Submitted by Renata Lopes (renatasil82@gmail.com) on 2015-12-08T11:13:05Z No. of bitstreams: 1 caiomarceluspaislevasseur.pdf: 4546598 bytes, checksum: be57e1ab62ac45ae2f9ffe3e165c9e75 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2015-12-09T13:38:24Z (GMT) No. of bitstreams: 1 caiomarceluspaislevasseur.pdf: 4546598 bytes, checksum: be57e1ab62ac45ae2f9ffe3e165c9e75 (MD5) / Made available in DSpace on 2015-12-09T13:38:24Z (GMT). No. of bitstreams: 1 caiomarceluspaislevasseur.pdf: 4546598 bytes, checksum: be57e1ab62ac45ae2f9ffe3e165c9e75 (MD5) Previous issue date: 2015-04-30 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Os sistemas de implantes osseointegráveis se apresentam em um ou mais componentes, e a correta inter-relação, passividade de assentamento e resistência biomecânica, definem a resistência / vulnerabilidade do mesmo frente aos fatores bacterianos e oclusais. Objetivo: Avaliar as deformações inerentes ao processamento laboratorial dos pilares calcináveis de corpo único para o sistema de implantes Cone Morse. Materiais e métodos: Utilizou-se 20 implantes Cone Morse da marca SIN, 10 componentes protéticos calcináveis e 10 não calcináveis. Após os processos laboratoriais, os conjuntos foram submetidos à Microscopia eletrônica de varredura (MEV) da interface pilar/implante, para análise qualitativa e quantitativa da desadaptação gerada. Os conjuntos foram levados a ciclos térmicos (1.000 ciclos) e de fadiga mecânica (500.000 ciclos) e novamente foi realizada a MEV. Os resultados foram comparados através de análise estatística de Mean-Whitmann. Resultados: O grupo de teste (G1) apresentou os maiores valores iniciais, com média de 34, 55 μm e 11,17 μm, para a subdivisões A (fundição) e B (aplicação de porcelana) respectivamente. A subdivisão B do grupo teste apresentou a maior alteração pós testes, com média de 19,28 μm de aumento da desadaptação protética. As subdivisões G1.A, G2.A, G2.B mostraram tendência à diminuição da desadaptação de -1,03 μm, - 1,64 μm, e -0,49 μm, respectivamente. Pilares Cone Morse não calcináveis apresentam-se com alta estabilidade e baixa taxa de desadaptações. Para o grupo teste pode-se afirmar que o processo de fundição nitidamente criou as maiores dilatações e desadaptações das estruturas. O processo de sinterização da porcelana em teste, criou uma redução da desadaptação medida, porém esta voltou a aumentar após os testes em laboratório. Para o grupo controle, houve a manutenção das taxas de desadaptações menores ao limite de 10 μm, e com tendência de redução após os testes. Conclusão: O pilar calcinável Cone Morse de corpo único mostrou-se como desfavorável quanto à biomecânica, e o processo de fundição gerou as maiores desadaptações. / The system of dental implants present in one or more components, and the correct interrelationship, settling and passive biomechanical strength, defining the strength / vulnerability of the same to the forward occlusal and bacterial factors.Objective: To evaluate the defects associated to laboratory processing of abutments of unique body to the system of Cone Morse implants. Methods: We used 20 Cone Morse implants SIN brand, prosthetic components 10 and 10 calcinable not calcinable. After the laboratory processes the sets were subjected to scanning electron microscopy (SEM) of the pillar / implant interface, for qualitative and quantitative analysis of the generated misfit. The samples were taken to alternated thermal cycles (1000 – 50 and 550) and mechanical fatigue (500,000 - 120 N/cm2) and again was carried out by SEM. The results were compared by statistical analysis Mean-Whitmann (P>0,05). Results: The test group (G1) showed the highest initial values, averaging 34.55 and 11.17 micrometres for subdivisions A (casting) and B (porcelain application) respectively. The B subdivision of the test group showed the greatest change after tests, averaging 19.28 mm of increasing prosthetic misfit. The G1.A subdivisions, G2.A, G2.B showed a tendency to decrease the mismatch of -1.03 micrometres - 1.64 micrometres and -0.49 micrometres respectively. Pillars Cone Morse calcinable not present with high stability and low rate misfits. For the test group it can be said that the casting process clearly created the largest expansion and mismatches of structures. The porcelain sintering process under test, created a reduction of the mismatch measure, however this increased again after the tests in the laboratory. For the control group, there was the maintenance of rates of minor mismatches to 10 micrometres limit, and with downward trend after the tests. Conclusion: Cone Morse castable pillars proved to be unfavorable on the biomechanics, and the casting process generated the biggest misfits.

