Berlin, Humboldt-Universiẗat, Diss., 2002.

Universiẗat, Diss., 2004--Würzburg.

Universiẗat, Diss., 2003--Marburg.

The present thesis deals with surface treatment, material improvement, and the electronic structure of the diluted magnetic semiconductor (Ga,Mn)As. The two key issues are the preparation of clean surfaces and the observation of potential valence hybridizations in (Ga,Mn)As by means of photoemission spectroscopy. Several cleaning methods are applied individually to (Ga,Mn)As and their e ects are compared in detail by various methods. Based on the results of each method, a sophisticated recipe has been elaborated, which provides clean, stoichiometric, and reconstructed surfaces, even if the sample was exposed to air prior to preparation. Moreover, the recipe works equally well for intentionally oxidized surfaces. The individual advantages of ex-situ wet- chemical etching and in situ ion-milling and tempering can be combined in an unique way. In regard to the post-growth annealing in order to optimize the electronic and magnetic properties of (Ga,Mn)As, the effect of surface segregation of interstitial Mn was quantifed. It turns out that the Mn concentration at the surface increases by a factor 4.3 after annealing at 190 C for 150 h. The removal of the segregated and oxidized species by wet-chemical etching allows a tentative estimate of the content of interstitial Mn. 19-23% of the overall Mn content in as-grown samples resides on interstitial positions. The complementary results of core level photoemission spectroscopy and resonant photoemission spectroscopy give hints to the fact that a sizeable valence hybridization of Mn is present in (Ga,Mn)As. This outlines that the simple Mn 3d5-con guration is too naive to refect the true electronic structure of substitutional Mn in (Ga,Mn)As. Great similarities in the core level spectra are found to MnAs. The bonding is thus dominantly of covalent, not ionic, character. Transport measurements, in particular for very low temperatures (<10 K), are in agreement with previous results. This shows that at low temperature, the conduction is mainly governed by variable-range hopping which is in line with the presence of an impurity band formed by substitutional Mn. In the light of the presented results, it is therefore concluded that a double-exchange interaction is the dominant mechanism leading to ferromagnetic coupling in (Ga,Mn)As. The valence hybridization and the presents of an impurity band, both of which are inherent properties of substitutional Mn, are indications for a double-exchange scenario, being at variance to a RKKY-based explanation. Contributions from a RKKY-like mechanism cannot definitely be excluded, however, they are not dominant. / Die vorliegende Arbeit befasst sich mit der Oberflächenbehandlung, der Materialoptimierung und der elektronischen Struktur des verdünnten magnetischen Halbleiters (Ga,Mn)As. Die beiden Hauptaspekte sind dabei die Präparation sauberer Oberflächen und die Identifikation einer möglichen Valenzhybridisierung in (Ga,Mn)As mithilfe von Photoemissionspektroskopie. Mehrere Reinigungsmethoden wurden einzeln auf (Ga,Mn)As Oberflächen angewandt und deren Wirkung anhand mehrerer Untersuchungsmethoden verglichen. Basierend auf den Einzelergebnissen wurde eine spezielle Reinigungsprozedur ausgearbeitet, welche stöchiometrische, reine und wohldefinierte Oberflächen liefert, selbst wenn die Proben Umgebungsluft ausgesetzt wurde. Die beschriebene Vorgehensweise funktioniert des Weiteren auch bei absichtlich oxidierten Proben. Hierbei werden die individuellen Vorteile von ex situ nass-chemischen Ätzen, in situ Ionenstrahlätzen und Erhitzen auf besondere Art und Weise kombiniert. Im Hinblick auf das Ausheilen nach dem Wachstum konnte die Oberflächensegregation von interstitiellem Mangan quantifiziert werden, wobei sich zeigte, dass die Mangankonzentration an der Oberfläche um einen Faktor 4.3 nach 150 Stunden Ausheilen an Luft zunahm. Ein Vergleich zwischen ausgeheilten und anschließend geätzen Proben lässt eine vorsichtige Abschätzung des Anteils an interstitiellem Mangan in nicht ausheilten Proben zu. Hierbei zeigt sich, dass sich 19-23% das Gesamtgehalts an Mangan auf interstitiellen Gitterplätzen befindet. Komplementäre Untersuchungen mit Photoemissionsmethoden an Rumpfniveaus und mithilfe resonanter Photoemission geben Hinweis darauf, dass für Mangan in (Ga,Mn)As eine Valenzhybridisierung vorliegt. Dies führt zu dem Schluss, dass die simple Annahme eines zweifach positiv geladenen Mn-Atoms in 3d5-Kon guration zu pauschal ist, um die tatsächliche elektronische Struktur von substitutionellem Mn in (Ga,Mn)As widerzuspiegeln. Die Spektren zeigen eine große Ähnlichkeit zu Manganarsenid, was beweißt, dass die Bindung vorherrschend kovalenter und nicht ionischer Natur ist. Darüber hinaus sind ebenfalls durchgeführte Transportmessungen im Einklang mit bereits veröffentlichten Ergebnissen aus der Literatur. Dabei zeigt sich, dass der Ladungstransport, vor allem bei tiefen Temperaturen unterhalb von 10 K, durch variable range hopping statt findet. Dieses Verhalten steht im Einklang mit dem Vorhandensein eines Störstellenbandes, welches von substitutionellem Mn gebildet wird. Angesichts der hier gezeigten Daten kann gefolgert werden, dass ein Doppelaustausch der ausschlaggebende Mechanismus für das Auftreten ferromagnetischer Kopplung in (Ga,Mn)As ist. Sowohl die Valenzhybridisierung substitutionellem Mn als auch die Ausbildung eines Störstellenbandes durch selbiges, deuten auf einen Doppelaustausch in, was im Gegensatz zu einer RKKY-basierten Erklärung steht. Hierbei kann ein gewisse Bedeutung des RKKY-Modells nicht vollständig ausgeschlossen werden, jedoch ist diese definitiv nicht dominant.

