71 |
Struktura a únavové vlastnosti vybrané titanové slitiny / Structure and fatigue properties of selected titanium alloyPrudíková, Alena January 2014 (has links)
Main topic of the thesis was to evaluate fatigue properties of the titanium alloy Ti-A13-V2,5, labelled by ASTM as Grade 9. Most attention was focused on fatigue behaviour of the alloy in the range of high cycle fatigue. Fatigue testing was realised to detect the fatigue properties and consequently to generate the Wöhler curve and the Haigh diagram. In addition to this, tension and bending tests were performed. Metallographic and fractographic analyses of fatigue fracture form part of the overview about material properties, which was accomplished by use of REM. Experimental part of the thesis was backed by the literature research. The first half of it contains a short summary of basic information about the titanium and its alloys, so as some chapters about the history and properties of titanium, the way of its production, classification of titanium alloys and its thermic treatment. The fatigue is thoroughly scrutinised in the second half of the background research. Here can also be found the information about the fatigue process, its stages, the fatigue life and the most significant attributes of the fatigue fracture. The last chapters of the thesis are dedicated to the alloy Ti-A13-V2,5 - being examined in the experimental part - so as to its fatigue properties. The main benefit of this thesis is the completion of the missing information concerning the fatigue behaviour of the alloy, which is – according to the literature research - generally not available.
|
72 |
Nízkocyklové a vysokocyklové únavové vlastnosti ADI / Low Cycle and High Cycle Fatigue Properties of Austempered Ductile IronZapletal, Josef January 2011 (has links)
The thesis is focused on assessment of fatigue behaviour of austempered ductile iron with nodular graphite. Optimal period of transformation was determined based on the best combination of stress and strain characteristics established by tensile test. Cyclic response and low-cycle fatigue life were studied under both stress-control and longitudinal strain-control mode at room temperature. For both modes, shapes of cyclic hardening curves are dependent on stress amplitude. Cyclic deformation curves (CDC) were fitted by power regression function. Results were compared with CDC established by multiple step test in both modes with verification of the influence of cyclic creep (high stress levels, stress-control mode). Experimental data of S-N curves are in agreement with the Manson-Coffin and the Basquin law. Fatigue and cyclic parameters were compared. Fatigue life time in high-cycle fatigue region was determined. Experimental data were fitted by suitable regression functions. Regression parameters and fatigue limit were established by means of each regression function. Experimental data in low- and high-cycle fatigue regions were used to construct S-N curve and to determine relevant parameters. Discontinuity of experimental data was not observed. Low-cycle fatigue behaviour was predicted. Approximation of tolerance bands was realized in high-cycle and both high and low cycle fatigue regions.
|
73 |
ÚNAVOVÉ CHARAKTERISTIKY MODIFIKOVANÝCH HOŘČÍKOVÝCH SLITIN PO KOROZNÍ DEGRADACI / FATIGUE CHARACTERISTICS OF MODIFIED MAGNESIUM ALLOYS AFTER CORROSION DEGRADATIONNěmcová, Aneta January 2013 (has links)
This doctoral thesis deals with the determination of the influence of plasma electrolytic oxidation (PEO) on fatigue behaviour of extruded AZ61 magnesium alloy in air and in the 3.5% NaCl solution. The coatings were formed in the silicate-phosphate electrolyte under pulsed current conditions at a frequency of 50 Hz. The influence of current density on coating formation was examined under current densities of 70, 130 and 200 mA cm-2 for different durations up to a maximum of 1800 s. 8 g dm-3 of KF were added to the electrolyte to study the influence of fluoride ions in plasma electrolytic oxidation. It is shown that fluoride ions inhibit localised oxidation in the initial stage of the process, associated with the secondary particles based on Al–Mn. The presence of fluoride also modified the sparking characteristics, decreased the rate of coating growth and changed the morphologies of the coatings. The influence of fluoride on the coating hardness, and the corrosion resistance of the alloy during exposure to salt spray, was negligible. Based on previous optimised PEO conditions, coatings formed under a current density of 130 mA cm-2 for 300 s in the electrolyte containing KF were chosen for fatigue testing. The high-cycle fatigue tests were carried out on cylindrical samples under a force controlled sinusoidal tension-tension cycle with asymmetry parameter R=0. The experimental data were fitted with Kohout & Věchet function. The fatigue limit of uncoated alloy in air for 107 cycles was determined at 145.4 MPa and the combination of PEO coating with chloride ions caused a reduction of ~55 %. Attention was paid to the fatigue crack initiation in different conditions of cyclic loading. The fracture surfaces underwent detailed fractography analysis including secondary crack observation on the gauge length. The contribution of Al–Mn particles were confirmed on the uncoated alloy in air and the presence of chloride ions were observed as another influential contributor to local corrosion attack. The cyclic loading caused spalling of the outer layer, and the multiple initiation was observed on PEO coated alloy, caused by cracks in the coating and stress transferring to the alloy.
