Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / This work investigated the effect of different types of homogenization on the microstructure and the cold deformation behavior of Ti-35Nb-0,15Si alloy. Homogenization was performed under two conditions. Condition 1: treatment in ambient air at 1000 °C for 8, 24, 48, 72, 96 and 120 hours. Condition 2: treatment in argon atmosphere at 1000 °C for 8 hours. For the cold deformation study samples of the Ti-35Nb-0,15Si alloy and samples of Ti CP were deformed by ECAP with up to 8 passes, using the routes A and BC in a matrix with angle of intersection between the channels of Φ = 120º. The microstructural characterization was performed in the internal and external regions with the aid of optical microscopy, scanning electron microscopy and X-ray diffractograms. Vickers microhardness measurements were performed to evaluate the changes caused by deformation. In the ambient air atmosphere the samples showed the presence of the oxide layer influencing the hardness and the level of cold deformation. With the deformation of Ti-35Nb-0,15Si by ECAP it was possible to refine the structure and increase the hardness with increasing the number of passes. XRD analysis showed the presence of the α” phase induced by deformation. With the Ti CP deformed by ECAP, it was possible to analyze the microstructural evolution throughout the sample. / Este trabalho investigou o efeito de diferentes tipos de homogeneização sobre a microestrutura e o comportamento em deformação a frio da liga Ti-35Nb-0,15Si. A homogeneização foi realizada em duas condições. Condição 1: tratamento em atmosfera de ar ambiente na temperatura 1000 °C por 8, 24, 48, 72, 96 e 120 horas. Condição 2: tratamento em atmosfera inerte de argônio de 1000 °C por 8 horas. Para o estudo de deformação a frio, amostras da liga Ti-35Nb-0,15Si e amostras de Ti CP foram deformadas via ECAP com até 8 passes, utilizando as rotas A e BC numa matriz com ângulo de intersecção entre os canais de Φ = 120º. A caracterização microestrutural foi realizada nas regiões internas e externas com o auxílio de microscopia óptica, microscopia eletrônica de varredura e difratogramas de raios-X. Medidas de microdureza Vickers foram realizadas para avaliar as mudanças ocasionadas pela deformação. Em atmosfera de ar ambiente as amostras apresentaram a presença da camada de óxido influenciando na dureza e no nível de deformação a frio. Com a deformação de Ti-35Nb-0,15Si por ECAP foi possível refinar a estrutura e aumentar a dureza com o aumento do número de passes. A análise de DRX mostrou a presença da fase α’’ induzida por deformação. Com o Ti CP deformado por ECAP foi possível analisar a evolução microestrutural ao longo da amostra. / São Cristóvão, SE

This work studied the deformation and recrystallization in Ti-35Nb-0,15Si alloy. Were produced alloys with four different compositions in arc melting furnace under controlled argon atmosphere. The amount of Nb was kept constant at 35 wt% and the amount of Si ranging between 0.15 and 0.55% wt%. The amount of Ti ranging according amount of Si. The alloys were homogenized at 1000 ° C for 8 hours, and then cold-deformed by compression in a matrix. Deformed alloys were recrystallized at the temperatures of 500, 600 and 700 ° C for 1 hour in the differential thermal analysis equipment (DTA). Were used techniques of the optical microscopy, X-ray diffraction and microhardness to evaluate the changes caused by the deformation and the recrystallization. The alloy with the composition Ti-35Nb-0, 15Si showed the highest level of deformation, resulting in increased hardness and formation of a martensitic phase. DTA curves provide information about the ß transus temperature, recovery and recrystallization of the alloys. The recrystallization at 500, 600 and 700 ° C propitiated stress relief, decreasing in the amount of a" and hardness reduction. / Este trabalho estudou a deformação e recristalização em ligas de Ti-Nb-Si. Foram produzidas ligas com quatro composições diferentes em forno de fusão a arco sob atmosfera controlada de argônio. A quantidade de Nb foi mantida constante em 35% em peso e a quantidade de Si variou entre 0,15 e 0,55% em peso. A quantidade de Ti variou de acordo com a quantidade de Si. As ligas produzidas foram homogeneizadas a 1000 °C por 8 horas e posteriormente deformadas a frio em uma matriz via compressão. As ligas deformadas foram recristalizadas nas temperaturas de 500, 600 e 700 °C por 1 hora no equipamento de análise térmica diferencial (DTA). Foram utilizadas as técnicas de microscopia óptica, difração de raios-X e microdureza Vickers para avaliar as mudanças ocasionadas pela deformação e pela recristalização. A liga com composição Ti-35Nb-0,15Si foi a que apresentou maior nível de deformação, gerando aumento na microdureza e formação da fase martensítica a . As curvas de DTA forneceram informações a respeito das temperaturas ß transus, recuperação e recristalização das ligas As recristalizações a 500, 600 e 700 oC propiciaram alívio das tensões, diminuição da quantidade de a e redução da microdureza.