In der Spintronik bestehen große Bemühungen Halbleiter und ferromagnetische Materialien zu kombinieren, um die Vorteile der hoch spezialisierten Mikroelektronik mit denen der modernen magnetischen Speichertechnologie zu verbinden. In vielen Bereichen der Elektronik wird bereits der III-V Halbleiter GaAs eingesetzt und ferromagnetisches (Ga,Mn)As könnte in die vorhandenen optischen und elektronischen Bauteile integriert werden. Deshalb ist eine intensive Erforschung der kristallinen Qualität, der elektrischen und magnetischen Eigenschaften von (Ga,Mn)As-Legierungsschichten von besonderem Interesse. Wegen der niedrigen Löslichkeit der Mangan-Atome in GaAs, muss (Ga,Mn)As außerhalb des thermodynamischen Gleichgewichtes mit Niedertemperatur-Molekularstrahl-Epitaxie hergestellt werden, um eine ausreichend hohe Konzentration an magnetischen Ionen zu erreichen. Dieses Niedertemperatur-Wachstum von Galliumarseniden verursacht Schwierigkeiten, da unerwünschte Defekte eingebaut werden können. Die Art der Defekte und die Anzahl ist abhängig von den Wachstumsparametern. Vor allem das überschüssige Arsen beeinflusst neben dem Mangan-Gehalt die Gitterkonstante und führt zu einer starken elektrischen und magnetischen Kompensation des (Ga,Mn)As Materials. Abhängig von den Wachstumsparametern wurden Eichkurven zur Kalibrierung des Mangan-Gehaltes aus Röntgenbeugungsmessungen, d. h. aus der (Ga,Mn)As-Gitterkonstanten bestimmt. Um ein besseres Verständnis über die Einflüsse der Wachstumsparameter neben dem Mangan-Gehalt auf die Gitterkonstante zu bekommen, wurden Probenserien gewachsen und mit Röntgenbeugung und Sekundärionen-Massenspektroskopie untersucht. Es wurde festgestellt, dass der Mangan-Gehalt, unabhängig von den Wachstumsparametern, allein vom Mangan-Fluss bestimmt wird. Die Gitterkonstante hingegen zeigte eine Abhängigkeit von den Wachstumsparametern, d. h. von dem eingebauten überschüssigen Arsen in das (Ga,Mn)As-Gitter. Im weiteren wurden temperaturabhängige laterale Leitfähigkeitsmessungen an verschiedenen (Ga,Mn)As-Einzelschichten durchgeführt. Es ergab sich eine Abhängigkeit nicht nur von dem Mangan-Gehalt, sondern auch von den Wachstumsparametern. Neben den Leitfähigkeitsmessungen wurden mit Kapazitäts-Messungen die Ladungsträgerkonzentrationen an verschiedenen (Ga,Mn)As-Schichten bestimmt. Es konnten Wachstumsbedingungen gefunden werden, bei der mit einem Mangan-Gehalt von 6% eine Ladungsträgerkonzentration von 2 · 10^(21) cm^(-3) erreicht wurde. Diese Schichten konnten reproduzierbar mit einer Curie-Temperatur von 70 K bei einer Schichtdicke von 70 nm hergestellt werden. Mit ex-situ Tempern konnte die Curie-Temperatur auf 140 K erhöht werden. Neben (Ga,Mn)As-Einzelschichten wurden auch verschiedene (GaAs/MnAs)- Übergitterstrukturen gewachsen und mit Röntgenbeugung charakterisiert. Ziel was es, Übergitter herzustellen mit einem hohen mittleren Mangan-Gehalt, indem die GaAs-Schichten möglichst dünn und die MnAs-Submonolagen möglichst dick gewachsen wurden. Dünnere GaAs-Schichten als 10 ML Dicke führten unabhängig von der Dicke der MnAs-Submonolage und den Wachstumsparametern zu polykristallinem Wachstum. Die dickste MnAs-Submonolage, die in einer Übergitterstruktur erreicht wurde, betrug 0.38 ML. Übergitterstrukturen mit nominell sehr hohem Mangan-Gehalt zeigen eine reduzierte Intensität der Übergitterreflexe, was auf eine Diffusion der Mangan-Atome hindeutet. Der experimentelle Wert der Curie-Temperatur von (Ga,Mn)As scheint durch die starke Kompensation des Materials limitiert zu sein. Theoretische Berechnungen auf der Grundlage des ladungsträgerinduzierten Ferromagnetismus besagen eine Erhöhung der Curie-Temperatur mit Zunahme der Mangan-Atome auf Gallium-Gitterplätzen und der Löcherkonzentration proportional [Mn_Ga] · p^(1/3). Zunächst wurden LT-GaAs:C-Schichten mit den Wachstumsbedingungen der LT-(Ga,Mn)As-Schichten gewachsen, um bei diesen Wachstumsbedingungen die elektrische Aktivierung der Kohlenstoffatome zu bestimmen. Es konnte eine Löcherkonzentration von 5 · 10^19 cm^(-3) verwirklicht werden. Aufgrund der erfolgreichen p-Dotierung von LT-GaAs:C wurden (Ga,Mn)As-Einzelschichten zusätzlich mit Kohlenstoff p-dotiert. Abhängig von den Wachstumsbedingungen konnte eine Erhöhung der Ladungsträgerkonzentration im Vergleich zu den (Ga,Mn)As-Schichten erreicht werden. Trotzdem ergaben magnetische Messungen für alle (Ga,Mn)As:C-Schichten eine Abnahme der Curie-Temperatur. Der Einfluss der Kohlenstoff-Dotierung auf die