101 |
Avaliação da deposição superficial do corante evidenciador de placa bacteriana em materiais hibridos de ionomero de vidro/resina compostaLima, Fernanda Augusta Passianoto de 21 November 1997 (has links)
Orientador: Jose Roberto Lovadino / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontolgia de Piracicaba / Made available in DSpace on 2018-07-23T01:38:54Z (GMT). No. of bitstreams: 1
Lima_FernandaAugustaPassianotode_M.pdf: 2606831 bytes, checksum: 5d64720edff903de70450358b2e6e7b4 (MD5)
Previous issue date: 1997 / Resumo: A proposta deste estudo foi verificar quantitativamente, por meio de espectrofotometria, a influência de uma solução evidenciadora de placa bacteriana na alteração de cor por deposição de corante de dois materiais híbridos de ionômero de vidro / resina composta. Os materiais restauradores utilizados foram: Vitremer, Variglass e a solução de fucsina básica a 0,5 %, usada como evidenciador de placa bacteriana. Foram confeccionados noventa corpos de prova que foram divididos em grupos e imersos em solução corante durante 1 minuto. Para determinar a quantidade de corante depositado sobre as amostras, foram obtidas soluções com a imersão dos corpos de prova em álcool absoluto por 48 horas. As soluções foram levadas ao aparelho de espectrofotometria para leitura de absorbância, regulado com comprimento de onda igual 550 nanômetros. Essas leituras foram submetidas à equações de retas .obtidas com leituras de soluções-padrão conhecidas. O resultado da concentração de corante presente nas soluções foi apresenta<lo em micrograma de corante por mililitro de solução. Esses resultados foram analisados pelo teste Kruskal Wallis e de Comparações Múltiplas, mostrando diferença estatística
significante (a = 0,01 %) entre os tratamentos. Verificou-se que o material híbrido resina composta modificada por poliácido (Variglass) apresentou maior deposição de corante que o híbrido ionômero de vidro modificado por resina (Vitremer). O híbrido ionômero de vidro modificado por resina (Vitremer) não sofreu deposição de corante significante, porém, quando avaliado com o componente de 'acabamento (Finishing Gloss), a deposição foi estatisticamente significante / Abstract: he purpose of this study was to evaluate the influence of the plaque disclosing in the staining of two glass-ionomer / composite resin hybrid materiaIs, by spectrophotometric method. The restorative materiaIs used were: Vitremer, Variglass and the basic fuhcsine solution at 0.5 % as the disclosing agent. Ninety specimens were randomly assigned in 3 equal groups and immersed in plaque disclosing during 1 minute. In order to determine the amount of dye uptake, solutions were obtained with specimens immersion in absolute a1cohol for 48 hours. The solutions were put in the spectrophotometer for absorbance reading and the equipment wavelengh was adjusted to 550 nanometers. The result of dye concentration was given in micrograms dye per millimeter of solution. These results were analysed by Kruskal Wallis Test and Multiple Comparisions Test, showing statistical differences (a = 0.01 %) among the treatments. The polyacid-modified composite resin hybrid (Variglass) presented higher dye uptake than the resin modified glass-ionomer hybrid (Vitremer). The resin-modified glass-. lOnomer (Vitremer) did not show significant staining. However, when the finish component (Finishing Gloss) was used the dye uptake was significant1y higher / Mestrado / Dentística / Mestre em Clínica Odontológica
|
102 |
Potencial antimicrobiano de materiais restauradores contendo fluor, durante a reação de presa e apos hidrataçãoFraga, Ricardo Carvalhaes 21 October 1997 (has links)
Orientador: Luis Roberto Marcondes Martins / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T00:04:28Z (GMT). No. of bitstreams: 1
Fraga_RicardoCarvalhaes_D.pdf: 2772557 bytes, checksum: 0370c405fbc3fe9273a3caad7a507335 (MD5)
Previous issue date: 1997 / Resumo: Foi realizada uma pesquisa in vitro, utilizando-se como método de avaliação a inibição de crescimento microbiano em caldo de cultura, com o intuito de determinar o potencial antibacteriano de materiais restauradores que contém flúor, além de avaliar a relação dessa capacidade com a alteração do pH do meio aquoso circundante, provocada pelos próprios materiais. Avaliou-se a atividade inibitória dos materiais, durante a reação de presa, contra cinco espécies bacterianas (Streptococcus sobrinus, Streptococcus sanguis, Streptococcus salivarius, Streptococcus mutans e Lactobacillus caseI). Foi testada também a capacidade antibacteriana dos materiais após a hidratação dos mesmos por 72 horas, utilizando-se para essa fase da pesquisa apenas duas espécies (S. mutans e S. sanguis). Na terceira fase do experimento mensurou-se a alteração de pH em água destilada, provocada pelos materiais, após a hidratação por 3 minutos, 4 horas e 72 horas. Constatou-se que, quando testados durante a reação de presa, a resina composta com flúor (Tetric) e a resina modificada por poliácidos (Dyract) atuaram de modo semelhante ao grupo controle, representado por uma resina composta sem flúor (Charisma), não apresentando atividade antibacteriana contra as cinco espécies. Os materiais Vidrion N, Vitremer, Chelon-Silver e Chelon-Fil apresentaram ação variada contra o crescimento microbiano nessa fase. Após a hidratação, quando testados contra S.sanguis e S.mutans, o material híbrido Vitremer foi o que apresentou maior ação inibitória contra o crescimento dos microrganismos, seguido pelo Vidrion N e pelo Dyract, que passou nesta fase a possuir ação antimicrobiana. Os ionoméricos Chelon Silver e Chelon-Fil perderam significativamente o potencial antibacteriano, e a resina composta Tetric mostrou uma ação praticamente nula. O Dyract foi o único que apresentou queda do pH do meio, quando realizada a hidratação pelo período de 4 horas, indicando que a acidificação superficial desse material acontece tardiamente pela absorção de água,
