Spelling suggestions: "subject:"como?mitos"" "subject:"como?ditos""
11 |
Desenvolvimento e caracteriza??o de um eco-comp?sito de poliuretano de mamona e fibra de l? caninaSilva, Francisco Claudivan da 14 December 2015 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-06-10T00:17:19Z
No. of bitstreams: 1
FranciscoClaudivanDaSilva_TESE.pdf: 104448273 bytes, checksum: 6fc093e63486403fa90fe3c9a04747ab (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-06-10T23:41:42Z (GMT) No. of bitstreams: 1
FranciscoClaudivanDaSilva_TESE.pdf: 104448273 bytes, checksum: 6fc093e63486403fa90fe3c9a04747ab (MD5) / Made available in DSpace on 2016-06-10T23:41:42Z (GMT). No. of bitstreams: 1
FranciscoClaudivanDaSilva_TESE.pdf: 104448273 bytes, checksum: 6fc093e63486403fa90fe3c9a04747ab (MD5)
Previous issue date: 2015-12-14 / A sustentabilidade tem sido cada dia mais um tema em evid?ncia no mundo,
atualmente organiza??es t?m buscado estar cada vez mais dentro desta filosofia em
seus processos, produtos ou servi?os. No presente trabalho foram fabricados ecocomp?sitos
com a fibra animal (l? canina) que atualmente ? descartada no meio
ambiente sem nenhum aproveitamento. As fases do projeto consistiram em
tratamento inicial das fibras em solu??o alcalina (NaOH) ? 0,05 mols para retirada
das impurezas presentes, e desenvolver m?todos para converter estas fibras
(refor?o) misturadas com o poliuretano de mamona (matriz) em eco-comp?sito com
distintas propor??es (5%, 10%, 15% e 20%). Foram estudadas as propriedades da
fibra pela an?lise de MEV, DRX e FTIR. Os comp?sitos foram fabricados em molde
por compress?o com dimens?es 30x30x1cm com um tempo de cura de 24 horas.
Para caracteriza??o dos comp?sitos foram realizados os seguintes ensaios
normatizados: mec?nicos (tra??o, compress?o, dureza shore A), testes absor??o de
?gua, moisture regain e biodegrada??o. As propriedades t?rmicas nas fibras e
comp?sitos foram analisadas por TG, DSC, condutividade t?rmica, resistividade,
capacidade calorifica, resist?ncia t?rmica e dilatometria. Analisando os resultados
destes testes, observou-se que o comp?sito refor?ado com 20% apresentou um
melhor comportamento t?rmico em rela??o aos demais comp?sitos e estabilidade
dimensional quando comparado aos isolantes t?rmicos comerciais. Sendo tamb?m
poss?vel observar um equil?brio na absor??o de umidade dos comp?sitos sendo
evidenciado com o seu maior ?ndice de absor??o nesta mesma amostra (20%). As
micrografias demonstram as regi?es de intera??o da fibra com o poliuretano com
preenchimento dos espa?os vazios. Nos testes de dureza e compress?o podemos
identificar que com o aumento do percentual de fibras o material adquire uma maior
rigidez fazendo se necess?ria uma maior tens?o utilizada para deforma??o. Portanto
mediante os testes realizados nos eco-comp?sitos, o de maior percentual de fibra
utilizado como refor?o em sua composi??o obteve melhor desempenho frente aos
demais eco-comp?sitos, chegando a valores bem pr?ximos ao do PU. / The Sustainability has been evidence in the world today; organizations have sought
to be more and more into this philosophy in their processes, whether products or
attendance. In the present work were manufactured eco-composites with animal fiber
(dog wool) that is currently discarded into the environment without any use. Project
phases consisted on the initial treatment of fibers with alkaline solution (NaOH) at
0.05 mols for removal of impurities, developing methods to convert these fibers
(reinforcement) blended with castor oil polyurethane (matrix) in eco-composite with
different proportions (5%, 10%, 15% and 20%). Fiber properties were evaluated by
analysis of SEM, XRD and FTIR. The composites were produced by compression
molding with dimensions 30x30x1cm. For characterization of the composites the
following tests were performed: mechanical (tensile, compression, shore hardness A)
according the standards and testing water absorption, moisture regain and
biodegradation. The analysis of thermal properties on fibers and composites were by
TG, DSC, thermal conductivity, resistivity, heat capacity and thermal resistance.
