Made available in DSpace on 2014-06-11T19:24:09Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-09-23Bitstream added on 2014-06-13T19:51:21Z : No. of bitstreams: 1 000735144.pdf: 2073236 bytes, checksum: 613ef7d6b680f1fe13f367e82696ff5c (MD5) / O objetivo deste trabalho foi avaliar a resistência de união ao microcisalhamento de diferentes sistemas adesivos autocondicionantes de dois passos e passo único, com graus de acidez distintos, em substrato dentinário normal e hipermineralizado artificialmente. Sessenta e cinco (n = 65) incisivos bovinos hígidos foram selecionados, sendo cinqüenta e sete (n = 57) para o teste de resistência de união ao microcisalhamento e oito (n = 8) para a observação da interface adesiva em microscopia eletrônica de varredura (MEV). Os dentes tiveram suas raízes removidas com o auxílio de um motor elétrico e disco diamantado. As coroas tiveram sua superfície vestibular desgastada com o objetivo de expor a superfície dentinária plana, sendo os dentes divididos aleatoriamente em dois diferentes grupos, de acordo com o tipo de dentina: normal (N/ n = 28) e hipermineralizada artificialmente (H/ n = 29). O conjunto H recebeu tratamento para hipermineralização e um espécime foi selecionado aleatoriamente para observação em MEV para a confirmação do procedimento de hipermineralização. Cada coroa foi incluída em um cilindro de PVC com o auxílio de resina acrílica autopolimerizável. Cada grupo foi dividido em 4 subgrupos de acordo com o sistema adesivo autocondicionante empregado: Clearfil SE Bond (n=7) – suave de dois passos, Adhese (n = 7) – moderado de dois passos, Adper Easy One (n = 7) – suave de passo único, Optibond All in One (n = 7) – moderado de passo único. Sobre essa superfície foram inseridos e fotopolimerizados cilindros de resina composta (FiltekTM Z350 XT - 3M ESPE). Após período de armazenagem de 24 horas em ambiente úmido a 37°C (± 1°C), foram realizados os testes de microcisalhamento em máquina de ensaios mecânicos com velocidade de 0,5 mm/min até à fratura dos espécimes. A fim de verificar a presença de interface e/ou a aparência de tags de resina, um... / The aim of this study was to evaluate the microshear bond strength of different self-etching two-step and all-in-one adhesive systems, with different acid concentrations to sound and artificially hypermineralized dentin. Sixty-five (n = 65) healthy bovine incisors were selected, fifty-seven (n = 57) to test the microshear bond strength and eight (n = 8) to observe the presence of adhesive interface with scanning electron microscopy (SEM). Teeth have roots removed using an electric motor and diamond disc. Vestibular surface were ground flat to expose a flat dentin surface, the teeth were divided randomly into two different groups according the type of dentin: sound (N / n = 28) or artificially hypermineralized (H / n = 29). The set H received hypermineralizing treatment and a specimen was selected randomly to observe the procedure with SEM. Each crown was included in a PVC cylinder using acrylic resin. Each group was divided into 4 subgroups according to dentin adhesive systems: Clearfil SE Bond (n = 7) - mild two steps, AdheSE (n = 7) - moderate two steps, Adper Easy One (n = 7) - mild all-in-one, Optibond All in One (n = 7) - moderate all-in-one. Then were inserted and cured resin cylinders (Filtek Z350 XT - 3M ESPE) at the surface. After 24 hours storage at 37 ° C (± 1°C), for humid environment, microshear was taked using mechanical testing machine with 0.5 mm/min speed until fracture of the specimens. For analysis the presence of an interface and/or appearance of resin tags, a specimen of each group was prepare for evaluating the adhesive interface with SEM. Bond strengths data were subjected to ANOVA and Bonferroni (p<0.05) test. The bond strength values were Clearfil = 15.65 ± 6.18, AdheSE = 14.71 ± 10.36, Easy One = 21.92 ± 6.40, OptiBond = 28.43 ± 6.55 to sound dentin and Clearfil = 20.96 ± 8.06, AdheSE = 17.23 ± 5.16, Easy One = 31.79 ± 8.31, OptiBond = 23.29 ± 3.66 to...

