Made available in DSpace on 2014-10-09T12:36:01Z (GMT). No. of bitstreams: 0 / Made available in DSpace on 2014-10-09T13:59:48Z (GMT). No. of bitstreams: 0 / Dissertação (Mestrado) / IPEN/D / Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP

Made available in DSpace on 2015-03-26T13:23:21Z (GMT). No. of bitstreams: 1 texto completo.pdf: 1441039 bytes, checksum: 1a4c158d5650dd52d4cba8016e068631 (MD5) Previous issue date: 2006-08-22 / Conselho Nacional de Desenvolvimento Científico e Tecnológico / This study was carried out to evaluate the potential of the sugarcane bagasse ash (CBC) as partial replacement material for the Portland cement in mortar. A residue generated at the Jatiboca sugar mill located in Urucânia county-MG was used as CBC. The use of the sugarcane bagasse as an ash source for mineral addition into cement-based materials is subjected to two factors: the production and chemical constitution of the ash. The sugarcane bagasse ash (CBC) is predominantly composed by silicon dioxide, that can develop pozollan activity depending on the characteristics of both burning and grain size. In this case, the reactivity between silica and the hydration products may improve the physical and mechanical properties of the cement-based materials with incorporated residues. The work was divided into two phases: CBC characterization and the evaluation of its addition to mortar, by using mechanical and physical assays. According to the results, the sugarcane bagasse showed 10% CBC production. CBC presents 84% SiO2 and 5% carbon. The CBC silica is shown either in amorphous phase and crystalline phase of Crystobalite and Quartz. Concerning to grain size and surface area, the ash under study is composed by either particles at the size range from 1 to 14 μm and specific surface area of 24 m2/g. When considering the initial and final time of the mortar hardening, it was observed that the additions of 10%, 20% and 30% CBC caused a 10min delay in the interval between the times of mortar hardening. Relative to pozzolan activity indexes, the results corroborate the reactivity by CBC. It was also observed that the mortars with higher ash contents tend to be more porous, which justifies the highest values found for absorption. Regarding the specific mass, the partial substitution of the Portland cement up to 30% ashes in the mixture provoked no significant modification. The mortar compression assays with CBC contents between zero and 30%, that were accomplished at 7th and 28th days pointed out the possibility for replacement up to 20% cement by CBC with no damaged resistance. / Este trabalho teve como objetivo avaliar o potencial da CBC como material de substituição parcial do cimento Portland em argamassa. A CBC empregada é um resíduo gerado na usina de açúcar Jatiboca, localizada no município de Urucânia-MG. A utilização do bagaço da cana de açúcar como fonte de cinza como adição mineral em materiais à base de cimento obedece a dois fatores: o rendimento de cinza e a sua constituição química. A cinza do bagaço da cana-de-açúcar (CBC) é composta predominantemente por dióxido de silício, o qual, dependendo das características de queima e da granulometria, pode desenvolver atividade pozolânica. Neste caso, a reatividade entre sílica e os produtos de hidratação podem acarretar em melhoria nas propriedades físicas e mecânicas doas materiais à base de cimento com incorporação de resíduos. O trabalho foi dividido em duas fases: caracterização da CBC e avaliação do seu emprego como adição em argamassa através de ensaios mecânicos e físicos. Os resultados mostraram que o bagaço apresenta um rendimento de CBC de 10%. A cinza de CBC apresenta 84% de SiO2 e 5% de carbono. A sílica na CBC apresenta-se tanto na fase amorfa quanto nas fases cristalinas de Cristobalita e Quartzo. Os resultados encontrados para a composição granulométrica e área de superfície demonstraram que a cinza em estudo é composta por partículas com tamanhos entre 1 e 14 μm e com uma área de superfície específica da ordem de 24 m2/g. Com relação ao estudo do tempo de pega inicial e final, foi observado que as adições de 10%, 20% e 30% de CBC acarretaram um retardo de 10 min no intervalo entre os tempos de pega. Os resultados encontrados para os índices de atividade pozolânica comprovam a reatividade da CBC. Observou-se que as argamassas com maiores teores de cinza tendem a ser mais porosas, o que justifica os maiores valores de absorção encontrados. Com relação à massa específica, a substituição parcial do cimento Portland por até 30% de cinzas na mistura não provocou qualquer modificação significativa. Os ensaios de compressão das argamassas com teores de CBC entre 0 e 30%, aos 7 e 28 dias, indicaram a possibilidade de substituição de até 20% do cimento pela CBC, sem prejuízo da resistência.