podendo, inclusive, estar relacionada com a sua capacidade antibacteriana / Abstract: The aim of this in vitro study was to determine the antibacterial potential of restorative materiais with fluoride-containing. In addition, it was evaluated the relation between antibacterial activity and pH changes on the surrounding aqueous medium of the these materiais. It was evaluated the inhibitory activity of the materiais, during setting reaction, against five bacterial species ( Streptococcus
sObrinus, Streptococcus sanguis, Streptococcus salivarius, Streptococcus mutans and Lactobacillus casei). On .the second phase of the experiment, the materiais were tested on their antibacterial activity afier their hydration for 72 hours, using only two species in this phase (S. mutans and S. sanguis). On the third phase, it was measured the pH alterations in distilled water, caused by the materiais afier hydration for 3 minutes, 4 hours and 72 hours. The composite resin with fluoride-containing (Tetric) and the resin modified by polyacids (Dyract) acted the same effect as the control group represented by a fluoride-free composite resin (Charisma), when tested during setting reaction, not showing any antibacterial effect against the five species. The materiais Vidrion N, Vitremer, Chelon-Silver and Chelon-Fil showed varying action against bacterial growth in this phase. Afier hydration, when tested against S. sanguis and S. mutans, the hybrid material Vitremer showed the highest inhibition action against bacterial growth, followed by Vidrion. N and Dyract, which started showing antimicrobial potential in this phase. The glass ionomers cements Chelon Fil and Chelon-Silver had a relevant loss of antibacterial effects, showing a
similar action of the composite resins. Dyract was the only one to present a pH fali of the environment medium, when hydration happened in a four-hour period, indicating a late superficial acidification of this material by water absorption, which may as well be related to its antibacterial activity / Doutorado / Dentística / Doutor em Clínica Odontológica
|
103 |
Estudo eletromiografico de musculos do sistema estomatognatico durante a mastigação de diferentes materiaisBiasotto, Daniela Aparecida 02 November 2000 (has links)
Orientador: Fausto Berzin / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-26T03:24:01Z (GMT). No. of bitstreams: 1
Biasotto_DanielaAparecida_M.pdf: 2842575 bytes, checksum: feb2616d252c3d3743c0889f8eeb8923 (MD5)
Previous issue date: 2000 / Resumo: O objetivo deste estudo foi comparar o comportamento de alguns dos principais músculos da mastigação (M. temporal, porção anterior, M. masséter e MM. suprahióideos), com a utilização de duas marcas comerciais de goma de mascar A e B e dois materiais insípidos, Rolinho de Algodão e Parafilm.M.@, através de análise dos sinais eletromiográficos. Participaram deste estudo dez (10) voluntários, do sexo feminino, adulto/jovem, com idade variando 18 a 27 anos, com normo oclusão, e sem história de disfunção craniomandibular. A atividade mastigatória foi realizada com o voluntário sentado com o plano de Frankfurt posicionado paralelo ao solo. Para tanto, foram realizados exames eletromiográficos dos mm. temporais, porção anterior e masséteres, bilaterais e supra-hióideos, bilateralmente; utilizando-se mini eletrodos passivos de superfície. Os voluntários foram orientados a mastigar bilateral e simultaneamente cada um dos produtos, em seqüência aleatória. Para o estudo da atividade mastigatória os traçados eletromiográficos foram tratados através de retificação, envoltório linear e normalização, de forma que o coeficiente de variação resultante do processamento fosse analisada comparativamente. Todos os dados foram tratados pela Análise de Variância Univariada e Multivariada. Os resultados do estudo demostrou que não existiu diferença estatística fortemente significativa entre o material Rolinho de Algodão e Parafilm. Estes produtos revelam que no contexto geral ambos são indicados para execução do exame eletromiográfico, pois apresenta menor variação com relação aos demais produtos / Abstract: The purpose of this study was to investigate and to compare the behavior of the chewing muscles (M.Temporales, anterior portion, M.Masseter and M.Suprahyoid), through the use to two chewing gums commercial A and B and two insipid product, Cotton Sal! and Parafilm.M.@, with the objective of analysis of the electromyographyc trace. A total of 10 young adults subjects, of the female sex, with an age ranger from 18 to 27 years, with normal Angle's class I occlusion assessed by intra-oral examination. No signs or symptoms of stomatognathic dysfunctions or other general disease affecting the neuromuscular system were presented. The chewing activity was accomplished with subjects were confortably seat in straight-backed chairs with head unsupported and positioned so that the Frankfort plane was parallel to the floor. For this EMG took place, using bipolar electrodes surface, positioned on the anterior temporal, masseter, bilateral!y, and suprahyod muscles. The subjectives were guided to chew bilaterally and simultaneously each one of the products, in aleatory sequence. For study for the masticatory activity were the electromyographyc signals were processed by fullwave rectification, linear enveloped and normalisation, so that the coefficient of variation (CV%) of chewing activity. The statistic method used was the data based on by the Analysis of Variation. The results of this research demonstrated that didn't exist statistical significant difference between the Cotton Sal! And Parafilm.M.@ / Mestrado / Anatomia / Mestre em Biologia e Patologia Buco-Dental
|
104 |
Influencia do tempo da armazenagem na resistencia ao cisalhamento da união de sistemas adesivos a dentina bovinaKonno, Alysson Noriyuki Kajishima 11 December 2000 (has links)
Orientador: Mario Alexandre Coelho Sinhoreti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T14:08:34Z (GMT). No. of bitstreams: 1
Konno_AlyssonNoriyukiKajishima_M.pdf: 5065610 bytes, checksum: 162774622b59258f8fc8b8e7ba68fa95 (MD5)
