The use of living radical polymerization methods has shown significant potential to control grafting of polymers from inert polymeric substrates. The objective of this thesis is to create advanced substrates for use in combinatorial chemistry applications through the use of g-radiation as a radical source, and the use of RAFT, ATRP and RATRP living radical techniques to control grafting polymerization. The substrates grafted were polypropylene SynPhase lanterns from Mimotopes and are intended to be used as supports for combinatorial chemistry. ATRP was used to graft polymers to SynPhase lanterns using a technique where the lantern was functionalized by exposing the lanterns to gamma-radiation from a 60Co radiation source in the presence of carbon tetra-bromide, producing short chain polystyrene tethered bromine atoms, and also with CBr4 directly functionalizing the surface. Styrene was then grafted off these lanterns using ATRP. MMA was graft to the surface of SynPhase lanterns, using g-radiation initiated RATRP at room temperature. It was found that the addition of the thermal initiator, AIBN, successfully increased the concentration of radicals to a level where we could achieve proper control of the polymerization. RAFT was used to successfully control the grafting of styrene, acrylic acid and N,N???-dimethylacrylamide to polypropylene SynPhase Lanterns via a -initiated RAFT agent mediated free radical polymerization process using cumyl phenyldithioacetate and cumyl dithiobenzoate RAFT agents. Amphiphilic brush copolymers were produced with a novel combined RAFT and ATRP system. Polystyrene-co-poly(vinylbenzyl chloride) created using gamma-radiation and controlled with the RAFT agent PEPDA was used as a backbone. The VBC moieties were then used as initiator sites for the ATRP grafting of t-BA to give a P(t-BA) brush that was then hydrolyzed to produce a PAA brush polymer. FMOC loading tests were conducted on all these lanterns to assess their effectiveness as combinatorial chemistry supports. It was found that the loading could be controlled by adjusting the graft ratio of the lanterns and had a comparable loading to those commercially produced by Mimotopes.

The use of living radical polymerization methods has shown significant potential to control grafting of polymers from inert polymeric substrates. The objective of this thesis is to create advanced substrates for use in combinatorial chemistry applications through the use of g-radiation as a radical source, and the use of RAFT, ATRP and RATRP living radical techniques to control grafting polymerization. The substrates grafted were polypropylene SynPhase lanterns from Mimotopes and are intended to be used as supports for combinatorial chemistry. ATRP was used to graft polymers to SynPhase lanterns using a technique where the lantern was functionalized by exposing the lanterns to gamma-radiation from a 60Co radiation source in the presence of carbon tetra-bromide, producing short chain polystyrene tethered bromine atoms, and also with CBr4 directly functionalizing the surface. Styrene was then grafted off these lanterns using ATRP. MMA was graft to the surface of SynPhase lanterns, using g-radiation initiated RATRP at room temperature. It was found that the addition of the thermal initiator, AIBN, successfully increased the concentration of radicals to a level where we could achieve proper control of the polymerization. RAFT was used to successfully control the grafting of styrene, acrylic acid and N,N???-dimethylacrylamide to polypropylene SynPhase Lanterns via a -initiated RAFT agent mediated free radical polymerization process using cumyl phenyldithioacetate and cumyl dithiobenzoate RAFT agents. Amphiphilic brush copolymers were produced with a novel combined RAFT and ATRP system. Polystyrene-co-poly(vinylbenzyl chloride) created using gamma-radiation and controlled with the RAFT agent PEPDA was used as a backbone. The VBC moieties were then used as initiator sites for the ATRP grafting of t-BA to give a P(t-BA) brush that was then hydrolyzed to produce a PAA brush polymer. FMOC loading tests were conducted on all these lanterns to assess their effectiveness as combinatorial chemistry supports. It was found that the loading could be controlled by adjusting the graft ratio of the lanterns and had a comparable loading to those commercially produced by Mimotopes.

