<p>U disertaciji su prikazani rezultati sopstvenog eksperimentalnog istraživanja mogućnosti primjene biopepela, nastalog sagorjevanjem žetvenih ostataka, kao mineralnog dodatka u cementnim kompozitima: malterima i betonima. Istraživanje je zasnovano na komparativnoj analizi 27 vrsta maltera u kojima je varirana vrsta biopepela i vrsta sitnozrnog agregata i 12 vrsta betona koje se razlikuju u vrsti veziva i u krupnom agregatu. Na očvrslom malteru su ispitani: konzistencija, čvrstoća pri pritisku i kapilarno upijanje vode, a na očvrslom betonu ispitivani su kapilarno upijanje vode, skupljanje pri sušenju, čvrstoća pri pritisku, dinamički modul elastičnosti, otpornost na habanje, vodonepropustljivost i čvrstoća na savijanje. Istaknuto je da se primjenom biopepela kao zamjene dijela cementa mogu dobiti konstrukcijski malteri i betoni, odnosno betoni sa zadovoljavajućim fizičkim i mehaničkim karakteristikama.</p> / <p>The dissertation presents the results of an own experimental research on the possibility of using biomass ash as a mineral additive in cement composites: mortar and concrete. The research is based on a comparative analysis of 27 types of mortars in which the type of biomass ash and the type of fine-grained aggregate were varied, as well as 12 types of concrete that differ in the type of binder and coarse aggregate. Following properties were tested on hardened mortars: consistency, compressive strength and capillary water absorption, and on hardened concrete: capillary water absorption, drying shrinkage, compressive strength, dinamic modulus of elasticity, wear resistance, waterpermeability and flexural strength. It was pointed out that biomass ash can be used as a replacement of a part of cement, thereby obtaining satisfactory physical and mechanical characteristics.</p>

From the Proceedings of the 1972 Meetings of the Arizona Section - American Water Resources Assn. and the Hydrology Section - Arizona Academy of Science - May 5-6, 1972, Prescott, Arizona / Land is subsiding over a heavily mined aquifer in south central Arizona. Subsidence damages are inventoried to help provide a basis upon which cost studies can be performed to determine actions to lessen the economic impact of these damages. Water table drawdown produces increasing loading stress by three ways: changes in bouyant support of aquifer grains, changes in water table, or both. Two types of subsidence are recognized--one-directional compression, and near surface phenomenon. Damages due to natural structures, and to man-made structures are reviewed. Agricultural damages include field releveling, ditch repair and well damage. Damages to transportational facilities include highways, bridges, pipelines, and railroads. Damages to domestic and urban structures are suggested. Questionnaires, interviews and on-site inspections were used to collect information on land subsidence damages in the study area.

In the face of technological advances in concrete science emerged so-called special concretes and, among these, the self-compacting concrete (SCC), developed in Japan in the 1980s. This concrete is currently considered one of the greatest advances in concrete technology in view of its numerous advantages (decrease of construction duration, decrease of concreting labor, improvement of the working environment, improvement of the quality and durability of structures etc.). The production of SCC requires different mix design methods related to those applied for conventional concrete. Among these differences are highlighted the determination of the aggregate compositions and the addition of fine materials and chemical admixtures. In the case of determining the aggregate composition, the method of unit mass has been applied in SCC. However, it is common the use of this method in binary combinations, but for ternary and quaternary combinations it is quite limited. Thus, this work aimed to analyze the influence of different combinations and compositions of aggregates, determined by the method of unit mass and void ratio, to obtaining and characterization of SCC. For this, initially the procedures of the method was standardized. It was used two types of natural fine and coarse aggregates with different physical characteristics. It was produced 9 different aggregate compositions, four binary, ternary and quaternary four. For each composition, one SCC was formulated, based on previous dosage studies. The selfcompactability properties of the concrete were analyzed by spreading, V funnel test and L box test. In case hardened state the compressive strength was determined. The results showed that different methods of execution procedures showed no differences. The method of unit mass proved to be efficient in determining aggregate compositions to supply the SCC. For the same volume and paste composition (cement, water, chemical and mineral admixtures) the quaternary composition was the most efficient in meeting the properties of selfcompactability and compressive strength. / Diante dos avanços tecnológicos na ciência do concreto surgiram os chamados concretos especiais e, dentre estes, pode-se citar o concreto autoadensável (CAA), desenvolvido no Japão, na década de 1980. Este concreto é atualmente considerado um dos maiores avanços na tecnologia do concreto tendo em vista as suas inúmeras vantagens (diminuição do tempo da obra, diminuição da mão de obra de concretagem, melhora o ambiente de trabalho, melhora a qualidade e durabilidade da estrutura e etc.). A obtenção do CAA requer métodos de dosagens diferentes dos aplicados em concretos convencionais. Dentre essas diferenças se destacam a determinação das composições de agregados e a adição de materiais finos e aditivos químicos. Em se tratando da determinação da composição de agregados o método da massa unitária vem sendo aplicado em CAA. Entretanto é comum sua utilização em combinações binárias, já para combinações ternárias e quaternárias é bastante limitado. Neste sentido, foram analisadas diferentes combinações e composições de agregados, determinadas pelo método da massa unitária e do índice de vazios, na obtenção e caracterização de CAA. Para isso, inicialmente procurou-se padronizar os procedimentos de execução do método. Utilizou-se dois tipos de agregados miúdos e graúdos naturais com diferentes características físicas, sendo produzidas 9 composições distintas, sendo quatro binárias, quatro ternárias e uma quaternária. Para cada composição foi formulado um CAA, tomando como base a dosagem em estudos prévios. As propriedades de autoadensabilidade do concreto foram analisadas através dos ensaios de espalhamento, funil V e caixa L. No estado endurecido a resistência à compressão foi determinada. Os resultados mostraram que os diferentes procedimentos de execução do método não apresentaram divergências. O método da massa unitária mostrou-se eficiente na determinação de composições de agregado para atendimento ao CAA. Para um mesmo volume e composição de pasta (cimento, água, aditivos e adições) a composição quaternária foi a mais eficiente no atendimento às propriedades de autoadensabilidade e resistência à compressão.

