Purpose: To compare the in-vitro shear bond strengths of a new paste-paste formulation of resin-modified glass-ionomer cement (Rm-GIC) to an exising powder-liquid formulation. The study will test the hypothesis that the new paste-paste formulation of Rm-GIC (Fuji-Cem ™, GC Corp, Tokyo, Japan) has the same bond strength as an existing popular powder-liquid formulation of Rm-GIC (Rely-X ™ Luting Cement, 3M, St. Paul, MN)Materials and Methods: A total of 33 human molars were sectioned parallel to the occlusal surface to expose mid-coronal dentin and mounted parallel to the bond shearing device on the universal testing machine (Instron). For Group I samples (Rely-X, n=15), the powder and liquid were measured and adjusted to achieve a ratio of 1.6 and mixed for 30 seconds as recommended by the manufacturer. For Group II (Fuji-Cem, n=18), the paste-paste was expressed from the paste-dispenser provided by the manufacturer and mixed for 10 seconds as recommended. After testing, the teeth from group II were bonded on a different site with the same material but mixed for 20 seconds (n=18). To ensure a uniform flow and bond surface area, the mixed cement was syringed into a cylindrical mould (diameter 2.38mm, height 2mm) and allowed to set under constant force. All samples were subjected to fracture by shear loading on a universal testing machine (Instron) at a uniform crosshead speed of .02" per minute and expressed as MPa. Values were analyzed at the pResults: Wilcoxon rank sums test showed significantly higher shear bond strength values for Rely-X compared to Fuji-Cem mixed both at 10 seconds and 20 seconds. Mixing for 20 seconds resulted in stronger bonds for Fuji-Cem compared to 10 seconds, but was still significantly lower than Rely-X.Conclusions: Within the limitations of the study, the Rely-X powder-liquid formula shows a significantly stronger dentin shear bond strength when compared to the new paste-paste formula of resin-modified glass ionomer cement, Fuji-Cem.

Orientador: Angela Cristina Cilense Zuanon / Resumo: O cimento de ionômero de vidro (CIV) é um material amplamente utilizado na odontopediatria uma vez que possui, entre outras características, capacidade de liberação de íons flúor. Sua associação aos vidros bioativos (VB) pode favorecer ainda mais a remineralização da lesão de cárie, porém, pouco se sabe sobre a sua influência nas propriedades físicas, mecânicas e microbiológicas do material. O objetivo deste estudo foi avaliar a associação de um CIV convencional com VB 45S5 ou F18 em duas diferentes porcentagens (5 e 10%) em relação a porosidade (n=10) por meio da avaliação do número e área ocupada por poros, a microdureza Vickers (n=10), utilizando microdurômetro digital, a rugosidade superficial (n=10), com auxílio de rugosímetro, a resistência à compressão (n=10) medida em máquina de ensaios mecânicos (EMIC) e a atividade antibiofilme (n=10), por contagem de unidades formadoras de colônia (UFC) após 1,7, 14 e 21 dias de incubação. Para obtenção de dados de molhabilidade, realizou-se medidas de ângulos de contato (n=4). Análise de superfície em espectroscopia de raios x por dispersão em energia (EDX) (n=1) também foi realizada. Os dados obtidos foram analisados estatisticamente quanto à normalidade e a homogeneidade. Uma vez que houve aderência à curva normal, foi realizad o teste paramétrico de análise de variância (ANOVA) seguida pelo teste de Tukey. Todos os testes foram realizados com nível de significância de 5%. Pô... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract:The glass ionomer cement (GIC) is a widely used material in dentistry. It has, among other features, fluoride ion release capacity. Its association with bioactive glasses (BG) can further promote remineralization of carious lesions. However, their influence on physical, mechanical and microbiological properties of the material needs to be study. Therefore, the aim of this study was to evaluate the association of a conventional GIC to BG 45S5 or F18 in 2 different concentrations (5 or 10%) in relation to porosity (n=10) by means of the evaluation of the pore number and pore area, Vickers microhardness (n=10), using a digital microdurometer, the surface roughness (n=10), using a rugosimeter, compressive strength (n=10) measured in universal testing machine (UTM) and the antibiofilm activity (n=10), for colony forming units (CFU) counts after 1, 7, 14 and 21 days of incubation. To obtain wettability data, measurements of contact angle (n=10) were performed. Surface analysis in energy-dispersive x-ray spectroscopy (EDS) (n=1) were also performed. The data obtained were statistically analyzed for normality and homogeneity. Once the normal curve was adhered, a parametric test of analysis of variance (ANOVA) was performed, followed by the Tukey test. All tests were performed at a significance level of 5%. It was observed that the addition of 10% of BG 45S5 or F18 to the conventional GIC increased its surface roughness, the area occupied by the pores and decreased its compressive strength when compared to the control group or to the one with 5% of BG. There was no difference in microhardness. Microbiological evaluation showed difference at 14 days, when the groups that received addition of BG had the worst results. It can be observed that the concentration of 5% did not bring damages to the studied properties. Thus, this work points strongly to the fact that 5% 45S5 or F18 BG can be studied in search of ...