<p>Solid state Friction stir welding (FSW) is of major interest in the welding of aluminium since it improves the joint properties. Many applications where Al-alloys are used are subject to varying load conditions, making fatigue failure a critical issue. In the scope of this thesis, the fatigue performance of friction stir welded AlMgSi-alloy 6082 has been investigated. Static and dynamic properties of different joint configurations and welds produced with varying process parameters have been determined. Microstructures of fractured surfaces have been studied to evaluate the effect of weld discontinuities on fatigue. The mechanical strength of the friction stir welds was set in relation to that of conventional fusion welds, and that of other FS welded Al-alloys.</p><p>The friction stir process produced aluminium butt welds with high and consistent fatigue strengths, which exceeded the strengths of similar fusion welded samples. A smooth weld geometry showed to be of great importance for the fatigue performance, favouring the friction stir welds. Welding speed in a tested range of 0.35-1.4 m/min had only a modest influence on the properties of the friction stir welds; properties were not deteriorating at the highest speed. The softening of the alloy around the weldline was modelled. A fair description of the hardness profiles across the weld was obtained. At a low and high welding speed a full and partial softening respectively was predicted, indicating that full softening is not required to obtain a flawless weld.</p><p>In case of friction stir overlap welds, tool design is even more important than in butt welding to secure weld quality. A broad tool shoulder with a concave pin end gave the best performance. In particular, the minimal influence on the sheet interface when welding with such a tool was beneficial for the fatigue strength. The stress distribution in overlap and T-type test specimens has been modelled. The stress intensity factors were determined. The corresponding crack propagation rates were in fair accordance with the experimental results. It was found that a simplified approach, developed to estimate ∆K for overlap spot welds, could be used also for friction stir overlap joints.</p>

The problem was to determine the effectiveness of using polyethylene glycol 1000 in the treatment of green wood for the purpose of forming projects made of wood veneer and of simple design for use in junior high or high school woodworking classes. The purpose of this study was to seek answers to the following questions. 1. Is polyethylene glycol 1000 an effective stabilizing agent for green wood veneer that can be used in school woodworking classes? 2. Can green wood veneer treated with polyethylene glycol 1000 be bent to form simple woodwork projects? 3. Can green wood veneer treated with polyethylene glycol 1000 be successfully used in junior high and high school woodworking classes? 4. What length of treatment time is best for green wood veneer that is to be used to form simple bent wood projects? 5. Is one-fourth inch thickness suitable for green wood veneer that is to be treated with polyethylene glycol 1000 and used to form simple bent wood projects?

A study conducted by the World Health Organization and United Nations Children's Fund, concluded that approximately 768 million people worldwide are not receiving sanitary drinking water suitable for consumption. While there are many water treatment methods, lime softening proves to be one of the more effective approaches as it removes a wide variety of harmful compounds including arsenic, lead, mercury, and cadmium under the correct conditions. The greatest issues with lime softening on a smaller scale include the complexity of the chemistry and need for monitoring. By designing the system for groundwater sources and with a smaller capacity, this thesis hoped to reduce the level of monitoring, chemical expertise, and cost needed for operation. While promising results occurred in the removal of arsenic and total hardness, this project was unable to obtain consistent results and final water samples with pH values between the recommended standard of 6.5 to 8. / Includes bibliography. / Thesis (M.S.)--Florida Atlantic University, 2015. / FAU Electronic Theses and Dissertations Collection