Gitterkonstante, die elektrische Leitfähigkeit und die Magnetisierung ließ auf einen veränderten Einbau der Mangan-Atome verursacht durch die Kohlenstoff-Dotierung schließen. / In the field of spintronics there are efforts to combine semiconductors and ferromagnetic materials in order to merge the advantages of highly specialised microelectronics with modern magnetic hard disk technology. The III-V semiconductor GaAs is employed in many electronic circuits and the ferromagnetic (Ga,Mn)As could be integrated in current optical and electronic devices. Therefore an intensive investigation of its crystalline quality and its electrical and magnetic properties is of particular interest. Because of the low solubility of manganese atoms in GaAs, (Ga,Mn)As must be fabricated far from thermal equilibrium with low-temperature molecular beam epitaxy in order to achieve a high concentration of magnetic ions and holes. This low-temperature growth of gallium-arsenide compounds creates difficulties because undesirable defects are built into the host lattice. The type and quantity of defects is dependent on growth parameters. The lattice constant is influenced not only by the manganese concentration, but also by the arsenic excess, which causes a high electrical and magnetic compensation of the (Ga,Mn)As material. Depending on the growth parameters, calibration curves for manganese incorporation were determined from x-ray diffraction, i. e. from the lattice constant of (Ga,Mn)As. To get a better understanding about the influence of growth parameters other than manganese concentration on the lattice constant, we grew several series of samples for investigation by x-ray diffraction and secondary ion mass spectroscopy. It was shown that the manganese concentration is determined only by the manganese flux and is independent of other growth parameters. However the lattice constant shows a dependence on the growth parameters, i. e., on the excess arsenic build into the host lattice (Ga,Mn)As. Furthermore the temperature dependence of the lateral conductivity of different (Ga,Mn)As layers was investigated. A dependence on growth parameters in addition to a dependence on the manganese concentration was observed. Beside these conductivity measurements, capacitance measurements were carried out in order to determine the carrier concentration of various (Ga,Mn)As layers. Growth parameters yielding were determined which resulted in a carrier concentration of 2 × 1021 cm-3 for a manganese concentration of 6 %. Such layers were reproducibly fabricated, with a Curie temperature of 70 K, for a layer thickness of 70 nm. With ex situ annealing it was possible to raise the Curie temperature to 140 K. In addition to (Ga,Mn)As single layers, several (GaAs/MnAs) superlattices were grown and characterized by x-ray diffraction. The aim was to grow superlattices with a high average manganese concentration consisting of thin GaAs layers and thick MnAs submonolayers. GaAs layers thinner than 10 ML lead to polycrystalline growth independent of the thickness of the MnAs submonolayer. The thickest MnAs submonolayer which could be realized was 0.38 ML. Superlattices with a nominally high manganese concentration have reduced satellite peak intensities in x-ray diffraction, indicating a diffusion of the manganese atoms. The experimental value of the (Ga,Mn)As Curie temperature seems to be limited due to strong compensation of the material. Theoretical calculations based on the carrier induced ferromagnetism model predict an increase of the Curie temperature with increasing manganese atoms on gallium sites and with hole concentration following ~ [Mn_Ga] × p^(1/3). Initially, LT-GaAs:C layers were grown with the same parameters as LT-(Ga,Mn)As layers in order to determine the electrical activation of the carbon atoms with these growth parameters. A hole concentration of 5 × 10^(19) cm^(-3) was achieved. Because of the promising p-doping of the LT-GaAs:C several (Ga,Mn)As layers were additionally doped with carbon. Depending on growth parameters, an increase in the hole concentration could be achieved compared to the intrinsic (Ga,Mn)As layers. However magnetisation measurements show a decrease in the Curie temperature for all (Ga,Mn)As:C layers. The influence of the carbon doping on the lattice constant, the electrical conductivity, and the magnetism indicates that the manganese atoms are incorporated into the lattice host differently as result of the carbon doping.

