Avaliação da microinfiltração marginal em cavidades classe II de molares decíduos restauradas com diferentes cimentos de ionômero de vidro / Evaluation of marginal microleakage in class II cavities of primary molars restored with different glass ionomer cementsMarlus Roberto Rodrigues Cajazeira 26 February 2008 (has links)
O objetivo desta pesquisa foi avaliar a microinfiltração em restaurações classe II realizadas com diferentes cimentos de ionômero de vidros em molares decíduos. Para tal, foram selecionados quarenta molares decíduos humanos a partir de um Banco de Dentes. Nas faces mesial e distal de cada dente foram preparadas cavidades classe II com dimensões padronizadas. Em seguida, os dentes foram divididos em oito grupos experimentais correspondentes ao material restaurador utilizado: grupo MXR (Maxxion R); grupo VDR (Vidrion R); grupo VTR (Vitremer); grupo VTF (Vitro Fill LC); grupo FUJ (Fuji IX); grupo KTM (Ketac Molar); grupo VMO (Vitro Molar); grupo MGS (Magic Glass ART). Ao término de vinte e quatro horas de imersão em água destilada, os dentes foram mantidos em solução de nitrato de prata a 50% pelo mesmo período e, então, em solução reveladora de radiografias (hidroquinona, Kodak) por quinze minutos. Os dentes foram então seccionados através do centro das restaurações, e observados em lupa estereoscópica sob o aumento de quarenta vezes. A microinfiltração foi graduada co base em escores relacionados à penetração do nitrato de prata na interface adesiva. Os resultados, após submetidos à análise estatística, demonstraram que nenhum dos materiais testados impediu completamente a microinfiltração. No entanto, o Vitremer apresentou os escores mais baixos, seguido do Ketac Molar e do Fuji IX. Os materiais Magic Glass ART, Vitro Molar, Vitro Fill LC e Vidrion R apresentaram comportamento intermediário em relação aos demais, enquanto o Maxxion R apresentou os piores resultados. Com base na metodologia empregada e nos resultados obtidos, pode-se concluir que nenhum dos materiais testados foi capaz de impedir completamente a microinfiltração, apesar de apresentarem graus varáveis de suscetibilidade a esse fenômeno, destacando-se, entre eles o Vitremer, o Ketac Molar e o Fuji IX por apresentarem baixos níveis de microinfiltração, seguidos do Magic Glass ART, Vitro Molar, Vitro Fill LC e Vidrion R. Em contrapartida, o Maxxion R apresentou os piores resultados, fato constatado pelos altos escores de microinfiltração registrados. / The aim of this study was to evaluate the microleakage in class II glass ionomer cement restorations in primary molars. For this, were selected fourty primary molars in a human teeth bank. At mesial and distal surfaces of the teeth were prepared standard class II cavities. In sequence, the teeth were subdivided in eight experimental groups in according with the restorative material used: group MXR (Maxxion R); group VDR (Vidrion R); group VTR (Vitremer); group VTF (Vitro Fill LC); group FUJ (Fuji IX); group KTM (Ketac Molar); group VMO (Vitro Molar); group MGS (Magic Glass ART). After past twently four hours in immersing water, the restored teeth were immersed in a 50% solution of silver nitrate for similar period, and, then, in radiographic solution (hydroquinone, Kodak) for fiteen minutes. The teeth were sectioned at the center of restorations, and observed at stereoscope under forty-fold increase. The microleakage was graduated in scores related with the grade of silver nitrate penetration at the adhesive interface. The results, after submitted statistical analysis, showed that none of the materials impeded completely the microleakage. Thus, Vitremer showed the minor scores, followed by Ketac Molar and Fuji IX. The materials, Magic Glass ART, Vitro Molar, Vitro Fill LC and Vidrion R showed intermediary results, while Maxxion R showed the worse ones. Based in methodology used in this study and in their results, its possible concluded that none of the materials was able to impede the microleakage, although presented variable grades susceptibility of this phenomenom, with emphasis to Vitremer, Ketac Molar and Fuji IX because presented minor microleakage, following Magic Glass ART, Vitro Molar, Vitro Fill LC and Vidrion R. On the other hand, Maxxion R presented the worse results, fact confirmed by high microleakage scores observed.
