Made available in DSpace on 2019-03-30T00:26:47Z (GMT). No. of bitstreams: 0 Previous issue date: 2018-09-04 / Adhesion of orthodontic brackets in ceramic crowns is a challenge found in orthodontic clinical practice. Therefore, the purpose of this study was to evaluate the shear bond strength ofAdhesion of orthodontic brackets in ceramic crowns is a challenge found in orthodontic clinical practice. Therefore, the purpose of this study was to evaluate the shear bond strength of cemented orthodontic brackets to a lithium disilicate dental ceramic, having as variables: ceramic surface treatment, bracket type and thermocycling. For this purpose, 80 rectangular samples of vitreous ceramic based on lithium disilicate (15 mm wide x 13 mm high x 2 mm thick) were made. Samples were included in cylinders of polyvinyl chloride containing chemically activated acrylic resin and initially divided into 4 groups of 20 units according to the surface treatment: 37% phosphoric acid, for 30 seconds; 10% hydrofluoric acid for 60 seconds; blasting with aluminum oxide for 4 seconds; and diamond-tipped roughing for 10 seconds. Each group was divided into two subgroups for Edgwise, metallic and ceramic brackets. Subsequently the groups were subdivided into two new groups: thermocycled or not. The thermocycled samples went through 500 cycles with temperature variations between 5 ° C and 55 ° C. All samples were stored in distilled water at 37 ° C for 24 hours prior to the shear strength test. This test was performed in a universal test machine with a velocity of 1.0 mm /min. The type of failure was also recorded using the IRA (Remaining Adhesive Index) through a 8-fold magnification stereoscope. The numerical values obtained in the shear test were submitted to descriptive statistical analysis (mean and standard deviation), and the Shapiro- Wilk normality test and the non-parametric Mann-Whitney and Kruskal-Wallis tests were performed. From our results, it was found that there were no statistically significant differences regarding the type of surface treatment and the performance or not of thermocycling, observing a statistically significant difference only in the bracket type, being the union strength in the bracket metal than ceramic. Thus, it can be concluded that neither the type of surface treatment nor the thermocycling performance were decisive in the bond strength of orthodontic brackets to the lithium disilicate ceramic, and the type of bracket is more closely related to the adhesion quality considering methodological conditions of this research.cemented orthodontic brackets to a lithium disilicate dental ceramic, having as variables: ceramic surface treatment, bracket type and thermocycling. For this purpose, 80 rectangular samples of vitreous ceramic based on lithium disilicate (15 mm wide x 13 mm high x 2 mm thick) were made. Samples were included in cylinders of polyvinyl chloride containing chemically activated acrylic resin and initially divided into 4 groups of 20 units according to the surface treatment: 37% phosphoric acid, for 30 seconds; 10% hydrofluoric acid for 60 seconds; blasting with aluminum oxide for 4 seconds; and diamond-tipped roughing for 10 seconds. Each group was divided into two subgroups for Edgwise, metallic and ceramic brackets. Subsequently the groups were subdivided into two new groups: thermocycled or not. The thermocycled samples went through 500 cycles with temperature variations between 5 ° C and 55 ° C. All samples were stored in distilled water at 37 ° C for 24 hours prior to the shear strength test. This test was performed in a universal test machine with a velocity of 1.0 mm /min. The type of failure was also recorded using the IRA (Remaining Adhesive Index) through a 8-fold magnification stereoscope. The numerical values obtained in the shear test were submitted to descriptive statistical analysis (mean and standard deviation), and the Shapiro- Wilk normality test and the non-parametric Mann-Whitney and Kruskal-Wallis tests were performed. From our results, it was found that there were no statistically significant differences regarding the type of surface treatment and the performance or not of thermocycling, observing a statistically significant difference only in the bracket type, being the union strength in the bracket metal than ceramic. Thus, it can be concluded that neither the type of surface treatment nor the thermocycling performance were decisive in the bond strength of orthodontic brackets to the lithium disilicate ceramic, and the type of bracket is more closely related to the adhesion quality considering methodological conditions of this research. / A adesão de braquetes ortodônticos em coroas cerâmicas é um desafio encontrado na