This study investigated the vibration serviceability of timber structures with dowel-type connections. It addressed the use of such connections in cutting-edge timber structures such as multi-storey buildings and long-span bridges, in which the light weight and flexibility of the structure make it possible that vibration induced by dynamic forces such as wind or footfall may cause discomfort to occupants or users of the structure, or otherwise impair its intended use. The nature of the oscillating force imposed on connections by this form of vibration was defined based on literature review and the use of established mathematical models. This allowed the appropriate cyclic load to be applied in experimental work on the most basic component of a dowel-type connection: a steel dowel embedding into a block of timber. A model for the stiffness of the timber in embedment under this cyclic load was developed based on an elastic stress function, which could then be used as the basis of a model for a complete connector. Nonlinear and time-dependent behaviour was also observed in embedment, and a simple rheological model incorporating elastic, viscoelastic and plastic elements was fitted to the measured response to cyclic load. Observations of the embedment response of the timber were then used to explain features of the behaviour of complete single- and multiple-dowel connections under cyclic load representative of in-service vibration. Complete portal frames and cantilever beams were tested under cyclic load, and a design method was derived for predicting the stiffness of such structures, using analytical equations based on the model for embedment behaviour. In each cyclic load test the energy dissipation in the specimen, which contributes to the damping in a complete structure, was measured. The analytical model was used to predict frictional energy dissipation in embedment, which was shown to make a significant contribution to damping in single-dowel connections. Based on the experimental results and analysis, several defining aspects of the dynamic response of the complete structures, such as a reduction of natural frequency with increased amplitude of applied load, were related to the observed and modelled embedment behaviour of the connections.

Ce manuscrit présente des récentes extensions au modèle PFVD, basé sur l'hétérogénéité de la dynamique des polymères vitreux à l'échelle de quelques nanomètres et résolu par simulation en 3D, afin de fournir une description physique unifiée des propriétés mécaniques et dynamiques des polymères vitreux soumis à déformation plastique. Trois sujets principaux sont traités : La plastification. Sous déformation, les polymères atteignent le seuil de plasticité (yield) à quelques pourcents de déformation et quelques dizaines de MPa. Nous proposons que l'énergie élastique absorbée à l'échelle des hétérogénéités dynamiques accélère la dynamique locale. On observe contraintes ultimes de quelques dizaines de MPa à quelques pourcents de déformation et que la plastification est due à un nombre relativement petit d'événements locaux. Il a été observé que la dynamique devient plus rapide et homogène dans le régime plastique et que la mobilité moyenne atteint une valeur stationnaire, linéaire avec le taux de déformation. Nous proposons que la contrainte locale stimule la diffusion de monomères des domaines lents à ceux rapides (mécanisme de facilitation) et accélère dynamique locale. Ceci permets d'observer l'homogénéisation de la dynamique, avec des caractéristiques proches de l'expérience. L'écrouissage, dans les polymères enchevêtrés ou réticulés. A grande déformation, la contrainte augmente avec une pente caractéristique d'ordre 10 – 100 MPa au-dessous de la transition vitreuse. De manière analogue à une théorie récente, nous proposons que la déformation locale oriente les monomères dans la direction d'étirage et ralentie la dynamique, suite à l'intensification des interactions locales. Les modules d'écrouissage mesurés, les effets de la réticulation et du taux de déformation sont comparables aux données expérimentales. En outre, on trouve que l'écrouissage a un effet stabilisateur sur les phénomènes de localisation et sur les bandes de cisaillement / This manuscript presents recent extensions to the PFVD model, based on the heterogeneity of theh dynamics of glassy polymers at the scale of a few nanometers et solved by 3D numerical simulation, which aim at providing a unified physical description of the mechanical and dynamical properties of glassy polymers during plastic deformation. Three main topics are treated: Plasticization. Under applied deformation, polymers undergo yield at strains of a few percent and stresses of some 10 MPa.We propose that the elastic energy stored at the scale of dynamical heterogeneities accelerates local dynamics. We observe yield stresses of a few 10 MPa are obtained at a few percent of deformation and that plastification is due to a relatively small amount of local yields. It has been observed that dynamics becomes faster and more homogeneous close to yield and that the average mobility attains a stationary value, linear with the strain rate. We propose that stress-induced acceleration of the dynamics enhances the diffusion of monomers from slow domains to fast ones (facilitation mechanism), accelerating local dynamics. This allows for obtaining the homogeneisation of the dynamics, with the same features observed during experiments. Strain-hardening, in highly entangled and cross-linked polymers. At large strain, stress increases with increasing strain, with a characteristic slope (hardening modulus) of order 10 – 100 MPa well below the glass transition. Analogously to a recent theory, we propose that local deformation orients monomers in the drawing direction and slows dows the dynamics, as a consequence of the intensification of local interactions. The hardening moduli mesured, the effect of reticulation and of strain rate are comparable with experimental data. In addition, strain-hardening is found to have a stabilizing effect over strain localization and shear banding

