Made available in DSpace on 2014-06-11T19:24:43Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-08-06Bitstream added on 2014-06-13T19:31:37Z : No. of bitstreams: 1 000756934.pdf: 1452179 bytes, checksum: 821c01bc2b142723fd36a737540c3fc0 (MD5) / Este estudo teve como objetivo avaliar densidade de carga da produção de cavacos em função da granulometria de dois sistemas florestais de curta rotação de Eucalyptus urograndis. Um ensaio foi realizado em Botucatu- SP, o plantio da área em ocorreu em julho 2010, com espaçamento de 2,8 x 1,5 m, e com 30 meses a área foi colhida, com a utilização de uma carreta com células de carga e com volume conhecido e foi realizada pesagens para seis dimensões de cavacos (5 mm, 10 mm, 15 mm, 20 mm, 25 mm e 33 mm) tendo três repetições para cada, para poder determinar a densidade de carga. Em janeiro de 2010, foi implantado em Taiobeiras- MG, o outro ensaio, com os diferentes clones (I-144, I-224, I-042 e I-60) no espaçamento de 4,0 x 0,5 m com a finalidade de produção de bioenergia na forma cavacos de 33 mm. A colheita foi realizada com 37 meses, com uma carreta de volume conhecido e uma balança rodoviária para determinar a densidade de carga. Para os dois ensaios foi utilizado o mesmo sistema mecanizado específico para produção de cavaco. Os resultados foram analisados pela análise de variância e, posteriormente, teste de Tukey. Concluindo que quanto maior dimensão dos cavacos menor a densidade de carga e que numa mesma situação para diferentes clones da mesma espécie de eucalipto se encontra diferentes valores de densidade de carga / This study aimed to evaluate the bulk density of a wood chip production as a function of particle size of two short forestry rotation system of Eucalyptus urograndis. One trial was conducted in Botucatu-SP, the planting area occurred in July 2010, with spacing of 2.8 x 1.5 m, and within 30 months the area was harvested with the use of a trailer with load cells and known volume, and was weighing carried out for six dimensions chip (5 mm, 10 mm, 15 mm, 20 mm, 25 mm and 33 mm) with three replicates for each, in order to determine the bulk density. In January 2010, it was deployed in Taiobeiras-MG, the second test, with different clones (I-144, I-224, I-042 and I-60) at a spacing of 4.0 x 0.5 m with purpose of bioenergy production in 3 the form of 33 mm wood chips. The harvest was performed 37 months, with a cartload of known volume and scale road to determine the bulk density. For both tests the same specific mechanical system was used to produce chip. The results were analyzed by analysis of variance and then the Tukey test. In conclusion that the larger dimension of the wood chips minus the bulk density and in the same situation for different clones of the same species of eucalyptus is different values of bulk density.

Orientador : Antonio Salvio Mangrich / Co-orientador : Fábio Simonelli / Tese (doutorado) - Universidade Federal do Paraná / Resumo: A caracterização química de substâncias húmicas (SH) é uma importante etapa na compreensão do processo de humificação. A despeito de seu papel imprescindível na sustentabilidade da vida, a natureza química e a reatividade das SH são ainda pouco conhecidas. SH são misturas originadas da degradação de restos vegetais, do metabolismocatabolismo microbiano, ou de ambos processos. A compostagem é um processo bioxidativo de tratamento de resíduos orgânicos que, sob condições controladas, pode servir para o estudo químico detalhado do processo de humificação e da formação de SH, propiciando a formação de um húmus menos heterogéneo e a partir de materiais de partida bem caracterizados quimicamente. O objetivo deste trabalho foi estudar as alterações químicas ocorridas no material durante a compostagem da mistura de serragem de Pinns taeda e lodo biológico de fábrica de celulose de Pinns. Este material foi usado para estudar o processo de humificação, através da caracterizaçãoespectroscópica e de cromatografia de exclusão por tamanho das fiações húmicas. Os resultados mostraram que o húmus produzido gerou SH de tamanho molecular entre 800 e 12000 Da, ricos em grupos oxigenados (carboxilas e fenóis), em complexos metálicos de ferro, cobre e manganês e em radicais livres orgânicos. A variação do tamanho dos agregados durante a compostagem s e relacionou a aspectos como aeração e relação O/C. O índice de oxidação das estruturas parece reger estas relações. Em húmus "jovens", a fiação fulvica parece ser especialmente afetada por estas relações. O modelo