[Complete abstract electronic access below) / Doutor

O objetivo deste estudo foi avaliar o desgaste à abrasão decorrente da escovação simulada de cimentos de ionômero de vidro sonificados, por análise da alteração de massa e da textura superficial. Os materiais avaliados foram: Fuji II LC (GC América), Resiglass (Biodinâmica), Vitro Fil LC (DFL), Fuji IX (GC América), Ketac Molar (3M ESPE), Vitro Molar (DFL), Bioglass (Biodinâmica), Vitro Fil (DFL), que foram manipulados conforme instruções do fabricante, constituindo-se no grupo controle, e um grupo submetido ao ultra-som EMS FT-081 DN Mini PIEZON (EMS, Nyon, Geneva, Switzerland), constituindo-se no grupo experimental. Os corpos-deprova foram confeccionados em uma matriz de dente bovino, com um orifício central com dimensões de 5mm de diâmetro e 3mm de espessura. Foram confeccionados 10 corpos-de-prova para cada material e cada grupo (experimental e controle). O teste de simulação da escovação foi realizado numa máquina automática para simulação de escovação (M.N. São Carlos - Brasil). A alteração de massa foi verificada pela diferença entre a massa inicial (antes da escovação) e final (após a escovação), em balança de precisão (cap. 210g, sens. 0,0001g mod. Mark 210A LICiT-Bel/Proc. Italian), com precisão de quatro casas decimais. A análise da rugosidade superficial em Ra foi determinada pela diferença entre as médias de cinco leituras, iniciais e finais, com um rugosímetro Hommel Tester T1000 (Hommelwerke, GmbH, Alte Tuttinger Strebe 20. D-7730 VS-Schwenningen). Os resultados obtidos foram submetidos à análise de ANOVA a dois critérios e Tukey (p<0,05). Quanto à perda de massa não houve diferença estatisticamente significante em relação à aplicação do ultra-som (p=0,403). No entanto, houve diferença estatisticamente significante para os diferentes Ionômeros estudados, onde p<0,001, mais precisamente do Resiglass e do Vitro Molar com os demais materiais. No que se refere à alteração de rugosidade houve diferença estatisticamente significante para a condição utilização ou não do ultra-som (p=0,043), mas não para os diferentes materiais estudados, onde p=0,264. A excitação ultra-sônica durante a presa inicial piora a rugosidade de superfície e não apresenta nenhuma influência na perda de peso. / The purpose of this work was to evaluate abrasion resistance, by means of weight loss, and surface roughness (SR) of GIC, using ultrasonic excitation as a command set. The materials tested were Fuji II LC and Fuji IX (GC Corporation), Ketac Molar (3M ESPE), Resiglass and Bioglass (Biodinâmica), Vitro Fil LC, Vitro Molar and Vitro Fil (DFL). Twenty specimens of each GIC brand were evaluated, being half submitted to ultrasound (US) (Piezon - EMS, Switzerland). The materials were placed in bovine tooth matrix (5mm inner diameter and 3mm of thickness). Initial weight was carried out by means of a digital balance (210A LICiT/Italian). The initial SR was quantitatively assessed by measuring the surface roughness using Hommel Tester T1000 (Hommelwerke, Germany) determined by the average of 5 random measurements in each sample. The specimens were submitted to brushing abrasion test. Weight loss and surface roughness, for each specimen were calculated based on the difference between the initial and final weight and surface roughness means, respectively. Weight loss (g) varied between 0,0001 and 0,0090 with US and 0,0001 and 0,0123 without US. Surface roughness (µm) varied between 0,0770 and 0,4330 with US and -0,0270 and 0,3520 without US. The results, analyzed by two way ANOVA and Tukey\'s test (p<0,05), presented statistically significant difference in the surface roughness when the GIC was submitted or not to US (p=0,043) while no statistical difference was observed among the GIC brands (p=0,264). The weight loss presented statistically significant difference between the tested GIC brands (p<0,010), while no influence on the weight loss by the use of US was observed (p=0,403). Ultrasonic excitation during initial cure does not improve surface roughness of GIC, and does not present any influence on weight loss.