|
74 |
Strain Rate Sensitivity of Ti-6Al-4V and Inconel 718 and its Interaction with Fatigue Performance at Different SpeedsJuratovac, Joseph M. January 2020 (has links)
No description available.
|
75 |
AN EXPERIMENTAL INVESTIGATION OF MULTIPLE MODE EXCITATION OF AN INTEGRALLY BLADED DISKGarafolo, Nicholas Gordon January 2006 (has links)
No description available.
|
76 |
Fatigue Testing of Human Flexor Tendons Using a Customized 3D-Printed Clamping SystemScholze, Mario, Safavi, Sarah, Ramezani, Maziar, Ondruschka, Benjamin, Hammer, Niels 06 December 2023 (has links)
Improved surgical procedures and implant developments for ligament or tendon repair
require an in-depth understanding of tissue load-deformation and fatigue properties. Cyclic testing
will provide crucial information on the behavior of these materials under reoccurring loads and
on fatigue strength. Sparse data are available describing soft tissue behavior under cyclic loading.
To examine fatigue strength, a new technology was trialed deploying 3D-printing to facilitate and
standardize cyclic tests aiming to determine tendon fatigue behavior. Cadaveric flexor digitorum
tendons were harvested and mounted for tensile testing with no tapering being made, using 3Dprinted clamps and holder arms, while ensuring a consistent testing length. Loads ranging between
200 to 510 N were applied at a frequency of 4 Hz, and cycles to failure ranged between 8 and >260,000.
S–N curves (Woehler curves) were generated based on the peak stresses and cycles to failure. Power
regression yielded a combined coefficient of determination of stress and cycles to failure of R
2 = 0.65,
while the individual coefficients for tissues of single donors ranged between R
2 = 0.54 and R
2 = 0.88.
The here-presented results demonstrate that S–N curves of human tendons can be obtained using a
standardized setting deploying 3D-printing technology
|
77 |
Materialoptimering av Kranbom och Framtagning av Provstav : Ett undersökande arbete mot högcykelutmattning av kallformade ståldetaljerJansson, Jonathan January 2020 (has links)
Utmattning av stålmaterial är ett fenomen som varit känt i närmare 190 år men trots det är det fortfarande långt ifrån helt utforskat. Utmattningsegenskaper hos grundmaterial och svetsar är idag relativt utforskat, medan områden som utmattningsegenskaper hos kallformade stålprofiler fortfarande mer eller mindre är outforskat. Med utforskningen av utmattningsegenskaper hos kallformade stålprofiler som huvudsyfte delades examensarbetet upp i två delar. En överliggande kranbomsoptimering med huvudmålet att sänka vikten så mycket som möjligt med hjälp av materialbyte till ett mer höghållfast stål och optimal användning av material med avseende på utmattning. Den andra delen av examensarbetet är en framtagning av en provkropp med huvudmålet att kunna testa utmattningsegenskaper för kallformade stålprofiler samt att ge dimensionerande värden till kranbomsoptimeringen. Provstavsframtagningen resulterade i tre versioner av provkroppar som i teorin ska ge utmattningsegenskaper i longitudinell riktning för kallformade stålprofiler. Eftersom provstavarna inte kunde prövas på grund av tidsbrist baserades kranbomsoptimeringen på teoretiska värden. Resultatet av kranbomsoptimeringen var att vikten kunde sänkas från 1027 kg till 435 kg utan att påverka andra beaktade kranegenskaper. / Even though fatigue in steel structures is a phenomenon that was discovered almost 190 years ago it is still far from fully explored. The fatigue properties of base materials and welded materials are currently relatively well known, but the fatigue properties of cold-formed steel profiles are still more or less unknown. With the investigation of fatigue properties of cold-formed steel profiles as the main purpose, this master thesis was divided into two parts. An overhead optimization of a crane with the main goal of reducing weight as much as possible with the help of upgrading materials to higher strength steels and using the materials in an optimal way with respect to fatigue. The second part of the master thesis is the development of a test specimen with the main goal of testing the fatigue properties of cold-formed steel profiles and to provide dimensioning values for the optimization of the crane. The development of test specimen resulted in three versions of specimens which in theory will provide fatigue properties in the longitudinal direction for cold-formed steel profiles. Since the test specimens could not be tested because of shortage of time, the optimization of the crane had to be based on theoretical values. The results of the optimization were that the weight could be lowered from 1027 kg to 435 kg without affecting any other consideration characteristics of the crane.
