Made available in DSpace on 2015-05-14T13:21:25Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 8077133 bytes, checksum: 30c8277061aca1c53f3eb1e59e831b55 (MD5) Previous issue date: 2013-02-18 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Strontium stannate, SrSnO3, is a perovskite wile orthorhombic structure which has interesting dielectric properties, besides several technological applications such as catalysis of nitrogen oxides. In this work, SrSnO3, SrSn0,9Fe0,1O3-x and Sr0,9Sn0,9Fe0,1O3-x were obtained by the polymeric precursor method using metallic tin as precursor (Sn0) and were deposited on commercial catalytic supports (CeO2, TiO2, -Al2O3 and ZrO2) for application as catalysts in the reaction of reduction of NO with CO. The catalysts were characterized by thermogravimetric analysis (TG / DTA), Xray diffraction (XRD), ultraviolet-visible spectroscopy (UV-Vis), infrared spectroscopy (IR), Raman spectroscopy, analysis of the surface area by the BET method and scanning electron microscopy with field emission (FE-SEM). The catalytic tests were conducted in a reactor with gas mixture containing stoichiometric quantities of nitrogen monoxide (NO) and carbon monoxide (CO), in helium, in the temperature range from 300 °C to 700 °C. The XRD results showed that the perovskite had a high long-range order, and low amount of secondary phase (SrCO3). The IR spectra confirmed these data by presenting a reduction of vibration bands related to carbonates groups. The Raman spectra and the calculation of the inclination angles among the octahedra indicated a short range disorder. The deposition of perovskite on the supports presented good dispersion. The catalytic tests showed that the perovskite doped with iron showed the best percentage of conversion of NO and CO. The perovskite deposited on the ZrO2 showed the best catalytic conversion. / O estanato de estrôncio, SrSnO3, é uma perovskita do tipo ortorrômbica que apresenta propriedades dielétricas interessantes, além de várias aplicações tecnológicas, tais como catálise de óxidos de nitrogênio. Neste trabalho, SrSnO3, SrSn0,9Fe0,1O3-x e Sr0,9Sn0,9Fe0,1O3-x foram obtidos pelo método dos precursores poliméricos utilizando estanho metálico como precursor (Sn0) e depositados sobre suportes catalíticos comerciais (CeO2, TiO2, γ-Al2O3 e ZrO2) para aplicação como catalisadores na reação de redução de NO com CO. Os catalisadores foram caracterizados por análise termogravimétrica (TG/DTA), difração de raios-X (DRX), espectroscopia de absorção na região do ultravioleta e do visível (UV-Vis), espectroscopia vibracional na região do infravermelho (IV), espectroscopia Raman, análise da área superficial pelo método de BET e microscopia eletrônica de varredura com emissão de campo (MEV-EC). Os testes catalíticos foram realizados em um reator contendo mistura gasosa com quantidades estequiométricas de monóxido de nitrogênio (NO) e monóxido de carbono (CO) em hélio na faixa de temperatura de 300°C a 700°C. Os resultados de DRX mostraram que as perovskitas apresentaram uma alta organização a longo alcance, e diminuição de fase secundária (SrCO3). Os espectros de IV confirmaram estes dados ao apresentarem uma redução das bandas referentes às vibrações de grupos carbonatos. Os resultados de Raman e o cálculo dos ângulos de inclinação entre os octaedros indicaram uma desorganização a curto alcance. As perovskitas depositadas sobre os suportes apresentaram uma boa dispersão. Os testes catalíticos mostraram que as perovskitas dopadas com ferro apresentaram os melhores percentuais de conversão de NO e CO. As perovskitas depositadas sobre o suporte ZrO2 mostraram os melhores valores de conversão catalítica.