The reduction behaviour of the olivine iron ore pellet MPBOwas studied in laboratory scale at KTH as well as in the LKABexperimental blast furnace. Initially, a newreduction-under-load, or so-called reduction/softening/melting,test equipment was developed. Experiments using differentreducing conditions, corresponding to different radialpositions of the blast furnace, were conducted. The experimentsincluded different temperature profiles, reducing atmospheresand mechanical loads applied on the sample bed to simulate thevarying conditions in the blast furnace process. The progressof reduction was investigated, as well as the processes ofsintering and contraction during reduction. A model of thecarburisation (pick-up of carbon by the reduced iron) andmelt-down process during rapid contraction was presented. Laboratory testing of MPBO pellets was compared with resultsfrom the LKAB experimental blast furnace. The reduction of ironore pellets in the experimental blast furnace was surveyed by adissection of the furnace after quenching. The high temperaturephenomena occurring when reducing the MPBO pellet, with limitedsoftening and a short temperature range of the melting process,resulting in a thin cohesive zone, were found to be the same inlaboratorytests and in the experimental blast furnace. Thereduction down through the burden of the experimental blastfurnace was similar, but not identical to the results of theRUL experiments. The differences were found to be due todifferent reducing conditions. Therefore, it was concluded thata simulation of the reduction occurring in the blast furnacecan be performed in laboratory scale, provided the experimentalconditions are correctly chosen. Finally, a modification to further improve the properties ofthe MPBO pellets was examined. With the aim to improve theblast furnace process, coating of blast furnace pellets wasinvestigated in laboratory scale, as well as in the LKABexperimental blast furnace. Olivine, dolomite and quartzitewere used as coating agents. In laboratory scale the stickingprevention action of the different coating materials wasverified, in established test methods as well as in new testmethods, modified for blast furnace conditions. Testing of thecoated pellets in the experimental blast furnace revealedseveral advantages; significantly reduced blast furnace fluedust generation, improved gas utilisation and a smoother blastfurnace operation with a potential for a lowered fuel rate. <b>Keywords:</b>Olivine, pellets, pellet testing,reduction/softening/melting, MPBO, blast furnace, reduction,quenching, dissection, coating, sticking, coated pellets.

Solid state Friction stir welding (FSW) is of major interest in the welding of aluminium since it improves the joint properties. Many applications where Al-alloys are used are subject to varying load conditions, making fatigue failure a critical issue. In the scope of this thesis, the fatigue performance of friction stir welded AlMgSi-alloy 6082 has been investigated. Static and dynamic properties of different joint configurations and welds produced with varying process parameters have been determined. Microstructures of fractured surfaces have been studied to evaluate the effect of weld discontinuities on fatigue. The mechanical strength of the friction stir welds was set in relation to that of conventional fusion welds, and that of other FS welded Al-alloys. The friction stir process produced aluminium butt welds with high and consistent fatigue strengths, which exceeded the strengths of similar fusion welded samples. A smooth weld geometry showed to be of great importance for the fatigue performance, favouring the friction stir welds. Welding speed in a tested range of 0.35-1.4 m/min had only a modest influence on the properties of the friction stir welds; properties were not deteriorating at the highest speed. The softening of the alloy around the weldline was modelled. A fair description of the hardness profiles across the weld was obtained. At a low and high welding speed a full and partial softening respectively was predicted, indicating that full softening is not required to obtain a flawless weld. In case of friction stir overlap welds, tool design is even more important than in butt welding to secure weld quality. A broad tool shoulder with a concave pin end gave the best performance. In particular, the minimal influence on the sheet interface when welding with such a tool was beneficial for the fatigue strength. The stress distribution in overlap and T-type test specimens has been modelled. The stress intensity factors were determined. The corresponding crack propagation rates were in fair accordance with the experimental results. It was found that a simplified approach, developed to estimate ∆K for overlap spot welds, could be used also for friction stir overlap joints. / QC 20101008

