USAGE OF SOCIAL MEDIA IN 1ST CZECH FOOTBALL LEAGUE Objectives: The main aim of this diploma thesis is to assess the situation around the Gambrinus league clubs communication through social media towards to fans and supporters. Based on the results recommendations for communication through social media will be proposed. Methods: In this thesis following methods were used: case study, survey and finding dependence between two variables using regression analysis. Case study method was applied in the evaluation of communication of three clubs through social media. The survey recorded opinions of the fans. Regression analysis examined the dependence between the average home attendance of clubs and the number of fans on Facebook. Results: The results of the thesis correspond to the selected aims and are summarized in a separate chapter as suggestions and recommendations for communication through social media. Key words: social media, Facebook, Twitter, YouTube, Google +, football club, Gambrinus league, football

In this paper, I deal with the issue of press conferences after matches of 1st soccer league. My goal is in the first place to describe press conferences as a part of public relations and as one of main and most important categories of respondents interacting with journalists. In the first part of my master thesis I examine sports journalism and its specifics and differences against other fields of this profession. For research itself I used techniques of observation and questioning, but mainly I worked with the data gained during interviews and information obtained by myself, as an involved observer. During my observation I have visited 14 press conferences throughout one season of 1st soccer league in total that took place all around Czech Republic. The goals of researching these events were its course, specifically how long the events were and in which environment, but also what are the rules for its organisation and how those rules are complied. Another subject of my research was a position of a spokespersons and work of journalists, whose job is to question. I was also interested in a manner of questioning and topics of questions in this area. Among main conclusions of my thesis there is significantly larger focus of media on the three biggest Czech soccer teams which are Slavia Prague, Sparta...

Materiais empregados em polos petroquímicos têm sofrido exigências cada vez mais criteriosas em relação as suas condições de trabalho e desempenho em campo e, atualmente, a liga metálica mais utilizada para a confecção de tubos centrifugados para aplicação nesses locais de trabalho é a liga de aço inoxidável HP modificada com microadições (HPNb-MA). Esses materiais, cuja microestrutura na condição bruta de fundição é composta por uma matriz austenítica com carbonetos de cromo e nióbio nos contornos dos grãos e que apresentam propriedades paramagnéticas em temperatura ambiente, são empregados em polos petroquímicos por apresentarem excelentes propriedades mecânicas em temperaturas elevadas, além de considerável resistência a carburização e perda de massa por oxidação. Visando melhores desempenhos e maiores durabilidades, as microadições são realizadas de maneira intencional e controlada durante o processo de centrifugação. Entre elas, os elementos pertencentes as terras raras têm apresentado resultados satisfatórios em relação a melhorias em propriedades mecânicas em temperatura ambiente e em temperaturas elevadas. O presente trabalho busca padronizar a microadição de ítrio e titânio na liga em estudo, realizando comparações com um material similar cuja composição química se diferencia apenas pela não adição de terras raras durante a confecção dos tubos. Análises comparativas e estatísticas foram realizadas com o intuito de se determinar qual amostra obteria o melhor desempenho em campo. Como parâmetros, foram adotados ensaios de análise química, propriedades mecânicas em temperatura ambiente e temperaturas elevadas, ruptura por fluência, macrografia, microscopia eletrônica de varredura, raios-X, MET, carburização e oxidação. Em paralelo, foi desenvolvido um equipamento capaz de quantificar o nível de carburização dos materiais em estudo em função de alterações das propriedades ferromagnéticas dessas ligas metálicas quando expostas a ambientes carburizantes e com elevadas temperaturas, utilizando para isso, resultados obtidos a partir de simulações laboratoriais e amostras obtidas diretamente de fornos de pirólise. / Materials used in petrochemical poles have undergone increasingly demanding requirements regarding their working conditions and performance in the field. Today, the most used metal alloy for the manufacture of centrifugally cast tubes applied in these work places is the HP stainless steel alloy, modified with micro-addition (HPNb-MA). These materials, which microstructure in as-cast condition is made of an austenitic array of chromium and niobium carbides contouring the grains, exhibit paramagnetic properties at room temperature. They are employed in the petrochemical poles because of its excellent mechanical properties at elevated temperatures, in addition to considerable resistance to carburization and mass loss by oxidation. Aiming for a better performance and longer durability, the micro-addition is carried out in an intentional and controlled way during the centrifugation process. Between them, the elements belonging to rare earths have presented satisfactory results regarding to improvements in its mechanical properties at room temperature and at elevated temperatures. The present work seeks to standardize the micro-addition process of yttrium and titanium in the alloy under study, making comparisons with a similar material which chemical composition differs only by not adding rare earths during the tubes manufacture. Comparative and statistics analysis were carried out with the intent of determining which sample would attain the best performance in the field. Chemical analysis tests, mechanical properties at room temperature and at elevated temperatures, creep rupture, macrography, scanning electron microscopy, X-ray, TEM, carburization and oxidation were adopted as parameters. In parallel, an equipment capable of quantifying the carburization level of the materials under study was developed. These levels are measured in function of changes in the ferromagnetic properties of these metallic alloys when exposed to carburizing and high temperature environments. The equipment makes use of results obtained from laboratory simulations and samples obtained directly from pyrolysis furnaces.