Submitted by Ana Hilda Fonseca (anahilda@ufba.br) on 2016-04-26T17:56:02Z No. of bitstreams: 1 TESE RAMOS, M S.pdf: 2946477 bytes, checksum: 8026fd4ce243b1a078f0ecbe41882b0e (MD5) / Approved for entry into archive by Ana Hilda Fonseca (anahilda@ufba.br) on 2016-05-12T15:38:08Z (GMT) No. of bitstreams: 1 TESE RAMOS, M S.pdf: 2946477 bytes, checksum: 8026fd4ce243b1a078f0ecbe41882b0e (MD5) / Made available in DSpace on 2016-05-12T15:38:09Z (GMT). No. of bitstreams: 1 TESE RAMOS, M S.pdf: 2946477 bytes, checksum: 8026fd4ce243b1a078f0ecbe41882b0e (MD5) / FAPESB e CNPq / Devido à crescente demanda pela diminuição dos custos de obtenção de produtos de alto valor comercial, bem como pela preservação do meio ambiente, diversos estudos têm sido conduzidos visando ao aproveitamento de resíduos de diversas origens, que são acumulados no meio ambiente. Neste contexto estudou-se, neste trabalho, a preparação de carvões ativados, a partir de resíduos industriais (resinas sulfônicas exauridas) e de mesocarpo do coco, com a finalidade de empregá-los como adsorventes, catalisadores ou suportes catalíticos. Para fins de comparação, uma resina sulfônica preparada em laboratório e a resina sulfônica comercial nova foram incluídas no estudo. Em todos os casos, foi empregado o copolímero estireno- divinilbenzeno. Os carvões ativados, obtidos a partir do copolímero, foram preparados através das etapas de calcinação (250 ºC), carbonização (900 ºC), ativação física com vapor d´água (800 ºC) e funcionalização (800 ºC), enquanto os carvões ativados preparados a partir do mesocarpo do coco verde foram carbonizados e ativados físicamente (em uma única etapa) com vapor d’água e funcionalizados, em diferentes temperaturas (600 e 800 ºC). As amostras foram caracterizadas por termogravimetria, análise térmica diferencial, difração de raios X, medida da área superficial específica e porosidade, redução termoprogramada, espectroscopia de infravermelho com transformada de Fourier, microscopia eletrônica de varredura e espectroscopia Raman. Todas as amostras, obtidas a partir do copolímero, foram sólidos macroporosos contendo mesoporos e microporos e com áreas superficiais específicas elevadas, que variaram com a origem do copolímero e com os tratamentos ao longo do processo de síntese. A desordem estrutural dos carvões também variou com esses parâmetros. Em todos os casos, foram observados grupos fenólicos, carboxílicos, éster, quinonas e carbonatos. Os carvões ativados e/ou funcionalizados obtidos a partir do copolímero sintetizado em laboratório apresentaram os mais altos valores de área superficial específica (753 m2 g-1). No caso dos sólidos obtidos a partir do mesocarpo de coco verde, foram obtidos sólidos mesoporosos contendo microporos, com altas áreas superficiais específicas e com elevada organização estrutural, que variaram com os sucessivos tratamentos térmicos. O valor de área superficial específica mais elevado foi apresentado pelo carvão ativado e funcionalizado a 800 oC (527 m2 g-1). Comparando-se os carvões ativados e funcionalizados, obtidos a partir dos diferentes resíduos (resina polimérica e mesocarpo do coco), conclui-se que ambos são adequados para a obtenção de carvões ativados para emprego como adsorventes, catalisadores ou suportes catalíticos. Ambos produzem carvões ativados com áreas superficiais específicas elevadas (superiores a 527 m2 g-1) e com porosidade desenvolvida, formada por mesoporos e microporos. Dessa forma, o emprego desses materiais pode reduzir os custos de produção do carvão ativado e contribuir para a preservação do meio ambiente, pela diminuição de resíduos industriais e da agricultura, muitas vezes dispostos de forma indiscriminada. / Due to increasing demand for lower costs of obtaining products of high commercial value, as well as the preservation of the environment, many studies have been carried out addressed to the use of waste from various sources, which are accumulated in the environment. In this context, the preparation of activated carbons from industrial waste (exhausted sulfonic