Made available in DSpace on 2015-03-26T13:28:29Z (GMT). No. of bitstreams: 1 texto completo.pdf: 3488671 bytes, checksum: a0cc64cf7989ec79afc7a4c8c0b12ea6 (MD5) Previous issue date: 2013-10-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / In this work, with a view of environmental protection and the use of a waste residue as a raw material for productive applications, the possibility of using water treatment plant (WTP) sludge in the making of soil-cement bricks was evaluated. By means of a mixture experimental design, several soil-cement- sludge compositions were tried, using: a sand soil from 'Nô Silva' field, located in the surroundings of Viçosa-MG; and a Portland cement type CP III-40-S. The suitability of WTP sludge for being used in soil-cement was initially evaluated in the basis of its physical (e.g. granulometric composition and Atterberg limits), mineralogical (X-ray diffraction), chemical (energy dispersive X-ray analysis EDS) and morphological (scanning electron microscopy SEM) characterization. Some of the physical characteristics of the sludge (e.g. high proportions of fine particles, and high liquid and plastic limits) as well as the relatively high organic matter content, suggested from the beginning that the incorporation of WTP sludge in soil-cement bricks should be done in small proportions. In effect, the trials carried out with bricks that were prepared with different proportions of soil, cement and sludge showed that the higher the sludge fraction the lesser the bricks mechanical resistance. The results also indicated that Brazilian standard of 2,0 MPa mechanical resistance for soil- cement bricks with no structural function would be attained only with mixtures containing 6% of sludge (partially replacing the soil) and a minimum of 15% of cement. It is suggested that further experiments should look at solutions that make it possible to add higher fractions of sludge, turning soil-cement-sludge bricks a more attractive option from the economic point of view. / Neste trabalho foi avaliada a possibilidade de incorporação de lodo de estação de tratamento de água (ETA) na manufatura de tijolos de solo-cimento, na perspectiva de preservação ambiental e aproveitamento de um resíduo como matéria prima em aplicação produtiva. Por meio de delineamento experimental de misturas foram avaliados vários traços de composições solo-cimento-lodo: solo com características arenosas, proveniente da jazida Nô Silva na microrregião de Viçosa, MG; lodo do decantador da ETA da Universidade Federal de Viçosa (UFV) e cimento Portland tipo CP III-40-RS. A aptidão do lodo para aplicação em solo-cimento foi inicialmente avaliada com base em caracterização física (granulometria e limites de Atterberg, dentre outras), mineralógica (difração de raios-X), química (análise de raios-X por dispersão de energia EDS) e morfológica (microscopia eletrônica de varredura MEV). As características granulométricas e de consistência do lodo (material predominantemente fino, com limites de liquidez e de plasticidade elevados), além da presença de teores relativamente elevados de matéria orgânica, sugerem que a incorporação do lodo em tijolos de solo-cimento deva se dar em baixas proporções. Com efeito, os testes com tijolos preparados com diversos traços de mistura solo-cimento-lodo revelaram que a resistência mecânica diminuiu com o incremento de lodo e que o requisito da norma NBR 8491 para aceitação do tijolo em obras de alvenaria sem função estrutural (2,0 MPa) seria atendido com traços com 6% de lodo (substituindo parcialmente o solo) e no mínimo 15% de cimento. Sugere-se a continuidade dos estudos na busca de opções que viabilizem a incorporação de proporções mais elevadas de lodo e tornem os tijolos de solo-cimento-lodo uma opção mais atrativa do ponto de vista econômico.