Os implantes cone morse apresentam um travamento e vedamento por meio de atrito entre as paredes do implante e do pilar protético. Nos sistemas convencionais do tipo Hexágono externo e interno, para reduzir o afrouxamento dos parafusos protéticos, são utilizados materiais de cobertura de superfície, como carbono e ouro. Não foram encontradas referências na literatura da utilização desse tipo de deposição em componentes do sistema cone morse. O propósito desse estudo é mensurar, registrar e avaliar os valores do torque de desaperto em pilares protéticos dos tipos sólido e parafuso passante do sistema cone morse com a deposição de carbono na zona de atrito do pilar protético. Foram utilizados 40 implantes cone morse com seus respectivos pilares divididos em 4 grupos (n=10): G1- pilar sólido; G2- pilar sólido com deposição de carbono na zona de atrito do sistema morse; G3- estudo somente do parafuso do pilar passante; G4- estudo somente do parafuso do pilar passante com deposição de carbono na ponta ativa; G5- estudo somente do pilar passante sem ação do parafuso; G6- estudo somente do pilar passante revestido em carbono na zona de atrito do sistema morse sem ação do parafuso. Cada pilar recebeu uma seqüência de 5 apertos e desapertos (20Ncm para o pilar sólido e 10Ncm para o parafuso passante). Os resultados mostraram no teste estatístico ANOVA para dois fatores de variação (desaperto e carbono), haver diferença estatística significante entre os grupos: G1 maior que G2 (p < 0,01); G4 maior que G3 (p < 0,01); G6 maior que G5 (p < 0,01). Esse estudo concluiu que o grupo controle G1 mostrou maior valor através da media aritmética (23,706 Ncm) em relação ao grupo experimental G2 (22,114 Ncm); o grupo experimental G4 mostrou maior valor através da media aritmética (8,218 Ncm) em relação ao grupo controle G3 (7,354 Ncm) e o grupo experimental G6 mostrou maior valor através da media aritmética (10,268 Ncm) em relação ao grupo controle G5 (6,906 Ncm), mostrou também que não houve diferença significativa (p > 0,01) para o fator desaperto em todos os grupos estudados, ou seja, não houve interferência da deformação do material com a repetição dos ciclos de aperto e desaperto. / The morse taper implants present a locking and sealing by means of the attrition between implants internal walls and the abutment. In the external and internal conventional hexagon system, to reduce the prosthetic screw loosing, its used covering surface materials, as carbon and gold. Literature reference using these kind of surface deposition were not found in morse taper abutment implants. The aim of this study is to measure, register and evaluate the removal torque values in morse taper solid abutment and passing screw abutment with carbon deposition in attrition zone. They were used 40 morse taper implants with their respective abutments divided in 4 groups (n = 10): G1 solid abutment; G2 - solid abutment with carbon deposition in attrition zone; G3 evaluation only in the screw of the passing abutment; G4 - evaluation only in the screw of the passing abutment with carbon deposition in the screw thread; G5 - evaluation only in the passing abutment without the screw action; G6 - evaluation only in the passing abutment with carbon deposition in attrition zone without the screw action. Each abutment received a sequence of 5 tightening and removal torque (20Ncm in solid abutment and 10Ncm in passant screw abutment). The results of ANOVA statistic test for two factors of variation (removal torque and carbon), showed that there is significant statistic difference between the groups: G1 higher than G2 (p < 0.01); G4 higher than G3 (p < 0.01); G6 higher than G5 (p < 0.01). This study concluded that control group G1 showed a higher value through the arithmetical media (23.706Ncm) in relation of the experimental group G2 (22.114Ncm); the experimental group G4 showed higher value through the arithmetical media (8.218Ncm) in relation of the control group G3 (7.354Ncm) and the experimental group G6 showed higher values through the arithmetical media (10.268Ncm) in relation of the control group G5 (6.906Ncm), and also showed that there was not significant difference (p < 0.01) to the removal torque factor in all the groups studied, that is, there was not a material deformation interference with the tightening and removal torque cycles repetition.

