Orientador: Mário Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-22T06:42:26Z (GMT). No. of bitstreams: 1 Vitti_RafaelPino_D.pdf: 971338 bytes, checksum: 04747212bf9b8bde6e4a37081ac788e6 (MD5) Previous issue date: 2013 / Resumo: Os objetivos neste trabalho foram (1) avaliar e comparar propriedades físico-químicas de cimentos endodônticos, sendo um recentemente desenvolvido à base de mineral trióxido agregado (MTA Fillapex, Angelus, Londrina, Brasil) e outro à base de resina epóxica (AH Plus, Dentsply, Konstanz, Alemanha); e (2) desenvolver e avaliar propriedades físico-químicas de três cimentos endodônticos experimentais à base de MTA e uma resina de salicilato com diferentes fosfatos de cálcio (CaP). Os materiais foram manipulados de acordo com as instruções dos fabricantes. Os cimentos experimentais foram compostos de pastas bases e catalisadoras misturadas em 1:1. A pasta base foi composta de 60% de óxido de bismuto e 40% de butilenoglicol dissalicilato. Três diferentes pastas catalisadoras foram formuladas contendo: (1) 60% de MTA, 39% de Resimpol 8 e 1% de dióxido de titânio; (2) 40% de MTA, 39% de Resimpol 8, 20% de hidroxiapatita e 1% de dióxido de titânio e; (3) 40% de MTA, 39% de Resimpol 8, 20% de fosfato dibásico de cálcio diidratado e 1% de dióxido de titânio. MTA Fillapex foi usado como controle. O tempo de trabalho e escoamento foi testado de acordo com a ISO 6876:2001 e o tempo de presa de acordo com a ASTM C266 (n=3 para cada material e teste). Os materiais foram colocados em moldes de PVC (8 mm x 1,6 mm) e armazenados em recipientes contendo 20 ml (testes de solubilidade e absorção de água) ou 10 ml (ensaios de pH e liberação de cálcio) de água deionizada a 37ºC (n=10 para cada material e teste). Em 1, 7, 14 e 28 dias as amostras foram removidas dos recipientes e secas para aferiação da solubilidade e absorção de água. Após 3 e 24 horas e 4, 7, 14 e 28 dias, a água dos recipientes foi coletada para análises do pH e liberação de cálcio. Os dados foram analizados usando ANOVA um fator e teste de Tukey (5%). MTA Fillapex mostrou menores valores de escoamento e tempos de trabalho e presa em relação ao AH Plus (p<0,05). MTA Fillapex obteve os maiores valores de escoamento e tempos de trabalho e presa em comparação aos materiais experimentais (p<0,05). MTA Fillapex apresentou os menores valores de solubilidade e absorção de água (p<0,05). Todos os cimentos experimentais e o MTA Fillapex apresentaram pH básico e liberação de íons cálcio. MTA Fillapex e AH Plus mostraram valores de acordo com a ISO 6876:2001. Os materiais experimentais apresentaram propriedades físico-químicas satisfatórias / Abstract: The aims of this study were (1) to evaluate and to compare physicochemical properties of endodontic sealers, a recent calcium-silicate based sealer (MTA Fillapex, Angelus, Londrina, Brazil) and other an epoxy resin based sealer (AH Plus, Dentsply, Konstanz, Germany); and (2) to develop and to evaluate physicochemical properties of three experimental root canal sealers made by mineral trioxide aggregate (MTA) and a salicylate resin with different calcium phosphates (CaP). The materials were handled following the manufacturer's instructions. The experimental materials were composed of a base and a catalyst pastes mixed in a 1:1. The base paste was made by 60% bismuth oxide and 40% butyl ethylene glycol disalicylate. Three different catalyst pastes were formulated with: (1) 60% MTA, 39% Resimpol 8 and 1% titanium dioxide; (2) 40% MTA, 39% Resimpol 8, 20% hydroxyapatite and 1% titanium dioxide and; (3) 40% MTA, 39% Resimpol 8, 20% dibasic calcium phosphate dihydrate and 1% titanium dioxide. MTA Fillapex was used as control. The working time and flow were tested according to ISO 6876:2001 and the setting time according to ASTM C266 (n=3 for each material and test). The materials were placed into PVC molds (8 mm x 1.6 mm) and stored in containers with 20 mL (solubility and water absorption tests) or 10 mL (calcium release and hydroxyl ions tests) of deionized water at 37°C (n=10 for each material and test). At 1, 7, 14 and 28 