Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2018. / Submitted by Raquel Almeida (raquel.df13@gmail.com) on 2018-05-18T17:29:27Z No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) / Approved for entry into archive by Raquel Viana (raquelviana@bce.unb.br) on 2018-05-29T18:39:18Z (GMT) No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) / Made available in DSpace on 2018-05-29T18:39:18Z (GMT). No. of bitstreams: 1 2018_RaissaCarneiroAntunes.pdf: 57842534 bytes, checksum: c28ca83f1743bbc2e054101b0de749f9 (MD5) Previous issue date: 2018-05-29 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES). / Os objetivos do presente estudo consistiram em avaliar in vitro, por meio de teste de condutância hidráulica, a redução da permeabilidade dentinária ao longo do tempo e, por meio de teste de microtração, a resistência de união de sistemas adesivos universais à dentina de sistemas adesivos universais variando-se o modo de aplicação (convencional e autocondicionante) e o tipo de smear layer (espessa e delgada). Foram testados dois sistemas adesivos universais em suas técnicas autocondicionante e convencional: Single Bond™ Universal e Clearfil™ Universal. Como controle positivo foram utilizados os sistemas adesivos: Adper™ Scotchbond Multi-Purpose e o Clearfil™ SE Bond. Cento e vinte terceiros molares humanos foram utilizados, sendo sessenta destinados para cada teste. Para o teste de permeabilidade, os dentes foram seccionados em discos de dentina com auxílio de uma máquina de cortes e, após uma leitura de permeabilidade inicial, os procedimentos adesivos foram executados. As leituras de permeabilidade foram realizadas nos tempos: T0- após remoção da smear layer; T1 – imediatamente ao procedimento adesivo; T2 – 24 horas após ao procedimento adesivo; T3 – 7 dias após ao procedimento adesivo; T4 – 21 dias após ao procedimento adesivo; T5 – 6 meses após ao procedimento adesivo. Foram realizadas moldagem das superfícies adesivas de um espécime de cada grupo e preparo de réplicas em resina epóxica para análise em Microscopia Eletrônica de Varredura (MEV). Para o teste de microtração, os dentes foram seccionados em hemi-dentes, seguida de remoção a parte coronal, expondo dentina. Os procedimentos adesivos foram realizados seguido de restauração em resina composta de 4mm de altura. Com as restaurações prontas, cada hemi-dente foi seccionado em palitos com área adesiva de 0,8mm2. Após um período de 48h, os palitos foram fixados em jigs plásticos e submetidos à teste de microtração. As fraturas foram classificadas em: adesiva, coesiva em dentina, coesiva em resina e mista. Após o término do experimento, alguns palitos de cada tipo de fratura foram levados para metalização seguida de posterior análise em MEV. Os valores de condutância hidráulica foram avaliados ao longo do tempo utilizando o teste two-way ANOVA para medidas repetidas. Observou-se que a interação entre as variáveis tratamento (diferentes sistemas adesivos e tipo de smear layer) e tempo (T1 a T5) foi significativa (p=0.0020), assim como ambas as variáveis isoladamente, sendo o valor de p igual a 0.0279 para a variável tratamento e de 0.0023 para a variável tempo. Até o período T4, não houve diferença entre os grupos experimentais (p >0.05). Entretanto, para o período de avaliação de 6 meses (T5), observou-se um aumento significativo na permeabilidade dentinária Single Bond™ Universal utilizado na técnica autocondicionante associado a smear layer espessa), quando comparados aos demais grupos (two-way ANOVA; p<0.05). As imagens de MEV confirmam esse resultado, uma vez, que para esse grupo foram observadas uma maior quantidade de bolhas de agua na superfície do disco. Os valores de resistência de união foram analisados pelo teste de Kruskall Wallis e não foram observadas diferenças significativas entre os grupos (p=0.078). A partir dos dados obtidos, foi possível concluir que o adesivo Single-Bond Universal apresentou uma redução na sua capacidade de selamento dentinário apos 6 meses quando aplicado sobre smear-layer espessa. / The aims of this study were to evaluate, by hydraulic conductance, the sealing effectiveness over time and the resin-dentin microtensile bond strength of universal adhesive systems in its two techniques (self-etch and etch-and-rinse), ranging the thickness of smear layer (SL - thick and thin). Two universal adhesive systems were tested: Single Bond™ Universal and Clearfil™ Universal. The positive controls were: Adper™ Scotchbond Multi-Purpose and Clearfil™ SE Bond. Sixty human thirdmolars were used for each test. To the hydraulic conductance test, the teeth were sectioned in discs, and after an initial permeability measurement, the adhesive procedures were executed. The hydraulic conductance tests were performed in the following periods: T0 – after removal of smear layer; T1 – immediately after the adhesive application; T2 – 24 hours after the adhesive application; T3 – 7 days after the adhesive application; T4 – 21 days after the adhesive application; T5 – 6 months after the adhesive application. It was performed an impression with silicon of one specimen of each group and epoxy resin replicas were obtained and analyzed in Scanning Electron Microscope (SEM). To the microtensile test, the teeth had their dentin exposed by removing the coronal layer. The adhesive procedures were executed followed by the construction of 4mm composite restorations. The teeth were sectioned obtaining 0,8mm2 resin-dentin sticks, which were fixed in plastic supports and submitted to microtensile test after 48 hours. The fracture modes were categorized in: adhesive, mixed, cohesive failure within dentin and cohesive failure within resin composite. Some sticks were chosen to be observed under SEM. The hydraulic conductance values were analyzed by two-way repeated measures ANOVA. The interaction between the variables treatment (different adhesive systems and smear layer) and time (T1 to T5) were significant (p=0.0020), as so the variables independently (treatment: p=0.0279; time; p=0.0023). Until T4, there weren’t differences between the experimental groups (p>0.05). However, in T5, a significant increase in hydraulic conductance was observed for Single Bond™ Universal in the self-each mode with thick smear layer (two-way ANOVA; P<0.05). The SEM micrographs confirmed the greater amount of bubbles on the disc surface for this group. The microtensile bond strength values were analyzed by Kruskall Wallis and no statistical differences between groups (p=0.078). Based on the present data, it was concluded that Single Bond™ Universal presented a reduction on its ability of dentin sealing after 6 months when applied over a thicker smear-layer.

