Orientador: Inez Valeria Pagotto Yoshida / Tese (doutorado) - Universidade Estadual de Campinas, Instituto de Quimica / Made available in DSpace on 2018-08-03T12:10:42Z (GMT). No. of bitstreams: 1 Schiavon_MarcoAntonio_D.pdf: 4981766 bytes, checksum: 51310456b293a2887ba0d13a19ef723e (MD5) Previous issue date: 2002 / Doutorado

Orientador : Rachel Negrão Cavalcanti / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Geociencias / Made available in DSpace on 2018-08-03T14:44:10Z (GMT). No. of bitstreams: 1 Coimbra_MarcelideMenezes_M.pdf: 4854711 bytes, checksum: f5158aa4dc91efe776781588476394a6 (MD5) Previous issue date: 2003 / Resumo: Neste trabalho buscou-se apresentar, adaptar e aplicar o método denominado FMEA, verificando sua eficácia na avaliação da significância de impactos ambientais. Trata-se de uma etapa decisiva na implantação de um Sistema de Gestão Ambiental numa organização, uma vez que todas as demais etapas serão influenciadas por ela. Foram apresentados cinco casos bem sucedidos em que o FMEA adaptado foi aplicado em organizações de grande porte de diferentes segmentos industriais. Para cumprir com os demais objetivos da dissertação, uma adaptação do método foi testada em quatro indústrias cerâmicas de revestimento nas suas principais etapas de produção. Quanto aos resultados obtidos, o método demonstrou-se eficaz porque aponta com precisão o aspecto e o impacto ambiental associado, correspondendo respectivamente ao modo e efeitos da falha, permitindo a avaliação da significância dos impactos ambientais. Por outro lado, se não houver uma integração profissional responsável e perfeita sintonia de interesses, o resultado não será confiável, ocorrendo desvios de interesse. Os principais requisitos identificados, necessários à avaliação de impactos ambientais foram: motivação do mais alto cargo da empresa, envolvimento dos técnicos responsáveis por todos os setores relacionados com o meio ambiente e, principalmente, o comprometimento de todos através da sensibilização com programas de educação para todos os níveis de funcionários / Abstract: The aim of this work was to present, adapt and put into practice the method calIed FMEA, by checking its efficiency when evaluating the importance of environmental impacts. It is a decisive step in the implementation of a System of Environmental Management in an organization, since alI the folIowing phases wilI be affected by it. Five successful cases in wich FMEA was adapted and put into practice in large-scale organizations were presented. In order to reach the objectives established this dissertation, an adaptation of the method was tested in four ceramic tile industries in their main production phases. As for the obtained results, the method proved to be efficient because it shows, with precision, the relation the environmental aspect and impact have with the mo de and the effect of the failure presented, allowing the evaluation of the importance of the environmental impacts. On the other hand, if there is no professional and responsible integration of interests, the results wilI not be reliable, generating diversion of interests. The folIowing principal requisites were detected for an accurate evaluation of environmental impacts: the motivation of ranking members of the organization; the involvement of the technicians responsible for alI the areas related to environment; and mainly, everyone's commitment through environmental training and awareness programs for alI employees / Mestrado / Administração e Politica de Recursos Minerais / Mestre em Geociências