Die vorgelegte Arbeit untersucht den ferromagnetischen Halbleiter (Ga,Mn)As mit seinen komplexen Eigenschaften im Hinblick auf die Optimierung der Materialeigenschaften sehr dünner (4 nm) (Ga,Mn)As Schichten, welche mit der Technologie der Molekularstrahlepitaxie (MBE) hergestellt wurden. Zuerst werden die strukturellen, ferromagnetischen und elektrischen Eigenschaften von (Ga,Mn)As vorgestellt. Die Einflüsse von Punktdefekten, Grenzflächen- und Oberflächen-Effekten auf dicke und dünne (Ga,Mn)As Schichten werden mit Hilfe von vereinfachten, selbstkonsistenten Berechnungen der Bandkantenverläufe diskutiert. Der Experimental-Teil ist in drei Teile unterteilt: Der erste Teil untersucht den Einfluss der epitaktischen Wachstumsbedingungen auf die elektrischen und magnetischen Eigenschaften von dicken (70 nm) (Ga,Mn)As Schichten. Der zweite Teil führt ein alternatives, parabolisches Mn-Dotierprofil mit effektiver Schichtdicke von 4 nm ein im Vergleich zu einer gleich dünnen Schicht mit homogenem Mn-Dotierprofil. Es konnten einerseits verbesserte Eigenschaften dieser parabolischen Schicht erreicht werden, anderseits sind die magnetischen und elektrischen Eigenschaften vergleichbar zu dicken (Ga,Mn)As Schichten mit gleichem Mn-Gehalt von 4%. MBE Wachstumsbedingungen für (Ga,Mn)As Schichten mit parabolischem Mn-Dotierprofil und verringertem nominellem Mn-Gehalt von 2.5% wurden ebenfalls untersucht. Ein schmales Wachstumsfenster wurde hierbei ermittelt, in dem die Tieftemperatur-Eigenschaften verbessert sind. Der letzte Teil der Arbeit präsentiert eine Anwendung der magnetischen Anisotropiekontrolle einer dicken (Ga,Mn)As Schicht. / The present thesis studies the (Ga,Mn)As material in terms of optimization of very thin (4 nm) (Ga,Mn)As layers, epitaxially fabricated by the molecular beam epitaxy (MBE) technology. First of all, the ferromagnetic semiconductor (Ga,Mn)As with its structural, magnetic and electrical properties is introduced. The influences of point defects, interface and surface effects on bulk and thin (Ga,Mn)As layers are discussed by simplified self-consistent band alignment calculations. The experimental part is divided in three blocks: The first part studies the influence of epitaxial growth parameter conditions on electrical and magnetic properties of bulk (70 nm) (Ga,Mn)As layers. The second part introduces an alternative, parabolical Mn doping-profile instead of a 4 nm layer with a homogeneous Mn doping-profile. Improved properties of the parabolic layer have been observed as well as comparable magnetic and electrical properties to bulk (Ga,Mn)As layers, both with a Mn content of 4%. MBE growth parameters for the (Ga,Mn)As layers with a parabolically graded Mn profile and lowered nominal Mn content of 2.5% have been investigated. A narrow growth window has been found in which low-temperature (LT) layer properties are improved. The last part of this thesis presents an application of magnetic anisotropy control of a bulk (Ga,Mn)As layer.

University, Diss., 2005--Würzburg.