|
78 |
[en] MODIFICATIONS IN THE THEORY OF EQUIVALENT DEFECTS FOR FATIGUE LIFE ASSESSMENT IN ULTRALONG REGIME OF A HIGH STRENGTH STEEL / [pt] MODIFICAÇÕES NA TEORIA DOS DEFEITOS EQUIVALENTES PARA AVALIAR A VIDA-FADIGA EM REGIME ULTRALONGO DE UM AÇO DE ALTA RESISTÊNCIATHIAGO ABREU PEREIRA PEIXOTO 28 November 2023 (has links)
[pt] O presente trabalho se baseia na teoria dos defeitos equivalentes, também
conhecida como teoria de Murakami, que permite a predição da vida-fadiga de
materiais estruturais adotando o parâmetro (raiz quadrada de area), responsável por uma
equivalência quantitativa entre heterogeneidades microestruturais (inclusões
metalúrgicas) existentes na região de análise do material e descontinuidades
mecânicas (furos) usinados nos corpos de prova.
Neste contexto, a tese propõe novas equações, a partir da teoria de Murakami,
para prever falhas por fadiga em carregamentos ultralongos (fadiga de altíssimo
ciclo, VHCF) do aço DIN42CrMo4, de larga aplicação na fabricação de eixos
virabrequins para unidades geradoras de usinas termoelétricas.
Corpos de prova do aço DIN42CrMo4 foram usinados com furos de
diâmetros variando entre 0,18 mm e 0,70 mm e ensaiados num regime de fadiga de
altíssimo ciclo, variando o valor da amplitude de tensão do ensaio, para assim
determinar em quais condições o material falha e obter a curva experimental S-N
do aço DIN42CrMo4 na presença de diferentes tamanhos de defeitos (furos).
Os resultados experimentais permitiram o desenvolvimento de equações em
função do parâmetro e curvas de Wohler do material, em conformidade com
diferentes descontinuidades mecânicas nos corpos de prova e resistências à fadiga
do material. Consequentemente, se estabeleceu uma metodologia que permite uma
correlação entre inclusões metalúrgicas, tensão aplicada e vida superlonga em
fadiga de eixos virabrequins em serviço em usinas termoelétricas. / [en] The present work is based on the theory of equivalent defects, also known as
Murakami s theory, which allows the prediction of the fatigue life of structural
materials by adopting the parameter (square root of area), responsible for a quantitative
equivalence between microstructural heterogeneities (metallurgical inclusions)
existing in the region analysis of the material and mechanical discontinuities (holes)
machined in the specimens.
In this context, the thesis proposes new equations, based on Murakami s
theory, to predict fatigue failures in ultralong loads (very high cycle fatigue, VHCF)
of DIN42CrMo4 steel, widely used in the manufacture of crankshafts for generating
units of thermoelectric power plants.
DIN42CrMo4 steel specimens were machined with holes with diameters
varying between 018 mm and 0.70 mm and tested in a very high cycle fatigue
regime, varying the value of the test stress amplitude, to determine under what
conditions the material failure and obtain the experimental S-N curve of
DIN42CrMo4 steel in the presence of different sizes of defects (holes).
The experimental results allowed the development of equations as a function
of the parameter and Wohler curves of the material, in accordance with different
mechanical discontinuities in the test specimens and resistance to fatigue of the
material. Consequently, a methodology was established that allows a correlation
between metallurgical inclusions, applied stress and super-long fatigue life of
crankshafts in service in thermoelectric power plants.