Orientador: Carlos Roberto de Souza Filho / Dissertação (mestrado) - Universidade Estadual de Campinas, Instituto de Geociencias / Made available in DSpace on 2018-08-03T17:53:29Z (GMT). No. of bitstreams: 1 Senna_JulianoAlvesde_M.pdf: 29384046 bytes, checksum: 502f53773f990894ceffb68e0c81d0b3 (MD5) Previous issue date: 2003 / Resumo: As argilas estão entre as mais importantes matérias primas devido as suas múltiplas funções industriais. No caso especial da indústria de cerâmica, as argilas têm ampla utilidade, sendo o principal produto para a fabricação de louças, porcelanas, revestimentos, entre outros. A caracterização de argilas, do ponto de vista químico, fisico e tecoológico, é um requisito cada vez mais necessário. Entretanto, o planejamento de lavra sucinto, a falta de controle dos padrões requeridos pela indústria e a separação essencialmente subjetiva e empírica das argilas quanto ao uso, fazem com que muitos materiais química e tecnologicamente diferentes sejam classificados como semelliantes, com conseqüências danosas para a extração e industrialização da matéria prima. Considerando as complexidades envolvidas na caracterização de argilas de utilização na indústria cerâmica por métodos convencionais, esta pesquisa objetivou (i) avaliar o potencial da espectroscopia de reftectância como um método aplicável de forma expedita na defmição de tipos e de pureza de argilas; (ii) determinar parâmetros espectrais que possam subsidiar a classificação de argilas quanto ao uso na indústria, com ênfase nos materiais apropriados para a produção de cerâmica de revestimentos e louça sanitária. Dois jazimentos de argila foram estudados: um primeiro, fonte de matéria prima para indústria de revestimentos cerâmicas, explorado pela Mineração Cruzeiro, em Limeira (SP); e outro, fonte de matéria prima para a indústria de porcelana e louça sanitária (incluindo argilas do tipo ball clay), explorado pela Mineração Mateus Leme, em São Simão (SP). A Mina de Cruzeiro compreende rochas ricas em argila das Formações Irati, Serra Alta, Corumbataí e Serra Geral (Bacia do Paraná), tendo o horizonte Corumbataí como principal fonte de matéria prima. Com base em métodos e dados obtidos por espectroscopia de reftectância, foi possível construir uma coluna 'espectro-litológica', onde cada compartimento (Formação) e sub-compartimento (grupos da Formação Corumbataí) possui uma assinatura espectral caracteristica, a qual pode ser diretamente relacionada a uma determinada composição e uso (ou não) do material como matéria-prima na indústria cerâmica de revestimentos. No depósito de São Simão, a caracterização das argilas por espectroscopia de reftectância foi plena. Três tipos de argila, hospedados no aluvião do ribeirão Tamanduá, foram separados. Nas argilas brancas foi possível quantificar e detectar as porcentagens de caulinita e seu grau de criStalinidade, argilo-minerais expansivos e micas, e a lepidocrosita (inédita em depósitos aluvionares brasileiros). Nas argilas cinzas, também cauliníticas, a matéria orgânica tem intima relação com a presença dos argilo-minerais expansivos. As argilas marrons possuem a maior quantidade de caulinita e de variedades bem estruturadas e cristalinas; os argilo-minerais expansivos ocorrem numa proporção ideal em relação a caulinita, conferindo maior plasticidade geral ao material; a siderita, identificada pela primeira vez no aluvião, também é comum nessas argilas. Cada grupo de argilas caracterizadas no depósito de São Simão como distintas do ponto de vista espectral, coincidentemente tem uma aplicação específica na indústria de cerâmica fina. Considerando o caráter exploratório desta pesquisa, que buscou, aparentemente pela primeira vez, utilizar a espectroscopia de reftectância e técnicas relacionadas para caracterização de argihls empregadas como matéria-prima na indústria cerâmica, os resultados foram muito promissores / Abstract: Clays are among the ver)' important primary, raw materiais due to their broad spectrum uses in the industIy. In the specific case of the ceramic industl)', cIays are used in many fields, incIuding the manufacturing of porcelains, pottery, chimney-flue tile, roofing tile, conduit, light-weight aggregate, floor tile, sewer pipe, drain tile and so on. The characterization of cIays from the physical, chemical, and ceramic standpoint in pre- and -within mining stages is a must in modero industry. However, succinct mining planning, lack of industry-oriented standards and the usual bond to empirical discrimination of clays as regards their use, put chemically and technologically different materiais as similar standards, with serious consequences to the mining