1 |
Estudo do comportamento cinético e mecânico-dinâmico de resinas epóxi a base de óleo de soja epoxidadoCosta, Ana Paula Oliveira January 2001 (has links)
Óleo de soja epoxidado foi curado com os anidridos: dodecenilsuccínico (DDS), maleico (MAL), ftálico (FTA), succínico e hexahidroftálico (CH). As reações foram iniciadas com aminas terciárias tais como trietilamina (TEA), N,N’-dimetilanilina (ARO) e 1,4- diazobiciclo[2,2,2]octano (DABCO). Calorimetria diferencial de varredura (DSC) foi aplicada com êxito no estudo da reação de cura e usada para a determinação dos parâmetros cinéticos e termodinâmicos. Foram estudados os efeitos eletrônicos, os fatores estéreos e a rigidez do segmento diéster formado devido na conversão de grupos anidridos. Foi observado que os anidridos maleico e ftálico reagem mais rápido do que os outros anidridos. A influência do iniciador e da razão molar (anidrido/grupo epóxido) foi igualmente considerada. As propriedades mecânicas e térmicas das resinas epóxi curadas usando TEA como iniciador foram investigadas por análise térmica dinâmico-mecânica (DMTA) e termogravimétrica (TGA). Todas as amostras apresentaram características de materiais termofixos. Os materiais termofixos obtidos a partir de anidridos com estruturas rígidas (FTA, MAL e CH) mostraram alta temperatura de transição vítrea e densidade de reticulação. Quando um excesso de grupos epóxido foi usado (R= 0,5), a temperatura de transição vítrea do material diminuiu. As resinas epóxi exibiram estabilidade térmica até 300ºC. Um comportamento inesperado foi observado para aquelas resinas obtidas com o anidrido dodecenilsuccínico (DDS). A influência do grau de epoxidação do óleo de soja nas propriedades mecânicas e na temperatura de transição vítrea foi investigada. Quanto maior o conteúdo de grupos epóxido, maior é a Tg e a dureza do material. As resinas epóxi preparadas a partir de óleo de soja epoxidado mostram excelente resistência química em NaOH e ácido sulfúrico, mas resistência pobre quando em contato com solventes orgânicos (tolueno, acetona, gasolina e etanol).
|
2 |
Estudo do comportamento cinético e mecânico-dinâmico de resinas epóxi a base de óleo de soja epoxidadoCosta, Ana Paula Oliveira January 2001 (has links)
Óleo de soja epoxidado foi curado com os anidridos: dodecenilsuccínico (DDS), maleico (MAL), ftálico (FTA), succínico e hexahidroftálico (CH). As reações foram iniciadas com aminas terciárias tais como trietilamina (TEA), N,N’-dimetilanilina (ARO) e 1,4- diazobiciclo[2,2,2]octano (DABCO). Calorimetria diferencial de varredura (DSC) foi aplicada com êxito no estudo da reação de cura e usada para a determinação dos parâmetros cinéticos e termodinâmicos. Foram estudados os efeitos eletrônicos, os fatores estéreos e a rigidez do segmento diéster formado devido na conversão de grupos anidridos. Foi observado que os anidridos maleico e ftálico reagem mais rápido do que os outros anidridos. A influência do iniciador e da razão molar (anidrido/grupo epóxido) foi igualmente considerada. As propriedades mecânicas e térmicas das resinas epóxi curadas usando TEA como iniciador foram investigadas por análise térmica dinâmico-mecânica (DMTA) e termogravimétrica (TGA). Todas as amostras apresentaram características de materiais termofixos. Os materiais termofixos obtidos a partir de anidridos com estruturas rígidas (FTA, MAL e CH) mostraram alta temperatura de transição vítrea e densidade de reticulação. Quando um excesso de grupos epóxido foi usado (R= 0,5), a temperatura de transição vítrea do material diminuiu. As resinas epóxi exibiram estabilidade térmica até 300ºC. Um comportamento inesperado foi observado para aquelas resinas obtidas com o anidrido dodecenilsuccínico (DDS). A influência do grau de epoxidação do óleo de soja nas propriedades mecânicas e na temperatura de transição vítrea foi investigada. Quanto maior o conteúdo de grupos epóxido, maior é a Tg e a dureza do material. As resinas epóxi preparadas a partir de óleo de soja epoxidado mostram excelente resistência química em NaOH e ácido sulfúrico, mas resistência pobre quando em contato com solventes orgânicos (tolueno, acetona, gasolina e etanol).