Made available in DSpace on 2015-04-01T11:58:39Z (GMT). No. of bitstreams: 1 arquivototal.pdf: 3583715 bytes, checksum: 18e9b18d6b0151c38251cd2a26b3f40a (MD5) Previous issue date: 2013-11-22 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / The final destination for waste polymers EVA (Ethylene Vinyl Acetate) discarded by footwear industries has been recognized as a increasing problem of impact on the environment. However, studies have show that these residues have characteristics suitable for recycling purposes transforming them into lightweight aggregates, which may provide benefits to the environment for example, their use to attenuate effects of noise impacts problems on the floors, which are very common in multi floor buildings. This research aims to evaluate the acoustic performance of cement boards, consisting of waste aggregates EVA (EVA boards), applied as a resilient material in the composition of floating floor. In this study three types of EVA boards were developed with different thickness and geometries, one of which has whole flat surface (EVA_ar0) and the other with a low relief surfaces (EVA_ar1 and EVA_ar2,5), to yield a layer of air between these boards and the slab. The plates were evaluated for the ability to soundproofing, following the guidelines of ISO 140-7:1998 and ISO 717-2:2013, seeking to compare their performance with some materials available for use in floating floors, for example, polyethylene acoustic blanket and rock wool. The assessment of the level of sound insulation to mitigate the noise impact was performed in a Testing Laboratory of Materials and Structures, Federal University of Paraiba, simulating a situation between two adjacent floors. Based on the results it can be stated that the boards EVA, according to their performance achieved, has the potential to rank as an alternative material used for mitigation of impact noise between floors of multi floor buildings. The floating floor system composed with the board EVA_ar2 , 5 (with air 2.5 cm layer ) had global number (L'nT,w) equal to 64 dB, framed with better intermediate level of performance (I) the that the performance of other systems with boards EVA_ar0 (without air layer) and EVA_ar1 (with air 1 cm layer) obtained global number 67 and 66 dB respectively classifying performance with minimal (M), according to NBR 15.575-3:2013. / A destinação final para os resíduos de polímeros de EVA (Etileno Acetato de Vinila) descartados pelas indústrias calçadistas tem sido reconhecida como um problema crescente de impacto no meio ambiente. Contudo, estudos têm comprovado que esses resíduos possuem características adequadas para propósitos de reciclagem transformando-os em agregados leves, que podem trazer benefícios ao ambiente construído, como por exemplo, o seu aproveitamento visando atenuação de problemas de ruídos de impactos nos pisos, que são muito comuns nas edificações multipavimentos. Portanto, essa pesquisa tem como objetivo avaliar o desempenho acústico de placas cimentícias, executadas com agregados de resíduos de EVA (placas de EVA), aplicadas como material resiliente na composição de sistemas de piso flutuante. Nesse estudo foram desenvolvidas três placas de EVA com espessura e geometrias diferentes, sendo uma delas com todas as superfícies planas (EVA_ar0) e outras duas com uma das superfícies com baixo relevo (EVA_ar1 e EVA_ar2,5), de modo a resultar uma camada de ar entre tais placas e a laje. As placas foram avaliadas quanto a capacidade de isolamento acústico, seguindo as diretrizes das normas ISO 140-7:1998 e ISO 717-2:2013, procurando comparar seu desempenho com alguns materiais disponíveis no mercado para uso em pisos flutuantes, como por exemplo, manta acústica de polietileno e lã de rocha. A avaliação do nível de isolamento acústico para atenuar os ruídos de impacto foi realizada em protótipo no Laboratório de Ensaio de Materiais e Estruturas da Universidade Federal da Paraíba, simulando uma situação entre dois pavimentos sobrepostos. Com base nos resultados pode-se afirmar que as placas de EVA, de acordo com seu desempenho alcançado, tem potencial para se classificar como um material alternativo utilizado para atenuação de ruído de impacto entre os pisos de edificações multi pavimento. O sistema de piso flutuante composto com a placa de EVA_ar2,5 (com camada de ar de 2,5 cm) obteve número global (L´nT,w) igual a 64 dB, enquadrado com nível de desempenho intermediário (I) melhor do que os desempenhos dos outros sistemas com as placas do EVA_ar0 (sem camada de ar) e EVA_ar1 (com camada de ar de 1 cm) obtiveram número globais 67 e 66 dB respectivamente se classificando com desempenho mínimo (M), segundo a NBR 15.575-3:2013.