Os implantes cone morse apresentam um travamento e vedamento por meio de atrito entre as paredes do implante e do pilar protético. Nos sistemas convencionais do tipo Hexágono externo e interno, para reduzir o afrouxamento dos parafusos protéticos, são utilizados materiais de cobertura de superfície, como carbono e ouro. Não foram encontradas referências na literatura da utilização desse tipo de deposição em componentes do sistema cone morse. O propósito desse estudo é mensurar, registrar e avaliar os valores do torque de desaperto em pilares protéticos dos tipos sólido e parafuso passante do sistema cone morse com a deposição de carbono na zona de atrito do pilar protético. Foram utilizados 40 implantes cone morse com seus respectivos pilares divididos em 4 grupos (n=10): G1- pilar sólido; G2- pilar sólido com deposição de carbono na zona de atrito do sistema morse; G3- estudo somente do parafuso do pilar passante; G4- estudo somente do parafuso do pilar passante com deposição de carbono na ponta ativa; G5- estudo somente do pilar passante sem ação do parafuso; G6- estudo somente do pilar passante revestido em carbono na zona de atrito do sistema morse sem ação do parafuso. Cada pilar recebeu uma seqüência de 5 apertos e desapertos (20Ncm para o pilar sólido e 10Ncm para o parafuso passante). Os resultados mostraram no teste estatístico ANOVA para dois fatores de variação (desaperto e carbono), haver diferença estatística significante entre os grupos: G1 maior que G2 (p < 0,01); G4 maior que G3 (p < 0,01); G6 maior que G5 (p < 0,01). Esse estudo concluiu que o grupo controle G1 mostrou maior valor através da media aritmética (23,706 Ncm) em relação ao grupo experimental G2 (22,114 Ncm); o grupo experimental G4 mostrou maior valor através da media aritmética (8,218 Ncm) em relação ao grupo controle G3 (7,354 Ncm) e o grupo experimental G6 mostrou maior valor através da media aritmética (10,268 Ncm) em relação ao grupo controle G5 (6,906 Ncm), mostrou também que não houve diferença significativa (p > 0,01) para o fator desaperto em todos os grupos estudados, ou seja, não houve interferência da deformação do material com a repetição dos ciclos de aperto e desaperto. / The morse taper implants present a locking and sealing by means of the attrition between implants internal walls and the abutment. In the external and internal conventional hexagon system, to reduce the prosthetic screw loosing, its used covering surface materials, as carbon and gold. Literature reference using these kind of surface deposition were not found in morse taper abutment implants. The aim of this study is to measure, register and evaluate the removal torque values in morse taper solid abutment and passing screw abutment with carbon deposition in attrition zone. They were used 40 morse taper implants with their respective abutments divided in 4 groups (n = 10): G1 solid abutment; G2 - solid abutment with carbon deposition in attrition zone; G3 evaluation only in the screw of the passing abutment; G4 - evaluation only in the screw of the passing abutment with carbon deposition in the screw thread; G5 - evaluation only in the passing abutment without the screw action; G6 - evaluation only in the passing abutment with carbon deposition in attrition zone without the screw action. Each abutment received a sequence of 5 tightening and removal torque (20Ncm in solid abutment and 10Ncm in passant screw abutment). The results of ANOVA statistic test for two factors of variation (removal torque and carbon), showed that there is significant statistic difference between the groups: G1 higher than G2 (p < 0.01); G4 higher than G3 (p < 0.01); G6 higher than G5 (p < 0.01). This study concluded that control group G1 showed a higher value through the arithmetical media (23.706Ncm) in relation of the experimental group G2 (22.114Ncm); the experimental group G4 showed higher value through the arithmetical media (8.218Ncm) in relation of the control group G3 (7.354Ncm) and the experimental group G6 showed higher values through the arithmetical media (10.268Ncm) in relation of the control group G5 (6.906Ncm), and also showed that there was not significant difference (p < 0.01) to the removal torque factor in all the groups studied, that is, there was not a material deformation interference with the tightening and removal torque cycles repetition.

Na implantodontia visa-se dois grandes resultados para os desdentados parciais e totais, função mastigatória e estética. Ambos têm o mesmo grau de importância, para tanto se deve pensar no que se tem de mais seguro e prático nos dias de hoje. O cone Morse, na implantodontia oral, é um sistema de estabilidade entre o implante dentário e o parafuso intraósseo de sustentação. Para seu correto uso se faz necessário uma série de análise de suas características e condições. No presente trabalho focou-se em desenvolver protocolo de validação de torque, além de analisar parâmetros de acabamento, deformação e estabilidade précarga e pós-carga dentro de protocolos já recomendados. Avaliou-se sua condição antes e após os efeitos de carga mastigatória simulada por ensaio de fadiga. Concluiu-se que o uso do cone Morse dentro dos protocolos indicados deve ser revisto quanto a padrões similares de torque nos pilares sólidos e indexados, cada um possui limites e indicações diferentes para se manter estável. Concluiu-se também que não é um sistema totalmente livre de trânsito de bactérias e que esse trânsito aumenta de forma proporcional ao uso e força mastigatória, indicando que melhorias no acabamento entre as peças devem ser implementadas e/ou adição de material que afaste crescimento bacteriano priorizando a saúde do periodonto e do tecido ósseo de sustentação mantendo o sistema seguro em longevidade. / In implantology it is aimed two major outcomes for the partial and total toothless persons, mastigatory function and aesthetics. Both have the same degree of importance, therefore it must be thought about what is safer and more practical these days. Morse taper in oral implantology is a system of stability between the dental implant and the intraosseous screw support. For its correct use a series of analysis of its features and conditions is required. This work was focused on developing torque validation protocol, and analyzing surface finishing parameters, deformation and stability as before load and after load in recommended protocols. The implants condition before and after the effects of habitual masticatory load was simulated by fatigue testing. It was concluded that the Morse taper use within the specified protocols should be reviewed for similar patterns of torque in solids and indexed pillars, each has different limits and signs to remain stable. It was also concluded that it is not a traffic totally free system of bacteria and that this influence increases in proportion to the use and masticatory forces, improvements in the surface finish between parts and / or addition of material that hinders bacterial growth is needed if it is prioritized the health of the periodontium and the bone tissue keeping the system safe in the long therm.