Dissertação (mestrado)—Universidade de Brasília, Faculdade de Ciências da Saúde, Programa de Pós-Graduação em Ciências da Saúde, 2017. / Submitted by Albânia Cézar de Melo (albania@bce.unb.br) on 2017-04-19T15:49:50Z No. of bitstreams: 1 2017_FernandaSantoroNogueira.pdf: 1185479 bytes, checksum: d994ba44e6dfe5527d91eedf16d9b748 (MD5) / Approved for entry into archive by Raquel Viana(raquelviana@bce.unb.br) on 2017-04-27T21:46:52Z (GMT) No. of bitstreams: 1 2017_FernandaSantoroNogueira.pdf: 1185479 bytes, checksum: d994ba44e6dfe5527d91eedf16d9b748 (MD5) / Made available in DSpace on 2017-04-27T21:46:52Z (GMT). No. of bitstreams: 1 2017_FernandaSantoroNogueira.pdf: 1185479 bytes, checksum: d994ba44e6dfe5527d91eedf16d9b748 (MD5) / Várias estratégias têm sido desenvolvidas com o intuito de promover a remineralização da dentina através de mecanismos biomiméticos. O objetivo desta revisão foi de avaliar como as distintas técnicas de remineralização biomimética influenciam na longevidade da união dentina-resina. A pesquisa foi realizada nas bases de dados Pubmed, Lilacs, Cochrane, Web of Science, Scopus e, como fonte de literatura cinzenta, pesquisa no Google Scholar. Na busca foram encontrados 1837 artigos, dos quais 1731 foram excluídos após a seleção final. Após leitura completa dos estudos, 16 artigos foram incluídos nesta revisão. Todos os estudos foram submetidos à análise de qualidade pelo método GRADE e análise de risco de viés pelo CRIS Guideline. Sete artigos relataram o uso de análogos biomiméticos e / ou moléculas polianiônicas como fonte de cálcio e um meio para favorecer a remineralização. Seis estudos descreveram métodos que utilizam agentes do tipo cross-linkers, tais como proantocianidina e clorexidina. Dois estudos descreveram a utilização do peptídeo E8DS e a utilização de ácido meta-fosfórico. A atual revisão sistemática confirma o potencial das técnicas de remineralização biomimética em favorecer a longevidade da união dentina -resina. De acordo com os achados desta revisão, são necessários mais estudos que avaliem os efeitos a longo prazo, os mecanismos individuais envolvidos em cada abordagem de remineralização biomimética e a aplicabilidade clínica. / Various strategies have been developed in order to promote the remineralization of dentin by the use of biomimetic mechanisms.The aim of this systematic review is to evaluate how these strategies influence the durability of the resin-dentin bond. Studies were gathered by searching the databases Pubmed, Lilacs, Cochrane, Web of Science, Scopus and, as a grey literature, in Google Scholar. A total of 1837 studies were found, and 1731 were excluded after initial screening. After retrieving the full text, 16 were included in this systematic review. All studies were submitted to quality assessment and risk of bias analyses by the GRADE method and CRIS Guideline, respectively. Seven papers reported the use of biomimetics analogs and/or polyanionic molecules as a calcium source and as a path to favor remineralization. Six studies have described methods that use cross-linking agents, such as proanthocyanidin and chlorhexidine.Two studies described the use of peptide E8DS and the use of meta-phosphoric acid. The present systematic review confirms the potential value of the biomimetic techniques in favoring the durability of dentin-resin bond. According to the findings, it is required more studies that evaluate the long-terms effects, the individual mechanisms involved in each approach and the clinical applicability.