Analyzing the results of these tests, it was observed that the composite reinforced
with 20% showed a better thermal performance between others composites and
dimensional stability when compared to commercial thermal insulation. Also is
possible to observe a balance in moisture absorption of the composite being shown
with its higher absorption rate in this same sample (20%). The micrographs show the
fiber interaction regions with polyurethane to fill the empty spaces. In hardness and
compression testing can identify that with increasing percentage of the fiber material
acquires a greater stiffness by making a higher voltage is used for forming
necessary. So by the tests performed in eco-composites, the highest percentage of
fiber used as reinforcement in their composition obtained a better performance
compared to the remaining eco-composites, reaching values very close to the PU.
|
12 |
Modelagem do comportamento ? fadiga de comp?sitos de fibra de vidro a partir de um modelo misto de RNARebou?as, Igor Guedes 17 December 2015 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-06-14T20:19:26Z
No. of bitstreams: 1
IgorGuedesReboucas_DISSERT.pdf: 4109459 bytes, checksum: 9d05bc4fe3e1208e2195bfe4405550de (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-06-15T23:42:40Z (GMT) No. of bitstreams: 1
IgorGuedesReboucas_DISSERT.pdf: 4109459 bytes, checksum: 9d05bc4fe3e1208e2195bfe4405550de (MD5) / Made available in DSpace on 2016-06-15T23:42:40Z (GMT). No. of bitstreams: 1
IgorGuedesReboucas_DISSERT.pdf: 4109459 bytes, checksum: 9d05bc4fe3e1208e2195bfe4405550de (MD5)
Previous issue date: 2015-12-17 / Este trabalho consiste na elabora??o de uma Rede Neural Artificial (RNA) com o fim
de modelar o comportamento de comp?sitos quando submetidos a carregamento de fadiga. A
proposta ? desenvolver e apresentar um modelo misto, que associa uma equa??o anal?tica
(Equa??o de Adam) ? estrutura da RNA. Tendo em vista que os comp?sitos geralmente
apresentam comportamentos semelhantes quando sujeitos a carregamentos flutuantes, essa
equa??o visa estabelecer um padr?o pr?-definido de compara??o para um material gen?rico, a
fim de que a RNA ajuste o comportamento de outro comp?sito a esse padr?o. Dessa forma, a
RNA n?o precisaria aprender por completo o comportamento de determinado material, pois a
Equa??o de Adam faria boa parte do trabalho. Este modelo foi utilizado em duas arquiteturas
de rede diferentes, modular e perceptron, com o objetivo de analisar a sua efici?ncia em
estruturas distintas. Al?m das diferentes arquiteturas, foram analisadas as respostas geradas a
partir de dois conjuntos de dados diferentes ? com tr?s e duas curvas S-N. Esse modelo
tamb?m foi comparado com os resultados da literatura especializada, que utilizam uma
estrutura convencional de RNA. Os resultados consistem em analisar e comparar algumas
caracter?sticas, como a capacidade de generaliza??o, a robustez e os Diagramas de Goodman,
desenvolvidas pelas redes. / This work consists basically in the elaboration of an Artificial Neural Network (ANN)
in order to model the composites materials? behavior when submitted to fatigue loadings. The
proposal is to develop and present a mixed model, which associate an analytical equation
(Adam Equation) to the structure of the ANN. Given that the composites often shows a
similar behavior when subject to float loadings, this equation aims to establish a pre-defined
comparison pattern for a generic material, so that the ANN fit the behavior of another
composite material to that pattern. In this way, the ANN did not need to fully learn the
behavior of a determined material, because the Adam Equation would do the big part of the
job. This model was used in two different network architectures, modular and perceptron,
with the aim of analyze it efficiency in distinct structures. Beyond the different architectures,
it was analyzed the answers generated from two sets of different data ? with three and two SN
curves. This model was also compared to the specialized literature results, which use a
conventional structure of ANN. The results consist in analyze and compare some
characteristics like generalization capacity, robustness and the Goodman Diagrams, developed
by the networks.