Made available in DSpace on 2016-12-08T17:19:16Z (GMT). No. of bitstreams: 1 Cap 1.pdf: 354743 bytes, checksum: 0343c49a38673dd157dcd55a3475b0c2 (MD5) Previous issue date: 2012-02-16 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The environmental efficiency permeates all production sectors through a closed cycle of production and consumption of materials. The recycling of solid waste should be priorized against the consumption of natural raw materials as long as environmental and technical viability have been proved. The foundries are great ferrous scrap recyclers, but generate huge amount of waste, especially the foundry sand. In order to contribute to the sustainability of foundry and construction industries this work investigates the possibility of recycling spent foundry sand (ADF) in soilcement (SC) bricks. The soil-cement construction uses soil as natural raw material, sand and gravel if necessary correction, and cement as a stabilizer. The research involves the characterization of the raw materials by X-ray diffraction, thermal analysis, particle size, leaching and solubilization tests. In blends cement makes up 10% by weight and the soil, predominantly clayey, was partially replaced by spent foundry sand and gravel in different percents. The influence of the residue on the physico-chemical and mechanical properties of the mixtures was analyzed through compaction tests, isothermal conduction calorimetry, compressive strength, durability and water absorption in cylindrical specimens and modular bricks. The interface between the components was observed by electron microscopy scanning. The addition of spent foundry sand decreases the water absorption of the mixture and increases the maximum density with small changes in mechanical strenght. The bricks produced have water absorption and mass loss in the durability test in accordance with the current technical standards. The addition of ADF combined with gravel rises mechanical resistance to acceptable levels of soil-cement standards. The results attest the technical and environmental feasibility for the use of spent foundry sand in soil-cement bricks for masonry seal. / A eficiência ambiental permeia todos os setores produtivos através de um ciclo fechado de produção e consumo de materiais. A reciclagem de resíduos sólidos deve ser priorizada frente ao consumo de matérias-primas naturais, desde que comprovada viabilidade ambiental e técnica para tal. As fundições são grande recicladoras pois utilizam sucatas ferrosas como matéria-prima, porém geram enorme quantidade de resíduos, com destaque para as areias de moldagem. Buscando contribuir para a sustentabilidade das indústrias de fundição e da construção civil esse trabalho investiga a possibilidade da reciclagem de areia descartada de fundição (ADF) em tijolos de solo-cimento (SC). A construção com solo-cimento utiliza o solo como matéria-prima natural, se necessário areia e pedrisco para correção e o cimento como estabilizante. O estudo passa pela caracterização das matérias-primas utilizadas por difração de raios-X, análise térmica, granulometria, lixiviação e solubilização. Nas misturas o cimento compõe 10% em peso e o solo, de predominância argilosa, foi parcialmente substituído por areia descartada de fundição e pó de brita em diferentes percentuais. Assim foi analisada a influência da adição do resíduo nas propriedades físico-químicas e mecânicas das misturas através de ensaios de compactação, calorimetria de condução isotérmica, resistência à compressão, durabilidade e absorção de água em corpos de prova cilíndricos e tijolos modulares. A interface entre os materiais constituintes do solo-cimento foi observada por microscopia eletrônica de varredura. A adição do resíduo de areia de fundição diminui a absorção de água da mistura e aumenta a densidade máxima com pequenas alterações na resistência mecânica. Os tijolos produzidos apresentam absorção de água e perda de massa no ensaio de durabilidade em conformidade com as normas técnicas vigentes. A adição combinada de ADF e de pó de brita eleva a resistência mecânica a níveis aceitos pelas normas de solo-cimento. Os resultados obtidos atestam a viabilidade técnica e ambiental para a utilização da areia descartada de fundição em tijolos de solo-cimento para alvenaria de vedação.

