Made available in DSpace on 2019-03-30T00:26:32Z (GMT). No. of bitstreams: 0 Previous issue date: 2018-09-13 / The prevalence of dental caries has decreased over the years and there has been an increase in restorative treatments of non-carious lesions. The presence of acids in the oral cavity is the main etiological factor of dental erosion, and may be due to dietary habits as well as systemic diseases. Another commonly diagnosed injury is abrasion caused by wear and tear because of the brushing technique. The use of resinous infiltrating agents has been used in the approach of preventive dentistry in cases of carious lesions of enamel, inhibiting the progression, and this material may be an alternative for prevention or paralysis of initial lesions of dental erosion, however, there are not enough studies performed at the dentin level. This study aimed to verify the preventive action of the resin infiltrating agent in erosion / abrasion at the dentin level. Dentin blocks were prepared, divided into 3 groups (n = 15) and submitted to cycles of erosion / abrasion and remineralization. Group 1 (AC-citric acid) received no treatment, groups 2 (ACI-citric acid and infiltrating) and 3 (ACDI-citric acid, deproteinization and infiltrating) received treatment with infiltrating agent and only 3 (ACDI) received previous deproteinization. The erosion / abrasion and remineralization cycle consisted of demineralization with citric acid for 60 seconds, washing with distilled water for 5 seconds, remineralization in artificial saliva for 60 minutes and abrasion by simulated brushing with fluoride dentifrice. At the end of a cycle, they were abrasioned by moist brushing with fluoride dentifrice. The cycles occurred 3 times a day for 5 days. The values of mean and standard deviation (SD) were calculated by group. The ANOVA and Tukey tests were used to compare the groups (p¿0.05). For both groups there was loss of mineralized tissue (AC and ACI) and for the CIDI group, a protective film was formed after 5 days of erosion / abrasion and remineralization cycles. The tissue loss observed in the negative control (AC) and in the treatment (ACI) groups did not present a statistically significant difference [p = 0.063]. However, AC and ACI groups differed from the ACDI group which was deproteinized followed by treatment with (p <0.001). As for the presence of the infiltrating film after the erosion / abrasion and remineralization cycles, it was observed that in the ACI group only 25% of the blocks had partially the presence of the infiltrating film. While in the ACDI group, 80% of the blocks presented the treated surface completely covered with the film. It is concluded that the use of resin infiltrating is indicated as a preventive of erosive / abrasive lesions with previous deproteinization, however, further studies are necessary to explore its effectiveness in the oral cavity. / A prevalência da cárie dentária reduziu ao passar dos anos e houve um aumento nos tratamentos restauradores de lesões não cariosas. A presença de ácidos na cavidade bucal é o principal fator etiológico da erosão dentária, podendo ser devido a hábitos alimentares como também por doenças sistêmicas. Outra lesão comumente diagnosticada é a abrasão causada através do desgaste por causa da técnica de escovação. O uso de agentes infiltrantes resinosos vem sendo utilizado na abordagem da odontologia preventiva em casos de lesões iniciais cariosas de esmalte, inibindo a progressão, podendo este material ser uma alternativa para prevenção ou paralisação de lesões iniciais de erosão dentária, porém, não há estudos suficientes realizados a nível de dentina. Esse estudo teve como objetivo verificar a ação preventiva do agente infiltrante resinoso em erosão/abrasão a nível de dentina. Blocos de dentinas foram confeccionados, divididos em 3 grupos (n=15) e submetidos a ciclos de. O grupo 1 (AC-ácido cítrico) não recebeu tratamento, os grupos 2 (ACI-ácido cítrico e infiltrante) e 3 (ACDI ácido cítrico, desproteinização e infiltrante) receberam tratamento com agente infiltrante e apenas o 3 (ACDI) recebeu desproteinização prévia ao uso do infiltrante. O ciclo de erosão/abrasão e remineralização constava de desmineralização com ácido cítrico por 60 segundos, lavagem com água destilada por 5 segundos, remineralização em saliva artificial por 60 minutos e abrasão através de escovação simulada com dentifrício com flúor. Os ciclos ocorreram 3 vezes ao dia, durante 5 dias para todos os grupos. Os valores da média e desvio padrão (DP) foram calculados por grupo. Os testes ANOVA e Tukey foram utilizados para comparação entre os grupos (p¿0,05). Para dois grupos houve perda de tecido mineralizado (AC e ACI) e para o grupo ACDI houve a formação de uma película protetora após 5 dias de ciclos de erosão/abrasão e remineralização. A perda de tecido observada nos grupos controle negativo (AC) e o com tratamento (ACI) não apresentaram diferença estatisticamente significante [p=0,063]. Entretanto, os grupos AC e ACI diferiram do grupo ACDI que foi desproteinizado seguido do tratamento (p<0,001). Quanto a presença da película do infiltrante após os ciclos de erosão/abrasão e remineralização, observou que no grupo ACI apenas 25% dos blocos apresentaram parcialmente a presença da película do infiltrante. Enquanto que no grupo ACDI, 80% dos blocos apresentaram a superfície tratada completamente recoberta com a película. Conclui-se que o uso de infiltrante resinoso é indicado como preventivo de lesões erosivas/abrasivas com desproteinização prévia, no entanto, mais estudos são necessários para explorar a sua eficácia na cavidade bucal.