days the samples were removed from the solutions and dry for solubility and water absorption tests. After 3 and 24 h and 4, 7, 14, 28 days the soaking water was collected for Ca and pH analysis. The data were analyzed using one-way ANOVA with Tukey's test (5%). MTA Fillapex showed lower values of flow and working and setting times when compared to AH Plus (p<.05). MTA Fillapex had the higher values of flow and working and setting times when compared to experimental materials (p<.05). MTA Fillapex presented the lowest values of solubility and water absorption (p<.05). All experimental cements and MTA Fillapex showed basifying activity and released calcium ions. MTA Fillapex and AH Plus showed values in according to the ISO 6876:2001. The experimental materials showed satisfactory physicochemical properties / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

Orientador: Antonio Carlos Guastaldi / Banca: Maria Aparecida Zaghete Bertochi / Banca: Idelmo Rangel Garcia Júnior / Resumo: As pesquisas em biomateriais caminham na busca de dispositivos nos quais, além da resistência mecânica, oferece adequada relação entre bioatividade/biocompatibilidade quando em contato com tecidos biológicos. Atualmente os biomateriais para serem utilizados como implantes são classificados como bioinertes, biotoleráveis e bioativos. No presente trabalho estudou-se as fases de apatitas presentes nos recobrimentos obtidos pelo método biomimético em substratos de titânio pré-modificados superficialmente empregando-se ablação por feixe de laser, objetivando a interação entre o substrato e o recobrimento, visando à aplicação clínica em implantes dentários e ortopédicos. Após estudos piloto, definiu-se condições pré-estabelecidas e as amostras tiveram suas superfícies irradiadas pelo laser Nd:YAG, em atmosfera normal. As amostras foram irradiadas pelo Laser pulsado Nd:YAG, e foram estabelecidas quatro condições de estudo para o trabalho, onde as irradiações foram realizados em ar e pressão atmosférica. Os recobrimentos, sobre as superfícies irradiadas, foram realizados pelo método biomimético, onde as amostras modificadas foram imersas na solução SBF (Simulated Body Fluid) e permaneceram por 4 dias, para a formação da camada de apatitas, este grupo ganhou destaque por possuírem composição semelhante ao tecido ósseo humano. As caracterizações das amostras foram realizadas pelas técnicas de microscopia eletrônica de varredura, espectroscopia de energia dispersiva, difração de raios-X e espectroscopia no infravermelho com transformada de Fourier. Resultados da modificação por feixe de Laser mostraram que as quatro condições estabelecidas sugeriram ter energia suficiente para promover a ablação na superfície irradiada. Verificou-se que na irradiação por feixe de laser ocorre o processos de fusão e solidificação rápida proveniente... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The researches biomaterials in walk in the search of devices us which, besides the mechanical resistance, offer appropriate relationship among bioativity/biocompatibility when in contact with woven biological. Nowadays the biomaterials to be used as implants are classified as bioinert, biotolerability and bioactives. In the work present was study the apatites phases current in the coating obtained by the biomimetic method in substratum of titanium pré-modify superficially being used ablation by laser bunch, aiming at the interaction between the substratum and the coating, seeking to the clinical application in dental and orthopedical implants. After pilot study, it was defined pré-established conditions and the samples had their surfaces irradiated by the laser Nd:YAG, in normal atmosphere. The samples were irradiated by the pulsed Laser Nd:YAG, and they were established four study conditions for the work, where the irradiations were accomplished in air and atmospheric pressure. The coatings, on the irradiated surfaces, were accomplished by the biomimetic method, where the modified samples were immersed in the solution SBF (Simulated Body Fluid) and they stayed for 4 days, for the