Submitted by Marcele Costal de Castro (costalcastro@gmail.com) on 2017-09-04T16:54:30Z No. of bitstreams: 1 CELINA CÁNDIDA RIBEIRO BARBOSA D.pdf: 8959321 bytes, checksum: ba63053953807bce0238b186e984e673 (MD5) / Made available in DSpace on 2017-09-04T16:54:30Z (GMT). No. of bitstreams: 1 CELINA CÁNDIDA RIBEIRO BARBOSA D.pdf: 8959321 bytes, checksum: ba63053953807bce0238b186e984e673 (MD5) Previous issue date: 1994-12 / Copolímeros à base de estireno e divinilbenzeno impregnados com fosfato monoácido de bis (2-etil-hexila), DEHPA, foram preparados para utilização em cromatografia de extração. A impregnação de DEHPA foi realizada durante e após a síntese dos copolímeros. Durante a síntese, DEHPA foi impregnado puro ou combinado com metil-etil-cetona (MEK) ou com querosene (QUER). A influência das condições de síntese como a razão DEHPA/QUER, o grau de diluição e a adição do MEK ou QUER à uma quantidade fixa de DEHPA na morfologia dos copolímeros foi investigada. Soluções de DEHPA em metanol foram utilizadas na impregnação pós-síntese do copolímero. A capacidade e a velocidade de retenção de íons praseodímio III e neodímio III variaram com o grau de impregnação e com a morfologia dos copolímeros. Os copolímeros impregnados com DEHPA durante a síntese apresentaram capacidades de retenção mais altas do que os impregnados com DEHPA pós-síntese. Os suportes impregnados com DEHPA com as melhores características quanto à cinética e à capacidade de retenção foram utilizados na separação em coluna de íons Pr3+ e Nd3+. A eficiência de separação variou com o grau de impregnação, com a estrutura porosa e com a distribuição de DEHPA no interior das pérolas de copolímero.

A adição de elementos dopantes e elementos de liga aos magnetos permanentes policristalinos à base de terras raras tem como objetivo a melhora das propriedades magnéticas. Neste trabalho estudou-se a adição de 0,1% at. dos elementos: Ti, V, Cr, Ni, Zr, Nb ou Mo na composição Pr14FebalCo16B6 ; as adições de 0,1 % at., 0,3 % at. e 0,5 % at. dos elementos Al, Si, P, Cu ou Ga na composição Pr14FebalCo16B6Nb0,1 ; e a variação de cobalto de 0 % at. até 16 % at. ao sistema Pr2Fe14-xCoxB. Através de processo HDDR (hidrogenação, desproporção, dessorção e recombinação) obteve-se pós com tamanho de grão da ordem de 200 a 300 nm para quase todas as composições estudadas. Os pós foram utilizados para a confecção de magnetos consolidados por cianoacrilato de baixa viscosidade. De maneira geral, a adição destes dopantes resultou no aumento ou diminuição da remanência e da coercividade intrínseca da liga quando comparadas com os valores obtidos para magnetos de referência sem adição de dopantes. Porém, não foram observadas correlações entre as composições estudadas quer quanto ao número atômico ou em relação à concentração do elemento adicionado. Os resultados obtidos com a adição de Al, Si, P, Ti, V, Cr, Ni, Cu, Ga, Zr ou Nb indicaram que alguns elementos atuam como substituintes do átomo de ferro na estrutura cristalina da fase magnética dura ou como modificador da microestrutura da liga. A determinação dos parâmetros da célula unitária, as posições atômicas, os sítios de substituição do ferro pelo cobalto (fator de ocupação) para a sistema Pr2Fe14-xCoxB foi realizada pelo refinamento dos padrões de pó obtidos por difração de raios X pelo método de Rietveld. Estes dados foram utilizados no cálculo das iii propriedades magnéticas por ab-initio com base na teoria do funcional densidade empregando o método LAPW (linearized augmented plane wave). A comparação dos resultados teórico e experimental apresentou forte concordância mostrando que este método é importante para o estudo da adição de dopantes ao sistema Pr-Fe-Co-B. / Estudo de Ligas e Ímãs Preparados pelo Processo Hidrogenação, Desproporção, Dessorção e Recombinação (HDDR) à Base de Pr-Fe-B com Adição de Dopantes e Elementos de Liga Eguiberto Galego RESUMO A adição de elementos dopantes e elementos de liga aos magnetos permanentes policristalinos à base de terras raras tem como objetivo a melhora das propriedades magnéticas. Neste trabalho estudou-se a adição de 0,1% at. dos elementos: Ti, V, Cr, Ni, Zr, Nb ou Mo na composição Pr14FebalCo16B6 ; as adições de 0,1 % at., 0,3 % at. e 0,5 % at. dos