As resinas compostas fotoativáveis apresentam limitações inerentes ao sistema restaurador, como a tensão gerada durante a contração volumétrica de polimerização e a baixa resistência ao desgaste, principalmente nas regiões de contato oclusal. Na tentativa de diminuir estas tensões ou minimizar os seus efeitos, o uso de baixa densidade de potência nos momentos iniciais da reação de polimerização tem sido proposto. Acredita-se, no entanto, que as propriedades físicoquímicas do material possam ser afetadas negativamente, podendo resultar em um polímero mais frágil mecanicamente e mais susceptível à degradação. Face à esta problematização, avaliou-se o efeito que diferentes métodos de fotoativação exercem na resistência ao desgaste de uma resina composta, bem como na suscetibilidade da estrutura polimérica final formada, em função da variação do meio de armazenamento, aquoso ou alcoólico. O aparelho VIP (BISCO), que possibilita comandos independentes de densidade de potência e tempo foi selecionado. Quatro diferentes métodos de fotoativação foram investigados: Convencional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s) e Softstart (SS: 200mW/cm2 X 10s + 600mW/cm2 X 30s). Após a fotoativação, os espécimes foram armazenados em dois meios distintos, água destilada e solução de etanol a 75%, por 24 horas, e submetidos ao teste de escovação simulada. Os dados foram analisados pelos testes estatísticos ANOVA à 2 critérios e key. Os métodos de fotoativação que utilizaram baixa densidade de potência inicial não comprometeram a resistência à abrasão da resina composta testada. / In an attempt to reduce the stresses generated during polymerization shrinkage of composite resins or minimize its effects, different light-curing techniques have been proposed as alternatives to the conventional technique, which are known as lightcuring modulation techniques, and suggest the use of low power density at the initial moments of the polymerization reaction. However, due to the low power density applied to the composite resin, it is believed that some properties of the material would be negatively affected, which might produce a polymer mechanically more fragile. Considering that, this study was conducted to investigate the in vitro abrasive wear of a composite resin subjected at four different photoactivation methods, as well as in the susceptibility of the final polymer structure formed, in function of the variation of the way of storage, watery or alcoholic. Device VIP (BISCO), that it makes possible independent commands of power density and time was selected. Four different photoactivation methods had been investigated: Conventional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s) and Soft-start (SS: 200mW/cm2 X 10s 600mW/cm2 X 30s). After the photoactivation, the specimens had been stored in two distinct ways, distilled water and solution of ethanol 75%, for 24 hours, and submitted to the test of simulated toothbrushing. The data had been analyzed by statistical tests two-way ANOVA and Tukey. Photoactivation methods which use low power density had not compromised the abrasive resistance of the composite resin tested, when comparable to that with high intensity.

PASSOS, Vanara Florêncio. Influência de agentes protetores na prevenção da erosão extrínseca ou intrínseca : estudos in vitro e in situ. 2012. 87 f. Tese (doutorado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2012. / Submitted by denise santos (denise.santos@ufc.br) on 2013-12-02T16:31:33Z No. of bitstreams: 1 2012_tese_vfpassos.pdf: 1963544 bytes, checksum: 342c353d2be21f25db42dc0e33ba1cb2 (MD5) / Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2013-12-02T16:32:30Z (GMT) No. of bitstreams: 1 2012_tese_vfpassos.pdf: 1963544 bytes, checksum: 342c353d2be21f25db42dc0e33ba1cb2 (MD5) / Made available in DSpace on 2013-12-02T16:32:30Z (GMT). No. of bitstreams: 1 2012_tese_vfpassos.pdf: 1963544 bytes, checksum: 342c353d2be21f25db42dc0e33ba1cb2 (MD5) Previous issue date: 2012 / Considering the decline in the prevalence of caries and periodontal diseases in society, there is greater tooth longevity. Thus, non-carious cervical lesions have been observed with greater frequency. Therefore, products that enable the reduction of tooth wear, with easy access and daily use, are ideal alternatives for reducing the loss of mineralized tissue. This thesis consists of three papers that aim, respectively: (1) verify the preventive effect of three commercial AmF, AmF/SnF2 or SnF2-containing dentifrices through an erosive/abrasive model on human dentin; (2) investigate the effect of Mg(OH)2 present in commercial dentifrices in preventing the erosion of enamel by extrinsic and intrinsic acids, as well as, the influence of the number of experimental days in erosion progression; (3) evaluate in situ the action of Mg(OH)2 and NaF in prevention of intrinsic erosion on human enamel. In Articles 1 and 2, were conducted in vitro models, randomized, blind, cyclic, in which the specimens were subjected to the process of de- and remineralization. In Article 1, the erosion was simulated by intrinsic acid, while in Article 2, was intrinsic and extrinsic acids. In Article 1, was added the process of abrasion for toothbrushing. For both studies, the cycle was repeated three times daily for 5 days. In Article 3, the study was in situ, randomized, double-blind, crossover in three phases of five days each, with the participation of 18 volunteers who wore palatal appliances containing 2 blocks of human enamel treated with different toothpastes: control (0 ppm F), Mg(OH)2 (2%) and NaF (1450 ppm F). The specimens were subjected to erosion by immersion them in a cup containing 0.01 M hydrochloric acid (pH = 2) for 60 seconds, 4 times a day, in predetermined times. Then, the volunteers brushed their teeth for 25 seconds with the device in the mouth, and the dilution dentifrice/saliva was rinsed mouthwash for 60 seconds. The alterations caused in specimens of all articles were evaluated by hardness and/or stylus profilometry. Data were tested using ANOVA (p <0.05). The Tukey test was used when required, in cases in which ANOVA revealed difference statistically significant. The results showed that in the article 1, AmF/SnF2 or SnF2 significantly reduced (p <0.05) the loss of dentin surface after erosion/abrasion. In Article 2, Mg(OH)2 or NaF-containing dentifrices were effective in reducing demineralisation caused by citric acid 0.05 M (p <0.001) compared to control. However, none prevention was observed for simulation of intrinsic acid, for both products. The results of the article 3 showed that tested dentifrices reduced the loss of surface enamel (p = 0.021). However, these products not present remineralizing effects (p = 0.349). Thus, it is concluded that dentifrices