Este ensaio clínico randomizado, controlado, duplo-cego, em paralelo, objetivou comparar o efeito do cimento de hidróxido de cálcio (grupo HC) ao de um material inerte (grupo cera) sobre a dentina cariada de molares decíduos submetidos à remoção incompleta de tecido cariado, bem como verificar a correlação entre coloração, consistência e contaminação da dentina. A amostra foi constituída por 30 crianças, de 4 a 8 anos de idade, que apresentavam um molar decíduo com lesão de cárie ativa em dentina profunda, sem sinais clínicos e radiográficos de patologia pulpar irreversível. Após anestesia local e isolamento absoluto do campo operatório, a dentina cariada das paredes laterais da cavidade foi totalmente removida, e a da porção pulpar, parcialmente removida. Um examinador calibrado avaliou visualmente o grau de coloração e de consistência da dentina cariada remanescente. Uma amostra do tecido cariado foi coletada para avaliação ao microscópio eletrônico de varredura (MEV). Aplicou-se, aleatoriamente, um dos materiais capeadores sobre o tecido, e os dentes foram restaurados com sistema adesivo e resina composta. Passados 90 dias realizou-se o exame clínico e radiográfico, remoção da restauração e do material capeador, avaliação da coloração e consistência do tecido e coleta de amostra da dentina remanescente. Após a fixação e preparo para MEV, foi realizado um registro, em 2000x de aumento, da região central de cada amostra e o escore do grau de contaminação foi determinado. Para comparação entre os grupos dos graus de coloração, consistência e contaminação atribuídos no início e no final do estudo aplicou-se a prova U de Mann-Whitney. Através do teste de Wilcoxon, as variáveis estudadas foram comparadas entre a fase inicial e final do estudo, dentro de um mesmo grupo. O teste de correlação de Spearman foi realizado para avaliar a correlação entre as variáveis clínicas e a contaminação da dentina. O nível de significância estabelecido foi de 5%, e o indivíduo considerado a unidade analítica. Não houve diferença entre os grupos quanto à coloração (p=0,355), consistência (p=0,329) e contaminação (p=0,561) dentinária no início do estudo. Ao final, houve diferença quanto à coloração (p=0,023) e consistência (p=0,022), demonstrando que o hidróxido de cálcio promoveu endurecimento e escurecimento da dentina significativamente maior do que a cera. Quanto aos graus de contaminação, não houve diferença entre os grupos (p=0,703). Entre as fases do estudo, o hidróxido de cálcio promoveu alteração significativa nos graus de coloração (p=0,011), consistência (p=0,003) e contaminação (p=0,006) da dentina; enquanto a cera promoveu alteração nos níveis de consistência (p=0,007) e contaminação (p=0,003), não alterando os graus de coloração (p=0,564) da dentina. A coloração e contaminação iniciais apresentaram correlação positiva (rS=0,40; p=0,028), enquanto a consistência e contaminação finais apresentaram correlação negativa (rS=-0,50; p=0,005). Concluiu-se que o cimento de hidróxido de cálcio e a cera, quando utilizados como capeadores da dentina cariada, promoveram a inativação do processo carioso verificada por meio da alteração na consistência, bem como redução na contaminação do tecido.

Orientador: Josimeri Hebling / Banca: Fabio Duparte Nacimento / Banca: Linda Wang / Banca: Elisa Maria Aparecida Giro / Banca: Gelson Luis Adabo / Resumo: O objetivo geral deste trabalho foi avaliar a citotoxicidade transdentinária da carbodiimida (EDC), bem como sua influência na degradação do colágeno dentinário e na estabilidade da união resina-dentina. No estudo 1, células MDPC- 23 foram plantadas na superfície pulpar de discos de dentina e a superfície oclusal foi tratada por 60s com uma das seguintes soluções: sem tratamento; EDC 0,1M; 0,3M ou 0,5M; glutaraldeído 5% (GA); tampão Sorensen ou H2O2 29%. A viabilidade e a morfologia celular foram analisadas pelos testes de MTT, Live/dead, produção de proteína total (PT), de colágeno e MEV. Os dados foram analisados pelos testes de Kruskal-Wallis e Mann-Whitney (p<0,05). O GA promoveu aumento do metabolismo celular. A morte por necrose e a morfologia celular não foram influenciadas pelos agentes cross-linkers. Não houve redução na produção de PT e colágeno após 7 dias. Para o estudo 2, espécimes de dentina foram completamente desmineralizados e a variação do módulo de elasticidade (E), inibição de MMP, perda de massa, liberação de hidroxiprolina (HYP) e degradação térmica do colágeno (DTC) foram analisados após tratamento com uma das seguintes soluções por 30s ou 60s: água deionizada (controle); EDC 0,5M; EDC 1M; EDC 2M e GA 10%. Os dados referentes ao E, atividade de MMP e liberação de HYP foram submetidos aos testes de Wilcoxon e Kruskal- Wallis ou Mann-Whitney. Os valores de perda de massa e DT foram analisados pelos testes de ANOVA e Tukey (p<0,05). Os melhores resultados quanto ao E foram observados para o GA. Todos os cross-linkers reduziram a atividade de MMP e a liberação de HYP e aumentaram a temperatura de DT do colágeno. No estudo 3, sessenta palitos de dentina foram divididos em 6 grupos de acordo com a solução de tratamento: água deionizada (controle); EDC 0,1M; EDC 0,5M; EDC 0,5M + HEMA 35%; proantocianidina 5% (PA) ou clorexidina (CHX) 2%. Após... / Abstract: The purpose of this study was to evaluate the trandentinal cytotoxicity of carbodiimide (EDC), as well as its influence on dentinal collagen degradation and