This work is an investigation of giant magnetoresistance (GMR), tunneling magnetoresistance (TMR) and tunneling anisotropic magnetoresistance (TAMR)effects in (Ga,Mn) based ferromagnetic semiconductor junctions. Detailed results are published in the following articles: [1] C. Rüster, T. Borzenko, C. Gould, G. Schmidt, L.W. Molenkamp, X. Liu, T.J.Wojtowicz, J.K. Furdyna, Z.G. Yu and M. Flatt´e, Very Large Magnetoresistance in Lateral Ferromagnetic (Ga,Mn)As Wires with Nanoconstrictions, Physical Review Letters 91, 216602 (2003). [2] C. Gould, C. Rüster, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling Anisotropic Magnetoresistance: A Spin-Valve-Like Tunnel Magnetoresistance Using a Single Magnetic Layer, Physical Review Letters 93, 117203 (2004). [3] C. Rüster, C. Gould, T. Jungwirth, J. Sinova, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Very Large Tunneling Anisotropic Magnetoresistance of a (Ga,Mn)As/GaAs/(Ga,Mn)As Stack, Physical Review Letters 94, 027203 (2005). [4] C. Rüster and C. Gould, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling anisotropic magnetoresistance: Creating a spin-valve-like signal using a single ferromagnetic semiconductor layer, Journal of Applied Physics 97, 10C506 (2005). / Diese Arbeit enthält Untersuchungen von Magnetowiderstandseffekten in (Ga,Mn)As basierten ferromagnetischen Halbleiterdioden. Die Resultate wurden in den folgenden Artikeln veröffentlicht: [1] C. Rüster, T. Borzenko, C. Gould, G. Schmidt, L.W. Molenkamp, X. Liu, T.J.Wojtowicz, J.K. Furdyna, Z.G. Yu and M. Flatt´e, Very Large Magnetoresistance in Lateral Ferromagnetic (Ga,Mn)As Wires with Nanoconstrictions, Physical Review Letters 91, 216602 (2003). [2] C. Gould, C. Rüster, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling Anisotropic Magnetoresistance: A Spin-Valve-Like Tunnel Magnetoresistance Using a Single Magnetic Layer, Physical Review Letters 93, 117203 (2004). [3] C. Rüster, C. Gould, T. Jungwirth, J. Sinova, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Very Large Tunneling Anisotropic Magnetoresistance of a (Ga,Mn)As/GaAs/(Ga,Mn)As Stack, Physical Review Letters 94, 027203 (2005). [4] C. Rüster and C. Gould, T. Jungwirth, E. Girgis, G.M. Schott, R. Giraud, K. Brunner, G. Schmidt and L.W. Molenkamp, Tunneling anisotropic magnetoresistance: Creating a spin-valve-like signal using a single ferromagnetic semiconductor layer, Journal of Applied Physics 97, 10C506 (2005).

The study of magnetic phases in spintronic materials is crucial to both our fundamental understanding of magnetic interactions and for finding new effects for future applications. In this thesis, we study the basic electrical and magnetic transport properties of both epitaxially-grown MnSi thin films, a helimagnetic metal only starting to be developed within our group, and parabolic-doped ultra-thin (Ga,Mn)As layers for future studies and applications. / Um einerseits ein fundamentales Verständnis magnetischer Wechselwirkungen zu erhalten und andererseits neue Effekte für zukünftige Anwendungen zu finden, ist es entscheidend, magnetische Phasen spintronischer Materialien zu untersuchen. In dieser Arbeit fokussieren wir uns auf grundlegende elektrische und magnetische Transporteigenschaften zweier Materialsysteme. Das sind zum Ersten ultradünne (Ga,Mn)As Filme mit parabolischen Dotierprofilen, und zum Zweiten epitaktisch gewachsene Dünnschichten aus MnSi, einem helimagnetischen Metal, dessen Entwicklung seit Kurzem in unserer Gruppe vorangetrieben wird.