A Ti-35Nb-7Zr é uma liga Ti-ß desenvolvida pelo Grupo de Biomateriais da Escola de Engenharia de Lorena da Universidade de São Paulo, que demonstrou, em estudos anteriores, propriedades mecânicas favoráveis para ser usada como biomaterial, tais como, limite de resistência (~800 Mpa), resistência à corrosão e baixo módulo de elasticidade (33 GPa). Uma vez que o implante dentário traz melhores resultados no tocante à função mastigatória, fonação, conforto e estética, melhorando a qualidade de vida das pessoas, o presente estudo descreve a avaliação da biofuncionalidade dos implantes dentários da liga Ti-35Nb-7Zr comparados aos implantes comerciais de Ti-Cp da marca Titaniumfix. A biofuncionalidade foi avaliada por meio de testes in vitro e in vivo. A avaliação in vitro foi realizada com células mesenquimais indiferenciadas retiradas da medula óssea de fêmures de ratos, que foram cultivadas em meio de cultura osteogênico e posteriormente realizados os testes de citotoxicidade, quantificação de proteína total e avaliação da atividade da fosfatase alcalina. A avaliação in vivo compreendeu a realização de implantes de Ti-Cp Titaniumfix e da liga Ti-35Nb-7Zr em tíbias de coelhos para avaliação histológica, histomorfométrica por meio do cálculo da Fração da área óssea ocupada (BAFO) e aposição óssea, e de remoção ao torque com intuito de avaliar a osteointegração. Considerando os resultados obtidos nesta pesquisa, com relação aos testes in vitro, é possível concluir que a liga possui maior hidrofilicidade que o Ti-Cp; apresenta espraiamento celular similar ao Ti-Cp o que corrobora para o resultado de viabilidade celular classificando-a como não citotóxica. Nos testes de quantificação de proteína total e atividade da fosfatase alcalina a liga apresenta resultados similares ao Ti-Cp, favorecendo a ocorrência de diferenciação e proliferação das células osteoblásticas. Desta forma, pode-se concluir que a liga possui boa compatibilidade in vitro. Os resultados obtidos nas avaliações in vivo, por meio da fração de área óssea ocupada (BAFO), comprovam a semelhança entre a liga e o Ti-Cp pois tiveram o valor percentual de osso neoformado similar. A análise de fluorescência, após a administração dos marcadores tetraciclina e alizarina, mostra que a aposição óssea também foi semelhante entre a liga e o Ti-Cp nos períodos estudados. Com relação a força de interação avaliada pelo torque de remoção é possível afirmar que a liga apresenta osteointegração comparável aos implantes comerciais Ti-Cp. Esses resultados demonstraram que os implantes da liga Ti-35Nb-7Zr apresentaram biocompatibilidade e biofuncionalidade semelhantes ao dos implantes de Ti-Cp. Além de possuir um baixo módulo de elasticidade, a liga apresentou uma osteointegração bem similar ao Ti-Cp, reunindo características que demonstram seu potencial para ser usada como biomaterial intraósseo. / Ti-35Nb-7Zr is a Ti-ß alloy developed by the Biomaterials Group of the Lorena School of Engineering of the University of São Paulo, which demonstrated, in previous studies, favorable mechanical properties to be used as biomaterial, such as resistance (~800 Mpa), corrosion resistance and low modulus of elasticity (33 GPa). Since the dental implant brings better results regarding masticatory function, phonation, comfort and aesthetics, improving the quality of life of the people, the present study describes the evaluation of the biofunctionality of the Ti-35Nb-7Zr ally dental implants compared to the Titaniumfix implants of Ti-Cp. The biofunctionality was evaluated by means of in vitro and in vivo tests. The in vitro evaluation was perfomed with undifferentiated mesenchymal cells removed from the bone marrow of rat femurs, which were cultured in osteogenic culture medium and subsequently perfomed cytotoxicity tests, total protein quantification and evaluation of alkaline phosphatase activity. The in vivo evaluation included the implantation of Ti-Cp Titaniumfix and Ti-35Nb-7Zr alloy implants in rabbit tibiae for histological, histomorphometric evaluation by calculating the Bone Area Fractional Occupied (BAFO) and bone apposition, and torque removal in order to evaluate the osseointegration. Considering the results obtained in this research, related to in vitro tests, it is possible to conclude that the alloy has a higher hydrophilicity