|
52 |
Estudo da resistência adesiva de cimentos de ionômero de vidro à dentina: microtração x microcisalhamento / Bond stregth of glass-ionomer cements to dentin: microtensile x microshearClarissa Calil Bonifacio 29 October 2008 (has links)
Este estudo objetivou avaliar quantitativamente e qualitativamente a resistência adesiva de três diferentes tipos de cimentos de ionômero de vidro (CIV) por meio dos ensaios mecânicos de microtração e microcisalhamento. Quarenta superfícies planas de dentina foram divididas aleatoriamente em dois grupos, segundo o ensaio mecânico: microtração (n=24) e microcisalhamento (n=16). Posteriormente, cada grupo foi novamente dividido em quatro subgrupos, segundo o material restaurador utilizado: CIV de alta viscosidade (Ketac Molar Aplicap - 3M/ESPE), CIV modificado por resina (Fuji II LC encapsulado - CG Corporation), nano-ionômero (Ketac N100 - 3M/ESPE) e resina composta (Z100 - 3M/ESPE). Para o teste de microtração os dentes foram seccionados perpendicularmente a interface de união obtendo-se espécimes com área de superfície aderida de aproximadamente 1mm2. Para o teste de microcisalhamento foram confeccionados três cilindros de material restaurador em cada superfície de dentina. Todos os grupos foram armazenados em água destilada por 24h. Os ensaios foram realizados em Mini Instron a velocidade de 1mm/min. Os valores obtidos, expressos em MPa, foram submetidos à Análise de Variância (p<0,05) e o método de comparações múltiplas LSD. Foi encontrada diferença estatisticamente significante entre testes e entre materiais, demonstrando que o comportamento dos valores de resistência adesiva dos quatro tipos de materiais estudados depende do tipo de ensaio mecânico utilizado. A análise qualitativa dos padrões de fratura em lupa estereoscópica revelou fraturas predominantemente adesivas e mistas quando da utilização do microcisalhamento para todos os materiais estudados, enquanto para a microtração, observou-se um grande número de fraturas coesivas em material para o Ketac Molar e para o Fuji II LC. Os valores de resistência adesiva do Ketac Molar e do Fuji II LC são semelhantes aos encontrados à resina Z100, quando o teste utilizado foi o microcisalhamento. Com o teste de microtração houve diferença entre os grupos, sendo que Ketac Molar se comportou de maneira semelhante a N100 que foram estatisticamente inferiores a Fuji II LC, que por sua vez também foi inferior a Z100. Com base nesses resultados conclui-se que o ensaio mecânico de microcisalhamento foi o que melhor avaliou a resistência adesiva dos materiais ionoméricos. / The present study aim to quantitatively and qualitatively evaluate the adhesive resistance of three types of Glass Ionomer Cements (GIC) through microtensile and microshear tests. Forty flat dentine surfaces were randomly divided between the two types of mechanical test: microtensile (n=24) and microshear (n=16). Furthermore, each group was divided into four subgroups, according the material used: High Viscosity GIC (Ketac Molar Aplicap - 3M/ESPE), Resin Modified GIC (Fuji II LC encapsulated - CG Corporation), nano-ionomer (Ketac N100 - 3M/ESPE) and composite resin (Z100 -3M/ESPE) resin. For the microtensile test, the teeth were sectioned perpendicularly to the adhesive interface so 1mm2 surface specimens could be obtained. For the microshare test three cylinder shaped restorative material were produced per each dentine surface. All groups were stored in distillated water for 24h. All tests were performed with a Mini Instron machine at a crosshead speed of 1mm/min. The results obtained, expressed in MPa, were submitted to variance - ANOVA (p<0,05) and least significant differences (LSD) analysis. Test and materials were statistically different, indicating that the values for adhesive resistance obtained per material depend on the test used. The qualitative analysis of the fractures, carried out by light microscope at 40x magnification, revealed that fracture produced by the microshear test were mainly adhesives or mixed. Microtensile fractures were mainly cohesive within the material for Ketac Molar and for Fuji II LC. According to the microshear test, the adhesive resistance figures found for Ketac Molar and for Fuji II LC were similar to the ones found in Z100 resin. Nevertheless, the microtensile test demonstrated that there was difference between the groups, as Ketac Molar behaved in line with N100, which were statistically inferior to Fuji II LC that was poorer than Z100. The conclusion, base on these results, was that the microshear was the mechanical test that better evaluated the adhesive resistance of the studied ionomer-based materials.
