Made available in DSpace on 2016-06-02T20:34:07Z (GMT). No. of bitstreams: 1 1950.pdf: 7192146 bytes, checksum: 68b89ea2608351b8183463ad5baf024e (MD5) Previous issue date: 2008-05-27 / Universidade Federal de Minas Gerais / Studies on the influence of the nature of the growth electrolyte on the properties of oxide films grown on the Ti-50Zr at.% alloy were carried out. The results obtained through the different measurements done (chronoamperometry, open circuit potentials, and reconstruction rates) showed that phosphate incorporation into the matrix of oxide films grown in H3PO4 make them unstable, bringing a greater dissolution compared to the ones grown in CH3SO3H, H2SO4, and HNO3. The electrochemical impedance spectroscopy measurements showed that the phosphate incorporation into the oxide films grown on the Ti-50Zr at.% alloy by different methods and thickenesses lead to high values of electrical resistance when compared with the ones of films grown in CH3SO3H, H2SO4, and HNO3. The nature of the growth electrolyte was observed to also affect the semiconducting properties of the different oxide films grown on the alloy, leading to different voltammetric profiles of these films when illuminated with radiation of energy greater than that of the band gap. The studies on the effect of the exchange of the electrolyte solution in the galvanostatic growth of anodic films in two steps showed that the breakdown potentials are dependent on the nature of the electrolyte. On the other hand, these measurements also revealed that the initial electrical breakdown of the film or the nature of the electrolyte in which it was initially grown do not alter the film growth kinetics during the second step, carried out in another electrolyte. / Foram realizados estudos da influência da natureza do eletrólito de crescimento nas propriedades de filmes de óxido crescidos sobre a liga Ti-50Zr at.%. Os resultados obtidos por meio das diferentes medidas realizadas (cronoamperometria, potencial de circuito aberto e taxas de reconstrução) mostraram que a incorporação de fosfato na matriz dos filmes de óxido crescidos em H3PO4 provoca instabilidade dos mesmos, fazendo com que haja maior dissolução em relação aos crescidos em CH3SO3H, H2SO4 e HNO3. As medidas de espectroscopia de impedância eletroquímica mostraram que a incorporação de fosfato na matriz dos filmes de óxido crescidos sobre a liga Ti- 50Zr at.% por diferentes métodos e espessuras proporciona elevados valores de resistência elétrica quando comparados com os de filmes crescidos em CH3SO3H, H2SO4 e HNO3. Foi observado que a natureza do eletrólito de crescimento afeta também as propriedades semicondutoras dos diferentes filmes de óxido crescidos sobre a liga, proporcionando diferentes perfis voltamétricos destes filmes quando iluminados com radiação de energia maior que a da banda proibida. Os estudos do efeito da troca da solução eletrolítica no crescimento por via galvanostática de filmes anódicos em duas etapas mostraram que os potenciais de ruptura são dependentes da natureza do eletrólito. Por outro lado, estas medidas também revelaram que a ruptura elétrica inicial do filme de óxido ou a natureza do eletrólito em que ele foi inicialmente crescido não alteraram a cinética de crescimento durante a segunda etapa, feita em um outro eletrólito.