formation of the apatites layer, this group won prominence for they possess composition similar to the human bone fabric. The characterizations of the samples were accomplished by the techniques o SEM, EDS, XRD and FTIR. Results of the modification for beam of Laser showed that the four established conditions suggested to have enough energy to promote the ablation in the irradiated surface. It was verified that in the irradiation for laser beam happens the processes melt and originating from fast solidification the irradiation for laser, in normal atmosphere, they induce the oxides formation of titanium stoichiometric and non-stoichiometric with different oxidation degrees as Ti3O and Ti6O and with different... (Complete abstract click electronic access below) / Mestre

Vápenaté fosforečnany jsou nejčastěji využívané keramické materiály v medicíně pro regeneraci kostní tkáně. Vápenaté fosforečnany jsou biokompatibilní, bioaktivní a mezi sebou se odlišují především rozpustností a související degradací v organismu, proto jsou nejčastěji využívány k regeneraci malých defektů nebo jako vrstvy na kovových implantátech. U již zmíněné rozpustnosti materiálu po implantaci, hraje důležitou roli poměr zastoupení jednotlivých vápenatých fosforečnanů, od kterého se pak odvíjí rychlost degradace materiálu v organismu. Tato práce se zabývá vlivem tvarovacích metod na mikrostrukturu a zejména fázové složení vápenatých fosforečnanů. Výchozím materiálem pro pozorování změn ve fázovém složení byl komerční hydroxyapatit, který byl upraven kalcinací při 800 °C po dobu jedné hodiny. Při kalcinaci došlo k vytvoření dvoufázové směsi, obsahující hydroxyapatit a -fosforečnan vápenatý. Tato dvoufázová směs byla poté využita pro přípravu suspenze s plněním 15 obj.%, a také k přímé přípravě polotovarů s různou výslednou mikrostrukturou a fázovým složením. S cílem zjistit vliv procesu byly v této práci porovnány vzorky připravené pomocí metod: freeze-casting, izostatické lisování za studena, uniaxiální lisování a suspenzní odlévání. U polotovarů a slinutých vzorků byla provedena charakterizace mikrostruktury a analýza fázového složení. V práci se potvrdil vliv tvarovací metody na oba stanovené parametry – mikrostrukturu a fázové složení. Nově pak bylo zjištěno, že se zvyšující se hodnotou porozity a velikostí pórů se zvyšuje i zastoupení hydroxyapatitu ve vzorcích. Tento trend byl pozorován u vzorků vykazujících unimodální i bimodální zastoupení velikosti pórů.

No description available.

Orientador: Antonio Carlos Guastaldi / Resumo: O desenvolvimento de biomateriais para a regeneração de tecidos é de grande importância e sua demanda aumenta a cada dia, devido ao aumento do envelhecimento da população, da expectativa e qualidade de vida, bem como ao aumento das taxas de acidentes (trânsito e violência). Os Scaffolds são uma estrutura tridimensional, projetada para suportar infiltração, crescimento e diferenciação celular, a fim de melhorar o desenvolvimento e a formação de novos tecidos. Muitos biomateriais podem ser usados para fabricar essas estruturas, como as biocerâmicas e biopolímeros. No entanto, poucos estudos foram realizados para avaliar sua contaminação microbiológica e a influência dos métodos de esterilização podem ter sobre a estrutura e propriedades dos implantes. Dessa forma, o objetivo deste trabalho foi avaliar as propriedades mecânicas, físico-químicas e microbiológicas, antes e após três métodos de esterilização. Esses Scaffolds foram feitos de celulose bacteriana, alginato de sódio e fosfato de cálcio amorfo. Os Scaffolds foram elaborados mediante processo de liofilização. Eles foram divididos em quatro grupos: um grupo controle e três diferentes métodos de esterilização (esterilização a vapor, esterilização por irradiação ultravioleta e esterilização por micro-ondas). O número de colônias viáveis (UFC/mL) foi obtido através do plaqueamento das amostras em Ágar Dextrose Sabouraud com Cloranfenicol (SDA), Ágar Infusão Cérebro e Coração (BHI), Chromagar e Ágar Sangue. Todos os experimen... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The development of biomaterials for the regeneration of tissues is of great importance and their demand increases every day, due to the increase of the aging population, of the expectation and quality of life, as well as the increase of the accident rates (traffic and violence). Scaffolds are a three-dimensional structure designed to withstand cellular infiltration, growth and differentiation in order to improve the development and formation of new tissues. Many biomaterials can be used to make these structures, such as bioceramics and biopolymers. However, few studies have been conducted to evaluate its microbiological contamination and the influence of sterilization methods may have on the structure and properties of implants. Thus, the aim of this work was to evaluate the mechanical, physicochemical and microbiological properties of Scaffolds, before and after three different sterilization methods. These Scaffolds were made of bacterial cellulose, sodium alginate and amorphous calcium phosphate. Scaffolds were made by lyophilization process. They were divided into four groups: a control group and three different sterilization techniques (steam sterilization, sterilization by ultraviolet irradiation and microwave sterilization). The number of viable colonies (CFU/mL) was obtained by plating the samples in Sabouraud Dextrose Agar with Chloramphenicol (SDA), Brain and Heart Infusion Agar (BHI), Chromagar and Blood Agar. All experiments were performed in triplicate and analyze... (Complete abstract click electronic access below) / Mestre

Cílem disertační práce bylo připravit trojrozměrné biokeramické podpůrné systémy („skafoldy“), které by v budoucnu mohly pomoci při rekonstrukci a regeneraci poškozených kostních tkání. Porézní keramické pěny byly připraveny dvěma způsoby – replikační technikou a polymerizací in situ. Co se složení týče, byly studovány keramické materiály zejména na bázi oxidu hlinitého, zirkoničitého a kalcium fosfátů. Byl studován jednak vliv procesních parametrů jako je složení suspenzí a jejich viskozit, dále pak vliv tepelného zpracování na strukturu a výsledné vlastnosti připravených materiálů. U slinutých pěn byla pomocí rastrovací elektronové mikroskopie hodnocena zejména morfologie – velikost pórů, jejich propojenost a celková porozita, charakterizace mikrostruktury nebyla opomenuta. Dále bylo stanoveno fázové složení a pevnost v tlaku. Z biologických vlastností byla testována a diskutována bioaktivita a cytotoxicita materiálů. Disertační práce je členěna do několika částí. V literární rešerši je popsána stavba a vlastnosti kosti, požadavky kladené na kostní náhrady, výhody a nevýhody současně používaných materiálů a způsoby přípravy keramických pěn. Následuje experimentální část, kde byly nejprve studovány pěny připravené replikační technikou. Všechny takto vyrobené pěny měly propojené póry o velikostech 300 až 2000 m, celková porozita se pohybovala v rozmezí 50 – 99 %. Pevnost pěn na bázi kalcium fosfátů – 0,3 MPa (při celkové porozitě 80%) byla nedostatečná pro kostní náhrady, kde je požadována pevnost větší než 2 MPa. Kalcium fosfátové keramiky byly tedy zpevněny buďto inertním jádrem na bázi oxidu hlinitého nebo ATZ (oxidem zirkoničitým zhouževnatělým oxidem hlinitým). Dále byl přípraven částicový kompozit, ve kterým byl hydroxyapatit pojený oxidem křemičitým. Pevnost pěn se podařilo zvýšit až na více než 20 MPa. V poslední kapitole experimentální části byly studovány keramické pěny pěněné in situ, kde byly póry vytvářeny oxidem uhličitým unikajícím během reakce mezi diisokyanátem a polyalkoholem. Po vypálení polymerního pojiva měly pěny propojené póry o průměrné velikosti 80 až 550 m. Celková porozita se pohybovala v rozmezí 76 – 99%. Výhodou oproti replikační technice byly plné trámečky bez velké středové dutiny vznikající vypálením polymerní předlohy. Žádný ze studovaných materiálů nebyl pro buňky toxický, navíc všechny studované pěny vykazovaly bioaktivní chování. Z hlediska kostního tkáňového inženýrství se jako nejslibnější jeví kompozitní materiál zpevněný oxidem křemičitým.

No description available.

