Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-06-08T20:19:50Z No. of bitstreams: 1 geraldohenriquessilva.pdf: 20536600 bytes, checksum: 9b626b89b88c550fa0fff1dcca169621 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2017-06-26T20:29:26Z (GMT) No. of bitstreams: 1 geraldohenriquessilva.pdf: 20536600 bytes, checksum: 9b626b89b88c550fa0fff1dcca169621 (MD5) / Made available in DSpace on 2017-06-26T20:29:26Z (GMT). No. of bitstreams: 1 geraldohenriquessilva.pdf: 20536600 bytes, checksum: 9b626b89b88c550fa0fff1dcca169621 (MD5) Previous issue date: 2014-02-28 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / Neste trabalho estudou-se vidros co-dopados por meio de técnicas espectroscópicas de absorção óptica, espectroscopia Raman, fotoluminescência, fotoluminescência resolvida no tempo, lente térmica e capacidade térmica volumétrica. A classe de vidro estudada é a de vidros fosfatos denominados PZABP (P205 – ZnO – Al203 – BaO – PbO), os quais foram dopados com íons de európio (Eu3+), em diferentes concentrações, e telúrio (Te), visando o surgimento de nanopartículas semicondutoras de Telureto de Zinco (ZnTe). O objetivo desse trabalho é investigar a emissão do Eu3+ e sua interação com as nanopartículas semicondutoras no sentido de melhorar as propriedades ópticas e/ou térmicas do sistema vítreo co-dopado. Com a técnica de absorção óptica foi possível observar a alta transparência desse sistema, com uma janela óptica cobrindo a região desde o ultravioleta (em torno de 300 nm) até ao infravermelho médio (em torno de 3000 nm). Observou-se uma banda de absorbância larga centrada em torno de 540 nm quando o sistema vítreo PZABP foi dopado com Te. Essa banda foi atribuída a nanopartículas de ZnTe com comportamento de material na forma bulk. Com a técnica de fotoluminescência observou-se uma emissão avermelhada intensa atribuída aos íons de Eu3+, sendo a transição 5D0 —> 7F2 (611 nm) a mais intensa. Os parâmetros de Judd-Ofelt foram obtidos a partir dos espectros de emissão e absorção. De posse desses parâmetros, encontrou-se o tempo de vida radiativo do estado 5D0 que, juntamente com o tempo de vida experimental, permitiu a determinação da eficiência quântica. Observou-se que a mesma não sofreu uma alteração significativa em função da concentração dos íons de Eu3+ e com a presença do ZnTe. Com a técnica de lente térmica, na presença de nanopartículas de ZnTe, observou-se que a difusividade térmica (D) permaneceu praticamente constante com o aumento da concentração de Eu3+. / IIn this work we have studied co-doped glasses by means of spectroscopic techniques such as optical absorption, Raman spectroscopy, photoluminescence, time-resolved photoluminescence, thermal lens and volumetric heat capacity. The class of studied glasses was of phosphate glasses called PZABP (P2O5 – ZnO – Al203 – BaO – PbO) doped with different concentrations of europium ions (Eu3+), and tellurium (Te), to nucleation of semiconductor nanoparticles of zinc telluride (ZnTe). The goal of this work is to investigate the emission of the Eu3+ and its interaction with the semiconductor nanoparticles aiming to improve the thermo/optical properties of the glass system. With the optical absorption technique was possible to observe the high transparency of the system, which covers an optical window going from the ultraviolet region (about 300 nm) to mid-infrared (about 3000 nm). Also, was observed a large absorbance band centered around 540 nm when the glass system PZABP was doped with Te. This band was attributed to bulk-like ZnTe nanoparticles. Through the photoluminescence technique was possible to observe an intense reddened emission attributed to Eu 3+ ions, being the 5D0 —>7 F2 transition ( 611 nm) the most intense. The Judd-Ofelt parameters were obtained from the absorption and emission spectra. From these parameters, the radiative lifetime of the state 5D0 was found which together with the experimentally measured lifetime allowed the determination of the quantum efficiency. The latter does not present a significant change when the concentration of Eu3+ ions increases and with the presence of ZnTe. With the thermal lens technique, in the presence of ZnTe nanoparticles, was observed that the thermal diffusivity (D) remained almost constant with the increasing of concentration of Eu3+.

