção forçada interna (tema 1), convecção forçada externa (tema 2) e convecção natural (tema 3). Para o primeiro tema, os testes foram realizados em uma célula Peltier (fonte de calor) encaixada em uma régua com e sem promotores de turbulência para velocidades variando de 3 a 15 m/s, abrangendo uma faixa de Reynolds entre 8140 e 40701. Os promotores de turbulência utilizados consistiam em arranjos de cilindros, em 6 configurações diferentes. Para o problema envolvendo convecção forçada externa foi desenvolvido um suporte possibilitando a variação do ângulo de ataque entre o componente aquecido e o escoamento de 0 a 90 graus em relação ao escoamento. Foram utilizadas as mesmas velocidades do primeiro problema. Já para o estudo de convecção natural foi utilizado o mesmo suporte da convecção forçada externa dentro de um cubo de acrílico com dimensões muito superiores as da célula Peltier. Os testes foram realizados para variação do ângulo de ataque entre 0 e 90 graus em relação a horizontal e utilizando 5 pares de tensões e correntes diferentes para alterar a temperatura da célula Peltier. A análise do processo de resfriamento para o tema 1 foi realizada da proposição de correlações Reynolds-Nusselt que representassem o efeito de novas geometrias configuracionais de promotores de turbulência. A mesma análise foi realizada para os testes do tema 2, porém com ênfase na influência do ângulo formado entre escoamento e componente aquecido nas taxas de troca de calor fluido-parede. A análise do tema 3 foi realizada através do número de Nusselt e do número de Rayleigh. Para o primeiro tema apresentamos os arranjos operacionais mais eficientes medidos do ponto de vista de maximização das taxas de troca de calor utilizando arranjos de promotores de turbulência. Para o Tema 2 foi observado que a configuração a 0 graus foi a que apresentou a maior transferência de calor para todos os números de Reynolds. Já para o tema 3 a configuração de 90 graus foi a que obteve um maior coeficiente de transferência de calor para todos os pares de tensão e corrente, e consequentemente maiores valores nos números de Nusselt. Todos os resultados obtidos são interpretados a luz de interpretações físicas baseadas na fenomenologia do escoamento e complementadas por análises de escala. / The experimental investigation presented is aimed on of the cooling process of an electronic component, represented by a Peltier cell. Such cooling is achieved via internal forced convection (first topic), external forced convection (second topic) and natural convection (third topic). Regarding the forced internal convection, measurements were made on a Peltier cell mounted on a rule with, and without, the turbulence promoters for incident flow velocities ranging from 3 to 15 m/s (8140 ≤ Re ≤ 40701). Such turbulence promoters consist in cylinders in six different arrangements. For the external forced convection an adaptive mount was employed, enabling the measurements on different attack angles between cell and flow direction ranging from 0 to 90 degrees. Same flow velocities applied to the internal convection were set to the external forced convection. Regarding the natural convection, measurements were made using the same setup employed on the external forced convection inside an acrylic cube much bigger than the Peltier cell. Natural convection investigations were conduced for different inclination angles 0 to 90 degrees on five different voltage and electric current intensities, resulting in 5 different temperatures on the Peltier cell. The cooling investigation conduced at the first topic was based on proposed Reynolds-Nusselt correlations, which represents the effect of different geometries of the turbulence promoters on the cooling process. A similar analysis was conduced on the second topic, although focused on the effect of the resultant angle on the heat transfer properties between the air and the cell. The analysis on the third topic was developed from the Nusselt and Rayleigh numbers. At the first topic, different arrangements are presented and a effectiveness evaluation is conduced, aimed on the optimization of the heat transfer properties for each arrangement. At the second topic it could be observed that the horizontal configuration resulted in a maximum heat transfer for all Reynolds numbers investigated. On the other hand, it was possible to measure a maximum heat transfer coefficient at the 90 degrees configuration, for all voltage-current intensity approached, resulting in higher Nusselt numbers measured. The obtained results are related to physical interpretations

Submitted by João Arthur Martins (joao.arthur@ufpe.br) on 2015-03-09T14:23:57Z No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertacao ER Final ABNT 2011.pdf: 6871278 bytes, checksum: 6ecbbeddc4e6910be616fbca6eefda32 (MD5) / Made available in DSpace on 2015-03-09T14:23:57Z (GMT). No. of bitstreams: 2 license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Dissertacao ER Final ABNT 2011.pdf: 6871278 bytes, checksum: 6ecbbeddc4e6910be616fbca6eefda32 (MD5) Previous issue date: 2012 / Este trabalho visa estudar o resfriamento de chapas metálicas soldadas através do uso de uma câmera termográfica. Foram utilizados seis painéis retangulares de aço ASTM A36 medindo 800 x 400 x 12,7 mm. Os painéis foram soldados manualmente na posição vertical ascendente, através de soldagem pelo processo arame tubular (FCAW-G). A velocidade média de alimentação do arame foi de 5 metros por minuto. O consumível utilizado foi o arame tubular Core 71 MB DG, diâmetro 1,2 mm. Os estudos para obtenção dos campos de temperatura foram realizados em duas etapas, mediante o uso de dois sistemas de instrumentação independentes: termopares e câmera termográfica. A primeira etapa coincide com o uso de ambos os sistemas de instrumentação instalada na face oposta à soldagem, quando então cinco termopares tipo K previamente calibrados norteiam as respostas dos campos de temperatura e em comparação, chega-se ao valor estatístico da emissividade. Nesta fase a temperatura captada na chapa atinge 712°C (≈ 985 K). A segunda etapa ocorreu na mesma face da soldagem sendo as temperaturas captadas apenas através da câmera termográfica, uma vez que a emissividade já havia sido corrigida. Os resultados mostram que a chapa alcança a temperatura de 1.237ºC (≈ 1.510 K), imediatamente após a execução da soldagem. Um dado importante que necessita ser bastante estudado trata-se da emissividade em medições com câmera infravermelha. Esse ponto foi bastante discutido no trabalho e uma curva de correção da emissividade de acordo com a temperatura é sugerida. Foram apresentadas várias imagens termométricas, algumas tridimensionais, representativas do perfil de temperatura na superfície da chapa soldada. Os resultados desse trabalho confirmam o potencial do uso da termocâmera em processos de soldagem para obter dados que confirmam os valores de importantes parâmetros que garantem a qualidade da junta soldada.