elementos Al, Si, P, Cu ou Ga na composição Pr14FebalCo16B6Nb0,1 ; e a variação de cobalto de 0 % at. até 16 % at. ao sistema Pr2Fe14-xCoxB. Através de processo HDDR (hidrogenação, desproporção, dessorção e recombinação) obteve-se pós com tamanho de grão da ordem de 200 a 300 nm para quase todas as composições estudadas. Os pós foram utilizados para a confecção de magnetos consolidados por cianoacrilato de baixa viscosidade. De maneira geral, a adição destes dopantes resultou no aumento ou diminuição da remanência e da coercividade intrínseca da liga quando comparadas com os valores obtidos para magnetos de referência sem adição de dopantes. Porém, não foram observadas correlações entre as composições estudadas quer quanto ao número atômico ou em relação à concentração do elemento adicionado. Os resultados obtidos com a adição de Al, Si, P, Ti, V, Cr, Ni, Cu, Ga, Zr ou Nb indicaram que alguns elementos atuam como substituintes do átomo de ferro na estrutura cristalina da fase magnética dura ou como modificador da microestrutura da liga. A determinação dos parâmetros da célula unitária, as posições atômicas, os sítios de substituição do ferro pelo cobalto (fator de ocupação) para a sistema Pr2Fe14-xCoxB foi realizada pelo refinamento dos padrões de pó obtidos por difração de raios X pelo método de Rietveld. Estes dados foram utilizados no cálculo das iii propriedades magnéticas por ab-initio com base na teoria do funcional densidade empregando o método LAPW (linearized augmented plane wave). A comparação dos resultados teórico e experimental apresentou forte concordância mostrando que este método é importante para o estudo da adição de dopantes ao sistema Pr-Fe-Co-B.

A adição de elementos dopantes e elementos de liga aos magnetos permanentes policristalinos à base de terras raras tem como objetivo a melhora das propriedades magnéticas. Neste trabalho estudou-se a adição de 0,1% at. dos elementos: Ti, V, Cr, Ni, Zr, Nb ou Mo na composição Pr14FebalCo16B6 ; as adições de 0,1 % at., 0,3 % at. e 0,5 % at. dos elementos Al, Si, P, Cu ou Ga na composição Pr14FebalCo16B6Nb0,1 ; e a variação de cobalto de 0 % at. até 16 % at. ao sistema Pr2Fe14-xCoxB. Através de processo HDDR (hidrogenação, desproporção, dessorção e recombinação) obteve-se pós com tamanho de grão da ordem de 200 a 300 nm para quase todas as composições estudadas. Os pós foram utilizados para a confecção de magnetos consolidados por cianoacrilato de baixa viscosidade. De maneira geral, a adição destes dopantes resultou no aumento ou diminuição da remanência e da coercividade intrínseca da liga quando comparadas com os valores obtidos para magnetos de referência sem adição de dopantes. Porém, não foram observadas correlações entre as composições estudadas quer quanto ao número atômico ou em relação à concentração do elemento adicionado. Os resultados obtidos com a adição de Al, Si, P, Ti, V, Cr, Ni, Cu, Ga, Zr ou Nb indicaram que alguns elementos atuam como substituintes do átomo de ferro na estrutura cristalina da fase magnética dura ou como modificador da microestrutura da liga. A determinação dos parâmetros da célula unitária, as posições atômicas, os sítios de substituição do ferro pelo cobalto (fator de ocupação) para a sistema Pr2Fe14-xCoxB foi realizada pelo refinamento dos padrões de pó obtidos por difração de raios X pelo método de Rietveld. Estes dados foram utilizados no cálculo das iii propriedades magnéticas por ab-initio com base na teoria do funcional densidade empregando o método LAPW (linearized augmented plane wave). A comparação dos resultados teórico e experimental apresentou forte concordância mostrando que este método é importante para o estudo da adição de dopantes ao sistema Pr-Fe-Co-B. / Estudo de Ligas e Ímãs Preparados pelo Processo Hidrogenação, Desproporção, Dessorção e Recombinação (HDDR) à Base de Pr-Fe-B com Adição de Dopantes e Elementos de Liga Eguiberto Galego RESUMO A adição de elementos dopantes e elementos de liga aos magnetos permanentes policristalinos à base de terras raras tem como objetivo a melhora das propriedades magnéticas. Neste trabalho estudou-se a adição de 0,1% at. dos elementos: Ti, V, Cr, Ni, Zr, Nb ou Mo na composição Pr14FebalCo16B6 ; as adições de 0,1 % at., 0,3 % at. e 0,5 % at. dos