Com o objetivo de se avaliar a relação entre o tempo de fotopolimerização e a alteração dimensional dos cimentos de ionômero de vidro modificados por resina foram analisadas três marcas comerciais deste material: Vitremer (3M/ESPE), Fuji II LC (GC International) e Vitro Fil LC (DFL). Foram confeccionados 60 espécimes no total, sendo 20 para cada marca comercial. Cada corpo-de-prova foi confeccionado em forma de disco, com dimensões de 5mm de diâmetro e 2mm de espessura, com auxílio de uma matriz de PTFE (politetrafluoretileno) vazada no centro, com as dimensões já especificadas. Após a manipulação e inserção do material dentro da cavidade da matriz, e cobertura desta com lâmina de vidro de cada lado, o conjunto foi colocado, durante 15 minutos, dentro de uma caixa de papelão hermeticamente fechada, o que impediu a entrada de luz em seu interior. Dos 20 espécimes confeccionados de cada marca comercial, quatro grupos (n=5) foram formados, variando-se a forma de polimerização com o aparelho de luz halógena Demetron (Dabi-Atlante). O grupo 1 foi fotopolimerizado por 20s, o grupo 2 por 40s, o grupo 3 por 60s, e o grupo 4 não sofreu o processo de fotopolimerização (grupo controle). Cada espécime foi armazenado em um frasco plástico, com 10ml de água destilada, em uma estufa, com temperatura interna de 37ºC. As alterações dimensionais das amostras foram avaliadas nos intervalos de 24 horas, 7 dias e 30 dias de armazenamento. Para o cálculo das alterações volumétricas foi utilizada uma equação física, baseada no princípio hidrostático de Arquimedes, na qual eram obtidas as massas dos espécimes dentro da água e fora dela. Para isso foi utilizada uma balança analítica (AT 261 Delta Range/Mettler Toledo) com aparato de especificação de densidade. As médias dos resultados, em porcentagem da alteração volumétrica, foram submetidas à análise de variância a três critérios seguido pelo teste de Tukey para a averiguação da significância entre os grupos (a=0,05). Os resultados demonstraram que todos os materiais se expandiram após 30 dias. O Vitremer sofreu o menor grau de expansão quando não fotopolimerizado, no entanto, o tempo de fotopolimerização não influenciou o grau de alteração volumétrica, com exceção do Fuji II LC, cuja expansão foi maior após 60s de fotoativação. O Vitro Fil LC teve o volume diminuído entre 7 e 30 dias. Concluiu-se que o tempo de fotopolimerização pode afetar a alteração de volume do cimento de ionômero de vidro modificado por resina, porém não é o único fator relacionado a isto. / This study evaluated the effect of photoativation and storage on the hygroscopic expansion of resin modified glass ionomers (Vitremer-3M/ESPE, Fuji II LC-GC Int., Vitro Fil LC-DFL). . Twenty specimens, 5 +/- 1mm in diameter and 2mm in thickness, were made of each material in a mold of PTFE, . The RMGIC were manipulated according to the manufacturers instructions and inserted into a mold under two glass microscope slides and kept in a darkness box for 15 minutes. Then, the samples were distributed into four groups (n=5): light-cured for 20s, light-cured for 40s, light-cured for 60s and not light-cured (control group). Each sample was storage in distilled water at 37ºC. The measurements of volumetric changes were made in three different times of storage: 24 hours, 7 days and 30 days. Volumetric changes were determined using Archimedes principle, which change in buoyancy of a material in a fluid depends on the volume changes of the material. Measurements were made by an analytic balance with density apparatus (AT 261 Delta Range/Mettler Toledo). Means and standard deviations values were analyzed by three-way analysis of variance and Tukey\'s test to compare significance between the groups (a=0,05). All materials underwent volumetric expansion after 30 days. Vitremer showed the less expansion when no light-cured. The time of light-cure did not influence the volumetric change, except for Fuji II LC, that showed great expansion when activated for 60s. Vitro Fil LC showed some degree of shrinkage after 7 days. This study concluded that photocuring can influence the volumetric change of resin modified glass ionomer cement.

Este estudo objetivou avaliar quantitativamente e qualitativamente a resistência adesiva de três diferentes tipos de cimentos de ionômero de vidro (CIV) por meio dos ensaios mecânicos de microtração e microcisalhamento. Quarenta superfícies planas de dentina foram divididas aleatoriamente em dois grupos, segundo o ensaio mecânico: microtração (n=24) e microcisalhamento (n=16). Posteriormente, cada grupo foi novamente dividido em quatro subgrupos, segundo o material restaurador utilizado: CIV de alta viscosidade (Ketac Molar Aplicap - 3M/ESPE), CIV modificado por resina (Fuji II LC encapsulado - CG Corporation), nano-ionômero (Ketac N100 - 3M/ESPE) e resina composta (Z100 - 3M/ESPE). Para o teste de microtração os dentes foram seccionados perpendicularmente a interface de união obtendo-se espécimes com área de superfície aderida de aproximadamente 1mm2. Para o teste de microcisalhamento foram confeccionados três cilindros de material restaurador em cada superfície de dentina. Todos os grupos foram armazenados em água destilada por 24h. Os ensaios foram realizados em Mini Instron a velocidade de 1mm/min. Os valores obtidos, expressos em MPa, foram submetidos à Análise de Variância (p<0,05) e o método de comparações múltiplas LSD. Foi encontrada diferença estatisticamente significante entre testes e entre materiais, demonstrando que o comportamento dos valores de resistência adesiva dos quatro tipos de materiais estudados depende do tipo de ensaio mecânico utilizado. A análise qualitativa dos padrões de fratura em lupa estereoscópica revelou fraturas predominantemente adesivas e mistas quando da utilização do microcisalhamento para todos os materiais estudados, enquanto para a microtração, observou-se um grande número de fraturas coesivas em material para o Ketac Molar e para o Fuji II LC. Os valores de resistência adesiva do Ketac Molar e do Fuji II LC são semelhantes aos encontrados à resina Z100, quando o teste utilizado foi o microcisalhamento. Com o teste de microtração houve diferença entre os grupos, sendo que Ketac Molar se comportou de maneira semelhante a N100 que foram estatisticamente inferiores a Fuji II LC, que por sua vez também foi inferior a Z100. Com base nesses resultados conclui-se que o ensaio mecânico de microcisalhamento foi o que melhor avaliou a resistência adesiva dos materiais ionoméricos. / The present study aim to quantitatively and qualitatively evaluate the adhesive resistance of three types of Glass Ionomer Cements (GIC) through microtensile and microshear tests. Forty flat dentine surfaces were randomly divided between the two types of mechanical test: microtensile (n=24) and microshear (n=16). Furthermore, each group was divided into four subgroups, according the material used: High Viscosity GIC (Ketac Molar Aplicap - 3M/ESPE), Resin Modified GIC (Fuji II LC encapsulated - CG Corporation), nano-ionomer (Ketac N100 - 3M/ESPE) and composite resin (Z100 -3M/ESPE) resin. For the microtensile test, the teeth were sectioned perpendicularly to the adhesive interface so 1mm2 surface specimens could be obtained. For the microshare test three cylinder shaped restorative material were produced per each dentine surface. All groups were stored in distillated water for 24h. All tests were performed with a Mini Instron machine at a crosshead speed of 1mm/min. The results obtained, expressed in MPa, were submitted to variance - ANOVA (p<0,05) and least significant differences (LSD) analysis. Test and materials were statistically different, indicating that the values for adhesive resistance obtained per material depend on the test used. The qualitative analysis of the fractures, carried out by light microscope at 40x magnification, revealed that fracture produced by the microshear test were mainly adhesives or mixed. Microtensile fractures were mainly cohesive within the material for Ketac Molar and for Fuji II LC. According to the microshear test, the adhesive resistance figures found for Ketac Molar and for Fuji II LC were similar to the ones found in Z100 resin. Nevertheless, the microtensile test demonstrated that there was difference between the groups, as Ketac Molar behaved in line with N100, which were statistically inferior to Fuji II LC that was poorer than Z100. The conclusion, base on these results, was that the microshear was the mechanical test that better evaluated the adhesive resistance of the studied ionomer-based materials.