Problemas com desenho de conexões protéticas sobre implantes, microfendas, afrouxamento e, consequentemente, perdas das estruturas protéticas reabilitadoras são tópicos frequentes do estudo odontológico. Conexões do tipo Cone Morse, devido às suas características, diminuíram o índice desses problemas, abrindo uma nova perspectiva para o sucesso da prótese sobre implante. Contudo, ainda é frequente encontrar componentes que falham no desempenho, levando à falência da restauração, especialmente quando esses componentes não são bem ajustados, bem fixados ou, ainda, não possuem, na sua geometria, características suficientes para suportar as forças laterais e oclusais de um ciclo mastigatório. O objetivo deste estudo é avaliar a influência do jateamento com óxido de alumínio sobre a superfície externa dos componentes protéticos, separadamente e em conjunto, com um adesivo industrial, em uma tentativa de aumentar os valores de torque de abertura de componentes apertados em seu torque recomendado, pelo fabricante ou menor. Neste ensaio, foram utilizados 36 implantes da marca Straumann®, de 10mm de comprimento com diâmetro de 4,8 mm, os quais foram divididos em 6 grupos: Grupo 1 = controle, torque de 35 N.cm; Grupo 2 = superfície jateada com óxido de alumínio (# 320) e torque de 35 N.cm; Grupo 3 = superfície jateada com óxido de alumínio (# 320) e torque de 25 N.cm; Grupo 4 = superfície jateada com óxido de alumínio (# 100) e torque de 25 N.cm; Grupo 5 = superfície jateada com óxido de alumínio (# 320), aplicação de adesivo e torque de 25 N.cm; Grupo 6 = superfície jateada com óxido de alumínio (# 100), aplicação de adesivo e torque de 25 N.cm, que receberam componentes protéticos sólidos de 5,5 mm de altura, regulares e alterados. As modificações incluídas foram o jateamento com partículas de óxido de alumínio (100 e 320 micra) e o uso de Loctite® 277 como adesivo industrial. Os conjuntos implante-componente foram levados até uma máquina de controle de tração, Instron®, e, após a sua calibração, as amostras dos grupos foram apertadas em 35 e 25 N.cm, com um conjunto catraca-torquímetro, com checagem visual e registro no software acoplado à máquina de ensaio. Após trinta dias, os grupos foram levados à máquina novamente e o conjunto abutment-implante foi desapertado, agora somente com registro no software da máquina de ensaio. Os valores e porcentagens da diferença entre torque de aperto e desaperto foram avaliados estatisticamente, e comparados entre os grupos. Para todas as associações, o valor de p deveria ser menor ou igual 0,05, para relevância. O grupo Jateado 35 N.cm, 320 micra, não apresentou valores mais altos do que o grupo Controle no momento do torque de desaperto, assim como os grupos Jateados 25 N.cm 100 e 320 micra. Os grupos Jateados 25 N.cm, 100 e 320 micra, com adesivo, mostraram uma resistência por volta de uma vez e meia maior, no torque de desaperto do que o grupo Controle 35 N.cm. / Problems with design of prosthetic implant connections, microleakage,! loosening which leads to loss of rehabilitative prosthetic structures are frequent topics of dental study. Morse taper connections, due to its characteristics, decreased the rate of these problems opening a new perspective to the success of the prosthesis supported over implant. However, it is still frequent to find components that fail in performance leading to failure of restoration especially when these components are not well adjusted, tightened or do not have in its geometry enough characteristics to support the occlusal and lateral forces in a masticatory cycle. The aim of this study is to evaluate the influence of blasting with aluminum oxide on the outer surface of the prosthetic components separately and in conjunction with an industrial adhesive in an attempt to increase the opening torque values of components tightened on their recommended torque by the manufacturer or less, therefore allowing the dentist an early intervention in the prosthetic rehabilitation. In this test, 36 Straumann® implants of 10mm high and 4,8mm wide were used. They were divided into six groups: Group 1 Solid abutments control group - 35 N.cm tightened; Group 2 - Solid sandblasted abutments, 35 N.cm aluminum oxide 320 microns size particles; Group 3 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles; Group 4 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles; Group 5 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles with glue application; Group 6 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles with glue application, which received 5,5 mm high regular and modified solid abutments. The included modifications were sandblasting with aluminum oxide particles (100 and 320 microns) and the use of Loctite® 277 as an industrial adhesive. The samples were taken to a traction control test machine, Instron ®, and after calibration the group samples were tightened on 35 and 25 N.cm with a ratchet-wrench set with visual check. The data was recorded in a software coupled to the test machine. After thirty days the groups were brought again to the test machine and the samples were untightened. At this point the resulting data was recorded only in the testing machine software. The values and percentages of the changes between the tightening and loosening torques were recorded and compared among the study groups. For all associations a p-value < 0.05 was considered significant. The group blasted 35 N.cm, 320 microns did not show higher values than the control group at the time of loosening torque as well as groups blasted 25 N.cm 100 and 320 microns. The groups blasted 25 N.cm, 100 and 320 microns with adhesive showed a resistance around one and a half times greater in the loosening torque than the control group 35 N.cm.