The discovery of the Giant Magneto Resistance (GMR) effect in 1988 by Albert Fert [Baib 88] and Peter Grünberg [Bina 89] led to a rapid development of the field of spintronics and progress in the information technology. Semiconductor based spintronics, which appeared later, offered a possibility to combine storage and processing in a single monolithic device. A direct result is reduced heat dissipation. The observation of the spin Seebeck effect by Ushida [Uchi 08] in 2008 launched an increased interest and encouraged research in the field of spin caloritronics. Spintronics is about the coupling of charge and spin transport. Spin caloritronics studies the interaction between heat and spin currents. In contrast to spintronics and its variety of applications, a particular spin-caloritronic device has not yet been demonstrated. However, many of the novel phenomena in spin caloritronics can be detected in most spintronic devices. Moreover, thermoelectric effects might have a significant influence on spintronic device operation. This will be of particular interest for this work. Additional knowledge on the principle of coupling between heat and spin currents uncovers an alternative way to control heat dissipation and promises new device functionalities. This thesis aims to further extend the knowledge on thermoelectrics in materials with strong spin-orbit coupling, in this case the prototypical ferromagnetic semiconductor (Ga,Mn)As. The study is focused on the thermoelectric / thermomagnetic effects at the interface between a normal metal and the ferromagnetic (Ga,Mn)As. In such systems, the different interfaces provide a condition for minimal phonon drag contribution to the thermal effects. This suggests that only band contributions (a diffusion transport regime) to these effects will be measured. Chapter 2 begins with an introduction on the properties of the studied material system, and basics on thermoelectrics and spin caloritronics. The characteristic anisotropies of the (Ga,Mn)As density of states (DOS) and the corresponding magnetic properties are described. The DOS and magnetic anisotropies have an impact on the transport prop- erties of the material and that results in effects like tunneling anisotropic magnetores- istance (TAMR) [Goul 04]. Some of these effects will be used later as a reference to the results from thermoelectric / thermomagnetic measurements. The Fingerprint tech- nique [Papp 07a] is also described. The method gives an opportunity to easily study the anisotropies of materials in different device geometries. Chapter 3 continues with the experimental observation of the diffusion thermopower of (Ga,Mn)As / Si-doped GaAs tunnel junction. A device geometry for measuring the diffusion thermopower is proposed. It consists of a Si - doped GaAs heating channel with a Low Temperature (LT) GaAs / (Ga,Mn)As contact (junction) in the middle of the channel. A single Ti / Au contact is fabricated on the top of the junction. For transport characterization, the device is immersed in liquid He. A heating current technique is used to create a temperature difference by local heating of the electron system on the Si:GaAs side. An AC current at low frequency is sent through the channel and it heats the electron population in it, while the junction remains at liquid He temperature (experimentally con- firmed). A temperature difference arises between the heating channel and the (Ga,Mn)As contact. As a result, a thermal (Seebeck) voltage develops across the junction, which we call tunnelling anisotropic magneto thermopower (TAMT), similar to TAMR. TAMT is detected by means of a standard lock-in technique at double the heating current frequency (at 2f ). The Seebeck voltage is found to be linear with the temperature difference. That dependence suggests a diffusion transport regime. Lattice (phonon drag) contribution to the thermovoltage, which is usually highly nonlinear with temperature, is not observed. The value of the Seebeck coefficient of the junction at 4.2 K is estimated to be 0.5 µV/K. It is about three orders of magnitude smaller than the previously reported one [Pu 06]. Subsequently, the thermal voltage is studied in external magnetic fields. It is found that the thermopower is anisotropic with the magnetization direction. The anisotropy is explained with the anisotropies of the (Ga,Mn)As contact. Further, switching events are detected in the thermopower when the magnetic field is swept from negative to positive fields. The switchings remind of a spin valve signal and is similar to the results from previous experiments on spin injection using a (Ga,Mn)As contacts in a non-local detection scheme. That shows the importance of the thermoelectric effects and their possible contribution to the spin injection measurements. A polar plot of the collected switching fields for different magnetization angles