clássico de descrição das SH como macromoléculas poliméricas não explica os resultados obtidos neste trabalho. Estes resultados parecem concordar com a descrição das SH como associações supramoleculares de moléculas relativamente pequenas, unidas por forças fracas em sistema de "self-assembly", ao invés da descrição destas substâncias como macromoléculas. Forças atrativas hidrófobas e ligações de hidrogénio parecem reger os processos de agregação em soluções diluídas, resultando em agregados de tamanhos moleculares maiores, com o aumento da concentração. A repulsão eletrostática predominante quando um limite crítico de concentração é ultrapassado, faz com que os tamanhos dos agregados moleculares se tornem menores. A interação das SH com espécies anfifílicas tais como ácidos orgânicos, parece atuar especialmente desta forma. / Abstract: The chemical characterization of humic substances (HS) is an important step to understand the humification process. Despite their role in the sustainability of life, the basic chemical nature and reactivity of HS are still poorly understood. HS are mixtures developed from plant and animal decays, from microbial metabolism-catabolism, or from both. Composting is a bioxidative process of organic wastes treatment, which could be used, under specified conditions, for H S formation s tudies, s ince i t i s possible t o o btain homogeneous and well chemical well-defined materials. The aim of this work was to study the chemical alterations during the composting of Pinus taeda sawdust and paper mill sludge. The humic fractions obtained from compost were studied by using spectroscopic techniques (EPR, DRIFT, UV-vis and NMR) and sizeexclusion chromatography. The results show that the humus compost formed HS with molecular size between 800 and 12000 Da, rich in oxygenated groups as carboxyl and phenols, in metallic complex as iron, copper and manganese, and in free organic radicals. The molecular size variation of the humic aggregates from compost was correlated with O/C ratio and aeration. In fresh humus, fixlvic fraction seems to be specially affected by this parameters. Such results would have been difficult to explain based on the polymeric description of humic substances. Conversely, our findings can be easily explained on the basis of the supramolecular understanding of humic substances that describes these natural materials as heterogeneous and rather small molecules associated by dispersive forces in supramolecular structures. Hydrophobic forces (%-n, CH-71, van der Waals, charge-transfer bonds) and H-bondings seems to rule the aggregation process in diluted solutions, resulting in greater aggregates with the increase of concentration. Electrostatic repulsion predominates when a critical concentration limit is exceeded and as a result, the molecular size becomes smaller. Humic superaggregates interactions with amphiphilic species as organic acids seems might to have such behavior.

Orientador: Saulo Philipe Sebastião Guerra / Coorientador: José Mauro Santana da Silva / Banca: Fabio Minoru Yamaji / Banca: Franciane Andrade de Pádua / Resumo: Este estudo teve como objetivo avaliar densidade de carga da produção de cavacos em função da granulometria de dois sistemas florestais de curta rotação de Eucalyptus urograndis. Um ensaio foi realizado em Botucatu- SP, o plantio da área em ocorreu em julho 2010, com espaçamento de 2,8 x 1,5 m, e com 30 meses a área foi colhida, com a utilização de uma carreta com células de carga e com volume conhecido e foi realizada pesagens para seis dimensões de cavacos (5 mm, 10 mm, 15 mm, 20 mm, 25 mm e 33 mm) tendo três repetições para cada, para poder determinar a densidade de carga. Em janeiro de 2010, foi implantado em Taiobeiras- MG, o outro ensaio, com os diferentes clones (I-144, I-224, I-042 e I-60) no espaçamento de 4,0 x 0,5 m com a finalidade de produção de bioenergia na forma cavacos de 33 mm. A colheita foi realizada com 37 meses, com uma carreta de volume conhecido e uma balança rodoviária para determinar a densidade de carga. Para os dois ensaios foi utilizado o mesmo sistema mecanizado específico para produção de cavaco. Os resultados foram analisados pela análise de variância e, posteriormente, teste de Tukey. Concluindo que quanto maior dimensão dos cavacos menor a densidade de carga e que numa mesma situação para diferentes clones da mesma espécie de eucalipto se encontra diferentes valores de densidade de carga / Abstract: This study aimed to evaluate the bulk density of a