University, Diss., 2006--Augsburg.

Techn. Universiẗat, Diss., 2006--Chemnitz.

Stuttgart, Univ., Diss., 2006.

Thesis (Ph.D.)--Michigan State University. Dept. of Civil & Environmental Engineering, 2008. / Title from PDF t.p. (viewed on Apr. 2, 2009) Includes bibliographical references (p. 217-225). Also issued in print.

Este trabalho visou avaliar a utilização de refugos de revestimentos cerâmicos em substituição da areia para confecção de argamassas cimentícias. Foram analisados dois resíduos, fornecidos pela mesma empresa, e provindo de quebra na produção de porcelanato esmaltado e de azulejo. Estes resíduos foram caracterizados quanto à sua distribuição granulométrica, composição química, mineralógica e comparados com a areia do Rio Jacuí, e incorporados em argamassas cimentíceas. Corpos-de-prova de 40x40x160mm3 foram moldados e submetidos a ensaios de resistência à tração na flexão, após 7, 28 e 63 dias de cura, enquanto que corpos-de-prova cilíndricos com 50 mm de diâmetro e 50mm de altura foram avaliados quanto às fases mineralógicas formadas por difração de raio-x, e quanto à resistência à compressão, absorção de água (após 28 dias), índices de vazios e massa específica. Os resultados mostram que, apesar do aumento da relação água/cimento, para que um mesmo espalhamento fosse mantido, a mistura utilizando resíduo apresenta um desempenho mecânico e físico igual ou mesmo superior em comparação às apresentadas pelas argamassas utilizando areia de rio. / The trend of using recycled materials is increasing. This fact is noted in several areas, but mainly in the construction industry. Therefore, it behooves researchers to identify and evaluate the potential use of waste mixtures of mortar and concrete. This study aims to evaluate the use of waste from the manufacture of floor and wall tiles, called grog, as a replacement for sand for making mortar. In this paper we analyzed two residues, supplied by the same company, and coming break in the production of porcelain and tile. These residues were physically characterized and compared with the sand of Rio Jacuí and evaluated in the form of mixing in cimentitious matrix. Specimens of 40x40x160 mm3 were cast and tested, the bending and compression at 7, 28 and 63 days of curing, while body-of-proof cylindrical 50 mm diameter and 50mm were evaluated for water absorption rates voids and density, after 28 days of healing, being held after the breakup of the specimens x-ray diffraction. The results show that, despite the increase of water cement ratio, so mechanical and physical performance in relation to river sand.

Made available in DSpace on 2015-03-03T11:52:20Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-08-01Bitstream added on 2015-03-03T12:07:29Z : No. of bitstreams: 1 000803462.pdf: 1084374 bytes, checksum: 89f9f44ae8ab96cbcd8292604a3f0e5f (MD5) / O trabalho está entre os dez países que possuem a maior produção mundial de fundidos, movimentando aproximadamente onze bilhões de dólares por ano para uma produção de mais de três milhões de toneladas/ano. Com esta alta produtividade, a indústria de fundição gera um grande volume de resíduos, dentre eles, destacam-se os finos de areia oriundos dos sistemas de areia captados durante os processos de moldagem e desmoldagem. Este resíduo é gerado em considerável quantidade e por isso seu descarte é um dos motivos da diminuição do espaço disponível em aterros, acarretando um alto custo para as indústrias de fundição. Assim, faz-se necessário a obtenção de técnicas para reaproveitamento deste resíduo, sendo uma das alternativas aq sua utilização em matriz de cimento Portland. Esta opção além de reduzir custos com descartes em aterros, também contribui com a redução do consumo e dos custos de insumos na área da construção civil. Com o objetivo de estudar este reaproveitamento, o presente trabalho foi realizado com finos de areia coletados em dois pontos do sistema de areia de uma fundição de aço. Estes resíduos foram caracterizados por fluorescência de raios X (FRX), por espectroscopia de energia dispersiva (EDS), difração de raios X (DRX) e análises da morfologia e do tamanho das partículas. Sua incorporação em argamassa de cimento foi realizada com corpos de prova em substituição à parte do agregado miúdo e corpos de prova em substituição à parte do cimento. Estes corpos de prova com diferentes percentuais de resíduos foram avaliados através de ensaios de resistência à compreensão, absorção de água, índice de vazios e massas específicas. Os resultados da caracterização do resíduo demonstraram uma predominância de óxidos de ferro, cromo, alumínio e silício, caracterizando-o como proveniente de uma areia de cromita, com propriedades hidrofilicas e de granulometria fina... / Brazil is among the ten countries with highest wordwide production of casting products, driving about eleven billion dollars a year, producing more than three million tons/year. With this high productivity, the foundry industry generates large amounts of waste, which stands out the fine sand originating from the sand systems, during the process of molding and demolding. This waste is begotten in considerable quantity, so their disposal is one of the reasons for the decrease in available space in landfills, resulting in a high cost for foundry industry. Thus, it is necessary to find techniques to reuse this waste, as an alternative to this, it use in Portland cement matrix. This option could reduce costs with disposal at landfills and also contributes to the reduction of consumption and input costs in the construction area. In order to study this reuse, this work was performed with fine sand had gathered at two points of sand system on a steel foundry. These waste were characterized by X-ray fluorescence (XRF), energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), and analysis of morphology and particle size. Their incorporation into coment mortar was performed with specimens to replace part of the aggregate and speciments to replace part of the cement. These specimens with different percentages of waste were evaluated by compressive strength test, water absorption, voids and densities. The results of waste's characterization showed a predominance of iron oxides, chromium, aluminum and silicon, characterizing them as a them as a chromite sand, with hydrophilic properties and fine particle size. These characteristics influenced the other analyses, resulting in a more brittle and porous mortar, the compressive strength reduced proportionally with the increase percentages of waste. However the results were satisfactory, because these ar according to the standard NBR-13281 - mortar for laying and coatings. Concluding that the...