Phosphorus (P) released in overland flow is related to P form, soil solution P concentration and the release rate of P from soil. Models relating soil test P (STP) to water soluble P (WSP) and the degree of P saturation (DPS) to STP are used in Virginia to estimate P loss potential. Typically the reservoir of biologically available P in eastern soils has been attributed to P sorbed onto surface sites of non-crystalline aluminum (Al) and iron (Fe) oxides, extractable in ammonium oxalate. More recently, soils with a long-term history of manure application have exhibited properties that indicate calcium (Ca) may also be limiting P, especially in soils impacted by poultry manure. Accurate estimation of P loss potential is critical for justification of long-term management approaches. To evaluate the accuracy of model estimation of P loss potential and P source, we evaluated the (i) soil chemical properties, (ii) soil solution equilibria, (iii) inorganic speciation, and (iv) P desorption capacity of soils impacted over a long period of time by poultry litter (broiler and layer), dairy manure and commercial fertilizer applications. Soil chemical properties were measured with various extractions, while soil solution was measured in samples equilibrated at field capacity. Inorganic material was analyzed using scanning electron microscopy with electron dispersive capacities. Phosphorus desorption capacity was determined by calculating the rate of P release into a 0.01 M NaCl batch reactor. Out of the said analysis, we found that Al and Ca were the primary soil chemical elements limiting soil test P extractability and release. Soils with a high P sorbing capacity (PSC), that were not yet saturated, retained the most total soil P over a 60 hr. batch release experiment. Phase diagrams show that all soils were supersaturated with respect to common Al-, and Fe â P minerals. Saturation indices calculated with Visual Minteq were correlated with the degree of P saturation, and suggested that as the DPS increased, formation of less soluble Ca -P minerals occurs. The soils found to be supersaturated with respect to tri-calcium phosphate (TCP) and octa-calcium (OCP) had the highest P release rate coefficients for both the first (k1) and second (k2) phases of release. Scanning electron microscopy with electron dispersive analysis (SEM-EDS) found that for some manure impacted soils, Al formed associations with P that are stable over a large soil to solution ratio. Additionally, it appears that as non-crystalline Al becomes saturated with P, Ca-P forms may act as an additional reservoir of P in soils with a long-term history of poultry manure application. / Master of Science

Orientadora: Daniele Botticelli / Banca: Idelmo Rangel Garcia Junior / Banca: Francisley Ávila Souza / Banca: Ronaldo Célio Mariano / Banca: Adolfo Embacher Filho / Resumo: Este trabalho teve por objetivo avaliar o tecido ósseo periimplantar formado após o enxerto sinusal com hidroxiapatita e beta-tricálcio fosfato (HA + -TCP), nas apresentações em grânulos e em pasta, concomitante à instalação de implantes em coelhos. Trinta e quatro seios maxilares de coelhos foram enxertados com HA + -TCP, sendo metade do grupo grânulos e metade do grupo pasta. Concomitantemente, foi realizada a instalação de implantes. Aos 7 e 40 dias pós-operatórios, realizou-se a eutanásia dos animais, e as amostras foram preparadas para as análises tomográfica, microtomográfica, histológica (coloração por hematoxilina e eosina - HE), imunoistoquímica (marcação de fator de transcrição Runt-2 - RUNX2 -, fator de crescimento endotelial vascular - VEGF -, osteocalcina - OCN - e fosfatase ácida resistente ao tartarato - TRAP) e de torque de remoção dos implantes. Na tomografia, foi observada a manutenção da integridade da membrana sinusal, sem extravasamento de material, nos dois grupos e períodos. Parâmetros morfométricos de volume ósseo, porcentagem do volume ósseo e número de trabéculas foram significativamente superiores para o grupo pasta do que para o grupo grânulos aos 7 dias, enquanto que a porosidade foi maior para o grupo grânulos nesse mesmo período. Aos 40 dias, não houve diferença significativa entre os grupos para a maioria dos parâmetros microtomográficos estudados. Nos cortes histológicos corados por HE, observou-se que em ambos os grupos ocorreu a formação d... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: This work aimed to evaluate the peri-implant bone tissue after maxillary sinus grafting with hydroxyapatite and beta-tricalcium phosphate (HA + -TCP), in granular and paste formulations, concomitant with implant placement in rabbits. Thirty four rabbit maxillary sinuses were grafted with HA + -TCP, being half of the granular group and half of the paste group. Concomitantly, the implant placement was performed. At 7 and 40 postoperative days, animals were euthanized, and the samples were prepared for tomographic, microtomographic, histological (hematoxylin and eosin staining), immunohistochemical (Runt-related transcription factor 2 - RUNX2, vascular endothelial growth factor - VEGF -, osteocalcin - OCN - and tartrate-resistant acid phosphatase - TRAP - staining) and implant torque removal analyses. In computed tomography, the maintenance of sinus membrane integrity, with no material extravasation, was observed in both groups and periods. Morphometric parameters of bone volume, percentage of bone volume and trabecular number were significantly higher for paste than granular group at day 7, while the porosity was higher for granular group in this period. At day 40, there were no significant differences between both groups for the majority of the microtomographic parameters studied. In the HE-stained histological sections, it was observed that bone healing around implant threads occurred for both groups at day 40, enhancing osseointegration. Similar positive immunostainings we... (Complete abstract click electronic access below) / Doutor

La presente Tesis Doctoral se titula "Obtención y caracterización de nuevos cementos óseos de fosfatos de calcio en el sistema DCP&#8213;alfa-TCP". Los cementos de fosfatos de calcio (CFC) son materiales biocompatibles que tienen la propiedad de endurecer en condiciones fisiológicas formando una estructura porosa de cristales interconectados de hidroxiapatita, i.e. la fase mineral de los tejidos óseos. Estos materiales pueden ser diseñados para que sean inyectables y tengan distintos porcentajes de porosidad. Este hecho permite obtener cementos con distintas tasas de reabsorción ósea que pueden aplicarse con técnicas de mínima invasión. En general, estas propiedades otorgan a estos biomateriales un excelente interés en campos de aplicación de prevención, reconstrucción o estabilización ósea (p.e.: osteoporosis, cirugía craneofacial, vertebroplastia, cifoplastia).Esta Tesis Doctoral consta de 6 capítulos. El Capítulo 1 (Cementos óseos de fosfatos de calcio) recoge el estado del arte de los CFC. Se realiza una revisión bibliográfica crítica de toda la información de interés. Se concluye la necesidad de realizar estudios cinéticos que expliquen adecuadamente las propiedades de fraguado de estos cementos y permitan diseñar cementos con mejores propiedades. El Capítulo 2 (Materiales y métodos utilizados en la fabricación y caracterización de cementos óseos de fosfatos de calcio) describe el protocolo de trabajo seguido para caracterizar los CFC física y químicamente. Este protocolo permite establecer correlaciones entre la microestructura y las propiedades macroscópicas. El Capítulo 3 (Estudio de la cinética de la reacción de fraguado de un cemento óseo de fosfato de calcio) investiga la cinética de fraguado de un cemento octocálcico en el sistema DCP&#8213;alfa-TCP. Los resultados mostraron que: (a) sólo el alfa-TCP reaccionó para dar una hidroxiapatita deficiente en calcio (CDHA); (b) el porcentaje de reacción y la resistencia mecánica a compresión estaban correlacionadas; (c) el cemento presentó una estructura de cristales interconectados con distinto grado de compacidad. El Capítulo 4 (Estudio de nuevas formulaciones de cementos de fosfatos de calcio en el sistema DCP&#8213;alfa-TCP) investiga las propiedades de fraguado y de resistencia mecánica de cementos del sistema DCP&#8213;alfa-TCP en el intervalo de relaciones Calcio/Fósforo (Ca/P) 1.26<Ca/P<1.50. Se estudia cómo varían la trabajabilidad, los tiempos de fraguado y la resistencia a la compresión. También se estudia el efecto de la adición de carbonato cálcico (CC) sobre las propiedades de fraguado ya que se espera obtener como producto final de la reacción de fraguado una hidroxiapatita deficiente en calcio carbonatada y, por lo tanto, más semejante a la apatita de la fase mineral ósea. Los resultados mostraron que la adición de un 10 % de CC produjo un efecto fluidificante sobre los cementos con un incremento en los valores de los tiempos de fraguado. El análisis de la evolución de la resistencia a la compresión con el tiempo demostró que el CC actúa como un retardador. Sin embargo, la resistencia final alcanzada representa en muchos casos un incremento de más del 40 %. El Capítulo 5 (Discusión general) discute los resultados más relevantes analizados a lo largo de los Capítulos 3 y 4 para comprender las posibilidades clínicas que este tipo de materiales nos ofrece. El Capítulo 6 (Conclusiones) presenta una serie de conclusiones obtenidas a partir de los resultados de los Capítulos 3 y 4. Son conclusiones extraídas a partir del análisis de los resultados de determinadas poblaciones de muestras. Como los intervalos de variabilidad de los parámetros de cada población son diferentes, muchas de las conclusiones no son generalizables a todo el sistema DCP&#8213;alfa-TCP, sino que se han de leer dentro de este sistema y en las condiciones experimentales estudiadas. Finalmente, la Tesis Doctoral lista el conjunto de referencias bibliográficas utilizadas en este trabajo de investigación.