containing stannous fluoride or magnesium hydroxide are effective in performing some protective effect on the dental substrate after action of acids exogenous or endogenous. / Considerando o declínio da prevalência da doença cárie e periodontal na sociedade, observa-se uma maior longevidade dentária. Assim, lesões cervicais não-cariosas têm sido observadas com maior freqüência. Portanto, produtos que possibilitem a redução do desgaste dentário, sendo de fácil acesso e de uso diário, são alternativas ideais para a redução da perda de tecido mineralizado. Dessa forma, esta tese é constituída por três artigos que objetivaram, respectivamente: (1) verificar o efeito preventivo de três pastas comerciais contendo AmF, AmF/SnF2 or SnF2 através de um modelo erosivo/abrasivo em dentina humana; (2) investigar o efeito do Mg(OH)2 presente em dentifrícios comercializados na prevenção do processo erosivo no esmalte por ácidos extrínseco ou intrínseco, bem como, a influência do número de dias experimentais na progressão da erosão; (3) avaliar in situ a ação do Mg(OH)2 e NaF na prevenção da erosão por ácidos de origem intrínseca em esmalte humano. Nos artigos 1 e 2, foram realizados modelos in vitro, cíclico, randomizado, cego, no qual os espécimes foram submetidos a processo de des- e remineralização. No artigo 1, foi simulado processo erosivo por ácido de origem intrínseca, enquanto no artigo 2, foi avaliada erosão por ácido de origem intrínseca e extrínseca. No artigo 1, foi acrescentado o processo abrasivo através da escovação. Para ambos os estudos, o ciclo foi repetido três vezes ao dia durante cinco dias. No artigo 3, foi realizado um estudo in situ, randomizado, duplo-cego, cruzado, em três fases de 5 dias cada, com a participação de 18 voluntários, que utilizaram dispositivos palatinos, contendo 2 blocos de esmalte dentário humano tratados com diferentes dentifrícios: controle (0 ppm F), Mg(OH)2 (2%) e NaF (1450 ppm F). Os espécimes foram submetidos à erosão por imersão do dispositivo em um copo contendo HCl 0,01 M (pH=2) por 60 segundos, 4 vezes ao dia, em horários pré-determinados. Em seguida, os voluntários escovaram seus dentes por 25 segundos e, com o dispositivo na boca, bochecharam a suspensão dentifrício/saliva formada por 60 segundos. As alterações ocasionadas nos espécimes de todos os artigos foram avaliadas por testes de dureza e/ou perfilometria mecânica. Os dados obtidos foram testados usando ANOVA (p< 0,05). O teste de Tukey foi aplicado, quando necessário, em casos no qual ANOVA revelou diferença estatística. Os resultados do artigo 1 mostraram que dentifrícios contendo AmF/SnF2 ou SnF2 reduziram significativamente (p<0,05) a perda de superfície dentinária após o processo erosivo/abrasivo. No artigo 2, dentifrícios contendo Mg(OH)2 ou NaF foram efetivos em reduzir a desmineralização ocasionada por ácido cítrico 0,05 M (p<0,001) comparados ao grupo controle. Entretanto, para simulação de erosão por origem intrínseca não houve prevenção para ambos os produtos. Os resultados do artigo 3 demonstraram que houve efeito dos dentifrícios testados na redução da perda de superfície de esmalte (p = 0,021). Entretanto, os mesmos não evidenciaram efeitos na redução da desmineralização (p = 0,349). Dessa forma, conclui-se que dentifrícios contendo fluoreto estanhoso ou hidróxido de magnésio são efetivos em realizar algum efeito protetor no substrato dentário após ação de ácidos de origem exógena ou endógena.

As resinas compostas fotoativáveis apresentam limitações inerentes ao sistema restaurador, como a tensão gerada durante a contração volumétrica de polimerização e a baixa resistência ao desgaste, principalmente nas regiões de contato oclusal. Na tentativa de diminuir estas tensões ou minimizar os seus efeitos, o uso de baixa densidade de potência nos momentos iniciais da reação de polimerização tem sido proposto. Acredita-se, no entanto, que as propriedades físicoquímicas do material possam ser afetadas negativamente, podendo resultar em um polímero mais frágil mecanicamente e mais susceptível à degradação. Face à esta problematização, avaliou-se o efeito que diferentes métodos de fotoativação exercem na resistência ao desgaste de uma resina composta, bem como na suscetibilidade da estrutura polimérica final formada, em função da variação do meio de armazenamento, aquoso ou alcoólico. O aparelho VIP (BISCO), que possibilita comandos independentes de densidade de potência e tempo foi selecionado. Quatro diferentes métodos de fotoativação foram investigados: Convencional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s + 3 min + 600mW/cm2 X 37s) e Softstart (SS: 200mW/cm2 X 10s + 600mW/cm2 X 30s). Após a fotoativação, os espécimes foram armazenados em dois meios distintos, água destilada e solução de etanol a 75%, por 24 horas, e submetidos ao teste de escovação simulada. Os dados foram analisados pelos testes estatísticos ANOVA à 2 critérios e key. Os métodos de fotoativação que utilizaram baixa densidade de potência inicial não comprometeram a resistência à abrasão da resina composta testada. / In an attempt to reduce the stresses generated during polymerization shrinkage of composite resins or minimize its effects, different light-curing techniques have been proposed as alternatives to the conventional technique, which are known as lightcuring modulation techniques, and suggest the use of low power density at the initial moments of the polymerization reaction. However, due to the low power density applied to the composite resin, it is believed that some properties of the material would be negatively affected, which might produce a polymer mechanically more fragile. Considering that, this study was conducted to investigate the in vitro abrasive wear of a composite resin subjected at four different photoactivation methods, as well as in the susceptibility of the final polymer structure formed, in function of the variation of the way of storage, watery or alcoholic. Device VIP (BISCO), that it makes possible independent commands of power density and time was selected. Four different photoactivation methods had been investigated: Conventional (C: 600mW/cm2 X 40s), Pulse-delay (PD: 200mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s), Pulse-delay plus (PDP: 600mW/cm2 X 3s 3 min wait 600mW/cm2 X 37s) and Soft-start (SS: 200mW/cm2 X 10s 600mW/cm2 X 30s). After the photoactivation, the specimens had been stored in two distinct ways, distilled water and solution of ethanol 75%, for 24 hours, and submitted to the test of simulated toothbrushing. The data had been analyzed by statistical tests two-way ANOVA and Tukey. Photoactivation methods which use low power density had not compromised the abrasive resistance of the composite resin tested, when comparable to that with high intensity.