Submitted by ANA FLÁVIA NUNES E REIS null (dra-anaflavia@uol.com.br) on 2016-01-26T19:16:31Z No. of bitstreams: 1 merged (4).pdf: 4937949 bytes, checksum: c052666784bd930ac4748e41040c73bd (MD5) / Approved for entry into archive by Ana Paula Grisoto (grisotoana@reitoria.unesp.br) on 2016-01-28T13:31:20Z (GMT) No. of bitstreams: 1 reis_afn_me_sjc.pdf: 4937949 bytes, checksum: c052666784bd930ac4748e41040c73bd (MD5) / Made available in DSpace on 2016-01-28T13:31:20Z (GMT). No. of bitstreams: 1 reis_afn_me_sjc.pdf: 4937949 bytes, checksum: c052666784bd930ac4748e41040c73bd (MD5) Previous issue date: 2015-12-15 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi infiltrar sílica em uma cerâmica Y-TZP, avaliar seu efeito na resistência à flexão Biaxial, e na união com a porcelana feldspática. Para a análise da resistência à flexão foram confeccionados 180 discos de zircônia, 120 de 0,5mm e 60 com 1,2mm discos (14 mm de diâmetro). 90 discos foram infiltrados com sílica pelo método sol-gel em temperatura ambiente (n = 30). A espessura do disco foi de 1,2 mm para os espécimes controle (espécime sem porcelana, n = 30). O recobrimento por porcelana feldspática foi de duas espessuras (0,5mm e 1 mm) sobre a zircônia que tinha 0,5 mm. Os espécimes com porcelana foram polidos com lixas de carbeto de silício (SiC) de granulação # 400, 600, 800 e 1200. Obtivemos 6 grupos: dois monolíticos (ZR- Zircônia Monolítica sem infiltração e ZRI- Zircônia Monolítica Infiltrada) (controle) e quatro estratificados: ZRF 1,0 (0,5mm Zircônia coberta com 0,5 mm porcelana), ZRIF 1,0 (0,5 mm Zircônia infiltrada coberta com 0,5 mm de porcelana), ZRF 1,5 (0,5 mm Zircônia infiltrada coberta com 1,0 mm de porcelana) ZRIF 1,5- Zircônia infiltrada (0,5 mm Zircônia infiltrada coberta com 1,0 mm de porcelana). Após o ensaio de flexão biaxial em meio aquoso, foram determinados o módulo de Weibull (m) e resistência característica (σθ). Os fragmentos foram analisados em EDS, MEV, DRX e FTIR. A Dureza (H) e tenacidade a fratura foram analisadas pela nanoindentação, já o módulo elástico (E) por duas técnicas, nanoindentação e por impulso, e para avaliar a adesão entre a zircônia e a porcelana foi aplicado o Teste de Scratch. Foram modeladas 7 condições experimentais e analisados pelo método por elementos finitos. A zircônia monolítica infiltrada mostrou uma estrutura com grãos arredondados envoltos em uma matriz de sílica, e a presença de zircônia cúbica e tetragonal. O DRX revelou a formação de ZrSiO4 nos grupos infiltrados. Os grupos monolíticos apresentaram módulos de Weibull superiores aos dos grupos com porcelana. Com a análise (AEF) não houve diferença entre os grupos com a mesma espessura, já para o grupo recoberto com 0,5 mm de porcelana, os valores de tração e compressão foram maiores. A cerâmica infiltrada apresentou microestrutura diferente, e a adesão da porcelana à zircônia não-infiltrada foi superior à da zircônia infiltrada. / The objective was to infiltrate silica in a Y- TZP ceramics, evaluate its effect on resistance biaxial strenght, and the union with feldspathic porcelain. For the analysis of flexural strength were prepared zirconia discs 180, 120 and 60 of 0.5 mm to 1.2 mm disks (14 mm diameter). 90 discs were infiltrated with silica by the sol-gel method at room temperature (n = 30). The thickness of the disk was 1.2 mm for the samples control (no porcelain specimen, n = 30). The coating was feldspathic porcelain by two thicknesses (0.5 mm and 1 mm) of zirconia, which had 0.5 mm. Specimens with porcelain were polished with sandpaper silicon carbide (SiC) granulation # 400, 600, 800 and 1200. We obtained six groups: two monolithic (Zr-Zirconia Monolithic without infiltration and ZRI- Zirconia monolithic Infiltrated) (control) and four laminated ZRF 1.0 (0.5 mm zirconia covered with 0.5 mm porcelain), ZRIF 1.0 (0.5 mm infiltrated zirconia covered with 0.5 mm of porcelain), ZRF 1.5 (0.5 mm infiltrated zirconia covered with 1.0 mm of porcelain) ZRIF 1,5-infiltrated Zirconia (0.5 mm infiltrated zirconia covered with 1.0 mm of porcelain). After the biaxial bending test in an aqueous medium were determined Weibull modulus (m) and the characteristic strength (σθ). The fragments were analyzed by EDS, SEM, XRD and FTIR. The hardness (H) and fracture toughness were analyzed by nanoindentation, since the elastic modulus (E) by two