Made available in DSpace on 2014-06-11T19:31:26Z (GMT). No. of bitstreams: 0 Previous issue date: 2006Bitstream added on 2014-06-13T20:41:44Z : No. of bitstreams: 1 conti_ecg_dr_arafo.pdf: 812838 bytes, checksum: c0f89cff921f9b0a2343ffde10308ae3 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O objetivo desse estudo foi avaliar a microdureza Vickers de um cimento resinoso químico (C&B Cement - Bisco) e um de ativação dual (RelyX ARC - 3M ESPE), fotopolimerizado por diferentes fontes de luz, em função de diferentes profundidades do canal radicular, na cimentação de pinos de fibra de vidro. Os aparelhos fotopolimerizadores empregados foram: Optilux 360 (Demetron) - luz halógena; Radii (SDI) - LED; UltraLume 5 (Ultradent) - LED. Nenhuma diferença estatisticamente significante foi observada nos valores de microdureza Vickers, dos terços cervical, médio e apical do canal radicular, para o cimento resinoso químico (G1), e os terços cervicais do cimento resinoso dual, para todos os aparelhos fotopolimerizadores (G2, G3 e G4) (p>0.05). Porém, o aparelho de luz halógena (G2) e o LED UltraLume 5 (G4) apresentaram comportamentos semelhantes, proporcionando uma diminuição gradativa nos valores médios de microdureza do cimento resinoso dual, do terço cervical para o apical (p<0.001). Os menores valores de microdureza foram encontrados nos terços apical do sistema RelyX ARC fotopolimerizado com luz halógena ou com LED UltraLume 5. / This study evaluated the Vickers microhardness of a chemically cured resin cement (C&B Cement - Bisco) and a dual cure cement (RelyX ARC - 3M ESPE), light cured by different light sources, according to the different root canal depths, for luting of glass fiber posts. The light curing units employed were Optilux 360 (Demetron) - halogen lamp; Radii (SDI) - LED; UltraLume 5 (Ultradent) - LED. No statistically significant difference was observed in Vickers microhardness values at the cervical, middle and apical root thirds for the chemically cured resin cement (G1), and at the cervical third for the dual resin cement, for all light curing units (G2, G3 and G4) (p>0.05). However, the halogen lamp unit (G2) and LED UltraLume 5 (G4) presented similar performance, providing gradual reduction in mean microhardness values for the dual resin cement from the cervical to the apical third (p<0.001). The lowest microhardness values were found at the apical third for the system RelyX ARC light cured with halogen lamp or LED UltraLume 5.

Made available in DSpace on 2014-06-11T19:35:03Z (GMT). No. of bitstreams: 0 Previous issue date: 2010-07-22Bitstream added on 2014-06-13T20:45:50Z : No. of bitstreams: 1 zamboni_sroc_dr_sjc.pdf: 562964 bytes, checksum: 96289338fffdaef0884f0ad0364b5145 (MD5) / O objetivo neste estudo foi avaliar e comparar a resistência à fratura de incisivos centrais restaurados usando dois tipos de pinos intra-radiculares: núcleo metálico fundido e pinos de fibra de quartzo, reconstruídos com diferentes tipos de coroas. A hipótese nula testada foi que a resistência a fratura desses corpos de prova não apresentariam diferença quanto ao tipo de pino e tipo de coroa. Sessenta incisivos centrais superiores foram divididos em 6 grupos: G1- núcleo metálico fundido + coroa em cerômero, G2- núcleo metálico fundido + coroa metalo-cerâmica, G3- núcleo metálico fundido + coroa em e-max, G4 – pino de fibra de quartzo e pinos acessórios + coroa em cerômero, G5- pino de fibra de quartzo e pinos acessórios + coroa metalo-cerâmica e G6- pino de fibra de quartzo e pinos acessórios + coroa em e-max. Todos os espécimes foram submetidos à ciclagem mecânica com freqüência de 2 Hz e 500.000 ciclos com carga de 3Kg. Os corpos de prova foram submetidos a teste de compressão em uma máquina universal de ensaios (Emic) com velocidade de carga de 1,0 mm/min até a sua fratura. Os valores de resistência à fratura foram G1- 47.44 ± 10.39, G2- 54.74 ±7.76, G3-49.71 ± 8.66, G4- 54.97 ± 8.67, G5-73.50 ± 11.83 e G6- 55.47 ± 10.62. A análise de variância (ANOVA) (p<0,05) mostrou diferença estatisticamente significante para os pinos. Quanto à análise de fratura, os núcleos metálicos fundidos apresentaram o maior número de amostras com fratura desfavoráveis quando comparados os pinos de fibra de quartzo. O conjunto pino de fibra restaurados com coroa metalo cerâmica, apresentou valor de resistência à fratura estatisticamente maior quando comparado aos demais grupos segundo o teste de Tukey (5%), Metalo cerâmica - 64,12±13,69 kgf, difere estatisticamente das demais coroas metal free - 52,59±9,88 kgf e