O objetivo deste trabalho foi avaliar in situ a ação do bochecho com solução de sulfato ferroso para reduzir a ação erosiva e o efeito sinérgico entre erosão e abrasão, em espécimes de esmalte e de dentina humanos, quando expostos a um refrigerante (Coca-cola®). O estudo foi realizado em duas fases cruzadas, de 5 dias cada (SB- sem e CB- com bochecho), na qual 10 voluntários utilizaram placas palatinas com 6 blocos de esmalte e 6 de dentina, distribuídos em três fileiras horizontais contendo 4 blocos, correspondendo aos grupos: erosão (Eros); erosão + abrasão (1 Min) e após 30 minutos (30 Min). Os dispositivos foram imersos 4 x/dia, por 5 minutos na bebida. O dispositivo foi colocado na boca por 1 minuto com ou sem o bochecho, dependendo da etapa. Em seguida os voluntários escovaram com dentifrício fluoretado 4 espécimes de uma das fileiras indicada como 1 Min, e recolocaram o aparelho. Depois de 30 minutos escovaram mais 4 espécimes de outra fileira indicada como 30 Min e nada realizaram na fileira restante (Eros). A análise foi realizada por meio de teste de microdureza (%PDS), rugosidade superficial (µm) e perfilometria (µm). Foram aplicados os testes ANOVA e Tukey (p<0,05). A %PDS, a rugosidade e o desgaste em esmalte foram: SB Eros (-80,80%, -0,077µm, 9,30µm); SB 1Min (-76,05%, 0,024µm, 10,70µm); SB 30Min (-70,79%, -0,160µm, 10,82µm); CB Eros (-68,37%, -0,190µm, 8,56µm); CB 1 Min (-69,90%, 0,053µm, 7,13µm); CB 30 Min (-68,31%, -0,136µm, 6,81µm), respectivamente. Para dentina: SB Eros (-46,09%, -0,050µm, 8,03µm); SB 1Min (-35,07%, 0,011µm, 6,75µm); SB 30Min (-40,30%, -0,298µm, 6,13µm); CB Eros (-41,66%, -0,042µm, 5,12µm); CB 1 Min (-41,18%, 0,043µm, 5,68µm); CB 30 Min (-40,06%, -0,030µm, 3,41µm), respectivamente. O uso do bochecho propiciou redução significativa na %PDS para o esmalte quando comparado à condição sem bochecho, além de desgaste significativamente menor em dentina, independente da situação de erosão. O esmalte apresentou maior desgaste que a dentina, independente das condições experimentais. Concluiu-se que o bochecho com a solução de FeSO4 foi capaz de minimizar a erosão dentária após o uso do refrigerante e reduzir o efeito sinérgico entre erosão e abrasão tanto em esmalte quanto em dentina humanos . / The aim of this study was to evaluate in situ evaluation the effect of ferrous sulfate solution-containing mouthrinse on the reduction of the erosive action and synergistic effect between erosion and abrasion, in human enamel and dentin specimens, when exposed to a soft drink (Coca-cola®). The study was performed in two crossover stages, with 5 days each (SB- without and CB- with mouthrinse). Ten volunteers used palatal appliances with 6 enamel and 6 dentin blocks, arranged in three horizontal rows containing 4 blocks, corresponding to the groups: erosion (Eros); erosion + abrasion (1 Min) and after 30 minutes (30 Min). The appliances were immersed 4 times a day in the drink for 5 minutes. The appliance was placed in the mouth for 1 minute with or without the mouthrinse, depending on the stage. The volunteers then brushed 4 specimens of the row designed as 1 Min with fluoridated dentifrice and placed the appliance into the mouth. After 30 minutes, they brushed 4 specimens of the row designed as 30 Min, and no procedure was performed for the other row (Eros). Analysis was performed by microhardness (%PDS), surface roughness (µm) and profilometer (µm) tests. ANOVA and Tukey’s tests were applied (p<0.05). The % PDS, roughness and wear in enamel were: SB Eros (-80.80%, -0.077µm, 9.30µm); SB 1Min (-76.05%, 0.024µm, 10.70µm); SB 30Min (-70.79%, -0.160µm, 10.82µm); CB Eros (-68.37%, -0.190µm, 8.56µm); CB 1 Min (-69.90%, 0.053µm, 7.13µm); CB 30 Min (-68.31%, -0.136µm, 6.81µm), respectively. Concerning the dentin: SB Eros (-46.09%, - 0.050µm, 8.03µm); SB 1Min (- 35.07%, 0.011µm, 6.75µm); SB 30Min (-40.30%, -0.298µm, 6.13µm); CB Eros (-41.66%, -0.042µm, 5.12µm); CB 1 Min (-41.18%, 0.043µm, 5.68µm); CB 30 Min (-40.06%, -0.030µm, 3.41µm), respectively. The use of the mouthrinse provided a significant reduction in % PDS for the enamel compared to the condition without mouthrinse, besides significantly smaller wear in dentin, regardless of the situation of erosion. The enamel exhibited more wear than dentin, regardless of the study conditions. It was concluded that mouthrinse with ferrous sulfate solution was able to reduce the dental erosion after the use of soft drink and reduce the synergistic effect between erosion and abrasion, both in human enamel and dentin.