Made available in DSpace on 2014-06-11T19:33:26Z (GMT). No. of bitstreams: 0 Previous issue date: 2011-07-29Bitstream added on 2014-06-13T19:23:22Z : No. of bitstreams: 1 andrade_dp_dr_sjc.pdf: 981103 bytes, checksum: 368bc6b13475a5629a9213ad35edf3ea (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Titânio (Ti) é um dos melhores biomateriais para a confecção de implantes cirúrgicos, porém, estudos com novas ligas de Ti e variações da topografia visam otimizar os resultados da osseointegração. O objetivo deste estudo in vitro foi avaliar a biocompatibilidade de amostras densas e porosas da liga titânio- 35nióbio submetidas ou não ao tratamento biomimético, comparadas a amostras de Ti puro grau 2. As amostras foram divididas em 6 grupos (G): a) G1- Ti denso; b) G2 - Ti poroso; c) G3 – Ti poroso tratado; d) G4 - Ti-35Nb denso; e) G5 - Ti-35Nb poroso; f) G6 - Ti-35Nb poroso tratado. Células osteogênicas obtidas da calvária de ratos recémnascidos foram plaqueadas sobre as amostras e a adesão celular foi avaliada após 4 e 24 horas, enquanto a proliferação celular foi avaliada em 1, 3, 7 e 10 dias. A viabilidade foi avaliada em 1, 3, 7 e 10 dias. Para os demais testes as células foram cultivadas por 7, 10 e 14 dias. Após 14 dias, as culturas foram coradas com vermelho de Alizarina S para detecção dos nódulos de mineralização. As amostras foram caracterizadas por espectroscopia por dispersão de energia (EDS), difração de raio X (DRX), análise metalográfica e de rugosidade. Os dados da análise metalográfica foram submetidos ao teste de Kruskal Wallis e os dados das análises celulares foram comparados pelos testes Kruskal Wallis, Mann-Whitney e T-Student, (p<0,05). O EDS demonstrou a presença de íons sódio, fósforo, magnésio e cálcio nas amostras tratadas de ambos os grupos. O DRX demonstrou a presença dos metais titânio e nióbio na liga teste. A análise metalográfica demonstrou que as amostras porosas apresentavam poros interligados, com morfologia variada e a análise pelo rugosímetro demonstrou... / Titanium (Ti) is one of the best biomaterials for surgical implants fabrication. Studies with new titanium alloys and varied surface topographies seek for improved osseointegration results. The aim of the present in vitro study was to evaluate dense and porous titanium- 35 niobium alloys, submitted or not to biomimetic treatment in comparison to degree 2 pure titanium specimens. Specimens were divided into 6 groups (G): a) G1 – dense Ti; b) G2 – porous Ti; c) G3 – treated porous Ti; d) G4 – dense Ti-35Nb; e) G5 – porous Ti-35Nb and f) G6 – treated porous Ti-35Nb. Osteogenic cells from newborn rats calvarium were plated over the samples and cell adhesion assessed after 4 and 24 hours. Cell proliferation and viability were assessed at 1, 3, 7 and 10 days. Cells were cultured for 7, 10 and 14 days for further testings. Cell cultures were stained with Alizarin Red S after 14 days for mineralization nodules detection. Specimens were characterized by means of Energy Dispersion Spectrophotometry (EDS), X-Ray Diffraction (XRD), metallographic and profilometer analyses. Metallographic data were submitted to Kruskal Wallis, while cell analyses were assessed with Kruskal Wallis, Mann-Whitney and T-Student tests (P<0.05). EDS results detected the presence of sodium, phosphor, magnesium and calcium ions in treated specimens from both groups. XRD showed the presence of titanium and niobium for the test alloy. Metallographic analysis revealed interconnected pores and varied morphology within the porous specimens. Greater rugosity was detected by the profilometer analysis within the dense alloy specimens. In vitro tests revealed similar biocompatibility of Ti- 35Nb and degree 2 pure Ti. Porosity did not interfere, but in some scenarios improved alloy biocompatibility. The biomimetic treatment favor greater production... (Complete abstract click electronic access below)

Dissertação apresentada ao Programa de Pós-Graduação em Educação da Universidade do Extremo Sul Catarinense – UNESC para a obtenção do título de Mestre em Educação. / This dissertation sought to understand how the Power of Kindness, located in the public schools of the South of Santa Catarina (1953 - 1970), contributed in building the school culture. In order to deepen this study, some specific objectives were established: Understand what led schools to deploy the Power of Kindness in Brazil; identify with that order was created League of Goodness in public schools in southern Santa Catarina; Investigate assignments League of Kindness (goals and objectives); Understanding how the leagues of Kindness worked in public schools in southern Santa Catarina; Identify who the participants were members of the League of Kindness and their actions. For this, were analyzed by means of desk research, reports Leagues Goodness of EEB de Meleiro (Meleiro), EEB Professor Lapagesse (Criciúma) and EEB Manoel Gomes Baltazar (Maracajá), from some of these documents students (as) and teachers cited (as) in them, were interviewed (as) to contribute their memories about the League of Goodness. With this research we can say that through the records of the League of Goodness and memory of (the) students (as) and interviewed teachers (as) there was an approach to school culture of each breed. Among the activities most frequently recorded in the minutes is the Christmas campaign of Lazarus, which leads me to say that schools subject to imagine that they build a kind, compassionate spirit, making the attitudes of students, male and female were useful to school, society and the Catholic Church. The imposition of Catholicism as a religion was evident not only in the records, but also in the interviews. Can infer that the League of Kindness served to attract more faithful and also to keep those already. / A presente dissertação buscou perceber como a Liga da Bondade, implantada nas escolas públicas estaduais do sul de Santa Catarina (1953 – 1970), contribuiu na construção da cultura escolar. Com o intuito de aprofundar este estudo, foram estabelecidos alguns objetivos específicos: Compreender o que levou as escolas a implantarem a Liga da Bondade no Brasil; Identificar com que intuito foi criada Liga da Bondade nas escolas públicas estaduais do sul de Santa Catarina; Investigar sobre as atribuições da Liga da Bondade (objetivos e finalidades); Entender como funcionavam as Ligas da Bondade nas escolas públicas estaduais do sul de Santa Catarina; Identificar quem eram os membros participantes da Liga da Bondade e suas ações. Para isso, foram analisados, por meio de uma pesquisa documental, os relatórios das Ligas da Bondade da EEB de Meleiro (Meleiro), da escola EEB Professor Lapagesse (Criciúma) e da EEB Manoel Gomes Baltazar (Maracajá). A partir desses documentos alguns alunos(as) e professoras, citados(as) nos mesmos, foram entrevistados(as) para contribuírem com suas memórias acerca da Liga da Bondade. Com a realização desta pesquisa é possível afirmar que por meio dos registros da Liga da Bondade e da memória dos(as) alunos(as) e professoras entrevistados(as) houve uma aproximação com a cultura escolar de cada educandário. Entre as atividades mais registradas nas atas está a Campanha do Natal dos Lázaros, o que me leva a afirmar que as escolas intencionavam construir um sujeito com espírito bondoso, caridoso, fazendo com que as atitudes de alunos e alunas participantes fossem úteis à escola, à sociedade e à Igreja Católica. O cultivo do catolicismo enquanto religião ficou evidente, não só nos registros, mas também nas entrevistas. Posso inferir que a Liga da Bondade serviu para atrair mais fiéis e, também, para manter os que já eram.

Made available in DSpace on 2016-06-02T19:11:49Z (GMT). No. of bitstreams: 1 1795.pdf: 5550885 bytes, checksum: 1be0da6e81e9e84eb153d9eafe8f1116 (MD5) Previous issue date: 2007-09-14 / Universidade Federal de Sao Carlos / The corrosion resistance of aluminum alloy can be impaired due to intermetallic precipitation during thermal treatment to improve mechanical properties. This work investigates the corrosion resistance of aluminum alloy 2024-T351 and the joint welded by FSW. Microstructural analysis and microhardness tests were made. Intergranular corrosion tests according to ASTM G110-97, exfoliation corrosion tests according to ASTM G 34-01 and stress corrosion cracking in 3.5% NaCl according to ASTM G 129-00, were carried out. Anodic behavior was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was not detected intermetallic precipitates by electron and optical microscopy. It was also detected that the joint was more severe attacked than the base metal by intergranular corrosion and exfoliation tests. The welded joint was susceptible to stress corrosion cracking in tests carried out with low nominal strain rate of 10-7 s-1. Base metal and the joint in tests carried out in air and in 3.5% NaCl at strain rate of 10-6 s-1 showed ductile behavior, while the joint with strain rate of 10-7 s-1 showed fragile behavior. The polarization test in chloride medium of aluminum alloys didn t show passive breakdown what make difficult to determinate the pitting potential. Polarization curves indicated that the welded joint had lower current density and higher potential than the base metal. In lower potentials pitting was formed majoritary at grain boundaries / A resistência à corrosão de ligas de alumínio pode ser degradada devido à precipitação de intermetálicos quando submetidas a tratamentos térmicos para elevar a resistência mecânica. Este trabalho investiga a resistência à corrosão da liga de alumínio 2024-T351 e também da junta soldada por FSW. Foram feitos análise microestrutural e microdureza. Foram