stability of resin-dentin bonds. In the first experiment, MDPC-23 cells were seeded on the pulp surface of the disks and one of the following solutions was applied on the occlusal surface for 60s: no treatment (negative control), 0.1M, 0.3M or 0.5M EDC; 5% glutaraldehyde (GA); Sorensen buffer or 29% hydrogen peroxide (positive control). Cell viability and morphology were analyzed by MTT, Live/Dead assays, total protein (TP) and collagen production and SEM. Data were analyzed by Kruskal-Wallis and Mann-Whitney tests (p<0.05). Only GA increased cellular metabolism. Cell death by necrosis and cell morphology were not affected by the cross-linker agents. There was no reduction in TP and collagen production after 7 days. For the second experiment, dentin beams were completely demineralized and the variation in elastic modulus (E), MMP activity, dry mass loss, hydroxyproline release (HYP) and collagen thermal degradation (CTD) were analyzed after the dentin treatment for 30s or 60s with the following solutions: water; 0.5M; 1M or 2M EDC and 10% GA. Data from E and MMP activity and HYP release were submitted to Wilcoxon and Kruskal-Wallis or Mann-Whitney tests. Dry mass loss and CTD data were analyzed by ANOVA and Tukey's tests (p>0.05). GA group obtained the highest E values. All cross-linking agents decreased MMP activity and HYP release and increased CTD. In the third experiment, sixty dentin beams were randomly divided into 6 groups according to the treatment solution: deionized water (control), 0.1M EDC, 0.5M EDC, 0.5M EDC+35% HEMA, 5% proanthocyanidin (PA) or 2% chlorhexidine (CHX). The beams were acid etched and treated for 60s. The total MMP activity was analyzed by a colorimetric assay (Sensolyte®). Data were expressed as absorbance values... / Doutor

Made available in DSpace on 2014-06-11T19:24:07Z (GMT). No. of bitstreams: 0 Previous issue date: 2005Bitstream added on 2014-06-13T20:51:26Z : No. of bitstreams: 1 dutracorrea_m_me_sjc.pdf: 1252552 bytes, checksum: ac3c9bb37ab987d17287a6ac4f663595 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Dentes bovinos são amplamente utilizados substituindo dentes humanos em pesquisas in vitro, para avaliar o comportamento dos materiais odontológicos. Utilizaram-se sessenta dentes bovinos e sessenta humanos. Esmalte e dentina foram avaliados individualmente em Análises Termodiferencial, Termogravimétrica e Condutividade Térmica. A Dissolução foi avaliada em diferentes tempos e concentrações de ácido. No teste de Desidratação os fragmentos foram colocados em estufa por tempos diferentes. Na Incorporação de Água, após a retirada dos fragmentos da estufa, foram resfriados e depois imersos em água destilada. Verificou-se o quanto o tecido incorporou de água em sua massa. A Penetrabilidade de Corante foi avaliada pela Espectroscopia de Fluorescência. Para avaliar a Microdureza Vickers os dentes foram incluídos em resina de poliéster e polidos até expor esmalte ou dentina. No termodiferencial as dentinas comportaram-se semelhantemente. O esmalte bovino absorveu mais energia, indicando mudanças estruturais e apresentando comportamento estável a partir de 450ºC, enquanto que o humano continuou instável. No Termogravimétrico a dentina humana foi duas vezes mais susceptível à perda de massa. Os esmaltes apresentaram Condutividades Térmicas semelhantes. A dentina humana foi mais condutora do que a bovina. Na Dissolução a perda de massa foi mais lenta no dente humano. Na Desidratação o esmalte bovino perdeu aproximadamente 25% e o humano perdeu 2,5%. No esmalte humano houve menor Penetrabilidade de Corante, porém semelhante nas dentinas. Assim, não se deve extrapolar resultados para dente humano em relação à incorporação de água, à penetrabilidade de corante, à dissolução e ao comportamento térmico. / Bovine teeth are widely required in substitution of human teeth in in vitro researches to evaluate the behavior of dental materials. Sixth human teeth and sixth bovine teeth were used. Enamel and dentin were individually evaluated under Differential Thermal Analysis, Thermogravimetry and Thermal Conductivity. The dissolution was evaluated for different periods of time and different concentrations of acid. In the dehydration test, the fragments were placed inside a stove for different periods of time. In sorption of water, after the fragments were removed from stove, cooled and immersed in distilled water. It was weighted how much water mass the tissues absorbed. The dyeing penetrability was evaluated under Fluorescence Spectroscopy. To evaluate Vickers Micro hardness, the teeth were placed in polyester resin and polished until enamel or dentin was exposed. In the Differential Thermal the dentin behaved similarly. The bovine enamel absorbed more energy, showing structural changes and reaching stability for temperatures up to 450ºC, while human teeth remained unstable. In the Thermogravimetry, the human dentin was two times more susceptible to mass loss. Both enamels presented similar thermal conductivity. Human dentin presented better conductivity than bovine. In the dissolution, mass loss was slower for human teeth. In the dehydration, bovine enamel lost approximately 25 % while human lost 2.5%. There was smaller dyeing penetrability for human enamel however similar in dentins. Therefore, the results for human teeth may not be extrapolated when related to water absorbing, dyeing penetrability, dissolution and thermal behavior.