O objetivo deste estudo foi avaliar a rugosidade superficial (&micro;m) e microdureza Vickers (VH) de materiais restauradores temporários: cimento Biodentine&trade; (M1) e o cimento de ionômero de vidro - Fuji IX (M2) submetidos a diferentes enxaguatórios bucais. Foram confeccionados 54 corpos de prova (cps) por meio de uma matriz de teflon (6mm x 2mm), distribuídos aleatoriamente em 6 grupos de acordo com a solução utilizada: água destilada (S1), enxaguatório com álcool - Listerine Cool Mint (S2) e enxaguatório sem álcool - Colgate Plax (S3). Todos os cps foram mantidos em umidade relativa de 100%, em estufa 37±1°C durante todo o experimento, exceto nos períodos de imersão nos enxaguatórios estabelecidos. Os cps foram colocados individualmente em um frasco contendo 8mL do enxaguatório específico para cada grupo, durante 2 minutos, sob vibração, duas vezes ao dia, por um período de 21 dias. As leituras foram realizdas por meio do microdurômetro e rugosímetro nos tempos de 48 horas (T0), 7 dias (T1), 14 dias (T2) e 21 dias (T3). Os dados obtidos foram agrupados em tabelas e submetidos aos testes estatísticos de normalidade, Kolmogorov-Smirnov, Shapiro-Wilk, Anova e Teste de Tukey por meio do Programa Estatístico Assistat Versão 7.7 beta (2016). Resultados: Verificou-se que os fatores Tempo (T), Solução (S) e Material (M) isoladamente e a interação TxM e SxM tiveram efeito estatisticamente significante na rugosidade superficial. Isoladamente, T3 (0,92±0,02) e M1 (0,87±0,01) apresentaram maior média de rugosidade e S3 (0,72±0,02) a menor média de rugosidade. Nas interações MxT e SXM, respectivamente o M1T3 (1,10±0,03) e M1S1 (1,03±0,03) apresentaram maiores médias de rugosidade. Para a microdureza o fator Material isoladamente, e a interação TxS, TxM e SxM tiveram efeito estatisticamente significante. O M1 (61,2±0,87) apresentou maior microdureza, que M2 (54,4±0,87). Para a interação TxS, a condição S2T2 (54,09±2,61) apresentou menor média de microdureza. Para a interação TxM, o M1 comparado com M2 determinou maior microdureza nos tempos T0, T1 e T2. E para a interação SxM, M1S1 (61,59±1,51) e M1S2 (62,86±1,51) apresentaram maior microdureza que M2S1 (51,53±1,51) e M2S2 (54,34±1,51). De acordo com a metodologia pode-se concluir que: a) o M1 apresentou maior rugosidade superficial nos tempos T1, T2 e T3 e maior microdureza nos tempos T0, T1, e T2 do que o M2 b) O material M1 apresentou maior microdureza independente das soluções. / The aim of this study was to evaluate the surface roughness (&micro;m) and Vickers microhardness of provisory restorative materials: BiodentineTM (M1) and Fuji IX - glass ionomer cement (M2) were submitted to different mouthwashes. Fifty-four specimens were prepared using a Teflon mold (6mm x 2mm), randomly distributed into 6 groups according to the solution used: distilled water (S1), mouthwash containing alcohol -Listerine Cool Mint (S2) and alcohol-free mouthwash - Colgate Plax (S3). During the experiment, all specimens were carried out at a relative humidity of 100% in an oven at 37±1°C, except in the soaking periods in the established mouthwashes. The samples were individually placed in a flask containing 8mL of the specific mouthwash for each group for 1 minute, under vibration twice a day for a period of 21 days. The readings of the variables were carried out at the time of 48 hours (T0), 7 days (T1), 14 days (T2) and 21 days (T3). The obtained data were grouped in tables and submitted to the Normality Tests for Statistical Analysis Kolmogorov-Smirnov, Shapiro-Wilk, Anova and Tukey\'s Test provided by the Statistical software Assistat Program Version 7.7 beta (2016). Results: It was found that there was a significant effect on surface roughness when considered alone Time (T), Solution (S), Material (M) and the interaction between TxM and SxM. On the other hand, T3 (0.92±0.02) and M1 (0.87±0.01) presented the higher roughness and S3 (0.72±0.02) the lowest average roughness. For the interactions MxT and SxM, M1T3 (1,10±0,03) and M1S1 (1,03±0,03) presented higher roughness averages. To microhardness analysis, the material as a alone factor and the interaction TxS, TxM and SxM had a statistically significant effect. M1 (61.2±0.87) presented a higher microhardness than the M2 (54.4±0.87). For the TxS interaction, S2T2 (54.09 ± 2.61) had a lower microhardness average. To TxM interaction, the M1 compared to M2 determined a higher microhardness at T0, T1 and T2. In interaction SxM, M1S1 (61.59±1.51) and M1S2 (62.8 ±1.51) had a higher microhardness than M2S1 (51.53±1.51) and M2S2 (54.3 ±1,51). According to the methodology, it can be concluded that: a) M1 presented greater surface roughnes at T1, T2 and T3 and higher microhardness at T0, T1, and T2 than M2 b) M1 presented a higher microhardness than M2 for S1 and S2.