and manufacturing industry. Considering the intrinsic complexities involved in characterizing ceramic industry-aimed materiais by conventional methods, this works aims: (i) to evaluate the potential of reflectance spectroscopy as a relevant, expedite method to define types and purity of cIays; (ii) to study the possibility to relate cIays' spectral variables and parameters to their specific uses in the ceramic industIy, with emphasis on the materiais employed in the manufacturing of porcelains and floor tiles. T wo cIay deposits were investigated in this study: One, named 'Cruzeiro', is located in Limeira (São Paulo) , and is a source of cIays to the tile industIy; the other, named São Simão, is located in the analogous town, hosts important ball cIay-type deposits and it is an important source of primary materiais to the porcelain industIy. The Cruzeiro deposit comprises cIay-rich sediments of the Irati, Serra Alta and Corumbataí Formations (paraná Basin stratigraphic units), although the Corumbataí strata are the main source of clays. Using reflectance spectroscopy methods and data, it was possible to built a 'spectro-lithological' column, where every compartment (Formation) and sub-divisions of the Corumbataí Formation show an unambiguous spectral signature. This signature can be directly related to cIay composition and possible uses (or not) for these cIays in the tile manufacturing industry. The São Simão days are associated to the Tamanduá river alluvium deposits, where three types of cIays were spectrally distinguished on the basis of reflectance spectroscopy methods and data. The white cIays comprise kaolinite with several degrees of crystallinity, expansive cIay mineraIs, micas and lepidocrosite (an unique fmding in Brazilian alluvium deposits). The gray cIays, also kaolinite-rich, display an intrinsic relation between organic matter and expansive cIay minerais. The brown cIays show the highest content of well-ordered, highly crystalline kaolinites; they contain expansive cIay minerais, which occur in an ideal proportion to kaolinite, conferring more plasticity to the cIays; and they also host some amounts of siderite (first time found in this alluvium). Each ofthese cIay groups characterized in the São Simão deposit coincidentally has a specific application in the fine ceramics industry. In view of the exploratory nature of this research, the results using reflectance spectroscopy to characterize particular industIy-aimed cIays proved very promising. / Mestrado / Metalogenese / Mestre em Geociências

Orientador: Alvaro Della Bona, Altair A. Del Bel Cury / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T13:44:44Z (GMT). No. of bitstreams: 1 Boscato_Noeli_D.pdf: 1647960 bytes, checksum: 3d012e02dce78a5277da1ede4cc574e4 (MD5) Previous issue date: 2005 / Resumo: Este estudo avaliou o efeito do tratamento de superfície na resistência adesiva à tração (s) entre resina e as cerâmicas IPS Empress®(E1) e VITAVM7®(V7) e o modo de falha nessa interface adesiva. A metodologia proposta teve por finalidade testar a hipótese de que a s entre resina e cerâmica é controlada pelo tratamento de superfície das cerâmicas. Foram confeccionados 10 blocos de uma cerâmica a base de leucita, (E1) e de uma cerâmica feldspática com duas fases vítreas (V7), que foram polidos até a granulação de 1 µm. Os blocos de cada cerâmica foram divididos aleatoriamente em dois grupos e tiveram suas superfícies tratadas como segue (n=5): Grupos E1HF e V7HF: aplicação de ácido hidrofluorídrico a 9,5% (HF - Ultradent) aplicado por 60 s; Grupos E1CS e V7CS: jateamento com partículas de alumina modificadas por sílica (CS ¿ Cojet System, 3M-Espe), aplicado por 15 s. As superfícies cerâmicas tratadas foram lavadas, secadas e o silano foi aplicado deixando-o evaporar. Aplicaram-se duas camadas finas de adesivo (Single Bond, 3M), seguido da aplicação de camadas de 2 mm de resina composta (Z250, 3M), que foram fotopolimerizadas durante 40 s cada uma. Os blocos cerâmica-adesivo-resina composta foram seccionados em dois eixos, x e y, obtendo-se corpos-de-prova em forma de barras (n=30), com