wood chip production as a function of particle size of two short forestry rotation system of Eucalyptus urograndis. One trial was conducted in Botucatu-SP, the planting area occurred in July 2010, with spacing of 2.8 x 1.5 m, and within 30 months the area was harvested with the use of a trailer with load cells and known volume, and was weighing carried out for six dimensions chip (5 mm, 10 mm, 15 mm, 20 mm, 25 mm and 33 mm) with three replicates for each, in order to determine the bulk density. In January 2010, it was deployed in Taiobeiras-MG, the second test, with different clones (I-144, I-224, I-042 and I-60) at a spacing of 4.0 x 0.5 m with purpose of bioenergy production in 3 the form of 33 mm wood chips. The harvest was performed 37 months, with a cartload of known volume and scale road to determine the bulk density. For both tests the same specific mechanical system was used to produce chip. The results were analyzed by analysis of variance and then the Tukey test. In conclusion that the larger dimension of the wood chips minus the bulk density and in the same situation for different clones of the same species of eucalyptus is different values of bulk density. / Mestre

Orientador: Cláudio Angeli Sansígolo / Banca: Elias Taylor Durgante Severo / Banca: Gustavo Ventorim / Resumo: A celulose de fibra curta branqueada produzida no Brasil é toda proveniente de madeira de florestas de Eucalyptus spp. A qualidade dos cavacos usados na produção de celulose é considerada um fator importante para operabilidade da indústria e para a qualidade da polpa. Os cavacos desejáveis são aqueles que apresentam poucas variações nas características físicas e químicas, isentos de contaminantes, alta densidade a granel, impregnação homogênea, baixa degradação de polissacarídeos e alto rendimento na transformação em polpa celulósica. Na indústria a classificação do tamanho dos cavacos passou a ser adotada depois que estudos demonstraram que os cavacos muito grandes e/ou muito pequenos poderiam interferir no processo de deslignificação e na qualidade da polpa celulósica, mas os cavacos utilizados pela indústria ainda apresentam variações no tamanho depois da classificação industrial. O objetivo do estudo foi identificar nos cavacos classificados industrialmente, dimensões que favoreçam ou desfavorecem o processo de deslignificação e a resistência da polpa. Para tanto, foi coletada uma amostra de cavacos em uma indústria de celulose, a amostra foi separada em sete frações, e mensurada às dimensões (comprimento, largura e espessura), determinado à densidade básica, densidade a granel, e composição química dos cavacos. As frações também foram deslignificadas e determinado o rendimento bruto, rendimento depurado, rejeitos base celulose, rejeitos base madeira e o número Kappa da polpa marrom. As fibras dos cavacos grande e pequenos foram classificadas pelo comprimento, e determinado algumas características físico-mecânicas da celulose. As dimensões dos cavacos variaram entre as frações, houve aumento do teor de holocelulose nas duas frações com as menores dimensões dos... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Bleached hardwood pulp produced in Brazil is entirely from wood of Eucalyptus spp forests. The quality of the chips used in pulp production is considered an important factor in the industry operability and the pulp quality. Desirable chips have few variations of physical and chemical characteristics are free of contaminants, and present high bulk density, homogeneous uptake, low degradation of polysaccharides and high milling yield in kraft pulp. In manufacturing, the chip size classification has been adopted after studies have shown that very large and / or very little chips could interfere in the delignification process and pulp quality; however, the chips used by the industry still vary in size after industrial grading. The aim of this study was to identify, among the industrially classified chips, dimensions that favor or not the delignification process and pulp strength. Thus, a chip sample was collected in a pulp mill, then the chips were separated into seven fractions and their dimensions (length, width and thickness) were measured, and the chip basic density, bulk density, chemical composition were determined. The chips were also delignified, and the total yield, screening yield, pulp-based wastes, wood- based wastes, and Kappa number of unbleached pulp were determined. The fibers of large and small chips were classified by length, and some physical and mechanical properties of cellulose were determined. The chip dimensions varied among fractions, and there was an increase of holocellulose content in the two fractions that had the smallest chips. The total yield, screening yield, and pulp-based waste content did not differ significantly, but, when the chip size dimension decreased, the waste content and kappa number were likely to reduce and the specific wood use was likely to increase. The fiber length... (Complete abstract click electronic access below) / Mestre