techniques, nanoindentation and on impulse, and to evaluate the adhesion between the zirconia and porcelain was applied Scratch Test. 7 experimental conditions were modeled and analyzed by the finite element method. The infiltrated zirconia showed a monolithic structure with rounded grain wrapped in a silica matrix, and the presence of cubic and tetragonal zirconia. The XRD showed the formation of ZrSiO4 infiltrates in groups. The monolithic modules Weibull groups showed superior to porcelain groups. With the analysis (FEA) there was no difference between the groups with the same thickness, for now the group covered with 0.5 mm of porcelain, the tensile and compressive values were higher. The infiltrated ceramic showed different microstructure, and the accession of porcelain to non- infiltrated zirconia was higher than the infiltrated zirconia.

To develop a project sizing concrete pavement is necessary to know the mechanical properties and the different treatment processes of material to be used. This study aimed to analyze the mechanical properties such as flexural strenght, compressive strength, indirect tensile strength and static modulus of concrete paving. The three types of concrete were studied: An actual reference (typically used in paving, one with the addition of polypropylene fibers (common practice for floors), and a high strength concrete used to rapidly release the traffic. Different methods of curing were applied: chemical cure with and without the use of wet burlap bags (widely applied in pavements) and curing in a moist chamber (as recommended by standard). This evaluation of the mechanical properties for the concrete studied in different curing methods applied, showed that the microstructure of concrete is significantly interfering with the results, especially in cured concrete to track conditions (chemical cure without and with the placement of burlap sacks). Where factors such as the absorption and reabsorption of water evaporation to cement hydration, cracking the interface folder / aggregate, ambient conditions related to temperature and humidity, are interfering with the tensile strength in bending, compressive strength, indirect tensile strength and particularly in the static modulus and still, from the results obtained in this study and those reported by other authors who studied a high-strength concrete, it is possible to verify that there are particularities still unknown about the behavior of high strength concrete. / Para o desenvolvimento de um projeto de dimensionamento de pavimentos de concreto é necessário conhecer as propriedades mecânicas e os diferentes processos de tratamento do material a ser utilizado. Este trabalho teve por objetivo analisar as propriedades mecânicas, tais como, resistência à tração na flexão, resistência à compressão axial, resistência à tração por compressão diametral e módulo de elasticidade estático em concretos para pavimentação. Foram estudados os três tipos de concretos: um concreto referência, (tipicamente empregado em pavimentação, outro com a adição de fibras de polipropileno (prática comum em pavimentos) e um concreto de alta resistência, utilizado para rápida liberação ao tráfego. Diferentes métodos de cura foram aplicados: cura química com e sem a utilização de sacos de aniagem úmidos (largamente aplicados em pavimentos) e cura em câmara úmida (conforme preconizado por norma). A avalição das propriedades mecânicas para os concretos estudados, nos diferentes métodos de cura aplicados, mostrou que a microestrutura dos concretos, está interferindo de forma significativa nos resultados obtidos, principalmente nos concretos curados para condições de pista (cura química sem e com a colocação de sacos de aniagem), onde fatores como a absorção e reabsorção da água de evaporação para hidratação do cimento, a fissuração da interface pasta/agregado, as condições ambientes relacionadas à temperatura e umidade, estejam interferindo na resistência à tração na flexão, resistência à compressão axial, resistência à tração por compressão diametral e principalmente no módulo de elasticidade estático e ainda, a partir dos resultados obtidos na presente pesquisa e daqueles apresentados por outros autores que estudaram um concreto de alta resistência, é possível verificar que existem particularidades ainda desconhecidas sobre o comportamento do concreto de alta resistência.