realizados ensaios de corrosão intergranular segundo a norma ASTM G110-97, corrosão por esfoliação de acordo com a norma ASTM G34-01 e também ensaio de corrosão sob tensão em solução de NaCl 3,5% com taxa de deformação de 10- 6 e 10-7 s-1, segundo a norma ASTM G129-00. O comportamento anódico foi avaliado por testes potenciodinâmicos em solução de NaCl 3,5%. Os precipitados intermetálicos não foram observados por microscopias ótica e eletrônica. Nos ensaios de corrosão intergranular e esfoliação foi observado que a junta soldada sofreu corrosão mais acentuada do que o metal base. A junta soldada foi suscetível a corrosão sob tensão, somente em ensaios realizados com taxa de deformação baixa, de 10-7 s-1. O metal base e a junta ensaiada ao ar e em NaCl 3,5% com taxa de deformação de 10-6 s-1 apresentaram comportamento dútil, enquanto a junta com taxa de deformação 10-7 s-1, apresentou comportamento frágil. Nos ensaios de polarização em meio de cloretos a liga 2024-T351 não foi observado patamar de passivação o que dificultou a determinação do potencial de pite. As curvas de polarização mostraram que a junta soldada possui densidade de corrente menor e maiores potenciais do que o metal base. Em baixos potenciais os pites foram formados preferencialmente nos contornos dos grãos

Made available in DSpace on 2016-06-02T19:11:53Z (GMT). No. of bitstreams: 1 2130.pdf: 6968456 bytes, checksum: 505fdf9c92f4d73ed148ba801ec77c8d (MD5) Previous issue date: 2008-09-08 / Universidade Federal de Sao Carlos / Aluminum alloys having a particle dispersion in nanometric scale, which present elevated values of mechanical strength at both ambient and high temperatures have been studied for some time. These alloys are known for presenting icosahedral particles embedded in an &#945;-Al matrix and they are called nanoquasicrystalline alloys, having large thermal stability as their major characteristic. The present work aims to evaluate the mechanical properties and the possibility of formation of quasicrystalline phases in an Al92Fe3Cr2Mn3 rapidly solidified to produce bulk samples. The alloy was characterized by scanning electron microscopy (SEM), X-ray diffraction (DRX) and differential scanning calorimetry (DSC). The mechanical properties were evaluated by compression tests at ambient and high temperatures and also by microhardness tests. The results showed refined microstructure and possibility of presence of quasicrystalline phase. Elevated mechanical strength was observed for the alloy even in temperatures up to 300°C, always associated with good plasticity in compression. / Ligas de alumínio (Al) contendo dispersão de partículas em escala nanométrica que apresentam valores elevados de resistência mecânica em temperaturas ambientes e em altas temperaturas já são estudadas há algum tempo. Estas ligas são conhecidas por apresentar partículas icosaedrais embebidas numa matriz de Al-&#945; e são chamadas de ligas nanoquasicristalinas, tendo como característica marcante grande estabilidade térmica. O presente trabalho visou avaliar as propriedades mecânicas e a possibilidade de formação de fases quasicristalinas de uma liga Al92Fe3Cr2Mn3 solidificada rapidamente através da produção de corpos de prova de grande volume. A caracterização da liga foi feita via microscopia eletrônica de varredura (MEV), difração de raios-X (DRX) e calorimetria diferencial de varredura (DSC). As propriedades mecânicas foram avaliadas através de ensaios de compressão em temperatura ambiente e em elevadas temperaturas e através de testes de micro-dureza. Os resultados mostraram microestrutura refinada e possibilidade de presença de quasicristais. Os valores de resistência mecânica apresentados pela liga foram elevados inclusive em temperaturas de 300°C, associados com alta plasticidade em compressão.

Made available in DSpace on 2016-06-02T19:12:32Z (GMT). No. of bitstreams: 1 5520.pdf: 15957813 bytes, checksum: 79aec06af1bae5d8465f546113e03184 (MD5) Previous issue date: 2013-07-29 / Sn-Pb traditional solder alloys were overly utilize in electronic devices industry, since their properties and features use were adequate and well known. In the last years many restrictions and directives were and have been designed with a view to minimize or eliminate the use of this metal in the electronic industry. Thereby, several lead-free solder alloys emerged. Among these alloys, eutectic Sn-0.7wt%Cu (TE=227°C) appears as potential candidate to replace eutectic Sn-37wt%Pb alloys, because present low cost when compared with the other lead-free solder alloys. Fatigue resistance and fluidity are quite similar compared with those obtained for the traditional Sn-Pb alloys. Small alloying additions of Ni in Sn-Cu eutectics between levels 20-1000ppm Ni can improve welding properties such as good fluidity, reliability, fine degree of