|
53 |
Efeito de materiais restauradores em contato proximal com lesões de cárie em dentes decíduos / Mineral content of enamel carious lesions in approximal contact with different restorative materials in primary teethCamila de Almeida Brandão Guglielmi 02 August 2013 (has links)
Por ser comum a existência de lesão de mancha branca em superfícies proximais adjacentes à lesões de cárie já cavitadas, este estudo teve como objetivo investigar o efeito terapêutico de materiais que liberam flúor sobre lesões com as quais estejam em contato proximal, in vitro (I) e in situ (II). Para o estudo I, 130 blocos de esmalte obtidos de caninos decíduos passaram pelo processo de indução de lesão de cárie por ciclagem de pH, durante 10 dias. As medições do conteúdo mineral foram realizadas por meio da análise de fluorescência induzida pela luz (QLF e VistaProof), no momento inicial (esmalte hígido) e após a formação das lesões de mancha branca. Dez espécimes foram recolhidos e seccionados transversalmente, no centro da lesão, para análise de dureza transversal (Shimadzu Micro Hardness tester, 25g, 15s). Posteriormente, blocos cilíndricos foram preparados com 6 diferentes materiais restauradores (n=20): resina composta (Z350®), cimento de ionômero de vidro (CIV) de alta viscosidade (Ketac Molar® e Riva Self Cure®), CIV modificado por resina (Vitremer®), CIV modificado por resina nanoparticulado (Ketac Nano®) e resinas compostas modificadas por poliácidos (Dyract Extra®). Cada bloco de esmalte foi unido a um bloco de material, de modo que a face da lesão e a do material simulassem o ponto de contato existente em uma restauração ocluso-proximal. Estes conjuntos sofreram então novo desafio cariogênico (ciclagem de pH) durante 7 (n=10) ou 14 dias (n=10). Após o desafio, os 120 espécimes foram recolhidos e novamente analisados com relação à fluorescência induzida. Em seguida, foram seccionados transversalmente no centro da lesão para que fosse feita a análise de dureza transversal. Para o estudo II, os espécimes foram preparados de maneira semelhante ao estudo I, porém, para a etapa do desafio cariogênico (após o contato com os materiais restauradores), os 120 espécimes foram inseridos em dispositivos intra-orais. Dez voluntários utilizaram os dispositivos em duas fases (7 e 14 dias), com intervalo de 1 semana entre elas. Os voluntários gotejaram solução de sacarose 20%, 8 vezes/dia e utilizaram dentifrício fluoretado (1.450 ppm) 3 vezes/dia durante o estudo. Ao final de ambos os estudos, todos os espécimes foram recolhidos e analisados com relação ao conteúdo mineral pelos métodos de fluorescência induzida e pelo teste de microdureza transversal. Para análise de normalidade e homogeneidade dos dados obtidos foram utilizados os testes de Anderson-Darling e Levene, respectivamente. Para o estudo I, ANOVA de dois fatores com teste complementar de Tukey não demonstrou diferença entre os valores obtidos com o QLF para os diferentes grupos e tempos após desafio (=0,05). Para os valores de dureza, no entanto, o mesmo teste confirmou que há menor perda mineral para as lesões em contato com o CIV de alta viscosidade, quando comparado com a resina composta e com o resinas compostas modificadas por poliácidos. Após 14 dias de desafio, o CIV de alta viscosidade mostra-se superior também aos CIVs modificados por resina e compômer. Para o estudo II, análise de multinível demonstrou haver maior perda para aquelas lesões em contato com a resina composta e o resinas compostas modificadas por poliácidos, para os valores obtidos com o QLF, enquanto que para os valores de dureza o mesmo teste demonstra que os CIVs de alta viscosidade desempenham melhor performance comparado a todos os outros grupos de materiais, independente do tempo de desafio. Os valores obtidos com o equipamento Vista Proof não diferiram estatisticamente com relação aos grupos ou períodos experimentais, em ambos os estudos, de acordo com os testes de Mann-Whitney e Kruskal-Wallis (=0,05). Embora diferentes materiais liberadores de flúor possam reduzir a progressão de lesões de cárie quando em contato proximal, o CIV de alta viscosidade mostra-se com uma melhor opção para este fim. / This study investigated the possibility of caries lesions arrest when in approximal contact with fluoride-releasing restorative materials, in vitro (I) and in situ (II). White-spot lesions were initially formed in 130 primary enamel specimens via a pH cycling regimen during 10 days. Light-induced fluorescence images (QLF and Vista Proof) were made of each enamel slab at the beginning and after the lesions induction to assess the mineral loss/gain of the artificial caries lesions. Ten specimens were collected and transversally cut for microhardness analysis. The rest of them were put in contact with cylindrical blocks of 6 different materials (n=20): composite resin (Z350®), high viscous glass ionomer (GIC) (Ketac Molar® and Riva Self