Orientador: Josimeri Hebling / Banca: Daniela Prócida Raggio / Banca: Regina Maria Puppin Rontani / Banca: Edson Alves de Campos / Banca: Welingtom Dinelli / Resumo: O objetivo geral deste trabalho, o qual foi dividido em três estudos, foi avaliar o efeito da clorexidina (CLX) em diferentes excipientes, etanol e água, na produção e estabilidade mecânica da união resina-dentina afetada por cárie. Materiais e Métodos. No primeiro estudo foi avaliada a influência da CLX em solução aquosa ou alcoólica na umectabilidade da dentina hígida e afetada por cárie por um sistema adesivo. Foram preparadas superfícies planas de dentina em 100 terceiros molares hígidos, das quais 50 foram submetidas ao processo microbiológico de indução de cárie. Dentro de cada condição de substrato, hígido e afetado por cárie, as superfícies foram divididas em 5 grupos (n=10): com smear layer (SL), sem smear layer impregnada com água, sem smear layer impregnada com CLX em água, sem smear layer impregnada com etanol e sem smear layer impregnada com CLX em etanol. Ângulos de contato entre a superfície de dentina e o sistema adesivo Single Bond 2 foram mensurados por meio de um goniômetro, e os dados submetidos aos testes de ANOVA e Tukey ( =0,05). No segundo estudo foi avaliado o efeito da solução de CLX em diferentes excipientes, etanol ou água, na presença de colágeno exposto na união resina-dentina hígida e dentina afetada por cárie. Foram produzidas superfícies planas de dentina em 24 molares humanos hígidos, sendo metade delas cariadas artificialmente. Os dentes foram divididos em 8 grupos (n=3) segundo o tratamento da dentina após o condicionamento ácido (CLX associada a etanol, CLX associada a água, somente etanol ou somente água) e segundo o tipo de substrato utilizado para a adesão. Espécimes foram produzidos de cada dente e preparados histologicamente para coloração com tricrômico de Goldner. A zona de colágeno exposta (ZC) foi quantificada (μm) em... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Purpose. The overall purpose of this work, divided into three studies, was to evaluate the effect of chlorhexidine (CHX) in different excipients, ethanol and water, on the production and mechanical stability of resin-caries affected dentin bonds. Materials and Methods. In the first study, it was evaluated the influence of aqueous and alcoholic solution of CHX on the wettability of noncarious and caries-affected dentin by an adhesive system. Flat dentin surfaces (n=100) were produced, and 50 were submitted to a biological method of artificial caries induction. Within each type of substrate, noncarious and caries-affected dentin, the surfaces were divided into 5 groups (n=10): with smear layer, smear layer-free impregnated with water, smear layer-free impregnated with CHX in water, smear layer-free impregnated with ethanol and smear layer-free impregnated with CHX in ethanol. Contact angles between the dentin surface and the adhesive system Single Bond Plus were measured by using a goniometer and the data were submitted to ANOVA and Tukey tests ( =0.05). In the second study, it was evaluated the effect of CHX in different excipients, ethanol or water, on the collagen exposure in interfaces produced on noncarious and caries-affected dentin. Flat dentin surfaces were prepared in 24 noncarious human molars, and half of them were artificially decayed. The surfaces were divided into 8 groups (n=3) according to the treatment of the dentin after its conditioning with phosphoric acid (CHX in ethanol, CHX in water, water and ethanol) and to the type of substrate used for the adhesive procedures. Specimens were produced from each tooth and histologically prepared to be stained by Goldner's trichrome. The zone of exposed collagen (CZ) was quantified (μm) under a light microscope and the data submitted to... (Complete abstract click electronic access below) / Doutor

Banca: Roberto Antonio Nicodemo / Banca: Èlcio Marcantônio / Banca: Sylvestre Arnaldo Grandine / Banca: Tetuo Okamoto / Banca: Antenor Araújo / Resumo: Não disponível / Abstract: Not available

Orientador: Milton Carlos Kuga / Resumo: O objetivo dos estudos são avaliar a capacidade de limpeza superfie dentinaria impregnada por AH Plus e MTA Fillapex, proporcionada pelo etanol a 95,0% (E) ou xilol (X) e seus efeitos sobre a interface adesiva e resistência de união do sistema adesivo etch-and-rinse, com condicionamento ácido (CA) imediato (I) ou após 7 dias (T). Publicação 1: Cinquenta espécimes de coroas de incisivos bovinos foram impregnados com o cimento e divididos em quatro grupos (n=10): G1(EICA), E e CA imediato; G2(XICA), X e CA imediato; G3(ETCA), E e CA após 7 dias e G4(XTCA), X e CA após 7 dias e G5(controle), CA imediato. Escores foram atribuídos, em relação à persistência de resíduos na dentina, por análises em MEV(500X). Cinquenta fragmentos foram preparados, restaurados com resina composta e obtidas imagens em microscopia confocal laser (1024X), para avaliar a formação de camada hibrida, mensurada no Image J. Cinquenta fragmentos foram igualmente preparados e submetidos ao teste de microcisalhamento para avaliar os efeitos sobre a resistência de união do sistema adesivo etch-and-rinse na dentina. Em relação à persistência de resíduos, G1 e G2 apresentaram maiores valores que G3 e G4 (P<0,05). Entre G1 e G2 ou G3 e G4 não houve diferença (P>0,05). Em relação à interface adesiva, a extensão da formação da camada hibrida foi G5>G4=G3=G2=G1. Em relação à resistência de união do sistema adesivo G5=G4 e G4=G2 (P=0,05), porém G5>G2 (P<0,05) e G1=G2=G3 (P>0,05). Publicação 2: Cinquenta espécimes de co... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim was to evaluate the cleaning protocol in dentin impregnated with different endodontic sealers using 95% ethanol (E) or xylol (X) and its effects on adhesive interface and on bond strength of etch-and-rinse adhesive system when the acid etching (AE) was immediately (I) carried out or 7 days delay (D).Publication 1:Fifty bovine incisors specimens were impregnated with epoxy resin-based sealer (AH Plus) sealer and divided into four groups (n = 10): G1 (EIAE); G2 (XIAE); G3 (EDAE); G4 (XDAE) and G5 (control, IAE). The persistence of residues was evaluated using scores by SEM (500X). Fifty fragments were prepared similarly as described before, restored with composite resin and subjected to laser confocal microscopy (1024X). The hybrid layer formation was measured using Image J program. Another fifty fragments were similarly prepared and submitted to microshear bond test to access the bond strength of etch-and-rinse adhesive system to dentin.Regarding the persistence of residues, G1 and G2 presented higher values than G3 and G4 (P<0.05). No statistical difference was found between G1 and G2 or G3 and G4 (P>0.05). Regarding the adhesive interface, the extend of hybrid layer formation G5>G4=G3=G2=G1.Regarding the bond strength of adhesive system: G5=G4 and G4=G2 (P=0.05), however G5>G2 (P<0.05) and G1=G2=G3 (P>0.05).Publication 2: Fifty bovine crown specimens were impregnated with mineral trioxide aggregate-based (MTA) sealer and divided into four groups (n = 10): G1 (EIAE); G2 (XIAE); G3 (EDAE); G4 (XDAE) and G5 (control, IAE). The residues persistence using scores by SEM (500x). Fifty fragments were prepared similarly as described before and subjected to laser confocal microscopy (1024X). The hybrid layer formation was measured using Image J program. Fifty fragments were similarly prepared and submitted to microshear bond test to access the bond strength of etch-and-rinse ...(Complete abstract electronic access below) / Doutor

Orientador: Edson Alves de Campos / Banca: Milton Carlos Kuga / Banca: Marco Antonio Húngaro Duarte / Resumo: O objetivo deste estudo foi avaliar, por meio de ensaio push-out, a resistência de união de pinos de fibra de vidro cimentados com cimento resinoso empregando-se diferentes protocolos de tratamento da dentina, com clorexidina e etanol. Cinqüenta dentes caninos humanos extraídos por motivos periodontais, tratados endodonticamente tiveram suas raízes preparadas para receber pino de fibra de vidro. As raízes foram aleatoriamente divididas em cinco grupos (n=10), de acordo com o tratamento da dentina condicionada: Grupo 1 (controle): água destilada; Grupo 2: solução aquosa de diacetato de clorexidina a 1% ; Grupo 3: solução alcoólica de diacetato de clorexidina a 1%; Grupo 4: etanol a 99% e Grupo 5: solução de digluconato de clorexidina 2%. Após o tratamento da dentina condicionada, aplicou-se o sistema adesivo e pino de fibra foi cimentado com cimento resinoso. Todos os espécimes foram armazenados em água destilada por 24 h. Após este tempo, foram obtidas secções horizontais de cada um dos terços da raiz e o teste push-out foi realizado para avaliação da resistência de união. Os resultados foram obtidos (em MPa) e os dados analisados com ANOVA e teste de Tukey (P < 0,05). Os padrões de falha foram classificados em adesiva, coesiva ou mista. Em todos os terços, G3 e G4 apresentaram valores médios de resistência de união similares, mas maior que os outros grupos. G1, G2 e G5 foram semelhantes entre si. Independentemente dos terços da raiz, G3 e G4 exibiram mais incidência de falhas mista. O tratamento da dentina radicular com etanol, isolado ou associado com diacetato de clorexidina a 1% aumentou a resistência de união do pino de fibra cimentado com cimento resinoso, em comparação com o tratamento da dentina radicular com água destilada ou diacetato de clorexidina a 1% ou 2%, em curto prazo / Abstract: The aim of this study was to evaluate if radicular dentine pretreatment with various protocols using chlorhexidine and/or ethanol improves the push-out bond strength of fiber posts luted with resin cement. A total of 50 space post prepared in