área adesiva média de 1,04 mm2. Os corpos-de-prova foram armazenados em água destilada a 37°C por uma semana antes do teste de tração em uma máquina de ensaios universal com velocidade de carga de 1.0 mm.min-1, seguido da análise microscópica da superfície fraturada. A análise estatística foi realizada pela análise de variância, teste de Tukey (a=.01) e análise de Weibull. As médias e desvio padrão da s (MPa) foram: E1HF: 29,8±4,5(a); E1CS: 24,6±5,6(b); V7HF: 22,3±4,0(b); V7CS: 15,7±6,9(c). Os valores médios de s do Grupo E1HF foram significativamente maiores que os valores médios dos demais grupos (p=0,0001). As duas cerâmicas apresentaram valores médios de s significativamente maiores quando tratadas com HF do que com CS (p=0,0001). Todas as fraturas ocorreram dentro da zona adesiva. O módulo de Weibull (m) foi mais alto para o Grupo E1HF (7,66), e o Grupo V7CS mostrou o valor mais baixo de m (2,54). Os resultados confirmam a hipótese inicial de que a s da resina à cerâmica é controlada, primariamente, pelo tratamento de superfície do material cerâmico / Abstract: This study evaluated the effect of ceramic surface treatments on tensile bond strength (s) and the mode of failure of a resin bonded to two types of ceramics, testing the hypothesis that s of ceramics to resin is controlled by the ceramic surface treatment. Methods: Ten blocks of each the hot-pressed leucite-based ceramic (E1- IPS Empress) and the two-phase glassy feldspathic ceramic (V7-VITAVM7) were fabricated, polished through 1 µm alumina abrasive, and divided into two groups per ceramic (n=5): Groups E1HF and V7HF, 9.5% hydrofluoric acid (HF) was applied for 60 s; Groups E1CS e V7CS, silica coating (CS) using Cojet System (3M-Espe) for 15 s. The treated ceramic surfaces were washed and dried. Silane was applied and let to evaporate. An adhesive resin (Single Bond, 3M) followed by a resin composite (Z250, 3M) were applied on the ceramic treated surfaces and light cured. The composite-ceramic blocks were cut to produce bar-shaped specimens with a mean bonding area of 1.04 mm2 (n=30). Specimens were stored in 37°C distilled water for 1 week before tensile loading to failure in a universal testing machine with cross-head speed of 1.0 mm.min-1. Fracture surfaces were examined under scanning electron microscope (SEM). Results were statistically analyzed using one way ANOVA, Tukey¿s test and Weibull analyses. Results: Mean s and standard deviation (MPa) values were as follows: E1HF: 29.8±4.5(a); E1CS: 24.6±5.6(b); V7HF: 22.3±4.0(b); V7CS: 15.7±6.9(c). Mean s value of Group E1HF was statistically higher than the other Groups mean values (p=0.0001). HF treatment produced significantly higher mean s value than CS treatment, independent of the ceramic material (p=0.0001). All fractures occurred within the adhesion zone. E1HF showed the highest Weibull modulus (m) value (7.66) and V7CS exhibited the lowest m value (2.54). Conclusion: Results confirmed the testing hypothesis that s of ceramics to resin is controlled primarily by the ceramic surface treatment / Doutorado / Protese Dental / Doutor em Clínica Odontológica

Banca: Álvaro de Souza Dutra / Banca: Denis Dalmazi / Banca: José Abdalla Helayel Neto / Banca: Dionísio Bazeia / Banca: Vilson Zanchin / Resumo: O objetivo central desta tese foi obter sistemas cerâmicos com estruturas perovskitas ferroelétricos e multiferróicos do tipo Bi4Ti3O12, BiFeO3, PZT, CaBi2Nb2O9 e observar a influencia dos métodos químicos de processamento na capacidade de formador da rede cristalina atuar na estabilidade dos complexos polióxidos. Para esse propósito, cerâmicas e filmes finos com composição complexa foram estudados e permitiram respostas elétricas que demonstram sem dúvida o avanço da tecnologia em eletroeletrônica e como guias de onda planar. O método dos precursores poliméricos que considera a capacidade de fixar metais de forma que estes utilizem sua memória química foi elucidado. Avanços consideráveis foram alcançados na formação de fases como Bi4Ti3O12, BiFeO3, PZT, CaBi2Nb2O9 sem a cristalização de fases deletérias, livre de aglomerados, distribuição