Cure®), resin-modified GIC (Vitremer®), resin- modified nano-ionomer (Ketac Nano®) and compomer (Dyract Extra®). These settings were designed to simulate the contact point between the restoration and the approximal lesion. For the study I, they were subjected to a new cariogenic challenge (pH cycling) for 7 (n=10) or 14 days (n=10). For the study II, the specimens were prepared in a similar manner and a randomized double-blind in situ design was conducted in two phases (7/14 days) for the subsequent cariogenic challenge. Ten volunteers wore palatal devices containing 6 specimens (caries lesion + restorative). The volunteers used fluoride dentifrice 3x/day and a 20% sucrose solution was dripped onto the slabs 8x /day. At the end of both studies, specimens were collected for mineral analysis by fluorescence methods and traversal microhardnes. Distribution of data and equality of variances were determined using KolmogorovSmirnov and Levene tests. Two-way ANOVA demonstrated no differences for values obtained with QLF for the study I (=0.05). The same test demonstrated lower mineral loss for specimens in contact with high viscous GIC for the CSMH analysis. After 14 days, high viscous GIC were even superior to resin-modified GIC or compomer. For the study II, multilevel analysis demonstrated higher mineral loss for the specimens in contact with composite resin and compomer for values obtained with QLF (=0.05). The CSMH analysis demonstrated that high viscous GIC had the best performance when compared to all other materials, regardless the duration of challenge. For both studies, Mann-Whitney and Kruskal-Wallis demonstrated no differences for values obtained with VistaProof (=0.05). In conclusion, high viscous GIC can arrest enamel lesion when in approximal contact with them, although other fluoride-releasing materials can moderately prevent enamel loss.
|
54 |
Avaliação "in vitro" da microinfiltração marginal em restaurações classe II, confeccionadas com um cimento de ionômero de vidro modificado por resina, uma resina composta "semicondensável" e uma resina composta "condensável". / In vitro evaluation of marginal microleakage in class II restorations, made with a glass ionomer cement modified through resin Vitremer, "semicondensable" composite resin Ariston pHc and "condensable" composite resin P-60.Bijella, Maria Fernanda Borro 25 August 2000 (has links)
Avaliou-se in vitro a microinfiltração marginal em restaurações classe II, realizadas com o cimento de ionômero de vidro modificado por resina Vitremer, a resina composta "semicondensável" Ariston pHc e a resina composta "condensável" P-60, com o propósito de verificar a influência da ciclagem térmica para estes materiais, como também dois métodos de análise da penetração do corante. Para tanto, 60 pré-molares, receberam cavidades classe II proximais, com a parede cervical localizada 1mm abaixo da junção cemento-esmalte. Os espécimes foram divididos em 3 grupos de 20 dentes cada. O grupo I foi restaurado com Vitremer, o grupo II com Ariston pHc e o grupo III com P-60. Após a restauração, os espécimes foram acondicionados em recipientes plásticos com água deionizada por 24 horas a 37°C. Decorrido esse período as restaurações receberam acabamento e polimento. Enquanto metade de cada grupo sofreu processo de termociclagem com 500 ciclos nas temperaturas de 5°C e 55°C, em banhos de 15 segundos cada, a outra metade permaneceu acondicionada em recipientes plásticos com água deionizada a 37°C. Após o período de teste, todos os espécimes foram imersos em solução de fucsina básica a 0,5% por 24 horas a 37°C, sendo em seguida lavados abundantemente em água corrente durante 24 horas. Para análise da microinfiltração os dentes foram incluídos em resina plástica autopolimerizável e seccionados no sentido mesio-distal, sofrendo uma média de quatro cortes cada dente. Para cada corte, foram obtidas duas imagens para serem analisadas através de um software denominado Imagetools. Os resultados foram avaliados através do teste estatístico de Análise de Variância a dois critérios (2-way ANOVA) e o teste de Tukey para comparações múltiplas entre os materiais, em nível de significância de 5%. Os resultados demonstraram que todos os grupos testados apresentaram microinfiltração marginal, sendo que o cimento de ionômero de vidro modificado por resina Vitremer apresentou resultados sempre melhores, vindo a seguir a resina composta "condensável" P-60 e por último a resina composta "semicondensável" Ariston pHc. Não houve diferença estatisticamente significante no uso ou não da termociclagem para estes materiais. Quando avaliou-se os métodos de análise de penetração do corante, o método através da máxima infiltração parece ser o melhor para detectar a extensão da microinfiltração. / It was the purpose of this work to assess in vitro marginal microleakage in class II restorations, made with a glass ionomer cement modified