Submitted by Stella Renata Machado Silva Esteves null (stellarmse@gmail.com) on 2018-03-15T12:49:21Z No. of bitstreams: 1 tese doutorado arquivo unico.pdf: 3856356 bytes, checksum: d346b9a5b9474275d35a835574475d08 (MD5) / Approved for entry into archive by Silvana Alvarez null (silvana@ict.unesp.br) on 2018-03-16T15:51:18Z (GMT) No. of bitstreams: 1 esteves_srms_dr_sjc.pdf: 3856356 bytes, checksum: d346b9a5b9474275d35a835574475d08 (MD5) / Made available in DSpace on 2018-03-16T15:51:18Z (GMT). No. of bitstreams: 1 esteves_srms_dr_sjc.pdf: 3856356 bytes, checksum: d346b9a5b9474275d35a835574475d08 (MD5) Previous issue date: 2018-02-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desse estudo foi avaliar um adesivo experimental com diferentes concentrações de água, bem como sua degradação morfológica, química, física e mecânica. A primeira etapa envolveu a manipulação do adesivo experimental contendo 45/55% de HEMA e BisGMA, 0.5% de canforoquinona, 0.5% EDMAB e 1% de DPIHP. Foram incorporadas diferentes concentrações de água a partir dessa formulação adesiva (0, 10 e 16%). Os modelos adesivos foram fotopolimerizados e as análises iniciais realizadas: Morfológicas (Estereomicroscopio e Micro-xct); Físicas (Rugosidade-Ru, Sorção-Sor, Solubilidade-Sol); Químicas (Grau de conversão-GC, Mapeamento do espécime com 16% de água e os monômeros liberados pela CLAE); Mecânicas (Resistência flexural-RF, Módulo de elasticidade-ME e Resistência a compressão-RC). Em seguida os espécimes foram divididos conforme a solução de envelhecimento (água, etanol e acetona). Foram realizadas novas análises após o envelhecimento por 2 e 84 dias. Os testes estatísticos ANOVA e Tukey (5%) foram realizados. Os resultados iniciais, sem o envelhecimento, mostraram que as diferentes concentrações de água influenciam as propriedades dos adesivos. Na análise morfológica notou-se a presença de bolhas no espécime com 16% de água. Para a Ru e GC os maiores valores foram encontrados para os espécimes com mais água em sua composição e os menores para 0%. Já nas análises mecânicas, para RF e ME os espécimes com 10% de água foram mais resistentes; e em RC os espécimes com 16% foram menos resistentes. Após o envelhecimento notou-se trincas nos espécimes 0% e 16% na solução de acetona. Nos testes físicos, os espécimes com 16% absorveram mais solução; o etanol mostrou menores valores de solubilidade; Para Ru a água e a acetona diferiram em todas as concentrações e períodos, o mesmo ocorrendo para as concentrações 0 e 16%. Nos testes químicos o GC não foi alterado pelo envelhecimento. O mapeamento na amostra com 16% de água mostrou que inicialmente perto do poro o GC é menor e a quantidade de HEMA é maior; longe do poro a relação é inversa. Porém, após o envelhecimento, o GC próximo ao poro se tornou similar ao distante do poro. Através da CLAE observou-se uma maior liberação de componentes do espécime com 0% de água que os espécimes com 10% e 16%. Os testes mecânicos mostraram que o envelhecimento em acetona foi mais prejudicial que em água. Para a RF e ME os espécimes com 0% de água foram mais afetados que os espécimes com 10% e 16% em 2 e 84 dias. Para a RC após 2 dias o espécime com 16% foi mais afetado que 0 e 10%, no entanto, após 84 dias o espécime com 0% foi mais afetado pelo envelhecimento. Pode-se constatar que a quantidade de água e o tipo de envelhecimento afetam as propriedades dos sistemas adesivos baseados na composição 45/55% HEMA/BisGMA. / The aim of this study was evaluated an experimental adhesive with different water content, as well the degradation morphological, physical, chemical and mechanical. Firstly the dental adhesive was manipulated with 45/55% of HEMA and BisGMA, 0.5% of CQ, 0.5% EDMAB e 1% of DPIHP. Was added different water content (0, 10 and 16%). The adhesive model was cured and the analysis was done: Morphological (Stereomicroscope and Micro-xct); Physical (Surface Roughness), Sorption, Solubility); Chemical (Degree of convertion, Map of the pore on 16% water content sample and the released monomers- HPLC); Mechanicals (Flexural strength, Modulus of elasticity and Compressive strength). After the these analyzes, the samples were divided to each evaluation into 3 groups according to solution for performed ageing (water, ethanol and acetone). Further analyzes were performed after aging for 2 and 84 days. Statistical tests of ANOVA and Tukey (5%) were performed. Initial results, without aging, showed that the different water content influence adhesive properties. In