cerômero - 51,20±10,08 kgf que... / The aim of this study was to compare the fracture resistance and failure of maxillary incisors restored using fiber post and metallic post under different types of full-coverage crowns. The null hypothesis tested was that fracture resistance and the failure pattern of these teeth were not affected by the use of fiber post, metallic post and typo of full coverage crown. Sixty maxillary incisors were divided into 6 groups of 10 each. G1- metallic post + metallic ceramic crowns, G2- metallic post + e-max system, G3- metallic post + cerômeros, G4- Fiber post and accessories post + metallic ceramic crowns, G5- Fiber post and accessories post + e-max system and G6- Fiber post and accessories post + cerômeros. The specimens were submitted a mechanical loading at a frequency of 2 Hz for a total of 500.000 cycles. After were taken to the Universal Test Machine for the fracture resistance at 1,0 mm/min speed. The fracture resistance values were G1- 47.44 ± 10.39, G2- 54.74 ±7.76, G3-49.71 ± 8.66, G4- 54.97 ± 8.67, G5-73.50 ± 11.83 e G6- 55.47 ± 10.62. Results show statistically significant differences in relation to the type of the posts (ANOVA) (p<0,05). Fracture analyses about metallic post showed the most unfavorable fracture and fiber post restored with metallic crown showed statistically significant difference in relation to the others groups. Tukey test (5%) showed Metallic-crown - 64,12±13,69 kgf, is statistically difference than the other crowns metal free - 52,59±9,88 kgf and Sinfony crowns - 51,20±10,08 kgf that was not different between itself. The result of this study indicate that the use of fiber posts increase their resistance to fracture and improve the prognosis in case of fracture

Orientador: Lafayette Nogueira Junior / Banca: Eduardo Shigueiuki Uemura / Banca: Mário Alexandre Coelho Sinhoreti / Banca: Mauro Antonio de Arruda Nóbilo / Banca: Tarcísio José de Arruda Paes Junior / Resumo: O objetivo neste estudo foi avaliar e comparar a resistência à fratura de incisivos centrais restaurados usando dois tipos de pinos intra-radiculares: núcleo metálico fundido e pinos de fibra de quartzo, reconstruídos com diferentes tipos de coroas. A hipótese nula testada foi que a resistência a fratura desses corpos de prova não apresentariam diferença quanto ao tipo de pino e tipo de coroa. Sessenta incisivos centrais superiores foram divididos em 6 grupos: G1- núcleo metálico fundido + coroa em cerômero, G2- núcleo metálico fundido + coroa metalo-cerâmica, G3- núcleo metálico fundido + coroa em e-max, G4 - pino de fibra de quartzo e pinos acessórios + coroa em cerômero, G5- pino de fibra de quartzo e pinos acessórios + coroa metalo-cerâmica e G6- pino de fibra de quartzo e pinos acessórios + coroa em e-max. Todos os espécimes foram submetidos à ciclagem mecânica com freqüência de 2 Hz e 500.000 ciclos com carga de 3Kg. Os corpos de prova foram submetidos a teste de compressão em uma máquina universal de ensaios (Emic) com velocidade de carga de 1,0 mm/min até a sua fratura. Os valores de resistência à fratura foram G1- 47.44 ± 10.39, G2- 54.74 ±7.76, G3-49.71 ± 8.66, G4- 54.97 ± 8.67, G5-73.50 ± 11.83 e G6- 55.47 ± 10.62. A análise de variância (ANOVA) (p<0,05) mostrou diferença estatisticamente significante para os pinos. Quanto à análise de fratura, os núcleos metálicos fundidos apresentaram o maior número de amostras com fratura desfavoráveis quando comparados os pinos de fibra de quartzo. O conjunto pino de fibra restaurados com coroa metalo cerâmica, apresentou valor de resistência à fratura estatisticamente maior quando comparado aos demais grupos segundo o teste de Tukey (5%), Metalo cerâmica - 64,12±13,69 kgf, difere estatisticamente das demais coroas metal free - 52,59±9,88 kgf e cerômero - 51,20±10,08 kgf que... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aim of this study was to compare the fracture resistance and failure of maxillary incisors restored using fiber post and metallic post under different types of full-coverage crowns. The null hypothesis tested was that fracture resistance and the failure pattern of these teeth were not affected by the use of fiber post, metallic post and typo of full coverage crown. Sixty maxillary incisors were divided into 6 groups of 10 each. G1- metallic post + metallic ceramic crowns, G2- metallic post + e-max system, G3- metallic post + cerômeros, G4- Fiber post and accessories post + metallic ceramic crowns, G5- Fiber post and accessories post + e-max system and G6- Fiber post and accessories post + cerômeros. The specimens were submitted a mechanical loading at a frequency of 2 Hz for a total of 500.000 cycles. After were taken to the Universal Test Machine for the fracture resistance at 1,0 mm/min speed. The fracture resistance values were G1- 47.44 ± 10.39, G2- 54.74 ±7.76, G3-49.71 ± 8.66, G4- 54.97 ± 8.67, G5-73.50 ± 11.83 e G6- 55.47 ± 10.62. Results show statistically significant differences in relation to the type of the posts (ANOVA) (p<0,05). Fracture analyses about metallic post showed the most unfavorable fracture and fiber post restored with metallic crown showed statistically significant difference in relation to the others groups. Tukey test (5%) showed Metallic-crown - 64,12±13,69 kgf, is statistically difference than the other crowns metal free - 52,59±9,88 kgf and Sinfony crowns - 51,20±10,08 kgf that was not different between itself. The result of this study indicate that the use of fiber posts increase their resistance to fracture and improve the prognosis in case of fracture / Doutor

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2008-03-05Bitstream added on 2014-06-13T19:10:18Z : No. of bitstreams: 1 clavijo_vgr_me_arafo.pdf: 1143518 bytes, checksum: fc7de1c4fc0422cee9413ae0dcdfbad7 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / A reabilitação de raízes fragilizadas é um procedimento complexo com prognóstico duvidoso. Este estudo, avaliou por meio de compressão, a resistência à fratura e o padrão de fratura de raízes fragilizadas reabilitadas com diferentes técnicas de construção de núcleos intra-radiculares. Quarenta incisivos bovinos hígidos foram divididos em quatro grupos de acordo com a técnica de construção de pinos intra-radiculares: Grupo 1- raízes fragilizadas reabilitadas com núcleo metálico fundido; Grupo 2- raízes fragilizadas reabilitadas com pinos de fibra de vidro e pinos acessórios de fibra de vidro; Grupo 3- raízes fragilizadas reabilitadas com pino anatômico direto (resina composta + pino de fibra de vidro) ; Grupo 4- raízes fragilizadas reabilitadas com pino anatômico indireto de fibra de vidro. Todos os grupos tiveram seus núcleos cimentados com o cimento resinoso Multilink e as porções coronárias padronizadas por uma matriz de resina acrílica. Os corpos de prova forma submetidos à Máquina de Ensaio Universal à uma velocidade de carga de 0,5mm/min até sua fratura numa angulação de 135° em relação ao longo eixo do dente sobre a face palatina. Os valores médios de resistência à fratura foram: Grupo 1- 575,54N; Grupo 2- 400,49N; Grupo 3- 483,39N; Grupo- 4 559,19N. A análise de variância (ANOVA) (p<0,05) a um critério mostrou diferença estatisticamente. O grupo 1 e 4 médias diferentes, porém estatisticamente iguais, mas maiores estaticamente que o grupo 2 e 3. Os percentuais de raízes com prognóstico favorável após a fratura foram: Grupo 1- 0%; Grupo 2- 80%; Grupo 3- 100% ; Grupo 4- 100%. Os pinos anatômicos direto e indireto mostraram ser uma nova opção para reabilitação de raízes fragilizadas. / The rehabilitation of weakened roots is a complex procedure with an unpredictable prognosis. This study evaluated by compression to fracture resistance and the fracture pattern of weakened roots restored with different construction techniques of intra-radicular posts. Forty hygid bovine incisors were divided into four groups according to each technique of construction of the intra-radicular posts: Group 1- weakened roots restored with metallic posts,; Group 2- weakened roots restored with glass fiber posts and accessory glass fiber posts; Group 3- weakened roots restored with direct anatomic posts (composite resin + glass fiber post); Group 4- weakened roots restored with indirect anatomic post (glass fiber post). All the groups were cemented with dual resinous cement (Multilink) and the coronal portions were patterned by an acrylic resin matrix. The specimens were submitted to a Universal Testing Machine at 0,5mm/min speed until its fracture at an angulation of 135° in relation to the long axis of the tooth. The mean values of fracture resistance were: Group 1- 575,54N; Group 2- 400,49N; Group 3- 483,39N; Group 4- 559,19N. The ANOVA values were (p<0,05) to one criteria showed statistic difference. Group 1 and the 4 different means were statistically the same, but statistically more than the ones of groups 2 and 3. The percentage of roots with favorable prognosis after fracture were: Group 1- 0%; Group 2- 80%; Group 3- 100%; Group 4- 100%. The direct and indirect anatomic post of glass fiber showed a new option to rehabilitate weakened roots.