Submitted by Renata Lopes (renatasil82@gmail.com) on 2017-06-27T20:21:11Z No. of bitstreams: 1 marcelinocordeironeto.pdf: 92399516 bytes, checksum: 0d59ef50bab71144a1450179047a4f30 (MD5) / Approved for entry into archive by Adriana Oliveira (adriana.oliveira@ufjf.edu.br) on 2017-08-07T21:07:35Z (GMT) No. of bitstreams: 1 marcelinocordeironeto.pdf: 92399516 bytes, checksum: 0d59ef50bab71144a1450179047a4f30 (MD5) / Made available in DSpace on 2017-08-07T21:07:35Z (GMT). No. of bitstreams: 1 marcelinocordeironeto.pdf: 92399516 bytes, checksum: 0d59ef50bab71144a1450179047a4f30 (MD5) Previous issue date: 2014-05-06 / CAPES - Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / O objetivo desta tese é analisar se as propriedades ópticas apresentadas neste trabalho qualificam o sistema vítreo PZABP, com composição nominal 60P2O5.15ZnO.5Al2O3.10BaO.10PbO (% mol), dopado com íons terras-raras trivalentes, itérbio (Yb3+) e európio (Eu3+) e, também, com nanopartículas semicondutoras de telureto de zinco (ZnTe) como potencialmente útil para construção de dispositivos de emissão de luz na região de 920 nm a 1060 nm. A teoria de Judd-Ofelt é usada nos cálculos dos parâmetros de intensidade Ωλ(λ = 2,4,6). Técnicas de microscopia de força atômica (AFM), absorção óptica (AO), fotoluminescência (FL) e fotoluminescência resolvida no tempo (FLRT) caracterizam o sistema vítreo. A finalidade do ZnTe é aumentar a seção de choque de absorção do sistema vítreo PZABP e transferir energia para os íonsEu3+ e/ouYb3+. A formação de dois tipos de nanopartículas semicondutoras de telureto de zinco ZnTe-propriedades de bulk e pontos quânticos – foram identificados. FL e FLRT sugerem transferência de energia dos íons de Eu3+ e/ou ZnTe para os íons deYb3+. / The aim of this thesis is to analyze if the optical properties presented in this work qualify the glass system PZABP, with nominal composition 60P2O5.15ZnO.5Al2O3.10BaO.10PbO(% mol), doped with trivalent rare earth ions, ytterbium (Yb3+) and europium (Eu3+) as well as zinc telluride (ZnTe) as potentially useful for light emission devices in the infrared region from 920 nm to 1060 nm. The Judd-Ofelt theory is used to calculate the intensity parameters Ωλ(λ = 2,4,6). Atomic force microscopy (AFM), optical absorption (OA), photoluminescence (PL) and time-resolved photoluminescence (TRPL) techniques characterized the vitreous system. The formation of two kinds of ZnTe semiconductor nanoparticles - bulk-like and quantum dots –were identified. PL and TRPL suggest the energy transfer from Eu3+ ions and/orZnTetoYb3+ ions.

Vidros teluritos são considerados fortes candidatos para aplicações em lasers e óptica não linear devido a importantes características, como o elevado índice de refração, baixa energia de fônons, baixa temperatura de transição vítrea e sua fácil preparação. Neste trabalho foram produzidas amostras dos sistemas vítreos TeO2- ZnO-Na2O, TeO2-Nb2O5-Na2O e Te2O-Na2O incluindo ou não dopagens de AgNO3 para estudos estruturais e ópticos. As propriedades estruturais e os mecanismos de recombinação destes vidros foram estudados por meio das técnicas de ressonância paramagnética eletrônica, termoluminescência e correntes de despolarização termicamente estimuladas. Já as propriedades ópticas como o coeficiente de absorção linear, índice de refração linear e não linear foram estudadas por meio das técnicas de absorção óptica, acoplamento de prismas e varredura Z. Foram ainda desenvolvidos estudos da precipitação de nanopartículas de prata para o sistema TeO2-ZnO-Na2O com dopagens de AgNO3 com diferentes temperaturas de tratamento térmico. A caracterização das nanopartículas metálicas foi realizada por meio da técnica de absorção óptica auxiliada por microscopia eletrônica de transmissão e espectrometria de energia dispersiva. Foram observadas por ressonância paramagnética eletrônica quatro respostas paramagnéticas dos vidros irradiados com raio , sendo uma de natureza desconhecida e as