than Ti-Cp; Show cellular spreading similar to Ti-Cp, which corroborates the result of cell viability classifying it as non-cytotoxic. In the tests of total protein quantification and alkaline phosphatase activity the alloy presents results similar to Ti-Cp, favoring the occurrence of differentiation and proliferation of osteoblastic cells. In this way, it can be concluded that the alloy has good compatiblity in vitro. The results obtained in the in vivo evaluations, through the BAFO, confirm the similarity between the alloy and Ti-Cp, since they had the percentage value similar to neoformed bone. Fluorescence analysis, after administration of the tetracycline and alisarin markers, show that bone apposition was also similar between the alloy and Ti-Cp in the periods studied. Regarding the interaction force evaluated by the removal torque, it is possible to affirm that the alloy show osseointegration comparable to commercial Ti-Cp implants. These results demonstrated that Ti-35Nb-7Zr alloy implants had similar biocompatibility and biofunctionality to Ti-Cp implants. In addition to having a low modulus of elasticity, the alloy presented an osseointegration very similar to Ti-Cp, bringing together characteristics that demonstrate its potential to be used as an intraosseous biomaterial.

As ligas de alumínio hipereutéticas fundidas por centrifugação apresentam a possibilidade de obtenção de um gradiente funcional de propriedades no material (Functionally Graded Material - FGM). Na fundição por centrifugação, os compostos menos densos tenderão a se concentrar no diâmetro interno de um tubo centrifugado. Como a massa específica do silício e do Mg2Si são menores do que a do alumínio, as partículas dessas fases tendem a concentrar-se na parede interna de tubos centrifugados. Em função disto, este estudo tem como objetivo dar uma contribuição ao entendimento dos mecanismos de migração das partículas de silício e de Mg2Si numa liga de alumínio hipereutética com 19% de silício e com adições de cobre e magnésio fundidas por centrifugação. Diante disto, foram obtidos tubos da liga Al-19%Si com adições de até 5% de cobre e 5% de magnésio por meio da fundição centrífuga numa rotação de 1700 rpm. A caracterização microestrutural em diversas regiões dos tubos centrifugados foi feita utilizando-se a microscopia óptica e eletrônica de varredura com sistema de análise de imagens. A fração das fases presentes e a dureza Vickers foram determinadas ao longo da parede do tubo em diversas posições de vazamento. A fundição centrífuga promove a segregação de partículas de silício primário e de Mg2Si, com massas específicas menores para a parede interna do tubo. Esta segregação é mais acentuada na região final de vazamento devido ao maior tempo de centrifugação até a solidificação. Uma retenção de partículas junto à parede externa do tubo ocorre em decorrência da mais elevada taxa de resfriamento da liga fundida em contato com a parede do molde mais frio. Esta retenção também foi maior na região do tubo de início de vazamento em relação à de final de vazamento. A adição de cobre intensificou a migração das partículas devido ao aumento da densidade do líquido. O aumento do teor de cobre na liga também inibiu a presença de dendritas de alumínio primário que ocorrem em grandes quantidades nas regiões centrais das paredes dos tubos centrifugados. O perfil de dureza ao longo da parede do tubo indicou um aumento de dureza relacionado diretamente à quantidade de partículas de silício (β) e Mg2Si. / A functionally gradient material, in terms of its properties, can be obtained with centrifugally cast hypereutectic aluminum alloys. In centrifugal casting, the less dense compounds tend to concentrate close to the inner wall of a centrifugally cast tube. Since the specific mass of silicon and Mg2Si are less than that of aluminum, particles of these phases tend to concentrate at the inner walls of centrifugally cast tubes. On the basis of this, the aim of this study was to contribute towards increased understanding of the mechanism of segregation of silicon and Mg2Si particles in a centrifugally cast hypereutectic aluminum - 19% silicon alloy to which copper and magnesium were added. Hence, tubes of Al-19%Si alloy with up to 5% copper and up to 5% magnesium were centrifugally cast at rotational speed of 