Made available in DSpace on 2014-06-11T19:24:08Z (GMT). No. of bitstreams: 0 Previous issue date: 2009-02-18Bitstream added on 2014-06-13T20:51:29Z : No. of bitstreams: 1 bandeca_mc_me_arafo.pdf: 1959058 bytes, checksum: 3e43b01e5b78c0aaf4e1c073391f6b76 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Este estudo objetivou: (1) testar a hipótese que a utilização de pinos nãometálicos em dentes tratados endodonticamente está associado a longevidade da restauração através de uma revisão sistemática; (2) avaliar o grau de conversão de dois cimentos resinosos em diferentes tempos após a fotoativação; (3) avaliar a resistência adesiva de diferentes cimentos resinosos usando dois pinos não-metálicos; (4) e avaliar a resistência a fratura e padrão de falha de dentes submetidos ao clareamento dental interno usando peróxido de hidrogênio a 35% restaurados com diferentes procedimentos. No artigo 1, 157 artigos participaram do estudo e após os critérios de inclusão-exclusão, restaram apenas 5 artigos. Para o artigo 2, vinte espécimes foram confeccionados para cada cimento, Panavia® F2.0 e RelyXTM Unicem Applicap. Cada espécime foi curado com luz LED e foram analisados imediatamente, 24 horas, 48 horas e 7 dias após a fotoativação. Os testes usados foram grau de conversão (FT-IR) e termogravimetria. No artigo 3, oitenta dentes pré-molares unirradiculares livres de coroas foram usados e divididos em 8 grupos: os pinos Exacto! e Everstick! foram cimentados com Breeze!, Nexus! 3, Panavia! e Bistite!. Os dentes foram obturados e preparados para cimentação dos pinos não-metálicos. Cada espécime foi perpendicularmente seccionado em aproximadamente 1 mm de espessura em 6 discos e divididos em região ! cervical, médio e apical. No artigo 4, oitenta dentes incisivos inferiores foram usados e metade foram clareados. Os dentes foram restaurados com resina composta, pinos de resina reforçado com fibra e pinos de fibra de vidro. Os pinos foram cimentados com Breeze! e Panavia!. Os espécimes foram submetidos ao teste de resistência a fratura pela máquina de testes universal. Todos os dados foram submetidos ao devido tratamento estatístico. Os pinos usados... / This study aimed: (1) To test the hypothesis that the placement of nonmetallic post in endodontically treated teeth is associated with improved survival rate of the restored teeth althouth systematic review; (2) to evaluate the degree of conversion of two resin cements in differents times after light-activated; (3) to evaluate the microtensile bond strength of different resin cement systems using two nonmetallic posts; (4) to evaluate the fracture resistance and failure pattern of endodontically treated teeth after intracoronal bleaching using 35% hydrogen peroxide with different restorative procedures. For the article 1, 157 papers were used and after the inclusion-exclusion procedure, only 5 papers remained. For the article 2, twenty specimens were made for each cement, Panavia® F2.0 and RelyXTM Unicem Applicap. Each specimen were cured with LED and were tested immediately, 24 hours, 48 hours and 7 days after light-activated. The tests used were degree of conversion (FT-IR) and thermogravimetric. For the article 3, eighty single-rooted human mandibular first premolar free crown were used and divided into 8 groups: Exacto! and Everstick! posts were cemented with Breeze!, Nexus! 3, Panavia! F 2.0 and Bistite! II DC. The teeth were obtured and prepared for cementation of the nonmetallic posts. Each specimen were perpendicularly sectioned into approximately 1 mm thick sections resulting in 6 serial slices and divided in cervical, meddium and apical region. For the !article 4, eighty mandibular incisors were used and the half teeth were bleached. The teeth were restored with composite resin, fiber-reinforced composite post and glass fiber post. The posts were cemented with Breeze! and Panavia!. The specimens were submitted to the fracture resistance test by universal test machine. Statistical analyses were performed for each article. The posts used... (Complete abstract click electronic access below)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O propósito desse trabalho foi verificar a retenção de pinos fibro resinosos cimentados em canais radiculares alargados simulando raízes extensamente comprometidas, fabricados por duas técnicas usadas para diminuir sua desadaptação; comparando-as ao pino fixado somente com cimento. Foram utilizados vinte e quatro raízes de dentes humanos unirradiculares, padronizadas com 15.0 mm de comprimento e 5.0 0.3 mm de diâmetro. As raízes foram incluídas em resina acrílica e divididas em grupos de acordo com a técnica usada: grupo I - pino DC White Post no2 cimentado com sistema adesivo quimicamente ativado e com cimento resinoso dual; grupo II mesmo pino reanatomizado com resina composta para copiar a anatomia do canal radicular, cimentado da mesma forma; e grupo III mesmo pino associado a três pinos acessórios, cimentados do mesmo modo. O canal radicular teve seu diâmetro padronizado pela broca no2 para o pino DC em uma profundidade de 12.0 mm e alargado com uma broca tronco cônica em uma profundidade de 10.0 mm. As oito raízes de cada grupo foram seccionadas transversalmente em três discos de 3.0 mm, a partir da cervical para a execução de um ensaio de extrusão, descartando-se os últimos 2.0 mm, que serviram somente