prática clínica ortodôntica. Diante disso, o objetivo do presente estudo foi avaliar a sistência ao cisalhamento de braquetes ortodônticos cimentados a uma cerâmica odontológica à base de dissilicato de lítio, tendo como variáveis: tratamento da superfície cerâmica, tipo de braquete e termociclagem. As 80 amostras retangulares de cerâmica vítrea à base de dissilicato de lítio (15 mm de largura x 13 mm de altura x 2 mm de espessura) foram confeccionadas. Em seguida, as amostras foram incluídas em cilindros de P.V.C. contendo resina acrílica ativada quimicamente e as amostras foram divididas inicialmente em 4 grupos de 20 unidades conforme o tratamento de superfície: ácido fosfórico 37% por 30 segundos (HP); ácido hidrofluorídrico 10% por 60 segundos (HF); jateamento com óxido de alumínio por 4 segundos (SB); e asperização com ponta diamantada por 10 segundos (DW). Cada grupo foi dividido em dois subgrupos para a cimentação com cimento resinoso de braquetes Edgwise: metálico e cerâmico. Os dois novos grupos foram subdivididos em termociclados ou não termociclados. As amostras termocicladas passaram por 500 ciclos com variações de temperatura entre 5°C a 55°C. Todas as amostras foram armazenadas em água destilada a 37° C por 24 horas antes do teste de resistência ao cisalhamento. Este teste foi realizado em máquina de ensaios universal com velocidade de 1 mm/min. O tipo de falha também foi registrado usando o IRA (Índice de Adesivo Remanescente) por meio de um estereoscópio com magnificação de oito vezes. Os valores numéricos obtidos no teste de cisalhamento foram submetidos a¿ análise estatística descritiva (média e desvio padrão), tendo sido realizado o teste de normalidade Shapiro-Wilk e os testes não paramétricos de Kruskal-Wallis e Mann-Whitney. Verificou-se que não houve diferença estatística significante em relação ao tipo de tratamento de superfície e a realização ou não de termociclagem, observando-se diferença estatisticamente significativa apenas no tipo de braquete, sendo a resistência de união no braquete metálico maior do que no de cerâmica. Assim, o tipo de tratamento de superfície e o envelhecimento por termociclagem não foram decisivos na resistência de união de braquetes ortodônticos à cerâmica de dissilicato de lítio. O tipo de braquete está mais atrelado à qualidade da adesão, sendo o braquete metálico mais resistente nas condições testadas no presente estudo.

O objetivo deste trabalho foi avaliar a quantidade de resina residual após a descolagem de braquetes e a perda e/ou desgaste de esmalte ocorrido durante as fases de: colagem, descolagem e remoção dos remanescentes resinosos, na área do braquete e adjacente. A amostra foi constituída de 150 pré-molares, dividida em dois grupos de acordo com o tipo de material do braquete utilizado: metálico (n=75) e cerâmico (n=75), nas duas primeiras fases do estudo, colagem e descolagem. Os procedimentos de colagem foram realizados de acordo com a International Organization for Standardization (2003), e a descolagem segundo a orientação preconizada pelo fabricante. Na fase de remoção dos remanescentes resinosos foram considerados cinco grupos de acordo com o protocolo de acabamento/polimento e prescrição dos respectivos fabricantes: FF diamantada + Soflex; Pedra Shofu; Dentaurum Carbide; Komet Carbide e Jet Carbide, com auxilio de lupas telescópicas sob a magnificação 3x. A avaliação qualitativa (ARIm e ESI) foi realizada por meio de fotografias digitais (lupa estereoscópica - Olympus SZ61). A avalição quantitativa foi realizada pelo método de medição por Coordenada - Coordinate Measuring Machines (Mitutoyo), mod. Legex CNC 9106 - Perfil de linha. As possíveis diferenças entre os protocolos de acabamento/polimento foram avaliadas pela análise de variância (ANOVA) e pelo teste de comparações múltiplas de Tukey. As quantidades médias de resina residual encontrada na área sob a base do braquete, após acabamento/polimento foram: Diamantada FF + Soflex (10,4 m ±10,5), Pedra Shofu (18,5 m ± 12,1), Dentaurum Carbide (11,2 m ± 11,9), Komet Carbide (9,5 m ± 10,8) e Jet Carbide (22,8 m ± 24,0). E na área adjacente: Diamantada FF + Soflex (14,9 m ± 13,0), Pedra Shofu (22,8 m ±19,5), Dentaurum Carbide (21,4 m ±18,5), Komet Carbide (9,6 m ± 7,7), Jet Carbide (27,8 m ± 24,5). Desta forma, constatou-se que, em geral, os protocolos de acabamento/polimento deixaram maior quantidade de resina residual sobre a área adjacente que na área do braquete, com exceção do protocolo Komet Carbide, que teve desempenho semelhante em ambas as áreas. E as quantidades médias de perda e/ou desgaste do esmalte na área do braquete foram: Diamantada FF + Soflex (-134,9 m ± 56,4), Pedra Shofu ( 39,2 m ± 12,8), Dentaurum Carbide ( 70,5 m ± 27,9), Komet