endodontically-treated extracted human canine roots were randomly divided into five groups (n = 10), according to dentine pretreatment: Group 1 (control): distilled water; Group 2: 1% chlorhexidine diacetate solution; Group 3: chlorhexidine diacetate + 99% ethanol; Group 4: 99% ethanol, and Group 5: 2% chlorhexidine digluconate solution . After pretreatment, an adhesive system was applied into radicular dentine and fiber post was luted with resin cement. All specimens were stored in distilled water for 24 h. After this time, horizontal slices were obtained from each root thirds and push-out bond strength was assessment. The results were obtained (in MPa) and data analyzed with ANOVA and Tukey tests (P = 0.05). Failure modes were classified in adhesive, cohesive or mixed. At all thirds, G3 and G4 presented similar push-out bond strength values (P > 0.05), but higher than other groups (P < 0.05). G1, G2 and G5 were similar (P > 0.05). Regardless the root thirds, G3 and G4 exhibited more mixed failures incidence. The radicular dentine pretreatment with ethanol, alone or associated with chlorhexidine diacetate increased the bond strength of fiber post luted with resin cement, in comparison to radicular dentine pretreatment with distilled water, 2% chlorhexidine digluconate solution or 1% chlorhexidine diacetate solution, independently of root thirds, when evaluated in short-time / Mestre

Avaliou-se a influência da aplicação do laser Nd:YAG ou solução de EDTA nas paredes de canais radiculares, sobre a capacidade seladora de obturações realizadas com dois tipos de cimento. Utilizou-se sessenta e oito dentes pré-molares inferiores humanos, dos quais sessenta e dois foram usados para analisar o selamento apical e seis para analisar as características das paredes dos canais radiculares sob M.E.V, após o tratamento pelo EDTA trissódico e pelo laser Nd:YAG. Os dentes tiveram suas coroas cortadas na junção cemento - esmalte e os canais radiculares foram instrumentados pela técnica automatizada com padronização dos forames apicais por uma lima tipo Kerr nº 25. Terminada a instrumentação dos canais, as superfícies externas radiculares foram impermeabilizadas, exceto o forame apical. As raízes foram, então, divididas em 4 grupos de 15, de acordo com o tipo de tratamento realizado nas paredes dos canais radiculares e o tipo de cimento utilizado para a mesma. Grupo I - aplicação do laser Nd:YAG e obturação com cimento AH Plus; Grupo II - aplicação do laser Nd:YAG e obturação com cimento Endofill; Grupo III - aplicação de EDTA por 5 minutos e obturação com cimento AH Plus; Grupo IV - aplicação de EDTA por 5 minutos e obturação com cimento Endofill. Dois dentes serviram de controles negativo e positivo. Em seguida, as raízes foram imersas em solução de azul de metileno a 2%, durante 48 horas. Após a remoção da impermeabilização foi realizado o desgaste das raízes para leitura da magnitude das infiltrações, por meio de um microscópio óptico pela técnica da planimetria. Os resultados indicaram que o cimento AH Plus foi o que permitiu menor infiltração apical, assim como a aplicação do laser Nd:YAG, quando utilizado no tratamento das paredes dos canais radiculares, anteriormente à obturação. / This study aimed at evaluating the influence of applying Nd:YAG laser or an EDTA solution in the root canal walls, on the sealing capacity of fillings performed with two sorts of cements. Sixty-eight human lower premolars, being 62 used for the analysis of apical sealing and 6 to analyse the wall characteristics of root canals under SEM, following treatment with trisodic EDTA and Nd:YAG laser were utilized. The teeth had their crowns cut at the cementoenamel junction and the root canals were instrumented through automatized technique with standardization of apical foramen by a # 25 Kerr file. Upon completion of root canal instrumentation, the external root surfaces were impermeabilized, except for the foramen. The roots were then divided into 4 groups of 15, according to the type of treatment performed on the root canal walls and the type of cement utilized in the filling. Group I – application of Nd:YAG laser and filling with AH Plus cement; Group II – application of Nd:YAG laser and filling with Endofill cement; Group III – application of EDTA for 5 minutes and filling with AH Plus cement; Group IV - application of EDTA for 5 minutes and filling with Endofill cement. Two teeth served as negative and positive controls. Afterwards, the roots were immersed in a 2%-methylene blue dye, for 48 hours. Wearing of the roots took place following the removal of impermeabilization for the reading of leakage magnitude, by means of a light microscope through planimetry technique. The results indicated AH Plus cement as the one to allow the least apical leakage, as well as Nd:YAG laser application, when utilized in the treatment of root canal walls, prior to filling.