The use of living radical polymerization methods has shown significant potential to control grafting of polymers from inert polymeric substrates. The objective of this thesis is to create advanced substrates for use in combinatorial chemistry applications through the use of g-radiation as a radical source, and the use of RAFT, ATRP and RATRP living radical techniques to control grafting polymerization. The substrates grafted were polypropylene SynPhase lanterns from Mimotopes and are intended to be used as supports for combinatorial chemistry. ATRP was used to graft polymers to SynPhase lanterns using a technique where the lantern was functionalized by exposing the lanterns to gamma-radiation from a 60Co radiation source in the presence of carbon tetra-bromide, producing short chain polystyrene tethered bromine atoms, and also with CBr4 directly functionalizing the surface. Styrene was then grafted off these lanterns using ATRP. MMA was graft to the surface of SynPhase lanterns, using g-radiation initiated RATRP at room temperature. It was found that the addition of the thermal initiator, AIBN, successfully increased the concentration of radicals to a level where we could achieve proper control of the polymerization. RAFT was used to successfully control the grafting of styrene, acrylic acid and N,N???-dimethylacrylamide to polypropylene SynPhase Lanterns via a -initiated RAFT agent mediated free radical polymerization process using cumyl phenyldithioacetate and cumyl dithiobenzoate RAFT agents. Amphiphilic brush copolymers were produced with a novel combined RAFT and ATRP system. Polystyrene-co-poly(vinylbenzyl chloride) created using gamma-radiation and controlled with the RAFT agent PEPDA was used as a backbone. The VBC moieties were then used as initiator sites for the ATRP grafting of t-BA to give a P(t-BA) brush that was then hydrolyzed to produce a PAA brush polymer. FMOC loading tests were conducted on all these lanterns to assess their effectiveness as combinatorial chemistry supports. It was found that the loading could be controlled by adjusting the graft ratio of the lanterns and had a comparable loading to those commercially produced by Mimotopes.

In the last decade processes known as living/controlled radical polymerizations (L/CRP) have been developed which permit the synthesis of high-value specialty polymers. Currently, the three processes that have demonstrated the most potential are: reverse addition fragmentation chain transfer polymerization (RAFT), atom transfer radical polymerization (ATRP) and stable free radical polymerization (SFRP). While each process has their strengths and weaknesses with regard to specific polymers and architecture, the viability of these systems to industrial scale production all lie in the ability to perform the polymerization in a water based system because of process, environmental and economic advantages. The most effective method of controlling the polymerization of vinyl acetate in bulk has been RAFT. We have developed a miniemulsion RAFT polymerization using the xanthate methyl (ethoxycarbonothioyl)sulfanyl acetate. The miniemulsion is stabilized with 3 wt% sodium lauryl sulfate, initiated with the azo-based water-soluble VA-060. The main focus of this research was adapting ATRP to a miniemulsion system. It was determined that ionic surfactants can be successfully employed in emulsion-based ATRP. The cationic surfactant cetyltrimethylammonium bromide provides excellent stability of the latex over a range of surfactant loadings (allowing the particle size to be easily manipulated), at temperatures up to 90 C, for a wide variety of ATRP formulations. A new method of initiation was developed for reverse ATRP, using the redox pair hydrogen peroxide/ascorbic acid. This nearly eliminated the induction period at the start of the polymerization, increased the polymerization rate 5 fold and, surprisingly, enabled the formation of well-controlled polymers with a number-average molecular (Mn) weight approaching 1 million (typically ATRP is limited to ~200 000). The ability to control the particle size and the number of polymer chains (through the target Mn) over a wide range of values allowed us to determine that ATRP is influenced by compartmentalization effects. The knowledge gained from our work in L/CRP was used to develop the surfactant-free SFRP of styrene. A multi-stage approach was adopted starting from dilute styrene/water solutions to favor the formation of the alkoxyamine and short chain SG1-oligomers (stage one) before the addition of the majority of the styrene (stage two). / Thesis (Ph.D, Chemical Engineering) -- Queen's University, 2007-09-14 12:09:32.266