Na implantodontia visa-se dois grandes resultados para os desdentados parciais e totais, função mastigatória e estética. Ambos têm o mesmo grau de importância, para tanto se deve pensar no que se tem de mais seguro e prático nos dias de hoje. O cone Morse, na implantodontia oral, é um sistema de estabilidade entre o implante dentário e o parafuso intraósseo de sustentação. Para seu correto uso se faz necessário uma série de análise de suas características e condições. No presente trabalho focou-se em desenvolver protocolo de validação de torque, além de analisar parâmetros de acabamento, deformação e estabilidade précarga e pós-carga dentro de protocolos já recomendados. Avaliou-se sua condição antes e após os efeitos de carga mastigatória simulada por ensaio de fadiga. Concluiu-se que o uso do cone Morse dentro dos protocolos indicados deve ser revisto quanto a padrões similares de torque nos pilares sólidos e indexados, cada um possui limites e indicações diferentes para se manter estável. Concluiu-se também que não é um sistema totalmente livre de trânsito de bactérias e que esse trânsito aumenta de forma proporcional ao uso e força mastigatória, indicando que melhorias no acabamento entre as peças devem ser implementadas e/ou adição de material que afaste crescimento bacteriano priorizando a saúde do periodonto e do tecido ósseo de sustentação mantendo o sistema seguro em longevidade. / In implantology it is aimed two major outcomes for the partial and total toothless persons, mastigatory function and aesthetics. Both have the same degree of importance, therefore it must be thought about what is safer and more practical these days. Morse taper in oral implantology is a system of stability between the dental implant and the intraosseous screw support. For its correct use a series of analysis of its features and conditions is required. This work was focused on developing torque validation protocol, and analyzing surface finishing parameters, deformation and stability as before load and after load in recommended protocols. The implants condition before and after the effects of habitual masticatory load was simulated by fatigue testing. It was concluded that the Morse taper use within the specified protocols should be reviewed for similar patterns of torque in solids and indexed pillars, each has different limits and signs to remain stable. It was also concluded that it is not a traffic totally free system of bacteria and that this influence increases in proportion to the use and masticatory forces, improvements in the surface finish between parts and / or addition of material that hinders bacterial growth is needed if it is prioritized the health of the periodontium and the bone tissue keeping the system safe in the long therm.