Submitted by Aelson Maciera (aelsoncm@terra.com.br) on 2017-04-25T16:48:28Z No. of bitstreams: 1 DissCEGS.pdf: 4427743 bytes, checksum: 5e99637e07f5406510f1f85b9c5e9cc1 (MD5) / Approved for entry into archive by Ronildo Prado (ronisp@ufscar.br) on 2017-04-26T19:34:47Z (GMT) No. of bitstreams: 1 DissCEGS.pdf: 4427743 bytes, checksum: 5e99637e07f5406510f1f85b9c5e9cc1 (MD5) / Approved for entry into archive by Ronildo Prado (ronisp@ufscar.br) on 2017-04-26T19:34:57Z (GMT) No. of bitstreams: 1 DissCEGS.pdf: 4427743 bytes, checksum: 5e99637e07f5406510f1f85b9c5e9cc1 (MD5) / Made available in DSpace on 2017-04-26T19:58:36Z (GMT). No. of bitstreams: 1 DissCEGS.pdf: 4427743 bytes, checksum: 5e99637e07f5406510f1f85b9c5e9cc1 (MD5) Previous issue date: 2016-12-02 / Não recebi financiamento / This research aimed to investigate, with the aid of the Brazilian standard NBR 7190 (1990) Wood Structures Project, of the Kruskal-Wallis analysis of variance (ANOVA), and the regrouping bootstrap technique, the influence of extraction regions Caracaraí, Bonfim and Claudia, in physical and mechanical properties of Cupiúba wood (Goupia Glabra Aubl), and assess the possibility of estimate (linear, exponential, geometric and logarithmic mathematical models) the physical and mechanical properties investigated as a function of density. The results of ANOVA indicated equivalence in 94% of the properties of the regions of Caracaraí and Claudia, and no equivalence in 50% of the properties in the region of Bonfim, even after extrapolated by the bootstrap technique, the non-equivalence was still 44%, whereas the results obtained from the regression model implied a possibility of an estimate of the physical and mechanical properties of Cupiúba wood due to its apparent density. / Esta pesquisa objetivou investigar, com o auxílio da norma brasileira NBR 7190 (1990) Projeto de Estruturas de Madeira, da Análise de Variância de Kruskal-Wallis (ANOVA) e da técnica bootstrap de reagrupamento, a influência das regiões de extração Caracaraí, Bonfim e Claudia, em propriedades físicas e mecânicas da madeira de Cupiúba (Goupia Glabra Aubl), assim como avaliar a possibilidade da estimativa (modelos linear, exponencial, geométrico, logarítmico) das propriedades físicas e mecânicas investigadas em função da densidade aparente. Os resultados da ANOVA indicaram equivalência em 94% das propriedades das regiões de Caracaraí e Cláudia, e não equivalência em 50% das propriedades da região de Bonfim, e mesmo depois de extrapolados pela técnica bootstrap, apresentou não equivalência em 44% das propriedades. Os resultados obtidos dos modelos de regressão implicaram na possibilidade da estimativa das propriedades físicas e mecânicas da madeira de Cupiúba em função da densidade aparente.