resins) and mesocarp of coconut was studied in this work, aiming to use them as adsorbents, catalysts or catalyst supports. For purposes of comparison, a sulfone resin prepared in the laboratory and a new commercial sulfonic resin were included in the study. For all cases, a styrene- divinylbenzene copolymer was used. The activated charcoals obtained from the copolymer were prepared through the steps of calcination (250 °C) carbonization (900 °C), physical activation using water vapor (800 °C) and functionalization (800 °C), while activated carbons prepared from the mesocarp of the coconut were carbonized and activated physically (in one step) with steam and functionalized at different temperatures (600 and 800 °C). The samples were characterized by thermogravimetry, differential thermal analysis, X-ray diffraction, specific surface area and porosity measurement, thermoprogrammed reduction, Fourier transform infrared spectroscopy, scanning electron microscopy and Raman spectroscopy. All samples obtained from the copolymer solids were macroporous containing mesopores and micropores and with high specific surface areas, which varied with the source of the copolymer and the treatments throughout the synthesis process. The structural disorder of activated carbons also varied with these parameters. For all cases, phenolic, carboxyl, ester, carbonate and quinones groups were observed. The activated carbons and / or functionalized obtained from the copolymer synthesized in the laboratory showed the highest values of specific surface area (753 m2 g-1). For solids obtained from coconut mesocarp mesoporous solids containing microporous materials with high specific surface areas and high structural organization, which varied with the successive heat treatments, were obtained. The value of the highest specific surface area was shown by the activated carbon functionalized at 800 oC (527 m2 g-1). Comparing the functionalized and activated carbons obtained through different residues (polymeric resin and coconut mesocarp), it can be concluded that both are suitable for obtaining activated carbons for use as adsorbents, catalysts or catalyst supports. Both produce activated carbons with high specific surface areas (higher than 527 m2 g-1) and developed porosity, formed by mesopores and micropores. Thus, the use of these materials can reduce the cost of production of activated carbon and contribute to preserve the environment by decreasing industrial and agriculture wastes, often indiscriminately disposed in i

Submitted by Maike Costa (maiksebas@gmail.com) on 2017-06-20T14:18:13Z No. of bitstreams: 1 arquivototal.pdf: 7366953 bytes, checksum: e2858ff3ade34aa9cdf821b90999c936 (MD5) / Made available in DSpace on 2017-06-20T14:18:13Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 7366953 bytes, checksum: e2858ff3ade34aa9cdf821b90999c936 (MD5) Previous issue date: 2017-04-28 / Calcium stannate, CaSnO3, is orthorhombic perovskite-type that presents technological applications as catalysts and photocatalysts. In this work, undoped CaSnO3 and doped with Fe3+, Co2+ or Cu2+ were obtained by the modified Pechini method and applied in photodegradation of the textile dye Remazol Golden Yellow and as catalysts in the reduction reaction of nitrogen monoxide (NO). Furthermore, these materials were deposited on the ZrO2 support or Pd2+-doped or Pd impregnated and evaluated in the reduction of NO with CO and NO with NH3. The catalysts were characterized by thermogravimetric analysis (TG/DTA), X-ray diffraction (XRD), ultraviolet-visible spectroscopy (UV-Vis), infrared spectroscopy (IR), Raman spectroscopy, analysis of the surface area by the BET method, scanning electron microscopy with field emission (FE-SEM) and transmission electron microscopy (TEM). XRD patterns showed a small change in the long range-order for the doped samples due to partial substitution of cations. The Raman spectra indicated that the incorporation of Fe3+, Co2+ and Cu2+ in the CaSnO3 lattice promoted a symmetry breaking, which was confirmed by the