VIEIRA, Gustavo Henrique Apolinário. Avaliação in vitro do efeito da escovação com dentifrícios clareadores sobre a superfície dentinária. 2012. 43 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia, e Enfermagem, Fortaleza, 2012. / Submitted by denise santos (denise.santos@ufc.br) on 2013-10-25T11:49:03Z No. of bitstreams: 1 2012_dis_ghavieira.pdf: 1153944 bytes, checksum: a5ce1178a6b7b8b1ae191774cca63540 (MD5) / Approved for entry into archive by denise santos(denise.santos@ufc.br) on 2013-10-25T11:50:10Z (GMT) No. of bitstreams: 1 2012_dis_ghavieira.pdf: 1153944 bytes, checksum: a5ce1178a6b7b8b1ae191774cca63540 (MD5) / Made available in DSpace on 2013-10-25T11:50:10Z (GMT). No. of bitstreams: 1 2012_dis_ghavieira.pdf: 1153944 bytes, checksum: a5ce1178a6b7b8b1ae191774cca63540 (MD5) Previous issue date: 2012 / Toothbrushing abrasion has an important role in the etiology of dentine hypersensitivity. The abrasion may be related to the abrasivity of the toothpaste. The aim of this study was to compare by mechanical profilometry the effect of toothbrushing abrasion with whitening and regular toothpastes on root dentine. Ninety dentine specimens (4x4x2 mm) were randomly divided into five experimental groups (n=18) according to the toothpaste: three whitening (W1, W2 and W3) and two regular toothpastes (C1 and C2), produced by two different manufacturers. Using a brushing machine, each specimen was brushed with constant load of 300g for 2500 cycles (4.5 cycles/second). The toothpastes were diluted at a ratio of 1:3 w/w (dentifrice/distilled water). The brush diamond tip of the profilometer moved at a constant speed of 0.05 mm/s with a force of 0.7 mN. The average reading value of brushing abrasion (μm; mean ± standard deviation) was obtained from five consecutive measurements of each specimen: W1 = 8.86 ± 1.58, W2 = 8.27 ± 2.39, W3 = 7.59 ± 1.04, R1 = 2.94 ± 1.29 and R2 = 2.89 ± 1.05. There was a significant difference between groups (ANOVA - p<0.0001). Post-hoc Tukey test for multiple comparison showed differences between all the whitening toothpastes and the regular ones, but not among the whitening or the regular against each other. Whitening toothpastes can cause more dentine abrasion than the regular ones. / A escovação tem um papel importante na etiologia da hipersensibilidade dentinária. Abrasão pode estar relacionada a abrasivos contidos nos dentifrícios. O objetivo deste estudo foi comparar por perfilometria mecânica o efeito da abrasão da escovação com dentifrícios clareadores e convencionais na dentina radicular. Noventa espécimes de dentina (4 x 4 x 2mm) foram aleatoriamente divididos em cinco grupos experimentais (n=18) de acordo com os dentifrícios: três clareadores (W1, W2, e W3) e dois convencionais (C1 e C2), produzidos por dois fabricantes distintos. Utilizando uma máquina de escovação, cada espécime foi escovado com carga constante de 300g por 2500 ciclos (4,5 ciclos por segundo). Os dentifrícios foram diluídos na proporção de 1:3 em peso (dentifrício/saliva artificial). A ponta diamantada do perfilômetro moveu-se em velocidade constante de 0,05mm/s com forca de 0,7mN. O valor médio das leituras da abrasão da escovação (μm; média ± desvio padrão) foi obtido de cinco leituras consecutivas em cada espécime: W1 = 8,86 ± 1,58, W2 = 8,27 ± 2,39, W3 = 7,59 ± 1,04, C1 = 2,94 ± 1,29 C2 = 2,89 ± 1,05. Houve diferença estatisticamente significante entre os grupos (ANOVA - p<0.0001). O teste de Tukey para múltiplas comparações mostrou diferenças entre todos os dentífricios clareadores e os convencionais, mas não entre os clareadores e os convencionais entre si. Dentifrícios clareadores podem causar mais abrasão na dentina do que os convencionais.

Orientador: Carlos Rocha Gomes Torres / Banca: Eduardo Moreira da Silva / Banca: Alessandra Buhler Borges / Resumo: O objetivo deste estudo foi avaliar a eficácia do laser Nd:YAG associado a diferentes sistemas adesivos autocondicionantes, na prevenção do desgaste erosivo e abrasivo do esmalte dental. Foram preparados 160 espécimes de esmalte bovino, polidos e submetidos a uma erosão inicial em ácido cítrico a 0,3 % por 5 min. Os perfis iniciais da superfície de esmalte foram medidos utilizando um perfilômetro, cuja unidade de medida é em micrométros (μm). Os espécimes foram distribuídos aleatóriamente em oito grupos (n=20): SB - Aplicação do adesivo Single Bond Universal (3M/Espe) e fotopolimerização; SB+L - Aplicação do adesivo Single Bond Universal, irradiação do laser de Nd:YAG (80 mJ,10 Hz) e fotopolimerização; FB - Aplicação do adesivo Futura Bond U (Voco) e fotopolimerização; FB+ L - Aplicação do adesivo Futura Bond U, irradiação do laser de Nd:YAG e fotopolimerização; GEN - Aplicação do adesivo G-aenial Bond (GC) e fotopolimerização; GEN +L - Aplicação do adesivo G-aenial Bond, irradiação do laser de Nd:YAG e fotopolimerização; L - Apenas irradiação do laser Nd:YAG; C - nenhum tratamento (Controle). Em seguida foram realizados diariamente os desafios erosivo, utilizando ácido cítrico a 0,3% (pH 2,6) por 2 min, e abrasivo realizado em uma máquina de escovação (40 ciclos, carga 200 g) com dentifrício diluído em saliva artificial (1:3 peso/peso). Foram realizados quatro ciclos por dia, durante 5 dias. Os perfis das superfícies do esmalte foram novamente avaliados utilizando um perfilômetro. Os dados foram analisados utilizando o teste de análise de variância ANOVA e Tukey. O nível de significância foi de 5 %. Para a ANOVA foram observadas diferenças estatisticamente significantes (p= 0,0000) de desgaste. Os valores de média (±dp) e os resultados do teste Tukey foram: GEN - 4,88 (±1,09) a; L - 5,04 (±0,99) a; FB - 5,32 (±0,93) ab; GEN.... / Abstract: The aim of this study was to evaluate the effectiveness of the Nd: YAG laser, alone or associated with different auto constraints adhesive systems, in the prevention of erosive and abrasive wear of the dental enamel. A hundred and sixty samples of bovine enamel were prepared, polished and subjected to an initial erosion in 0.3 % citric acid solution for 5 min. The initial profiles of the enamel surface were measured using a profilometer, whose unit is measured in micrometers (μm). The samples were randomly divided into eight groups (n = 20): SB - Single Bond Universal (3M/Espe) adhesive application and light curing; SB+L - Single Bond Universal adhesive