para centralizar o pino. Os valores de retenção foram registrados e tratados estatisticamente por ANOVA e pelo teste SNK (p<0.05). Diferenças significativas foram observadas entre três porções radiculares investigadas em todos os grupos, com os valores de retenção diminuindo da cervical para apical. A retenção na porção apical do grupo com pinos customizado com resina foi estatisticamente maior que na mesma região dos demais grupos. Nenhuma diferença foi encontrada entre o grupo com pinos acessórios e o grupo somente com pino e cimento nessa parte da raiz. Nenhuma diferença foi observada comparando as porções cervical e média dos diferentes grupos. Os tipos de falha após o teste de extrusão foram observados em microscópio eletrônico de varredura com aumento de 200, 600 e 1000 vezes. Elas ocorreram exclusivamente entre o pino e o cimento ou a resina composta. A camada de adesão (camada híbrida) foi mais facilmente observada nas porções cervical e média de todos os grupos. Isso sugere que a retenção nas porções apicais da raiz é predominantemente friccional. Uma vez que pinos acessórios somente alcançam até a porção média do canal radicular, a retenção do pino não é aumentada com essa técnica. / The aim of this study was to evaluate the retention of fiber posts cemented in enlarged root canals simulating compromised roots, fabricated with to two techniques used to minimize your desadptation; comparing it to posts fixed only with ciment. Twenty four single root human teeth standardized in 15.0mm length and 5.0 0.3mm diameter were used. The roots were imbibed in acrylic resin and divided in groups according to the technique used: group I - DC White Post no2 cemented with quimically cured adhesive system and a dual cured resin cement; group II the same post customized with composite resin to copy the root canal anatomy, cemented the same way; and group III the same post associated with three accessory posts, cemented the same way. The root canals had their diameter standardized using a no2 DC post burs 12.0 mm deep and enlarged with a chamfer bur 10.0 mm deep. The eight roots of each group were transversely sectioned in three 3.0 mm diameter discs, starting from cervical to make the push out test, discarding the last 2.0mm used only to centralize the post. The retention values were registered and statistically treated with ANOVA and SNK tests (p<0.05). Significant differences were observed when comparing the three root portions of all groups investigated, with retention values decreasing from cervical to apical. The retention in apical portion of customized posts was statistically greater than the same parts of other groups. No differences were found between the group with accessory posts and only cemented posts in this root portion. No differences was observed comparing cervical e middle portions of different groups. The failure types after the push out test were observed in MEV with 200, 600 e 1000x magnification. They occurred exclusively between the post and the resin cement or the composite resin. A hybrid layer was more easily observed in the cervical and middle portions of the roots in all groups. This suggests that the retention in the apical portions of roots is mostly frictional. Since accessory posts only eventually can reach the middle portion of root canal the post retention is not increased with this technique.

Os cimentos resinosos têm sido largamente utilizados em odontologia restauradora com a finalidade de reter o pino intra-radicular e dissipar tensões entre este e a raiz. Entretanto, o grau de conversão alcançado pelos mesmos influencia suas propriedades mecânicas, biocompatibilidade e degradação pela água e pelos ácidos bucais. Testes de microdureza podem ser aplicados para estimar o grau de conversão de compósitos, uma vez que apresentam boa correlação com a espectroscopia infravermelha. Este trabalho objetivou analisar a microdureza de quatro cimentos resinosos de polimerização dual utilizados na cimentação de pinos de fibra de vidro, nos períodos inicial, após 24 horas de imersão em etanol a 75% e após 3 meses de armazenamento em água, e testar a hipótese de que não há diferença entre a microdureza dos terços cervical, médio e apical na linha de cimento. Quarenta incisivos bovinos tratados endodonticamente foram distribuídos em quatro grupos para a cimentação de pinos Fibrekor® (Jeneric/Pentron) de 1mm de diâmetro, sendo: Grupo 1 - Panavia F 2.0 (Kuraray Medical Inc.), Grupo 2 - Variolink (Ivoclar), Grupo 3 - Rely X Unicem (3M ESPE) e Grupo 4 - Duolink (Bisco). Após a cimentação, as raízes foram divididas em 2 subgrupos, sendo 5 seccionadas após 7 dias para análise da microdureza inicial e 5 mantidas íntegras em água deionizada por 3 meses, para avaliação da microdureza final no microdurômetro Shimadzu HMV (Japan). Após a mensuração inicial, as raízes seccionadas eram armazenadas a 37º C por 24h em 10mL de solução de etanol a 75%, e reavaliadas. Foram identificadas diferenças estatisticamente significativas entre cimentos, terços e períodos (inicial ou após 24h de imersão em etanol a 75%), bem como interações entre cimento/terços e cimento/períodos de avaliação. O cimento Panavia exibiu os valores de microdureza inicial significativamente superiores, sem diferença estatística entre os demais cimentos. Os valores de microdureza inicial por terços não seguiram um padrão