Carbide (-44,8 m ± 14,3) e Jet Carbide ( 68,2 m ± 35,7) na área do braquete, enquanto na área adjacente: Diamantada FF + Soflex (-124,7 m ± 133,1), Pedra Shofu (- 37,9 m ± 25,1), Dentaurum Carbide (- 60,1 m ±32,4), Komet Carbide (-36,6 m ± 19,5) e (Jet Carbide 65,4 m ± 65,0) (Tabela 5.9). Ressalta-se que em ambas as áreas de avaliação, o protocolo (Diamantada FF + Soflex) foi responsável pela maior quantidade de perda e/ou desgaste, diferenciando-se com significância estatística dos demais protocolos. Com base nestes resultados podemos concluir que os protocolos de acabamento/polimento avaliados demonstraram excelente desempenho na remoção dos remanescentes resinosos embora nenhum deles tenha sido capaz de remover totalmente o material de colagem, todos danificaram o esmalte, sendo o protocolo Komet carbide o mais diferenciado. / The objective of this study was to evaluate the quantity of residual resin after removal of brackets and the loss and//or wear-and-tear of enamel occurring during the phases of fixing, detaching and removal of remnant resin in the bracket area and its adjacent. The sample was made up of 150 premolars, divided into two groups in accordance with the type of bracket material used: metal (n=75) and ceramic (n=75), in the two initial phases of study, fixing and removal. Fixing procedures were carried out in accordance with the International Organization for Standardization, (2003), and removal according to orientation advocated by the manufacturer. In the removal of remnant resin phase five groups were considered, all in agreement with the finishing/polishing protocol and prescription of the respective manufacturers: FF diamantada + Soflex; Pedra Shofu; Dentaurum Carbide; Komet Carbide and Jet Carbide, and with the aid of telescopic magnifying glass of three-fold magnification Qualitative evaluation (ARIm and ESI) was done by means of digital photographs(stereoscopic magnifying glass Olympus SZ61). Quantitative evaluation was conducted using the coordinate medication method - Coordinate Measuring Machines (Mitutoyo), mod. Legex CNC 9106 - line profile. Possible differences between finishing/polishing protocols were evaluated via variance analysis (ANOVA), and by Tukey Multiple Comparison test. Median quantities of residual resin found in the region below the base of the bracket, following finishing/polishing were: Diamantada FF + Soflex (10,4 m ±10,5), Pedra Shofu (18,5m ± 12,1), Dentaurum Carbide (11,2 m ± 11,9), Komet Carbide (9,5 m ± 10,8) and Jet Carbide (22,8 m ± 24,0). In this way, it was confirmed that finishing/polishing protocols, in general, left the major part of residual resin below the adjacent area than in the bracket area, with the exception of Komet Carbide protocol, displaying similar performance in both areas Median quantities of loss and/or wearand- tear of enamel in the bracket area were: Diamantada FF + Soflex (-134,9 m ± 56,4), Pedra Shofu ( 39,2 m ± 12,8), Dentaurum Carbide ( 70,5 m ± 27,9), Komet Carbide (-44,8 m ± 14,3) and Jet Carbide ( 68,2 m ± 35,7) in bracket area, while in adjacent area: Diamantada FF + Soflex (-124,7 m ± 133,1), Pedra Shofu (- 37,9 m ± 25,1), Dentaurum Carbide (- 60,1 m ±32,4), Komet Carbide (-36,6 m ± 19,5) and (Jet Carbide 65,4 m ± 65,0) (Table 5.9) Standing out in both areas of evaluation, protocol (Diamantada FF + Soflex) was responsible for the major quantity of loss and /or wear and tear, differentiating itself from the other protocols by significant statistics. Based on these results, we can conclude that the finishing/polishing protocols evaluated, displayed excellent performance in the removal of remnant resin, although none have totally been capable of removing fixing material, and all damaged the enamel, with Komet protocol being the most differentiated.

Made available in DSpace on 2014-06-11T19:33:22Z (GMT). No. of bitstreams: 0 Previous issue date: 2012-12-13Bitstream added on 2014-06-13T20:05:06Z : No. of bitstreams: 1 monini_ac_dr_arafo.pdf: 569037 bytes, checksum: 70156844614f17c25c89142213ee5c2e (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / O desenvolvimento tecnológico na fabricação de braquete trouxe consigo a ideia de que a tecnologia empregada no aparelho pode representar aumento na velocidade de movimentação dentária. O propósito deste estudo foi avaliar a taxa de movimentação mensal de caninos e a perda de ancoragem ocorrida durante o movimento de retração de caninos por deslizamento entre dois tipos de braquetes diferentes, um autoligado e outro convencionalmente ligado, bem como diferenças entre os arcos superior e inferior. A amostra consistiu de 25 pacientes biprotusos, portadores de má oclusão de classe I com necessidade de extração de quatro primeiros pré-molares