Made available in DSpace on 2014-06-11T19:32:20Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-03-31Bitstream added on 2014-06-13T21:04:02Z : No. of bitstreams: 1 soares_cj_dr_rcla.pdf: 2262021 bytes, checksum: 2a44d315aaf7a6f452976c1109079dfb (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / External Detector Method is a widely used technique in Fission Track Thermochronology, FTT, in which two different minerals are concomitantly employed: spontaneous tracks are observed in apatite and the induced ones in the external detector muscovite. They show intrinsic differences in detection and etching properties that should be taken into account. In this work, new geometry factor values, g, in apatite were obtained by ρED/ρIS ratio and GQR values through the measurement of projected lengths. Five mounts, two of which were large area prismatic sections (Mn-1 and Mn-2, Durango apatite) and three samples composed of random orientation pieces (D-2 and D-3, Durango apatite and TF-42, from crystalline rock) have been used to determine the g-values. A side effect of applying EDM is that the value of the initial confined induced fission track, L0, is not measured in routine analyses. The L0-value is an important parameter to quantify with good confidence the degree of annealing of the fossil fission tracks in the unknown age sample, being essential for accurate thermal history modeling. The impact of using arbitrary L0- values on the inference sample thermal history was investigated and discussed. The L0- value can be measured for each sample as an extension of the ρED/ρIS ratio method for measuring g, which consists in simultaneously irradiating pre-annealed apatite grains and the EDM mount of the same sample. The ratio between densities of induced tracks in the muscovite and in the extra apatite mount gives the value of g. L0 is the mean length of the confined fission tracks measured in the extra apatite mount. Eight apatite samples from crystalline basement, with grains at random orientation, were used to determine the gvalues. The resultant average found (0.560.02) is statistically in agreement with the values found for... (Complete abstract click electronic access below)

Made available in DSpace on 2015-05-14T16:53:15Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-12-16Bitstream added on 2015-05-14T16:59:07Z : No. of bitstreams: 1 000825266_20200120.pdf: 98338 bytes, checksum: f0dba0164d777f3f784873a6a5b2aadb (MD5) / O objetivo deste trabalho foi a produção e caracterização microestrutural, mecânica e fractografica de rochas sintéticas, obtidas por fabricação, a partir da mistura de resíduos dos pós de granito e vidro comercial. Esta pesquisa foi dividida em duas etapas. Na primeira etapa, a meta foi determinar a composição a ser utilizada na mistura e a temperatura de sinterização que produzisse uma rocha sintética com maior resistência mecânica e menor consumo de energia. Nesta fase foram definidas duas composições para produção das amostras: a primeira com massa de 1/3 de pó de granito, 1/3 de pó de vidro âmbar e 1/3 de pó de vidro transparente e uma segunda composição, com 60% de pó de granito, 30% de pó de vidro âmbar e 10% de pó de vidro transparente. Tais amostras foram sinterizadas em temperaturas que variaram de 800ºC a 1100ºC, e com base nos resultados obtidos pelo ensaio de flexão de três pontos, foi determinada para primeira composição, uma temperatura de sinterização de 850ºC e para a segunda 1050ºC. Na segunda etapa da pesquisa, aprofundou-se os estudos com relação às rochas sintéticas obtidas, realizando-se medidas de rugosidade, resistência a flexão, tenacidade a fratura pelo método SEVNB (Single-edge V-notch Beam), microdureza, molhabilidade e porosidade aparente. Além de difração de raios X, microscopia eletrônica de varredura e análise termogravimétrica e calorimetria diferencial de varredura. Os resultados obtidos nesta segunda etapa foram comparados com o granito comercial andorinha e mostraram que as rochas sintéticas obtidas são altamente promissoras e viáveis. As rochas sintéticas produzidas a partir das duas composições, apresentam menores valores de molhabilidade e porosidade e maiores valores de tensão de ruptura à flexão e microdureza, quando comparados as amostras do gra... (Resumo completo, clicar acesso eletrônico abaixo) / This paper was intended to produce and characterize synthetic rocks in a microstructural, mechanical and fractographic way. Such rocks were obtained from the mixture of commercial glass waste and granite powder. This research was divided in two steps: in the first one it was to determined the amount of materials used in the mixture and the sintering temperature in order to produce synthetic rocks with higher mechanical strength and lower energy consumption, while in the second the synthetic rocks were submited to some tests, such as roughness measurement, flexural strength, fracture toughness by the SEVNB method, hardness, wettability and apparent porosity. In this first step two compositions were defined in order to produce the samples. The first composition contained 1/3 of granite powder, 1/3 of ambar glass waste and 1/3 of transparent glass waste; the second one contained 60% of granite powder, 30% of ambar glass waste and 10% of transparent glass waste. It was also determined the sintering temperature: 850ºC for the first composition and 1050ºC for the second one. Other tests, such as: X-ray diffraction, scanning electron microscopy, thermogravimetric analysis and differential scanning calorimetry were also performed. The results of the experiments in the second step were compared to andorinha, an ordinary kind of Brazilian gray granite and showed that synthetic rocks are very promising and viable. Synthetic rocks presented lower wettability and porosity values and higher flexural strength and hardness values, when compared to the samples of andorinha. It could be concluded that the first composition was the most relevant from the commercial point of view (1/3 of granite powder, 1/3 of ambar glass waste and 1/3 of transparent glass waste) for it presents higher flexural strength value and lower sintiring temperature value. This represents a considerable economic gain

Resumo: O derrame Salto Segredo localiza-se a sudoeste do Estado do Paraná, entre os municípios de Reserva do Iguaçu e Magueirinha, na localidade conhecida como Salto Segredo. O derrame possui aproximadamente 40 m de espessura e é composto majoritariamente por labradorita, augita, minerais opacos e mesóstase. Pode ser dividido em três níveis internos de acordo com suas características estruturais, texturais e padrão de fraturas. (1) Nível vesicular de base, caracterizado pela textura ofítica e padrão irregular de fraturas; (2) Nível maciço central, o mais espesso do derrame, pode ser subdividido em duas porções de acordo com o padrão de fraturas: porção mediana-inferior, com fraturas irregulares e descontínuas subverticais; e porção mediana-superior, que apresenta fraturas regulares e contínuas subverticais, com traçados retilíneos ou sigmoidais; (3) Nível vesicular de topo, que contém diferentes populações de vesículas, amígdalas e geodos. Em direção ao topo do nível o tamanho das cavidades diminui, aumentando, porém, a abundância destas. Quartzo predomina nos geodos. As amígdalas são preenchidas mais comumente por quartzo, calcita, calcedônia, celadonita e subordinadamente heulandita, apofilita e estilbita. A presença de cilindros de vesículas (vesicle cylinders), zonas vesiculares horizontais, lençóis de vesículas (vesicle sheets) e amígdalas e geodos achatados sugerem a atuação de processos de inflação durante a formação do derrame Salto Segredo. Brechas e peperitos associam-se ao derrame. São identificados quatro tipos de brecha: brechas basáltica-calcítica e basáltica-quartzosa (intraderrame), e brechas basáltica-siltosa e basáltica-arenosa (interderrame). A gênese das brechas intraderrame está ligada a pressão de fluidos e processos tectônicos, enquanto que a formação das brechas interderrame é resultante da interação entre processos ígneos e sedimentares. A presença de basaltos associados a brechas com matriz sedimentar e peperitos indica contemporaneidade entre magmatismo e sedimentação.