1700 rpm. Microstructural examination of various regions of the centrifugally cast tubes was carried out using an optical microscope and a scanning electron microscope coupled to an image analyzer. The amount of phases that formed and the Vickers hardness were determined across the thickness of the tube at different positions. Centrifugal casting promotes segregation of primary silicon and Mg2Si particles, (with lower specific weights) towards the inner walls of the tube. This segregation was higher at regions that were last to be cast, and due to longer centrifugation until solidification. Retention of particles close to the outer wall of the tube took place due to higher cooling rate of the cast alloy in contact with the cold walls of the mold. This retention was also higher at regions of the tube that were cast first compared with those that were cast last. The addition of copper increased particle migration due to increase in density of the liquid. Increase in the amount of copper in the alloy also inhibited the presence of primary aluminum dendrites that form in large quantities at the central regions of centrifugally cast tube walls. The hardness profile along the tube wall indicated an increase in hardness and this is directly related to the quantity of (β) silicon and Mg2Si particles.

A liga binária Al-Cu é a base para todas as ligas da série 2xxx que são de grande importância em diversas aplicações como na indústria aeronáutica, transporte, máquinas e equipamentos. No entanto, pouco se conhece sobre os efeitos do tipo de solidificação desta liga e da deformação plástica sobre sua resistência à corrosão em meio aquoso. O escopo deste trabalho foi procurar correlacionar microestruturas da liga Al-4,5%p.Cu solidificada de maneira convencional e unidirecional vertical ascendente (brutas de fusão, deformadas plasticamente por forjamento rotativo a frio, e tratadas termicamente visando recristalização), orientações preferenciais de grãos com as características de resistência à corrosão. Foram utilizadas técnicas de microscopia eletrônica de varredura e óptica, difratometria de raios X e ensaios eletroquímicos em soluções de NaCl 0,6 M e Na2SO4 0,1M por polarização potenciodinâmica e espectroscopia de impedância eletroquímica. A taxa de corrosão foi maior em solução de NaCl 0,6 M do que em Na2SO4 0,1M para todas as amostras. O aumento da redução por deformação plástica conduziu a uma diminuição da resistência à corrosão da liga devido ao aumento das tensões internas e ao aparecimento de orientações preferenciais dos grãos de menor densidade planar como (200) e (220). As amostras recristalizadas apresentaram de uma forma geral uma resistência maior quando comparada às amostras não recristalizadas, comportamento atribuído ao alívio de tensões internas e ao desaparecimento da orientação preferencial do plano menos denso (220). / The binary Al-Cu alloy is the basis for all AA2xxx alloys, being important in several applications as aeronautical industry, transportation, machines and equipments. However, few is known about the effect of the type of solidification of this alloy and plastic deformation on the corrosion resistance in aqueous medium. The scope of this work was to correlate microstructures of the Al-4.5 % wt. Cu alloy solidified under conventional and upward direct chilling conditions (as cast condition, plastic formed by cold swaging, and heat treated seeking recristallyzation), crystallographic orientations and corrosion resistance characteristics. Scanning electron microscopy and optical, X ray diffractometry techniques and electrochemical measurements in NaCl 0,6 M and Na2SO4 0,1 M potentiodynamic polarization and electrochemical impedance spectroscopy were used. The corrosion rate in NaCl 0,6 M was higher than in Na2SO4 0,1 M for all samples. The increase of the plastic deformation led to alloy corrosion resistance decrease, due to the internal stresses increase and the arising of less dense grain preferred orientations of lower planar density as (200) and (220) orientations. The recristallyzed samples presented in a general way a higher corrosion resistance, when compared to the non recristallyzed samples, being imputed to the internal tension relieve and the extinction of the plane (220) of lower planar density to a structure of random orientation.

