Aim: To validate a method for the synthesis of a ZTA composite (Al2O3-80%/ Zr2O- 20%) and to characterize the experimental materials topography, optical, and mechanical properties in the as-sintered condition and after a simulated low temperature degradation (LTD) aging protocol compared to a translucent Y-TZP (ZPEX). Material and methods: Experimental ZTA (ZTA ZPEX 80/20) and translucent Y-TZP (ZPEX) green-state disc-shaped specimens were obtained by uniaxial/isostatic ceramic powder pressing technique. Discs were sintered according to a preestablished protocol. After sintering, two-sided polishing was performed with diamond discs and diamond suspensions to 1 m. Thirty specimens of each group underwent an aging protocol in autoclave (20h, 134ºC and 2.2 bar). The specimens were subjected to the following characterization tests, in the as-sintered condition and aged: 1) nanoindentation testing to acquire the materials elastic modulus (E) and hardness (H); 2) interferometry was utilized to characterize topographical parameters (Sa/Sq); 3) X-ray Diffraction (XRD) to assess the tetragonal-monoclinic phase transformation; 4) scanning electron microscopy (SEM) to evaluate the homogeneity of surfaces and distribution of grains; 5) reflectance tests on white and black background to determine the Contrast Ratio (CR) and the Translucency Parameter (TP) by color difference (E) and 6) biaxial flexural strength testing according to ISO 6872:2015. Apparent density was measured using Archimedes principle. Weibull 2-p was used to calculate characteristic stress, Weibull modulus, and probability of survival (reliability) at 300, 500 and 800 MPa. Data were statistically evaluated through Repeated Measures ANOVA following post-hoc comparisons by Tukey test (p<0.05). Results and Conclusion: The proposed method was able to successfully synthetize an aging resistant ZTA ZPEX 80/20 composite, with the elastic modulus being the only decreased property after aging. For such composite, the surface roughness parameters, hardness, optical and mechanical properties were not affected by simulated LTD aging. In contrast, the translucent Y-TZP zirconia presented a significant extent of tetragonal to monoclinic phase transformation compared to ZTA composite after aging, along with significant alterations in all evaluated parameters, except for surface roughness. / Objetivos: Validar um método para a síntese de um compósito ZTA (Al2O3-80%/ Zr2O- 20%) e caracterizar a topografia do material experimental e suas propriedades ópticas e mecânicas, antes e após um protocolo de envelhecimento simulando uma degradação em baixa temperatura (DBT), comparado a uma zircônia Y-TZP translúcida (ZPEX). Material e métodos: Os espécimes experimentais ZTA (ZTA ZPEX 80/20) e Y-TZP translúcido (ZPEX) em forma de disco foram obtidos por técnica de prensagem uniaxial / isostática do pó cerâmico. Os discos foram sinterizados de acordo com um protocolo pré-estabelecido. Após a sinterização, um polimento bilateral foi realizado com discos de diamante e suspensões de diamante de até 1 m. Trinta espécimes de cada grupo foram submetidos a um protocolo de envelhecimento em autoclave (20h, 134ºC e 2,2 bar). Os espécimes foram submetidos aos seguintes testes de caracterização, antes e após envelhecimento: 1) ensaios de nanoindentação para obtenção do módulo de elasticidade dos materiais (E) e dureza (H); 2) a interferometria foi utilizada para caracterizar os parâmetros topográficos (Sa / Sq); 3) difração de raios X (XRD) para avaliar a transformação da fase monoclínica para tetragonal; 4) microscopia eletrônica de varredura (MEV) para avaliar a homogeneidade da superfícies e distribuição dos grãos; 5) testes de refletância em fundo branco e preto para determinar a Relação de Contraste (RC) e o Parâmetro de Translucidez (PT) por diferença de cor (E) e 6) teste de flexão biaxial (TFB), de acordo com a ISO 6872: 2015 . A densidade aparente foi medida usando o princípio de Arquimedes. Weibull 2- p foi utilizada para calcular a resistência característica, módulo de Weibull e a probabilidade de sobrevida (confiabilidade) a 300, 500 e 800 MPa. Os dados foram submetidos à análise de variância medidas repetidas, seguida de comparações múltiplas pelo teste de Tukey (p <0,05). Resultados e Conclusão: O método proposto foi capaz de sintetizar com sucesso um compósito ZTA ZPEX 80/20 resistente ao envelhecimento, sendo o módulo de elasticidade a única propriedade que diminuiu após o envelhecimento. Para tal compósito, os parâmetros de rugosidade superficial, propriedade nanomecânica de dureza, propriedades ópticas e mecânicas não foram afetadas pelo envelhecimento simulado de DBT. Em contraste, a zircônia translúcida Y-TZP apresentou uma extensão significativa da transformação da fase tetragonal para monoclínica em comparação ao composto ZTA após o envelhecimento, juntamente com alterações significativas em todos os parâmetros avaliados, exceto a rugosidade superficial.