Previous issue date: 2000 / Resumo: O objetivo deste trabalho foi avaliar a resistência ao cisalhamento de cinco sistemas de união após 3 períodos de armazenagem (1 dia, 3 meses e 6 meses) e analisar em MEV o aspecto morfológico da superfície da dentina. Foram usadas 150 faces vestibulares de incisivos inferiores bovinos, incluídas em resina de modo que o esmalte ficasse saliente, o qual foi desgastado até expor uma superfície de dentina de aproximadamente 5mm de diâmetro. Um papel adesivo com um orifício no centro com 4mm de diâmetro foi colado sobre a dentina, delimitando a área a ser tratada com os sistemas de união Oearfil Liner Bond 2V (CLB2V); Scotchbond Multi Purpose Plus (SBMP); Optibond Solo (SOLO); Prime & Bond NT (PBNT) e Etch & Prime 3.0(E&P), de acordo com as instruções dos fabricantes. Com o auxílio de uma matriz metálica bipartida foi realizada a restauração, com forma de cilindro (4 mm de diâmetro X 5 mm de altura), sobre a superfície tratada, usando o compósito Z100. Após os períodos de armazenagem em água à 370<:, as amostras foram levadas à máquina Instron para realização do ensaio de cisalhamento com velocidade de 0,5 mm/min. Duas amostras de cada grupo receberam uma cobertura de ouro-paládio, sob alto vácuo, para exame em MEV. Os resultados foram submetidos à análise de variância e as médias comparadas pelo teste de Tukey em nível de 5% de significância. Verificou-se que os sistemas SBMP, PBNT e E&P não apresentaram valores estatisticamente diferentes entre si nos períodos testados. O CLB2V apresentou a maior média no período de 3 meses não diferindo com o período de 6 meses; obtendo também a maior média em todos os períodos testados. O SOLO, apresentou menor média no período de 6 meses, a qual diferiu estatisticamente dos demais períodos. O sistema de união CLB2V apresentou a maior média de resistência ao cisalhamento em todos os períodos de armazenagem / Abstract: The purpose of this study was to evaluate the shear bond strength of 5 bonding systems after 3 storage periods (1 day, 3 months and 6 months) and analyse the morphologic aspect of dentin surface in SEM. It was used 150 buccal faces of bovine inferior incisors embedded in auto-cured acrylic resin with enamel exposed. Teeth were flattened until minimum areas of 5mm in diameter were exposed. An circular adhesive tape with a central hole of 4mm in diameter was placed on dentin in order to mark out the area to be treated with the following adhesive systems: Oearfil Liner Bond 2V, Scotchbond Multi Purpose Plus, Optibond Solo, Prime & Bond NT and Etch & Prime 3.0. The restoration was carried out in a cylindrical shape (5mm height x 4mm in diameter) on the treated surface, with a metallic matrix and the Z100 restorative composite. After the storage period in water at 37° C, the samples were tested with an Instron testing machine, at crosshead speed of 0,5mmjmin. After, three samples of each group were covered with palladium-gold in vacuum conditions, for the SEM examination. Results were submitted to ANOV A and Tukey's test at 5% significance leveI. It was verified that Scotchbond Multi Purpose Plus, Prime & Bond NT and Etch & Prime 3.0 did not show statistical difference on the storage periods. Oearfil Liner Bond 2V showed the largest mean at 3 months don't differing with 6 months period / Mestrado / Mestre em Materiais Dentários
|
105 |
Aderencia de Candida albicans, Cepa 12A, em tres materiais de revestimento resiliente para protese total, submetidos ou não a ciclagem termicaKina, Sidney 02 May 2001 (has links)
Orientador: Saide Sarckis Domitti / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-27T22:22:53Z (GMT). No. of bitstreams: 1
Kina_Sidney_M.pdf: 3348251 bytes, checksum: fa871f0ac132f21ae41013ca2039119a (MD5)
Previous issue date: 2001 / Resumo: Este trabalho teve o objetivo de avaliar a adesão de leveduras (C. albicans, Cepa 12A) sobre a superfície de três materiais de revestimento resiliente, submetidos ou não à ciclagem térmica: MolloplastB@, Softliner@ e Eversoft@. Para tanto, foram confeccionados 24 corpos de prova com cada material, processados como indicado pelos fabricantes, que foram divididos em dois grupos, um sofrendo a ação de 1000 ciclos térmicos (1 minuto em banho a 5°C e 1 minuto em 65°C) e o outro não. Após a ciclagem térmica, todos os grupos foram esterilizados através de raios gama com dose de 25KGY. Posteriormente os corpos de prova foram submetidos ao teste de adesão utilizando-se para isso uma Cepa padrão para teste: C. albicans Cepa 12A. As leveduras foram cultivadas em meio de cultura a 3 t C por 18 horas, e então, coletadas em suspensão ajustada em espectofotômetro (Bauchse & Lamb) com 530 nm por 75% de transmitância. Os corpos de prova foram inoculados com 200 J.11 desta suspensão, e ficaram em estufa a 3tC sob agitação de 50 rpm durante uma hora. Após, as leveduras fracamente aderidas aos corpos de prova foram removidas através de lavagem em tubo com água miliQ. Foi preparada então, a solução para plaqueamento, através da lavagem fmal dos corpos de prova para remoção das leveduras fortemente aderidas. Este processo foi realizado com agitação em vortéx, por 30 segundos, com os corpos de prova imersos em 2 ml de STF, auxiliado ainda, por 1 grama de pérolas de vidro. Após, 100 J.11 desta suspensão foi plaqueada em ágar sabouraud, e guardadas em estufa a 37°C por 48 horas. Finalmente, processouse a contagem de colônias. Os resultados obtidos foram submetidos a análise de variância e corrigidos pelo método de Bonferroni. As diferenças dentro de cada um dos grupos com relação aos valores obtidos com e sem ciclagem térmica foram analisados usando Test- T de Student para amostras pareadas. O nível de significância estatística usado foi de 5%. Os resultados demonstraram diferença significante no Eversoft@, com e sem ciclagem térmica, quando comparado entre si e com os outros materiais, com nível de agregação de leveduras muito superior aos outros. O Molloplast-B@ após sofrer ciclagem térmica, apresentou maior tendência a adesão de leveduras, e quando comparada com o Softliner@ sem ciclagem térmica, não houve diferença