through resin Vitremer, "semicondensable" composite resin Ariston pHc and "condensable" composite resin P-60, pretending to verify the influence of thermocycling upon these materials, as well as of the performance of two methods for dye penetration analysis. Thus, 60 premolars received proximal class II cavities, with cervical wall situated above cement/enamel junction. The specimens were divided in three groups with 20 teeth each. Group I was restored with Vitremer, Group II with Ariston pHc and Group III with P-60. Following restoration, specimens were stored in plastic containers with deionized water for 24 hours under 37ºC. After this time period restorations were finished and polished. While half the group suffered a thermocycling process with 500 cycles under temperatures of 5ºC and 55ºC, in baths of 15 seconds each, the other half remained stored in plastic containers with deionized water under 37ºC. After testing period, all specimens have been immersed into a 0.5% basic fuchsin solution for 24 hours under 37ºC, being next thoroughly washed in running water for 24 hours. For microleakage analysis, teeth were embedded in autopolimerizing plastic resin and sectioned in a mesiodistal sense, each tooth suffering a mean of four sections. For each section two images were obtained for the analysis through a software called Imagetools. Results have been examined through a Variance Analysis statistical test through two criteria (2-way ANOVA) and Tukey test for multiple comparisons between materials, at a 5% significance level. Results showed that all tested groups presented marginal microleakage, glass ionomer cement modified with resin Vitremer always presenting the best results, followed by "condensable" composite resin P-60 and coming last "semicondensable" composite resin Ariston pHc. There was no statiscally significant difference between the use and non-use of thermocycling for these materials. When methods for dye penetration analyses were assessed the method of maximum leakage seems to be the best one for detecting microleakage extension.
|
55 |
Rugosidade superficial e microdureza de materiais restauradores provisórios submetidos a ação de enxaguatórios bucais / Surface roughness and microhardness of provisory restorative materials submitted to mouthwashesArnez, Mayara Manfrin 09 January 2017 (has links)
O objetivo deste estudo foi avaliar a rugosidade superficial (µm) e microdureza Vickers (VH) de materiais restauradores temporários: cimento Biodentine™ (M1) e o cimento de ionômero de vidro - Fuji IX (M2) submetidos a diferentes enxaguatórios bucais. Foram confeccionados 54 corpos de prova (cps) por meio de uma matriz de teflon (6mm x 2mm), distribuídos aleatoriamente em 6 grupos de acordo com a solução utilizada: água destilada (S1), enxaguatório com álcool - Listerine Cool Mint (S2) e enxaguatório sem álcool - Colgate Plax (S3). Todos os cps foram mantidos em umidade relativa de 100%, em estufa 37±1°C durante todo o experimento, exceto nos períodos de imersão nos enxaguatórios estabelecidos. Os cps foram colocados individualmente em um frasco contendo 8mL do enxaguatório específico para cada grupo, durante 2 minutos, sob vibração, duas vezes ao dia, por um período de 21 dias. As leituras foram realizdas por meio do microdurômetro e rugosímetro nos tempos de 48 horas (T0), 7 dias (T1), 14 dias (T2) e 21 dias (T3). Os dados obtidos foram agrupados em tabelas e submetidos aos testes estatísticos de normalidade, Kolmogorov-Smirnov, Shapiro-Wilk, Anova e Teste de Tukey por meio do Programa Estatístico Assistat Versão 7.7 beta (2016). Resultados: Verificou-se que os fatores Tempo (T), Solução (S) e Material (M) isoladamente e a interação TxM e SxM tiveram efeito estatisticamente significante na rugosidade superficial. Isoladamente, T3 (0,92±0,02) e M1 (0,87±0,01) apresentaram maior média de rugosidade e S3 (0,72±0,02) a menor média de rugosidade. Nas interações MxT e SXM, respectivamente o M1T3 (1,10±0,03) e M1S1 (1,03±0,03) apresentaram maiores médias de rugosidade. Para a microdureza o fator Material isoladamente, e a interação TxS, TxM e SxM tiveram efeito estatisticamente significante. O M1 (61,2±0,87) apresentou maior microdureza, que M2 (54,4±0,87). Para a interação TxS, a condição S2T2 (54,09±2,61) apresentou menor média de microdureza. Para a interação TxM, o M1 comparado com M2 determinou maior microdureza nos tempos T0, T1 e T2. E para a interação SxM, M1S1 (61,59±1,51) e M1S2 (62,86±1,51) apresentaram maior microdureza que M2S1 (51,53±1,51) e M2S2 (54,34±1,51). De acordo com a metodologia pode-se concluir que: a) o M1 apresentou maior rugosidade superficial nos tempos T1, T2 e T3 e maior microdureza nos tempos T0, T1, e T2 do que o M2 b) O material M1 apresentou maior microdureza independente das soluções. / The aim of this study was to evaluate the surface roughness (µm) and Vickers microhardness of provisory restorative materials: BiodentineTM (M1) and Fuji IX - glass ionomer cement (M2) were submitted to different mouthwashes. Fifty-four specimens were prepared using a Teflon mold (6mm x 2mm), randomly distributed into 6 groups according to the solution used: distilled water (S1), mouthwash containing alcohol -Listerine Cool Mint (S2) and alcohol-free mouthwash - Colgate Plax (S3). During the experiment, all specimens were carried out at a relative humidity of 100% in an oven at 37±1°C, except in the soaking periods in the established mouthwashes. The samples were individually placed in a flask containing 8mL of the specific mouthwash for each group for 1 minute, under vibration twice a day for a period of 21 days. The readings of the variables were carried out at the time of 48 hours (T0), 7 days (T1), 14 days (T2) and 21 days (T3). The obtained data were grouped in tables and submitted to the Normality Tests for Statistical Analysis Kolmogorov-Smirnov, Shapiro-Wilk, Anova and Tukey\'s Test provided by the Statistical software Assistat Program Version 7.7 beta (2016). Results: It was found that there was a significant effect on surface roughness when considered alone Time (T), Solution (S), Material (M) and the interaction between TxM and SxM. On the other hand, T3 (0.92±0.02) and M1 (0.87±0.01) presented the higher roughness and S3 (0.72±0.02) the lowest average roughness. For the interactions MxT and SxM, M1T3 (1,10±0,03) and M1S1 (1,03±0,03) presented higher roughness averages. To microhardness analysis, the material as a alone factor and the interaction TxS, TxM and SxM had a statistically significant effect. M1 (61.2±0.87) presented a higher microhardness than the M2 (54.4±0.87). For the TxS interaction, S2T2 (54.09 ± 2.61) had a lower microhardness average. To TxM interaction, the M1 compared to M2 determined a higher microhardness at T0, T1 and T2. In interaction SxM, M1S1 (61.59±1.51) and M1S2 (62.8 ±1.51) had a higher microhardness than M2S1 (51.53±1.51) and M2S2 (54.3 ±1,51). According to the methodology, it can be concluded that: a) M1 presented greater surface roughnes at T1, T2 and T3 and higher microhardness at T0, T1, and T2 than M2 b) M1 presented a higher microhardness than M2 for S1 and S2.
|
56 |
Investigations into the mechanical properties and curing characteristics of dental glass-ionomer cementsPrentice, Leon Hugh Unknown Date (has links) (PDF)
Conventional glass ionomer cements (GICs), which continue to gain acceptance as superbly biocompatible dental materials, were first released in the early 1970s as a result of research into combining the advantages of silicate cements and polyalkenate cements. The chemistry of GICs is based upon the aqueous reaction between an ion-leachable fluoride glass and polyacid which yields the final cross-linked insoluble ionomer (ionic polymer). The significant advantages of GICs include direct adhesion to tooth structures, fluoride release, minimal dimensional change on curing, significant ease of use and superb biocompatibility, to the extent that affected proximal tooth structures may be retained, remineralised , and strengthened against further caries. GICs have, however, been unfavourably compared with other restorative materials in their mechanical properties and setting characteristics, in particular their relative weakness, the time limitations for the acid-base reaction to proceed to acceptable maturity, and the susceptibility of the immature cement to water sorption or desiccation.
|
57 |
Arresting dentine caries lesions in Chinese preschool childrenZhi, Qinghui., 支清惠. January 2010 (has links)
published_or_final_version / Dentistry / Doctoral / Doctor of Philosophy
|
58 |
Investigations into the mechanical properties and curing characteristics of dental glass-ionomer cementsPrentice, Leon Hugh Unknown Date (has links) (PDF)
Conventional glass ionomer cements (GICs), which continue to gain acceptance as superbly biocompatible dental materials, were first released in the early 1970s as a result of research into combining the advantages of silicate cements and polyalkenate cements. The chemistry of GICs is based upon the aqueous reaction between an ion-leachable fluoride glass and polyacid which yields the final cross-linked insoluble ionomer (ionic polymer). The significant advantages of GICs include direct adhesion to tooth structures, fluoride release, minimal dimensional change on curing, significant ease of use and superb biocompatibility, to the extent that affected proximal tooth structures may be retained, remineralised , and strengthened against further caries. GICs have, however, been unfavourably compared with other restorative materials in their mechanical properties and setting characteristics, in particular their relative weakness, the time limitations for the acid-base reaction to proceed to acceptable maturity, and the susceptibility of the immature cement to water sorption or desiccation.