In cases of upper edentulous patients with atroffic maxilla, the zigomatic implant is one of the techniques used for rehabilitation with implanted fixed prosthesis. The screw s loosening is one of the main problems related to this type of prosthesis. The aim of this work was to evaluate the golden and abutments screws loosening in fixed prosthesis over two conventional implants and two zigomatic implants before and after fatigue test. Five samples with external hexagonal junctions (HE) and five with internal conical junctions (CM) had been used. Each specimen with two anterior conventional implants and two distal zigomatic implants. The respective abutments had been installed on the implants and metallic structures of screwed fixed prosthesis had been casted. The specimens had been submitted to four fatigue protocols with different load levels in cantilever and different number of cycles. Untorque values of retaining and abutment screws had been verified before and after each cyclic loading with a digital torquemeter. The prosthetic screws had had reduction in the untorques values when compared with the iniitial torques, but there was no difference between the two interfaces in study. The untorque values of the HE abutments screws after all cycles, had a reduction in 51,56% of the cases. 60,6% f these in zigomatic implants and 39,4% in conventional implants. The screws of the CM abutments had untorque loss in 39,58% of the cases. 21,05% had ocurred in zigomatic implants and 78,95% in conventional implants. The variation of junction type does not interfere in the untorque of retention screws of the prosthesis. The mechanical behavior was different when comparing CM and HE abutment screws. In the HE specimens the torque loss was greater in the zigomatic implants whereas in the CM specimens, the absolute untorque values of the zigomatic implants increased after the fatigue test. / Em casos de pacientes edêntulos superiores com maxilas atróficas, a utilização de implantes zigomáticos é uma das técnicas utilizadas para reabilitação com prótese fixa sobre implantes. Contudo, o desaperto de parafusos é um dos principais problemas relacionados a este tipo de prótese. O objetivo deste trabalho foi avaliar a diminuição de torque de desaperto dos parafusos protéticos e de intermediários em próteses fixas confeccionadas sobre dois implantes convencionais e dois zigomáticos, antes e após ensaio de fadiga. Foram utilizados cinco modelos com junções hexagonais externas (HE) e cinco com junções cônicas internas ou cone-morse (CM). Cada amostra com dois implantes convencionais anteriores e dois implantes zigomáticos distais. Sobre os implantes foram instalados pilares respectivos e confeccionadas estruturas metálicas fundidas de uma prótese fixa parafusada. As amostras foram submetidas a quatro níveis de carga em cantilever e diferentes números de ciclos. Utilizando torquímetro digital foram determinados valores de desaperto dos parafusos de retenção e dos pilares antes e após cada ciclagem. Os parafusos protéticos tiveram diminuição nos torques de desaperto quando comparados aos torques iniciais, mas não houve diferença entre os tipos de junção. Nos parafusos dos pilares HE observando os valores de desaperto após todos os ciclos, houve diminuição do torque de desaperto em 51,56% dos casos. Destes, 60,6% nos implantes zigomáticos e 39,4% nos convencionais. Os parafusos dos pilares CM tiveram valor de torque diminuído em 39,58% dos casos. Destes, 21,05% ocorreram nos zigomáticos e 78,95% nos convencionais. Nas amostras HE houve maior perda de torque para os implantes zigomáticos enquanto que nas CM ocorreu o contrário, sendo que em valores absolutos de torque de desaperto, os pilares CM dos zigomáticos apresentaram aumento de torque de desaperto após o ensaio de fadiga. Desta forma, a variação do tipo de junção não interferiu no torque de desaperto dos parafusos de retenção das próteses. Houve alteração no comportamento mecânico quando comparados parafusos de pilares HE e CM. / Mestre em Odontologia

Problemas com desenho de conexões protéticas sobre implantes, microfendas, afrouxamento e, consequentemente, perdas das estruturas protéticas reabilitadoras são tópicos frequentes do estudo odontológico. Conexões do tipo Cone Morse, devido às suas características, diminuíram o índice desses problemas, abrindo uma nova perspectiva para o sucesso da prótese sobre implante. Contudo, ainda é frequente encontrar componentes que falham no desempenho, levando à falência da restauração, especialmente quando esses componentes não são bem ajustados, bem fixados ou, ainda, não possuem, na sua geometria, características suficientes para suportar as forças laterais e oclusais de um ciclo mastigatório. O objetivo deste estudo é avaliar a influência do jateamento com óxido de alumínio sobre a superfície externa dos componentes protéticos, separadamente e em conjunto, com um adesivo industrial, em uma tentativa de aumentar os valores de torque de abertura de componentes apertados em seu torque recomendado, pelo fabricante ou menor. Neste ensaio, foram utilizados 36 implantes da marca Straumann®, de 10mm de comprimento com diâmetro de 4,8 mm, os quais foram divididos em 6 grupos: Grupo 1 = controle, torque de 35 N.cm; Grupo 2 = superfície jateada com óxido de alumínio (# 320) e torque de 35 N.cm; Grupo 3 = superfície jateada com óxido de alumínio (# 320) e torque de 25 N.cm; Grupo 4 = superfície jateada com óxido de alumínio (# 100) e torque de 25 N.cm; Grupo 5 = superfície jateada com óxido de alumínio (# 320), aplicação de adesivo e torque de 25 N.cm; Grupo 6 = superfície jateada com óxido de alumínio (# 100), aplicação