the morphological analysis, bubbles were present on the sample with 16% water. For Ru and DC all specimens differed from each other, with the highest values for the specimens with 16% and the lowest to 0%. In the mechanical analyzes, for RF and ME the specimens with 10% water were more resistant; and in RC the specimens with 16% were less resistant. After aging it is possible notice cracks on the border of specimens 0% and 16% in the acetone. In the physical tests, the specimens with 16% absorbed more solution; ethanol showed lower values of solubility; For Ru, water and an acetone are differed in all concentrations and periods, the same for the concentration 0 and 16%. In the chemical tests DC was not altered by aging. The mapping in the sample with 16% of water showed that near to the pore the DC is smaller and a quantity of HEMA is larger; far from the pore this relation is inverse. However, after aging solutions, the DC near the pore became similar to the far from pore. Through HPLC was possible observed that release more components of the sample with 0% than 10% and 16%. The mechanical tests showed that the acetone damage more samples than water. For an RF and ME the specimens 0% were more affected than 10% and 16% after 2 and 84 days. For a RC after 2 days the sample with 16% was more affected than 0 and 10%, however, after 84 days the specimen with 0% was more affected by aging. It can be seen that the amount of water and the type of aging affect the adhesive properties of the database systems based on the 45/55% HEMA / BisGMA composition.

Submitted by TAMIRIS DA COSTA NEVES POSSETTI null (tamipcn@yahoo.com.br) on 2017-04-27T19:29:01Z No. of bitstreams: 1 DISSERTAÇÃO MESTRADO TAMÍRIS - REPOSITÓRIO UNESP.pdf: 2125002 bytes, checksum: 3813c634d79cc97db4ee8148198ce8e7 (MD5) / Approved for entry into archive by Luiz Galeffi (luizgaleffi@gmail.com) on 2017-05-03T14:50:15Z (GMT) No. of bitstreams: 1 possetti_tcn_me_arafo.pdf: 2125002 bytes, checksum: 3813c634d79cc97db4ee8148198ce8e7 (MD5) / Made available in DSpace on 2017-05-03T14:50:15Z (GMT). No. of bitstreams: 1 possetti_tcn_me_arafo.pdf: 2125002 bytes, checksum: 3813c634d79cc97db4ee8148198ce8e7 (MD5) Previous issue date: 2017-01-13 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo deste trabalho foi avaliar a resistência de união imediata, de sistemas adesivos autocondicionantes, frente a diferentes tratamentos da superfície dentinária hipermineralizada artificialmente. Incisivos bovinos hígidos (N=80) foram preparados, incluídos em resina acrílica, hipermineralizados artificialmente e aleatoriamente distribuídos em dois grupos, de acordo com o sistema adesivo autocondicionante utilizado: Universal (3M ESPE; n=40); Optibond All in One (Kerr; n=40). Para cada sistema adesivo foram realizados cinco diferentes protocolos: (T1) sistema adesivo segundo recomendações do fabricante (n=8); (T2) ácido fosfórico 37% por 15” + sistema adesivo (n=8); (T3) laser Er,Cr:YSGG (Waterlaser Millenium, Biolaser Technology, San Clement, CA, USA) + sistema adesivo (n=8); (T4) ácido fosfórico 37% por 15” + laser Er,Cr:Y5GG + sistema adesivo (n=8); (T5) laser Er,Cr:YSGG + ácido fosfórico 37% por 15” + sistema adesivo (n=8). Após os procedimentos adesivos e restauradores, os dentes permaneceram em ambiente úmido, a 37ºC, por 24 horas, para posteriormente passarem pelo ensaio de microcisalhamento. Os resultados de resistência de união foram obtidos em MPa e submetidos à Análise de Variância e Teste de Tukey ao nível de significância de 5%. O padrão de fratura de cada espécime foi avaliado e observou-se um padrão de fratura predominantemente adesivo. Os resultados mostraram que, para o sistema adesivo Optibond All in One, o maior valor de resistência de união foi obtido no grupo T1, sendo que apenas o grupo T3 foi considerado estatisticamente semelhante à este. O menor valor de resistência de união para este material ocorreu em T5. Para o sistema adesivo Universal, todos os tratamentos foram estatisticamente semelhantes a T1, com exceção do grupo T2, que apresentou a menor média de resistência de união. / This study aims to evaluate the immediate bond strength of self-etching adhesive systems after different treatments of the artificially hypermineralized dentin. Bovine healthy incisors (n=80) were prepared, embedded in acrylic resin and randomly distributed into two groups according to the time of adhesive systems used: Group A - Universal (3M ESPE, n=40) and Group B - Optibond All in One (Kerr, n=40). For each adhesive