Made available in DSpace on 2016-12-08T17:19:20Z (GMT). No. of bitstreams: 1 Patrik Americo P Lopes.pdf: 19215385 bytes, checksum: b9a68e9cabd2bb83d1daa99db32ea92d (MD5) Previous issue date: 2013-02-21 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Portland cement is a material used in large scale in Brazil and worldwide. However, its manufacturing process is attached to impacting environmental problems. Thus, the use of recyclable materials with pozzolanic characteristics has been studied to partially replace cement in applications such as mortars and concretes. Therefore, this work aims to study the effect of partial replacement of Portland cement with clay brick waste (CBW) on properties of lime-cement mortars (cement and hydrated lime) for building applications. A statistical study using a fractional factorial design 33-1 considered three factors and three levels for each factor, which were the residue content for cement mortars (%CBW of 10%, 25% and 40%), his particle size (PS of 125μm, 75μm and 45μm) and water/cement ratio (W/C of 2.50, 2.85 and 3.20). The properties measured were the consistency index for fresh and the compressive strength at various ages for hardened properties. The physical, chemical and microstructural characterizations of mortars with and without RPT were performed in order to correlate their mechanical and microstructural properties. Thus, the CBW has been shown to act as a pozzolanic material, with an addition of up to 40% could be performed without the physical and mechanical properties were impaired. The particle size was found to be important in the pozzolanicity of the waste, being more efficient at lower values than 75μm, inclusive. Through the characterization of the mortars was observed the consumption of calcium hydroxide, caused by the pozzolanic reaction of the CBW, forming the calcium silicate hydrate gel, increasing the density of the cementitious matrix and improving the cohesion between the elements of the mixture. / O cimento Portland é um material consumido em grande escala no Brasil e no mundo. Porém, seu processo de fabricação é ligado a problemas ambientais impactantes. Com isso, a utilização de materiais recicláveis, com características pozolânicas, vem sendo estudado para substituir parcialmente o cimento em aplicações como argamassas e concretos. Portanto, este trabalho tem como finalidade estudar o efeito da substituição parcial do cimento Portland por resíduo particulado de tijolo (RPT) nas propriedades de argamassas mistas (cimento e cal hidratada) para aplicação na construção civil. Um estudo estatístico utilizando um projeto fatorial fracionado 33-1 levou em consideração três fatores e três níveis para cada fator, os quais foram o teor de resíduo em substituição ao cimento (%RPT de 10%, 25% e 40%), o tamanho de partícula do resíduo (TP de 125μm, 75μm e 45μm) e o fator água/cimento (W/C de 2,50, 2,85 e 3,20). As propriedades medidas foram o índice de consistência para o estado fresco e a resistência à compressão em várias idades para o estado endurecido. A caracterização física, química e microestrutural das argamassas com e sem RPT foram realizadas a fim de correlacionar suas propriedades mecânicas e microestruturais. Com isso, o RPT se mostrou capaz de agir como material pozolânico, sendo que uma adição de até 40% pôde ser realizada, sem que as propriedades físicas e mecânicas fossem prejudicadas. A granulometria mostrou-se importante na pozolanicidade do resíduo, sendo mais eficiente em valores menores do que 75μm, incluindo este. Através da caracterização das argamassas foi observado o consumo do hidróxido de cálcio causado pela reação pozolânica do RPT, formando o gel de silicato de cálcio hidratado, densificando a matriz cimentícia e melhorando a coesão entre os elementos da mistura.

Submitted by FLÁVIA FLORENTINO DE ALMEIDA null (flavialm_1@hotmail.com) on 2017-10-09T15:23:59Z No. of bitstreams: 1 Flavia Final rev 09. ...02.10.17_word2010.pdf: 3209005 bytes, checksum: c3164cf910a07e38e30d2c81a62eb29f (MD5) / Approved for entry into archive by Monique Sasaki (sayumi_sasaki@hotmail.com) on 2017-10-09T18:53:36Z (GMT) No. of bitstreams: 1 almeida_ff_me_bauru.pdf: 3209005 bytes, checksum: c3164cf910a07e38e30d2c81a62eb29f (MD5) / Made available in DSpace on 2017-10-09T18:53:36Z (GMT). No. of bitstreams: 1 almeida_ff_me_bauru.pdf: 3209005 bytes, checksum: c3164cf910a07e38e30d2c81a62eb29f (MD5) Previous issue date: 2017-08-30 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Uma das alternativas para a destinação de Resíduos de Equipamentos Eletroeletrônicos (REEE), termo adotado no Brasil e tradução literal do inglês Waste Eletronic and Electrical Equipament (WEEE), é a reciclagem. Em geral os metais presentes nesses resíduos apresentam maior interesse para as recicladoras, porém as carcaças dos equipamentos constituídas