wetting, ensuring suitable mechanical resistance of solder joint. Thus, the main goals of present study are investigate the influence of the Ni microadditions on solidification thermal parameters (transient interfacial heat transfer coefficient - hi), eutectic growth rate v and cooling rate - &#7786;), microstructure features (dendritic and cellular spacings, &#955;1 and &#955;C) and tensile properties in directionally solidified Sn-0.7wt%Cu, Sn-0.7wt%Cu-0.05wt%Ni e Sn-0.7wt%Cu-0.1wt%Ni alloys under unsteady-state conditions against AISI steel carbon 1020 water-cooled bottom part. Measurements of hi coefficient showed that Ni microadditions (500 and 1000ppm of Ni) in the eutectic Sn-0.7wt%Cu affected significantly the fluidity levels. The microstructures obtained for the Sn-0,7wt%Cu-(xNi) alloys presented eutectic colonies/cells along the casting length, with dendritic regions only on first positions close to the bottom. Small Ni additions promoted increase on ultimate tensile strength (&#963;u) and elongation (&#948;), with the Sn-0.7wt%Cu-0.05wt%Ni alloy corresponding to the better combination of &#963;u and &#948;, 36.6MPa and 12.1%, respectively. / As tradicionais ligas de soldagem Sn-Pb foram excessivamente utilizadas na indústria de dispositivos eletrônicos, uma vez que suas características de uso e propriedades eram adequadas e bem conhecidas. Contudo, devido aos problemas acarretados pela toxidade do Pb, várias restrições/diretrizes foram e estão sendo criadas a fim de minimizar ou eliminar o uso desse metal na indústria eletrônica. Com isso, diversas ligas de soldagem livres de Pb surgiram e dentre tais ligas, a liga eutética Sn-0,7%Cu (TE=227°C) surge com uma alternativa promissora para a substituição de ligas de solda contendo Pb, pois apresentam menor custo que as demais ligas de soldagem e propriedades como resistência à fadiga e fluidez semelhantes às obtidas para ligas do sistema Sn-Pb. Neste contexto, microadições de Ni em ligas eutéticas Sn-Cu em níveis entre 20 e 1000ppm podem trazer melhorias de propriedades de soldagem como boa fluidez, boa soldabilidade, bom grau de molhamento, garantindo adequada resistência mecânica da junta soldada. Assim, o presente estudo objetiva investigar a influência de microadições de Ni nos parâmetros térmicos de solidificação (coeficiente interfacial de transferência de calor metal/molde - hi, velocidade de solidificação - v e taxa de resfriamento - &#7786;), nas características estruturais (espaçamento intercelular e interdendrítico, &#955;C e &#955;1) e nas propriedades mecânicas de tração das ligas Sn-0,7%Cu, Sn-0,7%Cu-0,05%Ni e Sn-0,7%Cu-0,1%Ni solidificadas unidirecionalmente no sentido vertical ascendente contra chapa molde de aço carbono 1020. Os valores de hi mostraram que microadições de Ni (500 e 1000ppm) em ligas eutéticas Sn-0,7%Cu afetaram consideravelmente o nível de fluidez. As microestruturas das ligas Sn-0,7%Cu-(xNi) apresentaram colônias eutéticas ao longo dos lingotes, com regiões dendríticas apenas nas posições próximas da base refrigerada. As microadições de Ni promoveram um aumento do limite de resistência à tração (&#963;u) e do alongamento específico (&#948;), com a liga Sn-0,7%Cu-0,05%Ni apresentando a melhor combinação &#963;u/&#948;, 36,6 MPa e 12,1%, respectivamente.

Made available in DSpace on 2016-06-02T19:12:39Z (GMT). No. of bitstreams: 1 6341.pdf: 7602740 bytes, checksum: fec817279e952ea68e2131f1d4d86d90 (MD5) Previous issue date: 2014-07-03 / Financiadora de Estudos e Projetos / The objective of this study was to evaluate the microstructure and the mechanical properties of hot extruded bars and cold rotary swaging wires of an AA7050 alloy. The ingot for the mechanical conformation operations was obtained by spray forming using machining chips from an aircraft manufacturer as raw material. The microstructural characterization of the final and intermediaries products (deposit and extruded bar) was performed by optical microscopy and scanning electron microscopy; the mechanical characterization was done by tensile tests. The deposit obtained by spray deposition was submitted to hot compression tests with the aim to obtain the parameters of a constitutive equation for predict the hot deformation behavior in two different conditions homogenized and without any treatment. The process route adopted showed to be effective to eliminate the porosity produced by the spray process, and also to refine the microstructure, resulting in mechanical properties meeting the requirements of the standard of this alloy for aircraft applications. The extruded bar and the rotary swaged wires presented both slant and cup-cone fracture, being this phenomena kept after the age treatment in the extruded products, which was attributed to the occurrence of preferential crystalline orientation of the grains during extrusion. This