estatística, porém, nos corpos ciclados térmicamente o material apresentou maior tendência a agregação de leveduras do que o Softliner@. O Softliner@ não demonstrou diferença com ou sem ciclagem térmica, e teve a menor tendência a agregação de C. albicans destes materiais / Abstract: The aim of the present thesis was to evaluate the adhesion of yeast (c. albicans CEPA 12A) on the surface of 3 different soft lining materiaIs, Molloplast-B@, Softliner@ and Eversoft@. The study included 24 samples of each material. The samples were divided into 2 groups: (i) samples which were thermal cyc1ed 1000 times, each cyc1e lasting 1 minute in SOC and 1 minute in 6SoC water bath and (ii) samples which were not exposed to thermal cyc1ing. Following sterilization in gama rays, the samples were tested for yeast adhesion to their surfaces using C. albicans CEPA 12A. The samples were incorporated to 200 _l of a solution containing the yeast suspension at 37°C for 1 hour. The yeast which were loosen attached to the material surface were removed by water rins e (miliQ). Finally, the samples were further rinsed to remove the yeast intimately attached to the material. 1 00 _l of the second rinsed water was applied to agar sabouraud and kept in a stove at 37°C for 48 hours. After that, the number of newly formed yeast colonies were assessed. The differences in the number of yeast colonies among the various groups were evaluated using Analyse of Variance and corrected by the method of Bonferroni. The differences within the same group regarding the effect of thermal cyc1ing was, however, evaluated by Student- T test for paired samples. The results from the present thesis demonstrated that the Eversoft samples showed a statistically significant larger number of yeast colonies with and without thermal cycling than the remaining groups. The Molloplast-B samples with thermal cyc1ing presented larger number of yeast colonies than the corresponding samples in the Softliner group while, there were no differences between the samples which were not thermal cycled in these groups. The Softliner samples demonstrated the lowest number of newly formed yeast colonies on their surface, with and without thermal cycling / Mestrado / Protese Dental / Mestre em Odontologia
|
106 |
Influencia de sistemas utilizados em ensaio mecanico de tração sobre a resistencia da uniãoOshima, Hugo Mitsuo Silva 16 May 2001 (has links)
Orientador : Mario Alexandre Coelho Sinhoreti / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-28T04:59:52Z (GMT). No. of bitstreams: 1
Oshima_HugoMitsuoSilva_D.pdf: 7982934 bytes, checksum: fdb67b99c87b68354442f502888a1492 (MD5)
Previous issue date: 2001 / Resumo: O propósito deste estudo foi avaliar ín vítro, a influência de quatro métodos de tração sobre a resistência da união esmalte-resina composta. O método do Grupo A, empregou a matriz preconizada pela ISO TR 11405 e serviu como
padrão para comparação com os demais aparatos utilizados. O método do Grupo B, empregou uma matriz com uma travessa metálica em uma das extremidades. Os métodos dos Grupos C e O empregaram matrizes com uma ou duas juntas
universais articuladas. Foram utilizados 60 terceiros molares humanos hígidos e recém-extraídos, divididos em 4 grupos, os quais tiveram as raízes seccionadas e as coroas remanescentes separadas ao meio obtendo-se duas metades (face
vestibular e face lingual). Em seguida, as porções assim obtidas foram incluídas com resina acrílica ativada quimicamente em tubos plásticos, e lixadas até se obter uma superfície plana em esmalte de pelo menos 4 mm de diâmetro. Em
seguida, as superfícies de esmalte foram tratadas com o sistema adesivo Single Bond (3M), de acordo com as instruções do fabricante. Após este procedimento, a resina composta Z250 (3M) foi inserido no interior de um molde acrílico com
formato de tubo, contendo 3 mm de diâmetro interno, firmemente adaptado à superfície tratada e fotoativado com um aparelho XL3000 (3M). Todos os procedimentos de união foram realizados utilizando a matriz preconizada pela
ISO. Os corpos-de-prova assim obtidos foram armazenados a 37°C e 100% de umidade relativa, durante 1 hora, e posteriormente armazenados em água destilada a 37°C, por 23 horas. Após este período as amostras foram tracionadas
por um dos métodos propostos em uma máquina de ensaio universallnstron, a uma velocidade de 0,5 mm/min., até a ruptura. Os resultados obtidos foram transformados em MPa, e submetidos à análise de variância e ao teste de Tukey
(p<0,05). Todas as amostras foram observadas em M.EV para verificação dos tipos de falha ocorridos em cada um dos grupos. Os resultados mostraram que a metodologia de tração empregada influenciou de maneira significativa nos valores
de resistência de união encontrados e no coeficiente de variação de cada grupo. As fotomicrografias demonstraram que para o grupo D, as falhas foram sempre do tipo coesiva na resina composta. Já para os demais grupos (A, B e C), o tipo de
falha predominante foi do tipo mista a qual era caracterizada por fratura coesiva na resina composta/coesiva na camada de adesivo ou em algumas situações, coesiva no substrato dental (Grupo A). Ainda para esses grupos (A, B e C),
ocorreram falhas somente coesivas na resina composta, porém em número menor / Abstract: The purpose of this study was to evaluate in vitro the influence of four tensile test methods on the enamel-resin interface bond strength. The method of Group A was proposed as a standard ISO method. The method of Group B
employed the metallic rod at on end. The methods of Groups C and D employed one or two universal joints. Sixty human extracted third molars, divided into four groups were used. The roots were sectioned and the dental crowns divided in the middle to obtained two portions (buccal and lingual). The portions were embedded in selfcuring acrylic resin and ground to obtain a flat enamel surface. The enamel surface was treated with Single Bond adhesive system (3M), in accordance with