Aspersão térmica é um processo de produção de revestimentos com ampla aplicação industrial, utilizado na proteção de superfícies contra a corrosão e/ou o desgaste. Os setores aeronáutico e de moldes plásticos estão entre os que utilizam essa técnica para ampliação da vida útil de seus componentes. Este trabalho teve como objetivo avaliar a influência do processo de deposição de revestimentos metálicos (1248 T - Co-28,5%Mo-17,5%Cr-3,4%Si e 1256 F - Co-28%Cr-4%W-3%Ni-3%Fe), cerâmicos (CRO 192 - Cr2O3-5%SiO2-3%TiO2 e 25030 - TiO2-8%Al2O3) e composto (1342 - WC-12%Co), aspergidos pelas técnicas de combustão por chama convencional (cerâmicos) e HVOF (metálicos e composto), no substrato constituído de uma liga de alumínio AA 7475 endurecida por precipitação, visando o melhoramento de suas características tribológicas (desgaste e corrosão), sem alterar as propriedades mecânicas. A influência do processo no substrato foi avaliada por meio de ensaios de microdureza Vickers, microestruturais e de composição química. A resistência ao desgaste foi avaliada por meio de ensaios de desgaste microabrasivo com esfera, com o uso de uma solução abrasiva de alumina (Al2O3). A avaliação da resistência à corrosão de revestimentos e substrato foi realizada por meio de ensaios de polarização potenciodinâmica em meio de NaCl 3,5%. A deposição dos revestimentos por aspersão térmica não afetou significativamente a dureza, composição química e microestrutura do substrato constituído pela liga de alumínio, tornando viável a aplicação dessa técnica a essa classe de ligas. Os revestimentos foram altamente eficientes na proteção do substrato contra o desgaste microabrasivo, sendo que o revestimento constituído de WC-Co (1342) apresentou o melhor desempenho dentre eles. Quanto à corrosão, todos os revestimentos apresentaram resistênciassuperiores a do substrato, tendo o revestimento Co-Cr-W-Fe-Ni (1256 F) apresentado o melhor desempenho geral. Portanto, os revestimentos produzidos por aspersão térmica são alternativas altamente promissoras para o melhoramento tribológico das ligas de alumínio envelhecidas, sem o comprometimento de suas características mecânicas. / The thermal spray process is used in the production of coatings with a wide range of industrial application such as protection of surfaces against corrosion and/or wear. The aircraft and plastic molds industries are among the ones that use this technique to increase the useful life of components. This work aimed to evaluate the influence of the deposition process of metallic (1248 T Co-28.5%Mo-17.5%Cr-3.4%Si and 1256 F Co-28%Cr-4%W-3%Ni- 3%Fe), ceramic (CRO 192 Cr2O3-5%SiO2-3%TiO2 and 25030 TiO2-8%Al2O3) and composite (1342 WC-12%Co) coatings, deposited by flame spray (for the ceramic) and HVOF (for the metallic and composite) techniques, on the substrate of precipitation-hardened AA 7475 aluminum alloy, intended to improve the tribological characteristics (wear and corrosion), without changing its mechanical properties. The influence of the process on the substrate was measured by Vickers microhardness, microstructural tests and chemical analyses. The wear resistance was evaluated by the calowear microabrasive test, using abrasive slurry of alumina (Al2O3). The corrosion resistance evaluation of coatings and substrate was carried out using the potentiodynamic polarization test in NaCl 3.5%. The coating deposition by thermal spray did not significantly affect the hardness, chemical composition and microstructure of the aluminum alloy substrate, establishing the feasibility of using this technique on this class of alloys. Coatings were highly efficient in protecting the substrate against microabrasive wear, where of the WC-Co (1342) coating showed the best performance among them. Also, the corrosion resistance of all coatings was higher than that of the substrate of which the Co-Cr-W-Fe-Ni (1256 F) coating presented the best overall performance. Therefore, the coatings produced by thermal spray are a highly promising alternative for the improvement of the tribological properties of aged aluminum alloys, without compromising its mechanical characteristics.

