Weathering steel has been a primary construction material for bridges in the United States. Notches caused by corrosion are observed on the flange of steel I-beams. These notches reduce the cross section area of the structure and are threats to bridge safety. A606-04 Type 4 cold rolled weathering steel samples were studied in this thesis to understand the effect of notches that caused by corrosion. Weathering steel samples were in the shape of plates, which simulated flange of I-beams. The plate samples were notched across their surfaces by applying electrical current through an electrochemical circuit composed of an anode, a cathode and electrolyte. Sixteen samples were notched and cut into appropriate shape for fatigue testing. S-N (Stress-Number of cycles to failure) diagram established from fatigue data indicated that the fatigue strength decreased below AASHTO category B. Weibull analysis was also performed to understand the reliability distribution. / Includes bibliography. / Thesis (M.S.)--Florida Atlantic University, 2014. / FAU Electronic Theses and Dissertations Collection

Two duplex stainless steels rebars: UNS32304SS and UNS32101SS, were selected to investigate the corrosion initiation and propagation in reinforced concrete specimens. The investigation is divided in two phases with two different methods to accelerate the transport of chlorides through the concrete and initiate corrosion in a short period of time. After corrosion had initiated and propagated for some time; selected specimens were terminated for visual examination. On specimens selected for autopsy, the rebars in the top row showed corrosion to various degrees. Corrosion had propagated to such extent on the terminated specimens that the specimen showed cracks. Stray current might have caused accelerated corrosion on rebars where corrosion had initiated. Based on chloride concentrations measured at the rebar trace, corrosion initiated: on S32101 rebars on average at 7.9 kg/m3, and S32101 rebars on average at 6.0 kg/m3. The findings suggest that S32304 rebars corroded at a slower than S32101. / by Francisco Gutierrez Tellez. / Thesis (M.S.C.S.)--Florida Atlantic University, 2013. / Includes bibliography. / Mode of access: World Wide Web. / System requirements: Adobe Reader.