|
79 |
[en] ELLIPTICAL CURVE METHOD FOR FATIGUE LIFE PREDICTION OF STRUCTURAL STEELS UNDER MULTIAXIAL LOADINGS / [pt] MÉTODO DA CURVA ELÍPTICA PARA PREVISÃO DA VIDA EM FADIGA DE AÇOS ESTRUTURAIS SOB CARREGAMENTOS MULTIAXIAISTIAGO LIMA D ALBUQUERQUE E CASTRO 14 March 2024 (has links)
[pt] Uma relação direta onde a vida em fadiga Número de ciclos por falha pode ser descrita como função das amplitudes macroscópicas de tensão normal e cisalhante, Amplitude de tensão normal macroscópica e Amplitude macroscópica da tensão de cisalhamento, é obtida. Utilizando o critério de Carpinteri e Spagnoli (CeS) como uma ferramenta de inspeção, foram obtidas curvas de nível elípticas sobre um domínio Amplitude de tensão normal macroscópica x Amplitude macroscópica da tensão de cisalhamento. A expressão das curvas de nível obtidas foi generalizada, proporcionando uma ferramenta capaz de prever o número de ciclos para falha associado a qualquer combinação (Amplitude de tensão normal macroscópica, Amplitude macroscópica da tensão de cisalhamento). As previsões obtidas através do método da curva elíptica foram comparadas às observações experimentais, bem como a previsões obtidas a partir de versões adaptadas de modelos consagrados na literatura, a saber: Findley (F), Matake (M), McDiarmid (McD), Susmel e Lazzarin (SeL), Carpinteri e Spagnoli (CeS) e Papadopoulos (P). O modelo proposto forneceu previsões em boa concordância com as observações experimentais, e sua capacidade de avaliar o comportamento em fadiga se revelou o melhor dentro todos os critérios considerados. Por fim, uma leve tendência conservadora do modelo foi atenuada através da introdução de um parâmetro de ajuste, melhorando ainda mais sua capacidade de avaliação de comportamento em fadiga. / [en] A direct relation where fatigue life Number of cycles to failure can be determined as function of
macroscopic normal and shear stress amplitudes Macroscopic normal stress amplitude and Macroscopic shear stress amplitude is established. Using the
Carpinteri and Spagnoli (CandS) criterion as a survey tool, elliptical level curves in the
Macroscopic normal stress amplitude x Macroscopic shear stress amplitude domain were revealed and further generalised, providing means to
determine the number of cycles to failure for any given (Macroscopic normal stress amplitude, Macroscopic shear stress amplitude
) combination.
Predictions obtained through the elliptical curve method (E) were compared to
experimental observations, as well as to predictions obtained from adapted versions
of popular fatigue criteria, namely Findley (F), Matake (M), McDiarmid (McD),
Susmel and Lazzarin (SandL), Carpinteri and Spagnoli (CandS) and Papadopoulos (P).
The proposed model delivered predictions in fair agreement with experimental
observations and its predictive capability was seen to be the best among all the
considered criteria. Finally, a slight bias towards conservativeness was attenuated
with the introduction of an adjusting parameter, further improving the predictive
capability of the model.
|
80 |
Berechnungsansatz für Strukturbauteile aus Holzfurnierlagenverbundwerkstoff – WVC / Calculation approach of structures made from Wood Veneer Composite – WVCEichhorn, Sven 15 February 2013 (has links) (PDF)
Es wird ein einfacher Berechnungsansatz für ein Baukastensystem aus Kastenprofilen verschiedener Querschnittsabmessungen erarbeitet. Diese Profile bestehen aus WVC (Wood Veneer Composites, Holzfurnierlagenverbundwerkstoffen). Der Ansatz bildet den statischen Lastfall und das Ermüdungsverhalten unter schwellende Dreipunktbiegung ab. Am Beispiel eines ausgewählten Strukturbauteils aus handelsüblichen Birkensperrholz wird der Berechnungsansatz konkretisiert und durch Versuche evaluiert. Aufbauend auf dem Kraft-Verformungsverhalten der analysierten Einzelbauteile und der kapillarporösen Struktur des Holzes wird bei dem Berechnungsansatz auf eine Analyse der Spannungen verzichtet. Stattdessen wird als Berechnungskriterium die kritische Normaldehnung in der Randfaser der Strukturbauteile genutzt. Weiterhin wird eine Methode vorgestellt um mittels niederzyklischen Ermüdungsversuchs (LCF, ca. 1e+03 Lastwechsel) den „Knickpunkt“ der Zeitfestigkeitslinie eines einstufigen Ermüdungsversuchs bei hohen Lastspielzahlen (HCF, 1e+06 bis 1e+07 Lastwechsel) für diese Strukturbauteile zu bestimmen. / It was developed a simple approach for the calculation of a modular construction system for box sections (profile structures) of different cross-sectional dimensions. These profile structures consists of WVC (Wood Veneer Composites). The approach maps the static load case and the fatigue behavior under pulsating three-point bending. By using a structural component made from commercial birch plywood, the calculation approach is specified and verified. Based on the force-deformation behavior of the analyzed single components in connection with the capillary-porous structure of the wood, the calculation approach dispense on an analysis of the tensions. Instead, a criterion, which calculates the critical normal strain in the outer fibers of the structural components, is used. Furthermore, a method of a low-cycle fatigue test (LCF, abbr. 1e+03 cycles) is presented. This method detects the “knee point" of the fatigue limit line for the profiles. That point is usually determined by the use of a high-cycle fatigue tests (HCF, 1e+06 until 1e+07 cycles).
|