Submitted by Edileide Reis (leyde-landy@hotmail.com) on 2013-04-23T11:48:39Z No. of bitstreams: 5 Guilhermo Berrocal 5.pdf: 441982 bytes, checksum: ed6d9be182498c6b4db2d0c4a32f7ac8 (MD5) Guilhermo Berrocal 4.pdf: 1385591 bytes, checksum: c4e7c73fa8dc1eec5a3eb4d438068c56 (MD5) Guilhermo Berrocal 3.pdf: 1956923 bytes, checksum: f8dc8503637b206d198b9966a177a091 (MD5) Guilhermo Berrocal 2.pdf: 289780 bytes, checksum: 3fc530194e3c8918ac11f9c2ccdabc15 (MD5) Guilhermo Berrocal 1.pdf: 340675 bytes, checksum: 7e5ee755b290eae4c9ff083197916037 (MD5) / Made available in DSpace on 2013-04-23T11:48:39Z (GMT). No. of bitstreams: 5 Guilhermo Berrocal 5.pdf: 441982 bytes, checksum: ed6d9be182498c6b4db2d0c4a32f7ac8 (MD5) Guilhermo Berrocal 4.pdf: 1385591 bytes, checksum: c4e7c73fa8dc1eec5a3eb4d438068c56 (MD5) Guilhermo Berrocal 3.pdf: 1956923 bytes, checksum: f8dc8503637b206d198b9966a177a091 (MD5) Guilhermo Berrocal 2.pdf: 289780 bytes, checksum: 3fc530194e3c8918ac11f9c2ccdabc15 (MD5) Guilhermo Berrocal 1.pdf: 340675 bytes, checksum: 7e5ee755b290eae4c9ff083197916037 (MD5) Previous issue date: 2005 / Níquel suportado em alumina tem sido extensivamente usado para catalisar a reforma a vapor do metano, devido ao seu baixo custo, quando comparado a outros catalisadores, à base de metais nobres. Entretanto, ele não é estável durante a reação principalmente devido à transição de fase e à sinterização do suporte. Isto requer o desenvolvimento de novos catalisadores. Uma opção atrativa seria usar suportes baseados em zircônia, que possui diversas vantagens, tais como estabilidade térmica, dureza e propriedades anfotériças, mas esse sólido possui baixa área superficial específica, quando comparado a suportes catalíticos convencionais. Uma provável solução para esse problema é combinar as propriedades da alumina e da zircônia. Com este objetivo foi estudada, neste trabalho, a preparação e caracterização de catalisadores de níquel suportado em zircônia e alumina. Os suportes foram preparados por métodos de precipitação à temperatura ambiente, a partir de soluções aquosas de oxicloreto de zircônio e de nitrato de alumínio, seguido de calcinação a 500 oC. Foram obtidos sólidos com razões molares Zr/Al (molar) = 10; 5; 2; 1; 0,5; 0,2 e 0.1, além de alumina e zircônia puras. Os catalisadores foram preparados por métodos de impregnação de soluções de nitrato de níquel, seguido de calcinação a 500 oC. As amostras foram caracterizadas por energia dispersiva de raios X, termogravimetria, análise térmica diferencial, espectroscopia no infravermelho, com transformadas de Fourier, difração de raios X, redução termoprogramada, medidas de área superficial específica e porosidade e espectroscopia fotoeletrônica de raios X. O efeito da temperatura sobre a cristalização dos suportes foi estudada "in situ" por difração de raios X, usando uma câmara de aquecimento. Observou-se a presença das fases tetragonal e monoclínica na zircônia pura e g-Al2O3 na alumina pura. A adição de pequenas quantidades de alumínio estabilizou a fase tetragonal da zircônia, enquanto quantidades mais elevadas de alumínio levaram à produção de sólidos mal cristalizados. As amostras ricas em alumínio (Zr/Al= 0,1; 0,2 e 0,5) também produziram g-Al2O3. A altas temperaturas, os sólidos mal cristalizados formaram aluminato de níquel. A área superficial específica aumentou com a adição de alumínio, o que foi atribuído à presença desse metal na superfície do sólido, onde ele atua como espaçador. A amostra pobre em alumínio (Zr/Al= 0,1) mostrou a área superficial específica mais elevada. Entretanto, a área superficial específica decresceu devido à adição de níquel, provavelmente devido ao bloqueio de alguns poros por esse metal. As amostras apresentaram poros com diferentes formas e tamanhos e produziram isotermas dos Tipos II e III com "loops" de histerese, típicas de materiais mesoporosos. A adição de alumínio também afetou a redução de níquel, tornando esse processo mais difícil; este efeito aumentou com a quantidade de níquel nos sólidos. Entre as amostras à base de alumínio e zircônio, o sólido com quantidades iguais desses metais (Zr/Al (molar)= 1) apresentou o teor mais elevado de níquel na superfície. Ele apresenta área superficial específica elevada e pode ser facilmente reduzido, permitindo a formação da fase ativa do catalisador, na reforma a vapor do metano. Portanto, esse sólido é o catalisador mais promissor para essa reação. / Salvador