Thesis (Ph. D.)--Ohio State University, 2006. / Title from first page of PDF file. Includes bibliographical references (p. 220-225).

Many phenomena determining the microstructure of a tool steel and consequently the properties of the material, are governed by multicomponent diffusion. The diffusion driven reactions that take place during, for example, tempering of a hot-work tool steel or when the microstructure develops during hot isostatic pressing of cold-work tool steel, are dependent on the types and amounts of alloying elements. In order for computational methods to be usable, these alloying effects need to be understood and incorporated in the models. In this work the influence of some typical tool steel alloying elements on the coarsening behavior of precipitates is investigated. Experimental coarsening studies are performed and the impact of the diffusion mobility descriptions and the thermodynamic descriptions are investigated by means of DICTRA coarsening calculations. The kinetic descriptions for diffusion in the body centered-cubic phase in the case of the chromium-iron-vanadium system and the chromium-iron-molybdenum system are improved by assessments of diffusion mobility parameters, and are shown to have a large impact on the calculated coarsening rate for vanadium-rich and molybdenum-rich precipitates. The effect of cobalt is examined by a coarsening experiment for vanandiumrich carbides and by a diffusion couple experiment for the investigation of the vanadium interdiffusion. The presence of cobalt is experimentally shown to have retarding effect on the coarsening rate of the carbides, but not on the vanadium diffusion. The coarsening rate of nitrogen-rich precipitates is compared to the coarsening rate of carbon-rich precipitates, and a lower coarsening rate for nitrides compared to carbides can be confirmed. Correlation between coarsening calculations and experiments is obtained suggesting that the thermodynamic description of the two systems is the underlaying reason for the different coarsening rates. Further, calculations utilizing the DICTRA software are combined with experimental investigations in order to study the possibility to apply computational methods for compound material development and explore application areas for high nitrogen alloyed tool steels produced by powder metallurgy. / <p>QC 20121011</p>

In recent times, application of aluminum alloys is favored in the transportation sectors such as the aerospace and automobile industries where reduced fuel consumption and greenhouse gas emission are major priorities. In these applications, these alloys can be exposed to dynamic shock loading conditions as in the case of car crash and birds’ collision during aircraft’s take-off or landing. This study therefore focused on the deformation and damage mechanisms in AA 2017, AA 2024 and AA 2624 aluminum alloys under both quasi-static and dynamic impact loading conditions. Cylindrical specimens of the selected aluminum alloys were investigated under both quasi-static loading at 3.2 x10-3 s-1 using an Instron R5500 mechanical testing machine and dynamic impact loading using the split Hopkinson pressure bar at strain rates ranging between 2000 and 8000 s-1. The effects of strain rate and temper condition on the microstructural evolution in the alloys during mechanical loading were studied. The electron backscatter diffraction (EBSD) technique was used to investigate the texture of the naturally-aged AA 2017 and AA 2624 alloys before and after dynamic shock loading. The contributions of the major alloying elements such as copper, magnesium and silicon to the microstructural evolution and deformation behavior of the alloys under the dynamic shock loading condition were also studied using the energy dispersive spectroscopy (EDS) technique. Results showed that the morphology and atomic distribution of particles in the investigated alloys are functions of the temper condition. The hardness of all the three alloys was higher in the age-hardened conditions than the annealed ones. Although deformation of the alloy under quasi-static compressive loading was dominated by strain hardening, flow softening leading to strain localization and formation of shear bands occurred once certain critical strain values were reached. Under both quasi-static and dynamic loading, the alloys with low Cu:Mg ratio (AA 2024 and AA 2624) showed higher mechanical strength in age-hardened condition than that with high Cu:Mg ratio (AA 2017). All the alloys in the annealed condition exhibited an enhanced plasticity and formability. Intense strain localization leading to formation of adiabatic shear bands (ASBs) was the principal contributor to failure in the alloys under dynamic impact loading. Both deformed and transformed bands were observed, with cracking occurring mainly along the transformed shear bands. The tendency for formation of adiabatic shear bands is observed to be a function of the alloy composition, temper condition, strain, strain rate and strain hardening rate. In the natural aging condition, AA 2024 showed the highest susceptibility to formation of ASBs followed by AA 2624 and AA 2017 in that order. On the other hand, AA 2024 has the least susceptibility in the artificially-aged condition. Occurrence of bifurcation of transformed bands in dynamic impacted specimens is dependent on temper condition, strain and strain rate. The mechanism of fracture of the precipitation hardened samples is typical of ductile fracture occurring sequentially by nucleation, growth, and coalescence of micro-voids processes within transformed band. Elongated grains were observed to arrest propagating shear band depending on the angle the band makes with elongated grains. The higher the angle of inclination of a shear band to the grain on its path, the higher the tendency of the grain to stop its propagation. Texture analysis of the impacted specimens of AA 2017-T451 and AA 2624-T351 shows that the former has a higher tendency for the evolution of ultra-fine DRX grains within the transformed shear band. High strain rate led to the development of CD//<111> orientations at the expense of CD//<110> orientations. Schmid factor calculations performed on few different orientations in the starting microstructure shows that CD//<110> is less susceptible to slip deformation and consequently underwent rotation to CD//<111>.