<p>The reduction behaviour of the olivine iron ore pellet MPBOwas studied in laboratory scale at KTH as well as in the LKABexperimental blast furnace. Initially, a newreduction-under-load, or so-called reduction/softening/melting,test equipment was developed. Experiments using differentreducing conditions, corresponding to different radialpositions of the blast furnace, were conducted. The experimentsincluded different temperature profiles, reducing atmospheresand mechanical loads applied on the sample bed to simulate thevarying conditions in the blast furnace process. The progressof reduction was investigated, as well as the processes ofsintering and contraction during reduction. A model of thecarburisation (pick-up of carbon by the reduced iron) andmelt-down process during rapid contraction was presented.</p><p>Laboratory testing of MPBO pellets was compared with resultsfrom the LKAB experimental blast furnace. The reduction of ironore pellets in the experimental blast furnace was surveyed by adissection of the furnace after quenching. The high temperaturephenomena occurring when reducing the MPBO pellet, with limitedsoftening and a short temperature range of the melting process,resulting in a thin cohesive zone, were found to be the same inlaboratorytests and in the experimental blast furnace. Thereduction down through the burden of the experimental blastfurnace was similar, but not identical to the results of theRUL experiments. The differences were found to be due todifferent reducing conditions. Therefore, it was concluded thata simulation of the reduction occurring in the blast furnacecan be performed in laboratory scale, provided the experimentalconditions are correctly chosen.</p><p>Finally, a modification to further improve the properties ofthe MPBO pellets was examined. With the aim to improve theblast furnace process, coating of blast furnace pellets wasinvestigated in laboratory scale, as well as in the LKABexperimental blast furnace. Olivine, dolomite and quartzitewere used as coating agents. In laboratory scale the stickingprevention action of the different coating materials wasverified, in established test methods as well as in new testmethods, modified for blast furnace conditions. Testing of thecoated pellets in the experimental blast furnace revealedseveral advantages; significantly reduced blast furnace fluedust generation, improved gas utilisation and a smoother blastfurnace operation with a potential for a lowered fuel rate.</p><p><b>Keywords:</b>Olivine, pellets, pellet testing,reduction/softening/melting, MPBO, blast furnace, reduction,quenching, dissection, coating, sticking, coated pellets.</p>

The influence of disorder is an important area in materials research. A supersaturated solid solution is in a metastable state, in which the host lattice is forced to solve guest atoms over the thermodynamical stability limit. The guest atoms are point defects, which amount can be varied by changing the concentration. The increasing amount of point defects makes the lattice unstable against schare, which may ends up in an order-disorder transition. In this work especially the lattice dynamics was studied at the atomic level by means of inelastic neutron scattering. In case of both studied systems (ZrAl, CuFe) a softening of especially the tranverse phonons could be shown, which supports the existing theory. / Der Einfluß von Unordnung ist ein wichtiges Forschungsgebiet der Materialwissenschaft. Bei übersättigten festen Lösungen handelt es sich um einen metastabilen Zustand, bei dem das Wirtsgitter gezwungen ist, mehr Fremdatome aufzunehmen, als thermodynamisch stabil ist. Die Fremdatome im Wirtsgitter sind Punktdefekte, deren Menge mit der Konzentration variiert werden kann. Die Zunahme substitutionaler Defekte bewirkt eine Gitterinstabilität gegenüber Scherkräften und anschliessend möglicherweise einen Ordnungs - Unordnungs - Übergang. In dieser Arbeit wurden vor allem dynamische Aspekte betrachtet: die Gitterdynamik wurde auf atomarer Ebene mittels inelastischer Neutronenstreuung untersucht. Bei beiden untersuchten Systemen (ZrAl, CuFe) konnte ein Weichwerden (softening) von Phononen beobachtet werden, insbesondere von transversalen Moden, die einen direkten Nachweis der oben erwähnten Gitterinstabilität ergeben.