system, five different protocols were performed: (T1) adhesive system according to the recommendations of the manufacturer (n=8); (T2) phosphoric acid conditioning 37 % for 15" + adhesive system (n=8); (T3) laser Er,Cr:YSGG (Waterlaser Millenium, Biolaser Technology, San Clemente, CA, USA) + adhesive system (n=8); (4) phosphoric acid conditioning 37% for 15" + laser Er,Cr:Y5GG + adhesive system (n=8); (T5) laser Er,Cr:YSGG + phosphoric acid conditioning 37% for 15" + adhesive system (n=8). After the bonding procedures and composite insertion, the specimens were maintained in a humid environment at 37ºC for 24 hours, and then submitted to the microshear bond strength test. The bond strength results were obtained in MPa and submitted to Variance Analysis and Tukey's Test at a significance level of 5%. The fracture pattern of each specimen was evaluated. The pattern fracture of each specimen was evaluated and a predominantly adhesive pattern was observed. The results showed that, for the Optibond All in One adhesive system, the highest union resistance value was obtained in the T1 group, and only the T3 group was considered statistically similar to this. The lowest union resistance value for this material occurred at T5 group. For the Universal adhesive system, all treatments were statistically similar to T1, except for group T2, which presented the lowest union resistance average.

Orientador: Lourdes Aparecida Martins dos Santos-Pinto / Banca: Vanderlei Salvador Bagnato / Banca: Cristina Kurachi / Banca: Fábio César Braga de Abreu e Lima / Banca: Antonio Carlos Pizzolitto / Doutor

Orientador: José Roberto Rodrigues / Resumo: Dentes bovinos são amplamente utilizados substituindo dentes humanos em pesquisas in vitro, para avaliar o comportamento dos materiais odontológicos. Utilizaram-se sessenta dentes bovinos e sessenta humanos. Esmalte e dentina foram avaliados individualmente em Análises Termodiferencial, Termogravimétrica e Condutividade Térmica. A Dissolução foi avaliada em diferentes tempos e concentrações de ácido. No teste de Desidratação os fragmentos foram colocados em estufa por tempos diferentes. Na Incorporação de Água, após a retirada dos fragmentos da estufa, foram resfriados e depois imersos em água destilada. Verificou-se o quanto o tecido incorporou de água em sua massa. A Penetrabilidade de Corante foi avaliada pela Espectroscopia de Fluorescência. Para avaliar a Microdureza Vickers os dentes foram incluídos em resina de poliéster e polidos até expor esmalte ou dentina. No termodiferencial as dentinas comportaram-se semelhantemente. O esmalte bovino absorveu mais energia, indicando mudanças estruturais e apresentando comportamento estável a partir de 450ºC, enquanto que o humano continuou instável. No Termogravimétrico a dentina humana foi duas vezes mais susceptível à perda de massa. Os esmaltes apresentaram Condutividades Térmicas semelhantes. A dentina humana foi mais condutora do que a bovina. Na Dissolução a perda de massa foi mais lenta no dente humano. Na Desidratação o esmalte bovino perdeu aproximadamente 25% e o humano perdeu 2,5%. No esmalte humano houve menor Penetrabilidade de Corante, porém semelhante nas dentinas. Assim, não se deve extrapolar resultados para dente humano em relação à incorporação de água, à penetrabilidade de corante, à dissolução e ao comportamento térmico. / Abstract: Bovine teeth are widely required in substitution of human teeth in in vitro researches to evaluate the behavior of dental materials. Sixth human teeth and sixth bovine teeth were used. Enamel and dentin were individually evaluated under Differential Thermal Analysis, Thermogravimetry and Thermal Conductivity. The dissolution was evaluated for different periods of time and different concentrations of acid. In the dehydration test, the fragments were placed inside a stove for different periods of time. In sorption of water, after the fragments were removed from stove, cooled and immersed in distilled water. It was weighted how much water mass the tissues absorbed. The dyeing penetrability was evaluated under Fluorescence Spectroscopy. To evaluate Vickers Micro hardness, the teeth were placed in polyester resin and polished until enamel or dentin was exposed. In the Differential Thermal the dentin behaved similarly. The bovine enamel absorbed more energy, showing structural changes and reaching stability for temperatures up to 450ºC, while human teeth remained unstable. In the Thermogravimetry, the human dentin was two times more susceptible to mass loss. Both enamels presented similar thermal conductivity. Human dentin presented better conductivity than bovine. In the dissolution, mass loss was slower for human teeth. In the dehydration, bovine enamel lost approximately 25 % while human lost 2.5%. There was smaller dyeing penetrability for human enamel however similar in dentins. Therefore, the results for human teeth may not be extrapolated when related to water absorbing, dyeing penetrability, dissolution and thermal behavior. / Mestre