L'amélioration des propriétés mécaniques dans les alliages du système Fer-Silicium-Titane grâce à l'introduction d'une précipitation nanométrique a été démontrée dans la littérature. La haute valeur de limite d'élasticité qui peut être atteinte dans ces aciers en fait de bons candidats pour des applications dans l'élaboration de structures automobiles. Dans ce contexte, cette étude a pour objectif de caractériser et comprendre la séquence et la cinétique de précipitation dans ces alliages, ainsi que les relations entre microstructure de précipitation et propriétés mécaniques, dans une démarche de conception d'alliages optimisée. La démarche utilisée a tout d'abord consisté en une caractérisation multi-échelle de la précipitation par diffusion des neutrons aux petits angles, microscopie électronique en transmission et sonde atomique tomographique, qui a permis d'aboutir à une description précise de la structure, composition, taille et fraction volumique des précipités, qui ont ensuite été reproduites par modélisation. Dans un deuxième temps, les tests mécaniques réalisés à température ambiante ont révélé un fort potentiel durcissant, qui dépend du temps et de la température de vieillissement. Des modèles à base physique pour la limite d'élasticité et le taux d'écrouissage (tenant compte des contributions isotropes et cinématiques) ont été appliqués pour décrire les courbes de traction mesurées. Ceux-ci ont permis d'aboutir à une bonne compréhension des relations entre microstructures et propriétés dans le système Fe-Si-Ti. / The Iron-Silicon-Titanium alloy system is known to have an interesting hardening potential thanks to its ability to produce a fine and dense precipitation microstructure. The high yield stress obtained for steels from this system, makes them potential candidates for automotive applications. The aim of this study was to improve the understanding of the precipitation sequence and kinetics, as well as to analyze the influence of the precipitates on the mechanical properties (yield strength and strain hardening) in the objective of alloy design and process optimization. The approach used is classical in physical metallurgy. It consists namely, of the characterization of precipitation followed by the study of the mechanical properties. The characterization of precipitation has been carried out using the combination of Small-Angle Neutron Scattering, Transmission Electron Microscopy and Atom Probe Tomography. This provides an accurate description of the precipitates in terms of crystal structure, composition, size and volume fraction. These properties have been subsequently reproduced with a precipitation model. The mechanical tests performed on the alloy at room temperature, have revealed a high hardening potential that depends on ageing time and temperature. Physically-based models for yield strength and strain hardening rate (including the effect of isotropic and kinematic hardening) have been applied to interpret the measured stress-strain curves, and allow to reach a comprehensive understanding of the microstructure/properties relationship in the Fe-Si-Ti alloy system.