de adesivo e torque de 25 N.cm, que receberam componentes protéticos sólidos de 5,5 mm de altura, regulares e alterados. As modificações incluídas foram o jateamento com partículas de óxido de alumínio (100 e 320 micra) e o uso de Loctite® 277 como adesivo industrial. Os conjuntos implante-componente foram levados até uma máquina de controle de tração, Instron®, e, após a sua calibração, as amostras dos grupos foram apertadas em 35 e 25 N.cm, com um conjunto catraca-torquímetro, com checagem visual e registro no software acoplado à máquina de ensaio. Após trinta dias, os grupos foram levados à máquina novamente e o conjunto abutment-implante foi desapertado, agora somente com registro no software da máquina de ensaio. Os valores e porcentagens da diferença entre torque de aperto e desaperto foram avaliados estatisticamente, e comparados entre os grupos. Para todas as associações, o valor de p deveria ser menor ou igual 0,05, para relevância. O grupo Jateado 35 N.cm, 320 micra, não apresentou valores mais altos do que o grupo Controle no momento do torque de desaperto, assim como os grupos Jateados 25 N.cm 100 e 320 micra. Os grupos Jateados 25 N.cm, 100 e 320 micra, com adesivo, mostraram uma resistência por volta de uma vez e meia maior, no torque de desaperto do que o grupo Controle 35 N.cm. / Problems with design of prosthetic implant connections, microleakage,! loosening which leads to loss of rehabilitative prosthetic structures are frequent topics of dental study. Morse taper connections, due to its characteristics, decreased the rate of these problems opening a new perspective to the success of the prosthesis supported over implant. However, it is still frequent to find components that fail in performance leading to failure of restoration especially when these components are not well adjusted, tightened or do not have in its geometry enough characteristics to support the occlusal and lateral forces in a masticatory cycle. The aim of this study is to evaluate the influence of blasting with aluminum oxide on the outer surface of the prosthetic components separately and in conjunction with an industrial adhesive in an attempt to increase the opening torque values of components tightened on their recommended torque by the manufacturer or less, therefore allowing the dentist an early intervention in the prosthetic rehabilitation. In this test, 36 Straumann® implants of 10mm high and 4,8mm wide were used. They were divided into six groups: Group 1 Solid abutments control group - 35 N.cm tightened; Group 2 - Solid sandblasted abutments, 35 N.cm aluminum oxide 320 microns size particles; Group 3 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles; Group 4 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles; Group 5 - Solid sandblasted abutments, 25 N.cm aluminum oxide 320 microns size particles with glue application; Group 6 - Solid sandblasted abutments, 25 N.cm aluminum oxide 100 microns size particles with glue application, which received 5,5 mm high regular and modified solid abutments. The included modifications were sandblasting with aluminum oxide particles (100 and 320 microns) and the use of Loctite® 277 as an industrial adhesive. The samples were taken to a traction control test machine, Instron ®, and after calibration the group samples were tightened on 35 and 25 N.cm with a ratchet-wrench set with visual check. The data was recorded in a software coupled to the test machine. After thirty days the groups were brought again to the test machine and the samples were untightened. At this point the resulting data was recorded only in the testing machine software. The values and percentages of the changes between the tightening and loosening torques were recorded and compared among the study groups. For all associations a p-value < 0.05 was considered significant. The group blasted 35 N.cm, 320 microns did not show higher values than the control group at the time of loosening torque as well as groups blasted 25 N.cm 100 and 320 microns. The groups blasted 25 N.cm, 100 and 320 microns with adhesive showed a resistance around one and a half times greater in the loosening torque than the control group 35 N.cm.

Cargas oclusais excessivas podem promover tensões exageradas às estruturas de implantes/pilares/próteses, resultando em deformação, desadaptação ou mesmo fratura dos componentes e do próprio implante. Além disso, tais sobrecargas podem gerar necrose por compressão e perda óssea peri-implantar e, ainda, a ocorrência de microdeslocamentos na interface de conexão implante-pilar (I-P) ocasionando a formação de fendas propícias à colonização bacteriana, o que pode levar ao desenvolvimento de peri-implantite, contribuindo para o insucesso do conjunto. O presente estudo objetivou avaliar, por meio de uma técnica já amplamente utilizada na Engenharia e na Física a Interferometria Eletrônica por Padrões de Speckle (ESPI) as deformações a nível do colar de implantes com conexão cônica interna (cone Morse) de diferentes diâmetros (Kopp 4,3/5,5 mm e Neodent 3,5/5,0 mm), sob dois tipos (cêntrica e excêntrica) e intensidades (50 N e 100 N) de cargas, similares as quais os implantes ficam expostos durante a função mastigatória. Testou-se a hipótese de que a deformação do colar do implante seria inversamente proporcional ao diâmetro do implante. Além disso, discutiu-se vantagens e limitações da técnica ESPI frente a outros métodos comumente utilizados na avaliação de tensões. As maiores deformações foram sempre associadas às cargas excêntricas, com exceção do G1-Kopp. A maior deformação ocorreu no G1-Neodent sob carga excêntrica de 100 N e a menor, no G2-Neodent sob carga cêntrica de 