|
13 |
Obten??o e caracteriza??o de um comp?sito de matriz polim?rica com carga de res?duos vegetal proveniente do sabugo de milhoOliveira, Mariana Lima de 29 December 2015 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-07-22T15:34:02Z
No. of bitstreams: 1
MarianaLimaDeOliveira_DISSERT.pdf: 1436779 bytes, checksum: b40fe8dddf1d23473972fa9553244479 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-07-27T22:37:51Z (GMT) No. of bitstreams: 1
MarianaLimaDeOliveira_DISSERT.pdf: 1436779 bytes, checksum: b40fe8dddf1d23473972fa9553244479 (MD5) / Made available in DSpace on 2016-07-27T22:37:51Z (GMT). No. of bitstreams: 1
MarianaLimaDeOliveira_DISSERT.pdf: 1436779 bytes, checksum: b40fe8dddf1d23473972fa9553244479 (MD5)
Previous issue date: 2015-12-29 / Foi estudada a viabilidade do uso do farelo do sabugo de milho para a obten??o de um comp?sito de matriz polim?rica. Foram utilizadas tr?s granulometrias e algumas formula??es entre os elementos constituintes do comp?sito, resina poli?ster e farelo do sabugo de milho e determinada qual a formula??o mais adequada levando-se em conta par?metros mec?nicos e t?rmicos. Para a obten??o do farelo, o sabugo passou pelo processo de secagem em secador solar e posteriormente foi triturado numa forrageira, obtendo-se diferentes granulometria atrav?s de peneiramento. Para a caracteriza??o do comp?sito ser?o determinadas propriedades t?rmicas e mec?nicas. A principal vantagem do comp?sito proposto foi sua baixa densidade, abaixo da relativa a resina, em torno de 1,06 Kg/m? para a formula??o com P? Grosso. O comp?sito apresentou comportamento mec?nico inferior ao da resina para todas as granulometrias e formula??es estudadas. Apresentou resultados melhores para a flex?o, alcan?ando 25,3 MPa para o P? Grosso. O comp?sito tamb?m se demonstrou vi?vel para aplica??es t?rmicas, com condutividade t?rmica inferior a 0,21 W/m, classificando-se como isolante t?rmico. Em termos de homogeneidade da mistura a granulometria mais vi?vel ? a PF 20%, que tamb?m apresentou melhor est?tica e uma melhor processabilidade. Tal comp?sito pode ser utilizado para a fabrica??o de estruturas que n?o requeiram significativa resist?ncia mec?nica, como por exemplo, mesas, cadeiras, pranchas, e prot?tipos solares e e?licos, como fornos e fog?es solares e p?s de aero geradores. / The feasibility of using the corn cob to obtain a polymer matrix composite was studied. To obtain the bran, corncob passed the drying process in a solar dryer, and was subsequently triturated in forage and to obtain the different particle sizes, by sieving. Three different grain sizes were used: fine particles (FP) size between 0,10 and 2mm; sized particles (PM) with sizes between 2,10 and 3,35 mm; large particles (PG) sizes between 3,45 and 4,10 mm. Using 20% of residue relative to the resin, the test samples were constructed for characterization of the composite, taking into account thermal and mechanical parameters. The main advantage of the proposed composite is that it has a low density, below the relative resin, about 1.06 kg / m? for the PG. The composite showed a mechanical behavior less than of the resin to the grain sizes and for all formulations studied. Showed better results for the bending, reaching 25.3 MPa for the PG. The composite also showed be feasible for thermal applications, with thermal conductivity less than 0.21 W / m, ranking as insulation. In terms of homogeneity of the mixture, the most viable grain size is the PF, which also showed improved aesthetics and better processability. This composite can be used to make structures that do not require significant mechanical strength, such as tables, chairs, planks, and solar and wind prototypes, such as ovens and cookers and turbines blades.
|
14 |
Obten??o e caracteriza??o de um comp?sito de matriz polim?rica com carga de bucha vegetal luffa cylindricaMota, Maria Kalionara de Freitas 23 February 2016 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2016-08-09T22:54:12Z
No. of bitstreams: 1
MariaKalionaraDeFreitasMota_TESE.pdf: 2448911 bytes, checksum: 324edc16514bb1c73bf850667ec692d8 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2016-08-12T23:50:08Z (GMT) No. of bitstreams: 1
MariaKalionaraDeFreitasMota_TESE.pdf: 2448911 bytes, checksum: 324edc16514bb1c73bf850667ec692d8 (MD5) / Made available in DSpace on 2016-08-12T23:50:08Z (GMT). No. of bitstreams: 1
MariaKalionaraDeFreitasMota_TESE.pdf: 2448911 bytes, checksum: 324edc16514bb1c73bf850667ec692d8 (MD5)