outras três identificadas como g¹, g² e g³ atribuídas respectivamente ao centro de buraco do telúrio e do oxigênio, centro de buraco do oxigênio terminal e centro de elétron do telúrio. Foi proposto ainda um modelo para explicar os mecanismos de formação destes centros. A partir dos resultados de termoluminescência observou-se que os processos de recombinação destes centros de defeitos são não radioativos. Neste projeto foram estudados pela primeira vez na literatura os fenômenos de polarização e despolarização em vidros teluritos, com e sem irradiação gama, por meio da técnica de correntes de despolarização termicamente estimuladas. Quanto às propriedades ópticas, foi investigada a influência da adição de prata dos sistemas vítreos TeO2-ZnO-Na2O e TeO2-Nb2O5-Na2O em relação à energia do gap, a cauda de Urbach, índice de refração linear e não linear.Nos resultados de varredura Z do sistema vítreo TeO2-Nb2O5-Na2O foi observado o aumento da assimetria na curva com aumento da adição de AgNO3 Este fenômeno foi explicado por meio de uma adaptação do modelo de Sumi para processos não radiativos, responsáveis pelo aumento do caráter térmico do índice de refração não linear. Por fim um modelo foi criado para explicar a precipitação de nanopartículas de prata na matriz vítrea TeO2-ZnO-Na2O mediante tratamento térmico. / Tellurite glasses are considered powerful candidates for applications in lasers and nonlinear optics due to their important properties such as high refractive index, low phonon energy, relatively low glass transition temperature and easy glass production at room atmosphere. In this work glass samples of the systems ZnO-Na2O, TeO2-Nb2O5-Na2O and Te2O-Na2O were produced, including or not the AgNO3 doping for the structural and optical study purposes. The structural properties and the recombination mechanisms of these glasses were studied by means of the techniques of electron paramagnetic resonance, thermoluminescence and thermally stimulated depolarization currents. The optical properties such as the optical linear absorption coefficient, linear and nonlinear refractive index were studied by means of the optical absorption techniques, prism coupling and Z-scan. Further studies were developed on the precipitation of silver nanoparticles embedded in the glass system TeO2-ZnO-Na2O doped with AgNO3, by means of thermal treatments at different temperatures. The characterization of the metallic nanoparticles was carried out by optical absorption aided by transmission electron microscopy and dispersive energy spectroscopy. Four paramagnetic responses were observed by electron paramagnetic resonance of the -irradiated glasses, one not yet identified and the other three identified as g0, g1 and g3 attributed respectively to the tellurium-oxygen hole center, non-bridging oxygen hole center and tellurium electron center. A model to explain the formation mechanisms of these centers was proposed. The thermoluminescence results indicated that the recombination processes of these centers are non-radiative. This is the first study that deals with polarization and depolarization phenomena in tellurite glasses with and without gamma irradiation, by the technique of thermally stimulated depolarization currents. In what regards the optical properties of the glass systems TeO2-ZnONa2O and TeO2-Nb2O5-Na2O, the effect of the silver doping on the gap energy, Urbach tail, linear and nonlinear refractive indices were investigated. Through the Z-scan technique results of the glass system TeO2-Nb2O5-Na2O, an increasing asymmetry of the curve, with increasing AgNO3 content was observed. This phenomenon was explained through an adaptation of Sumi´s model for non-radiative processes, applied to a silver doped insulating glass, to explain the thermal character of the nonlinear refractive index. Finally, a model was developed to explain the silver nanoparticles precipitation in the TeO2-ZnO-Na2O glass matrix submitted to thermal treatment.