manufacturer's instructions. After this procedure, a light-activated resin composite (Z 250, 3M) was placed in an acrylic mold with 3 mm in diameter and firmly adapted on a treated surface and cured with a lamp (XL 3000, 3M). Ali bond procedures was
made with an ISO assembly specially designed for this purpose. The samples were stored in 100% relative humidity and 37°C for 1 hour, and then, in distilled water at 37°C for 23 hours. After the storage time, the samples were loaded in tension in an
Instron Universal Testing Machine at a crosshead speed of 0.5 mm/mín., until failure. The results (MPa) were submitted to ANOVA and Tukey's test (p<0.05). Ali samples were observed in S.E.M to verify the failure pattern into the Groups. The
results showed that the tensile methods affect significantly the bond strength data and the coefficient of variation observed. The photomicrographs showed that failures were always cohesive in composite for the Group D. For the Groups A, B and C, the
predominantly failures were mixed, or cohesive in composite and adhesive. Cohesive failures of the enamel were observed into the Group A. This Groups (A, B and C), showed cohesive failures in composite in a few samples / Doutorado / Doutor em Materiais Dentários
|
107 |
Avaliação da contração de polimerização e das tensões promovidas em função de deferentes sistemas de polimerização e de materiais restauradores estéticosLawrence Gonzaga Lopes 11 July 2003 (has links)
O objetivo deste trabalho foi avaliar a contração de polimerização e as tensões promovidas, no sentido de comparar o sistema de fotopolimerização por LED (130 mW/cm2) com o sistema halógeno na forma convencional (60 s 600 mW/cm2) e pulso de fotopolimerização (3s 200 mW/cm2 / 3 minutos / 59 s 600 mW/cm2). Da mesma forma, categorias distintas de resinas foram comparadas, como: resina híbrida (Z100 - 3M); resina de micropartículas (A110 3M); resina condensável (SureFil Dentsply); e resina composta de ativação química (Bisfil II Bisco). Para medir a contração de polimerização foram confeccionados cinco espécimes para cada condição experimental, obtidos pela inserção da resina em um anel de silicona com um diâmetro interno de 5mm e altura de 2mm. Um extensômetro elétrico (strain gauge), localizado abaixo da resina, registrou a deformação do material em função da contração de polimerização. Nessa mesma proposição, as tensões decorrentes da contração de polimerização foram medidas pelo método de fotoelasticidade. Para isto, foram confeccionados modelos com material transparente, contendo uma cavidade tipo Classe I, com 5mm de comprimento X 2mm de profundidade X 3mm de largura. Foram realizados sete corpos-de-prova para cada condição experimental. Após a inserção e polimerização da resina, secções com 2mm de espessura foram obtidas e avaliadas sob microscópio de luz polarizada, a fim de se verificar as franjas isocromáticas, que representavam as tensões formadas. Os dados referentes à contração de polimerização foram submetidos ao teste paramétrico de análise de variância a dois critérios (ANOVA) e, a um critério para os referentes ao teste de fotoelasticidade, seguido pelo teste de Tukey (p£0,05). Assim, foi observado que o sistema químico de ativação (Bisfil 2B) produziu os menores valores de contração de polimerização e de tensões; de forma geral, a técnica pulso interrompido reduziu os valores de contração de polimerização das resinas compostas e de tensões geradas, quando comparado com às técnicas convencionais (LED e Luz Halógena); a fonte de luz à base de LEDs produziu menores valores de contração de polimerização do que a fonte halógena, quando aplicados convencionalmente. Entretanto, o LED proporcionou a mesma quantidade de tensões de contração de polimerização, quando comparado à fonte de luz halógena (técnica convencional); de maneira geral e independente do meio de fotoativação, a resina SureFil produziu os menores valores de contração de polimerização e de tensões geradas, dentre as fotoativadas. Por outro lado, as resinas Z100 e A110 geraram maiores valores de contração e de tensões. / The aim of this work was to evaluate the polymerization shrinkage and stress, comparing the LED light source (130 mW/cm2) with quartz tungsten halogen (QTH) light source in the conventional mode (60s 600 mW/cm2) and pulse delay curing mode (3s 200 mW/cm2 + 3 min + 59s 600 mW/cm2). Different categories of composite resins were also evaluated, such as Z100 (hybrid), A110 (microfilled), SureFil (packable) and Bisfil 2B (chemical-cured resin). Silicone molds 2 mm high and 5 mm diameter were used to prepare five specimens for each experimental condition. A strain gauge located under the resin measured the material deformation due to polymerization shrinkage. The stresses were measured by photoelasticity analysis. Butt-joint box-shaped cavities (5.0 X 3.0 mm, 2.0 in depth) were prepared in photoelastic transparent resin. Seven specimens were made for each condition. After the insertion and polymerization of the composite resin, they were cross-sectioned perpendicularly to the longitudinal side of the cavity to determine, under polarized microscopic, the contraction stress by means of the observation of fringes in the photoelastic mould walls, which represented the created stress. The shrinkage data were statistically evaluated using two way ANOVA and Tukey tests (p£ 0.05) and for stress data one way ANOVA and Tukey tests (p£ 0.05) were used. It was observed that the chemical-cured system (Bisfil 2B) produced the lower means of polymerization shrinkage and stress; in general, the pulse delay mode reduced the contraction and the stress values when compared to conventional curing modes (LED and QTH); the LED light source produced lower contraction values than QTH light source, when used in conventional mode. However, the LED light source generated the same as stress QTH light source (conventional mode); in general, and independently of the activation mode, the SureFil resin produced lower contraction and stress values than others light-cured resins. Conversely, the Z100 and A110 resins produced the greater contraction and stress values.