|
3 |
Estudo do comportamento cinético e mecânico-dinâmico de resinas epóxi a base de óleo de soja epoxidadoCosta, Ana Paula Oliveira January 2001 (has links)
Óleo de soja epoxidado foi curado com os anidridos: dodecenilsuccínico (DDS), maleico (MAL), ftálico (FTA), succínico e hexahidroftálico (CH). As reações foram iniciadas com aminas terciárias tais como trietilamina (TEA), N,N’-dimetilanilina (ARO) e 1,4- diazobiciclo[2,2,2]octano (DABCO). Calorimetria diferencial de varredura (DSC) foi aplicada com êxito no estudo da reação de cura e usada para a determinação dos parâmetros cinéticos e termodinâmicos. Foram estudados os efeitos eletrônicos, os fatores estéreos e a rigidez do segmento diéster formado devido na conversão de grupos anidridos. Foi observado que os anidridos maleico e ftálico reagem mais rápido do que os outros anidridos. A influência do iniciador e da razão molar (anidrido/grupo epóxido) foi igualmente considerada. As propriedades mecânicas e térmicas das resinas epóxi curadas usando TEA como iniciador foram investigadas por análise térmica dinâmico-mecânica (DMTA) e termogravimétrica (TGA). Todas as amostras apresentaram características de materiais termofixos. Os materiais termofixos obtidos a partir de anidridos com estruturas rígidas (FTA, MAL e CH) mostraram alta temperatura de transição vítrea e densidade de reticulação. Quando um excesso de grupos epóxido foi usado (R= 0,5), a temperatura de transição vítrea do material diminuiu. As resinas epóxi exibiram estabilidade térmica até 300ºC. Um comportamento inesperado foi observado para aquelas resinas obtidas com o anidrido dodecenilsuccínico (DDS). A influência do grau de epoxidação do óleo de soja nas propriedades mecânicas e na temperatura de transição vítrea foi investigada. Quanto maior o conteúdo de grupos epóxido, maior é a Tg e a dureza do material. As resinas epóxi preparadas a partir de óleo de soja epoxidado mostram excelente resistência química em NaOH e ácido sulfúrico, mas resistência pobre quando em contato com solventes orgânicos (tolueno, acetona, gasolina e etanol).
|
4 |
Resinas epoxi sililadas retardantes a la llama. Síntesis, caracterización y propiedadesMercado Roca, Luis Adolfo 02 December 2005 (has links)
Las resinas epoxi son ampliamente utilizadas en soldaduras, recubrimientos, adhesivos y materiales compuestos. En algunas aplicaciones las resinas epoxi requieren de funciones especiales y versátiles, tales como alta adhesión a los sustratos, bajo encogimiento, bajo estrés térmico después del curado, buena dureza, baja inflamabilidad y buena resistencia química. La inflamabilidad de las resinas epoxi es una de las principales desventajas en su aplicación debido a que, como todo polímero orgánico, son inherentemente combustibles y en presencia de una fuente de calor y de oxígeno se queman fácil y rápidamente. Por consiguiente, algunos retardantes al fuego, tales como compuestos bromados, óxidos de antimonio, compuestos fósforo-halogenados, etc. son incorporados en las resinas epoxi para reducir su inflamabilidad. Estos compuestos son excepcionalmente efectivos pero presentan el inconveniente que incrementan las cantidades de humos y productos de descomposición tóxicos y corrosivos que se desprenden durante la combustión del polímero. Por esta serie de inconvenientes en la actualidad se ha incrementado la investigación de otros heteroátomos como retardantes a la llama para reemplazar a los halógenos.En los últimos años se han descrito algunas aproximaciones sobre resinas epoxi con silicio unido covalentemente a la matriz polimérica. Así, han sido descritas modificaciones sobre resinas epoxi comerciales y copolimerizaciones de monómeros glicidílicos que contienen silicio con resinas epoxi comerciales, consiguiéndose una mejora de las propiedades retardantes a la llama sin sacrificar las propiedades mecánicas de la resina curada.En este trabajo se ha planteado como objetivo general el desarrollo de resinas epoxi basadas en silicio con propiedades retardantes a la llama. Así, se ha llevado a cabo la síntesis de monómeros glicidílicos que contienen silicio en su estructura. Para establecer una relación entre la presencia y proporción del silicio y las propiedades físicas de los materiales resultantes, se han preparado polímeros termoestables a partir de mezclas de un glicidilo comercial con los monómeros que contienen silicio así como prepolímeros obtenidos a través de reacciones de crecimiento de cadena entre el DGEBA y un silanodiol. También se han sintetizado monómeros y agentes de curado que contienen fósforo en su estructura y se han preparado polímeros termoestables que contengan