Previous issue date: 2016-02-23 / Os materiais comp?sitos surgem da necessidade de materiais mais leves e com maiores resist?ncias mec?nica e t?rmica. As dificuldades de descarte, reciclagem ou reutiliza??o s?o hoje preocupa??es ambientais e por isso objeto de estudo de muitas pesquisas. Nessa perspectiva estudou-se a viabilidade do uso da bucha vegetal (Luffa Cylindrica) para a obten??o de um comp?sito de matriz polim?rica. Foram testadas seis configura??es/formula??es, com 4, 5 e 6 camadas tratadas e n?o tratadas. As buchas foram tratadas em ?gua fervente para retirar ligninas, ceras e impurezas presentes nas fibras, posteriormente secadas em secador solar de exposi??o direta. Para a caracteriza??o do comp?sito foram determinadas propriedades t?rmicas (condutividade, capacidade t?rmica, difusividade e resistividade), mec?nicas (tra??o e flex?o) e fisicoqu?micas (MEV, DRX, densidade, absor??o e degrada??o). Uma das vantagens do comp?sito proposto foi a baixa densidade das fibras, 066 g/cm?, quase metade da matriz de resina poli?ster, produzindo uma densidade m?dia do comp?sito em torno de 1,17g/cm?, inferior em 6,0% em rela??o a matriz. O tratamento realizado nas buchas trouxe aumento na resist?ncia mec?nica do comp?sito e diminui??o da absor??o de umidade. O comp?sito apresentou comportamento mec?nico inferior ao da resina matriz para todas as formula??es. O comp?sito tamb?m demonstrou-se vi?vel para aplica??es t?rmicas, com condutividade t?rmica inferior a 0,159 W/mk, classificando-se como um bom isolante t?rmico. Para todas as formula??es/configura??es ocorreu uma baixa ader?ncia entre fibras e matriz, com fissuras presentes, mostrando fragilidade em fun??o da baixa impregna??o da fibra pela matriz. Tal comp?sito pode ser utilizado para a fabrica??o de estruturas que n?o requeiram significativa resist?ncia mec?nica, como por exemplo, prot?tipos solares, como fornos e fog?es. / Composite materials arise from the need for lighter materials and with bigger mechanical and thermal resistance. The difficulties of discard, recycling or reuse are currently environmental concerns and, therefore, they are study object of much researches. In this perspective the feasibility of using loofahs (Luffa Cylindrica) for obtainment of a polymeric matrix composite was studied. Six formulations, with 4, 5 and 6 treated layers and untreated, were tested. The loofahs were treated in boiling water to remove lignins, waxes and impurities present in the fibers. After that, they were dried in a direct exposure solar dryer. For the characterization of the composite, thermal (thermal conductivity, thermal capacity, thermal diffusivity and thermal resistivity), mechanical (tensile and bending resistance) and physicochemical (SEM, XRD, density, absorption and degradation) properties were determined. The proposed composite has as advantage the low fiber density, which is around 0.66 g/cm? (almost half of the polyester resin matrix), resulting in an average composite density of around 1.17g/cm?, 6.0 % lower in relation to the matrix. The treatment carried out in the loofahs increased the mechanical strength of the composite and decreased the humidity absorption. The composite showed lower mechanical behavior than the matrix for all the formulations. The composite also demonstrated itself to be feasible for thermal applications, with a value of thermal conductivity of less than 0.159 W/m.K, ranking it as a good thermal insulator. For all formulations/settings a low adherence between fibers and matrix occurred, with the presence of cracks, showing the fragility due to low impregnation of the fiber by the matrix. This composite can be used to manufacture structures that do not require significant mechanical strength, such as solar prototypes, as ovens and stoves.
|
15 |
Viabilidade de utiliza??o de um comp?sito a partir de res?duos para a constru??o de casas popularesGomes, ?verton Rodrigo Barbosa 09 April 2010 (has links)
Made available in DSpace on 2014-12-17T14:57:59Z (GMT). No. of bitstreams: 1
Iverton_DISSERT.pdf: 4635371 bytes, checksum: 17eefa35604e9418c2942edfcdc41624 (MD5)
Previous issue date: 2010-04-09 / Conselho Nacional de Desenvolvimento Cient?fico e Tecnol?gico / Construiu-se uma unidade habitacional utilizando um comp?sito constitu?do de gesso, EPS, borracha triturada, areia e ?gua e foram realizados estudos de conforto t?rmico e de materiais. Utilizou-se uma t?cnica de constru??o conhecida como lan?amento in loco, onde o material comp?sito ? colocado em um molde e ap?s alguns minutos, o material j? se encontrava curado. No interior do molde foram colocadas garrafas PET com o intuito de se obter resist?ncia t?rmica e mec?nica nas paredes constru?das, como tamb?m dar-lhe um fim ecologicamente correto, tendo em vista que tais garrafas ocupam grande espa?o em aterros sanit?rios e necessitam de d?cadas para serem degradadas quando lan?adas ao meio ambiente. Os experimentos t?rmicos demonstraram o conforto proporcionado pelo comp?sito a partir da diferen?a de temperatura entre as superf?cies internas e externas nas paredes, sendo alcan?ados n?veis de at? 11,4?C e do ar no interior da constru??o, em torno de 30,0 ?C ficando dentro da zona de conforto t?rmico para pa?ses de clima quente. Demonstrou-se tamb?m a apropriada resist?ncia mec?nica de tal comp?sito para paredes de fechamento. A utiliza??o do comp?sito proposto pode contribuir para a diminui??o do extremo d?ficit habitacional do nosso pa?s, produzindo resid?ncias populares a baixo custo e com pequeno tempo de obra