homogênea do tamanho de partículas, elevada pureza e cristalinidade. Vale destacar que a concentração dos reagentes formadores da cadeia polimérica, a temperatura de decomposição e a atmosfera utilizada durante a combustão do polímero determinam a reatividade dos óxidos dos metais que se formam inicialmente complexados. Em específico para os pós cerâmicos, o controle da cristalização das fases secundárias e da morfologia permite ampliar o universo de aplicação dos desde sua compactação e sinterização em temperaturas menores com menor variação da estequiometria até sua aplicação em filmes espessos, capacitores, catalisadores, sensores, etc. Para obtenção de filmes finos por métodos químicos, por dip-coating ou spin-coating, um número muito grande de variáveis devem ser controlados como: composição, concentração, viscosidade, temperatura e tempo de tratamento do filme. As características das soluções são determinantes na morfologia, superfície,... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The main goal of the present work was to obtain ceramic systems with perovskite structure based on Bi4Ti3O12, BiFeO3, PZT, CaBi2Nb2O9 with ferroelectric and multiferroic properties and observe the influence of chemical processing methods in the capacity of the crystal lattice network providing stability of polyoxides complex. For this purpose, ceramics and thin films with complex composition were studied and allowed electrical responses that demonstrate the technology advances in electroeletronics and as planar waveguides. The polymeric precursor method that considers the ability to fix metal using its chemical memory has been elucidated. Considerable advances have been achieved in the formation of Bi4Ti3O12, BiFeO3, PZT CaBi2Nb2O9 phases without deleterious phases crystallization, free from agglomerates, homogeneous distribution of particle size, high purity and crystallinity. It is noted that the concentration of the polymer chain forming reactants, the decomposition temperature and atmosphere employed during combustion of the polymer determine the reactivity of the metals oxides initially complexed. In particular for the ceramic powders, controlling the crystallization of secondary phases and the morphology allows to extend the application universe from compaction and sintering at lower temperatures with less variation in stoichiometry allowing its application in thick films, capacitors, catalysts, sensors, etc. To obtain thin films by chemical methods, by dip-coating or spin-coating, some variables must be controlled such as: composition, concentration, viscosity, temperature and time of annealing. The solutions characteristics are crucial in morphology, surface, density and crystallinity of the films. The advantage of this method is the possibility to work with a minimum concentration of additives in order to deposit layers ... (Complete abstract click electronic access below)

Orientador: Itamar Ferreira / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecanica / Made available in DSpace on 2018-07-20T17:22:08Z (GMT). No. of bitstreams: 1 LombelloNeto_Amador_M.pdf: 13040046 bytes, checksum: 21ff8ae12a614e317c6ef784acbe59d8 (MD5) Previous issue date: 1994 / Resumo: Barras de Si3N4 foram brasadas com liga de Ag-Cu-Ti em vácuo à temperatura de 855°C. por 10 min. Variou-se a espessura da camada de liga de brasagem entre 50 e 100um. Foram feitos, análise semi-quantitativa da região de junção para levantamento da distribuição dos elementos após brasagem, imagens de raio-X para mapeamento dos elementos, ensaio de flexão em 4 pontos e fractografia. Notou-se urna descontinuidade entre as camadas interfaciais metálicas na espessura de 100um. Observou-se que o cobre e a prata não reagem com a cerâmica, mas o metal ativo, neste caso o titânio, difunde-se quase por completo na região da interface metal/cerâmica, com brusca queda de concentração para distâncias maiores de 10um. da cerâmica, comprovando a eficiência do titânio na molhabilidade do substrato cerâmico. A existência de titânio em pontos distantes da interface, mesmo que em pequenas concentrações, leva