Fundação de Amparo a Pesquisa do Estado de Minas Gerais / The SNABP [40SiO2.30Na2CO3.1Al2O3.25B2O3.PbO2 (mol%)] glass system, nanostructured with PbS Quantum Dots (QDs) and/or doped with Er3+ ions, was successfully synthesized by the Fusion Method, when it was subjected to appropriate thermal annealing. The glass transition temperatures (Tg) were obtained by Differential Thermal Analyze (DTA), in which it was possible to define a suitable temperature to be used in the thermal annealing of the synthesized samples. As results of these thermal annealing, the formation and growth of PbS QDs have occurred in the glass environment. The optical properties of samples were investigated by Optical Absorption (OA), Photoluminescence (PL), and Photoluminescence with Temporal Resolution (PLTR). Moreover, the Atomic Force Microscopy (AFM) and X-Ray Diffractometry were employed in study of morphological and structural properties of samples, respectively. The size dispersions of PbS QDs were determined from OA spectra. Once using both the Method and OA data, it was also possible to estimate the average diameters of these nanoparticles, which grow with the increase in annealing time. The characteristic transitions of Er3+ ions were clearly identified in OA spectra. In addition, it was observed that the increase in annealing time of samples had provoked amplification in the overlapping between PL bands of both the PbS QDs and Er3+ ions, as well as with the absorption 4I15/2 -> 4I13/2 of these ions. Thus, the PLTR measurements have confirmed the decrease in lifetime of the 4I13/2 level (of Er3+ ions), with the amplification in the overlapping of PL emissions. Finally, as a main result of this work, it was proved that the SNABP glass system, nanostructured with PbS QDs and doped with Er3+ ions, displays to be quite favorable to the radiative energy transfer process (from PbS QDs to Er3+ ions), as well as the occurrence of stimulated emission of 4I13/2 level. / O sistema vítreo SNABP [40SiO2.30Na2CO3.1Al2O3.25B2O3.PbO2 (mol%)] nanoestruturado com pontos quânticos (PQs) de PbS e/ou dopados com íons Er3+ foi sintetizado com sucesso pelo Método de Fusão, quando submetido a tratamentos térmicos apropriados. As temperaturas de transição vítrea (Tg) foram obtidas por Análise Térmica Diferencial (DTA), em que foi possível definir uma temperatura adequada para ser utilizada nos tratamentos térmicos das amostras sintetizadas. Como resultados desses tratamentos térmicos, a formação e crescimento dos PQs de PbS ocorreram no ambiente vítreo. As propriedades ópticas das amostras foram investigadas por Absorção Óptica (AO), Fotoluminescência (PL) e Fotoluminescência com Resolução Temporal (PLRT). Além disso, a Microscopia de Força Atômica (AFM) e Difratometria de Raios-X (DRX) foram empregadas no estudo das propriedades morfológicas e estruturais das amostras, respectivamente. As dispersões de tamanho dos PQs de PbS foram determinadas a partir dos espectros de AO. Com a utilização do Método e os dados de AO, foi também possível estimar os diâmetros médios dessas nanopartículas, que aumentaram com o aumento no tempo de tratamento térmico. As transições características dos íons Er3+ foram claramente identificadas nos espectros de AO. Em adição, foi observado que o aumento no tempo de tratamento das amostras provocou um aumento na sobreposição entre as bandas de PL dos PQs de PbS e dos íons Er3+, bem como com a absorção 4I15/2 -> 4I13/2 desses íons. Assim, as medidas de PLRT confirmaram o decréscimo no tempo de vida do nível 4I13/2 (dos íons Er3+) com o aumento dessa sobreposição das emissões de PL. Finalmente, como principal resultado deste trabalho, foi comprovado que o sistema vítreo SNABP nanoestruturado com PQs de PbS dopados com íons Er3+ mostrou-se bastante favorável ao processo de transferência de energia radiativa (dos PQs de PbS para os íons Er3+), bem como a ocorrência da emissão estimulada do nível 4I13/2. / Mestre em Física

Fundação de Amparo a Pesquisa do Estado de Minas Gerais / In this work, Zn1-xAxTe (A = Mn, Co) diluted magnetic semiconductors (DMS) nanocrystal (NCs) were successfully grown in the P2O5 ZnO Al2O3 BaO PbO glass system synthesized by the method of Fusion-Nucleation, after subjecting to appropriate thermal annealing. Various experimental techniques were used in this study in order to get a comprehensive understanding of the optical, morphological, structural and magnetic properties these NCs. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) images revealed the size of both of Zn1-xMnxTe and Zn1-xCoxTe NCs. From the vibrating sample magnetometer (VSM) technique, there was growth behavior of magnetization and magnetic susceptibility as a function of the Mn concentration in the samples containing Zn1-xMnxTe NCs. At lower Mn concentrations, the sp electrons of ZnTe host semiconductor interact with the d electrons of Mn2+ ions, resulting in the sp-d exchange interaction, which causes a small increase in susceptibility. At higher Mn concentrations, the d-d exchange interaction between Mn atoms dominates over the sp-d exchange interaction, resulting in an abrupt increase in susceptibility. The EPR spectra, in addition to prove the results exhibited the well-known sextet hyperfine lines of Mn2+ ions, since samples with low Mn concentrations revealed the presence of Mn2+ ions within and near the surface of the ZnTe NCs. From the optical absorption spectra (OA) and photoluminescence (PL), analyzed on the basis of crystal field theory (CFT) as well as of the diffraction X-ray (XRD), Raman scattering (RS) and electron microscopy transmission (TEM) techniques, the substitutional incorporation of Mn2+ ions was confirmed up to its solubility limit (x = 0.100) ZnTe NCs. Above this concentration, can observe the formation of manganese oxide NCs such as MnO and MnO2, since the nucleation rate for the formation of these NCs is greater than that of Zn1-xMnxTe NCs, at high concentrations. Furthermore, from the PL spectra, it was found that it is possible to tune the emission of energy related to transition 4T1(4G) → 6A1(6S) of Mn2+ ions, of the spectral orange region to the near infrared, depending on Mn concentration. This is possible due to the variation of the local crystal field, where these ions are inserted. From the OA spectra, analyzed on the basis of CFT, it showed that Co2+ ions are substitutionally incorporated in tetrahedral sites of ZnTe NCs, due to its characteristics transitions in visible and near infrared spectral region. This evidence has been enhanced from MFM images, since NCs doped with magnetic ions, magnetically respond when induced by the magnetization of the probe. / Neste trabalho, nanocristais semicondutores magnéticos diluídos (SMD) de Zn1-xAxTe (A = Mn; Co) foram crescidos com sucesso no sistema vítreo P2O5 ZnO Al2O3 BaO PbO, sintetizado pelo método de Fusão-Nucleação, após submetê-lo a tratamento térmico apropriado. Várias técnicas experimentais foram utilizadas neste estudo a fim de obter um entendimento compreensivo das propriedades ópticas, morfológicas, estruturais e magnéticas desses NCs. Imagens de microscopia eletrônica de transmissão (MET) e microscopia de força atômica (MFA) revelaram o tamanho tanto de NCs de Zn1-xMnxTe quanto de Zn1-xCoxTe. A partir da técnica de magnetometria de amostra vibrante (MAV), verificou-se o crescimento da magnetização e o comportamento da susceptibilidade magnética, em função da concentração de Mn, em amostras contendo NCs de Zn1-xMnxTe. Em baixas concentrações de Mn, os elétrons sp do semicondutor hospedeiro ZnTe, interagem com os elétrons d dos íons Mn2+, resultando na interação de troca sp-d, que provoca um pequeno aumento na susceptibilidade magnética. Já, em concentrações mais elevadas de Mn, a interação de troca d-d entre átomos de Mn domina a interação de troca sp-d, o que resulta em um aumento abrupto da susceptibilidade. Os espectros RPE, além de comprovar esses resultados, exibiram o bem conhecido sexteto de linhas hiperfinas de íons Mn2+, uma vez que amostras com baixas concentrações de Mn revelaram a presença de íons Mn2+ no interior e próximos à superfície dos NCs de ZnTe. A partir dos espectros de absorção óptica (AO) e fotoluminescência (FL), analisados com base na teoria do campo cristalino (TCC), bem como das técnicas de difração de raios-X (DRX), espalhamento Raman (ER) e microscopia eletrônica de transmissão (MET), confirmou-se a incorporação substitucional de íons Mn2+ até seu limite de solubilidade nominal (x = 0,100) em NCs de ZnTe. Acima dessa concentração, observa-se a formação de NCs de óxido de manganês, tais como MnO e MnO2, uma vez que a taxa de nucleação para a formação desses NCs é maior que a de NCs de Zn1-xMnxTe, em altas concentrações. Além disso, a partir dos espectros FL, verificou-se que é possível sintonizar a energia de emissão relacionada à transição 4T1(4G) → 6A1(6S) de íons Mn2+, da região espectral laranja ao infravermelho próximo, em função da concentração de Mn. Isso é possível devido à variação do campo cristalino local, onde esses íons estão inseridos. A partir dos espectros AO, analisados com base na TCC, evidenciou-se que íons Co2+ são incorporados substitucionalmente em sítios tetraédricos de NCs de ZnTe, devido às suas transições características na região espectral do visível e infravermelho próximo. Essa evidência foi reforçada a partir de imagens de MFM, uma vez que os NCs, dopados com íons magnéticos, respondem magneticamente quando induzidos pela magnetização da sonda. / Doutor em Física