Submitted by Leonardo Freitas (leonardo.hfreitas@ufpe.br) on 2015-04-14T13:58:42Z No. of bitstreams: 2 TESE Renata GUIMARÃES.pdf: 2863665 bytes, checksum: 158d65a6ff45fcb1c843a03fbded403d (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) / Made available in DSpace on 2015-04-14T13:58:42Z (GMT). No. of bitstreams: 2 TESE Renata GUIMARÃES.pdf: 2863665 bytes, checksum: 158d65a6ff45fcb1c843a03fbded403d (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Previous issue date: 2012-12-17 / CAPES / Objetivo: Avaliar o desempenho de cimentos resinosos frente à desproteinização dentinária através de ensaio de cisalhamento por extrusão de pinos de fibra de vidro. Método: Raízes de 83 pré-molares inferiores humanos foram divididas em 2 grupos conforme o tratamento da dentina (Convencional – recomendações do fabricante e Desproteinização – NaOCl 5,0%/1min). Cada grupo foi dividido em 4 subgrupos segundo o cimento utilizado na cimentação dos pinos de fibra de vidro (Relyx ARC/3M-ESPE; SET/SDI; RelyxU100/3M-ESPE; Cement Post/Angelus). Após 1 semana foi realizado o ensaio push-out. O padrão de falha pós-ensaio foi obtido, de cada corpo de prova, por microscopia óptica. Os dados foram analisados pelo teste F (ANOVA) com comparações de Tukey ou de Tamhane e t-Student (α=5%). Para 3 espécimes foi realizada análise em MEV quanto à morfologia da dentina segundo o tipo de condicionamento. Resultados: A desproteinização influenciou positivamente o desempenho do Cement Post (Terço médio) e Relyx U100 (Terço apical), negativamente para o RelyxARC (Terços cervical e apical) e indiferentemente para o SET. O RelyX U100 e ARC apresentaram os maiores valores de adesão comparados ao SET e Cement Post. O terço cervical apresentou os melhores resultados, com exceção do RelyX U100, no qual o terço apical foi superior. Falhas adesivas foram mais prevalentes no terço cervical (> 50%) e as mistas nos terços médio e apical (>50%). Conclusões: 1. A desproteinização influenciou positivamente a adesão quando empregados o Cement Post (terço médio) e RelyX U100 (terço apical); 2. O Relyx U100 e Relyx ARC obtiveram os melhores resultados

Orientador: Caio Cezar Randi Ferraz / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T09:00:03Z (GMT). No. of bitstreams: 1 Cecchin_Doglas_D.pdf: 5848627 bytes, checksum: c2fd006628320385f2b73dadf55f0781 (MD5) Previous issue date: 2010 / Resumo: A resistência de união de pinos à dentina radicular pode ser comprometida ao longo do tempo pela degradação da interface adesiva. Por isso, o objetivo deste estudo foi avaliar o efeito do pré-tratamento da dentina radicular com clorexidina 2% (CHX), etanol 100% (EtOH) e hipoclorito de sódio 5,25% (NaOCl) e a associação dessas substâncias, na resistência de união e durabilidade adesiva de pinos de fibra de vidro reembasados com resina composta à dentina radicular. Também foram avaliadas a técnica úmida (TU) e seca (TS) (secagem com jatos de ar por 5 segundos). No capítulo 1 que compõe este trabalho, os prétratamentos foram: G1(controle)- irrigação com soro fisiológico; G2- TS; G3- CHX por 5 minutos; G4- EtOH por 1 minuto; e G5- CHX por 5 minutos seguido de EtOH por 1 minuto. Logo após, os canais foram secos com cones de papel absorvente (TU) e a dentina hibridizada com Scotch Bond. No G2, após a TU foi realizada TS. Pinos fibra de vidro reembasados com resina composta foram cimentados com Rely X ARC. Cada grupo foi dividido em 3 subgrupos: 24 horas de armazenamento em água; 12 meses em água; 12 meses em óleo. Todos as raízes foram seccionadas, o teste de push-out realizado e os valores de resistência de união analisados estatisticamente pelos testes ANOVA/Tukey's (a=0,05). Os grupos imediatos apresentaram valores similares (P>0,05), com exceção da TS que resultou em menores valores de resistência de união (P<0,05). A CHX preservou os valores nos grupos estocados por 12 meses (P>0,05), e os demais grupos estocados apresentaram redução nos valores de resistência de união (P<0,05). Pode-se concluir que apenas a CHX foi capaz de preservar os