50 N. A técnica ESPI mostrou-se altamente sensível e reprodutível para avaliar deformações a nivel do colar de implantes sendo possível confirmar a hipótese inicial, visto que a maior deformação esteve sempre associada aos implantes de menor diâmetro, em ambos os sistemas de implante pesquisados. / Occlusal overloading may promote excessive stresses to the implants/abutments/prosthesis, resulting in deformation, misfit or fracture of the components, until the implants. Futhermore, strains of the implant-abutment connection can cause the formation of microgaps propitious to bacterial colonization, which leads to the development of peri-implant sites, leading to the failure of the rehabilitation. This study aimed to evaluate, by a technique widely used in the engineering and physics Electronic Speckle Pattern Interferometry (ESPI) the strains related to the implant collar with internal tappered connection (Morse taper) with different diameters (Kopp 4.3/5.5 mm and Neodent 3,5/5,0 mm), under two types (centric and eccentric) and intensities (50 N and 100 N) of loads, similar which implants are exposed during masticatory function. We tested the hypothesis that the strains of the implants collar would be inversely proportional to the diameter of the implant. In addition, the survey discussed the advantages and limitations of the ESPI technique over other methods commonly used to assess strains. The largest strain was always associated with eccentric loads, except for G1-Kopp. The largest strain occurred in the G1-Neodent under the eccentric loads of 100 N and the lowest in the G2-Neodent under the centric loads of 50 N. The ESPI technique was a highly sensitive and reproducible to evaluate the strains at the level of the collar of implants being possible to confirm the initial hypothesis, since most strains was always associated with narrower-diameter implants in both implant systems studied.

O meio cientifico na área odontológica está sempre procurando materiais e tratamentos que de maior previsibilidade e sucesso em longo prazo. Este trabalho procurou avaliar, por meio de análise fotoelástica, o comportamento das tensões geradas de cargas exercidas em prótese sobre implante posteriores adjacente ou não a réplicas de dentes. Todos os implantes cone-Morse utilizados eram da marca ANKYLOS®, da Dentsply, de 3,5 x 9,5 mm. Para a confecção das réplicas dos dentes utilizou-se resina Luxatemp e foram confeccionadas coroas unitárias de cerâmica. Foram confeccionados três modelos contendo dente-implante-dente, entretanto em cada modelo o implante apresentava-se em uma altura diferente em relação à crista marginal (nível, 1,5 mm e 3,0 mm subcristal). Foram fabricados mais três modelos com as mesmas características, mas com ausência do segundo molar e três modelos com apenas o implante em posição. Os modelo com três elementos com carregamento axial (oclusão balanceada) apresentaram tensões com direção para a região apical conforme o implante apresentava-se mais subcristal; os modelo com dois elementos com carregamento axial (oclusão balanceada), modelos com implantes unitários com carregamento axial (pontual central), modelos com implantes unitários com carregamento axial (pontual distal) e os modelos com implante unitário com carregamento não axial (vestibular-lingual) apresentaram também o mesmo comportamento em relação ao direcionamento das tensões para a região apical. A diferenciação entre os modelos foi observada apenas em relação a intensidade das tensões de algumas regiões. Desta maneira pode-se concluir que quanto mais subcristal o implante se encontra menor é a tensão na região cristal, independentemente da presença ou não de dentes adjacentes, e a presença de dentes adjacentes à prótese sobre implante influência na intensidade de tensão gerada nos implantes, mas não há influência no direcionamento dessas tensões. / The scientific environment in dentistry is always searching for materials and treatments more predictable and which presented a long-term success. The aim of this study was to evaluate by photoelastic analysis, the stresses behavior generated by loads applied to the implant prosthesis posterior between or not to teeth. All implants Morse taper used (Ankylos®,Dentsply Implants) with 3.5mm x 9.5mm. The teeth were made by Luxatemp resin and ceramic crowns were fabricated. Three models containing tooth - implant - tooth were built, meanwhile each model had the implant in different height from the marginal bone crestal level (equicrestal, 1.5mm and 3.0 mm the crest). Subsequently, other three models were made with the same characteristics, but without the second molar and another three models just with the implant in position. Models witch three elements with axial loading (balanced occlusion) had tensions with direction to the apical region as the implant had become more subcristal , models with two elements with axial loading ( balanced occlusion ) , models with single implants with axial loading ( central point ) , models with single implants with axial loading (distal point ) and models with single implant with no axial loading (buccal - lingual) also showed the same behavior with respect to the direction of the stresses to the apical region. The differentiation between the models was only observed for the intensity of the stresses in some regions. Thus it can be concluded that the more the implant is subcristal lower the tension in the crystal region regardless of the presence or absence of adjacent teeth, and the presence of adjacent teeth prosthesis on the implant influence on the stress intensity generated in the implants but no influence on the direction of these stresses.