|
16 |
Avalia??o do comportamento tribol?gico de comp?sitos poli?ster/fibra de vidro utilizando res?duos de poli?ster/fibra de vidro e carbonato de c?lcio como cargaSouza, Juliana Ricardo de 20 January 2011 (has links)
Made available in DSpace on 2014-12-17T14:58:09Z (GMT). No. of bitstreams: 1
JulianaRS_DISSERT.pdf: 6750114 bytes, checksum: 69dd16ef44916920b2691ed04c45bb4e (MD5)
Previous issue date: 2011-01-20 / The use of composite materials and alternative is being increased every day, as it becomes
more widespread awareness that the use of renewable and not harmful to the environment is
part of a new environmentally friendly model. Since its waste (primarily fiberglass) can not be
easily recycled by the difficulty that still exists in this process, since they have two phases
mixed, a polymeric matrix thermoset difficult to recycle because it is infusible and phase of
fiber reinforcements. Thermoset matrix composites like Polyester + fiberglass pose a threat
due to excessive discharge. Aiming to minimize this problem, aimed to reuse the composite
Polyester + fiber glass, through the wastes obtained by the grinding of knifes and balls. These
residues were incorporated into the new composite Polyester/Fiberglass for hot compression
mold and compared tribological to composites with filler CaCO3, generally used as filler,
targeting a partial replacement of CaCO3 by such waste. The composites were characterized
by thermal analysis (TGA, DSC and DMA), by the surface integrity (roughness
determination, contact angle and surface energy), mechanical properties (hardness) and
tribological tests (wear and coefficient of dynamic friction) in order to evaluate the effect of
loads and characterize these materials for applications that can take, in the tribological point
of view since waste Polyester + fiberglass has great potential for replacement of CaCO3 / A utiliza??o de materiais comp?sitos e alternativos vem sendo incrementada a cada dia, na
medida em que se torna mais generalizada a conscientiza??o de que o uso de recursos
renov?veis e n?o agressivos ao meio ambiente faz parte de um novo modelo ecologicamente
correto. Uma vez que seus res?duos (principalmente Fibra de vidro) n?o podem ser facilmente
reciclados pela dificuldade ainda existente neste processo, j? que apresentam duas fases
misturadas, sendo uma a matriz polim?rica termofixa de dif?cil reciclagem por ser infus?vel e
a fase de refor?os de fibras. Comp?sitos do tipo matriz termofixa de Poli?ster + Fibra de vidro
representam uma amea?a devido ao excesso de descarte. Visando minimizar este problema,
objetivou-se reutilizar o comp?sito Poli?ster + Fibra de vidro, atrav?s de res?duos obtidos pela
moagem de facas e bolas. Estes res?duos foram incorporados a novos comp?sitos de
Poli?ster/Fibra de vidro pela moldagem por compress?o a quente e comparados
tribologicamente a comp?sitos com CaCO3, utilizada geralmente como carga de enchimento,
visando uma substitui??o total ou parcial do CaCO3 por esses res?duos. Os comp?sitos foram
caracterizados por meio t?rmico (TGA, DSC e DMA), da integridade superficial
(determina??o da rugosidade, ?ngulo de contato e energia de superf?cie), de propriedades
mec?nicas (dureza) e de ensaios tribol?gicos (coeficiente de atrito din?mico e desgaste), a fim
de avaliar o efeito das cargas e caracterizar tais materiais para as aplica??es a que podem
assumir, do ponto de vista tribol?gico, j? que res?duos de Poli?ster + Fibra de vidro tem
grande potencial de substitui??o ao CaCO3
|
17 |
Comp?sito para fabrica??o de blocos para constru??o de casas: estudos t?rmico e de materiaisLeite, Jeronimo Mailson Cipriano Carlos 19 August 2011 (has links)
Made available in DSpace on 2014-12-17T14:58:12Z (GMT). No. of bitstreams: 1
JeronimoMCCL_DISSERT.pdf: 5076231 bytes, checksum: e74065a4d5a5c4b4dc38897aa1a14778 (MD5)
Previous issue date: 2011-08-19 / We present two models of blocks made of composite material obtained from the use of
cement, plaster, EPS crushed, shredded tire, mud, sand and water, for the construction of
popular housing. Were made metal molds for the manufacture of blocks to be used in the
construction of a residence for low-income families. Performed tests of compressive strength
of the composite for various formulations that met the specific standard for blocks used in
construction. To study the thermal conductivity of the composite for further study of thermal
comfort generated in a residence built with the proposed composite. We also determined the
mass-specific and water absorption for each formulation studied. Using a home already built
with another composite material, made up the closing of a window with the building blocks
and found the thermal insulation, measuring external and internal temperatures of the blocks.