Made available in DSpace on 2016-12-08T17:19:23Z (GMT). No. of bitstreams: 1 Andrea Luciane M Soares.pdf: 1356785 bytes, checksum: 08654c7f08e5db11d8746af3551cd3ed (MD5) Previous issue date: 2014-07-28 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / This work investigates the effect by partial replacement of nanosilica (nS) of Portland cement on the mechanical, physical, chemical and microstructural Portland cement mortar properties. For better understanding of the effects and a more detailed analysis of the results, the 33-1 fractional factorial design to design of experiments was used with three factors, each at three levels: nS content cement replacement (1, 2 and 3wt. %), water/cement ratio (1.1, 1.4 and 1.7 weight) and the aggregate/cement ratio (7.04 factor, 8.53 and 10.05 weight). The processing of the nine mortar mixtures was performed according to standards of the manufacture of such construction materials (composition, mixing, molding, curing and specimen preparation). Mechanical properties were evaluated in the fresh state (flow table) and in the hardened state (compressive strength at 7, 28 and 90 days of curing). In order to correlate the compressive strength with the microstructural characteristics, physic, chemical and microstructural characterization was performed. X-ray diffraction (XRD), infrared spectroscopy (FTIR), thermal (TG/DTA) and scanning electron microscopic with energy-dispersive X-ray spectrometry (SEM/EDS) analyses were used on selected samples. The use of fractional factorial design and the response surface methodology was found to be in the design the experimental and statistical analyses. The addition of nS affects the mechanical properties of mortars, both in the fresh, and in the hardened state. Materials with adequate workability for use in construction industry (consistency of 230 ± 10 mm) and high compressive strength after 7 (&#8805; 3 MPa) and 28 days of curing (&#8805; 6 MPa) were obtained with the following composition: 1.5 wt. % nS, 1.3 water/cement ratio and aggregate/cement ratio kept constant of 10.1. The physical-chemical and microstructural characterization showed that nS contributes to improve the packing of the amorphous calcium silicate hydrate (C-S-H) and crystalline phases matrix and aggregate. Moreover, nS participates in the hydration reactions of Portland cement due to its reaction with calcium hydroxide. Thus, a more cohesive matrix and less calcium hydroxide contributes to lower porosity, thus reducing permeability, which contributes for better durability of the mortars containing nS. / Este trabalho investiga o efeito da substituição parcial de cimento Portland por nanosílica (nS) nas propriedades mecânicas, físico-químicas e microestruturais de argamassas de cimento Portland. Para melhor compreensão dos efeitos e uma análise mais detalhada dos resultados, foi usado o planejamento fatorial fracionado 33-1 para projeto dos experimentos. No projeto foram utilizados três fatores, cada qual em três níveis: o teor de nS em substituição ao cimento (1%, 2% e 3% em massa), a proporção de água/cimento (1,1; 1,4 e 1,7 em massa) e o fator agregado/cimento (7,04; 8,53 e 10,05 em massa). O processamento das nove misturas de argamassas foi realizado de acordo com as normas de fabricação desses materiais de construção civil (pesagem, mistura, moldagem, cura e preparação de corpos de prova). Propriedades mecânicas foram avaliadas no estado fresco (índice de consistência) e no estado endurecido (resistência mecânica à compressão em 7, 28 e 90 dias de cura). Com o objetivo de correlacionar a resistência à compressão com as características microestruturais, foi realizada a caracterização físico-química e microestrutural, por meio de análises de raios X (DRX), espectroscopia de infravermelho por transformada de Fourier (FTIR), análises térmicas (TG) e análise térmica diferencial (ATD) e de microscopia eletrônica de varredura (MEV/EDS) em amostras selecionadas. O uso do projeto fatorial fracionado se mostrou eficiente para o planejamento experimental e análises estatísticas juntamente com o uso da metodologia de superfície de resposta. A adição de nS nas argamassas afeta as propriedades mecânicas das argamassas, tanto no estado fresco, como no endurecido. Materiais com trabalhabilidade adequada para uso na construção civil (índice de consistência de 230 ± 10 mm) e elevada resistência à compressão após 7 (&#8805; 3MPa) e 28 dias de cura (&#8805; 6 MPa) foram obtidas com as seguintes composições: 1,5% de nS, 1,3 água/cimento e 10,1 agregado/cimento. A caracterização físico-química e microestrutural mostrou que a nS contribui para melhorar o empacotamento da matriz formada pelo silicato de cálcio hidratado amorfo (C-S-H), fases cristalinas e os agregados. Além disso, a nS participa das reações de hidratação do cimento Portland, por meio do consumo de hidróxido de cálcio. Dessa forma, uma matriz mais coesa e menos hidróxido de cálcio contribui para uma menor porosidade, reduzindo a permeabilidade, que se traduz numa melhor durabilidade das argamassas contendo nS.