Made available in DSpace on 2014-06-11T19:30:20Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-08-15Bitstream added on 2014-06-13T19:00:14Z : No. of bitstreams: 1 grande_jp_me_botfca.pdf: 868693 bytes, checksum: 1b60e7dad21aa293ae0a9ac74ced70cc (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / A celulose de fibra curta branqueada produzida no Brasil é toda proveniente de madeira de florestas de Eucalyptus spp. A qualidade dos cavacos usados na produção de celulose é considerada um fator importante para operabilidade da indústria e para a qualidade da polpa. Os cavacos desejáveis são aqueles que apresentam poucas variações nas características físicas e químicas, isentos de contaminantes, alta densidade a granel, impregnação homogênea, baixa degradação de polissacarídeos e alto rendimento na transformação em polpa celulósica. Na indústria a classificação do tamanho dos cavacos passou a ser adotada depois que estudos demonstraram que os cavacos muito grandes e/ou muito pequenos poderiam interferir no processo de deslignificação e na qualidade da polpa celulósica, mas os cavacos utilizados pela indústria ainda apresentam variações no tamanho depois da classificação industrial. O objetivo do estudo foi identificar nos cavacos classificados industrialmente, dimensões que favoreçam ou desfavorecem o processo de deslignificação e a resistência da polpa. Para tanto, foi coletada uma amostra de cavacos em uma indústria de celulose, a amostra foi separada em sete frações, e mensurada às dimensões (comprimento, largura e espessura), determinado à densidade básica, densidade a granel, e composição química dos cavacos. As frações também foram deslignificadas e determinado o rendimento bruto, rendimento depurado, rejeitos base celulose, rejeitos base madeira e o número Kappa da polpa marrom. As fibras dos cavacos grande e pequenos foram classificadas pelo comprimento, e determinado algumas características físico-mecânicas da celulose. As dimensões dos cavacos variaram entre as frações, houve aumento do teor de holocelulose nas duas frações com as menores dimensões dos... / Bleached hardwood pulp produced in Brazil is entirely from wood of Eucalyptus spp forests. The quality of the chips used in pulp production is considered an important factor in the industry operability and the pulp quality. Desirable chips have few variations of physical and chemical characteristics are free of contaminants, and present high bulk density, homogeneous uptake, low degradation of polysaccharides and high milling yield in kraft pulp. In manufacturing, the chip size classification has been adopted after studies have shown that very large and / or very little chips could interfere in the delignification process and pulp quality; however, the chips used by the industry still vary in size after industrial grading. The aim of this study was to identify, among the industrially classified chips, dimensions that favor or not the delignification process and pulp strength. Thus, a chip sample was collected in a pulp mill, then the chips were separated into seven fractions and their dimensions (length, width and thickness) were measured, and the chip basic density, bulk density, chemical composition were determined. The chips were also delignified, and the total yield, screening yield, pulp-based wastes, wood- based wastes, and Kappa number of unbleached pulp were determined. The fibers of large and small chips were classified by length, and some physical and mechanical properties of cellulose were determined. The chip dimensions varied among fractions, and there was an increase of holocellulose content in the two fractions that had the smallest chips. The total yield, screening yield, and pulp-based waste content did not differ significantly, but, when the chip size dimension decreased, the waste content and kappa number were likely to reduce and the specific wood use was likely to increase. The fiber length... (Complete abstract click electronic access below)