elementos Al, Si, P, Cu ou Ga na composição Pr14FebalCo16B6Nb0,1 ; e a variação de cobalto de 0 % at. até 16 % at. ao sistema Pr2Fe14-xCoxB. Através de processo HDDR (hidrogenação, desproporção, dessorção e recombinação) obteve-se pós com tamanho de grão da ordem de 200 a 300 nm para quase todas as composições estudadas. Os pós foram utilizados para a confecção de magnetos consolidados por cianoacrilato de baixa viscosidade. De maneira geral, a adição destes dopantes resultou no aumento ou diminuição da remanência e da coercividade intrínseca da liga quando comparadas com os valores obtidos para magnetos de referência sem adição de dopantes. Porém, não foram observadas correlações entre as composições estudadas quer quanto ao número atômico ou em relação à concentração do elemento adicionado. Os resultados obtidos com a adição de Al, Si, P, Ti, V, Cr, Ni, Cu, Ga, Zr ou Nb indicaram que alguns elementos atuam como substituintes do átomo de ferro na estrutura cristalina da fase magnética dura ou como modificador da microestrutura da liga. A determinação dos parâmetros da célula unitária, as posições atômicas, os sítios de substituição do ferro pelo cobalto (fator de ocupação) para a sistema Pr2Fe14-xCoxB foi realizada pelo refinamento dos padrões de pó obtidos por difração de raios X pelo método de Rietveld. Estes dados foram utilizados no cálculo das iii propriedades magnéticas por ab-initio com base na teoria do funcional densidade empregando o método LAPW (linearized augmented plane wave). A comparação dos resultados teórico e experimental apresentou forte concordância mostrando que este método é importante para o estudo da adição de dopantes ao sistema Pr-Fe-Co-B.

Made available in DSpace on 2017-07-21T19:26:08Z (GMT). No. of bitstreams: 1 Yuri Aparecido Opata.pdf: 4954287 bytes, checksum: c870711b60baa7a02a2a9d07afe3f6bd (MD5) Previous issue date: 2014-03-21 / This work presents an experimental study of changes in structural, electrical, magnetic, and mechanical properties / No presente trabalho é apresentado um estudo experimental das mudanças nas propriedades estruturais, elétricas, magnéticas e mecânicas

Pós magnéticos foram produzidos utilizando o processo de hidrogenação, desproporção, dessorção e recombinação (HDDR). A primeira parte deste trabalho envolveu o estudo do efeito da adição de Co na liga Pr14FebalCoxB6Nb0.1 (x= 0, 4, 8, 10, 12, 16) variando a de temperatura de dessorção/ recombinação de 800° a 900°C, com o objetivo de otimização do tratamento HDDR. A liga Pr14Fe80B6 foi utilizada como padrão. As ligas foram tratadas termicamente a 1100°C por 20 horas para eliminação do Fe- exixtente na liga em estado bruto de fusão. A temperatura de dessorção/ recombinação afetou a microestrutura e as propriedades magnéticas dos ímãs moldados com polímeros. A liga com baixa adição de cobalto (4 at.%) exigiu a temperatura de reação mais alta (880°C) entre os demais ímãs. As temperaturas ótimas para as ligas com 8 at.% Co e 10 at.% Co foram 840°C e 820°C, respectivamente. Ligas com altas concentrações de cobalto (12 at.% and 16 at.%) foram processadas a 840°C. A temperatura de dessorção/ recombinação que apresentou alta anisotropia nas ligas Pr14Fe80B6 e Pr14Fe79,9B6Nb0,1 foi de 820°C. O ímã que apresentou melhor remanência (862mT) foi processado com a liga Pr14Fe67,9Co12B6Nb0,1. Cada liga apresentou uma temperatura de reação otimizada e exibiu uma microestrutura particular, de acordo com a composição. A segunda parte deste trabalho envolveu a caracterização, dos pós HDDR de Pr14Fe80B6, que foram analisadas por difração de raios X com fonte síncrotron para a identificação e quantificação de fases cristalinas, e ainda para a determinação do tamanho médio de cristalitos da fase principal. A microscopia eletrônica de varredura (MEV) foi utilizada para revelar a morfologia dos pós HDDR. / Fine magnetic powders were produced using the hydrogenation disproportionation desorption and recombination (HDDR) process. The first stage in this work involved an investigation of the effect of the Co content and range of desorption/ recombination temperatures between 800 and 900°C with the purpose of optimizing the HDDR treatment for Pr14Fe80B6 and Pr14FebalCoxB6Nb0,1 (x= 0, 4, 8, 10, 12, 16) alloys. The cast alloys were annealed at 1100°C for 20 hours for homogenization. The processing temperature (desorption/ recombination) affected the microstructure and magnetic properties of the bonded magnets. The alloy with low cobalt content (4 at.