valores de resistência por 12 meses. No capítulo 2, foi realizado o pré-tratamento da dentina radicular com NaOCl isolado e em associação com CHX e/ou EtOH, além da realização da TU e TS. O sistema adesivo, os demais procedimentos e análise estatística foram similares ao capítulo 1. Os resultados mostraram maiores valores de resistência de união nos grupos onde apenas o NaOCl foi utilizado ou associado à CHX, com a TU ou TS, nos grupos imediatos e armazenados por 12 meses (P>0.05). Nos grupos onde EtOH foi utilizado, os valores de resistência de união foram menores (P<0,05). Foi possível concluir que o NaOCl isolado ou associdado com CHX foi capaz de preservar os valores de resistência de união por 12 meses. No capítulo 3, os grupos foram iguais aos do capítulo 1, no entanto a TS não foi estudada e o adesivo utilizado foi o Clearfil SE Bond. O preparo das amostras e análise estatística foram similares ao capítulo 1. Os grupos imediatos apresentaram valores similares de resistência de união (P>0,05). Houve diminuição significante nos grupos controles após 12 meses de armazenamento (P<0,05). O uso de CHX e/ou EtOH preservou os valores de resistência de união por 12 meses (P>0,05). Pode-se concluir que o pré-tratamento da dentina com CHX e/ou EtOH foi capaz de preservar a resistência de união por 12 meses. / Abstract: The bond strength of posts to root dentin can be compromised over time by adhesive interface degradation. Therefore, the aim of this study was to investigate the effects of pre-treatment of root dentin with 2% chlorhexidine (CHX), 100% ethanol (EtOH) and 5.25% sodium hypochlorite (NaOCl), as well as the association of these substances, on the bond strength and adhesive durability of fiber posts relined with resin composite to root dentin. The wet (WT) and dry (ST) (air-drying for five seconds) techniques were also evaluated. The first chapter of this work, the pre-treatments were: G1-control, irrigation with physiologic solution; G2, ST; G3, 5 minutes with CHX; G4, 1 minute with EtOH; and G5, 5 minutes with CHX followed by 1 minute EtOH. Afterwards, the root canals were dried with absorbent paper cones (WT) and the dentin hybridized with Scotch Bond. In G2, after WT was realized ST. Fiber post relining with resin composite was cemented with RelyX ARC. Each group was randomly divided into three subgroups: 24 h of water storage, 12 months of water storage, and 12 months of oil storage. All roots were sectioned transversely, the push-out test was performed and bond strength values were analyzed by ANOVA/Tukey's test (a=0.05). Immediate groups showed similars bond strengths (P>0.05), except that the ST significantly decreased bond strength (P<0.05). The use of CHX preserved bond strength in the groups stored in water and oil for 12 months (P>0.05). The other groups stored for 12 months showed a significant decrease in bond strength (P<0.05). It may be concluded that CHX preserved the bond strength for 12 months. In the second chapter, pretreatment of root dentin was performed with NaOCl alone, and associated with CHX and/or EtOH. In addition ST and WT were performed. The adhesive system, the sample preparation and statistical analysis were similar to those used in the first chapter. The results showed that the groups in which NaOCl was used alone or associated with CHX showed the highest bond strength values with ST or WT in the immediate and groups stored for 12 months (P>0.05). The groups that used EtOH showed lower bond strength and there was a statistical similarity between them (P<0.05). It may be concluded that the use of NaOCl or NaOCl associated with CHX preserved the bond strength to root dentin for 12 months. In the third chapter, the treatments were the same as those in the first chapter. However, the ST was not studied and the adhesive used was Clearil SE Bond. The sample preparation and statistical analysis were similar to those used in the first chapter. Immediate groups showed similar bond strength values with or without CHX and/or EtOH pre-treatment (P>0.05). A significant decrease in the bond strength was observed in the control groups after 12 months of storage in water and oil (P<0.05). It may be concluded that the use of CHX and/or EtOH preserved bond strength in the groups stored in water and oil for 12 months (P<0.05). / Doutorado / Endodontia / Doutor em Clínica Odontológica