The blocks had made good thermal insulation of the environment, resulting in differences of
up to 12.6?C between the outer and inner faces. It will be shown the feasibility of using
composite for the end proposed and chosen the most appropriate wording / Apresentam-se doismodelos de blocosfabricados em material comp?sito obtido a partir da
utiliza??o de cimento, gesso, EPS triturado, pneu triturado, barro, areia e ?gua, destinados ?
constru??o de resid?ncias populares. Foram confeccionados moldes met?licos para a
fabrica??o dos blocos a serem utilizados na constru??o de uma resid?ncia para fam?lias de
baixa renda. Foram realizados testes de resist?ncia ? compress?o para v?rias formula??es do
comp?sito que atenderam a norma espec?fica para blocos utilizados na constru??o civil. Foi
tamb?m avaliada a condutividade t?rmica do comp?sito para posterior estudo de conforto
t?rmico gerado em uma resid?ncia constru?da com o comp?sito proposto. Determinou-se
tamb?m a massa espec?fica para cada e a absor??o de ?gua para cada formula??o estudada.
Utilizando-se uma resid?ncia j? constru?da com outro material comp?sito, fez-se o
fechamento de uma janela com os blocos constru?dos e verificou-se a capacidade de
isolamento t?rmico, medindo-se as temperaturas externa e interna dos blocos. Os blocos
confeccionados apresentaram bom isolamento t?rmico do ambiente, obtendo-se diferen?as de
at? 12,6? C entre as faces externa e interna. Ser? demonstrada a viabilidade de utiliza??o do
comp?sito para o fim proposto e escolhida a formula??omais adequada
|
18 |
Avalia??o mec?nica e microestrutural de comp?sitos de poli?ster com adi??o de cargas minerais e res?duos industriaisSantos, Eylisson Andr? dos 26 July 2007 (has links)
Made available in DSpace on 2014-12-17T14:58:25Z (GMT). No. of bitstreams: 1
EylissonAS.pdf: 1489335 bytes, checksum: 8fcffdaaafca0f8691545bd2bc5dd5fc (MD5)
Previous issue date: 2007-07-26 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / With the current growth in consumption of industrialized products and the resulting increase in garbage production, their adequate disposal has become one of the greatest challenges of modern society. The use of industrial solid residues as fillers in composite materials is an idea that emerges aiming at investigating alternatives for reusing these residues, and, at the same time, developing materials with superior properties. In this work, the influence of the addition of sand, diatomite, and industrial residues of polyester and EVA (ethylene vinyl acetate), on the mechanical properties of polymer matrix composites, was studied. The main objective was to evaluate the mechanical properties of the materials with the addition of recycled residue fillers, and compare to those of the pure polyester resin. Composite specimens were fabricated and tested for the evaluation of the flexural properties and Charpy impact resistance. After the mechanical tests, the fracture surface of the specimens was analyzed by scanning electron microscopy (SEM). The results indicate that some of the composites with fillers presented greater Young s modulus than the pure resin; in particular composites made with sand and diatomite, where the increase in modulus was about 168 %. The composites with polyester and EVA presented Young s modulus lower than the resin. Both strength and maximum strain were reduced when fillers were added. The impact resistance was reduced in all composites with fillers when compared to the pure resin, with the exception of the composites with EVA, where an increase of about 6 % was observed. Based on the mechanical tests, microscopy analyses and the compatibility of fillers with the polyester resin, the use of industrial solid residues in composites may be viable, considering that for each type of filler there will be a specific application / Com o crescimento acelerado do consumo de produtos industrializados, principalmente de produtos descart?veis, o aumento excessivo de lixo e sua disposi??o em lugares inadequados tornaramse um dos grandes problemas da sociedade moderna. A utiliza??o de res?duos s?lidos industriais como carga em comp?sitos ? uma id?ia que surge com o intuito de buscar alternativas adequadas para o reaproveitamento desses res?duos, visando tamb?m o desenvolvimento de materiais com propriedades superiores ?quelas dos materiais convencionais. Neste trabalho, estudouse a influ?ncia da adi??o de res?duos industriais de poli?ster e EVA (Etileno Acetato de Vinila), al?m de cargas de areia e diatomita, nas propriedades mec?nicas de comp?sitos de matriz poli?ster. O principal objetivo foi avaliar o comportamento mec?nico desses materiais com a adi??o de cargas de res?duo industrial, comparandoos com as propriedades da resina pura. Corposdeprova foram confeccionados e as propriedades mec?nicas dos comp?sitos obtidos foram analisadas, atrav?s de testes de flex?o e de impacto. Ap?s os ensaios mec?nicos, a superf?cie de fratura dos corposdeprova foi analisada por microscopia eletr?nica de varredura (MEV). Os resultados dos ensaios de flex?o mostraram que alguns