por polímeros acabam sendo destinadas a aterros. O presente trabalho apresenta uma forma simples e barata de se agregar valor a esse resíduo, tornando-o mais vantajoso financeiramente. Um estudo do comportamento do concreto com adição de polímeros fracionados provenientes de carcaças de equipamentos eletroeletrônicos descartados em substituição a parte do agregado graúdo é apresentado. Para isso foi feita a caracterização dos polímeros proveniente do REEE e foi estudado o comportamento de corpos de prova produzidos com adição de 5%, 8%, 10%, 15% e 20% em massa desse resíduo, mantendo um traço sem incorporação para comparação. O agregado graúdo obtido a partir dos polímeros advindos do REEE tem predominância da sua granulometria na faixa dos 6,3 mm, são identificados como sendo constituídos por HIPS (High Impact Polystyrene), e apresentam-se como material hidrofílico possibilitando boa interação com argamassa de cimento e água. Os concretos obtidos com até 20% de incorporação desse resíduo apresentam densidade superior a 2,0g/cm3, permitindo classifica-los como um concreto estrutural normal. O aumento da porcentagem de incorporação de REEE ao concreto leva a uma diminuição da resistência a compressão, porém esse valor é sempre superior a 20 MPa, identificando-o como um concreto de resistência média. A incorporação desse resíduo, devido ao seu formato, contribui com uma característica semelhante a de utilização de fibras em concreto impedindo o rompimento completo dos corpos. Esses resultados evidenciam a viabilidade de se incorporar REEE ao concreto, possibilitando uma valorização desse resíduo como agregado graúdo para concreto. / One of the alternatives for the disposal of Waste Electrical and Electronic Equipment (WEEE), is recycling. In general, the metals present in these wastes are of greater interest to recyclers, but the carcasses of equipment made of polymers end up being destined to landfills. The present paper presents a simple and inexpensive way to add value to this waste, making it more advantageous financially. A study on the behavior of concrete with addition of fractionated polymers from carcasses of discarded electro-electronic equipment replacing part of the large aggregate is presented. For this, was done the characterization of the polymers from WEEE and analyzed the behavior of test specimens produced with addition of 5%, 8%, 10%, 15% and 20% in mass of this residue, maintaining a trace without incorporation for comparison. The large aggregate obtained from the WEEE polymers has a predominance of their granulometry in the range of 6.3 mm. They are identified as HIPS (High Impact Polystyrene) and are presented as a hydrophilic material allowing a good interaction with cement and water. The concretes obtained with up to 20% of incorporation of this residue present density superior to 2,0 g / cm3, allowing to classify them like a normal structural concrete. The increase in the percentage of incorporation of WEEE into the concrete leads to a decrease in the compressive strength, but this value is always higher than 20 MPa, identifying it as a medium-strength concrete. The incorporation of this residue, due to its shape, contributes with a characteristic similar to the use of fibers in concrete preventing the complete rupture of the bodies. These results demonstrate the feasibility of incorporating WEEE into the concrete, allowing a valorization of this waste as a large aggregate for concrete.

Orientador: José Augusto de Lollo / Banca: Reinaldo Lorandi / Banca: Milton Dall'Aglio Sobrinho / Resumo: As barreiras de proteção ambiental são os dispositivos mais usados na atualidade para reduzir riscos associados à infiltração de fluidos nocivos no subsolo. O presente trabalho dedicou-se ao estudo, em laboratório, de misturas de solo arenoso fino laterítico com cal e cimento para a produção de barreiras desta natureza. Para tanto, foram compactadas misturas a fim de produzir corpos de prova submetidos a ensaios, visando à avaliação da condutividade hidráulica e da capacidade de retenção de soluções de origem orgânica (chorume e água residuária) e inorgânica (soluções contendo os íons K+, Na+ e Cl-) destas misturas. A condutividade hidráulica foi avaliada com ensaios de permeabilidade em duas condições: à carga variável (corpos de prova de 10cm de diâmetro e 12cm de altura) e em área plena (corpos de prova miniatura - 5cm de altura e diâmetro). Para avaliação da capacidade de retenção foram considerados dois tipos de ensaios: em colunas (25cm de altura e 7cm de diâmetro) e em corpos miniatura (5cm de altura e diâmetro). Os resultados obtidos mostram que os materiais produzidos em tais condições atendem aos requisitos técnicos para seu uso como barreiras de proteção ambiental. Os valores de condutividade hidráulica obtidos foram menores que os exigidos e os processos de