para realização do tratamento ortodôntico, com apinhamento no arco superior e inferior menores que 4mm, idade variando entre 18 anos até 34 anos e sem ausências dentárias sendo facultativa a presença dos terceiros molares. Em todos eles foram colados dois braquetes autoligados, um no canino superior e outro no canino inferior de maneira randomizada e num sistema split-mouth. Os demais dentes receberam braquetes convencionais e tubos nos molares. Os primeiros pré-molares foram extraídos após o alinhamento e nivelamentos dos arcos e 7 a 15 dias após deu-se início à retração dos caninos. Telerradiografias laterais de 45º foram realizadas antes do início da retração e após a completa retração de cada canino. A superposição dos traçados cefalométricos iniciais e após a retração permitiu o cálculo da perda de ancoragem ocorrida e a quantidade de retração para cada canino. A divisão da quantidade de retração pelo tempo decorrido permitiu o cálculo da taxa de movimentação mensal dos caninos. Os resultados demonstraram que não existe diferença na taxa de movimentação mensal dos caninos e nem na perda de ancoragem entre os dois tipos de braquetes... / The technological development in bracket manufacturing brought with it the belief that enhanced technology might translate as faster in tooth movement. The aim of this study was to evaluate the monthly rate of canine movement as well as the rate of anchorage loss during the retraction of canines by sliding mechanics with two different types of brackets: self-ligated and conventional and also, as well as differences between upper and lower arches. The sample comprised 25 biprotusive class I patients with need of four bicuspid extractions for orthodontic treatment, with upper and lower crowding less than 4 mm, age between 18 and 34 years old and no missing teeth except for the third molars. In all of them selfligated brackets were randomly bonded on the upper and lower canines in a split mouth design. The remaining teeth were bonded and banded with conventional brackets. First bicuspids were extracted after leveling and alignment and after 7 to 15 days canine retraction was initiated. Forty-five degree radiographic were taken before retraction and after complete canine retaraction. Cephalometrics tracings before and after canine retraction allowed the measurement of the resultant anchorage loss and the amount of canine retraction. By dividing the amount of canine retraction by it allowed the calculation of the canine movement monthly rate. The results showed that there is no difference between the rate of canine monthly movement and loss of anchorage between the two types of bracket. When arches were compared, upper canines were found to move faster than the lower ones and no difference was found on anchorage loss. It was concluded that canine retraction by sliding mechanics with either brackets occur at the same rate as well as the loss of anchorage of the molars. Upper... (Complete abstract click electronic access below)

Orientador: Sérgio Eduardo de Paiva Gonçalves / Co-orientador: Alessandra Nara de Souza Rastelli / Banca: Maria Filomena Rocha Lima Huhtala / Banca: Ricardo Scarparo Navarro / Banca: Luciane Hiramatsu Azevedo / Banca: Eduardo Bresciani / Resumo: O trabalho in vitro avaliou a eficácia da inativação fotodinâmica (PDI) da eritrosina (E) e hematoporfirina IX (H), com 10 µM, utilizando LED azul, dose de 75 J/cm2 em células planctônicas e biofilme de S. mutans (UA 159). Suspensões padrões contendo 107 células/mL foram preparadas e submetidas a diferentes condições experimentais: a) hematoporfirina IX e LED (H+L+); b) eritrosina e LED (E+L+); c) apenas LED (F-L+); d) tratamento somente com hematoporfirina IX (H+L-); e) somente com eritrosina (E+L-); e f) grupo controle, sem tratamento com fotossensibilizador (F) e sem a utilização de LED (F-L-). As cepas foram semeadas em ágar MSBS para contagem de unidades formadoras de colônias (UFC/mL). Na segunda parte do trabalho foi realizado a PDI em biofilme de S. mutans sobre bráquetes metálicos e cerâmicos, com H a 10 µM e LED azul. Os resultados foram submetidos à análise de variância e teste de Tukey (p<0,05) e demonstraram que a E sob efeito do LED (E+L+) não foi eficaz na PDI de células planctônicas, nos parâmetros usados (p=0,3644). No entanto, a H promoveu redução de 6,78 log10 (p<0,0001), no grupo de tratamento (H+L+). A PDI com a associação da H e LED foi efetiva na redução de 100% de culturas planctônicas de S. mutans, porém o mesmo não foi observado na associação com a E, na dosimetria utilizada no experimento. A PDI no biofilme de S. mutans sobre bráquetes metálicos, com a H e LED não foi eficaz nos parâmetros utilizados (p=0,1023), no entanto, ocorreu diminuição