ambos heteroátomos. Con objeto de estudiar el mecanismo de reacción de monómeros que contienen silicio con aminas primarias, se ha sintetizado un monómero sililado monofuncional, fenilglicidiloxidimetilsilano (GDMPS), y se ha comparado su reactividad frente a una amina primaria, anilina, con la de un glicidilo comercial, fenilglicidiléter (PGE). El estudio cinético fue llevado a cabo mediante NIR y aplicando a los datos espectrales obtenidos métodos de análisis multivariante de resolución de curvas (MCR-ALS). Se ha llevado a cabo el estudio cinético del curado de un diglicidilo que contiene silicio, fenildiglicidiloximetilsilano (DGPMS), y de las mezclas de éste con DGEBA con una diamina primaria, DDM, mediante DSC isotérmico y dinámico. Además, se han estudiado los fenómenos de gelificacion y vitrificación de estos sistemas mediante DMTA en modo cizalla y TMDSC. Se han preparado polímeros termoestables y se han evaluado sus propiedades termodinamomecánicas, térmicas y de retardancia a la llama. Las propiedades termodinamomecánicas han sido estudiadas mediante DMTA en modo de flexión. La estabilidad térmica de estos compuestos se ha estudiado mediante análisis termogravimétrico en atmósfera de nitrógeno y de aire. Las propiedades de retardancia a la llama fueron evaluadas mediante el test ASTM-D-2683 del índice de oxígeno limitante (LOI). Finalmente, se ha estudiado la degradación térmica de los polímeros obtenidos para establecer el modo de actuación del silicio durante la degradación. Para ello, se ha realizado el estudio cinético de la degradación a partir datos obtenidos por TGA, estudios de las etapas iniciales de la degradación mediante quimioluminiscencia (QL) y la caracterización de los productos formados por TGA-MS, GC-MS, ATR-FTIR y DRX.De los resultados obtenidos se han podido establecer las siguientes conclusiones: (1) Se ha determinado que la presencia del silicio produce un aumento en la reactividad del epóxido probablemente debido a efectos electrónicos. Esta mayor reactividad además reduce la importancia del camino autocatalítico en el curado con aminas primarias. (2) Las resinas epoxi sililadas termoestables muestran una disminución de la Tg y de la densidad de entrecruzamiento con el incremento del porcentaje de silicio.Esta disminución está relacionada con un aumento del volumen libre debido a la mayor longitud de los enlaces Si-O. (3) Los polímeros termoestables que contienen silicio muestran un incremento del LOI a partir de un contenido de silicio del 3%. En los polímeros que contienen silicio y fósforo, se encontraron evidencias de la existencia de sinergia entre los dos heteroátomos. (4) La degradación de los polímeros que contienen silicio, tanto en atmósfera inerte como oxidante, conlleva la formación de oligómeros cíclicos de fenilmetilsiloxano, lo que implica que parte del silicio abandona la fase condensada. El residuo contiene silicio como SiO2, formando probablemente una capa aislante que actúa como barrera térmica y de transferencia de masa disminuyendo de esta manera la producción de volátiles. / The epoxy resins are widely used in coatings, adhesives, composites, etc. In some applications of epoxy resins special and versatile features are required, such as high adhesion to the substrates, low shrinkage, low thermal stress after curing, toughness, chemical resistance and low flammability. The flammability of epoxy resins is the main drawback in their application. Some flame retardants compounds, such as brominebased compounds, antimony oxides, phosphorous-halogen compounds etc. are incorporated in the epoxy resins to reduce their flammability. These compounds are exceptionally efficient but they have the inconvenience that they increase the smoke and toxic and corrosive gas evolution during the combustion of the polymer. For these drawbacks in the last years it has been increased the investigation of other heteroatoms like flame retardants to replace the halogens.Some approaches about epoxy resins with silicon covalently bonded to the polymeric matrix have been reported. In this way, modifications of commercial epoxy resins and copolymerizations of silicon-based monomers with commercial epoxy resins giving to good flame retardancy, thermal and mechanical properties have been reported.The aim of this thesis is the development of novel fire retardant silicon-based epoxy resins. Glycidyl monomers with silicon in their structure, prepolymers obtained by mean of growth of chain reactions between diphenyl silanediol and diglycidylether of bisphenol A (DGEBA) and a phosphorous-containing glycidyl monomer and two phosphorilated diamines were