In this thesis the superconducting and magnetic phases of LiOH(Fe,Co)(Se,S), CuFeAs/CuFeSb, and LaFeP_1-xAs_xO - belonging to the 11, 111 and 1111 structural classes of iron-based arsenides and chalcogenides - are investigated by means of 57Fe Mössbauer spectroscopy and muon spin rotation/relaxation (μSR). Of major importance in this study is the application of high magnetic fields in Mössbauer spectroscopy to distinguish and characterize ferro- (FM) and antiferromagnetic (AFM) order. A user-friendly Mössbauer data analysis program was developed to provide suitable model functions not only for high field spectra, but relaxation spectra or parameter distributions in general.
In LaFeP_1-xAs_xO the reconstruction of the Fermi surface is described by the vanishing of the Γ hole pocket with decreasing x. The continuous change of the orbital character and the covalency of the d-electrons is shown by Mössbauer spectroscopy. A novel antiferromagnetic phase with small magnetic moments of ~ 0.1 μ_B state is characterized. The superconducting order parameter is proven to continuously change from a nodal to a fully gapped s-wave like Fermi surface in the superconducting regime as a function of x, partially investigated on (O,F) substituted samples.
LiOHFeSe is one of the novel intercalated FeSe compounds, showing strongly increased T_C = 43 K mainly due to increased interlayer spacing and resulting two-dimensionality of the Fermi surface. The primary interest of the samples of this thesis is the simultaneously observed ferromagnetism and superconductivity. The local probe techniques prove that superconducting sample volume gets replaced by ferromagnetic volume. Ferromagnetism arises from magnetic order with T_C = 10 K of secondary iron in the interlayer. The tendency of this system to show (Li,Fe) disorder is preserved upon (Se,S) substitution. However, superconductivity gets suppressed. The results of Mössbauer spectroscopy indicate that the systems tends to a secondary structural phase, where the local iron environment observed in pure FeS is absent. Moreover, two interlayer positions of the iron are identified. The absence of enhanced superconducting T_C in LiOHFeS thus is related to a structural instability.
Also, in CuFeAs the role of secondary iron at the Cu position turns out to be decisive for the observed magnetic behaviour. As in LiOHFeSe, it orders ferromagnetically at T_C ~ 11 K and superimposes with the magnetic instability of the main iron site. It is shown that a small charge doping of 0.1e/Fe, which is expected from (Cu,Fe) disorder, is sufficient to switch the system between a paramagnetic and an AFM ground state. Both magnetic orders are indistinguishable, because the magnetic order parameters are strongly coupled. This coupling was observed in the structurally identical CuFeSb, where the magnetic order parameters of both iron sites scale perfectly. The magnetically unstable CuFeAs and the ferromagnetic CuFeSb can be classified according to the theory of As height driven magnetism, predicting a change from paramagnetism to AFM and finally FM with increasing As height.
Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa.de:bsz:14-qucosa-222083 |
Date | 29 March 2017 |
Creators | Kamusella, Sirko |
Contributors | Technische Universität Dresden, Fakultät Mathematik und Naturwissenschaften, Prof. Dr. Hans-Henning Klauß, Prof. Dr. Hans-Henning Klauß, Dr. Vadim Ksenofontov |
Publisher | Saechsische Landesbibliothek- Staats- und Universitaetsbibliothek Dresden |
Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
Language | English |
Detected Language | English |
Type | doc-type:doctoralThesis |
Format | application/pdf |
Page generated in 0.0016 seconds