Orientador: Sérgio Eduardo de Paiva Gonçalves / Banca: Rebeca Di Nicoló / Banca: Marta Solange Rampani Duarte / Resumo: A adesão continua a ser um desafio na Odontologia, principalmente em tecidos morfologicamente distintos e valendo-se de sistemas adesivos de mecanismos de ação também distintos. O objetivo deste estudo in vitro foi comparar a resistência adesiva de dois sistemas (autocondicionante e convencional) em dois substratos (esmalte e dentina), associados ou não à tecnologia laser (Nd:YAG). Foram utilizados 120 dentes bovinos, recém-extraídos, embutidos, que tiveram a superfície de esmalte ou dentina exposta por meio de lixas. Uma área de 3mm de diâmetro na região cérvico-vestibular-mediana foi selecionada para adesão, de acordo com os seguintes grupos: a) G1: AF/ esmalte (adesivo autocondicionante em esmalte seguindo especificação do fabricante); b) G2: AF/ dentina (adesivo autocondicionante em dentina seguindo especificação do fabricante); c) G3: AL/ esmalte (adesivo autocondicionante em esmalte + laser Nd:YAG + fotopolimerização); d) G4: AL/ dentina (adesivo autocondicionante em dentina + laser Nd:YAG + fotopolimerização); e) G5: CF/ esmalte (condicionamento ácido + adesivo convencional em esmalte); f) G6: CF/ dentina (condicionamento ácido + adesivo convencional em dentina); g) G7: CL/ esmalte (condicionamento ácido + adesivo convencional em esmalte + laser Nd:YAG + fotopolimerização); h) G8: CL/ dentina (condicionamento ácido + adesivo convencional em dentina + laser Nd:YAG + fotopolimerização). A resina composta Z 250 foi inserida com auxílio de matriz de teflon e fotopolimerizada com luz halógena, seguida da realização do teste de cisalhamento em máquina universal Emic, com carga de100kgf e velocidade de 0,5mm/min. Os valores médios em MPa obtidos para os diferentes grupos foram: G1 (20,291), G2 (14,142), G3 (23,615), G4 (22,235), G5 (20,899), G6 (11,291), G7 (22,102), G8 (15,980). Após aplicação do teste de ANOVA e Tukey 5%, concluiu-se que... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Bonding continues to be a challenge in Dentistry, particularly in morphologically different tissues, and adhesive systems with different action mechanisms are also valid. The aim of this study was to compare the bond strength of two systems (self-etching and conventional) to two substrates (enamel and dentin) either associated with laser technology (Nd:YAG) or not. One hundred and twenty (120) recently extracted, embedded bovine teeth were used, and abrasive papers were used to expose the enamel or dentin surfaces. An area of 3mm in diameter in the cervical-vestibular-median region was selected for bonding, according to the following groups: a) G1: AF/ enamel (self-etching adhesive to enamel in accordance with the manufacturer's specification); b) G2: AF/ dentin (self-etching adhesive to dentin in accordance with the manufacturer's specification); c) G3: AF/ enamel (self-etching adhesive to enamel + laser Nd:YAG + light polymerization ; d) G4: AL/ dentin (self-etching adhesive to dentin + laser Nd:YAG + light polymerization ; e) G5: CF/ enamel (acid etching + conventional adhesive to enamel); f) G6: CF/ dentin (acid etching + conventional adhesive to dentin); g) G7: CL/ enamel (acid etching + conventional adhesive to enamel + laser Nd:YAG + light polymerization ; h) G8: CL/ dentin (acid etching + conventional adhesive to dentin + laser Nd:YAG + light polymerization). Resin composite Z250 was inserted with the aid of a Teflon matrix and light polymerized, followed by the shear test in an EMIC universal machine, with a load of 100 Kgf and speed of 0.5 mm/min. The mean values obtained in Mpa for the different groups were: G1 (20.291), G2 (14.142), G3 (23.615), G4 (22.235), G5 (20.899), G6 (11.291), G7 (22.102), G8 (15.980). After applying the ANOVA and Tukey tests 5%, it was concluded that the application of laser Nd:YAG significantly increased the bond strength under all the experimental... (Complete abstract click electronic access below) / Mestre