change of the band gap values of the samples. The photocatalytic tests of RNL dye were performed in the reactor using a UVC lamp (λ = 254 nm). The catalytic tests were carried out in a reactor containing a gaseous mixture with stoichiometric amounts of nitrogen monoxide (NO) and carbon monoxide (CO) in helium in the temperature range of 300 °C to 700 °C or in a reactor containing a mixture of NO and ammonia (NH3) in helium in the temperature range of 250 °C to 500 °C. The results of the photocatalytic evaluation showed that CaSnO3 doping with transition metals increased the photocatalytic efficiency of the material, especially for the Cu2+ (76% of discoloration), which was related to the while the decrease in the intensity of the photoluminescence spectrum as a function of doping. The catalytic tests of NO with CO showed that Co2+ and Cu2+-doped perovskites showed 100% of conversion, at temperatures above 500ºC. The palladium impregnation promoted the conversion of NO with CO throughout the evaluated temperature range, but it did not favor the reaction of NO with NH3, probably due to the oxidation of NH3 by Pd. The perovskite deposited on the ZrO2 support showed the best catalytic conversion values. The results of FEG and TEM confirmed the deposition of the active phase on the ZrO2 support and indicated the formation of core@shell systems. / Estanato de cálcio, CaSnO3, é uma perovskita do tipo ortorrômbica que apresenta aplicações tecnológicas como catalisadores e fotocatalisadores. Neste trabalho, CaSnO3 não dopado e dopado com Fe3+, Co2+ ou Cu2+ foram obtidos pelo método Pechini-modificado e aplicados na fotodegradação do corante têxtil remazol amarelo ouro (RNL), e como catalisadores na reação de redução de monóxido de nitrogênio (NO). Além disso, esses materiais foram depositados sobre o suporte catalítico ZrO2 ou impregnados ou dopados com paládio e avaliados na redução de NO com CO e NO com NH3. Os catalisadores foram caracterizados por análise termogravimétrica (TG/DTA), difração de raios-X (DRX), espectroscopia de absorção na região do ultravioleta e do visível (UV-Vis), espectroscopia vibracional na região do infravermelho (IV), espectroscopia Raman, análise da área superficial (SBET), microscopia eletrônica de varredura com emissão de campo (MEV-EC) e microscopia eletrônica de transmissão (MET). Os resultados de DRX mostraram uma pequena mudança na ordem a longo alcance das amostras dopadas devido à substituição parcial dos cátions. Os espectros Raman indicaram que a incorporação dos metais Fe3+, Co2+ e Cu2+ na rede do CaSnO3 promoveu quebra de simetria, o que foi confirmado pela mudança nos valores do band gap das amostras. Os ensaios fotocatalíticos do corante RNL foram realizados em reator utilizando uma lâmpada UVC (λ= 254 nm). Por sua vez, os testes catalíticos foram realizados em um reator contendo uma mistura gasosa, com quantidades estequiométricas de monóxido de nitrogênio (NO) e monóxido de carbono (CO), em hélio, na faixa de temperatura de 300°C a 700°C ou em um reator contendo mistura de NO e amônia (NH3), em hélio, na faixa de temperatura de 250°C a 500°C. Os resultados da avaliação fotocatalítica mostraram que a dopagem do CaSnO3 com os metais de transição aumentou a eficiência fotocatalítica do material, sendo mais expressiva para o material dopado com Cu2+ (76% de descoloração), o que foi relacionado à diminuição na intensidade dos espectros de fotoluminescência em função da dopagem. Os testes catalíticos de NO com CO mostraram que as perovskitas mássicas dopadas com Co2+ e Cu2+ apresentaram 100% de conversão, em temperaturas superiores a 500ºC. A impregnação com paládio favoreceu a conversão de NO com CO em toda a faixa de temperatura avaliada, no entanto, desfavoreceu a reação de NO com NH3, provavelmente devido à oxidação de NH3 pelo Pd. As perovskitas depositadas sobre o suporte ZrO2 mostraram os melhores valores de conversão catalítica. Os resultados de MEV-EC e MET confirmaram a deposição da fase ativa sobre o suporte ZrO2 e indicaram a formação de sistemas core@shell.