Materiais odontológicos inovadores que apresentem propriedades antimicrobianas são altamente desejáveis na cavidade oral. O objetivo deste estudo foi avaliar a atividade antimicrobiana do vanadato de prata nanoestruturado (&beta;-AgVO3) incorporado em duas resinas acrílicas frente a Candida albicans, Streptococcus mutans, Staphylococcus aureus e Pseudomonas aeruginosa, além de examinar as propriedades mecânicas e o padrão de incorporação do nanomaterial nas resinas. O nanomaterial foi caracterizado por difração de raios X (DRX), espectroscopia no infravermelho por transformada de Fourier (FTIV), análise elementar por energia dispersiva (EDS) e microscopia eletrônica de varredura (MEV). As propriedades antimicrobianas das resinas acrílicas incorporadas com diferentes porcentagens de &beta;-AgVO3 foram investigadas pelo método de redução do XTT, unidades formadoras de colônias (UFC) e microscopia confocal à laser e o comportamento mecânico por meio de ensaios de dureza e rugosidade superficial, resistência à flexão, à compressão e ao impacto. O padrão de incorporação do &beta;-AgVO3 nas resinas foi analisado por microscopia eletrônica de varredura (MEV) e análise elementar por energia dispersiva (EDS). Os dados foram analisados por ANOVA, Tukey e pelo teste Generalized Linear Models (&alpha;=0,05). Para ambas as resinas, em relação ao grupo controle, a incorporação de 5% e 10% de &beta;-AgVO3 reduziram significantemente a atividade metabólica de C. albicans e P. aeruginosa (p<0,05), enquanto que para S. mutans houve redução significante apenas com a incorporação de 10% (p<0,05). Não houve diferença na atividade metabólica pelo método do XTT frente a S. aureus (p> 0,05). Para ambas as resinas, observou-se uma redução significativa no número de UFC/mL de C. albicans para o grupo incorporado com 10% de &beta;-AgVO3 e de S. mutans para os grupos com 2,5%, 5% e 10% do nanomaterial (p<0,05). Para S. aureus e P. aeruginosa, houve redução significante com a incorporação de 5% e 10% (p<0,05). A dureza superficial da resina termopolimerizável permaneceu inalterada pela incorporação do nanomaterial (p>0,05) e da autopolimerizável aumentou com 0,5% (p<0,05). Concentrações maiores que 1% promoveram redução na resistência flexural das resinas (p<0,05) enquanto que a rugosidade superficial permaneceu inalterada (p>0,05). A resistência à compressão da resina autopolimerizável permaneceu inalterada (p>0,05) e da termopolimerizável reduziu com a incorporação de 0,5% e 10% (p<0,05). As concentrações de 5% e 10% promoveram redução significante na resistência ao impacto das resinas, em relação ao controle (p<0,05). A caracterização das resinas quanto a dispersão da carga utilizada mostrou a presença de domínios de &beta;-AgVO3 ao longo da matriz polimérica seguindo um padrão circular. Conclui-se que o método proposto foi capaz de promover atividade antimicrobiana às resinas acrílicas frente aos micro-organismos avaliados, sendo a mesma dependente da concentração do nanomaterial. Porém, alterações na dispersão do &beta;-AgVO3 na matriz dos polímeros são necessárias para não sacrificar as propriedades mecânicas e para potencializar o efeito antimicrobiano / Innovative dental materials that have antimicrobial properties are highly desirable in the oral cavity. The aim of this study was to evaluate the antimicrobial activity of nanostructured silver vanadate (&beta;-AgVO3) incorporated into two acrylic resins against Candida albicans, Streptococcus mutans, Staphylococcus aureus and Pseudomonas aeruginosa, while examining the mechanical properties and the pattern of nanomaterial incorporation into resins. The nanomaterial was characterized by X-ray diffraction (XRD), infrared spectroscopy Fourier transform (FTIR), elemental analysis by energy dispersive (EDS) and scanning electron microscopy (SEM). The antimicrobial properties of acrylic resins incorporated with different percentages of &beta;-AgVO3 were investigated by the reduction of XTT method, colony forming units (CFU) and confocal laser microscopy and the mechanical behavior through hardness, surface roughness, flexural, compression and impact tests. The pattern of incorporation of &beta;-AgVO3 resins was analyzed by scanning electron microscopy (SEM) and elemental analysis by energy dispersive (EDS). Data were analyzed by ANOVA, Tukey test and the Generalized Linear Models (&alpha; = 0.05). For both resins, compared to the control group, the incorporation of 5% and 10% &beta;-AgVO3 caused a significantly reduced in the metabolic activity of C. albicans and P. aeruginosa (p <0.05), while for S. mutans significant reduction was observed only with the incorporation of 10% (p <0.05). There was no difference in metabolic activity by XTT method against S. aureus (p> 0.05). For both resins, there was a significant reduction in the number of CFU / mL for C. albicans incorporated group with 10% &beta;-AgVO3 and S. mutans in groups with 2.5%, 5% and 10% of nanomaterial (p <0.05). For P. aeruginosa and S. aureus, there was a significant decrease with the incorporation of 5% to 10% (p <0.05). The surface hardness of the heat-cured resin was unchanged by the incorporation of the nanomaterial (p <0.05) and increased self-cured with 0.5% (p <0.05). Concentrations above 1% promote the reduction in flexural strength of the resins (p <0.05) while the surface roughness remained unchanged (P> 0.05). The compressive strength of the self-cured resin remained unchanged (P> 0.05) and heat-cured reduced with the incorporation of 0.5% and 10% (p <0.05). Concentrations of 5% and 10% caused a significant reduction in impact strength of resins, compared to control (p <0.05). The characterization of the resins as the dispersion of the filler used showed the presence of &beta;-AgVO3 domains along the polymer matrix following a circular pattern. It was concluded that the proposed method was able to promote antimicrobial activity to acrylic resins against microorganisms evaluated, with the same concentration dependent of the nanomaterial. However, changes in the &beta;-AgVO3 dispersion in the polymer matrix are necessary to do not sacrifice the mechanical properties and to enhance the antimicrobial effect

Made available in DSpace on 2014-07-29T15:03:32Z (GMT). No. of bitstreams: 1 dissertacaoDanilo.pdf: 2147690 bytes, checksum: c918dd24c275d43fcca4fc1283e857a6 (MD5) Previous issue date: 2008-10-03 / Even though the different sizes of cylindrical specimens for tests in concrete are standardized to get the simple compressive strength and the modulus of elasticity, this factor is not usually studied in most researches. So, the goal of this thesis was to evaluate the influence of the size of the specimens in the initial tangent modulus of elasticity (Eci) and in the compressive strength (fc), correlate the values of fc and Eci, and compare the values of modulus of elasticity that were estimated by the equations proposed by the Brazilian code (NBR 6118/2003) and by the American norm (ACI 318/2002). Concretes with three levels of strength were used after 28 days: 25MPa, 30MPa and 40MPa. They were all proportionally mixed with materials of the region and supplied by only one concrete batching plant of Goiânia GO. The tests of compressive strength and initial tangent modulus of elasticity were done in cylindrical specimens of 100 x 200 mm and 150 x 300 mm after 28 days. The samples were collected during the delivery of the concrete in the construction sites. For each truck, ten specimens were molded, five of 100 x 200 mm and five of 150 x 300 mm. Of the 600 specimens that were molded, 240 tests of compressive strength and 360 tests of modulus of elasticity were done. The cure was in a tank with water saturated with limestone. After the tests were done, the statistical analysis of the results was done. The variance analysis (ANOVA) indicated that the size of the specimen exerts influence only on the results of the initial tangent modulus of elasticity (Eci). There is a tendency for the specimens of 100 x 200 mm to show greater results for the modulus of elasticity of the concrete than the specimens of 150 x 300 mm. In the compressive strength, only the level of strength significantly exerted influence on the results. It was also observed that the NBR 6118/2003 overestimates the values of modulus of elasticity of the researched concretes and the results are better adequate to the model proposed by the ACI 318/02. / Apesar dos parâmetros de ensaios, como o tamanho do corpo de prova, influenciarem nos resultados do módulo de deformação e da resistência a compressão, normalmente esse fator não é estudado na maioria das pesquisas. Assim, esta dissertação objetivou avaliar a influência do tamanho dos corpos de prova no módulo de deformação tangente inicial (Eci), e na resistência a compressão (fc), correlacionar os valores de fc e Eci e comparar os valores de módulo de deformação alcançados com os valores estimados pelas equações propostas pela norma brasileira (NBR 6118/2003) e pelo amaericana (ACI 318/2002). Utilizaram-se concretos com três níveis de resistência aos 28 dias: 25MPa, 30MPa e 40Mpa, todos dosados com materiais da região e fornecidos por uma mesma central de concreto de Goiânia - GO. Os ensaios de resistência à compressão e de módulo de deformação tangente inicial foram realizados em corpos de prova cilíndricos de 100 x 200 mm e 150 x 300 mm aos 28 dias. As amostras foram coletadas durante a entrega do concreto nas obras. A cada caminhão, eram moldados dez corpos de prova, cinco de 100 x 200 mm e cinco de 150 x 300 mm. Foram moldados 600 corpos de prova, onde realizaram-se 240 ensaios de resistência à compressão e 360 de módulo de deformação. A cura foi em tanque com água saturada com cal. Após a realização dos ensaios, fez-se a análise estatística dos resultados obtidos. A análise de variância (ANOVA) indicou que o tamanho do corpo de prova exerce influência apenas nos resultados do módulo de deformação tangente inicial (Eci). Houve uma tendência dos corpos de prova de 100 x 200 mm apresentarem maiores resultados para o módulo de deformação do concreto que os corpos de prova 150 x 300 mm. Na resistência à compressão, como já era esperado, apenas a classe de resistência influenciou significativamente nos resultados. Observou-se também que a NBR-6118/2003 superestima os valores de módulo de deformação dos concretos estudados e que os resultados obtidos se adequam melhor ao modelo proposto pelo ACI318/02.