Este trabalho visou avaliar a utilização de refugos de revestimentos cerâmicos em substituição da areia para confecção de argamassas cimentícias. Foram analisados dois resíduos, fornecidos pela mesma empresa, e provindo de quebra na produção de porcelanato esmaltado e de azulejo. Estes resíduos foram caracterizados quanto à sua distribuição granulométrica, composição química, mineralógica e comparados com a areia do Rio Jacuí, e incorporados em argamassas cimentíceas. Corpos-de-prova de 40x40x160mm3 foram moldados e submetidos a ensaios de resistência à tração na flexão, após 7, 28 e 63 dias de cura, enquanto que corpos-de-prova cilíndricos com 50 mm de diâmetro e 50mm de altura foram avaliados quanto às fases mineralógicas formadas por difração de raio-x, e quanto à resistência à compressão, absorção de água (após 28 dias), índices de vazios e massa específica. Os resultados mostram que, apesar do aumento da relação água/cimento, para que um mesmo espalhamento fosse mantido, a mistura utilizando resíduo apresenta um desempenho mecânico e físico igual ou mesmo superior em comparação às apresentadas pelas argamassas utilizando areia de rio. / The trend of using recycled materials is increasing. This fact is noted in several areas, but mainly in the construction industry. Therefore, it behooves researchers to identify and evaluate the potential use of waste mixtures of mortar and concrete. This study aims to evaluate the use of waste from the manufacture of floor and wall tiles, called grog, as a replacement for sand for making mortar. In this paper we analyzed two residues, supplied by the same company, and coming break in the production of porcelain and tile. These residues were physically characterized and compared with the sand of Rio Jacuí and evaluated in the form of mixing in cimentitious matrix. Specimens of 40x40x160 mm3 were cast and tested, the bending and compression at 7, 28 and 63 days of curing, while body-of-proof cylindrical 50 mm diameter and 50mm were evaluated for water absorption rates voids and density, after 28 days of healing, being held after the breakup of the specimens x-ray diffraction. The results show that, despite the increase of water cement ratio, so mechanical and physical performance in relation to river sand.

abstract: Manufacture of building materials requires significant energy, and as demand for these materials continues to increase, the energy requirement will as well. Offsetting this energy use will require increased focus on sustainable building materials. Further, the energy used in building, particularly in heating and air conditioning, accounts for 40 percent of a buildings energy use. Increasing the efficiency of building materials will reduce energy usage over the life time of the building. Current methods for maintaining the interior environment can be highly inefficient depending on the building materials selected. Materials such as concrete have low thermal efficiency and have a low heat capacity meaning it provides little insulation. Use of phase change materials (PCM) provides the opportunity to increase environmental efficiency of buildings by using the inherent latent heat storage as well as the increased heat capacity. Incorporating PCM into concrete via lightweight aggregates (LWA) by direct addition is seen as a viable option for increasing the thermal storage capabilities of concrete, thereby increasing building energy efficiency. As PCM change phase from solid to liquid, heat is absorbed from the surroundings, decreasing the demand on the air conditioning systems on a hot day or vice versa on a cold day. Further these materials provide an additional insulating capacity above the value of plain concrete. When the temperature drops outside the PCM turns back into a solid and releases the energy stored from the day. PCM is a hydrophobic material and causes reductions in compressive strength when incorporated directly into concrete, as shown in previous studies. A proposed method for mitigating this detrimental effect, while still incorporating PCM into concrete is to encapsulate the PCM in aggregate. This technique would, in theory, allow for the use of phase change materials directly in concrete, increasing the thermal efficiency of buildings, while negating the negative effect on compressive strength of the material. / Dissertation/Thesis / M.S. Civil Engineering 2013