application, Nd:YAG laser irradiation (80 mJ, 10 Hz) and light curing; FB - Futura Bond U (Voco) adhesive application and light curing; Group FB+L - Futura Bond U adhesive application, Nd:YAG laser irradiation and light curing; GEN - G-aenial Bond (GC) adhesive application and light curing; GEN+L - G-aenial Bond adhesive, Nd:YAG laser irradiation and light curing; L - Only Nd:YAG laser irradiation; C - No treatment (control group). The erosive challenge, using citric acid 0.3 % (pH 2.6) for 2 min, and abrasive challenge, using a tooth brushing machine (40 cycles, load of 200 g) with toothpaste diluted in artificial saliva (1:3 wt/wt), were performed. Four cycles a day were performed during 5 days. The profiles of the enamel surfaces were again measured using the profilometer. Data were analyzed using analysis of variance (ANOVA) and Tukey statistical tests. The level of significance was 5%. When ANOVA (one factor) test was applied, it was observed statistical difference (p=0,0000) of surface wear. Mean values (± SD) and results of the Tukey test were: GEN - 4,88 (±1,09) a; L - 5,04 (±0,99) a; FB - 5,32 (±0,93) ab; GEN + L - 5,46 (±1,27) abc; SB + L - 5,78 (±1,12) abc; FB + L - 6,23 (±1,25) bc; SB - 6,35 (±1,11) c; C ..... / Mestre

Made available in DSpace on 2011-12-27T14:14:22Z (GMT). No. of bitstreams: 2 000409048-0.pdf: 15543106 bytes, checksum: 5a31b56713c6a1640f963b2da4cb91a1 (MD5) license.txt: 581 bytes, checksum: 44ea52f0b7567232681c6e3d72285adc (MD5) / The purpose of this study was to evaluate the marginal breakdown in resin composite restorations after toothbrush-dentifrice abrasion. Twelve specimens were prepared with bovine incisors and four restorations had been done in the facial enamel surface of each bovine tooth. Two nanocomposites (Filtek Supreme XT and Filtek Z350, 3M/ESPE) and two hybrid composites (without nanotechnology) (4Seasons and Tetric Ceram HB, Ivoclar Vivadent) were used. Each specimen was subjected to toothbrush-dentifrice abrasion using toothbrush (Colgate Professional, Colgate-Palmolive) and dentifrice (Colgate Tripla Ação, Colgate-Palmolive) in a wear test machine (Idea-PUCRS). At baseline and each cycle interval (1; 2; 4 and 6 years) a surface profilometer (XP-2, Ambios Technology) was used to determine the marginal breakdown. Five profilometric tracings were performed in each one of the 4 restorations of the 12 samples after each period of time. The average of these 5 tracings was calculated using software Origin 7. 0 (OriginLab Corporation) and graphics were obtained where was possible to measure the marginal breakdown in the two sides of the restoration. The average of the two sides was taken as being the value of marginal breakdown (μm) of the composite resin in that period. Data were analyzed using the Analysis of Variance for Mixing Models for Repeated Measures with Subdivided Parcel and Tukey’s test adjustment. The results indicate that all composites had presented a marginal breakdown’s increased throughout the evaluated periods. Both hybrid’s composites (4Seasons and Tetric Ceram HB) exhibited a statistical significantly increase in the marginal breakdown after 4 and 6 years of toothbrushing when compared with the nanocomposites (Filtek Supreme XT and Z350), without presenting differences between itself in each period. The Filtek Supreme XT showed no significant increase over the periods and Filtek Z350 exhibited statistical significantly increase in the marginal breakdown after 6 years, without statistically significant differences in periods of 1, 2 and 4 years. The SEM images illustrate the behavior of composites throughout the time. In conclusion, the results suggest that the interfaces tooth/composite of the nanocomposites restorations (Filtek Supreme XT and Filtek Z350) are less subject to the marginal breakdown after toothbrushing. / O objetivo deste estudo foi avaliar o valamento marginal em restaurações de resina composta após ensaio de abrasão por escovação. Para isto, foram realizadas quatro restaurações na face vestibular de 12 incisivos bovinos, devidamente planificados e incluídos em resina acrílica. Os compósitos avaliados foram: Filtek Supreme XT, Filtek Z350 (3M/ESPE), ambos com nanopartículas, 4Seasons e Tetric Ceram HB (Ivoclar Vivadent), classificados como híbridos. Cada uma das 12 amostras foi submetida ao ensaio de abrasão em máquina de escovação (Idéia-PUCRS), com escova (Colgate Professional, Colgate-Palmolive) e dentifrício (Colgate Tripla Ação, Colgate-Palmolive), nos períodos correspondentes a 1, 2, 4 e 6 anos de escovação simulada. Para a análise do valamento marginal, antes e após cada período, foi utilizado um Perfilômetro XP-2 (Ambios Technology), sendo realizadas 5 varreduras em cada uma das restaurações das 12 amostras, após cada período. A média destas 5 varreduras foi calculada utilizando o software Origin 7. 0 (OriginLab Corporation) gerando um gráfico (n=240) onde foi possível medir a discrepância entre a margem em esmalte e a resina composta, nos dois lados da restauração. A média dos dois lados foi tomada como sendo o valor de valamento marginal, em μm, da resina no período avaliado. Os resultados foram submetidos à Análise de Variância por Modelos Mistos para Medidas Repetidas com Parcela Subdividida e para a análise pós-teste foi utilizado o ajuste de Tukey com nível de significância de 5%. Todas as resinas apresentaram um aumento no valamento marginal ao longo dos períodos avaliados. Tanto a resina 4Seasons como a Tetric Ceram HB apresentaram um aumento significativo no valamento marginal após 4 e 6 anos de escovação simulada e não apresentaram diferenças estatisticamente significativas entre si em cada período.A resina Filtek Supreme XT não apresentou aumento significativo ao longo dos períodos avaliados. A Filtek Z350 apresentou aumento significativo do valamento marginal no período de 6 anos, sem apresentar diferenças estatisticamente significantes nos períodos de 1, 2 e 4 anos. Os aspectos morfológicos, de amostras de cada resina observadas em MEV, após cada período avaliado, ilustram o comportamento dos compósitos ao longo do tempo frente ao ensaio de abrasão por escovação. As interfaces dente/restauração das restaurações realizadas com os compósitos Filtek Supreme XT e Filtek Z350 apresentaram menor formação de valamento marginal após a abrasão por escovação ao longo do tempo.