Por ser comum a existência de lesão de mancha branca em superfícies proximais adjacentes à lesões de cárie já cavitadas, este estudo teve como objetivo investigar o efeito terapêutico de materiais que liberam flúor sobre lesões com as quais estejam em contato proximal, in vitro (I) e in situ (II). Para o estudo I, 130 blocos de esmalte obtidos de caninos decíduos passaram pelo processo de indução de lesão de cárie por ciclagem de pH, durante 10 dias. As medições do conteúdo mineral foram realizadas por meio da análise de fluorescência induzida pela luz (QLF e VistaProof), no momento inicial (esmalte hígido) e após a formação das lesões de mancha branca. Dez espécimes foram recolhidos e seccionados transversalmente, no centro da lesão, para análise de dureza transversal (Shimadzu Micro Hardness tester, 25g, 15s). Posteriormente, blocos cilíndricos foram preparados com 6 diferentes materiais restauradores (n=20): resina composta (Z350®), cimento de ionômero de vidro (CIV) de alta viscosidade (Ketac Molar® e Riva Self Cure®), CIV modificado por resina (Vitremer®), CIV modificado por resina nanoparticulado (Ketac Nano®) e resinas compostas modificadas por poliácidos (Dyract Extra®). Cada bloco de esmalte foi unido a um bloco de material, de modo que a face da lesão e a do material simulassem o ponto de contato existente em uma restauração ocluso-proximal. Estes conjuntos sofreram então novo desafio cariogênico (ciclagem de pH) durante 7 (n=10) ou 14 dias (n=10). Após o desafio, os 120 espécimes foram recolhidos e novamente analisados com relação à fluorescência induzida. Em seguida, foram seccionados transversalmente no centro da lesão para que fosse feita a análise de dureza transversal. Para o estudo II, os espécimes foram preparados de maneira semelhante ao estudo I, porém, para a etapa do desafio cariogênico (após o contato com os materiais restauradores), os 120 espécimes foram inseridos em dispositivos intra-orais. Dez voluntários utilizaram os dispositivos em duas fases (7 e 14 dias), com intervalo de 1 semana entre elas. Os voluntários gotejaram solução de sacarose 20%, 8 vezes/dia e utilizaram dentifrício fluoretado (1.450 ppm) 3 vezes/dia durante o estudo. Ao final de ambos os estudos, todos os espécimes foram recolhidos e analisados com relação ao conteúdo mineral pelos métodos de fluorescência induzida e pelo teste de microdureza transversal. Para análise de normalidade e homogeneidade dos dados obtidos foram utilizados os testes de Anderson-Darling e Levene, respectivamente. Para o estudo I, ANOVA de dois fatores com teste complementar de Tukey não demonstrou diferença entre os valores obtidos com o QLF para os diferentes grupos e tempos após desafio (=0,05). Para os valores de dureza, no entanto, o mesmo teste confirmou que há menor perda mineral para as lesões em contato com o CIV de alta viscosidade, quando comparado com a resina composta e com o resinas compostas modificadas por poliácidos. Após 14 dias de desafio, o CIV de alta viscosidade mostra-se superior também aos CIVs modificados por resina e compômer. Para o estudo II, análise de multinível demonstrou haver maior perda para aquelas lesões em contato com a resina composta e o resinas compostas modificadas por poliácidos, para os valores obtidos com o QLF, enquanto que para os valores de dureza o mesmo teste demonstra que os CIVs de alta viscosidade desempenham melhor performance comparado a todos os outros grupos de materiais, independente do tempo de desafio. Os valores obtidos com o equipamento Vista Proof não diferiram estatisticamente com relação aos grupos ou períodos experimentais, em ambos os estudos, de acordo com os testes de Mann-Whitney e Kruskal-Wallis (=0,05). Embora diferentes materiais liberadores de flúor possam reduzir a progressão de lesões de cárie quando em contato proximal, o CIV de alta viscosidade mostra-se com uma melhor opção para este fim. / This study investigated the possibility of caries lesions arrest when in approximal contact with fluoride-releasing restorative materials, in vitro (I) and in situ (II). White-spot lesions were initially formed in 130 primary enamel specimens via a pH cycling regimen during 10 days. Light-induced fluorescence images (QLF and Vista Proof) were made of each enamel slab at the beginning and after the lesions induction to assess the mineral loss/gain of the artificial caries lesions. Ten specimens were collected and transversally cut for microhardness analysis. The rest of them were put in contact with cylindrical blocks of 6 different materials (n=20): composite resin (Z350®), high viscous glass ionomer (GIC) (Ketac Molar® and Riva Self Cure®), resin-modified GIC (Vitremer®), resin- modified nano-ionomer (Ketac Nano®) and compomer (Dyract Extra®). These settings were designed to simulate the contact point between the restoration and the approximal lesion. For the study I, they were subjected to a new cariogenic challenge (pH cycling) for 7 (n=10) or 14 days (n=10). For the study II, the specimens were prepared in a similar manner and a randomized double-blind in situ design was conducted in two phases (7/14 days) for the subsequent cariogenic challenge. Ten volunteers wore palatal devices containing 6 specimens (caries lesion + restorative). The volunteers used fluoride dentifrice 3x/day and a 20% sucrose solution was dripped onto the slabs 8x /day. At the end of both studies, specimens were collected for mineral analysis by fluorescence methods and traversal microhardnes. Distribution of data and equality of variances were determined using KolmogorovSmirnov and Levene tests. Two-way ANOVA demonstrated no differences for values obtained with QLF for the study I (=0.05). The same test demonstrated lower mineral loss for specimens in contact with high viscous GIC for the CSMH analysis. After 14 days, high viscous GIC were even superior to resin-modified GIC or compomer. For the study II, multilevel analysis demonstrated higher mineral loss for the specimens in contact with composite resin and compomer for values obtained with QLF (=0.05). The CSMH analysis demonstrated that high viscous GIC had the best performance when compared to all other materials, regardless the duration of challenge. For both studies, Mann-Whitney and Kruskal-Wallis demonstrated no differences for values obtained with VistaProof (=0.05). In conclusion, high viscous GIC can arrest enamel lesion when in approximal contact with them, although other fluoride-releasing materials can moderately prevent enamel loss.

Orientador: Cristiane Duque / Coorientador: Alberto Carlos Botazzo Delbem / Banca: Denise Pedrini / Banca: Thiago Cruvinel da Silva / Resumo: O objetivo deste estudo foi avaliar a influência da incorporação de nanopartículas de trimetrafosfato de sódio (TMP) e clorexidina (CHX) nas propriedades microbiológicas, físico-mecânicas e na capacidade de redução da desmineralização de um cimento de ionômero de vidro modificado por resina (CIV) indicado para restauração. Inicialmente, foram determinados nove grupos de estudo: 1) CIV; 2) CIV + CHX 1,25%; 3) CIV + CHX 2,5%; 4) CIV + TMP 7%; 5) CIV+ CHX 1,25% + TMP 7%; 6) CIV + CHX 2,5% + TMP 7%; 7) CIV+ TMP 14%; 8) CIV + CHX 1,25% + TMP 14%; 9) CIV + CHX 2,5% + TMP 14%. Para determinar a atividade antimicrobiana desses CIV contendo ou não TMP e CHX foi realizado o teste de difusão em ágar com Streptococcus mutans, Lactobacillus acidophilus, Actinomyces israelii e Candida albicans. Após 24h, os halos de inibição obtidos pelos CIV foram mensurados com o auxílio de um paquímetro digital. Corpos-de-prova dos CIV foram confeccionados utilizando matrizes específicas e avaliadas as seguintes propriedades físico-mecânicas para cada grupo de materiais do estudo: resistência à compressão e à tração diametral e dureza de superfície, além de determinar a liberação total de fluoreto (F) e de TMP. Foram preparados 80 blocos a partir de incisivos bovinos e selecionados pelo teste de dureza de superfície do esmalte (DS1). Os corpos-de-prova dos CIV foram adaptados aos blocos de esmalte recém-preparados e submetidos às ciclagens de pH. A seguir, foi analisada a dureza de superfície final do esmalte (DS2) para o cálculo da porcentagem da perda de dureza de superfície (%PDS) e verificar a capacidade do material em reduzir a desmineralização. Os dados foram submetidos aos testes de ANOVA e Bonferroni ou Student-Newman-Keuls, considerando p≤0,05. Os resultados mostraram que a adição... / Abstract: The aim of this study was to evaluate the influence of the association of sodium trimetaphosphate nanoparticles (TMP) and chlorhexidine (CHX) on the microbiological, physical-mechanical and enamel demineralization reduction of glass ionomer cement (GIC). Initially, nine groups of the study were defined: 1) control - GIC Fuji LII; 2) GIC+ 1.25% CHX; 3) GIC + 2.5% CHX; 4) GIC + 7%TMP; 5) GIC+ 1.25% CHX + 7%TMP; 6) GIC + 2.5% CHX + 7%TMP; 7) GIC+ 14%TMP; 8) GIC + 1.25% CHX + 14%TMP; 9) GIC+ 2.5% CHX + 14% TMP. The antimicrobial activity of GIC containing or not CHX/TMP was determined by agar diffusion test against Streptococcus mutans, Lactobacillus acidophilus, Actinomyces israelii and Candida albicans. After 24h, the inhibition zones obtained by the GIC were measured with a digital caliper. GIC specimens were prepared using specific stainless steel molds in order to evaluate the following physical-mechanical properties for each material group: compressive and diametral tensile strength and superficial hardness, besides to determine total fluoride and TMP release. Eighty enamel blocks were prepared from extracted bovine incisors and selected through the initial surface hardness test (SH1). GIC specimens were adjusted to the enamel blocks and submitted to pH-cyclings. After that, final superficial hardness (SH2) was determined in order to obtain the percentage of superficial hardness loss (%SHL) and observe the capacity of the materials in reducing enamel demineralization. Data were submitted to ANOVA and Bonferroni or Student-Newman-Keuls statistical tests, considering p≤0.05. The results showed that the addition of chlorhexidine increased the antimicrobial activity of GIC for all groups. The physical-mechanical properties of GIC, especially compressive strength, were jeopardized by the association... / Mestre