significativa de 53% sobre bráquetes cerâmicos (p=0,004). A H IX modificada é promissora como agente fotossensibilizador a ser empregado na técnica de PDI em associação ao LED azul, sendo necessários outros ensaios, em novas concentrações e/ou dosimetrias para se conseguir a inativação bacteriana / Abstract: The in vitro study evaluated the efficacy of photodynamic inactivation (PDI) with erythrosine (E) and hematoporphyrin (H) 10 µM, using a blue light-emitting diode (LED), a fluence of 75 J/cm2, on planktonic cultures and biofilm of S. mutans (UA 159). Suspensions containing 107 cells/mL were prepared and were tested under different experimental conditions: a) hematoporphyrin IX and LED (H+L+); b) erythrosine and LED irradiation (E+L+); c) only LED (P-L+); d) only hematoporphyrin IX (H+L-); e) only erythrosine (E+L-); and f) control group, no LED irradiation or photosensitizer (P) treatment (P-L-). After treatment, the strains were seeded onto MSBS agar in order to determine the number of colony-forming units (CFU/mL). The second part of this work consisted of the PDI of S. mutans biofilm on metal and ceramic brackets with the H 10 μM and blue LED. The results were submitted to analysis of variance and the Tukey test (p<0.05) and showed that E under the effect of LED proved to be ineffective in the PDI of planktonic cultures with the parameters used (p=0.3644). H, however, caused a reduction of 6.78 log10 (p<0.0001) in the treatment group (H+L+). PDI with H and LED exerted antimicrobial effect of 100% of the S. mutans strain studied, whereas the same was not observed in the association with E in the dosimetry used in this work. PDI on S. mutans biofilm on metal brackets, with H and LED was not effective with the parameters used (p=0.1023), however on ceramic brackets caused a significant reduction of 53% (p=0,004). Modified H IX is a promising photosensitizer to be used in the PDI technique in combination with blue LED. Therefore, new tests with new concentrations and/or dosimetry are needed to achieve bacterial inactivation / Doutor

Orientador: Luiz Gonzaga Gandini Junior / Banca: Ary dos Santos-Pinto / Banca: Dirceu Barnabé Raveli / Banca: Claudio de Góis Nery / Banca: Marcos Augusto Lenza / Resumo: O desenvolvimento tecnológico na fabricação de braquete trouxe consigo a ideia de que a tecnologia empregada no aparelho pode representar aumento na velocidade de movimentação dentária. O propósito deste estudo foi avaliar a taxa de movimentação mensal de caninos e a perda de ancoragem ocorrida durante o movimento de retração de caninos por deslizamento entre dois tipos de braquetes diferentes, um autoligado e outro convencionalmente ligado, bem como diferenças entre os arcos superior e inferior. A amostra consistiu de 25 pacientes biprotusos, portadores de má oclusão de classe I com necessidade de extração de quatro primeiros pré-molares para realização do tratamento ortodôntico, com apinhamento no arco superior e inferior menores que 4mm, idade variando entre 18 anos até 34 anos e sem ausências dentárias sendo facultativa a presença dos terceiros molares. Em todos eles foram colados dois braquetes autoligados, um no canino superior e outro no canino inferior de maneira randomizada e num sistema split-mouth. Os demais dentes receberam braquetes convencionais e tubos nos molares. Os primeiros pré-molares foram extraídos após o alinhamento e nivelamentos dos arcos e 7 a 15 dias após deu-se início à retração dos caninos. Telerradiografias laterais de 45º foram realizadas antes do início da retração e após a completa retração de cada canino. A superposição dos traçados cefalométricos iniciais e após a retração permitiu o cálculo da perda de ancoragem ocorrida e a quantidade de retração para cada canino. A divisão da quantidade de retração pelo tempo decorrido permitiu o cálculo da taxa de movimentação mensal dos caninos. Os resultados demonstraram que não existe diferença na taxa de movimentação mensal dos caninos e nem na perda de ancoragem entre os dois tipos de braquetes... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The technological development in bracket manufacturing brought with it the belief that enhanced technology might translate as faster in tooth movement. The aim of this study was to evaluate the monthly rate of canine movement as well as the rate of anchorage loss during the retraction of canines by sliding mechanics with two different types of brackets: self-ligated and conventional and also, as well as differences between upper and lower arches. The sample comprised 25 biprotusive class I patients with need of four bicuspid extractions for orthodontic treatment, with upper and lower crowding less than 4 mm, age between 18 and 34 years old and no missing teeth except for the third molars. In all of them selfligated brackets were randomly bonded on the upper and lower canines in a split mouth design. The remaining teeth were bonded and banded with conventional brackets. First bicuspids were extracted after leveling and alignment and after 7 to 15 days canine retraction was initiated. Forty-five degree radiographic were taken before retraction and after complete canine retaraction. Cephalometrics tracings before and after canine retraction allowed the measurement of the resultant anchorage loss and the amount of canine retraction. By dividing the amount of canine retraction by it allowed the calculation of the canine movement monthly rate. The results showed that there is no difference between the rate of canine monthly movement and loss of anchorage between the two types of bracket. When arches were compared, upper canines were found to move faster than the lower ones and no difference was found on anchorage loss. It was concluded that canine retraction by sliding mechanics with either brackets occur at the same rate as well as the loss of anchorage of the molars. Upper... (Complete abstract click electronic access below) / Doutor

Submitted by Lucelia Lucena (lucelia.lucena@ufpe.br) on 2015-03-13T18:08:55Z No. of bitstreams: 2 DISSERTAÇÃO MESTRADO MONICA SCHAFFER.pdf: 1718738 bytes, checksum: 96f6f213957ec36cb4878c8cabad2599 (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) / Made available in DSpace on 2015-03-13T18:08:55Z (GMT). No. of bitstreams: 2 DISSERTAÇÃO MESTRADO MONICA SCHAFFER.pdf: 1718738 bytes, checksum: 96f6f213957ec36cb4878c8cabad2599 (MD5) license_rdf: 1232 bytes, checksum: 66e71c371cc565284e70f40736c94386 (MD5) Previous issue date: 2012-08-08 / Objetivos: No presente trabalho foi objetivo avaliar a superfície do esmalte após a descolagem de brackets ortodônticos e remoção da resina remanescente, por meio da técnica da Tomografia por Coerência Óptica (TCO), em 2D e 3D. Materiais e Métodos: Sessenta coroas de incisivos bovinos foram incluídas em resina acrílica, com auxílio de matriz metálica, e em seguida submetidas a polimento manual com lixas d’água com granulações crescentes. A colagem do bracket foi realizada com o sistema TransbondTM XT (3M), e o armazenamento das amostras, em ambiente úmido por 1 semana. No artigo 1, vinte dentes foram divididos (n=10) em grupo A, descolagem com alicate 346/ICE e B, descolagem com pistola 346/Zatty. Foram feitas imagens das amostras em Microscópio Óptico (MO) e TCO 3D, e três avaliadores as classificaram quanto o Índice de Adesivo Remanescente (IAR), que posteriormente foi calculado pelo Teste de Kappa. As imagens em TCO 2D serviram para calcular a espessura do ARI e perda de esmalte. No artigo 2, quarenta dentes foram descolados com alicate 346/ICE e sem seguida divididos (n=10) em G1, remoção da resina remanescente com broca carbide de tungstênio (BCT) 30 laminas em alta rotação + pasta diamantada e disco de feltro/Diamond; G2,Pontas de fibra de vidro em baixa rotação/TDV; G3,Laser Er:YAG 100 mJ/1.00 W e G4,BCT 30 laminas + polimento com discos de óxido de alumínio/Dhpro. Medidas de rugosidade foram tomadas antes e depois da remoção, bem como imagens em TCO 2D,3D e Microscópio Eletrônico de Varredura (MEV). Foi usado teste estatítisco ANOVA. Resultados: O MO e TCO 3D apresentaram 0,83% e 0,70% de concordância no teste de Kappa, respectivamente. Através do TCO 2D, observou-se espessura da resina residual após descolagem do bracket, em torno de 164μm (±34 μm). Resultados do IAR mostraram 72,7% em score 3 e 27,3% em score 2 no grupo A; e 55,6% em score 1, 33,3% em score 2 e 11,1% em score 3, no grupo B. G1, G3 e G4 tiverem rugosidades finais similares, diferente do G2 que apresentou aumento significante (p<0.05). Análises da superfície mostraram ranhuras horizontais e verticais no G1 e G4, áreas pontuais de perda mineral no G3. Conclusões: MO e TCO 3D foram considerados satisfatórios para mensurar o IAR. TCO 2D foi preciso para medir a espessura de resina remanescente. O grupo do alicate (A) apresentou fratura predominantemente na interface bracket/adesivo que preserva mais estrutura de esmalte que o grupo da pistola (B) que a fratura ocorreu frequentemente na interface esmalte/adesivo. A remoção da resina remanescente apresenta influencia direta na rugosidade final. Nenhum método de remoção foi considerado perfeito. Laser Er:YAG produziu a maior perda mineral, e a ponta de fibra de vidro não foi capaz de promover um polimento adequado, apresentando a maior rugosidade final. Todos os 3 métodos de avaliação da superfície foram considerados bons para mensurar a perda de esmalte, entretanto, o TCO apresenta a possibilidade de ser aplicada clinicamente.