M.Sc. / Please refer to full text to view abstract

Hot-work tool steels make up an important group of steels that are able to perform with good strength and toughness properties at elevated temperatures and stresses. They are able to gain this behavior through their alloy composition and heat treatment, which relies on the precipitation of alloy carbides to counter the loss in strength as the tempered material becomes more ductile. As demand grows for materials that are suitable for even harsher applications and that show improved mechanical qualities, the steel industry must continuously investigate the development of new steel grades. Within this context, the present work focuses on examining the mechanical properties and microstructure of two hot-work tool steels, of which one is a representative steel grade (Steel A) and the second a higher-alloyed variant (Steel B), at different tempering conditions. To complement the experimental work, precipitation simulations are used to monitor the progression of secondary carbide precipitation and to examine the predicted microstructural changes through varying the alloy composition. The study finds that Steel B does not actually have improved properties with respect to Steel A and suggests that the precipitation behavior of both steels is virtually identical. Despite this, the simulation work reveals that this behavior can change dramatically to favor more positive hardness contributions by increasing the alloy content of V. In short, with the project being part of an ongoing investigation, there remain several areas of analysis that need to be completed before offering a complete picture that can ultimately play a part in the development of a new hot-work tool steel grade.

No description available.

Among the commercial aluminum alloys, aluminum 319 (Al-7wt%Si-4wt%Cu) type alloys are popularly used in automobile engine parts. These alloys have good casting characteristics and excellent mechanical properties resulting from a suitable heat treatment. To get a high strength in the 319 type alloys, grain refining, reducing the porosity, solid solution hardening, and precipitation hardening are preferred. All experimental variables such as solidification condition, composition, and heat treatment are influence on the precipitation behavior; however, precipitation hardening is the most significant because excess alloying elements from supersaturated solid solution form fine particles which act as obstacles to dislocation movement. The challenges of the 319 type alloys arise due to small size of precipitate and complex aging response caused by multi components. It is important to determine the chemical composition, crystal structure, and orientation relationship as well as precipitate morphology in order to understand the precipitation behavior and strengthening mechanism. In this study, the mechanical properties and microstructure were investigated using transmission electron microscopy and three dimensional atom probe tomography. The Mn and Mg effects on the microstructure and mechanical properties are discussed with crystallographic study on the iron intermetallic phases. The microstructural evolution and nucleation study on the precipitates in the low-Si 319 type aluminum alloys are also presented with sample preparation and analysis condition of TEM and 3DAP tomography.