synthesized. Thermoset polymers were obtained from curing reactions of the compounds synthesized. To study the reaction kinetics of silicon-containing epoxy monomer with primary amines, a monofunctional silicon-containing epoxy monomer has been sinthesized, glycidyloxydimethylphenyl silane (GDMPS), and its reactivity with a primary amine, aniline, has been compared with that of a commercial epoxy monomer, phenylglycidylether (PGE). Kinetics studies were carried out by Near Infrared Spectroscopy (NIR) and applying to the spectral data obtained the multivariate resolution of curves methods. Likewise, the kinetic and curing behaviour studies for the difunctional silicon-containing epoxy monomer, diglycidyloxyphenylmethyl silane (DGPMS), and the mixtures of this monomer with DGEBA with a primary diamine, 4,4'- diaminediphenylmethane (DDM), have been carried out by means of isothermal and dynamic DSC. The gelation and vitrification for these systems have been studied by thermodinamechanical analysis (DMTA) with a shear sandwich clamp and modulated temperature differential scanning calorimetry (TMDSC).The relationship between the amount of silicon and the thermodinamomechanical, thermal and flame retardancy properties of the thermoset materials obtained have been established. Thermoset materials were obtained from mixtures of commercial glycidyl monomer, DGEBA, with a silicon-containing glycidyl monomer, diglycidyloxyphenylmethyl silane (DGPMS), and their properties have been evaluated.Thermodinamomechanical properties have been evaluated by DMTA using a 3-point bending clamp. The thermal stability have been analyzed by thermogravimetric analysis (TGA) in nitrogen and air atmospheres. The flame retardant properties have been evaluated by means of ASTM-D-2683, the limiting oxygen index test (LOI).Finally, the thermal degradation of the silicon-containing polymers has been investigated by means of chemiluminiscence (CL), TGA-MS, GC-MS, ATR-FTIR andDRX.From the results obtained the following conclusions can be infered: (1) The silicon occurrence increases the reactivity of the epoxide due to electronic effects. This higher reactivity also reduces the importance of the autocatalytic path in the curing reactions with primary amines. (2) The thermoset epoxy resins showed a decrease in the Tg and the crosslinking density when the amount of silicon increases. This decrease is related with an increase of the free volume due to the Si-O and Si-C bonds. (3) The siliconcontaining thermosets show an increment of the LOI for silicon contents higher than 3%. In the polymers that contain silicon and phosphorous, there are evidences of the synergyc effect. (4) During the degradation of the silicon-containing materials in both, nitrogen and air atmospheres, cyclic siloxane oligomers were released. A silicon oxide rich char is formed, probably forming an insulating layer.
|
5 |
Estudo do envelhecimento físico de sistemas epoxidílicos estequiométricos DGEBA/DDM através de análise térmicaGiugno, Izabel Cristina Riegel January 1997 (has links)
o comportamento, frente ao envelhecimento físico, do sistema diglicidil éter do bisfenol-A (DGEBA) curado com diaminodifenilmetano (DOM) foi estudado em função da estrutura química, induzida pela cura, e do tempo de envelhecimento. Sistemas estequiométricos foram submetidos a Calorimetria Diferencial de Varredura (DSC) e Análise Térmica Dinâmico-Mecânica (DMTA). A cura isotérmica da resina epóxi foi realizada em uma etapa a 115°C e 135°C, por 20, 30, 45, 60 e 90 mino As amostras foram envelhecidas a 100°C por períodos de 4 até 72h. A extensão do envelhecimento físico foi associado com a área do pico endotérmico que aparece na região da transição vítrea, de acordo com os termogramas de DSC. Foi observado que a entalpia de relaxação aumenta gradualmente com o tempo de envelhecimento. Por DMT A, observou-se variações na magnitude do fator de perda (tan õ), no pico máximo, em função do grau de cura e do tempo de envelhecimento. O módulo dinâmico de armazenamento a 100°C (E'1CX)) deslocou-se para valores maiores assim como a Tg, medida através do pico a da curva log E", com o aumento do tempo de envelhecimento. A velocidade de envelhecimento e as energias de ativação da transição α foram obtidas a partir de parâmetros dinâmico-mecânicos e após associados com as diferentes histórias de cura e envelhecimento do material. De modo geral, a velocidade de envelhecimento (Ra) decresce com o aumento do grau de reticulação para sistemas curados a 115°C e passa por um mínimo para as amostras curadas a 135°C. As energias de ativação mostram uma tendência crescente com o tempo de