|
59 |
Estudo in vitro do efeito antibacteriano de cimentos de ionômero de vidro incorporados com diacetato de clorexidina / In vitro study of the antimicrobial effect of glass ionomer cements incorporated with chlorhexidine diacetateRenato Mayhé 19 February 2014 (has links)
O objetivo deste trabalho foi o de avaliar in vitro o efeito da ação antibacteriana de cimentos de ionômero de vidro (CIVs) convencionais incorporados com diacetato de clorexidina (DCHX) sobre o Streptococcus mutans. Foram testados os CIVs Maxxion R e Vitro Fil R com a incorporação dos percentuais de 0,5%, 1% e 2% de DCHX através de difusão em ágar e pela exaustão do DCHX por até 40 dias, a fim de observar a longevidade de sua ação inibitória. Foi também avaliado o efeito do fluoreto de sódio na ação antibacteriana do DCHX. Para determinar a diferença entre a média dos halos de inibição Os resultados foram analisados por análise de variância e pelo teste Student-Newman-Keuls (SNK). Todos os corpos de prova com DCHX apresentaram halo para os CIVs variando de 2,29mm a 6,82mm para o Maxxion R e de 1,73mm a 8,97mm para o Vitro Fil R. A capacidade de inibição foi proporcional à concentração de DCHX. Através do teste SNK apenas os grupos Vitro Fil R 0,5% e1% não variaram significativamente entre si. O 15o dia foi o de maior atividade antibacteriana para ambos os CIVs. Os grupos Maxxion R 1% e 2% foram os que menos apresentaram diferenças ao longo do tempo. Não houve crescimento de S mutans para os períodos de 7 e 15 dias de exaustão, sendo verificado o crescimento de colônias apenas na superfície do meio após o período de 96hs de incubação. Não foi observado efeito antagônico na capacidade antibacteriana do DCHX na presença de fluoreto de sódio. A incorporação de DCHX aos CIVs Maxxion R e Vitro Fil R, nas concentrações testadas e por um período de até 40 dias, apresentam resultados positivos no controle bacteriano de S mutans. Dentro das limitações deste estudo é lícito concluir que: efeito da inibição ao S mutans é dependente da concentração do DCHX; o fluoreto por si só não é capaz de inibir o crescimento de S mutans; a associação do DCHX com os CIVs não alterou a capacidade da ação antibacteriana da CHX; a ação antibacteriana da CHX incorporada aos CIVs se mantém eficaz por 15 dias, independente do CIV testado. / The purpose of this study was to evaluate (the in vitro the effect) of antibacterial action of conventional glass ionomer cements (GICs glass ionomer cements) incorporated with chlorhexidine diacetate (DCHX) on Streptococcus mutans. We tested the GICs Maxxion Vitro Fil R & R with the incorporation of the percentage of 0.5%, 1% and 2% DCHX by agar diffusion and the depletion of DCHX by up to 15 days to observe the longevity of its inhibitory action. It was also evaluated the effect of sodium fluoride on the antibacterial action of DCHX. To determine the difference between the mean of the inhibition zones, the results were analyzed by analysis of variance and the Student-Newman-Keuls test (SNK). All specimens presented with DCHX halo for GICs ranging from 2.29 mm to 6.82 mm for Maxxion R and 1.73 mm to 8.97 mm for the FIL Vitro R. The inhibition capacity were proportional to the concentration of DCHX. Through the SNK test only groups Vitro Fil R 0.5% e1% did not vary significantly. The 15th day was the one with highest antibacterial activity for both GICs. The R Maxxion 1% and 2% were the groups with less differences over time. No growth was observed of S. mutans for periods of 7 and 15 days of exhaustion, with observed growth of colonies only on the surface of the culture media after 96 hours of incubation period. No antagonistic effect was observed in the ability of the antibacterial DCHX in the presence of sodium fluoride. Incorporating DCHX GICs Maxxion Vitro Fil R & R, in tested concentrations and for a period up to 40 days showed a positive bacterial control of S. mutans. Despite the limitations of this study, we may conclude that: inhibition effect of S. mutans is dependent on the concentration of DCHX; fluoride alone is not able to inhibit growth of S. mutans; the association of DCHX with VSDs did not alter the capacity of the antibacterial action of CHX and the antibacterial action of CHX incorporated into GICs remains effective for 15 days, regardless of the GIC tested.