Made available in DSpace on 2017-07-24T19:22:28Z (GMT). No. of bitstreams: 1 Vania Aparecida Oliveira Queiroz.pdf: 2334313 bytes, checksum: edfd28d0622cb45ff6c0fde23b982588 (MD5) Previous issue date: 2012-12-06 / Evaluate an alternative sequence for the sandwich technique using the microtensile bond strength testing on glass-ionomer cement (GIC)-dentin and GICcomposite resin (CR) interfaces (in 7 days), and to analyze the mechanical properties (hardness and modulus of elasticity) of GIC-RC interface (in 7 days and 24 months), by the use of nano-indentation. Methods: For that, class I cavities were cut into 60 extracted human molars. The cavities were filled using two diferent sequences of closed sandwich technique with conventional glass-ionomer cement (CGIC) (KetacTM Fil Plus/3M), and resin-modified glass-ionomer cement (RMGIC) (VitrebondTM/3M).The sequences were called, convencional sequence (CS) (etching GICs surface) and alternative sequence (AS) (without etching GICs surface), and they were used in all groups RMGIC-CR, RMGIC-dentin, CGIC-CR, and CGIC-dentin. After storage period, the teeth were horizontally sectioned, along vestibular wall of the class I cavities, for the bond strength of GICs-dentin tests. For analysis of the mechanical properties and bond strength of GICs-CR, the teeth were longitudinally sectioned.The specimens intended for mechanical properties testing have been removed from the sandwich restorations center areas. For the adhesion tests, the beams were aligned, and attached to a jig employing the active gripping method and stressed in tension (MPa). For the mechanical test, the specimens were embedded, and polished, and submitted to nano-indentation (GPa). The data were analyzed by Kruskal-Wallis, Dunn, and Chi-square tests (p<0.05). Results: The GICRM presented better adhesion to dentin and CR, and the CGIC presented better mechanical properties. When was used the RMGIC, both sequences did not present differences in adhesion (dentin and CR), and in mechanical properties (RMGIC,interface, and CR) in 7 days and 24 months. Concerning CGIC-dentin and CGIC-CR,also did not find a significant difference between both sequences, despite the adhesion means difference CGIC-CR between the CS (0.96 MPa) and AS (5.78 MPa). The CS presented a significant number of spontaneously debonded beams at interface with the CR before testing (77.33%) than AS (16%). The mechanical properties analysis of CGIC-interface-CR, in 7 days and 24 months, showed significant differences between techniques. At seven days, no GICC-RC interface data was obtained due to deteriorating condition, while AS showed 0.42 GPa (hardness) and 7.50 GPa (modulus of elasticity) values. After 24 months, AS showed hardness and modulus of elasticity, respectively, 1.24 e 20.96 GPa (CGIC), and 0.40 e 7.05 GPa (interface), while CS showed 0.51 e 8.14 GPa (CGIC) without any interface value. Conclusion: The AS has performed a good option for laminate or sandwich technique when RMGIC was used, and it was the best option when a CGIC was used. / Avaliar uma sequência alternativa para a técnica do sanduíche pela análise da resistência adesiva por microtração nas interfaces cimento de ionômero de vidro (CIV)-dentina e CIV-resina composta (RC) (aos 7 dias) e pela análise das propriedades mecânicas (dureza e módulo de elasticidade) por nanoendentação na interface CIV-RC (aos 7 dias e 24 meses). Material e métodos: Para isto, foram preparadas cavidades de classe I em 60 molares humanos extraídos. As cavidades foram restauradas utilizando duas sequências técnicas diferentes para o sanduíche fechado: com cimento de ionômero de vidro convencional (CIVC) (KetacTM Fil Plus/3M) e com cimento de ionômero de vidro modificado por resina (CIVMR) (VitrebondTM/3M). As técnicas foram denominadas, sequência convencional (SC) (com condicionamento superficial do CIV) e sequência alternativa (SA) (sem condicionamento superficial do CIV), e empregadas em todos os grupos de CIVMRRC, CIVMR-dentina, CIVC-RC e CIVC-dentina. Após períodos de armazenamento, os dentes foram seccionados horizontalmente, ao longo da parede vestibular do preparo de classe I, para o teste de resistência adesiva CIV-dentina. Para análise das propriedades mecânicas e para o teste de resistência adesiva CIV-RC, os dentes foram seccionados longitudinalmente. Os espécimes destinados às análises das propriedades mecânicas foram retirados do centro das restaurações de sanduíche. Para o teste de resistência adesiva, os palitos foram alinhados e colados ao dispositivo da máquina