envelhecimento. Concluiu-se que a técnica de DMTA é muito sensível às mudanças estruturais devido à cura e ao envelhecimento físico realizados nos sistemas investigados. Os resultados dinâmico-mecânicos obtidos para as misturas curadas segundo diferentes histórias térmicas salientam a importância da seleção adequada das condições de cura para que se possam obter as melhores propriedades destes materiais. / Physical aging behavior of diglycidyl ether of bisphenol-A (DGEBA) cured with diaminodiphenylmethane (DDM) have been investigated as a function of chemical structure, induced by cure, and aging time. Stoichiometric systems have been submitted to Differencial Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA) measurements. The isothermal curing of the epoxy resin was carried out in one step at 115°C and at 135°C for 20, 30, 45, 60 and 90 mino Samples were aged at 100°C for periods of time from 4 to a maximum of 72 h. The extent of physical aging has been measured by the area of the endothermic peak which appears within the glass transition region according to DSC thermograms. The enthalpy relaxation was found to increase gradually with aging time. Variations on magnitude of the loss factor (tan õ), on the maximum peak, have been observed as a function of degree of cure and aging time. The dynamic storage modulus at 100°C ( E' 100) changed with increasing physical aging to higher values as well as the glass transition temperature (Tg) as measured by the a peak on log E" curves. Aging rates and α transition activation energies were obtained through DMT A parameters analysis and then associated with different curing and aging histories of the material. Generally, the aging rate (Ra) decreases with increasing crosslinking degree for the systems cured at 115°C and passes through a minimum for those cured at 135°C. The activation energies demonstrate a tendecy to increase with aging time. It was concluded that the DMTA technique is very sensitive to structural changes in the investigated epoxy systems due to curing and physical aging . The DMTA results obtained from mixtures cured with different thermal histories underline the importance of adequate selection of curing conditions in order to obtain the optimum properties for these materiais.
|
6 |
Estudo do comportamento reocinético, propriedades de temperatura de transição vitrea e viscosidade de sistemas de resinas epoxiNascimento, Richard Rangel do 20 August 2010 (has links)
Made available in DSpace on 2016-06-02T20:37:45Z (GMT). No. of bitstreams: 1
3291.pdf: 2970196 bytes, checksum: bd8509cafdf12e15798864a0a09ea39e (MD5)
Previous issue date: 2010-08-20 / In this work, we have developed a study of the impact of two variables (Water and Monohydroyized Epoxy Resin) to Epoxy resin raw material in the behavior of the reactivity and viscosity of a " Epoxy System (Parts A - Resin Modified + Component B - Curing Agent) used in the manufacturing of blades Reinforced Plastic (FRP) for wind power generators. Over 90% of Global manufacturers of blades utilize the infusion process, which requires the speed of evolution of viscosity depending on the reactivity of the epoxy system meets specific conditions and limitations of the infusion process in their plants. Knowing that those two variables have a direct impact on the property of viscosity, we have evaluated separately the correlation of the variables with the epoxy resin and the component "A" of epoxy system. The objective of this project was to obtain the ability to predict and then set the best parameters for those variables that did not cause any disturbance rheokinetic when using Epoxy System. / Neste trabalho, foi desenvolvido um estudo do impacto de duas variáveis (Água e Resina Monohidrolisada) da matéria prima resina Epóxi no comportamento da reatividade e viscosidade de um Sistema Epóxi (Componentes A Resina Modificada + Componente B Agente de Cura), utilizado na fabricação de pás em Plástico Reforçado (FRP) para geradores de energia eólica. Mais de 90% dos fabricantes Globais de pás utilizam-se do processo de infusão, o qual exige que a velocidade da evolução da viscosidade em função da reatividade do sistema epóxi atenda às condições e limitações específicas do processo de infusão em suas plantas. Sabendo-se que as duas variáveis impactam diretamente na propriedade de viscosidade avaliamos isoladamente a correlação das mesmas na própria resina epóxi e no Componente A do sistema Epóxi. O objetivo deste projeto foi à obtenção da capacidade de prever e estabelecer os melhores parâmetros para que estas variáveis não causem nenhum distúrbio reocinético quando da utilização do Sistema Epóxi.