homogêneo; os cimentos Variolink e Duolink exibiram valores de microdureza significativamente superiores no terço cervical, sem diferença significativa entre os terços para os demais cimentos. A imersão em etanol reduziu significativamente a média dos valores de dureza para todos os cimentos; o comportamento por terços variou em função do material. O armazenamento em água por 3 meses não exerceu influência sobre a dureza da maioria dos cimentos, com exceção do Unicem, que exibiu aumento significativo dos valores de dureza após esse período. Portanto, a hipótese proposta neste estudo foi rejeitada. / Resin cements have been largely used in dentistry for retaining intraradicular posts and to minimize tension between them. However, the degree of conversion influences mechanical properties, biocompatibility and susceptibility of water and acid degradation of these polymers. Hardness tests are used to estimate the degree of conversion of composites, as it shows good correlation with infrared spectroscopy. The aim of this study was to evaluate the microhardness of four resin cements used for fiber posts cementation at the nitial period, 24h-immersion in a 75% ethanol solution and after 3-month water storage. Forty bovine incisives were endodontically treated and restored with 1mm diameter Fibrekor® posts (Jeneric/Pentron), being: Group 1 - Panavia F 2.0 (Kuraray Medical Inc.), Group 2 - Variolink (Ivoclar), Group 3 - Rely X Unicem (3M ESPE) and Group 4 - Duolink (Bisco). After cementation, each group was divided in two subgroups: 5 roots were sectioned 7 days after cementation for initial hardness measurement and 5 roots were immersed in deionized water for 3 months for final hardness measurements using Shimadzu Micro Hardness Tester (HMV, Japan). After the initial measurements, the sectioned roots were immersed in 10mL 75% ethanol solution for 24h at 37ºC, and tested again. Differences in hardness values have been detected among resin cements, radicular thirds and periods (initial or 24h-immersion in a 75% ethanol solution). Data also revealed significant interaction to cement/third and cement/period of evaluation. Panavia showed higher hardness values, with no statistical differences among the other cements. It was not verified a homogeneous pattern regarding radicular third; Variolink and Duolink exhibited higher hardness values for the cervical third, without differences among radicular thirds for the other cements. Hardness values decreased after ethanol immersion for all resin cements and the hardness according to radicular thirds varied among the materials. The hardness of tested resin cement showed no influence after 3-month water storage, except for Unicem as it showed an increase in Knoop hardness after this period. Therefore, the null hypotesis proposed was rejected.

Este trabalho teve como objetivo avaliar a microdureza de dois cimentos resinosos de polimerização dual (RelyX U100®, 3M-ESPE e Panavia F 2.0®, Kuraray), empregados na cimentação de pinos de fibra de vidro (Fibrekor-Jeneric® Pentron) variando o modo de polimerização em químico, fotoativação imediata ou tardia após 5min através de luz halógena, avaliando também o efeito do armazenamento em água deionizada por três meses. Este trabalho testou as seguintes hipóteses nulas: não há diferença nos valores de microdureza entre os cimentos, modo de polimerização, efeito do armazenamento e entre os terços radiculares. Sessenta raízes de incisivos bovinos, com 16mm de comprimento cérvico-apical, tiveram seus condutos obturados e, posteriormente, preparados para cimentação do pino intracanal. Os espécimes foram divididos em 6 grupos (n = 10), cada um subdividido em 2 subgrupos com 5 espécimes para cada cimento. Os pinos foram cimentados de acordo com o protocolo descrito por cada fabricante. No grupo A1, os espécimes foram mantidos em ambiente à prova de luz para que ocorresse apenas a polimerização química. No grupo B1, os espécimes foram cimentados e submetidos à fotoativação imediata, e, no grupo C1, realizou-se a fotoativação após 5 minutos. As raízes foram seccionadas longitudinalmente, para que a linha de cimento pudesse ser exposta e os testes de microdureza realizados. Após 7 dias, as médias de microdureza (± desvio padrão) foram obtidas, para os terços cervical, médio e apical, respectivamente: A1 (Panavia) - 41,25 ±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. Para os grupos armazenados em água, os valores médios de microdureza (± desvio padrão) obtidos nos 3 grupos, químico (grupo A2), fotoativado imediatamente (grupo B2) e fotoativado tardiamente (grupo C2), nos terços cervical, médio e apical, respectivamente, foram: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. Os resultados foram submetidos ao teste ANOVA a 4 critérios (cimento, modo de polimerização, armazenamento e terços), que detectou diferenças estatísticas entre os grupos, e o teste de Tukey foi aplicado para comparações individuais. Os resultados mostraram que: a fotoativação com luz halógena promoveu um aumento significativo nos valores de microdureza para o cimento Panavia; o armaz namento em água por três meses reduziu os valores de microdureza para a maioria dos grupos, sendo que o cimento o U100 apresentou menor variação de dureza quando comparado ao Panavia; os terços que receberam maior intensidade de luz halógena tiveram maior aumento de microdureza