|
108 |
Efeito da ciclagem de pH na liberação/recarga de flúor e na microinfiltração de materiais restauradores resinososRosa Maria Viana de Bragança Garcez 26 June 2006 (has links)
Quedas cíclicas de pH no meio bucal parecem ser um dos maiores desafios aos quais estão expostos os materiais restauradores. Desta forma, a capacidade de liberação/recarga de flúor (F¯) e a avaliação da interface dente/restauração pelo teste de microinfiltração em ciclagem de pH (CpH), durante 15 dias, pode complementar in vitro, a simulação de situações clínicas de alto desafio cariogênico. Foram confeccionados 12 corpos-de prova na forma de discos (1,1 cm de diâmetro, 0,15 cm de espessura) dos materiais, distribuídos em dois grupos sem e com recarga (R), Vitremer (V/VR), Dyract AP (DY/DYR), Ariston®AT (A/AR), Definite® (D/DR), Tetric®Ceram (TC/TCR). Os corpos-de-prova foram imersos individualmente em 4 mL de solução CpH, 6 horas em solução desmineralizante (DES¯) e 17 horas em solução remineralizante (RE). A recarga foi iniciada no 2º dia com pasta fluoretada fluida 3:1(Crest), realizada diariamente, entre as trocas das soluções DES¯/RE. As soluções DES¯/RE dos dois grupos, com e sem recarga eram trocadas diariamente, e armazenadas durante 15 dias. A análise da concentração de F¯ da liberação e da recarga foi medida com 0,5 mL de solução teste adicionada a igual volume de TISAB II, por um eletrodo íon F¯ específico acoplado ao aparelho analisador pH/F¯. Os resultados foram submetidos a ANOVA e teste de Tukey (p<0,05). Os maiores valores F¯ foram registrados em solução DES¯ (pH 4.3). Todos os materiais, em ambos experimentos, apresentaram o mesmo padrão de liberação de F¯ e, os maiores valores foram do V (418,04 µgF¯/cm²) e VR (818,39 µgF¯/cm²). Ao 3º dia, materiais sob recarga apresentaram maiores valores de F¯ liberado, com declínio lento e alcançando valores estáveis ao 15º dia, quando os valores de F¯ aproximaram-se aos sem recarga, obtidos ao 2º dia. As resinas compostas D e TC apresentaram os mais baixos valores de F¯ liberados, D (5,16 µgF¯/cm²); DR (10,25 µgF¯/cm²); TC (10,09µgF¯/cm²); TCR (16,85 µgF¯/cm²), em ambos experimentos, mas sem diferenças estatísticas significantes entre DR e TC. Entre as resinas compostas, a maior liberação foi da AR (327,20 µgF¯/cm²). Para avaliar a microinfiltração, foram utilizados 3ºs molares extraídos preparados com cavidades Classe V (4,00 mm, 2,00 mm, 1,5 mm), em esmalte, restaurados com os mesmos materiais e distribuídos em dois meios de imersão, água deinozada (A) e CpH (DES¯/RE) durante 15 dias. Em seguida, foram imersos em fucsina básica 0,5% por 24 horas, lavados, seccionados, visualizados em estereomicroscópio óptico com 60X de aumento. Os cortes mais infiltrados foram escaneados e uma medida linear (0,5 cm=115 pixels) foi obtida pelo softweare Image Tool. Ao teste de Tukey, houve diferença estatística significante entre os meios de imersão, o maior grau de microinfiltração foi em CpH. Todos os materiais apresentaram microinfiltração na interface dente/restauração, sendo observada a maior infiltração na resina composta D, seguida da TC, V, DY e A. Entretanto, não houve diferença estatisticamente significante entre os materiais TC, V, DY e A. Diante das limitações desse estudo e frente aos resultados encontrados, observa-se que apesar das quantidades de F¯ liberadas no experimento sem e com recarga, não deixou de ocorrer o processo de microinfiltração na interface dente/restauração dos materiais avaliados. / pH cyclic alterations in the oral environment seems to be one of the largest challenges in which the restoratives materials are subjected. Therefore, fluoride (F¯) release/uptake capacity evaluation of the tooth/restorative interfaces by microleakage test under pH-cycling (CpH) regimen, for 15 days might simulate in vitro the clinical situations of caries challenging. Twelve cylindrical samples with diameter of 11mm and thickness of 1.5mm of the materials Vitremer (V/VR), Dyract AP (DY/DYR), Ariston®AT (A/AR), Definite® (D/DR), Tetric®Ceram (TC/TCR) were fabricated and distributed in two groups of F¯ release and uptake. Samples were individually immersed in 4mL of CpH solution, i.e., 6 hours in demineralizing solution (pH 4.3) followed by 17 hours in remineralizing solution (pH 7.0). The fluoride uptake was started at 2nd day by means of dentifrice slurry containing 1.100 ppm of F¯ (Crest), applied daily, before DES¯/RE solutions changing. The analysis of F¯ release/uptake concentration was measured by a specific F¯ ionelectrode with 0.5mL of test solution added to 0.5mL of TISAB II. The results were submitted to ANOVA and Tukey\'s Test (p<0.05). The highest F¯ values were registered in DES¯ solution. All materials, in both experiments, presented the same pattern of fluoride release and the highest rates were obtained by V (418.04µgF¯/cm²) and VR (818.39µgF¯/cm²) groups. At 3rd day, all materials presented the highest amount of F¯ releasing after the uptake, with slowly decrease, reaching stable values at the 15th day, when fluoride release presented similar levels of that at 2nd day. Composite resins D and TC released the lowest fluoride amounts, D (5.16µgF¯/cm²); DR(10.25µgF¯/cm²); TC (10.09µgF¯/cm²); TCR (16.86µgF¯/cm²), in both experiments, although no statistically difference was observed between DR and TC. AR released the highest amount of F¯ (327.21µgF¯/cm²) among composites. Eighty human 3rd molars were used to evaluate microleakage under pH-cycling regimen. Class V cavities (4.0mm, 2.0mm, 1.5mm) with margins in enamel were prepared and restored with the same materials. They were distributed in two immersion media, groups: deionized water (A) 112 and pH-cycling (DES¯/RE), for 15 days. After this period, specimens were then immersed in 0.5% basic fucsine dye for 24 hours. They were washed in tap water and sectioned for evaluation. The samples were analyzed by means of an optical stereomicroscope (60X) and slices with the greatest dye penetration were choosen and submitted to Image Tool area analysis softweare. Data was submitted to stattiscal analysis using two-way ANOVA and Tukeys test (=0.05), revealing that there was statistically difference between immersion media factor. The greatest level of dye penetration was obtained in CpH. All materials tested registered some microleakage but the greatest level was registered by Definite® followed by TC, V, DY and A. However, there were no statistically significant differences amongst TC, V, DY and A. Definite® was significantly different to A and DY. Within the limits of this study and in the basis of the obtained results, the fluoride release/uptake was not able in reducing preventing the microleakage of the evaluated materials. Therefore, the restorative material to each clinical situation should be analyzed on his physical, chemical and mechanical aspects as well as his behavior under caries challenge.