de tração pelo método de fixação ativo e estressados em tensão (MPa). Para análise das propriedades mecânicas, os espécimes foram fixados com parafina no suporte de teste, polidos e submetidos a nanoendentação (GPa). Os testes Kruskal-Wallis, Dunn e Qui-Quadrado foram utilizados para análise dos dados (p<0,05). Resultados: O CIVMR demonstrou maior adesão, à dentina e à RC, e o CIVC demonstrou melhores propriedades mecânicas. Quando foi utilizado o CIVMR, as duas sequências técnicas estudadas não apresentaram diferenças na resistência adesiva (à dentina e à RC) e nas propriedades mecânicas, aos 7 dias e 24 meses. Quanto à resistência adesiva CIVC-dentina e CIVC-RC, também não houve diferenças significantes entre as sequências estudadas, apesar da diferença de médias de adesão CIVC-RC entre a SC (0,96 MPa) e SA (5,78 MPa). A SC também apresentou significante maior número de palitos deslocados espontaneamente na interface com a RC antes do teste (77,33%) que a SA (16%). A análise das propriedades mecânicas, aos 7 dias e 24 meses, demonstrou diferenças significantes entre as técnicas. Aos 7 dias, não foi possível obter valores na interface CIVC-RC na SC devido ao grau de deterioração existente enquanto a SA apresentou valores 0,42 GPa (dureza) e 7,50 GPa (módulo de elasticidade). Após 24 meses, a SA apresentou valores de dureza e módulo de elasticidade, respectivamente, 1,24 e 20,96 GPa (CIVC), e 0,40 e 7,05 GPa (interface), enquanto a SC apresentou 0,51 e 8,14 GPa (CIVC) e nenhum valor para interface.Conclusão: A SA apresentou-se como boa opção para a técnica laminada ou do sanduíche quando foi utilizado o CIVMR, e como a melhor opção quando foi utilizado o CIVC.

Orientador: André Luiz Fraga Briso / Coorientador: Paulo Henrique dos Santos / Banca: Ticiane Cestari Fagundes Tozzi / Banca: Anderson Catelan / Resumo: O objetivo neste estudo foi avaliar o efeito da contaminação do tecido dentinário e dos métodos normalmente empregados na limpeza do substrato sobre a resistência de união obtida na interface cimento de ionômero de vidro modificado por resina (CIVMR)/dentina. Para tanto, os 168 dentes bovinos foram desgastados até o tecido dentinário divididos em doze grupos (n=14), de acordo com o agente contaminante e a técnica de limpeza, sendo: NN - sem contaminação (N) e sem limpeza do substrato (N); NA - sem contaminação (N) e limpeza com spray ar/água (A); NP - sem contaminação (N) e limpeza com ácido poliacrílico 26% (P); SaN - contaminação por saliva (Sa) e sem limpeza do substrato (N); SaA - contaminação por saliva (Sa) e limpeza do substrato com spray ar/água (A); SaP - contaminação por saliva (Sa) e limpeza do substrato com ácido poliacrílico 26% (P); SgN - contaminação por sangue (Sg) e sem limpeza do substrato (N); SgA - contaminação por sangue (Sg) e limpeza do substrato com spray ar/água (A); SgP - contaminação por sangue (Sg) e limpeza do substrato com ácido poliacrílico 26% (P); HN - contaminação por agente hemostático (H) e sem limpeza do substrato (N); HA - contaminação por agente hemostático (H) e limpeza do substrato com spray ar/água (A); HP - contaminação por agente hemostático (H) e limpeza do substrato com ácido poliacrílico 26% (P). Todos os espécimes foram restaurados com o material ionomérico encapsulado Riva Light Cure (SDI) e, posteriormente foram obtidos palito... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The objective of this study was to evaluate the effect of the contamination of the dentin tissue and the methods normally employed in the cleaning of the substrate on the bond strength obtained at the resin modified glass ionomer cement (RMGIC) / dentin interface. For this purpose, 168 bovine teeth were selected, which were worn to dentin tissue, and were then divided into twelve groups (n = 14), according to the contaminating agent and the cleaning technique: NN - without contamination (N) and without substrate cleaning (N); NW - no contamination (N) and spray / water cleaning (W); NP - without contamination (N) and cleaning with 26% polyacrylic acid (P); SaN - contamination by saliva (Sa) and without substrate cleaning (N); SaW - saliva contamination (Sa) and spray / water substrate cleaning (W); SaP - saliva contamination (Sa) and substrate cleaning with 26% polyacrylic acid (P); BN - blood contamination (B) and no substrate cleaning (N); BW - blood contamination (B) and cleaning the substrate with spray / water (W); BP - blood contamination (B) and substrate cleaning with 26% polyacrylic acid (P); HN - contamination by hemostatic agent (H) and without cleaning of the substrate (N); HW - hemostatic agent contamination (H) and spray / water substrate cleaning (W); HP - hemostatic agent contamination (H) and substrate cleaning with 26% polyacrylic acid (P). All specimens were restored with the Riva Light Cure (SDI) encapsulated ionomeric material and, afterwards, sticks of a... (Complete abstract click electronic access below) / Mestre