Este trabalho visou avaliar a utilização de refugos de revestimentos cerâmicos em substituição da areia para confecção de argamassas cimentícias. Foram analisados dois resíduos, fornecidos pela mesma empresa, e provindo de quebra na produção de porcelanato esmaltado e de azulejo. Estes resíduos foram caracterizados quanto à sua distribuição granulométrica, composição química, mineralógica e comparados com a areia do Rio Jacuí, e incorporados em argamassas cimentíceas. Corpos-de-prova de 40x40x160mm3 foram moldados e submetidos a ensaios de resistência à tração na flexão, após 7, 28 e 63 dias de cura, enquanto que corpos-de-prova cilíndricos com 50 mm de diâmetro e 50mm de altura foram avaliados quanto às fases mineralógicas formadas por difração de raio-x, e quanto à resistência à compressão, absorção de água (após 28 dias), índices de vazios e massa específica. Os resultados mostram que, apesar do aumento da relação água/cimento, para que um mesmo espalhamento fosse mantido, a mistura utilizando resíduo apresenta um desempenho mecânico e físico igual ou mesmo superior em comparação às apresentadas pelas argamassas utilizando areia de rio. / The trend of using recycled materials is increasing. This fact is noted in several areas, but mainly in the construction industry. Therefore, it behooves researchers to identify and evaluate the potential use of waste mixtures of mortar and concrete. This study aims to evaluate the use of waste from the manufacture of floor and wall tiles, called grog, as a replacement for sand for making mortar. In this paper we analyzed two residues, supplied by the same company, and coming break in the production of porcelain and tile. These residues were physically characterized and compared with the sand of Rio Jacuí and evaluated in the form of mixing in cimentitious matrix. Specimens of 40x40x160 mm3 were cast and tested, the bending and compression at 7, 28 and 63 days of curing, while body-of-proof cylindrical 50 mm diameter and 50mm were evaluated for water absorption rates voids and density, after 28 days of healing, being held after the breakup of the specimens x-ray diffraction. The results show that, despite the increase of water cement ratio, so mechanical and physical performance in relation to river sand.

Nos revestimentos de paredes a fixação de placas de rochas pode ser feita com inserts metálicos ou por aderência com argamassas. Nos assentamentos com argamassas os valores de aderência, por norma, devem ser superiores a 1 MPa e a altura máxima do revestimento não pode ultrapassar 3 m. No presente trabalho foram feitos ensaios com ladrilhos de três tipos de \"granitos\" para comparar a aderência da argamassa existente no mercado, específica para estas rochas, com uma argamassa colante para porcelanatos, de mesmo custo de produção, desenvolvida por pesquisadores do Departamento de Arquitetura da Escola de Engenharia de São Carlos da Universidade de São Paulo. As rochas escolhidas foram \"Vermelho Brasília\" (sienogranito), \"Verde Labrador\" (charnoquito) e \"Preto Indiano\" (migmatito) apresentam características petrográficas e serrabilidades diferentes, o que implica em valores distintos de rugosidade das chapas obtidas pelo desdobramento dos blocos em teares. A aderência destas rochas com as com argamassas foi determinada, tanto na face rugosa como na face polida por meio do ensaio de arrancamento por tração, normatizado para cerâmica. Os resultados mostraram para estas rochas que a aderência das argamassas está relacionada à rugosidade e à mineralogia/textura. A aderência obtida para a argamassa colante desenvolvida para porcelanato foi aproximadamente 2 vezes superior a encontrada para argamassa comercial, mostrando sua excelente qualidade para o assentamento de placas de \"granitos\". / In coverings of walls the setting of dimension stones can be made with metallic inserts or by tack with mortar. In the nestings with mortar the values of tack, for norm, must be superior the 1 MPa and the maximum height of covering cannot exceed 3 m. In the present work, assays with floor tiles of three types of \"granites\" had been made to compare the tack of the existing mortar in the market, specific for these granites, with a adhesive mortar for porcelain, of same cost of production, developed for researchers of the Department of Architecture of the School of Engineering of São Carlos of the University of São Paulo. The chosen stones had been \"Vermelho Brasília\" (sienogranite), \"Verde Labrador\" (charnockite) and \"Preto Indiano\" (migmatite) they present petrographics analysis and saw different, what implies in distinct values of the rugous of plates gotten for the unfolding of the blocks in sewing presses, that use grain of steel as abrasive element. The tack of plates of these stones with mortar was determined in such a way in the rugose face as in the polishing face by way of the assay of pulling up for traction, prescriptive for ceramics. The results had shown that the tack of mortar is related to the rugous and mineralogy/texture for these stones. The tack gotten for the developed adhesive mortar for porcelain was approximately two times superior the found one for commercial mortar, showing its excellent quality for the nesting of \"granite\" plates.