reveals a biaxial anisotropy and resembles earlier TAMR measurements of (Ga,Mn)As tunnel junction. A simple cartoon model is introduced to describe and estimate the expected thermopower of the studied junction. The model yields a Fermi level inside of the (Ga,Mn)As valence band. Moreover, the model is found to be in good agreement with the experimental results. The Nernst effect of a (Ga,Mn)As / GaAs tunnel junction is studied in Chapter 4. A modified device geometry is introduced for this purpose. Instead of a single contact on the top of the square junction, four small contacts are fabricated to detect the Nernst signal. A temperature difference is maintained by means of a heating current technique described in Chapter 3. A magnetic field is applied parallel to the device plane. A voltage drop across two opposite contacts is detected at 2f. It appears that a simple cosine function with a parameter the angle between the magnetization and the [100] crystal direction in the (Ga,Mn)As layer manages to describe this signal which is attributed to the anomalous Nernst effect (ANE) of the ferromagnetic contact. Its symmetry is different than the Seebeck effect of the junction. For the temperature range of the thermopower measurements the ANE coefficient has a linear dependence on the temperature difference (∆T). For higher ∆T, a nonlinear dependence is observed for the coefficient. The ANE coefficient is found to be several orders of magnitude smaller than any Nernst coefficient in the literature. Both the temperature difference and the size of the ANE coefficient require further studies and analysis. Switching events are present in the measured Nernst signal when the magnetic field is swept from positive to negative values. These switchings are related to the switching fields in the ferromagnetic (Ga,Mn)As. Usually, there are two states which are present in TAMR or AMR measurements - low and high resistance. Instead of that, the Nernst signal appears to have three states - high, middle and low thermomagnetic voltage. That behaviour is governed not only by the magnetization, but also by the characteristic of the Nernst geometry. Chapter 5 summarizes the main observations of this thesis and contains ideas for future work and experiments. / Die Entdeckung des Riesenmagnetowiderstands (GMR)-Effekts im Jahr 1988 von Albert Fert [Baib 88] und Peter Grünberg [Bina 89] führte zu einer raschen Entwicklung auf dem Gebiet der Spintronik und damit zu Fortschritten in der Informations-Technologie. Der darauf aufbauende Bereich der halbleiterbasierten Spintronik bietet darüber hinaus Möglichkeiten Speicherung und Datenverarbeitung in einem einzigen monolithischen Bauteil zu kombinieren. Eine direkte Folge davon ist eine reduzierte Wärmeableitung. Die Beobachtung des Spin-Seebeck-Effekts von Uchida [Uchi 08] im Jahr 2008 brachte ein erhöhtes Interesse hervor und führte zur Forschung im Bereich der Spin-Caloritronics. Während in der Spintronik die Kopplung von Ladungs-und Spintransport untersucht wird, liegt der Fokus der Spin-Caloritronics auf der Wechselwirkungen zwischen Wärme-und Spinstr¨omen. Im Unterschied zur Spintronik mit ihrer Vielzahl von Anwendungen wurde ein reines Spin-Caloritronics Bauteil noch nicht realiziert. Doch viele der neuen Phänomene in der Spin-Caloritronics können in den meisten Spintronik-Bauteilen auftreten. Darüber hinaus könnten thermoelektrische Effekte einen wesentlichen Einfluss auf den Betrieb der Spintronik-Bauteile haben. Dieser Punkt wird von besonderem Interesse für diese Arbeit sein. Tieferes Verständnis der Prinzipien der Kopplung zwischen Wärme- und Spinströmen kann einen alternativen Weg aufzeigen um die Wärmeableitung zu kontrollieren und verspricht neue Funktionalitäten. Diese Dissertation zielt darauf ab die Kenntnisse über die Thermoelektrik in Materialien mit starker Spin-Bahn-Wechselwirkung zu erweitern, in diesem Fall der prototypische ferromagnetische Halbleiter (Ga,Mn)As. Die Untersuchungen konzentrieren sich auf die thermoelektrischen und -magnetischen Effekte an der Grenzfläche zwischen einem normalen Metall und dem ferromagnetischen (Ga,Mn)As. In solchen Systemen führen die unterschiedlichen Grenzflächen zu einem minimalen Beitrag des Phonon-Drags zu den thermischen Effekten. Dies legt nahe, dass nur Bandbeiträge (ein Diffusionstransport- Regime) auf diese Effekte gemessen werden. Kapitel 2 beginnt mit einer Einführung über die Eigenschaften der untersuchten Materialsysteme, Grundlagen der Thermoelektrik und Spin-Caloritronics. Die charakteristischen Anisotropien der Zustandsdichte (DOS) von (Ga,Mn)As und die dadurch entstehenden magnetischen Eigenschaften werden beschrieben. Die DOS und die magnetische Anisotropie haben einen Einfluss auf die Transporteigenschaften des Materials und führen zu Effekten wie dem anisotropen Tunnelmagnetowiderstand (TAMR) [Goul 04]. Einige