%) required the highest reaction temperature (880°C) to yield anisotropic bonded magnets. The optimum temperature for alloys with 8 at.% Co and 10 at.% Co were 840°C and 820°C, respectively. Alloys with high cobalt content (12 at.% and 16 at.%) were processed at 840°C. The optimum desorption temperature for achieving high anisotropy for Pr14Fe80B6 and Pr14Fe79,9B6Nb0,1 was 820°C. The best remanence (862mT) was achieved with the Pr14Fe67,9B6Co12Nb0,1 magnet, processed at 840°C. Each alloy required an optimum reaction temperature and exhibited a particular microstructure according to the composition. The second stage of the work involved the characterization, for each temperature, of the Pr14Fe80B6 HDDR powder processed using X-ray diffraction analysis. The samples of the HDDR material were studied by synchrotron radiation powder diffraction using the Rietveld method for cell refinement, phase quantification and crystallite sizes determination. Scanning electron microscopy (SEM) has also been employed to reveal the morphology of the HDDR powder.

Made available in DSpace on 2017-07-21T20:42:31Z (GMT). No. of bitstreams: 1 Herve Stangler Irion.pdf: 4493069 bytes, checksum: 2fe9398c9c2006313a4b148ad265c9dd (MD5) Previous issue date: 2006-03-30 / In this work it was investigated the influence the in influence of the doping Pr6O11 in the electrical conductivity and in the microstructural properties in the basic ternary system (98,95 – x)%Sn02 1,0% Co0 0,05%Ta205. The used concentration of the doping Pr6011 had varied in 0,05%, 0.5% in mol, remaining constant the concentrations for the Co0 and Ta205. The processing applied was the conventional method of mixture of oxides in ambient atmosphere. The samples had been conformed in 50 MPa and sintered in 1350°C for 2 hours. After the sintering the densification of ceramics was verified with a value of 93,63% for the system with 0,1% in mol of Pr6011. The study of the electrical properties for the varistor system Sn02.Co0.Ta205 Pr6011 was carried out in continuous current in the ambient temperature and in function of the temperature. It was observed that the variation in the concentration of Pr6011 modifies the electrical behavior of the ceramics. The electrical parameters found are of [alfa]= 8,0, Er= 319 volts/cm and Vb= 0,66 volts/barrier for basic ternary system and [alfa]= 17,0 Er= 853 volts/cm and Vb= 1,15 volts/barrier with the addition of 0,10% in mol of Pr6011. The system with 0,05% mol 0.1% in mol Pr6011 presents the same value of the non linearity coefficient of the system with 0,1% in mol, however, with lower values of rupture tension and barrier tension (Er= 708 volts/cm and Vb= 0,98 volts/barrier). To concentration above of 0,1% in mol of Pr6011, the increase of the concentration of this doping, starts to be deleterious to the varistor characteristics. This effects is due to the increase in the concentration of the stannate of praseodymium phase (Pr2Sn207). This crystalline phase with the cassiterita phase (Sn02)was characterized by DRX and EDS and quantified by the refinement of Rietveld. / Neste trabalho investigou-se a influência do dopante Pr6O11 na condutividade elétrica e nas propriedades microestruturais no sistema ternário básico (98,95-x)%SnO2.1,0%CoO.0,05%Ta2O5. As concentrações utilizadas do dopante Pr6O11 variaram em 0,05%, 0,1%, 0,3% e 0,5% em mol, mantendo-se constante as concentrações para o CoO e Ta2O5 . O processamento empregado foi o método convencional de mistura dos óxidos. As amostras foram conformadas a 50 MPa e, sinterizadas a 1350ºC por 2 horas em atmosfera ambiente. Após a sinterização verificou-se densificação das cerâmicas, com valor de 93,63% para o sistema com 0,1% em mol de Pr6O11. O estudo das propriedades elétricas para o sistema varistor SnO2.CoO.Ta2O5 Pr6O11 foi realizado em corrente contínua a temperatura ambiente e, em função da temperatura. Observou-se que a variação na concentração de Pr6O11 altera o comportamento elétrico das cerâmicas. Os parâmetros elétricos