Emission regulations for heavy-duty diesel engines are becoming increasingly restrictive to limit the environmental impacts of exhaust gases and particles. Increasing the specific power output of diesel engines would improve fuel efficiency and greatly reduce emissions, but these changes could lead to increased exhaust gas temperature, increasing demands on the exhaust manifold material. This is currently the ferritic ductile cast iron alloy SiMo51, containing about 4 wt% Si and ~1 wt% Mo, which operates close to its fatigue and oxidation resistance limits at peak temperature (750C). To ensure high durability at higher temperatures, three different approaches to improving the life of exhaust manifolds were developed in this thesis. The first approach was to modify SiMo51 by adding different combinations of Cr and Ni to improve its high-temperature strength and oxidation resistance, or by applying a thermal barrier coating (TBC) to reduce the material temperature and thereby improve fatigue life. In the second approach, new materials for engine components, e.g. austenitic ductile iron and cast stainless steel, were investigated for their high-temperature fatigue and oxidation properties. In order to identify the most suitable alloys for this application, in the third the environmental effects of the corrosive diesel exhaust gas on the fatigue life of SiMo51 were investigated. The high-temperature oxidation resistance of SiMo51 at 700 and 800C in air was found to be improved by adding Cr, whereas Ni showed adverse effects. The effects of solid-solution hardening from Ni and precipitation hardening from Cr were low at 700C, with improvements only at lower temperatures. Applying a TBC system, providing thermal protection from a ceramic topcoat and oxidation protection from a metallic bond coat, resulted in only small reductions in material temperature, but according to finite element calculations still effectively improved the fatigue life of a turbo manifold. Possible alternative materials to SiMo51 identified were austenitic cast ductile iron Ni-resistant D5S and austenitic cast stainless steel HK30, which provided high durability of exhaust manifolds up to 800 and 900C, respectively. Corrosion fatigue testing of SiMo51 at 700C in diesel exhaust gas demonstrated that the corrosive gas reduced fatigue life by 30-50% compared with air and by 60-75% compared with an inert environment. The reduced fatigue life was associated with a mechanism whereby the crack tip oxidized, followed by crack growth. Thus another potential benefit of TBC systems is that the bond coat may reduce oxidation interactions and further improve fatigue life. These results can be used for selecting materials for exhaust applications. They also reveal many new research questions for future studies. Combining the different approaches of alloy modification, new material testing and improving the performance using coatings widened the scope of how component life in exhaust manifolds can be improved. Moreover, the findings on environmental interactions on SiMo51 fatigue provide a completely new understanding of these processes in ductile irons, important knowledge when designing components exposed to corrosive environments. The novel facility developed for high-temperature corrosion fatigue testing can be useful to other researchers working in this field. / <p>QC 20150507</p>

Due to coming emission legislations, the temperature is expected to increase in heavy-duty diesel engines, specifically in the hot-end of the exhaust system affecting components, such as exhaust- and turbo manifolds. Since the current material in the turbo manifold, a ductile cast iron named SiMo51, is operating close to its limits there is a need for material development in order to maintain a high durability of these components. When designing for increased life, many material properties need to be considered, for example, creep-, corrosion- and fatigue resistance. Among these, the present work focuses on the latter two up to 800°C improving the current material by additions of Cr, for corrosion resistance, and Ni, for mechanical properties. The results show improved high-temperature corrosion resistance in air from 0.5 and 1wt% Cr additions resulting in improved barrier layer at the oxide/metal interface. However, during oxidation in exhaust-gases, which is a much more demanding environment compared to air, such improvement could not be observed. Addition of 1wt% Ni was found to increase the fatigue life up to 250°C, resulting from solution strengthening of the ferritic matrix. However, Ni was also found to increase the oxidation rates, as no continuous SiO2-barrier layers were formed in the presence of Ni. Since none of the tested alloys showed improved material properties in exhaust gases at high temperature, it is suggested that the way of improving performance of exhaust manifolds is to move towards austenitic ductile cast irons or cast stainless steels. One alloy showing good high-temperature oxidation properties in exhaust atmospheres is an austenitic cast stainless steel named HK30. This alloy formed adherent oxide scales during oxidation at 900°C in gas mixtures of 5%O2-10%H2O-85%N2 and 5%CO2-10%H2O-85%N2 and in air. In the two latter atmospheres, compact scales of (Cr, Mn)-spinel and Cr2O3 were formed whereas in the atmosphere containing 5%O2 and 10%H2O, the scales were more porous due to increased Fe-oxide formation. Despite the formation of a protective, i.e. compact and adherent, oxide scale on HK30, exposure to exhaust-gas condensate showed a detrimental effect in form of oxide spallation and metal release. Thus, proving the importance of taking exhaust-gas condensation, which may occur during cold-start or upon cooling of the engine, into account when selecting a new material for exhaust manifolds. / <p>QC 20130508</p>

Reducing the heat losses in heavy-duty diesel engines is of importance for improving engine efficiency and reducing CO2 emissions. Depositing thermal barrier coatings (TBCs) onto engine components has been demonstrated to have great potential to reduce heat loss from the combustion chamber as well as from exhaust components. The overall aim of this thesis is to evaluate the thermal cycling lifetime and thermal insulation properties of TBCs for the purpose of reducing heat losses and thermal fatigue in heavy-duty diesel engines. In the thermal cycling test inside exhaust manifolds, nanostructured yttria-stabilized zirconia (YSZ) performed best, followed by YSZ with conventional microstructure and then La2Zr2O7. Forsterite and mullite could not withstand the thermal cycling conditions and displayed large cracks or spallation. Two sol-gel composite coatings displayed promising thermal cycling performance results in a furnace test under similar conditions. Thermal cycling testing of YSZ coatings having different types of microstructure, in a furnace at temperatures up to 800°C, indicated that the type of microstructure exerted a great influence. For the atmospheric plasma sprayed coatings, a segmented microstructure resulted in the longest thermal cycling lifetime. An even longer lifetime was seen for a plasma spray–physical vapour deposition (PS-PVD) coating. In situ heat flux measurements inside the combustion chamber indicated that plasma-sprayed Gd2Zr2O7 was the TBC material providing the largest heat flux reduction. This is explained by a combination of low thermal conductivity and high reflectance. The plasma-sprayed YSZ and La2Zr2O7 coatings provided very small heat flux reductions. Long-term testing indicated a running-in behaviour of YSZ and Gd2Zr2O7, with a reduction in heat flux due to the growth of microcracks in YSZ and the growth of macrocracks in Gd2Zr2O7. / <p>QC 20170821</p>