Living radical polymerization has proved to be a powerful tool for the synthesis of polymers as it allows for a high degree of control over the polymer microstructure and the synthesis of tailored molecular architectures. Although it has great potential, its use on an industrial scale is limited due to environmental and economical aspects. Nitroxide mediated polymerization is explored to bring this technology closer to adoption in commercial applications. One of the obstacles encountered using nitroxide mediated polymerization in microemulsion systems is the difficulty in controlling both the particle size and target molecular weight. Due to the nature of the formulation, a decrease in the target molecular weight is coupled to an increase in the particle size. For many applications, it is important to be able to design polymer particles with both specifications independently. Strategies to decouple these two properties and processing conditions required for targeting a range of particle sizes and molecular weights for n butyl acrylate latexes are presented. Furthermore, in an attempt to reduce the large amounts of surfactant typically used in microemulsions, these methods were explored at low surfactant to monomer ratios (0.2 to 0.5 by wt.) in order to reduce the costs associated with excess surfactant and post processing steps for surfactant removal (high surfactant levels also give poor water-resistance in coatings). Stable nanolatexes with particle sizes <40 nm have been obtained by other groups using NMP in microemulsions with SG1 but have done so by using much higher surfactant to monomer ratios (~2.5 by wt.) and at much lower solids content (6 10 wt. %). In this work, molecular weights of 20,000 to 80,000 g∙mol-1 were targeted and stable, n-butyl acrylate microemulsions with particle sizes ranging from 20 120 nm were prepared at a solids content of 20 wt. % using much lower surfactant concentrations. Although numerous studies have shown the effects of process parameters on particle sizes and methods to control the molecular weight, the decoupling of the molecular weight and particle size effect in NMP microemulsions under these conditions has not been done to this extent. In copolymer systems, nitroxide mediated polymerization also provides an efficient method to synthesize well defined block copolymers. Random copolymers are widely used as protective colloids, but the use of block copolymers for these applications has not been well studied. It is unclear what effects do the importance of a narrow molecular weight distribution and purity of block copolymers have on their performance as protective colloids. In order to investigate this, a range of block copolymers with different properties would need to be synthesized for systematic analysis. The direct synthesis of polystyrene b poly(acrylic acid) copolymers of varying lengths and compositions was successful by use of nitroxide mediated polymerization in bulk and solution polymerization. The characterization of these amphiphilic block copolymers was explored by titration and nuclear magnetic resonance spectroscopy. / Thesis (Master, Chemical Engineering) -- Queen's University, 2012-09-28 15:43:00.513

The use of living radical polymerization methods has shown significant potential to control grafting of polymers from inert polymeric substrates. The objective of this thesis is to create advanced substrates for use in combinatorial chemistry applications through the use of g-radiation as a radical source, and the use of RAFT, ATRP and RATRP living radical techniques to control grafting polymerization. The substrates grafted were polypropylene SynPhase lanterns from Mimotopes and are intended to be used as supports for combinatorial chemistry. ATRP was used to graft polymers to SynPhase lanterns using a technique where the lantern was functionalized by exposing the lanterns to gamma-radiation from a 60Co radiation source in the presence of carbon tetra-bromide, producing short chain polystyrene tethered bromine atoms, and also with CBr4 directly functionalizing the surface. Styrene was then grafted off these lanterns using ATRP. MMA was graft to the surface of SynPhase lanterns, using g-radiation initiated RATRP at room temperature. It was found that the addition of the thermal initiator, AIBN, successfully increased the concentration of radicals to a level where we could achieve proper control of the polymerization. RAFT was used to successfully control the grafting of styrene, acrylic acid and N,N???-dimethylacrylamide to polypropylene SynPhase Lanterns via a -initiated RAFT agent mediated free radical polymerization process using cumyl phenyldithioacetate and cumyl dithiobenzoate RAFT agents. Amphiphilic brush copolymers were produced with a novel combined RAFT and ATRP system. Polystyrene-co-poly(vinylbenzyl chloride) created using gamma-radiation and controlled with the RAFT agent PEPDA was used as a backbone. The VBC moieties were then used as initiator sites for the ATRP grafting of t-BA to give a P(t-BA) brush that was then hydrolyzed to produce a PAA brush polymer. FMOC loading tests were conducted on all these lanterns to assess their effectiveness as combinatorial chemistry supports. It was found that the loading could be controlled by adjusting the graft ratio of the lanterns and had a comparable loading to those commercially produced by Mimotopes.

京都大学 / 0048 / 新制・課程博士 / 博士(工学) / 甲第18522号 / 工博第3914号 / 新制||工||1601(附属図書館) / 31408 / 京都大学大学院工学研究科高分子化学専攻 / (主査)教授 辻井 敬亘, 教授 金谷 利治, 教授 山子 茂 / 学位規則第4条第1項該当 / Doctor of Philosophy (Engineering) / Kyoto University / DFAM