|
7 |
Estudo do envelhecimento físico de sistemas epoxidílicos estequiométricos DGEBA/DDM através de análise térmicaGiugno, Izabel Cristina Riegel January 1997 (has links)
o comportamento, frente ao envelhecimento físico, do sistema diglicidil éter do bisfenol-A (DGEBA) curado com diaminodifenilmetano (DOM) foi estudado em função da estrutura química, induzida pela cura, e do tempo de envelhecimento. Sistemas estequiométricos foram submetidos a Calorimetria Diferencial de Varredura (DSC) e Análise Térmica Dinâmico-Mecânica (DMTA). A cura isotérmica da resina epóxi foi realizada em uma etapa a 115°C e 135°C, por 20, 30, 45, 60 e 90 mino As amostras foram envelhecidas a 100°C por períodos de 4 até 72h. A extensão do envelhecimento físico foi associado com a área do pico endotérmico que aparece na região da transição vítrea, de acordo com os termogramas de DSC. Foi observado que a entalpia de relaxação aumenta gradualmente com o tempo de envelhecimento. Por DMT A, observou-se variações na magnitude do fator de perda (tan õ), no pico máximo, em função do grau de cura e do tempo de envelhecimento. O módulo dinâmico de armazenamento a 100°C (E'1CX)) deslocou-se para valores maiores assim como a Tg, medida através do pico a da curva log E", com o aumento do tempo de envelhecimento. A velocidade de envelhecimento e as energias de ativação da transição α foram obtidas a partir de parâmetros dinâmico-mecânicos e após associados com as diferentes histórias de cura e envelhecimento do material. De modo geral, a velocidade de envelhecimento (Ra) decresce com o aumento do grau de reticulação para sistemas curados a 115°C e passa por um mínimo para as amostras curadas a 135°C. As energias de ativação mostram uma tendência crescente com o tempo de envelhecimento. Concluiu-se que a técnica de DMTA é muito sensível às mudanças estruturais devido à cura e ao envelhecimento físico realizados nos sistemas investigados. Os resultados dinâmico-mecânicos obtidos para as misturas curadas segundo diferentes histórias térmicas salientam a importância da seleção adequada das condições de cura para que se possam obter as melhores propriedades destes materiais. / Physical aging behavior of diglycidyl ether of bisphenol-A (DGEBA) cured with diaminodiphenylmethane (DDM) have been investigated as a function of chemical structure, induced by cure, and aging time. Stoichiometric systems have been submitted to Differencial Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA) measurements. The isothermal curing of the epoxy resin was carried out in one step at 115°C and at 135°C for 20, 30, 45, 60 and 90 mino Samples were aged at 100°C for periods of time from 4 to a maximum of 72 h. The extent of physical aging has been measured by the area of the endothermic peak which appears within the glass transition region according to DSC thermograms. The enthalpy relaxation was found to increase gradually with aging time. Variations on magnitude of the loss factor (tan õ), on the maximum peak, have been observed as a function of degree of cure and aging time. The dynamic storage modulus at 100°C ( E' 100) changed with increasing physical aging to higher values as well as the glass transition temperature (Tg) as measured by the a peak on log E" curves. Aging rates and α transition activation energies were obtained through DMT A parameters analysis and then associated with different curing and aging histories of the material. Generally, the aging rate (Ra) decreases with increasing crosslinking degree for the systems cured at 115°C and passes through a minimum for those cured at 135°C. The activation energies demonstrate a tendecy to increase with aging time. It was concluded that the DMTA technique is very sensitive to structural changes in the investigated epoxy systems due to curing and physical aging . The DMTA results obtained from mixtures cured with different thermal histories underline the importance of adequate selection of curing conditions in order to obtain the optimum properties for these materiais.
|
8 |
Estudo da reação de cura da resina epoxi (araldit f) com anidrido ftálico e trietilamina como iniciadorRodrigues, Maria Regina Alves January 1992 (has links)
Este trabalho constitui-se do estudo da cinética e termodinâmica da reação de cura de um sistema bi-epoxi ( Araldit F + anidrido ftálico + trietilamina utilizando a Análise Térmica. através da técnica do DSC. o sistema foi analisado segundo métodos não-isotérmicos com a finalidade de verificar os efeitos da concentração da trietilamina bem como o da velocidade de aquecimento. Os métodos utilizados foram o da regressão multi-linear31, de freeman-carrol de Kissinger 49,50 e de. Osawa51. Os resultados obtidos demonstraram Que a reação de polimerização-reticulação do sistema segue a equação de Arrhenius, indicando um processo aproximadamente de primeira ordem (1. 