retenção observados mostraram resultados muito bons para os fluidos de origem orgânica e resultados bastante promissores para as soluções inorgânicas. / Abstract: Natural liners are the most useful environmental protection systems in order to reduce soil and ground water pollution risks. In this work we made laboratory tests to evaluate hydraulic conductivity and ions retention capability in mixtures produced with soil-cement and soil-lime. Mixtures were compacted, resulting specimens for laboratory tests of hydraulic conductivity and retention capability with organic (leachate and wastewater) and inorganic (solutions with K+, Na+ e Cl-) solutions. For hydraulic conductivity evaluation was used two kinds of tests: variable charge (specimens with 10cm of diameter and 12cm high) and total section test (specimens with 5cm of diameter and high). For retention capability we used also two kinds of tests: column test (specimens with 7cm of diameter and 25cm high) and total section test (specimens with 5cm of diameter and high). Obtained results show that the produced materials obey technical necessities for barriers usage. Hydraulic conductivity obtained show values lesser than the necessary, while capability retention results show good results also for organic and inorganic solutions. / Mestre

Made available in DSpace on 2014-12-17T14:58:21Z (GMT). No. of bitstreams: 1 FaisyPPS_DISSERT_Capa_ate _pag30.pdf: 3190627 bytes, checksum: 6b8c39ddf6fc3949b555ea3b2beef8a3 (MD5) Previous issue date: 2013-03-15 / The need to build durable structures and resistant to harsh environments enabled the development of high strength concrete, these activities generate a high cement consumption, which implies factor in CO2 emissions. Often the desired strength is not achieved using only the cement composition. This study aims to evaluate the influence of pozzolans with the addition of metakaolin on the physical mechanics of high strength concrete comparing them with the standard formulation. Assays were performed to characterize the aggregates according to NBR 7211, evaluation of cement and coarse aggregate through the trials of petrography (NBR 15577-3/08) and alkali-aggregate reaction (NBR 15577-05/08). Specimens were fabricated according to NBR 5738-1/04 with additions of 0%, 4%, 6%, 8% and 10% of metakaolin for cement mortars CP V in the formulations. For evaluation of the concrete hardened in fresh state and scattering assays were performed and compressive strength in accordance with the NBR 7223/1992 and NBR 5739-8/94 respectively. The results of the characterization of aggregates showed good characteristics regarding size analysis and petrography, as well as potentially innocuous as the alkali-aggregate reaction. As to the test of resistance to compression, all the formulations with the addition of metakaolin showed higher value at 28 days of disruption compared with the standard formulation. These results present an alternative to reduce CO2 emissions, and improvements in the quality and durability of concrete, because the fine particle size of metakaolin provides an optimal compression of the mass directly influencing the strength and rheology of the dough / A necessidade de construir estruturas dur?veis e resistentes a ambientes agressivos proporcionou o desenvolvimento do concreto de alta resist?ncia, tais atividades geram um alto consumo de cimento, fator que implica na emiss?o CO2. Muitas vezes a resist?ncia desejada n?o ? atingida utilizando apenas o cimento na composi??o. Este trabalho tem como objetivo avaliar a influ?ncia das pozolanas com a adi??o de metacaulim nas caracter?sticas f?sico mec?nicas do concreto de alta resist?ncia comparando-as com a formula??o padr?o. Foram realizados ensaios de caracteriza??o dos agregados de acordo com a norma NBR 7211, avalia??o do cimento e agregado gra?do atrav?s dos ensaios de petrografia (NBR 15577 - 3/08) e rea??o alcali-agregado (NBR 15577-05/08). Foram confeccionados corpos de prova de acordo com a norma NBR 5738-1/04 com adi??es de 0%, 4%, 6%, 8% e 10% de metacaulim em substitui??o ao cimento CP V nas formula??es. Para avalia??o do concreto no estado fresco e endurecido foram realizados ensaios de espalhamento e resist?ncia ? compress?o de acordo com as normas NBR 7223/1992 e NBR 5739-8/94 respectivamente. Os resultados da caracteriza??o dos agregados apresentaram boas caracter?sticas quanto ? an?lise granulom?trica e petrografia, bem como potencialmente in?cuos quanto ? rea??o alcali-agregado. Quanto ao ensaio de resist?ncia ? compress?o, todas as formula??es com adi??o de metacaulim apresentaram valor superior aos 28 dias de ruptura quando comparadas com a formula??o padr?o. Estes resultados apresentam uma alternativa de redu??o da emiss?o de CO2, al?m de melhorias na qualidade e durabilidade do concreto, pois a fina granulometria do metacaulim proporciona uma ?tima compacta??o da massa influenciando diretamente na resist?ncia mec?nica e reologia da massa