Orientador: Luis Alexandre Maffei Sartini Paulillo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-13T22:07:09Z (GMT). No. of bitstreams: 1 Humel_MariaMalerbaColombi_M.pdf: 94914593 bytes, checksum: c626dc60328a5176cf526d1c4fa76f3c (MD5) Previous issue date: 2009 / Resumo: O objetivo deste estudo foi analisar a resistência a microtração, microdureza Knoop do compósito e formação de fendas em restaurações classe I utilizando três sistemas adesivos: Clearfil S3 Bond (S3), Clearfil Protect Bond (ProtectB) e One-Up Bond F Plus (OneUp); E compósito TPH3, fotoativados por fontes de Luz Emitida por Diodo (LED) ou luz halógena, tendo o ângulo cavosuperficial em esmalte condicionado ou não por ácido fosfórico à 35%. Após o término das restaurações, foram obtidas réplicas em resina epóxica para análise em Microscopia Eletrônica de Varredura (MEV) da adaptação da margem em esmalte antes e após termociclagem (n=6). Através de sorteio, a metade dos 144 dentes restaurados foi utilizada no ensaio de microtração e a outra metade no ensaio de microdureza Knoop em 3 diferentes profundidades (n=6). Uma vez que a análise de variância apontou diferença entre os fatores estudados, o resultado do teste Tukey apontou, para análise de fendas nos grupos sem condicionamento prévio do esmalte cavosuperficial, independente do adesivo aplicado, apresentou diferença estatística significativa após os ciclos, quando comparados aos valores antes da termociclagem. Para o adesivo OneUp, o condicionamento do esmalte cavosuperficial contribuiu na redução de fenda. Para o teste de microtração, a análise de variância demonstrou não haver diferença estatística siginificativa entre os fatores estudados e suas inteirações (p = 0,05). Os adesivos OneUp e S3 apresentaram maiores valores de microdureza Knoop no topo, e o adesivo ProtectB não apresentou diferenças estatísticas entre as três profundidades. O adesivo S3 apresentou os menores valores de dureza nas profundidades de base e intermediária. Os sistemas autocondicionantes não apresentaram diferença na união ao substrato dentário, independente de sua forma de aplicação e do condicionamento prévio do esmalte cavosuperficial. Porém, o condicionamento do esmalte cavosuperficial contribuiu na diminuição da formação de fendas, apenas para o adesivo OneUp se comparados os grupos após termociclagem sem condicionamento e com condicionamento do esmalte cavosuperficial. A composição do adesivo utilizado teve influência na microdureza Knoop do compósito odontológico dependendo da profundidade da cavidade. A luz LED apresentou melhores valores de microdureza quando comparado à luz Halógen / Abstract: The aim of this study was to analyze the microtensile bond strength, Knoop microhardness and gap formation of class I restorations using three different self-etching adhesives: Clearfil S3 Bond (S3), Clearfil Protect Bond (ProtectB) and One-Up Bond F Plus (OneUp). TPH3 restorative composite was used with two different light activation: Light Emitted by Diode or Halogen Lamp and the superficial enamel was etched or not with 35% phosphoric acid. After restorative procedure, epoxy resin replicas were obtained before and after submitted teeth to thermal cycling for gap analyzes by Scanning Electronic Microscopy (SEM) of enamel marginal adaptation. Half of teeth were randomly divided to microtensile bond strength test and the other half to microhardness test (n=6). For gap formation, the Tukey's test showed statistical differences before and after thermal-cycling to the groups without enamel etching. For OneUp adhesive, the etched enamel contributed to avoid gap formation when compared groups before thermal-cycling with and without enamel cavosurface etching. OneUp and S3 