dieser Effekte werden im Weiteren als eine Referenz für die Ergebnisse der thermoelektrischen und magnetischen Messungen verwendet. Die Anisotropie- Fingerprintabduck-Technik [Papp 07a] wird ebenfalls beschrieben. Die Methode bietet die Möglichkeit, die Material-Anisotropien in verschiedenen Geometrien einfach zu unter- suchen. Kapitel 3 schließt sich mit der experimentellen Beobachtung der Diffusions - Thermospannung an einer (Ga,Mn)As / Si-dotierten GaAs-Tunnelübergang an. Eine Bauteilgeometrie zur Messung der Diffusions-Thermospannung wird vorgeschlagen. Sie besteht aus einem Si-dotierten GaAs-Heiz-Kanal mit einem GaAs/(Ga,Mn)As-Kontakt in der Mitte des Kanals. Ein einzelner Ti/Au-Kontakt wird an der Oberseite des Übergangs aufgebracht. Die Charakterisierung der Probe erfolgt bei 4.2 K. Ein Wechselstrom mit niedriger Frequenz wird durch den Kanal gesendet und erhöht dadurch dessen Temperatur, während der (Ga,Mn)As-Kontakt bei konstanter Temperatur im Helium-Bad bleibt. Aufgrund der Temperaturdifferenz zwischen dem Heizungskanal und dem (Ga,Mn)As- Kontakt entsteht eine thermische (Seebeck-)Spannung, die wir als anisotrope Tunnelmagnetothermospannung bezeichnen (TAMT), ähnlich dem TAMR. TAMT wird mittels Lock-In-Technik bei der doppelten Frequenz des Heizstroms detektiert. Die Seebeck- Spannung wächst dabei linear mit der Temperaturdifferenz an, was auf das Vorliegen eines reinen Diffusionstransport-Regimes hinweist. Ein Beitrag des Gitters (Phonon-Drag) zur Thermospannung, der in der Regel stark nichtlinear von der Temperatur abhängt, wird nicht beobachtet. Der Wert des Seebeck-Koeffizienten des Übergangs bei 4.2 K wird auf 0.5 µV/K abgeschätzt. Das ist ein um drei Größenordnungen kleinerer Betrag als zuvor von [Pu 06] berichtet. Anschließend wird die thermische Spannung unter Einfluss eines äußeren Magnetfelds untersucht. Es zeigt sich, dass die Thermospannung eine Anisotropie mit der Magnetisierungsrichtung aufweist. Diese Anisotropie wird mit den bekannten Eigenschaften des (Ga,Mn)As-Kontakts erläutert. Ferner werden Schaltvorgänge in der Thermospannung detektiert, wenn das Magnetfeld von negativen zu positiven Werten geändert wird. Die Schaltvorgänge erinnern an die Signale eines Spin-Ventils. Dieses Verhalten ist vergleichbar mit den Ergebnissen aus früheren Experimenten an Spininjektion mithilfe eines (Ga,Mn)As-Kontakts in nicht-lokaler Messgeometrie. Dies betont die Bedeutung der thermoelektrischen Effekte und deren mögliche Auswirkungen auf die Spininjektions-Messungen. Ein Polardiagramm der gesammelten Schaltfelder für verschiedene Magnetisierungswinkel zeigt eine zweiachsige Anisotropie und ähnelt früheren TAMR-Messungen an (Ga,Mn)As-Tunnelbarrieren. Ein einfaches Modell wird zur Beschreibung und Abschätzung der erwarteten Thermospannung am untersuchten Übergang eingeführt. Eine gute Übereinstimmung des Modells mit den experimentellen Ergebnissen ist evident. Der Nernst-Effekt an einem (Ga,Mn)As/GaAs-Kontakt wird im vierten Kapitel untersucht. Hierfür wird eine Modifizierung der Proben-Geometrie vorgenommen. Anstelle des einzelnen Kontakts oberhalb der Übergangsregion werden vier kleine Kontakte hergestellt. Die Temperaturdifferenz wird wiederum mittels Heizkanal gewährleistet. Das Magnetfeld ist parallel zur Probenoberfläche orientiert. Zwischen sich gegenüberliegenden Kontakten wird eine Spannungsdifferenz bei 2f detektiert. Es stellt sich heraus, dass eine Kosinus- Funktion, mit dem Winkel zwischen der Magnetisierung und der [100]-Kristallrichtung der (Ga,Mn)As Schicht als Parameter, das gemessene Signal gut beschreibt. Dieses wird auf den anormalen Nernst-Effekt (ANE) des ferromagnetischen Kontakts zurückgeführt. Die Symmetrie des ANE unterscheidet sich von der des Seebeck- Effekts des Übergangs. Im Temperaturintervall, in dem die Thermo-Spannung untersucht wurde, zeigt auch der ANE-Koeffizient lineares Verhalten mit der Temperaturdifferenz (∆T). Für größere ∆T jedoch zeigt sich eine nichtlineare Abhängigkeit. Der ermittelte ANE Koeffizient ist um mehrere Größenordnungen kleiner als jeder andere veröffentlichte Wert. Sowohl die Temperaturabhängikeit als auch die Größe des ANE bedürfen weiterer Untersuchungen. Wird das Feld von positiven zu negativen Werten gefahren, zeigen sich Schaltvorgänge im Nernst Signal. Diese Schaltvorgänge stehen im Zusammenhang mit den Schaltfeldern des ferromagnetischen (Ga,Mn)As. Normalerweise existieren bei TAMR oder AMR Messungen zwei Zustände, einer mit geringem und einer mit hohem Widerstand. Das gemessene Nernst Signal dagegen zeigt drei Zustände - hohe, mittlere und geringe Thermomagnetische Spannung. Dieses Verhalten ist nicht nur von der Magnetisierung, sondern auch von der Charakteristik der Nernst-Geometrie beeinflusst. Kapitel 5 fasst die wichtigsten Erkenntnisse dieser Arbeit zusammen und gibt einen Ausblick auf zukünftige Arbeiten und Experimente.