Nos últimos anos, a indústria de O&G tem enfrentado um considerável desafio no que tange a obtenção de materiais que associem elevada resistência à corrosão às propriedades mecânicas para exploração dos poços das bacias do Pré-Sal. Estes poços apresentam elevadas concentrações de CO2, H2S e cloretos de forma que a resistência à corrosão é uma necessidade. De outro lado, as elevadas profundidades de exploração acopladas com a necessária produtividade têm indicado que a pressão de trabalho destes materiais tende a aumentar. O desafio atualmente reside na obtenção de materiais para fabricação de peças de grandes dimensões como conectores e cabeças de poços. Uma das soluções mais promissoras para a solução deste desafio é a liga UNS N06625, visto que esta liga já é utilizada na indústria de O&G em aplicações nas quais a elevada resistência à corrosão é associada com resistência mecânica. A liga UNS N06625 é tipicamente vista pelo mercado como uma liga monofásica austenítica devido ao uso mais frequente ser associado com peças de pequenas dimensões, barras e arames para soldas e revestimentos, tipicamente tratadas em acordo com as normas ASTM B446 e ASTM B564. A obtenção desta liga na condição monofásica está associada com facilidades associadas com o tratamento termomecânico de peças de pequenas dimensões que aquecem e resfriam com elevadas taxas possibilitando atingir elevado refino de grão em uma estrutura monofásica. O presente trabalho estudou de forma controlada o efeito do teor de ferro na microestrutura e propriedades da liga UNS N06625. Foram avaliados os estados bruto de forjamento, solubilizado e envelhecido de forma a determinar o efeito do teor de ferro no diagrama TTT da liga UNS N06626. Através deste trabalho foi possível se observar que a cinética de precipitação da fase delta e do carboneto do tipo M6C sofrem alterações com o aumento do teor de ferro de forma a reduzir o tempo para precipitação. Adicionalmente foi realizado um estudo do efeito de rampas de aquecimento no tratamento de solubilização, partindo-se do estado conformado a quente, indicando que há um efeito sinérgico entre o encruamento e a precipitação de fase delta durante o aquecimento para o patamar de solubilização resultando sem severa alteração das resistências à corrosão e mecânica da liga. / Lately, the O&G industry has faced a big challenge to find materials that couple the high corrosion resistance with the desired mechanical resistance, for application in the oil and gas wells of the Pre-salt basins. This wells present high CO2, H2S and chlorine contents and the high corrosion resistance is essential. On the other hand, the high exploration depth associated with the necessary productivity has signalized that the working pressure of the materials will increase. Todays challenge is to obtain materials to manufacture large section parts as well heads and connectors. One of the more promising solutions to this challenge is the UNS N06625 alloy, as this alloy is already applied on the O&G industry in applications were the corrosion resistance must be coupled with the mechanical resistance. UNS N06625 alloy is typically understood by the market as an austenitic monophasic alloy, due to the more frequent use to be related with small section parts as bars, rods and wires for coating and welding, usually heat treated in accord with ASTM B446 and ASTM B564. The manufacture of this alloy in the monophasic condition is related to the conveniences of the thermomechanical treatment of small section parts that heat and cool at high rates, which allows high grain refinement and the monophasic structure. The present work has studied in a controlled way the iron content effect on the microstructure and properties of UNS N06625 alloy. UNS N06625 alloy was evaluated in the as forged, solution annealed and aged conditions in order to determine the effect of the iron content on the TTT diagram of UNS N06625 alloy. Through this work it was possible to verify that the kinetic of precipitation of delta phase and M6C carbide present some changes with the increase of the iron content by the reduction of the time needed to precipitation. Additionally the effect of the heating rate in the solution annealing heat treatment was studied, beginning in the as hot forged/rolled conditions which indicate that there is a synergic effect of the hardening and the delta phase precipitation during the heating of the material from the room temperature to the solution annealing temperature resulting in severe changes in the corrosion and mechanical resistances of the alloy.