Vidros teluritos são considerados fortes candidatos para aplicações em lasers e óptica não linear devido a importantes características, como o elevado índice de refração, baixa energia de fônons, baixa temperatura de transição vítrea e sua fácil preparação. Neste trabalho foram produzidas amostras dos sistemas vítreos TeO2- ZnO-Na2O, TeO2-Nb2O5-Na2O e Te2O-Na2O incluindo ou não dopagens de AgNO3 para estudos estruturais e ópticos. As propriedades estruturais e os mecanismos de recombinação destes vidros foram estudados por meio das técnicas de ressonância paramagnética eletrônica, termoluminescência e correntes de despolarização termicamente estimuladas. Já as propriedades ópticas como o coeficiente de absorção linear, índice de refração linear e não linear foram estudadas por meio das técnicas de absorção óptica, acoplamento de prismas e varredura Z. Foram ainda desenvolvidos estudos da precipitação de nanopartículas de prata para o sistema TeO2-ZnO-Na2O com dopagens de AgNO3 com diferentes temperaturas de tratamento térmico. A caracterização das nanopartículas metálicas foi realizada por meio da técnica de absorção óptica auxiliada por microscopia eletrônica de transmissão e espectrometria de energia dispersiva. Foram observadas por ressonância paramagnética eletrônica quatro respostas paramagnéticas dos vidros irradiados com raio , sendo uma de natureza desconhecida e as outras três identificadas como g¹, g² e g³ atribuídas respectivamente ao centro de buraco do telúrio e do oxigênio, centro de buraco do oxigênio terminal e centro de elétron do telúrio. Foi proposto ainda um modelo para explicar os mecanismos de formação destes centros. A partir dos resultados de termoluminescência observou-se que os processos de recombinação destes centros de defeitos são não radioativos. Neste projeto foram estudados pela primeira vez na literatura os fenômenos de polarização e despolarização em vidros teluritos, com e sem irradiação gama, por meio da técnica de correntes de despolarização termicamente estimuladas. Quanto às propriedades ópticas, foi investigada a influência da adição de prata dos sistemas vítreos TeO2-ZnO-Na2O e TeO2-Nb2O5-Na2O em relação à energia do gap, a cauda de Urbach, índice de refração linear e não linear.Nos resultados de varredura Z do sistema vítreo TeO2-Nb2O5-Na2O foi observado o aumento da assimetria na curva com aumento da adição de AgNO3 Este fenômeno foi explicado por meio de uma adaptação do modelo de Sumi para processos não radiativos, responsáveis pelo aumento do caráter térmico do índice de refração não linear. Por fim um modelo foi criado para explicar a precipitação de nanopartículas de prata na matriz vítrea TeO2-ZnO-Na2O mediante tratamento térmico. / Tellurite glasses are considered powerful candidates for applications in lasers and nonlinear optics due to their important properties such as high refractive index, low phonon energy, relatively low glass transition temperature and easy glass production at room atmosphere. In this work glass samples of the systems ZnO-Na2O, TeO2-Nb2O5-Na2O and Te2O-Na2O were produced, including or not the AgNO3 doping for the structural and optical study purposes. The structural properties and the recombination mechanisms of these glasses were studied by means of the techniques of electron paramagnetic resonance, thermoluminescence and thermally stimulated depolarization currents. The optical properties such as the optical linear absorption coefficient, linear and nonlinear refractive index were studied by means of the optical absorption techniques, prism coupling and Z-scan. Further studies were developed on the precipitation of silver nanoparticles embedded in the glass system TeO2-ZnO-Na2O doped with AgNO3, by means of thermal treatments at different temperatures. The characterization of the metallic nanoparticles was carried out by optical absorption aided by transmission electron microscopy and dispersive energy spectroscopy. Four paramagnetic responses were observed by electron paramagnetic resonance of the -irradiated glasses, one not yet identified and the other three identified as g0, g1 and g3 attributed respectively to the tellurium-oxygen hole center, non-bridging oxygen hole center and tellurium electron center. A model to explain the formation mechanisms of these centers was proposed. The thermoluminescence results indicated that the recombination processes of these centers are non-radiative. This is the first study that deals with polarization and depolarization phenomena in tellurite glasses with and without gamma irradiation, by the technique of thermally stimulated depolarization currents. In what regards the optical properties of the glass systems TeO2-ZnONa2O and TeO2-Nb2O5-Na2O, the effect of the silver doping on the gap energy, Urbach tail, linear and nonlinear refractive indices were investigated. Through the Z-scan technique results of the glass system TeO2-Nb2O5-Na2O, an increasing asymmetry of the curve, with increasing AgNO3 content was observed. This phenomenon was explained through an adaptation of Sumi´s model for non-radiative processes, applied to a silver doped insulating glass, to explain the thermal character of the nonlinear refractive index. Finally, a model was developed to explain the silver nanoparticles precipitation in the TeO2-ZnO-Na2O glass matrix submitted to thermal treatment.