comp?sitos apresentaram maior m?dulo, quando comparados com os resultados da resina pura; com destaque para os confeccionados com areia e diatomita, em que o aumento do m?dulo chegou a 168 %. Os comp?sitos confeccionados com adi??o de poli?ster e de EVA apresentaram m?dulo mais baixo que o da resina pura. Tanto o limite de resist?ncia quanto ? deforma??o m?xima, apresentaram redu??o nos seus valores, quando da adi??o de cargas. A resist?ncia ao impacto, em rela??o ? resina pura, foi reduzida em todos os comp?sitos com adi??o de cargas, exceto nos comp?sitos com a adi??o de EVA, onde houve um aumento de aproximadamente 6 %. Com base nos ensaios mec?nicos realizados, nas an?lises microsc?picas e na compatibilidade das cargas com a resina poli?ster, a utiliza??o das cargas de res?duos s?lidos industriais em comp?sitos mostrouse vi?vel, considerando que para cada tipo de carga haver? uma aplica??o espec?fica
|
19 |
An?lise da viabilidade na utiliza??o como isolante t?rmico de um comp?sito de poliuretano/p? de macambiraSoeiro, Eduardo Campelo 25 September 2017 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-01-23T14:20:38Z
No. of bitstreams: 1
EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-01-24T15:35:17Z (GMT) No. of bitstreams: 1
EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5) / Made available in DSpace on 2018-01-24T15:35:17Z (GMT). No. of bitstreams: 1
EduardoCampeloSoeiro_TESE.pdf: 5583136 bytes, checksum: 5052818cde51c6a095f3a8e0f7fa74bc (MD5)
Previous issue date: 2017-09-25 / Nos ?ltimos anos, a preocupa??o com a preserva??o do meio ambiente tem incentivado as pesquisas de novos materiais que utilizem mat?rias primas de fontes naturais renov?veis. Neste trabalho, foram produzidos materiais comp?sitos a partir da associa??o da espuma r?gida de poliuretano, derivado do ?leo de mamona, e o p? de macambira (Brom?lia Laciniosa). Produziram-se tr?s composi??es em molde fechado com 5, 10 e 15% em massa do p? de macambira, denominados PU5, PU10 e PU15, al?m da espuma r?gida de poliuretano puro, PU. As espumas r?gidas de PU e seus comp?sitos foram caracterizados fisicamente atrav?s da densidade aparente, absor??o de ?gua e teor de umidade. A morfologia foi observada atrav?s de imagens feitas por micrografia eletr?nica de varredura (MEV). A identifica??o dos principais grupos org?nicos foi poss?vel com a espectroscopia de infravermelho com transformada de Fourier (FTIR). Foram realizados ensaios de compress?o, tra??o, flex?o em tr?s pontos e dureza para avaliar o comportamento mec?nico. Al?m disso, as an?lises de DRX possibilitaram a determina??o da cristalinidade do material. A termogravimetria possibilitou determina??o das temperaturas limite de resist?ncia ? degrada??o t?rmica dos materiais. Par?metros como a capacidade calor?fica, a condutividade, difusividade e resistividade t?rmicas tamb?m foram determinados. Os comp?sitos PU10 e PU15 apresentaram propriedades t?rmicas semelhantes ao poliuretano puro. Isso mostrou que a utiliza??o do p? de macambira como carga nas propor??es de 10 e 15% em massa ? vi?vel, uma vez que, apesar das semelhan?as nas propriedades, as espumas comp?sitos apresentam vantagens do ponto de vista ambiental e econ?mico, pois parte do volume da espuma ? ocupado pelo p? de macambira, um material biodegrad?vel originado de fonte renov?vel. / In recent years, concern for the preservation of the environment has encouraged research into new materials that use raw materials from renewable natural sources. In this work, composite materials were produced from the association of rigid polyurethane foam derived from castor oil and macambira powder (Bromelia Laciniosa). Three compositions in closed mold with 5, 10 and 15% by mass of the macambira powder, denominated PU5, PU10 and PU15, were produced in addition to the rigid polyurethane rigid PU foam. The rigid PU foams and their composites were physically characterized by apparent density, water absorption and moisture content. The morphology was observed through images made by scanning electron micrograph (SEM). The identification of the main organic groups was possible with Fourier Transform Infrared Spectroscopy (FTIR). Compression, tensile, three point bending and hardness tests were performed to evaluate the mechanical behavior. In addition, the XRD analyzes enabled the determination of the crystallinity of the material. Thermogravimetry allowed the determination of the limiting temperatures of resistance to the thermal degradation of the materials. Parameters such as heat capacity, conductivity, diffusivity and thermal resistivity were also determined. The PU10 and PU15 composites presented thermal properties similar to pure polyurethane. This showed that the use of the macambira powder as a filling in the proportions of 10 and 15% by mass is feasible, because, despite the similarities in properties, the composite foams have advantages from the environmental and economic point of view, since part of the volume of the foam is occupied by the macambira powder, a biodegradable material originating from a renewable source.