Este trabalho avaliou o comportamento eletroquímico de três ligas de níquel-cromo e duas de cobalto-cromo in vitro e in vivo. Nos estudos in vitro foram fabricados eletrodos de trabalho a partir destas ligas. Estes eletrodos ficaram imersos em meio de NaCl 0,15 mol.L-1 a 36,5°C e foram submetidos às técnicas do potencial de circuito aberto, polarização potenciostática anódica e cronoamperometria. Para os estudos in vivo foram selecionados quinze pacientes com implantes já osseointegrados e aguardando a instalação das próteses. Esses pacientes foram distribuídos aleatoriamente em cinco grupos, correspondentes às cinco ligas diferentes. Deste modo, as estruturas protéticas dos implantes foram fundidas utilizando as cinco ligas. Foi utilizada a microscopia eletrônica de varredura (MEV) e a espectroscopia por dispersão de energia (EDS) como métodos de análise das superfícies linguais metálicas das próteses, antes da instalação em ambiente oral e após seis meses de permanência. Vistas por MEV, as ligas duas de cobalto-cromo Starloy C e Remanium 2001 e duas de níquel-cromo Wiron 99 e Remanium CSe apresentaram superfícies heterogêneas caracterizadas por uma fase semelhante à matriz da liga e a outra fase, composta por elementos de maior densidade atômica, correspondente à fase interdendrítica. Após seis meses, não houve sinais de corrosão e alterações significativas na composição destas ligas. As ligas de Co-Cr avaliadas, sob o ponto de vista eletroquímico, indicam comportamento catódico quando unidas ao implante sendo um fator indicativo de proteção à corrosão. Dentro dos limites dos estudos in vitro, as ligas de Ni-Cr apresentaram um filme passivo com ampla faixa de potencial em que se mantêm passiva e ausência de corrosão localizada. A liga de níquel-cromo Dan Ceramalloy apresentou a superfície heterogênea com quatro áreas distintas (área 1 rica em titânio; área 2 rica em níquel; área 3 correspondente à matriz; área 4 rica em molibdênio). Após seis meses, as três próteses metalo-cerâmicas apresentaram as regiões correspondentes à fase 2, rica em níquel, com depressões em baixo relevo, sugerindo a oxidação com a liberação de íons níquel. Nos estudos in vitro a liga Dan Ceramalloy apresenta potencial de corrosão mais negativo, uma faixa passiva de potencial mais estreita e um filme menos protetor, quando comparada com as demais ligas estudadas. Apesar de não ter sido observado clinicamente o processo de corrosão das ligas, os estudos in vitro e in vivo deste material, permitiram verificar o seu comportamento eletroquímico e sugerir a descontinuidade do seu emprego em estruturas protéticas de implantes orais. Os estudos in vitro e in vivo apresentaram concordância para todos os materiais estudados. / In this study, the electro-chemical behavior of three nickel-chrome and two cobalt chrome alloys was studied in vitro and in vivo. In the in vitro studies, working electrodes made of these alloys were fabricated. These electrodes were immersed in a medium of NaCl 0.15 mol.L-1 at 36.5°C and were submitted to the open circuit potential, anodic potentiostatic polarization and chronoamperometry techniques. For the in vivo studies, 15 patients whose implants had osseointegrated, and who were waiting for dental implant placement, were selected. These patients were randomly distributed into five groups, corresponding to the five different alloys. Thus the prosthetic implant superstructures were cast, using the five alloys. Scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used as methods to analyze the metal lingual surfaces of the prostheses, before they were placed in the oral environment, and after six months in place. Visualized by SEM, the two cobalt-chrome alloys Starloy C and Remanium 2001, and two types of nickel-chrome - Wiron 99 and Remanium Cse - presented heterogeneous surfaces characterized by a phase similar to that of the alloy matrix, and the other phase composed of elements of greater atomic density, corresponding to the interdendritic phase. After six months, there were no signs of corrosion and significant alterations in the composition of these alloys. The Co-Cr alloys evaluated, from an electrochemical point of view, indicated a cathodic behavior when united to the implant, this being a factor indicative of protection against corrosion. Within the limits of the in vitro studies, the Ni-Cr alloys presented a passive film with an ample range of potential in which they remained passive, with absence of corrosion due to pitting. The nickel-chrome alloy Dan Ceramalloy presented a heterogeneous surface with four distinct areas (Area 1 rich in titanium; Area 2 rich in nickel; Area 3 corresponding to the matrix; Area 4 rich in molybdenum). After six months, the three metal-ceramic dental prostheses presented the regions corresponding to Phase 2, rich in nickel, with depressions in low relief, suggesting oxidation with nickel ion release. In the in vitro studies, the alloy Dan Ceramalloy presented a more negative corrosion potential, a narrower range of passive potential and a less protective film, when compared with the other alloys studied. In despite of the process of corrosion of the alloys not having been clinically observed, the in vitro and in vivo studies of this material allowed verification of its electrochemical behavior, and suggest that its use in prosthetic superstructures for oral implants should be discontinued. The in vitro and in vivo studies were shown to be in agreement for all the materials studied.