|
109 |
'Creep' em resinas compostas fotopolimerizáveis. / Creep of light-cured posterior composite resinsMarcelo Guerino Pereira Couto 25 April 2000 (has links)
As resinas compostas vêm sofrendo inúmeras alterações com o objetivo de tornar o seu uso adequado para restaurações de dentes posteriores, entretanto, problemas clínicos associados à sua utilização são comumente observados, dentre eles sua resistência ao desgaste e à abrasão, a contração de polimerização, a microinfiltrção marginal, e sua deformação permanente (importante propriedade em situações clínicas onde existem áreas sujeitas às forças oclusais) e esta, normalmente não é considerada. Visando determinar o creep, por meio da deformação permanente, amostras confeccionadas com resinas compostas fotopolimerizáveis: ALERT [A] (Jeneric®/Pentron®), CHARISMA F [C] (Heraeus/Kulzer), HELIOMOLAR RADIOPAQUE [H] (Vivadent), SOLITAIRE [S] (Heraeus/Kulzer) e TETRIC CERAM [T] (Vivadent) após armazenamento em água, à temperatura de 37 + 1ºC, foram submetidas a uma carga compressiva constante de 36MPa, por períodos de: 15 minutos, 1 hora e 24 horas. Os resultados obtidos apresentam os valores quantitativos da diferença entre o comprimento original da amostra e o seu comprimento após o ensaio, em cada período estabelecido. A análise estatística dos dados apresentados pelas cinco resinas compostas avaliadas nos quatro períodos determinados, demonstrou resultados de creep estático (em ordem decrescente), para o período de 15 minutos: [H] (X=1,0192%), [T] (X=0,8787%), [C] (X=0,7469%), [S] (X=0,6738%) e [A] (X = 0,5095%). Para o período de 1 hora: [H] (X=1,5546%), [T] (X=1,2082%), [C] (X=0,9744%), [S] (X=0,8245%), [A] (X=0,6348%) e, para o último período observado, 24 horas, obteve-se a seguinte seqüência: [H] (X=2,3747%), [T] (X=1,7993%), [C] (X=1,2812%), [S] (X=1,2645%) e [A] (X=0,7600). Os valores médios do creep estático das resinas CHARISMA F e SOLITAIRE não foram estatisticamente diferentes em qualquer um dos períodos estudados, sendo que no período de 15 minutos, os resultados obtidos para a resina TETRIC CERAM também se assemelharam aos destas e, em 1 hora, os da resina composta ALERT foram similares aos das duas primeiras; porém, a resina HELIOMOLAR RADIOPAQUE, apresentou mensurações divergentes das anteriores, demonstrando piores características de deformação permanente, por possuir maiores valores de creep estático em qualquer período estudado. / The posterior composite resins dental restorative materials, have been, extensively, used in substitution of dental amalgam, in function of its aesthetic best. Although the use of those resins, in areas subject to the forces occlusal, increased significantly, the nead evaluation of the behavior of static creepimportant property to be considered in those situationsit is not very disclosed. For this reason, the objective of the present paper was to determine the static creep of the composite resins: Alert [A], Charisma F [C], Heliomolar Radiopaque [H], Solitaire [S] and Tetric Ceram [T], by evaluation means of the permanent deformation. That deformation was determined in specimens submitted to a constant compressive load of 36MPa, in 37 + 1ºC, immerged in recipient contend water, for periods of 15 minutes, 1 hour and 24 hours. The results obtained in that experiment present the quantitative values of the creep in crescent order, for the period of 15 minutes: H, T, C, S, A; in 1 hour: H, T, C, S, A and in 24 hours: H, T, C, S, A. The profile analysis of the creep for five composite resins evaluated in the four pre-determined periods demonstrated similar results for C, S, T in 15 minutes, A, C, S, in 1 hour and C, S for 24 hour, and different for H in every observed time.