Made available in DSpace on 2014-12-17T15:01:28Z (GMT). No. of bitstreams: 1 RomeroGSAF_DISSERT.pdf: 5251211 bytes, checksum: 91e35eccdc843f543fbc2744a816fb64 (MD5) Previous issue date: 2012-03-16 / Coordena??o de Aperfei?oamento de Pessoal de N?vel Superior / All around the world, naturally occurring hydrocarbon deposits, consisting of oil and gas contained within rocks called reservoir rocks , generally sandstone or carbonate exists. These deposits are in varying conditions of pressure and depth from a few hundred to several thousand meters. In general, shallow reservoirs have greater tendency to fracture, since they have low fracture gradient, ie fractures are formed even with relatively low hydrostatic columns of fluid. These low fracture gradient areas are particularly common in onshore areas, like the Rio Grande do Norte basin. During a well drilling, one of the most favorable phases for the occurrence of fractures is during cementing, since the cement slurry used can have greater densities than the maximum allowed by the rock structure. Furthermore, in areas which are already naturally fractured, the use of regular cement slurries causes fluid loss into the formation, which may give rise to failures cementations and formation damages. Commercially, there are alternatives to the development of lightweight cement slurries, but these fail either because of their enormous cost, or because the cement properties were not good enough for most general applications, being restricted to each transaction for which the cement paste was made, or both reasons. In this work a statistical design was made to determine the influence of three variables, defined as the calcium chloride concentration, vermiculite concentration and nanosilica concentration in the various properties of the cement. The use of vermiculite, a low density ore present in large amounts in northeastern Brazil, as extensor for cementing slurries, enabled the production of stable cements, with high water/cement ratio, excellent rheological properties and low densities, which were set at 12.5 lb / gal, despite the fact that lower densities could be achieved. It is also seen that the calcium chloride is very useful as gelling and thickening agent, and their use in combination with nanosilica has a great effect on gel strength of the cement. Hydrothermal Stability studies showed that the pastes were stable in these conditions, and mechanical resistance tests showed values of the order of up to 10 MPa / Em todo o mundo, ocorrem naturalmente dep?sitos de hidrocarbonetos, constitu?dos de petr?leo e g?s natural, contidos dentro de rochas denominadas "rochas reservat?rio", em geral arenitos ou carbonatos. Esses dep?sitos existem em variadas condi??es de press?o e profundidade, desde poucas centenas at? milhares de metros. Em geral, reservat?rios mais "rasos" t?m a tend?ncia a fraturar mais facilmente, pois possuem baixo gradiente de fratura, ou seja, as fraturas s?o formadas mesmo com colunas hidrost?ticas de fluido relativamente baixas. Essas zonas de baixo gradiente de fratura s?o particularmente mais comuns em zonas onshore, como aqui no Rio Grande do Norte. Um dos momentos mais prop?cios para a ocorr?ncia de fraturas ? durante a cimenta??o do po?o, ao se utilizar uma pasta cimentante de densidade superior ao m?ximo permitido pela estrutura rochosa. Al?m disso, em zonas j? naturalmente fraturadas, o uso de cimentos comuns causa perda de fluido para a forma??o, o que pode dar causa a cimenta??es falhas. Comercialmente, existem alternativas para o desenvolvimento de sistemas de pastas de cimento leves, mas esses falham ou em raz?o de seu elevad?ssimo custo, ou em fun??o das propriedades da pasta obtida n?o serem suficientemente boas para aplica??es mais gen?ricas, ficando restritas a cada opera??o para qual a pasta de cimento foi feita. Nesse trabalho foi realizado um planejamento estat?stico para determinar a influ?ncia de tr?s vari?veis, definidas como a concentra??o de cloreto de c?lcio, concentra??o de vermiculita e concentra??o de nano s?lica, nas v?rias propriedades do cimento. O uso da vermiculita, um min?rio de baixa densidade presente em grandes quantidades no nordeste brasileiro, como extensor para pastas cimentantes, permitiu a produ??o de pastas est?veis, com alta raz?o ?gua/cimento, propriedades reol?gicas excelentes e baixas densidades, que foram fixadas em 12,5 lb/Gal. Viu-se tamb?m que o cloreto de c?lcio ? um poderoso viscosificante e gelificante, e seu uso combinado com a nano s?lica possui grande efeito nas for?as g?is do cimento. Estudos de estabilidade hidrot?rmica mostraram que as pastas foram est?veis nessas condi??es, e os ensaios de resist?ncia mec?nica mostraram valores da ordem de at? 10 MPa