As ligas Ti-??constituem um grupo promissor de ligas de titânio em termos de processamento, propriedades e aplicações potenciais. Além do projeto da liga em termos de composição, a obtenção de microestruturas adequadas por meio de tratamentos térmicos é necessária para otimizar o balanço entre resistência mecânica e tenacidade. O presente trabalho teve por objetivo estudar o comportamento em fadiga de alto ciclo da liga Ti-13V-11Cr-3Al, uma liga de alta resistência mecânica destinada ao emprego na indústria aeroespacial, sob duas condições de tratamento. O material foi recebido na forma de barras com 7,6 mm de diâmetro, apresentando microestrutura composta por grãos alongados e propriedades em tração combinando alto limite de resistência (1.479 MPa) e razoável ductilidade (deformação verdadeira de fratura igual a 0,217). O material foi tratado termicamente em duas condições: recozimento a vácuo a 750?C por 1 h com resfriamento lento, e tratamento flash em banho de sal a 650?C por 6 min, com posterior têmpera em água. O tratamento flash resultou em melhor combinação de resistência mecânica e ductilidade, avaliadas pelo ensaio de tração. O estudo da resistência à fadiga baseou-se na obtenção de curvas ?/N por meio de ensaios de flexão rotativa (R = -1) empregando-se corpos de prova do tipo viga em balanço. Para cada condição microestrutural, foram obtidas duas curvas ?/N, uma com amostras polidas e outra empregando-se corpos de prova com concentradores de tensão geométricos (entalhes), visando avaliar a sensibilidade ao entalhe desta liga nas duas condições microestruturais. O material submetido ao tratamento flash apresentou maior dispersão e menor resistência à fadiga, comparado ao material recozido; no entanto apresentou também menor sensibilidade ao entalhe em vidas longas (106 ciclos). O trabalho foi complementado por exames fractográficos para a identificação dos pontos de iniciação da fratura. / The Ti-??alloys are a promising group of titanium alloys in terms of processing, properties and potential applications. In order to achieve the optimum balance between strength and toughness it is necessary, besides determining a proper composition in the alloy design, to obtain suitable microstructures by means of thermo-mechanical process and heat treatment. This study aimed to assess the high cycle fatigue behavior of Ti-13V-11Cr- 3Al alloy, a high-strength alloy intended for use in the aerospace industry. The material was received in the form of bars with 7.6 mm in diameter, whose microstructure comprises elongated grains and whose mechanical properties combines high tensile strength (1,479 MPa), and reasonable ductility (true strain fracture equal to 0.217). The material was heat treated in two conditions: vacuum annealing at 750?C for 1 h with slow cooling, and flash 650?C salt bath for 6 min with subsequent water quenching. The study was based on obtaining ??/ N curves through by rotary bending (R = -1) fatigue tests employing cantilever beam specimens. For each microstructural condition, two ??/ N curves were obtained, the former with smooth samples and the latter employing specimens with geometric stress concentrators (notches), to evaluate the notch sensitivity of this alloy in both microstructural conditions. The material subjected to flash treatment showed greater dispersion and lower fatigue strength compared to annealed; however also showed lower notch sensitivity at long life (106 cycles). The study was complemented by fractographics analysis to identify the fracture initiation points.