preferential orientation was not removed during the solution heat treatment before aging; on the other hand, the wires were completely recrystallized during solution heat treatment and this phenomenon has disappeared. Hot compression tests were performed with the aim of describe constitutive equations of the material behavior in both conditions previously to conformation (homogenized and without previously homogenization treatment). The hot compression test reveals distinct behaviors of dynamic recovering/hardening during the tests. / O objetivo deste trabalho foi o de avaliar a microestrutura e as propriedades mecânicas de barras extrudadas a quente e forjadas rotativamente a frio de uma liga AA7050. O lingote para as operações de conformação mecânica foi produzido por conformação por spray a partir de sucata proveniente da usinagem de componentes aeronáuticos. A caracterização microestrutural foi realizada por meio de microscopia óptica e eletrônica de varredura, a caracterização mecânica foi realizada por meio de ensaios de tração. O depósito obtido na conformação por spray foi submetido a ensaios de compressão a quente a fim de se obter equações constitutivas do comportamento do material sob deformação a quente, em duas condições iniciais (homogeneizado e como obtido). A rota de processamento adotada mostrou-se efetiva no fechamento dos poros inerentes ao processo de conformação por spray e no refino da microestrutura obtida, o que resultou em propriedades mecânicas atendendo aos requisitos de norma dessa liga para aplicação aeronáutica. O produto extrudado e os fios forjados apresentaram nos ensaios de tração fraturas tanto slant como uma mistura slant e taça cone, tendo este fenômeno continuado presente após envelhecimento nos produtos extrudados, o que foi atribuído à ocorrência de textura cristalográfica oriunda da extrusão, a qual não foi desfeita por recristalização durante tratamento térmico de homogeneização/solubilização; no caso dos arames os mesmos foram completamente recristalizados e o fenômeno desapareceu. Ensaios de compressão a quente foram realizados com o intuito de se descrever equações constitutivas do comportamento do material em ambas as condições prévias à conformação (homogeneizado e sem homogeneização prévia). Os ensaios de compressão revelaram comportamentos de amaciamento/endurecimento dinâmicos distintos durante os mesmos.

Submitted by Caroline Periotto (carol@ufscar.br) on 2016-09-19T15:15:58Z No. of bitstreams: 1 DissLFV.pdf: 6082147 bytes, checksum: 0c3dbc2525f0888e4029ab4c5ea27574 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-09-20T18:00:26Z (GMT) No. of bitstreams: 1 DissLFV.pdf: 6082147 bytes, checksum: 0c3dbc2525f0888e4029ab4c5ea27574 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-09-20T18:00:33Z (GMT) No. of bitstreams: 1 DissLFV.pdf: 6082147 bytes, checksum: 0c3dbc2525f0888e4029ab4c5ea27574 (MD5) / Made available in DSpace on 2016-09-20T18:00:39Z (GMT). No. of bitstreams: 1 DissLFV.pdf: 6082147 bytes, checksum: 0c3dbc2525f0888e4029ab4c5ea27574 (MD5) Previous issue date: 2015-08-07 / Não recebi financiamento / Residual stresses are those which remain in the part when all the external mechanical stress applied previously are removed. These residual stresses often appear in parts subjected to different thermal or mechanical processing along its thickness, among then may be cited the welding process. The objective of this work is the analysis of residual stresses generated by the recovery process for shielded metal arc welding” (SMAW) of sugarcane milling gear in Low Alloy Mild Steel ASTM C-148 for the identification of conditions with lower levels of residual stresses, aiming materials less susceptible to failure and longer service life. A comparative assessment of the levels of residual stresses in the aforementioned samples was performed by opting for performance or nonperformance of pre-heating and heat treatment of stress relieving after the completion of the welds in the field. It will be characterized by metallography and hardness profile. In order to determine the way the macro and microscopic residual stresses non-destructive, it was decided in this work by the diffraction of X-ray method. The characterization was carried out by optical microscopy, scanning electron microscopy and Vickers microhardness. The microstructure present in the base metal was characterized as microconstituent bainite, when there is a stress relieving treatment. When there isn`t such treatment, the microstructure is ferrite / pearlite. Although in the weld metal, due to the electrode composition, the microstructure is acicular ferrite. The Vickers microhardness analysis for the sample without pre-heating gave higher microhardness values along line profile (range of 250 – 325 HV) than the other conditions (range of 150 – 275 HV). Regarding