encontrados são de [alfa] = 8,0, Er= 319 volts/cm e Vb= 0,66 volts/barreira para o sistema ternário básico e, [alfa] = 17,0, Er= 853 volts/cm e Vb = 1,15 volts/barreira com a adição de 0,10% em mol de Pr6O11. O sistema com 0,05% em mol de Pr6O11 apresenta o mesmo valor do coeficiente de não linearidade do sistema com 0,1 % em mol, entretanto, com valores menores de tensão de ruptura e tensão de barreira (Er= 708 volts/cm e Vb= 0,98 volts/barreira). Para concentrações acima de 0,1% em mol de Pr6O11, o aumento da concentração desse dopante, passa a ser deletério para as características varistoras. Esse efeito é devido ao aumento na concentração da fase cristalina estanato de praseodímio (Pr2Sn2O7). Essa fase cristalina, juntamente com a fase cassiterita (SnO2), foi caracterizada por DRX e por EDS e, quantificadas pelo refinamento de Rietveld.

Pós magnéticos foram produzidos utilizando o processo de hidrogenação, desproporção, dessorção e recombinação (HDDR). A primeira parte deste trabalho envolveu o estudo do efeito da adição de Co na liga Pr14FebalCoxB6Nb0.1 (x= 0, 4, 8, 10, 12, 16) variando a de temperatura de dessorção/ recombinação de 800° a 900°C, com o objetivo de otimização do tratamento HDDR. A liga Pr14Fe80B6 foi utilizada como padrão. As ligas foram tratadas termicamente a 1100°C por 20 horas para eliminação do Fe- exixtente na liga em estado bruto de fusão. A temperatura de dessorção/ recombinação afetou a microestrutura e as propriedades magnéticas dos ímãs moldados com polímeros. A liga com baixa adição de cobalto (4 at.%) exigiu a temperatura de reação mais alta (880°C) entre os demais ímãs. As temperaturas ótimas para as ligas com 8 at.% Co e 10 at.% Co foram 840°C e 820°C, respectivamente. Ligas com altas concentrações de cobalto (12 at.% and 16 at.%) foram processadas a 840°C. A temperatura de dessorção/ recombinação que apresentou alta anisotropia nas ligas Pr14Fe80B6 e Pr14Fe79,9B6Nb0,1 foi de 820°C. O ímã que apresentou melhor remanência (862mT) foi processado com a liga Pr14Fe67,9Co12B6Nb0,1. Cada liga apresentou uma temperatura de reação otimizada e exibiu uma microestrutura particular, de acordo com a composição. A segunda parte deste trabalho envolveu a caracterização, dos pós HDDR de Pr14Fe80B6, que foram analisadas por difração de raios X com fonte síncrotron para a identificação e quantificação de fases cristalinas, e ainda para a determinação do tamanho médio de cristalitos da fase principal. A microscopia eletrônica de varredura (MEV) foi utilizada para revelar a morfologia dos pós HDDR. / Fine magnetic powders were produced using the hydrogenation disproportionation desorption and recombination (HDDR) process. The first stage in this work involved an investigation of the effect of the Co content and range of desorption/ recombination temperatures between 800 and 900°C with the purpose of optimizing the HDDR treatment for Pr14Fe80B6 and Pr14FebalCoxB6Nb0,1 (x= 0, 4, 8, 10, 12, 16) alloys. The cast alloys were annealed at 1100°C for 20 hours for homogenization. The processing temperature (desorption/ recombination) affected the microstructure and magnetic properties of the bonded magnets. The alloy with low cobalt content (4 at.%) required the highest reaction temperature (880°C) to yield anisotropic bonded magnets. The optimum temperature for alloys with 8 at.% Co and 10 at.% Co were 840°C and 820°C, respectively. Alloys with high cobalt content (12 at.% and 16 at.%) were processed at 840°C. The optimum desorption temperature for achieving high anisotropy for Pr14Fe80B6 and Pr14Fe79,9B6Nb0,1 was 820°C. The best remanence (862mT) was achieved with the Pr14Fe67,9B6Co12Nb0,1 magnet, processed at 840°C. Each alloy required an optimum reaction temperature and exhibited a particular microstructure according to the composition. The second stage of the work involved the characterization, for each temperature, of the Pr14Fe80B6 HDDR powder processed using X-ray diffraction analysis. The samples of the HDDR material were studied by synchrotron radiation powder diffraction using the Rietveld method for cell refinement, phase quantification and crystallite sizes determination. Scanning electron microscopy (SEM) has also been employed to reveal the morphology of the HDDR powder.