O objetivo deste trabalho foi avaliar a quantidade de resina residual após a descolagem de braquetes e a perda e/ou desgaste de esmalte ocorrido durante as fases de: colagem, descolagem e remoção dos remanescentes resinosos, na área do braquete e adjacente. A amostra foi constituída de 150 pré-molares, dividida em dois grupos de acordo com o tipo de material do braquete utilizado: metálico (n=75) e cerâmico (n=75), nas duas primeiras fases do estudo, colagem e descolagem. Os procedimentos de colagem foram realizados de acordo com a International Organization for Standardization (2003), e a descolagem segundo a orientação preconizada pelo fabricante. Na fase de remoção dos remanescentes resinosos foram considerados cinco grupos de acordo com o protocolo de acabamento/polimento e prescrição dos respectivos fabricantes: FF diamantada + Soflex; Pedra Shofu; Dentaurum Carbide; Komet Carbide e Jet Carbide, com auxilio de lupas telescópicas sob a magnificação 3x. A avaliação qualitativa (ARIm e ESI) foi realizada por meio de fotografias digitais (lupa estereoscópica - Olympus SZ61). A avalição quantitativa foi realizada pelo método de medição por Coordenada - Coordinate Measuring Machines (Mitutoyo), mod. Legex CNC 9106 - Perfil de linha. As possíveis diferenças entre os protocolos de acabamento/polimento foram avaliadas pela análise de variância (ANOVA) e pelo teste de comparações múltiplas de Tukey. As quantidades médias de resina residual encontrada na área sob a base do braquete, após acabamento/polimento foram: Diamantada FF + Soflex (10,4 m ±10,5), Pedra Shofu (18,5 m ± 12,1), Dentaurum Carbide (11,2 m ± 11,9), Komet Carbide (9,5 m ± 10,8) e Jet Carbide (22,8 m ± 24,0). E na área adjacente: Diamantada FF + Soflex (14,9 m ± 13,0), Pedra Shofu (22,8 m ±19,5), Dentaurum Carbide (21,4 m ±18,5), Komet Carbide (9,6 m ± 7,7), Jet Carbide (27,8 m ± 24,5). Desta forma, constatou-se que, em geral, os protocolos de acabamento/polimento deixaram maior quantidade de resina residual sobre a área adjacente que na área do braquete, com exceção do protocolo Komet Carbide, que teve desempenho semelhante em ambas as áreas. E as quantidades médias de perda e/ou desgaste do esmalte na área do braquete foram: Diamantada FF + Soflex (-134,9 m ± 56,4), Pedra Shofu ( 39,2 m ± 12,8), Dentaurum Carbide ( 70,5 m ± 27,9), Komet Carbide (-44,8 m ± 14,3) e Jet Carbide ( 68,2 m ± 35,7) na área do braquete, enquanto na área adjacente: Diamantada FF + Soflex (-124,7 m ± 133,1), Pedra Shofu (- 37,9 m ± 25,1), Dentaurum Carbide (- 60,1 m ±32,4), Komet Carbide (-36,6 m ± 19,5) e (Jet Carbide 65,4 m ± 65,0) (Tabela 5.9). Ressalta-se que em ambas as áreas de avaliação, o protocolo (Diamantada FF + Soflex) foi responsável pela maior quantidade de perda e/ou desgaste, diferenciando-se com significância estatística dos demais protocolos. Com base nestes resultados podemos concluir que os protocolos de acabamento/polimento avaliados demonstraram excelente desempenho na remoção dos remanescentes resinosos embora nenhum deles tenha sido capaz de remover totalmente o material de colagem, todos danificaram o esmalte, sendo o protocolo Komet carbide o mais diferenciado. / The objective of this study was to evaluate the quantity of residual resin after removal of brackets and the loss and//or wear-and-tear of enamel occurring during the phases of fixing, detaching and removal of remnant resin in the bracket area and its adjacent. The sample was made up of 150 premolars, divided into two groups in accordance with the type of bracket material used: metal (n=75) and ceramic (n=75), in the two initial phases of study, fixing and removal. Fixing procedures were carried out in accordance with the International Organization for Standardization, (2003), and removal according to orientation advocated by the manufacturer. In the removal of remnant resin phase five groups were considered, all in agreement with the finishing/polishing protocol and prescription of the respective manufacturers: FF diamantada + Soflex; Pedra Shofu; Dentaurum Carbide; Komet Carbide and Jet Carbide, and with the aid of telescopic magnifying glass of three-fold magnification Qualitative evaluation (ARIm and ESI) was done by means of digital photographs(stereoscopic magnifying glass Olympus SZ61). Quantitative evaluation was conducted using the coordinate medication method - Coordinate Measuring Machines (Mitutoyo), mod. Legex CNC 9106 - line profile. Possible differences between finishing/polishing protocols were evaluated via variance analysis (ANOVA), and by Tukey Multiple Comparison test. Median quantities of residual resin found in the region below the base of the bracket, following finishing/polishing were: Diamantada FF + Soflex (10,4 m ±10,5), Pedra Shofu (18,5m ± 12,1), Dentaurum Carbide (11,2 m ± 11,9), Komet Carbide (9,5 m ± 10,8) and Jet Carbide (22,8 m ± 24,0). In this way, it was confirmed that finishing/polishing protocols, in general, left the major part of residual resin below the adjacent area than in the bracket area, with the exception of Komet Carbide protocol, displaying similar performance in both areas Median quantities of loss and/or wearand- tear of enamel in the bracket area were: Diamantada FF + Soflex (-134,9 m ± 56,4), Pedra Shofu ( 39,2 m ± 12,8), Dentaurum Carbide ( 70,5 m ± 27,9), Komet Carbide (-44,8 m ± 14,3) and Jet Carbide ( 68,2 m ± 35,7) in bracket area, while in adjacent area: Diamantada FF + Soflex (-124,7 m ± 133,1), Pedra Shofu (- 37,9 m ± 25,1), Dentaurum Carbide (- 60,1 m ±32,4), Komet Carbide (-36,6 m ± 19,5) and (Jet Carbide 65,4 m ± 65,0) (Table 5.9) Standing out in both areas of evaluation, protocol (Diamantada FF + Soflex) was responsible for the major quantity of loss and /or wear and tear, differentiating itself from the other protocols by significant statistics. Based on these results, we can conclude that the finishing/polishing protocols evaluated, displayed excellent performance in the removal of remnant resin, although none have totally been capable of removing fixing material, and all damaged the enamel, with Komet protocol being the most differentiated.