Os aços inoxidáveis endurecidos por precipitação vêm sendo largamente empregados na indústria aeronáutica, por combinar resistência mecânica, tenacidade à fratura e resistência à corrosão. E deste modo, são materiais que possibilitam a substituição dos aços carbonos utilizados atualmente, que necessitam de tratamento superficial adicional, como o cádmio, para melhorar a resistência à corrosão. A utilização desses revestimentos traz desvantagens como o custo, a fabricação, a susceptibilidade à fragilização por hidrogênio além dos aspectos ambientais. Neste contexto, o aço endurecido por precipitação UNS S46500, designado como Custom 465® foi avaliado considerando o efeito da temperatura de envelhecimento sobre as propriedades mecânicas e a resistência à corrosão por pite. Amostras tratadas nas condições solubilizada e envelhecida a 510ºC (H950) e 538ºC (H1000) foram submetidas ao ensaio de tração, caracterização microestrutural e ensaios de polarização potenciodinâmica (PP) para determinar a resistência à corrosão por pite. Os exames microestruturais foram realizados com auxílio de microscopia óptica (MO), microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS) e difração de raios X. Também foram realizadas análises utilizando o software Thermo-Calc. A resistência à corrosão por pite foi avaliada em solução 0,6M NaCl com adições crescentes de Na2SO4. Os resultados obtidos nos ensaios de PP nas duas condições de tratamento térmico foram comparados entre si e com resultados disponíveis na literatura (CALDERÓN-HERNANDEZ, 2012) para o aço inoxidável UNS S30403 (304L). Os exames e análises da microestrutura revelaram que o aço Custom 465® envelhecido apresenta uma matriz martensítica, precipitados de fase chi, austenita e precipitados Ni3Ti. O tratamento H950 apresentou maior resistência mecânica e menor alongamento do que o tratamento H1000. Tal comportamento foi devido à produção de maior porcentagem de fase chi e menor porcentagem de austenita nesse tratamento de envelhecimento. Os diferentes tratamentos térmicos, condição solubilizada, H950 e H1000 apresentaram praticamente a mesma resistência à corrosão por pite. Por outro lado, o aço Custom 465® apresentou ótima resposta à inibição da nucleação de pite com adições crescentes de sulfato em meio de 0,6M NaCl, sendo que a condição H1000 se sobressai sobre a H950 nessa questão. Além disso, através da adição de sulfato foi 7 possível obter maior resistência a corrosão por pite do aço Custom 465® comparativamente ao aço 304L. Tal comportamento foi discutido em termos da afinidade química entre níquel, cloreto e sulfato, levando a maior resistência à corrosão por pite quando o aço contém maior teor de níquel (que é o caso do aço Custom 465®). Este trabalho indicou que o critério na escolha do tratamento de envelhecimento do aço Custom 465® deve ser o das propriedades mecânicas almejadas, uma vez que a resistência à corrosão por pite mostrou-se praticamente independente do tratamento térmico. / The precipitation hardened stainless steels have been widely used in the aircraft industry to combine mechanical strength, fracture toughness and corrosion resistance. And therefore, are materials that enable replacement of the carbon steels used today, which require additional surface treatment, such as cadmium plating, to improve the corrosion resistance. The use of such coatings brings disadvantages such as cost, manufacturing, susceptibility to hydrogen embrittlement beyond environmental aspects. In this context, the precipitation hardened steel UNS S46500, known as Custom 465® were evaluated for the effect of aging temperature on the mechanical properties and the resistance to pitting corrosion .Treated samples in solubilized and aged condition at 510°C (H950) and 538ºC (H1000) were subjected to tensile strength test, microstructural characterization and potentiodynamic polarization (PP) tests to determine the pitting corrosion resistance. The microstructural studies were performed with the aid of optical microscopy (OM), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction. Analyzes were also performed using the Thermo -Calc software. The resistance to pitting corrosion was evaluated at 0.6M NaCl solution with increasing additions of Na2SO4. The results obtained from tests of PP in both heat treatment conditions were compared with each other and with results available in the literature (CALDERÓN HERNANDEZ, 2012) to stainless steel UNS S30403 (304L). The analysis of the microstructure revealed that the steel aged Custom 465 ® presents a martensitic matrix, chi precipitates, Ni3Ti precipitates and austenite phase. The H950 age treatment had higher mechanical strength and lower elongation than the treatment H1000. Such behavior was due to the production of higher percentage of chi and a lower percentage of austenite phase in aging treatment. The different heat treatments, solubilized condition, H950 and H1000 showed almost the same pitting corrosion resistance. On the other hand, the Custom 465® showed good response to pitting inhibition with increasing nucleating additions of sulfate in 0.6M NaCl, with enhanced result for H1000 condition. Furthermore, by adding sulfate was possible to obtain greater pitting corrosion resistance of Custom 465® compared to the 304L steel. This behavior has been discussed in terms of the chemical affinity between nickel, chloride and sulphate, leading to higher pitting corrosion resistance when the steel contains a higher nickel 9 content (which is the case of steel Custom 465®). This study indicates that the criterion in selecting the aging heat treatment of Custom 465® steel must be the desired mechanical properties, since the pitting corrosion resistance was found to be substantially independent of heat treatment.

<p>Commercial alloys are continuously developed to improve their performance. Therefore it is important to develop new optimisation software, which could be used in development of new materials or in materials selection. In this study the mechanical properties which are important in materials selection in mechanical design are investigated. Two types of materials are analysed, aluminium alloys and stainless steels but focus will be on the aluminium alloys.</p><p>Thermodynamic analysis has been used to evaluate the effect of the microstructure. Solid solution hardening has been successfully modelled for both aluminium alloys and stainless steels and follows the theories by Labusch and Nabarro. The precipitation hardening is most dominant for the hardenable aluminium alloys, but the non-hardenable alloys also increase their strength from precipitation hardening. The non-hardenable alloys are divided into tempers, which differ in the amount of strain hardening. This has also been modelled successfully.</p><p>Combining these fundamental results with multiple regression, models for mechanical properties have been created. Separate models are developed for wrought aluminium alloys and stainless steels. For the aluminium alloys this includes the solid solution hardening and the precipitation hardening. For the stainless steels the thickness, nitrogen content and ferrite content are included together with the solid solution hardening.</p>