para ambos os cimentos, especialmente para o cimento Panavia. Conclui-se, portanto, que as hipóteses de nulidade propostas foram rejeitadas. / The objective of this study was to evaluate the microhardness of two dual cure resin cements (RelyX - U100®, 3M-ESPE and Panavia F 2.0®, Kuraray), used for fiberglass posts (Fibrekor ® - Jeneric Pentron) cementation. Chemical cure and a halogen immediate and late light cure source were compared, and the effect of storage in deionized water for three months was also evaluated. This study tested the following null hypotheses: there is no difference between the microhardness values for each dual cure resin cement, cure source type, storage time, or root thirds. Sixty bovine incisor roots 16mm long had their roots restored and then prepared for post cementation. The specimens were divided into 6 groups (n = 10), and each group was subdivided into 2 subgroups with 5 specimens for each cement. The posts were cemented according to manufacturers instructions. In group A1, the specimens were kept in a light-proof environment to ensure only a chemical cure. In group B1, the specimens were restored and subjected to immediate light curing, and in group C1, light curing was performed after 5 minutes. The roots were longitudinally sectioned to expose the cement line and perform microhardness tests. After 7 days, the average microhardness (± standard deviation) values were obtained for the cervical, medium and apical thirds, respectively: A1 (Panavia ) - 41,25±3,38 / 38,17±1,74 / 35,63±1,73; A1 (U100) - 59,43±4,32 / 52,14±3,00 / 50,27±4,13; B1 (Panavia) - 75,29±4,84 / 60,36±6,76 / 48,97±3,33; B1 (U100) - 62,41±6,83 / 53,99±4,74 / 49,04±2,20; C1 (Panavia) - 70,22±1,93 / 61,00±4,48 / 56,46±7,51; C1 (U100) - 62,40±6,66 / 53,69±2,00 / 51,54±2,18. For the 3 groups stored in deionized water (chemical [group A2], immediate light curing [group B2] and late light curing [group C2]), the average microhardness values (± standard deviation) obtained for the cervical, medium and apical thirds, respectively were: A2 (Panavia) - 37,17±1,38 / 35,01±0,74 / 34,10±2,37; A2 (U100) - 52,39±2,00 / 52,13±3,01 / 51,06±1,48; B2 (Panavia) - 63,01±2,17 / 55,94±2,10 / 48,55±1,62; B2 (U100) - 58,81±2,34 / 55,19±1,42 / 55,71±3,17; C2 (Panavia) - 56,99±1,21 / 51,29±1,81 / 48,29±3,00; C2 (U100) - 59,02±2,04 / 57,05±2,04 / 54,95±1,05. ANOVA testing was used to detect statistical differences among the 4 criteria (cements, cure mode, storage and thirds) and the Tukey test was used for individual comparisons. The results showed that the halogen light cure promoted a significant increase in microhardness values for Panavia cement; storage in water for three months reduced microhardness values for most of the groups, although U100 resulted in less microhardness variation compared to Panavia; the thirds that received a higher intensity of halogen light had a higher increase in the average values of microhardness for both cements, especially for Panavia. Therefore, the null hypotheses proposed in this work were rejected.

A raspagem e o aplainamento radicular removem o cemento presente nesta área, o qual funcionaria como barreira de dentina contra a penetração de bactérias, toxinas e outros produtos vindos da superfície externa do dente. O objetivo deste estudo foi avaliar, in vitro, em dentes tratados endodonticamente, a resistência apresentada por diferentes materiais de cimentação na infiltração do azul de metileno, que poderia atravessar a dentina radicular, quando submetido a duas diferentes situações: a) raspagem e aplainamento do cemento radicular e b) remoção de cemento com pontas diamantadas. Para isso, utilizou-se 48 dentes humanos unirradiculares, cedidos pelo banco de dentes da FOUSP, tratados endodonticamente e preparados para receberem pinos. Estes foram modelados com resina acrílica para que, por meio de fundição, fossem obtidos os retentores intrarradiculares metálicos. Os dentes foram divididos em 4 grupos com 12 espécimes, e a cada um dos grupos, destinado um tipo de material diferente para a cimentação: Cimento de Zinco® (SS White, Rio de Janeiro, Rio de Janeiro, Brasil), Cimentos resinosos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos). Após esse procedimento, delimitaram-se duas janelas na região cervical da raiz, sendo que num dos lados o cemento foi removido com uma ponta diamantada e no lado oposto, com 40 golpes de cureta Gracey 5-6 (Neumar, São Paulo, São Paulo, Brasil) paralelos ao longo eixo do dente. Exceto nas regiões instrumentadas, o dente foi impermeabilizado externamente e exposto à solução de azul de metileno a 1% e pH 7,2 durante 48 horas. As amostras foram desgastadas no sentido do longo eixo até o maior diâmetro do pino e a área impregnada pelo corante foi digitalizada e mensurada com o programa Imagelab®. A comparação da área impregnada pelo agente traçador na película dos cimentos, nos terços cervical e médio, revelou diferenças estatisticamente significantes entre si (p < 0,05). No lado em que a dentina foi removida com broca, houve diferença estatisticamente significante quando os três materiais adesivos foram comparados com o Cimento de Zinco (SS White, Rio de Janeiro, Rio de Janeiro, Brasil). Na comparação entre os cimentos resinosos houve diferença estatisticamente significante (p<05) somente entre os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan) e