Made available in DSpace on 2014-07-29T15:03:34Z (GMT). No. of bitstreams: 1 Dissertacao Suelio da S Araujo.pdf: 1201670 bytes, checksum: d9dc94ec3063ff4a2fbf8af7ce722d6b (MD5) Previous issue date: 2011-08-15 / The knowledge of the compressive strength and static modulus of elasticity is fundamental to the study of deformations of concrete, since deformations can cause cracks that compromise both the structural behavior of the element and serve as an entry to deleterious agents. For purposes of correlating values of compressive strength and static modulus of elasticity of concrete, cylinders were cast with different strengths, different types of strain measurements were taken, different specimen sizes and the loading speed of the testing machine. The specimens were tested at the age of 28 days to determine the compressive strength and static module of elasticity according to ABNT NBR 8522:2008, using different types of strain measurement devices: two mechanical dial indicators, surface bonded strain gages, clip gauges and LVDT (Linear Variable Differential Transducer). Two hundred and fifty eight specimens were cast with dimensions 150 mm x 300 mm and 100 mm x 200 mm using conventional normal strength concrete (NC - Class C30) and high strength concrete (HSC - Class C60). The experimental program was divided into two stages. First the static modulus of elasticity of concrete was measured to evaluate the accuracy of the method using different measuring devices and the accuracy of the method to a loading speed of 0.6 MPa/s. Then, the modulus of elasticity using different deformation measuring devices at a loading speed of 0.3 MPa/s and 0.6 MPa/s was measured. As for concrete NC and HSC, it was found that the specimens 100 mm x 200 mm obtained higher dispersion in relation to 150 mm x 300 mm specimens. In the first stage of the research, 100 mm x 200 mm specimens showed a higher dispersion when using mechanical dial gages and LVDT. The 150 mm x 300 mm NC class C30 specimens showed greater dispersion when using in mechanical dial gages and external strain gages. However, the HSC showed higher dispersion when mechanical dial gages and LVDT were used. In both concretes tested, the mechanical dial gages showed greater dispersion. In the second stage of the research, 150 mm x 300 mm specimens tested at the loading speed of 0.3 MPa/s showed greater dispersion when electrical strain gages and clip gauges were used. The 150 mm x 300 mm specimens tested at loading speed of 0.6 MPa/s showed greater dispersion when electrical strain gages and mechanical dial gages were used. / O conhecimento da resistência à compressão e do módulo estático de elasticidade é fundamental para o estudo das deformações do concreto, uma vez que as deformações podem gerar fissuras capazes de comprometer tanto o comportamento estrutural do elemento de concreto, como servir de caminho de entrada aos agentes deletérios. Não só fissuras, mas também deformações excessivas. Para fins de correlação de valores de resistência à compressão e módulo estático de elasticidade do concreto, foram moldados corpos-de-prova variando-se a classe do concreto, o tipo de medidores de deformação, a dimensão do corpo-de-prova e a velocidade de carregamento da máquina de ensaio. Os corpos-de-prova foram ensaiados na idade de 28 dias para determinação da resistência à compressão e do módulo estático de elasticidade, normalizado pela ABNT NBR 8522:2008, utilizando-se diferentes tipos de medidores de deformação, a saber: compressômetro mecânico com dois relógios comparadores acoplados, extensômetro elétrico resistivo de colagem superficial ( strain gage ), extensômetro elétrico resistivo de fixação externa ( clip gage ) e LVDT (Transdutor Diferencial de Variação Linear). Foram moldados 258 corpos-de-prova com dimensões 150 mm x 300 mm e 100 mm x 200 mm utilizando concreto convencional de resistência normal (CC Classe C30) e concreto de alta resistência (CAR Classe C60). O programa experimental foi dividido em duas etapas: a primeira contemplou o estudo do módulo estático de elasticidade do concreto para avaliação da precisão do método utilizando diferentes medidores de deformação e da acurácia do método com velocidade de carregamento e descarregamento da máquina de ensaio em um nível: 0,6 MPa/s. A segunda etapa contemplou o estudo de determinação do módulo estático de elasticidade utilizando diferentes medidores de deformação com velocidade de carregamento e descarregamento da máquina de ensaio em dois níveis: 0,3 MPa/s e 0,6 MPa/s. Quanto ao concreto Classe C30 e CAR, verificou-se que os corpos-de-prova de dimensão 100 mm x 200 mm apresentaram maior dispersão em relação aos corpos-de-prova de dimensão 150 mm x 300 mm. Na primeira etapa da pesquisa, quanto à dimensão 100 mm x 200 mm, verificou-se que o concreto Classe C30 e o concreto de alta resistência (CAR) apresentou maior dispersão nos medidores de deformação compressômetro mecânico e LVDT. Quanto à dimensão 150 mm x 300 mm, verificou-se que o concreto Classe C30 apresentou maior dispersão nos medidores de deformação compressômetro mecânico e extensômetro elétrico de fixação externa. Já no concreto de alta resistência (CAR) apresentou maior dispersão nos medidores de deformação compressômetro mecânico e LVDT. Em ambas as classes de concreto ensaiadas, o medidor de deformação compressômetro mecânico apresentou maior dispersão. Na segunda etapa da pesquisa, quanto à dimensão 150 mm x 300 mm ensaiada com velocidade de carregamento e descarregamento da máquina de ensaio de 0,3 MPa/s, verificou-se que apresentou maior dispersão nos medidores de deformação extensômetro elétrico de colagem superficial e extensômetro elétrico de fixação externa. Quanto à dimensão 150 mm x 300 mm ensaiada com velocidade de carregamento e descarregamento da máquina de ensaio de 0,6 MPa/s, verificou-se que apresentou maior dispersão nos medidores de deformação extensômetro elétrico de colagem superficial e compressômetro mecânico.