5 l em relação a amina, e que os valores da energia de ativação sofrem um aumento com a adição da amina ao meio reacional. Comparando-se o estudo!54 realizado anteriormente Araldit F + anidrido succínico + trietilaminal no Laboratório de Instrumentação e Dinâmica Molecular, deste Instituto, e o sistema em estudo ( Araldit F + anidrido ftálico + trietilamina ), verifica- se um comportamento cinético termodinâmico similar com diferenciação nos valores da energia de ativação e no fator pré-exponencial. sem diferenças nos valores da ordem de reação. A presença da amina causa um aumento considerável nos valores da energia de ativação nos dois sistemas. Este aumento da energia de ativação nos leva a considerar a amina como iniciador no processo de polimerização e não como um catalisador como comumente é considerada. / This work includes the Kinetic and Thermodynamical study by Thermal Analvsis, using DSC technics, of the cure reaction: Araldite F + Phtalic Anhydride + Triethylamine. The system was analysed by non-isothermal methods with the purpose to study the effects Df triethylamine concentration. as well the rate Df heating. The theoretical - mathematical treatment used here 31 was according to the multi linear regressl.on 43 Freeman-Carrol, kissinger 49,50 an d Osawa 51 techniques. The results demonstrated that the polymerization network-formation reaction Df the system studied followed the Arrhenius equation, indicating approximately a first order process (1.5) with refference to amine. The values Df the Activation Energy increased with addition of amine to reactional medium. The system studied in this work (Araldite F + Phtalic Anhydride + Triethylamine represents a Kinetic and Thermodynamical behaviour similar to the behaviour of the reaction system (Araldite F + Succinic Anhydride + Triethylamine) studied,4 before. We observed different values of Activation Energy as well as Pre-Exponencial Factor, but same reaction order for the two differents svstems. The amine addition leads to a remarkable increase Df the Activation Energv in the two systems. This increase in Activation Energy permited us to consider the amine as initiator Df the polymer-ization process, but not as catalvst as it is usuallv considerated.
|
9 |
Análise da integridade estrutural de compósitos através da caracterização fractal de sinais de emissão acústica / Analysis of the structural integrity of composites through fractal characterization of acoustic emission signalsSilva, Francisco Estênio da 13 November 2002 (has links)
SILVA, F. E. Análise da integridade estrutural de compósitos através da caracterização fractal de sinais de emissão acústica. 2002. 102 f. Dissertação (Mestrado em Ciência de Materiais) – Centro de Tecnologia, Universidade Federal do Ceará, Fortaleza, 2002. / Submitted by Marlene Sousa (mmarlene@ufc.br) on 2016-03-31T14:51:57Z
No. of bitstreams: 1
2002_dis_fesilva.pdf: 2440731 bytes, checksum: fc3599b468ac7fe3e3f4b8337018a9cd (MD5) / Approved for entry into archive by Marlene Sousa(mmarlene@ufc.br) on 2016-03-31T18:36:30Z (GMT) No. of bitstreams: 1
2002_dis_fesilva.pdf: 2440731 bytes, checksum: fc3599b468ac7fe3e3f4b8337018a9cd (MD5) / Made available in DSpace on 2016-03-31T18:36:30Z (GMT). No. of bitstreams: 1
2002_dis_fesilva.pdf: 2440731 bytes, checksum: fc3599b468ac7fe3e3f4b8337018a9cd (MD5)
Previous issue date: 2002-11-13 / In this work it is analysed the mechanical integrity of the composite material constituted of a polymeric matrix, epoxy resin DER 331, reinforced by glass fiber type E. This analysis has been done by using the acoustic emission testing with the aim to correlating the wave-form of the pulse with the flaw mechanisms associated to the tensile and bending loads applied to the samples. The analysis of the pulses as a function of time has been made by using box counting method, which provides the fractal dimension, and the rescaled Hurst analysis. The analysis in the frequency domain has been made by using the spectral Fourier method It has been shown that the exponents obtained from the spectral Fourier method and the rescaled Hurst analysis are correlated to the box counting fractal dimension, and satisfy the known relations obtained from the scaling laws. The results have also shown the existence of two scaling regions, characterized by the persistence of the pulse and by a random behaviour, respectively. The fractal dimensions have also been shown to be independent of time acquisition of the emitted pulse, and this indication of self-similarity confirms its fractal characteristics. Finally, it is conjectured a correlation between the Hurst coefficient/fractal dimension and the mechanical flaws observed. / Neste trabalho analisou-se a integridade mecânica do material compósito constituído por uma matriz polimérica, resina epoxi DER 331, e por fibra de vidro tipo ‘E’ como agente de reforço. Esta análise foi realizada utilizando-se o ensaio de emissão acústica, com o objetivo de correlacionar as formas de onda dos sinais com os mecanismos de falhas associados aos esforços de tração e flexão aplicados a espécimes fabricados com tal material. Na análise dos sinais como função do tempo foram utilizados os métodos de contagem de caixas, que fornece a dimensão fractal, e o do intervalo re-escalado de Hurst, sendo também utilizado o método espectral de Fourier para a análise no domínio da freqüência. Mostrou-se que os expoentes calculados pelos métodos espectral de Fourier e re-escalado de Hurst estão correlacionados com a dimensão fractal obtida pelo método de contagem de caixa, e satisfazem as relações previstas pelas leis de escala. Os resultados mostraram também a existência de duas regiões de escala distintas, sendo uma caracterizada pela persistência do sinal e outra por um comportamento aleatório característica do ruído presente. As dimensões fractais obtidas apresentaram-se independentes da taxa de aquisição da forma da onda emitida indicando a propriedade de auto-similaridade dos sinais estudados, o que confirma a sua característica fractal. Finalmente, é conjecturado uma correlação entre o coeficiente de Hurst/dimensão fractal e as falhas mecânicas observadas.