the residual stresses, it can be concluded that the pre-heating and the combination of it with a subsequent heat treatment reduces the levels of both longitudinal and transverse residual stress along the weld bead. / Tensões residuais são aquelas que permanecem na peça a temperatura ambiente quando todas as suas solicitações externas são removidas. Essas tensões aparecem frequentemente em peças submetidas a diferentes processamentos térmicos e/ou mecânicos, dentre os quais pode ser citada a soldagem. O principal objetivo desta dissertação é a análise da microestrutura e das tensões residuais geradas por diferentes estratégias de recuperação por soldagem a arco com eletrodo revestido (SAER) em engrenagens de moenda de cana fabricada em aço carbono ASTM A-148, para identificação das condições com menores níveis de tensões residuais e microestrutura adequada, visando materiais menos susceptíveis a falhas e com vida útil estendida. Foi realizada uma avaliação comparativa dos níveis de tensões residuais nas amostras mencionadas, optando pela realização ou não de pré-aquecimento e tratamento térmico de alívio de tensões após a realização das soldas em campo. As mesmas serão caracterizadas por metalografia e perfil de microdureza. Com o intuito de determinar de maneira não-destrutiva as tensões residuais macro e microscópicas, optou-se neste trabalho pelo método da Difração de Raios-X. A caracterização foi feita por: microscopia ótica, eletrônica de varredura, além de microdureza Vickers. A microestrutura presente no metal base é caracterizada por agulhas que correspondem ao microconstituinte bainita quando há o tratamento de alívio de tensões. Quando não há este tratamento, a microestrutura é ferrítica/perlítica. Já no metal de solda, devido à composição do eletrodo, a microestrutura presente é de ferrita acicular. Na análise de microdureza Vickers, para a amostra sem pré aquecimento, obteve-se maior microdureza em todo o perfil da linha (faixa de 250 a 325 HV) do que as demais (faixa de 150 a 275 HV). Quanto às tensões residuais, pode-se concluir que, o pré-aquecimento e a combinação dele com um tratamento térmico posterior reduzem os níveis de tensão residual longitudinal e transversal nos cordões.

Submitted by Caroline Periotto (carol@ufscar.br) on 2016-10-10T13:14:26Z No. of bitstreams: 1 TeseBTR.pdf: 7351575 bytes, checksum: b4b8c40821f19284081c4e4572e9f103 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-10-20T19:48:41Z (GMT) No. of bitstreams: 1 TeseBTR.pdf: 7351575 bytes, checksum: b4b8c40821f19284081c4e4572e9f103 (MD5) / Approved for entry into archive by Marina Freitas (marinapf@ufscar.br) on 2016-10-20T19:48:46Z (GMT) No. of bitstreams: 1 TeseBTR.pdf: 7351575 bytes, checksum: b4b8c40821f19284081c4e4572e9f103 (MD5) / Made available in DSpace on 2016-10-20T19:48:52Z (GMT). No. of bitstreams: 1 TeseBTR.pdf: 7351575 bytes, checksum: b4b8c40821f19284081c4e4572e9f103 (MD5) Previous issue date: 2015-08-28 / Não recebi financiamento / In orthopedic medicine and traumatology, the use of implants to help bone reconstitution is very common. They are divided in two groups: Internal and external fixation devices. After bone reconstitution, these components lose their function and therefore must be removed. However, in many cases, due to the cost or patient suffering, the devices are not removed. To avoid this, are under development bioabsorbable alloys that after bone healing degrade and are absorbed by the body, not requiring its removal. Among them, magnesium based alloys are under the spot. Regular magnesium alloys, however, present one main drawback: High corrosion rate, which leads to mechanical properties loss before the bone reconstitution and excessive production of gas hydrogen, leading to the formation of gas pockets, which cause adverse reactions and inhibit bone growth. This study aims to investigate surface coatings on the commercial alloy AZ91 in order to decrease the corrosion rate, making the material suitable for the use as biodegradable implants. Three modified SBF solutions were employed to coat the surfaces with apatites using the biomimetic method. The influences of pre-treatment of the samples in NaOH solution and heat treatment after coating on the electrochemical behavior of produced coatings were investigated. The results showed that the use of biomimetic method using modified SBF solutions was effective to produce apatite phases on the surface of the magnesium commercial alloy AZ91, considered a more suitable bone replacement than HA. The coated samples presented higher corrosion resistance than the uncoated material, as evaluated by electrochemical tests. This behavior was more pronounced for coatings obtained after the use of pre-treatment NaOH solution. / Na medicina ortopédica e traumatológica o uso de implantes para auxílio da reconstituição