|
20 |
Estudo da concentra??o de tens?o dos laminados comp?sitos sandu?ches de resina ep?xi com fibra de vidro e n?cleo de honeycomb carregados ? flex?o / A study on stress concentration in composite epoxi resin laminate sandwiches with glass fiber and honeycomb core under bending situationSilva, Franci?lio Gomes da 15 September 2017 (has links)
Submitted by Automa??o e Estat?stica (sst@bczm.ufrn.br) on 2018-01-23T14:20:39Z
No. of bitstreams: 1
FrancielioGomesDaSilva_TESE.pdf: 46200742 bytes, checksum: c273220eeb68db896d512c7a29a61eb3 (MD5) / Approved for entry into archive by Arlan Eloi Leite Silva (eloihistoriador@yahoo.com.br) on 2018-01-24T16:14:11Z (GMT) No. of bitstreams: 1
FrancielioGomesDaSilva_TESE.pdf: 46200742 bytes, checksum: c273220eeb68db896d512c7a29a61eb3 (MD5) / Made available in DSpace on 2018-01-24T16:14:11Z (GMT). No. of bitstreams: 1
FrancielioGomesDaSilva_TESE.pdf: 46200742 bytes, checksum: c273220eeb68db896d512c7a29a61eb3 (MD5)
Previous issue date: 2017-09-15 / Esse trabalho consiste no estudo do comportamento das propriedades mec?nicas do comp?sito laminado sandu?che com n?cleo de honeycomb, submetido ? flex?o em 4 pontos, fabricado pela ind?stria aeron?utica. O mesmo tem como principais objetivos a an?lise da concentra??o de tens?o e um estudo detalhado dos modelos e crit?rios de falha que ocorre nesses materiais. De acordo com normas ASTM, confeccionou-se corpos de prova sem furo LS e com furo LSF circular conc?ntrico. Este estudo foi realizado em diversos laminados comp?sitos sandu?ches com diferentes dimens?es de largura e di?metro do furo. Para o estudo de concentra??o de tens?o efetuou-se o comparativo entre os modelos te?rico como o Crit?rio da Tens?o M?dia (Average Stress Criterion - ASC), o Crit?rio da Tens?o Pontual (Point Stress Criterion - PSC), o modelo de falha inerente, (Inherent flaw model - IFM) e o Crit?rio de Tens?o M?xima (Maximum Stress criterion - MSC) em conjunto com os dados experimentais e os resultados de simula??o matem?tica pelo M?todo dos Elementos Finitos (MEF). Al?m disso, foram tamb?m desenvolvidas t?cnicas de an?lise, j? consagradas na literatura, para determina??o das propriedades mec?nicas residuais devido a influ?ncia do furo, com o objetivo de produzir um modelo de falha que defina o comportamento do material sob a??o da concentra??o de tens?o. Todos os comparativos foram feitos com o intuito de se obter uma boa previsibilidade entre os dados experimentais com os modelos propostos e os resultados num?ricos. J? a an?lise da concentra??o de tens?o em torno do furo foi realizada pelo monitoramento da tens?o m?dia dos extens?metros submetido at? a tens?o m?xima de flex?o. A modifica??o dos m?todos PSC, ASC e IFM, a partir dos resultados experimentais do LSF, ? algo que foi verificado com exclusividade neste trabalho, onde traz uma metodologia nova para a ?rea de concentra??o de tens?es em comp?sitos. A partir dos dados experimentais e da micromec?nica, dos resultados anal?tico e matem?ticos (MEF) gerou-se curvas de concentra??o de tens?o em torno do furo. Quando D/W era superior a 0,3 os valores anal?ticos come?aram a apresentar concentra??o de tens?es superior ao valor obtido experimentalmente, como no caso das amostras W90D32 e W90D38.
|
Page generated in 0.0724 seconds