Rely X U 100® (3M Dental, Seefeld, Alemanha) para o terço apical. Na superfície tratada com curetas periodontais, verificou-se diferença estatisticamente significante entre os grupos estudados (p < 0,05) apenas quando comparados o cimento Rely X U 100® (3M Dental, Seefeld, Alemanha) com Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) para o terço cervical. Concluiu-se que para o tratamento com ponta diamantada, que os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) têm comportamento semelhante para os terços cervical e médio, diferindo apenas no terço apical. Já para o tratamento com curetas periodontais, os cimentos Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Alemanha) e Rely X Luting 2® (3M Dental, Sant Paul, Estados Unidos) mostraram resultados similares para os terços médio e apical, diferindo apenas no terço cervical. / Scaling and root planning remove cementum present in this area, which would acts as a dentin barrier against penetration of bacterias, toxins and other products coming from the surface of the tooth. The objective of this study was to evaluate in vitro endodontically treated teeth, the resistance of different materials to methylene blue, which could cross the root dentin when submitted to two different situations: a) scaling and root planning b) removal of cementum with drills. It was used 48 human uniradicular teeth, assigned by FOUSPs teeth bank and were endodontically treated and prepared to receive pins. These were modeled with an acrylic resin in order to obtain the metallic intraradicular posts. The teeth were divided into four groups with twelve specimens. Each one of the groups received a different material for cementing: Cement of Zinc® (SS White, Rio de Janeiro, Rio de Janeiro, Brazil), Panavia F® Resin Cements (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States). After this procedure, it was delimited two windows in the cervical region of the root. One of the sides the cementum was removed with a diamond drill and on the other side, with 40 Gracey 5-6 curette strokes (Neumar, São Paulo, Brazil) parallel to the long axis of the tooth. Except on the instrumented regions, the tooth was externally sealed and exposed to a 1% methylen blue solution and pH 7.2 during 48 hours. The samples were scraped from the long axis until the largest post diameter. The impregnated area with the dye were scanned and measured with the Imagelab® program. The comparison between the impregnated area through the tracer agent on the cement film in the cervical and medium thirds revealed statistically significant differences (p<0,05). On the side where the dentin was removed with a drill, there was a statistically significant difference when the three adhesive materials were compared to the Zinc Cement (SS White, Rio de Janeiro, Rio de Janeiro, Brazil). In the comparison between the resin cements there was a statistically significant difference (p<0,05) only between the cements: Panavia F® (Kuraray, Kurashiki, Okayama, Japan) and Rely X U 100® (3M Dental, Seefeld, Germany) for the apical third. On the surface treated with periodontal curettes, it was identified a meaningful statistical difference between the studied groups (p<0,05) only when compared the cements: Rely X U 100® (3M Dental, Seefeld, Germany) with Rely X Luting 2® (3M Dental, Sant Paul, United States) for the cervical third. The conclusion was that when the treatment uses a drill, the cements: Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States) have similar behavior to the cervical and medium third. The unique difference comes from the apical third. On the other hand, the treatments using periodontal curettes, the cements Panavia F® (Kuraray, Kurashiki, Okayama, Japan), Rely X U 100® (3M Dental, Seefeld, Germany) and Rely X Luting 2® (3M Dental, Sant Paul, United States) resulted in similar results for the medium and apical thirds, only differing on the cervical third.

Sociala medier används mer och mer av kommuner och har bidragit med nya möjligheter för kommunerna. Det är ett verktyg som används av kommunerna för att förse sina följare med information. Det bidrar till att engagemanget hos följarna ökar och leder till att kommunerna använder sig av sociala medier för att integrera och ha en direkt kontakt med sina följare. Karlstads kommun är en av de 215 kommuner i Sverige som använder sig av sociala medier för att integrera med sina följare. Denna uppsats undersöker vad Karlstads kommun publicerar genom sin Facebooksida till sina följare. Syftet är att studera hur inläggen skiljer sig åt mellan de olika månaderna under ett helt år, och jämföras med Bellström et al. (2016) studie som lämnade intressanta resultat om än baserad på ett ganska snävt urval, inlägg under tre månader. Motiveringen till föreliggande studie var alltså att se om innehållsmönstret varierar med årstiderna. Resultatet av studien visar att Karlstads kommun publicerar flest inlägg som tillhör kategorierna ”Marknadsföra evenemang i kommunen” och ”Marknadsföra kommunen”. Skillnaderna över året är inte stora utan det är dessa två kategorier som är de kategorier som innehåller flest inlägg varje månad under denna studie och tidigare studier. Därför finns inga årstidsvariationer på inläggen Karlstads kommun publicerar och inläggen som publicerades under sommar 2015 och sommar 2016 stämmer överens med varandra.