|
110 |
Avaliação da Infiltração Marginal em Cavidades de Classe II Restauradas com Resina Composta Associada a Outros Materiais Restauradores.Adriana Maria Botelho 08 July 1999 (has links)
As resinas compostas vêm sofrendo inúmeras alterações, com o objetivo de tornar o seu uso adequado para restaurações de dentes posteriores, entretanto, problemas clínicos associados à sua utilização são comumente observados, dentre eles, a microinfiltração marginal. Algumas alternativas clínicas têm sido sugeridas, na tentativa de reduzir as falhas decorrentes do emprego deste material, principalmente em restaurações estendidas à região de cemento, local este onde os problemas se agravam. O objetivo deste trabalho consistiu, portanto, em estudar a efetividade do vedamento marginal de diferentes materiais aplicados no terço cervical com término em cemento para, em associação à resina composta, restaurar esteticamente cavidades de classe II, através da técnica mista, avaliandose com esta finalidade o índice de infiltração marginal tanto na interface cemento/material, quanto na interface dos materiais restauradores. Cavidades MOD com margens cervicais estendidas além da junção amelocementária foram confeccionadas em 84 dentes pré-molares humanos livres de cáries, os quais foram distribuídos em grupos de 12 elementos cada, correspondendo a 7 condições experimentais: 8 grupo 1 (controle) - Scotchbond MP/Z-100; 8 grupo 2 - verniz Copalite/Dispersalloy/Scotchbond MP/Z-100; 8 grupo 3 - Vitremer/Scotchbond MP/Z-100; 8 grupo 4 - Prime & Bond 2.1/Dyract/Scotchbond MP/Z-100; 8 grupo 5 - Prime & Bond 2.1/Dyract-AP/Scotchbond MP/Z-100; 8 grupo 6 - Stae/Freedom/ Scotchbond MP/resina composta Z-100; 8 grupo 7 - One Step/Bisfil-2B/Z-100. No sentido de evitar penetração da solução corante em áreas indesejadas, em todos os dentes os forames apicais foram obstruídos com amálgama. Após 24 horas, as restaurações foram polidas com discos Sof-Lex de granulação fina e submetidas posteriormente a um tratamento térmico correspondente a 500 ciclos de 20 segundos cada, nas temperaturas de 5ºC e 55ºC. Imediatamente após a termociclagem, os espécimes tiveram a superfície totalmente coberta por 2 camadas de esmalte de unha, exceto 1mm aquém e além da interface cemento/material em uma das caixas proximais e da interface dos materiais restauradores na caixa proximal oposta, sendo então imersos em solução de azul de metileno à 2%, onde permaneceram durante 24 horas, mantidos à 37ºC. Decorrido este período, os dentes foram incluídos em bases acrílicas apropriadas para serem adaptadas à máquina de corte, obtendo-se cerca de 4 a 5 cortes para cada espécime. Para avaliar o índice de penetração da solução corante nas interfaces das restaurações, optou-se pela análise qualitativa, através da atribuição de escores previamente determinados. Os resultados obtidos foram então organizados e submetidos aos cálculos estatísticos, concluindo-se que: - nenhum material restaurador utilizado foi apto em impedir 100% a penetração da solução corante nas margens cervicais em cemento; - o Dyract-AP e o Vitremer promoveram respectivamente os melhores resultados de selamento marginal, não ocorrendo entre os mesmos diferenças do ponto de vista estatístico, distinguindo-se significantemente em relação aos demais materiais utilizados; - o Bisfil-2B ocupou uma posição intermediária, diferenciando-se estatisticamente dos demais materiais, sendo porém de maneira desfavorável em relação ao Dyract-AP e ao Vitremer e favorável em comparação ao Dispersalloy, Z-100, Dyract e Freedom, os quais apresentaram, nesta ordem, os piores índices de infiltração marginal, não ocorrendo entre os mesmos diferenças estatisticamente significantes; - referindo-se à interface dos materiais restauradores resinosos, a maioria dos espécimes apresentava-se praticamente isenta de infiltração, apresentando-se esta severa na interface amálgama/resina composta. / Marginal leakage is one of the clinical problem associated with posterior resin composite restoration. The aim of this research was to determine the effectiveness of the marginal sealing of different materials applied at the cervical third of class II cavities in association with resin composite. Microleakage at the cement/material interface and between the restorative materials was measured. Eigth-four human non carie premolars were randomly distributed into seven groups as follow: ¨ group 1 - (control) Scotchbond MP/Z-100; ¨ group 2 - Copalite/Dispersalloy/Scotchbond MP/Z-100; ¨ group 3 - Vitremer/ Scotchbond MP/Z-100; ¨ group 4 - Prime & Bond 2.1/Dyract/Scotchbond MP/Z-100; ¨ group 5 - Prime & Bond 2.1/Dyract-AP/Scotchbond MP/Z-100; ¨ group 6 - Stae/Freedom/Scotchbond MP/composite resin Z-100; ¨ group 7 - One Step/Bisfil-2B/Z-100. Before the teeth were prepared and restored with the various materials, the apexes were sealed with amalgam. After 24 hours the restorations were polished with Sof-Lex discs and thermocycled alternately soaked at 5 oC and 55 oC for 20 seconds for a total of 500 cycles. After thermocycling the specimens were coated with 2 layers of fingernail polish, but the surface sealant did not approximate to the cement/material interface of the preparation closer than 1.0 mm in one of the proximal boxes and between the restorative materials interface in the opposite proximal box. The teeth were immersed in a 2% methylene blue solution for 24 hours at 37 oC. After this period, the teeth were embeded in acrylic bases and sectioned in 4 to 5 different planes parallel to one another in a cutting machine. Microleakage was determined by a qualitative analysis and allowed the following conclusions: ¨ None of the testing materials avoid 100% microleakage at cervical margins; ¨ Dyract-AP and Vitremer showed statistically significant better results for marginal sealing, when compared to the other materials; ¨ Bisfil-2B presented better results than Dispersalloy, Z-100, Dyract and Freedom which showed the worst rates of marginal leakage; ¨ It was not registred dye penetration at the interface materials/resin composite, except for the amalgam/resin composite interface.
|