CoordenaÃÃo de AperfeiÃoamento de Pessoal de NÃvel Superior / The present work deals about the synthesis and characterization of magnetic zeolites obtained by hydrothermal route using kaolin from Brazilian Northeast as silicon and aluminum source. By means of the X-ray diffraction technique it was possible to identify zeolite LTA and zeolite P1 as major crystalline phases for each synthesis, with low intensity peaks referent to unreacted quartz present in the kaolin used, which is in accordance to the. FTIR spectra; the nanoparticles were identified as magnetite, with low intensity peaks referent to goethite. In scanning electron microscopy, however, it was not possible to morphologically identify these minor components, while the zeolites showed well defined morphologies, presenting unchanged morphology when in the composites form, but with nanoparticles dispersed over their surface, as expected. From transmission electron microscopy it was observed that the nanoparticles were of ca. 50 nm. Magnetic measurements indicated magnetite presence with superior diameter to critical diameter to superparamagnetic particles and remanent magnetization. Thermogravimetric analyses showed for the composites, lower mass loss than compared to the pure zeolites what may be associated to the improvement of its thermal stability. Granulometric distribution indicated nanoparticles agglomeration in variable sizes, while zeolites formed agglomerates of ca. 10 Âm. Water softening was accomplished by using both zeolites, with high efficiency on Ca2+ removal and similar behavior between the zeolite and its respective composite, being the best result observed for zeolite A, with efficiency of 97,95%, reaching equilibrium in the first contact minutes. The dependence on mass studies also showed that zeolite A and its composite presented the best efficiency, whereas zeolite P achieved the same removal levels using corresponding zeolite masses (45 mg). This way, the proposed method for zeolites synthesis proved to be efficient, so that the use of a magnet is capable to attract them, leading their excellent separation from the aqueous medium with its ionic exchange capacity unaffected. / O presente trabalho trata da sÃntese e caracterizaÃÃo de zeÃlitas magnÃticas obtidas por impregnaÃÃo de nanopartÃculas de magnetita a zeÃlitas A e P, sintetizadas por mÃtodo hidrotÃrmico utilizando caulim branco do Nordeste brasileiro como fonte de silÃcio e alumÃnio. Por meio da tÃcnica de difraÃÃo de raios-X foi possÃvel identificar como fases cristalinas majoritÃrias a zeÃlita LTA e P1 para cada sÃntese, com picos de baixa intensidade referentes a quartzo, resistente ao processo tÃrmico de tratamento prÃvio do caulim, bem como nos espectros de infravermelho; as nanopartÃculas foram identificadas como magnetita, havendo ainda indÃcios da presenÃa de goethita em pequena quantidade. Nas anÃlises de microscopia eletrÃnica de varredura, entretanto, nÃo foi possÃvel identificar esses componentes minoritÃrios morfologicamente; enquanto que a morfologia das zeÃlitas mostrou-se bem definida, sem alteraÃÃes apÃs a formaÃÃo dos compÃsitos, apenas com nanopartÃculas espalhadas em sua superfÃcie, como desejado. A partir da microscopia eletrÃnica de transmissÃo, pÃde-se observar melhor a variaÃÃo de tamanho das nanopartÃculas, em mÃdia de 50 nm. Medidas magnÃticas das amostras com essa propriedade indicaram a presenÃa de magnetita com diÃmetro superior ao diÃmetro crÃtico para partÃculas superparamagnÃticas e magnetizaÃÃo remanente. As anÃlises termogravimÃtricas mostraram que a adiÃÃo das nanopartÃculas Ãs zeÃlitas diminuiu sua perda de massa diante do aumento de temperatura e as anÃlises de distribuiÃÃo granulomÃtrica indicaram a aglomeraÃÃo das nanopartÃculas em tamanhos variÃveis, enquanto que as zeÃlitas formaram aglomerados de aproximadamente 10 Âm. Os ensaios de abrandamento de Ãguas mostraram alta eficiÃncia das zeÃlitas em remover Ca2+, com comportamento similar entre a zeÃlita e o seu respectivo compÃsito, encontrando para a zeÃlita A o maior percentual de remoÃÃo, de 97,95 %, atingindo equilÃbrio nos primeiros minutos de aplicaÃÃo. Os estudos de massa tambÃm mostraram a eficiÃncia da zeÃlita A e de seu compÃsito, tendo a zeÃlita P se aproximado dos mesmos nÃveis de remoÃÃo em massas referentes a 45 mg de zeÃlita. Assim, o mÃtodo proposto para sÃntese das zeÃlitas magnÃticas mostrou-se eficiente, de modo que a utilizaÃÃo de um Ãmà à capaz de atraÃ-las facilitando a separaÃÃo do meio apÃs a aplicaÃÃo em meio aquoso e sua capacidade de troca iÃnica nÃo foi afetada.