Made available in DSpace on 2017-07-21T19:26:00Z (GMT). No. of bitstreams: 1 Cristiano Santos Lopes.pdf: 13551286 bytes, checksum: 1ba67329a96370d271e71e39f117ec62 (MD5) Previous issue date: 2010-11-19 / In this work we report on conductivity fluctuation measurements in polycrystalline samples of the Er1xPrxBa2Cu3O7 and Gd1xPrxBa2Cu3O7superconductor. Pr contents are 0.00, 0.05 and 0.10. Samples were prepared by the standard solid-state reaction technique and characterized by SEM, X-ray diffraction and electrical transport experiments. The samples were granular and homogeneous. The results were analyzed in terms of the temperature derivative of the resistivity and of the logarithmic temperature derivative of the conductivity, what allowed identifying power-law divergences of the conductivity. For Er1−xPrxBa2Cu3O7 samples, the results show that the transition proceeds in two stages: pairing and coherence transition. Also, our results, from the critical exponent analysis, show a two-peak splitting at pairing transition, indicating possibly a phase separation. On approaching the zero resistance state, our results show a power-law behavior that corresponds to a phase transition from paracoherent to a coherent state of the granular array. For Gd1−xPrxBa2Cu3O7 samples, it was observed that the critical temperature decreases and that the transition width increases with increasing Pr doping. Systematic measurements of fluctuation conductivity are reported and special attention is taken above the critical temperature, where Gaussian and critical regimes are observed. Below the critical temperature, on approaching the zero resistance state, our results show a power-law behavior consistent with a phase transition from a paracoherent to a coherent state of the granular array. / Neste trabalho foram estudados os efeitos das flutuações térmicas na condutividade elétrica de amostras policristalinas com base nos supercondutores Er1xPrxBa2Cu3O7 e Gd1xPrx Ba2Cu3O7. A quantidade de Pr considerada foi x = 0, 00, 0, 05 e 0, 10. As amostras foram preparadas pela técnica padrão de reação de estado sólido e caracterizadas por microscopia eletrônica de varredura, difração de raios-X e medidas de transporte eletrônico. As amostras são homogêneas e granulares. Para a obtenção dos expoentes críticos, os dados foram analisados em termos da derivada da resistividade em função da temperatura e da derivada logarítmica da resistividade em função da temperatura. Essa análise permitiu identificar regimes em lei de potência na paracondutividade durante a transição normal-supercondutora. Para a amostra de Er1−xPrxBa2Cu3O7, os resultados mostraram que a transição ocorre em dois estágios: transição de pareamento e transição de coerência. Contudo, os resultados obtidos através da análise dos expoentes críticos mostraram o desdobramento em dois picos da transição de pareamento, indicando uma possível separação de fase. Na aproximação do estado de resistência nula, os resultados mostraram um comportamento em lei de potência que corresponde à transição de fase paracoerente-coerente, típica de sistemas granulares. Para a amostra de Gd1−xPrxBa2Cu3O7, foi observado que a temperatura crítica diminuiu e que a largura da transição aumentou com o acréscimo da dopagem de Pr. Medidas sistemáticas na condutividade são apresentadas e é dada atenção especial em temperaturas ligeiramente acima da temperatura crítica, região na qual regimes Gaussianos e críticos são observados. Abaixo da temperatura crítica, na aproximação ao estado de resistência nula, os resultados mostram claramente regimes em lei de potência consistentes com a transição de fase paracoerente-coerente.