Verdazyl radicals are a family of multicoloured stable free radicals. Aside from the defining backbone of four nitrogen atoms, these radicals contain multiple highly modifiable sites that grant them a high degree of derivatization. Despite having been discovered more than half a century ago, limited applications have been found for the verdazyl radicals and little is known about their chemistry. This thesis begins with an investigation to determine whether verdazyl radicals have a future as mediating agents in living radical polymerizations and progresses to their application as substrates for organic synthesis, an application that to date has not been pursued either with verdazyl or nitroxide stable radicals. The first part of this thesis describes the successful use of the 1,5-dimethyl-3-phenyl-6-oxoverdazyl radical as a mediating agent for styrene and n-butyl acrylate stable free radical polymerizations. The study of other verdazyl derivatives demonstrated the impact of steric and electronic properties of the verdazyl radicals on their ability to mediate polymerizations. The second part of this thesis outlines the initial discovery and the mechanistic elucidation of the transformation of the 1,5-dimethyl-3-phenyl-6-oxoverdazyl radical into an azomethine imine, which in the presence of dipolarophiles, undergoes a [3+2] 1,3-dipolar cycloaddition reaction to yield unique pyrazolotetrazinone structures. The reactivity of the azomethine imine and the scope of the reaction were also examined. The third part of this thesis describes the discovery and mechanistic determination of a base-induced rearrangement reaction that transforms the verdazyl-derived pyrazolotetrazinone cycloadducts into corresponding pyrazolotriazinones or triazole structures. The nucleophilicity, or the lack thereof, of the base employed leading to various rearrangement products was examined in detail. The final part of this thesis demonstrates the compatibility of the verdazyl-initiated cycloaddition and rearrangement reactions with the philosophy of diversity-oriented synthesis in generating libraries of heterocycles. A library of verdazyl-derived heterocycles was generated in a short amount of time and was tested non-specifically for biological activity against acute myeloid leukemia and multiple myeloma cell lines. One particular compound showed cell-killing activity at the 250 mM range, indicating future potential for this chemistry in the field of drug discovery.

Verdazyl radicals are a family of multicoloured stable free radicals. Aside from the defining backbone of four nitrogen atoms, these radicals contain multiple highly modifiable sites that grant them a high degree of derivatization. Despite having been discovered more than half a century ago, limited applications have been found for the verdazyl radicals and little is known about their chemistry. This thesis begins with an investigation to determine whether verdazyl radicals have a future as mediating agents in living radical polymerizations and progresses to their application as substrates for organic synthesis, an application that to date has not been pursued either with verdazyl or nitroxide stable radicals. The first part of this thesis describes the successful use of the 1,5-dimethyl-3-phenyl-6-oxoverdazyl radical as a mediating agent for styrene and n-butyl acrylate stable free radical polymerizations. The study of other verdazyl derivatives demonstrated the impact of steric and electronic properties of the verdazyl radicals on their ability to mediate polymerizations. The second part of this thesis outlines the initial discovery and the mechanistic elucidation of the transformation of the 1,5-dimethyl-3-phenyl-6-oxoverdazyl radical into an azomethine imine, which in the presence of dipolarophiles, undergoes a [3+2] 1,3-dipolar cycloaddition reaction to yield unique pyrazolotetrazinone structures. The reactivity of the azomethine imine and the scope of the reaction were also examined. The third part of this thesis describes the discovery and mechanistic determination of a base-induced rearrangement reaction that transforms the verdazyl-derived pyrazolotetrazinone cycloadducts into corresponding pyrazolotriazinones or triazole structures. The nucleophilicity, or the lack thereof, of the base employed leading to various rearrangement products was examined in detail. The final part of this thesis demonstrates the compatibility of the verdazyl-initiated cycloaddition and rearrangement reactions with the philosophy of diversity-oriented synthesis in generating libraries of heterocycles. A library of verdazyl-derived heterocycles was generated in a short amount of time and was tested non-specifically for biological activity against acute myeloid leukemia and multiple myeloma cell lines. One particular compound showed cell-killing activity at the 250 mM range, indicating future potential for this chemistry in the field of drug discovery.