adhesives showed the highest square means on top surface for Knoop microhardness results, and S3 showed the lowest square means for the middle and base surfaces. ProtectB showed no significant differences for the different surface depth. The self-etching adhesives showed no significant difference to the microtensile Bond strength, irrespective to the different application procedure and previous etching or not of the enamel surface. However, the etched enamel contributed to avoid gap formation when OneUp adhesive system was used when compared groups befoure termocycling with and without enamel cavosurface etching. The adhesive system showed an influence on resin composite to Knoop microhardness test depending on the restoration depth. The LED light activation restorations showed the highest microhardness means when compared with Halogen Lamp. / Mestrado / Dentística / Mestre em Clínica Odontológica

O objetivo desse trabalho foi determinar o efeito do primer do cimento de ionômero de vidro modificado por resina, na resistência de união através de testes de microtração, de sistemas adesivos convencionais e autocondicionantes à dentina. O plano oclusal dentinário dos dentes terceiros molares humanos extraídos foi cortado na máquina de corte e depois preparado usando lixa de papel de granulação nos. 80, 320 e 600 com irrigação. Estes dentes foram divididos nos seguintes grupos: GRUPO 1 – ácido fosfórico a 35 % + sistema adesivo Single bond + resina Z-250 controle); GRUPO 2 - sistema adesivo autocondicionante One Up Bond F + resina Z-250 (controle); GRUPO 3 - primer + ácido fosfórico a 35 % por 15 s + sistema adesivo Single bond + resina Z-250; GRUPO 4 - primer + ácido fosfórico a 35 % por 30 s + sistema adesivo Single bond + resina Z-250; GRUPO 5 – primer + sistema adesivo autocondicionante One Up Bond F + resina Z-250. Foram preparados espécimes em forma de bastões de 1.0 × 1.0 mm de resina composta e submetidos ao teste de microtração à velocidade de 1.0 mm/ min em uma máquina de ensaio universal. Os resultados e respectivos desvios-padrão foram: GRUPO 1- 22.56 ± 6.43 MPa; GRUPO 2 - 22.51 ± 6.14 MPa; GRUPO 3 -19.24 ± 5.38 MPa; GRUPO 4 - 22.01 ± 6.23 MPa; GRUPO 5 - 24.95 ± 7.46 MPa.. Após análise estatística pelos testes ANOVA a um critério e teste de Tukey foi possívelconcluir que o primer do cimento de ionômero de vidro modificado por resina interfere na resistência adesiva à microtração dos sistemas adesivos convencionais, mas não altera a resistência adesiva à dentina dos adesivos autocondicionantes. / The purpose of this study is to determine the influence of the resin-modified glass ionomer cement primer on the microtensile strength of conventional and self-etching adhesive systems to dentin. Flat occlusal dentin surfaces of extracted human third molars were prepared using wet SiC paper from # 80, 320 and 600 and divided into the followed groups: GROUP 1 – Phosphoric acid 35 % + Single bond bonding system + Z-250 resin composite (group control) ; GROUP 2 - One up bond F self-etching adhesive + Z-250 resin composite (group control); GROUP 3 - primer + Phosphoric acid 35 % for 15 s + Single bond bonding system + Z-250 resin composite; GROUP 4 - primer + Phosphoric acid 35 % for 30 s + Single bond bonding system + Z-250 resin composite; GROUP 5 – primer + One up bond F self-etching adhesive + Z- 250 resin composite. Resin composite – dentin beams with areas on average of 1.0 mm2 were prepared and submitted to the microtensile test at a crosshead speed of 1.0 mm/min. Results of the microtensile test were: GROUP 1 - 22.56 ± 6.43 MPa; GROUP 2 - 22.51 ± 6.14 MPa; GROUP 3 - 19.24 ± 5.38 MPa; GROUP 4 - 22.01 ± 6.23 MPa; GROUP 5 - 24.95 ± 7.46MPa. The mean bond strengths were statiscally analyzed by a one-way ANOVA and Tukey tests which allowed to conclude that the resin-modified glass ionomer cement primer decreases the microtensile bond strengths of conventional adhesive system to dentin. The bond strengths of self-etching adhesive system to dentin were not altered by the presence of the primer.