|
10 |
Estudo do envelhecimento físico de sistemas epoxidílicos estequiométricos DGEBA/DDM através de análise térmicaGiugno, Izabel Cristina Riegel January 1997 (has links)
o comportamento, frente ao envelhecimento físico, do sistema diglicidil éter do bisfenol-A (DGEBA) curado com diaminodifenilmetano (DOM) foi estudado em função da estrutura química, induzida pela cura, e do tempo de envelhecimento. Sistemas estequiométricos foram submetidos a Calorimetria Diferencial de Varredura (DSC) e Análise Térmica Dinâmico-Mecânica (DMTA). A cura isotérmica da resina epóxi foi realizada em uma etapa a 115°C e 135°C, por 20, 30, 45, 60 e 90 mino As amostras foram envelhecidas a 100°C por períodos de 4 até 72h. A extensão do envelhecimento físico foi associado com a área do pico endotérmico que aparece na região da transição vítrea, de acordo com os termogramas de DSC. Foi observado que a entalpia de relaxação aumenta gradualmente com o tempo de envelhecimento. Por DMT A, observou-se variações na magnitude do fator de perda (tan õ), no pico máximo, em função do grau de cura e do tempo de envelhecimento. O módulo dinâmico de armazenamento a 100°C (E'1CX)) deslocou-se para valores maiores assim como a Tg, medida através do pico a da curva log E", com o aumento do tempo de envelhecimento. A velocidade de envelhecimento e as energias de ativação da transição α foram obtidas a partir de parâmetros dinâmico-mecânicos e após associados com as diferentes histórias de cura e envelhecimento do material. De modo geral, a velocidade de envelhecimento (Ra) decresce com o aumento do grau de reticulação para sistemas curados a 115°C e passa por um mínimo para as amostras curadas a 135°C. As energias de ativação mostram uma tendência crescente com o tempo de envelhecimento. Concluiu-se que a técnica de DMTA é muito sensível às mudanças estruturais devido à cura e ao envelhecimento físico realizados nos sistemas investigados. Os resultados dinâmico-mecânicos obtidos para as misturas curadas segundo diferentes histórias térmicas salientam a importância da seleção adequada das condições de cura para que se possam obter as melhores propriedades destes materiais. / Physical aging behavior of diglycidyl ether of bisphenol-A (DGEBA) cured with diaminodiphenylmethane (DDM) have been investigated as a function of chemical structure, induced by cure, and aging time. Stoichiometric systems have been submitted to Differencial Scanning Calorimetry (DSC) and Dynamic Mechanical Thermal Analysis (DMTA) measurements. The isothermal curing of the epoxy resin was carried out in one step at 115°C and at 135°C for 20, 30, 45, 60 and 90 mino Samples were aged at 100°C for periods of time from 4 to a maximum of 72 h. The extent of physical aging has been measured by the area of the endothermic peak which appears within the glass transition region according to DSC thermograms. The enthalpy relaxation was found to increase gradually with aging time. Variations on magnitude of the loss factor (tan õ), on the maximum peak, have been observed as a function of degree of cure and aging time. The dynamic storage modulus at 100°C ( E' 100) changed with increasing physical aging to higher values as well as the glass transition temperature (Tg) as measured by the a peak on log E" curves. Aging rates and α transition activation energies were obtained through DMT A parameters analysis and then associated with different curing and aging histories of the material. Generally, the aging rate (Ra) decreases with increasing crosslinking degree for the systems cured at 115°C and passes through a minimum for those cured at 135°C. The activation energies demonstrate a tendecy to increase with aging time. It was concluded that the DMTA technique is very sensitive to structural changes in the investigated epoxy systems due to curing and physical aging . The DMTA results obtained from mixtures cured with different thermal histories underline the importance of adequate selection of curing conditions in order to obtain the optimum properties for these materiais.
|