óssea de membros é muito comum. São formadas por dois grupos: Dispositivos de fixação interna e de fixação externa. Após a consolidação da fratura, esses componentes perdem sua função e por isso devem ser retirados. Muitas vezes, porém, não o são devido ao custo e sofrimento causado ao paciente. Para evitar isso, estão em desenvolvimento ligas biodegradáveis que, após a consolidação óssea, degradam e são absorvidas pelo organismo, não sendo necessária sua retirada. Entre elas se destacam as ligas a base de magnésio que, no entanto, vem apresentando altas taxas de corrosão, que fazem com que a peça perca as propriedades mecânicas antes da consolidação da fratura, além de proporcionarem a produção em excesso de gás hidrogênio que leva à formação de bolsas de gás, as quais causam reações adversas e inibem o crescimento ósseo. Este trabalho tem como objetivo investigar recobrimentos da superfície da liga comercial AZ91, a fim de possibilitar o desenvolvimento de um material com taxa de corrosão mais adequada, que permita a consolidação da fratura antes de sua biodegradação. Utilizou-se neste trabalho o recobrimento com apatitas através do Método Biomimético com o emprego de três soluções SBF modificadas. Foi investigada a influência do pré-tratamento das amostras em NaOH e também do tratamento térmico pós recobrimento, na obtenção e na composição dos recobrimentos, assim como no comportamento eletroquímico das amostras. Os recobrimentos obtidos foram compostos por fases de apatita consideradas substitutas ósseas mais adequadas que a Hidroxiapatita (HA) e mostraram nos ensaios eletroquímicos uma redução efetivada da taxa de corrosão, sendo esse comportamento mais acentuado para os recobrimentos obtidos após o emprego do pré-tratamento em solução de NaOH.

Submitted by Maria Suzana Diniz (msuzanad@hotmail.com) on 2015-11-11T15:09:33Z No. of bitstreams: 1 arquivototal.pdf: 1991641 bytes, checksum: ba8fcc8a2e4b18edbf9d9e8c286626b6 (MD5) / Made available in DSpace on 2015-11-11T15:09:33Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 1991641 bytes, checksum: ba8fcc8a2e4b18edbf9d9e8c286626b6 (MD5) Previous issue date: 2015-02-02 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / This paper presents an experimental design of a power control system and position, using, as actuator, a coil spring of Shape Memory Alloy (SMA), consisting of Ni-Ti alloys, in an adapted screw table. A controller, closed loop, based on Fuzzy logic has been modeled to control the force exerted by the spring which the spring is manipulating by the temperature. In this work, the spring temperature was controlled by an electric current, which produces heat generation by Joule effect. A restoring spring was used to make the shape memory spring to restore the system to its original position. To supply the shape memory spring we used a controlled current source, whose current value that determines the desired force applied which is measured with a load cell and position by a camera connected a computer. The shape memory spring characteristics were determined from conventional approach to helical traction springs, and then characterized by Differential Scanning Calorimetry (DSC). The Fuzzy controller was modeled on LabVIEW installed on a computer equipped with a data acquisition system. The experimental results were obtained from tests on test bench, with the shape memory alloy spring with and without training. / Neste trabalho apresenta-se um projeto experimental de um sistema de controle de força e de posição utilizando, como atuador, uma mola helicoidal de Liga de Memória de Forma (LMF), constituída de ligas de Ni-Ti, em uma mesa de fuso adaptada. Um controlador, em malha fechada, baseado em Lógica Fuzzy foi modelado para controlar a força exercida pela mola, a qual é manipulada através da temperatura da mola. Neste trabalho, a temperatura de mola foi controlada através de uma corrente elétrica, que produz geração de calor através do efeito Joule. Uma mola restauradora foi utilizada para fazer a mola de memória de forma restaurar o sistema à sua posição original. Para alimentar a mola de memória de forma utilizou-se uma fonte de corrente continua controlada, cujo valor dessa corrente determina a força aplicada desejada a qual foi medida com uma célula de carga e a posição através de uma câmera conectada a um computador. As características da mola de memória de forma foram determinadas a partir de abordagem convencional para molas helicoidais de tração, e em seguida caracterizada, através de calorimetria diferencial de varredura (DSC). O controlador Fuzzy foi modelado no ambiente LabVIEW instalado em um computador equipado com um sistema de aquisição de dados. Os resultados experimentais foram obtidos em ensaios realizados na bancada de teste, com a mola de liga de memoria de forma com e sem treinamento.