O objetivo deste trabalho foi avaliar in situ a ação do bochecho com solução de sulfato ferroso para reduzir a ação erosiva e o efeito sinérgico entre erosão e abrasão, em espécimes de esmalte e de dentina humanos, quando expostos a um refrigerante (Coca-cola®). O estudo foi realizado em duas fases cruzadas, de 5 dias cada (SB- sem e CB- com bochecho), na qual 10 voluntários utilizaram placas palatinas com 6 blocos de esmalte e 6 de dentina, distribuídos em três fileiras horizontais contendo 4 blocos, correspondendo aos grupos: erosão (Eros); erosão + abrasão (1 Min) e após 30 minutos (30 Min). Os dispositivos foram imersos 4 x/dia, por 5 minutos na bebida. O dispositivo foi colocado na boca por 1 minuto com ou sem o bochecho, dependendo da etapa. Em seguida os voluntários escovaram com dentifrício fluoretado 4 espécimes de uma das fileiras indicada como 1 Min, e recolocaram o aparelho. Depois de 30 minutos escovaram mais 4 espécimes de outra fileira indicada como 30 Min e nada realizaram na fileira restante (Eros). A análise foi realizada por meio de teste de microdureza (%PDS), rugosidade superficial (µm) e perfilometria (µm). Foram aplicados os testes ANOVA e Tukey (p<0,05). A %PDS, a rugosidade e o desgaste em esmalte foram: SB Eros (-80,80%, -0,077µm, 9,30µm); SB 1Min (-76,05%, 0,024µm, 10,70µm); SB 30Min (-70,79%, -0,160µm, 10,82µm); CB Eros (-68,37%, -0,190µm, 8,56µm); CB 1 Min (-69,90%, 0,053µm, 7,13µm); CB 30 Min (-68,31%, -0,136µm, 6,81µm), respectivamente. Para dentina: SB Eros (-46,09%, -0,050µm, 8,03µm); SB 1Min (-35,07%, 0,011µm, 6,75µm); SB 30Min (-40,30%, -0,298µm, 6,13µm); CB Eros (-41,66%, -0,042µm, 5,12µm); CB 1 Min (-41,18%, 0,043µm, 5,68µm); CB 30 Min (-40,06%, -0,030µm, 3,41µm), respectivamente. O uso do bochecho propiciou redução significativa na %PDS para o esmalte quando comparado à condição sem bochecho, além de desgaste significativamente menor em dentina, independente da situação de erosão. O esmalte apresentou maior desgaste que a dentina, independente das condições experimentais. Concluiu-se que o bochecho com a solução de FeSO4 foi capaz de minimizar a erosão dentária após o uso do refrigerante e reduzir o efeito sinérgico entre erosão e abrasão tanto em esmalte quanto em dentina humanos . / The aim of this study was to evaluate in situ evaluation the effect of ferrous sulfate solution-containing mouthrinse on the reduction of the erosive action and synergistic effect between erosion and abrasion, in human enamel and dentin specimens, when exposed to a soft drink (Coca-cola®). The study was performed in two crossover stages, with 5 days each (SB- without and CB- with mouthrinse). Ten volunteers used palatal appliances with 6 enamel and 6 dentin blocks, arranged in three horizontal rows containing 4 blocks, corresponding to the groups: erosion (Eros); erosion + abrasion (1 Min) and after 30 minutes (30 Min). The appliances were immersed 4 times a day in the drink for 5 minutes. The appliance was placed in the mouth for 1 minute with or without the mouthrinse, depending on the stage. The volunteers then brushed 4 specimens of the row designed as 1 Min with fluoridated dentifrice and placed the appliance into the mouth. After 30 minutes, they brushed 4 specimens of the row designed as 30 Min, and no procedure was performed for the other row (Eros). Analysis was performed by microhardness (%PDS), surface roughness (µm) and profilometer (µm) tests. ANOVA and Tukey’s tests were applied (p<0.05). The % PDS, roughness and wear in enamel were: SB Eros (-80.80%, -0.077µm, 9.30µm); SB 1Min (-76.05%, 0.024µm, 10.70µm); SB 30Min (-70.79%, -0.160µm, 10.82µm); CB Eros (-68.37%, -0.190µm, 8.56µm); CB 1 Min (-69.90%, 0.053µm, 7.13µm); CB 30 Min (-68.31%, -0.136µm, 6.81µm), respectively. Concerning the dentin: SB Eros (-46.09%, - 0.050µm, 8.03µm); SB 1Min (- 35.07%, 0.011µm, 6.75µm); SB 30Min (-40.30%, -0.298µm, 6.13µm); CB Eros (-41.66%, -0.042µm, 5.12µm); CB 1 Min (-41.18%, 0.043µm, 5.68µm); CB 30 Min (-40.06%, -0.030µm, 3.41µm), respectively. The use of the mouthrinse provided a significant reduction in % PDS for the enamel compared to the condition without mouthrinse, besides significantly smaller wear in dentin, regardless of the situation of erosion. The enamel exhibited more wear than dentin, regardless of the study conditions. It was concluded that mouthrinse with ferrous sulfate solution was able to reduce the dental erosion after the use of soft drink and reduce the synergistic effect between erosion and abrasion, both in human enamel and dentin.

