Spelling suggestions: "subject:"electron bem freeform fabrication""
1 |
Mechanical Properties of Inconel 718 Processed Using Electron Beam Free Form Fabrication (EBF<sup>3</sup>)Waters, Brent R. 01 March 2018 (has links)
Electron beam freeform fabrication (EBF3) is a rapid metal deposition process that works efficiently with the wieldable alloy Inconel 718 (IN 718). EBF3 is a developing additive manufacturing (AM) process that can manufacture IN 718 parts directly from computer aided design (CAD) data. EBF3 can produce parts significantly faster and more energy efficient than competing IN 718 AM technologies. The EBF3 process utilizes metal wire feedstock which is induced into a molten pool using a focused electron beam in a vacuum environment. This allows parts to be built layer by layer, creating intricate shapes that can be produced cheaper and faster than traditionally manufactured IN 718 parts. Furthermore, it allows traditionally manufactured parts to be modified as additional form is added to them using EBF3. Multiple industries rely on IN 718 parts and can utilize this technology including aerospace engineering, oil refinery, nuclear power generation, and food processing.A main drawback of EBF3 is the lack of knowledge of the effect different EBF3 build techniques will have on the properties of the deposited materials. Most of the reliable data on the mechanical properties relate to a linear build-up strategy and focus on the mechanical properties in the deposition direction (DD). There is no data related to other build-up techniques such as rotation build-up or transitional builds from forged material to EBF3 material. Reliable data on the behavior and microstructure of EBF3 material in a direction other than the DD is also difficult to find. Previous studies showed build-up height influenced mechanical properties but its role is not fully understood yet. This paper presents the mechanical properties and microstructure of an IN 718 plate built using a EBF3 rotational build-up strategy through utilizing a forged plug in the center. The tensile properties of samples at the transition from forged to EBF3 material showed higher ductility and reduced strength than pure EBF3 material. This is likely due the influence of the forge material in one half of the specimen. Samples taken at approximately 15 degree increments from 0 to 90 degrees rotation to the DD in the additive portion of the plate were subjected to tensile testing. Along the build height, or the transverse direction (TD), the lowest strength was demonstrated and the TD aligned strongly to a <001> texture. Samples 45 degrees to the DD showed the greatest strength due to their preference for aligning to a <111> texture. Samples low on the build height demonstrated a higher strength than those on the top and displayed grain structures along the TD which were long, linear, and narrow across multiple deposition layers.
|
2 |
Combined Compression and Shear Structural Evaluation of Stiffened Panels Fabricated Using Electron Beam Freeform FabricationNelson, Erik Walter 30 July 2008 (has links)
Unitized aircraft structures have the potential to be more efficient than current aircraft structures. The Electron Beam Freeform Fabrication (EBF3) process can be used to manufacture unitized aircraft structures. The structural efficiency of blade stiffened panels made with EBF3 was compared to panels made by integrally machining from thick plate. The panels were tested under two load cases in a combined compression-shear load test fixture. One load case tested the panels' responses to a higher compressive load than the shear load. The second load case tested the panels' responses to an equal compressive and shear load. Finite element analysis was performed to compare with the experimental results. The EBF3 panels failed at a 18.5% lower buckling load than the machined panels when loaded mostly in compression but at an almost two times higher buckling load than the machined panels when the shear matched the compressive load. The finite element analysis was in good agreement with the experimental results prior to buckling. The results demonstrate that the EBF3 process has the capabilities of manufacturing stiffened panels that behave similarly to machined panels prior to buckling. Once the EBF3 panels buckled, the buckled shape of the EBF3 panels was different from the machined panels, generally buckling in the opposite direction of what was observed with the machined panels. This was also expected based on the finite element analysis. The different post-buckling response between the two manufacturing techniques was attributed to the residual stress and associated distortion induced during the EBF3 manufacturing process. / Master of Science
|
3 |
Additive Manufacturing of Maraging 250 Steels for the Rejuvenation and Repurposing of Die Casting ToolingKottman, Michael Andrew 09 February 2015 (has links)
No description available.
|
Page generated in 5.459 seconds