The synthesis of well-defined polymer nanoparticles will have immediate applications in the biomedical industry as nanocontainers for the controlled delivery and release of water insoluble drugs. The ability to control molecular weight, particle morphology and chemical functionality and to obtain polymeric nanoparticles with narrow molecular weight and particle size distributions is paramount for their application-specific design. Two synthetic approaches were investigated in the synthesis of well-defined polymer nanoparticles, emulsion polymerization and self assembly. The successful implementation of Reversible Addition-Fragmentation Chain Transfer (RAFT) in emulsion polymerization was the first challenge faced when controlling nanoparticle molecular weight and size. Initially we showed that successful ‘living’ emulsion polymerizations of styrene could be carried out using a non-ionic surfactant. The success was achieved when preparing polymers of low molecular weight (5 and 9 K targeted Mn’s with polydispersities (PDIs) below 1.2). Deviation from ideal ‘living’ behavior occurred when targeting Mn’s greater than 20 K (at 100 % conversion). The ‘degassing technique’ was then investigated as an avenue to generate stable polystyrene nanoparticles by emulsion polymerization without the addition of surfactant (residual surfactant can result in detrimental effects on product quality). The polymerization of this emulsion system in the presence of a low reactive RAFT agent was ‘living’ in nature. In the presence of a high reactive RAFT agent the emulsion system showed ‘living’ nature, however, secondary nucleation occurred, which resulted in broad molecular weight distribution (MWD). Thus, the emulsion polymerization approach to preparing well-defined polymer nanoparticles was giving less than desirable results. An alternative method to prepare polymer nanoparticles with controlled chemical composition and morphology is to self assemble pre-synthesized block copolymers in water. This approach has several significant advantages over the emulsion systems: (i) all polymer chains are of near uniform chain length and chemical composition, (ii) the ratio between the hydrophobic and hydrophilic polymers can easily be controlled, (iii) chemical functionality can be located in different morphological regions, (iv) a wide range of 3-dimensional structures apart from spheres can be prepared (i.e. rods and vesicles), and (v) additives such as surfactant, stabilizers and residual monomer usually found after an emulsion polymerization are not required in the self assembly methodology. These advantages justify our shift in strategy. The only disadvantage of the self assembly process is that one cannot reach high weight fractions of polymer in water and is usually limited to below 2 wt-%, where as emulsion polymerizations can allow weight fractions of polymer close to 50 wt-%. Well-defined amphiphilic 4-arm star polyacrylic acid-block-polystyrene (PAA-b-PSTY) copolymers, prepared by RAFT solution polymerization, were dispersed in water to form core-shell micelles, in which the shell consisted of tethered PAA loops. The entropic penalty for having such loops resulted in a less densely packed PSTY core when compared to linear diblock copolymers of the same arm length. The surface of the shell was irregular due to the tethering points, but when cleaved the PAA chains extended to form a regular and relatively uniform corona. Controlling the polymer architecture enabled the synthesis of polymer micelles with tethered PAA loops, which could be opened to form uniform corona when desired. Three-miktoarm star and dendrimers with miktoarms consisting of PSTY, polytert-butyl acrylate (PtBA), polymethyl acrylate (PMA) and PAA were then synthesized using a combination of Atom Transfer Radical Polymerization (ATRP) and Huisgen 1,3-dipolar cycloaddition ‘click’ reactions. In all reactions, the stars and dendrimers were well-defined with PDIs lower than 1.09. This was the first step in the synthesis of well-defined highly ordered polymer structures. The synthesis of such structures demands high level of purity at each synthetic step eliminating the possibility of side reactions, which as of consequence lowers product yields. The synthesis and use of reactive solid supports to remove excess linear polymer to increase the yields of polymeric 3-arm stars and dendrimers was employed. These supports are a cheap approach to scavenge polymeric species with either azido or alkynyl functionality, after which the solid support can be filtered away from the product. These supports aided the synthesis of 3rd generation polymeric dendrons and dendrimers consisting of homopolymer PSTY with either solketals or alcohols at the periphery, diblock PSTY and PtBA, and amphiphilic diblock. The methodology used to construct these structures was a combination of ATRP to produce linear polymers with telechelic functionality, with the subsequent use of this functionality to join the polymers together via ‘click’ reactions. Micellization of the amphiphilic structures in water produced polymer nanoparticles of uniform size. The dendrimer nanoparticles were 18 nm in diameter, consisting of 19 individual dendrimers. The dendrimers most probably have no mutual interpenetration and thus pack uniformly to form the micelles. The dendron nanoparticles were 21 nm with an aggregation number of 43 dendrons per micelle, which suggests they form cone-like structures and self-assemble to form crew-cut micelles. Using a convergent approach polymer structures with unprecedented chemical diversity (hydrophobic or amphiphilic) and complexity (G2 miktoarm dendrimers with a degradable core) consisting of PSTY, PMA, PtBA and PAA were then synthesized with high purity using copper wire as the ‘click’ catalyst.