Este projeto teve como objetivos investigar o efeito do íon ferro (Fe+2), associado ou não ao íon flúor (F-), na redução da erosão do esmalte e da dentina bovinos, bem como desenvolver e avaliar um dentifrício enriquecido com Fe+2 para a prevenção da erosão associada à abrasão. Foram realizados 4 subprojetos: (1) Determinação do efeito protetor de concentrações crescentes do Fe+2 (0 a 120 mmol/L) associadas ou não ao F- (0 a 4 g/mL), contra a dissolução do pó de esmalte bovino in vitro; (2) Avaliação, in vitro, do efeito protetor do Fe+2 a 10 mmol/L contra a dissolução mineral da superfície do esmalte bovino; (3) Desenvolvimento e avaliação, in vitro, de dentifrícios fluoretados enriquecidos com diferentes concentrações de Fe+2, visando à prevenção da perda mineral do esmalte bovino; (4) Avaliação, in situ, do efeito inibidor do dentifrício acrescido de Fe+2 e F- na desmineralização do esmalte e dentina bovinos sadios ou previamente erodidos. As variáveis de resposta utilizadas foram a quantificação da perda de fósforo (colorimetria) e o desgaste (perfilometria, m) para os subprojetos 1 e 2, e 3 e 4, respectivamente. Os dados foram submetidos à análise estatística (p<0,05). Para o Subprojeto (1), a ANOVA a 2 critérios e o teste de Bonferroni revelaram que soluções contendo Fe+2 a 1,25, 2,5, 5,0, 10, 15 e 30 mmol/L reduziram significativamente a dissolução do pó de esmalte bovino em 18, 18, 23, 35, 35 e 55%, respectivamente, em comparação ao controle (sem Fe+2). Na presença de F-, o efeito do Fe+2 na inibição da dissolução do esmalte foi reduzido, não havendo efeito sinérgico entre estes íons nas condições testadas. No Subprojeto (2), a ANOVA a 2 critérios e o teste de Bonferroni, mostraram uma redução significativa na desmineralização da superfície do esmalte bovino em torno de 30 a 40%, quando se utilizou solução de Fe+2 a 10 mmol/L. No Subprojeto (3), a ANOVA revelou diferença significativa entre os grupos (Placebo, 1100 g/mL de F-, Crest®, Fe+2 1,0 mg/g, Fe+2 2,5 mg/g, Fe+2 5,0 mg/g, F- (1100 g/mL) + Fe+2 1,0 mg/g, F- (1100 g/mL) + Fe+2 2,5 mg/g e F- (1100 g/mL) + Fe+2 5,0 mg/g) (F=4,734, p<0,0001). O menor desgaste (0,48±0,24 m) foi apresentado pelo grupo em que foi utilizado o dentifrício contendo 1100 g/mL F- e 5 mg/g Fe+2. No Subprojeto (4), para o esmalte hígido a ANOVA a 2 critérios revelou uma diferença significativa entre os dentifrícios, (F=21,72, p<0,0001), mas não entre as condições (só erosão, erosão + slurry, erosão + abrasão) (F=1,20, p=0,32) e nem para a interação entre ambos (F = 1,04, p=0,41). O teste de Bonferroni revelou que os blocos que receberam o dentifrício contendo Fe+2 e F- apresentaram valores de desgaste significativamente menores quando comparados aos blocos submetidos aos demais dentifrícios, os quais não diferiram significativamente entre si. Para a dentina hígida, o esmalte previamente erodido e a dentina previamente erodida, o mesmo padrão foi seguido, apesar destes dois últimos terem apresentado valores de desgaste maiores que aqueles observados para os blocos hígidos. / The aims of this study were to investigate the effect of iron (Fe+2) associated or not to fluoride (F-) on the reduction of bovine enamel and dentin erosion, as well as to develop and evaluate a dentifrice containing Fe+2 to prevent erosion associated to abrasion. Four subprojects were done: (1) In vitro determination of the protective effect of increasing Fe+2 concentrations (0 to 120 mmol/L) associated or not to F- (0 to 4 g/mL) against the dissolution of powdered enamel; (2) In vitro evaluation of the protective effect of 10 mol/L Fe+2 against the mineral dissolution of superficial bovine enamel; (3) Development and in vitro evaluation of fluorided dentifrices containing different Fe+2 concentrations in order to prevent the mineral loss of bovine enamel; and (4) In situ evaluation of the effect of a dentifrice containing Fe+2 and F- on the demineralization of sound or previously eroded bovine enamel and dentin. The response variables were quantification of phosphate loss (colorimetry) and tooth wear (perfilometry, m) for the subprojects 1 and 2, and 3 and 4, respectively. Data were submitted to statistical analyses (p <0.05). In subproject (1), two-way ANOVA and Bonferronis test revealed that solutions containing 1.25, 2.5, 5.0, 10.0, 15.0 and 30.0 mmol/L Fe+2 significantly reduced the dissolution of powdered enamel at 18, 18, 23, 35, 35 and 55%, respectively, in comparison to control (without Fe+2). In the presence of F-, the effect of Fe+2 on the dissolution of enamel was reduced and no synergistic effect between these ions was observed in the tested conditions. In Subproject (2), two-way ANOVA and Bonferronis test showed a significant reduction on surface demineralization of bovine enamel (around 30-40%), when the solution containing Fe+2 at 10 mmol/L was used. In Subproject (3), ANOVA revealed a significant difference among the groups (Placebo, 1,100 g/mL F, Crest®, 1.0 mg/g Fe+2, 2.5 mg/g Fe+2, 5.0 mg/g Fe+2, F- (1, 100 g/mL) + 1,0 mg/g Fe+2, F- (1100 g/mL) + 2,5 mg/g Fe+2 and F- (1,100 g/mL) + 5,0 mg/g Fe+2) (F=4,734, p<0,0001). The lowest wear (0.48±0.24 m) was observed when the dentifrice containing F + Fe was used. In Subproject (4), for sound enamel, two-way ANOVA revealed a significant difference among the dentifrices, (F=21.72, p<0.0001), but not among the conditions (erosion only, erosion + slurry, erosion + abrasion) (F=1.20, p=0.32) or for the interaction of both (F = 1.04, p=0.41). The Bonferronis test revealed that the blocks which received the dentifrice containing Fe+2 and F- presented significantly lesser wear when compared to the blocks submitted to the other dentifrices, which did not differ significantly among each other. As for sound dentin as well as for previously eroded enamel and dentin, the same pattern was obtained but the latter two presented wear values higher than those seen for the sound blocks.