|
60 |
Resistência de união e limite de fadiga de nichos confeccionados em resina composta e cimentos à base de ionômero de vidroLopes, José Fernando Scarelli [UNESP] 17 February 2003 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:28:56Z (GMT). No. of bitstreams: 0
Previous issue date: 2003-02-17Bitstream added on 2014-06-13T18:58:07Z : No. of bitstreams: 1
lopes_jfs_me_arafo.pdf: 1497511 bytes, checksum: 5cff0da20eacc454b65a7066c2aba9f6 (MD5) / O objetivo desta investigação foi determinar a resistência de união e limite de fadiga de nichos confeccionados em resina composta e ionômeros de vidro. Setenta e cinco corpos-de-prova (incisivos mandibulares humanos hígidos) com etiquetas adesivas com perfurações de 3,5mm de diâmetro foram adaptadas sobre a superfície lingual de cada dente. Esta delimitação tinha como objetivo padronizar a área da superfície de esmalte a ser condicionada e, posteriormente, mantida em contato com os materiais restauradores. Para realização dos nichos, matrizes foram realizadas para cada corpo-de-prova onde o material restaurador foi inserido. Os corpos-de-prova foram imersos em água destilada a 37ºC por um período de 30 dias. Para os ensaios de resistência à união, a máquina de testes mecânicos MTS modelo 810 foi calibrada utilizando uma velocidade de deslocamento de 0,5mm/min. Para os testes de limite de fadiga a máquina de testes foi calibrada para submeter cada corpo-de-prova a 10.000 ciclos constantes, com uma freqüência de 5 Hz, amplitude inicial de 0,5 mm e velocidade de rampa inicial de 100N/s. Os valores originais do experimento foram convertidos de N para MPa em função da área da base do nicho (circular) previamente calculada. Os corpos-de-prova após a fratura foram avaliados através de microscopia eletrônica de varredura com aumento de 500 vezes. A médias de resistência à união e limite de fadiga foram comparadas estatisticamente usando o teste de Análise de Variância a um Critério. Nos teste de cisalhamento, a resina composta Z-100 produziu maior valor de resistência de união (12,25 MPa) ao esmalte dentário que o ionômero de vidro convencional Fuji IX (7,21MPa). Não foram observadas diferenças entre os valores do material Fuji II LC (10,29MPa) e os demais materiais. Para todos os materiais, os corpos-de-prova testados por meio de ensaio dinâmico de... / The aim of this study was to determine the bond strength and fatigue limit of rest seats prepared with composite resin and glass ionomer cements. The lingual aspect of seventy-five specimens (intact human mandibular incisors) was delimited by adhesive tags with 3.5-mm diameter perforations. This delimitation aimed at standardizing the area of enamel surface to be etched and later kept in contact with the restorative materials. For preparation of the rest seats, matrixes were obtained for each specimen on which the restorative material was placed. The specimens were immersed in distilled water at 37ºC for a period of 30 days. For the bond strength assays, the mechanical assay machine MTS model 810 was calibrated at a displacement speed of 0.5mm/min. For the fatigue limit tests, the assay machine was calibrated so as to submit each specimen to 10,000 constant cycles, at a 5-Hz frequency with an initial range of 0.5mm and initial sloping speed of 100N/s. The original values of the experiment were converted from N to MPa according to the previously calculated circular area of the base of the rest seat. After fracture, the specimens were evaluated by means of scanning electron microscopy with magnification of 500x. The means of bond strength and fatigue limits were statistically compared through the one-way variance analysis. For the shear resistance test, the composite resin Z-100 yielded a higher value of bond strength (12.25 MPa) to the dental enamel than the conventional glass ionomer cement Fuji IX (7.21MPa). No differences could be found between Fuji II LC (10.29MPa) and the further materials. For all materials, the specimens submitted to dynamic fatigue assay tests yielded lower mean values than those achieved through static shear assays. Regarding the fatigue limit values, all materials presented different behaviors, being that Fuji II LC obtained the higher mean value (6.4MPa), ...(Complete abstract, click electronic access below)
|
Page generated in 0.0728 seconds