Orientador: Ary dos Santos Pinto / Resumo: Neste estudo investigou-se in vivo a eficácia da técnica de colagem direta comparada a colagem indireta em relação ao número de falhas na colagem que ocorreram durante o tratamento ortodôntico. Foram selecionados cento e vinte pacientes com idades de 13 e 57 anos, de ambos gêneros tratados consecutivamente numa clínica privada nos anos de 2011 a 2017 com aparelho ortodôntico fixo metálico e divididos em dois grupos: grupo A, com 54 indivíduos no qual se realizou a colagem de bráquetes pela técnica direta e o grupo B com 66 indivíduos, no qual se realizou a colagem de bráquetes pela técnica indireta. A comparação estatística entre as duas técnicas de colagem de bráquetes foi baseada no número total de descolagens e no tempo para a primeira descolagem, tendo sido cada paciente observado por 25 meses. Utilizou-se, respectivamente, os testes de Qui-quadrado e de sobrevida de Kaplan-Meier, com a comparação entre as curvas realizada pelo teste de Log-rank. Foi empregado o modelo de regressão de Cox para avaliar a ação conjunta dos fatores de interesse sobre o tempo da primeira descolagem. Adotou-se sempre o nível de significância de 5% para a tomada de decisão. No período de avaliação de 25 meses após a colagem dos bráquetes nos arcos superior e inferior, ocorreu diferença significativa de 1,6% na porcentagem de quedas de bráquetes pela técnica de colagem indireta em relação à direta, porém, a baixa porcentagem destas quedas indicou a eficácia da técnica de colagem direta de 97,3% ... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: In this in vivo study it was investigated the effectiveness of the direct bonding technique compared to indirect one to evaluate the number of bond failures that occurred during orthodontic treatment. One hundred and twenty patients aged 13 to 57 years, of both genders consecutively treated in a private practice in the years 2011 to 2017 with fixed metallic orthodontic appliance were selected and divided into two groups: group A, with 54 individuals in which the brackets were bonded by the direct technique and group B with 66 individuals, in which the brackets were bonded by the indirect technique. The statistical comparison between the two techniques of bracket bonding were based on the total number of bond failures and the time to first bond failure, with each patient being observed for 25 months. The chi-square test was used to compare the survival rates of the brackets bonded with direct and indirect bonding. The log-rank test was used to compare the Kaplan-Meier survival curves of both bonding methods. The Cox regression model was used to evaluate the joint association of the factors of interest on the time to first bond failure. The level of significance of 5% was adopted for decision-making. In the evaluation period of 25 months after the bonding of the brackets in the upper and lower arches, there was a significant difference of 1.6% in the percentage of bracket failure in the indirect bonding technique in relation to the direct one. The low percentages of these failu... (Complete abstract click electronic access below) / Doutor

Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde. Programa de Pós-Graduação em Odontologia / Made available in DSpace on 2012-10-22T14:40:34Z (GMT). No. of bitstreams: 1 243331.pdf: 27385110 bytes, checksum: a00bf379a123c824c86d62da2f364103 (MD5) / A proposta deste estudo foi avaliar: a resistência de união de braquetes depois da aplicação ou não de um novo selante de superfície; o índice de cimento remanescente (ICR) no esmalte; o padrão de desunião na interface esmalte/selante/braquete e visualizar no MEV. Sessenta pré-molares foram divididos: Grupos MS e MC (braquetes metálicos colados sem e com selante, respectivamente); Grupos CS e CC (braquetes cerâmicos colados sem e com selante, respectivamente). Os espécimes foram submetidos ao teste de cisalhamento. Os resultados foram submetidos à análise de variância. Não houve diferença estatística significativa entre os grupos. O selante não afetou a resistência de união dos braquetes, o que sugere sua indicação na montagem do aparelho ortodôntico. Além disso, na descolagem dos braquetes ele permitiu uma superfície de esmalte livre do cimento

Tese (doutorado) - Pontifícia Universidade Católica do Paraná, Curitiba, 2012 / Inclui bibliografias / Na descolagem de brackets ortodônticos pode ocorrer a perda de esmalte na interface adesivo-esmalte. O objetivo deste estudo foi avaliar os possíveis danos à superfície do esmalte com três recolagens de brackets metálicos e cerâmicos novos por meio da res. / Debonding of orthodontic brackets may cause enamel surface loss primarily at the adhesive-enamel interface. The purpose of the present study was to evaluate by means of shear bond strength (SBS), adhesive remnant index (ARI), roughness before and after po.