a crer que o tempo de brasagem não foi suficiente para a difusão completa do elemento para a região da interface. Os ensaios de flexão foram realizados à temperatura ambiente e sem preparação dos corpos de prova pós-brasagem. Os níveis de resistência à flexão do material brasado foram da ordem de 50% da resistência da cerâmica monolítica. Partículas alongadas de nitreto de silício foram encontradas na região metálica da junção metal/cerâmica, estas partículas podem ser atribuídas a destacamentos na interface cerâmica no processo de brasagem, ou ainda, ao processo de polimento pós-brasagem. Imagens de raio-X mostram que a concentração de Ti nestas partículas é pronunciada / Abstract: Hot-pressed Si3N4 was joined using an active metal brazing filler metal at 1128 K (855°C) for 1O min. in vacuum for 2 different widths of metallic layer, 50 and 100um. A semi-quantitative analysis of joint region, X-ray images for mapping of elements, four-bend test and fractography have been done. The strength of the monolithic ceramic tested in the same apparatus of four-bend test has demonstrated values up to 200MPa at room temperature. The joint region was examined on a SEM on EDX mode. A discontinuity observed throughout the metallic layers suggests that pressure required to contact parts to be joined becomes very important when the process is based in a multi-layer metallic brazing filler. The 4 point bending tests were done without surface preparation. The copper and silver alloys do not react with the ceramic, but the active metal, titanium in this particular case, diffuse almost completely in the metal/ceramic interface region, varying greatly the concentration beyond 10um. of the ceramic interface within the metallic filler, evidencing the wettability of this element on the ceramic substrate. The existence of titanium in distant sites of the metal/ceramic interface, even in small concentrations, make believe brazing time was not enough to complete diffusion of the element to the interface's region. The results indicate a final joint strength values up to 50% of the monolithic one. Elongated particles of silicon nitride were found in the metallic region of the metal/ceramic joint. These particles could be attributed to detachment of Si3N4 from the ceramic interface in the brazing processo X-ray images show concentrations of Ti in these particles / Mestrado / Materiais e Processos de Fabricação / Mestre em Engenharia Mecânica

Orientador: Nivaldo Lemos Cupini / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Enge nharia Mecanica / Made available in DSpace on 2018-07-18T09:43:12Z (GMT). No. of bitstreams: 1 Costa_DalbertoDiasda_M.pdf: 2334002 bytes, checksum: 55b18c897a98d4f9761b97973158a9f6 (MD5) Previous issue date: 1993 / Resumo: Com as recentes melhorias em máquinas operatrizes e em materiais para ferramentas, a usinagem de materiais duros tem ganhado bastante interesse. Uma das metas mais importantes é a substituição da retificação pelo torneamento em operações de acabamento. Neste trabalho, estudou-se algumas características do torneamento de aços endurecidos (ABNT 52100 e ABNT M2), usando ferramentas cerâmicas e de PCBN. Vários experimentos foram delineados com objetivo de analisar o comportamento da rugosidade superficial, das componentes da força de usinagem e da potência de corte. Além disso, observou-se a deterioração da ferramenta e o tipo de cavaco formado. Encontrou-se que o torneamento de aços endurecidos é possível do ponto de vista tecnológico. O nível de rugosidade superficial obtido é similar ao do processo de retificação. / Abstract: Nowadays, with machine and tool material developments, there has been great interest on machining of hard materials. The most important target is to replace grinding by turning in finishing operations. In this work, some characteristics of hardened-steel turning (AISI 52100 and AISI H2), using ceramic and PCBN tools were studied. Experimental sets were designed to analyse surface roughness, cutting forces and cutting power behavior. Furthermore, tool deterioration and chip type were observed. It was found that turning of hardened steels is possible from technological point of view. The surface roughness is similar to that obtained in grinding processes. / Mestrado / Mestre em Engenharia Mecânica

Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:20:00Z (GMT). No. of bitstreams: 1 Guarda_GuilhermeBottene_D.pdf: 4899722 bytes, checksum: 60f4ee7ca07e4f49067ebdc1fbe3d374 (MD5) Previous issue date: 2015 / Resumo: O objetivo neste estudo foi avaliar a dureza Vickers, resistência à flexão biaxial, análise microestrutural e transmissão da luz da cerâmica vítrea prensada por calor após repetidas re-prensagem. Discos de cerâmica de IPS e.max Press (12,0 mm de diâmetro x 0,9 mm de espessura) foram prensadas e usadas como grupo controle (TP1). Sprues e botões cerâmicos restantes da primeira prensagem foram reaproveitados e utilizados para confecionar os grupos testes de re-prensagem (TP2 e TP3). Todos os procedimentos das termoprensagens foram feitas de acordo com as recomendações do fabricante. O teste de resistência à flexão biaxial (BFS) foi realizado para determinar a resistência dos discos cerâmica vítrea prensada (TP1) e re-prensada (TP2). Doze amostras por grupo (n=12) foram testadas, com velocidade de aplicação de carga de 0,5 mm/min., na máquina de ensaio universal (Instron). Para o teste de dureza Vickers foi realizado em um mucrodurômetro HMV 2 (Shimadzu) com carga de 500 gf por 15 segundos. Dez discos de cerâmica vítrea foram foram confeccionadas para primeira prensagem (TP1) e dez para cada reprensagem (TP2 e TP3), realizando 5 endentações por amostras. As características de superfície foram analisadas em MEV. Características de irradiancia e de espectro de luz transmitida através da cerâmica foram medidos utilizando-se um medidor de energia e um espectrômetro de luz. Os dados foram submetidos à analise de variância e teste de Tukey post-hoc (p <0,05). Os valores BFS em MPa (média e desvio-padrão) foram para TP1 (279,7 ±12,5), para TP2 (230,3 ±7,1) e para TP3 (220,8± 8,6). Os valores de TP1 foram significativamente maiores que os grupos TP2 e TP3. Os valores de dureza Vickers foram para TP1 (638,1 ±11,5), para TP2 (592,6± 6,6) e para TP3 (590,4 ±7,6). A dureza de TP1 foi significativamente maior que os grupos TP2 e TP3. As micrografias do material cerâmico em MEV mostrou aumento no tamanho e concentração dos cristais de disilicato de lítio (LeDiSi) após re-prensagem. A análise das imagens, re-prensagem mostrou homogeneidade na distribuição dos cristais de disilicato de lítio e aumento na densidade dos cristais. Redução na transmissão da luz foi detectada com aumento da espessura da cerâmica, alterações na emissão foi observada após repetidas prensagens. Conclui-se que a reutilização de material em repetidas re-prensagens diminuiu significativamente as propriedades de resistência à flexão biaxial e a dureza da cerâmica reforçada por di-silicato de lítio IPS e.max Press, alterou a microestrutura e influenciou na transmissão da luz através da cerâmica / Abstract: The aim of this study was to evaluate the Vickers hardness, biaxial flexural strength, microstructural analysis and light transmission of heat-pressed glass-ceramic material after repeated pressing. Ceramic discs of IPS e.max Press (12.0 mm in diameter x 0.9 mm thickness) were heat-pressed and used as control (HP1). Sprue and button parts of the heat-pressed material were retrieved and used for repeated heat-pressing to construct discs of two and three re-pressed groups (HP2 and HP3). All the heat-pressed casting procedures were performed according to the manufacturers' instructions. A biaxial flexural strength (BFS) test was performed to determine the strength of pressed (HP1) and re-pressed (HP2 and HP3) glass-ceramic disc specimens (n = 12) at a crosshead speed of 0.5 mm/min., in the universal testing machine (Instron). Vickers hardness test was conducted in a microhardness tester HMV-2 (Shimadzu) with a load of 500 g applied for 15 s. Ten glass-ceramic discs were made for pressed (HP1) and ten for re-pressed (HP2 and HP3) and five indentations were made for each disc. Surface characteristics were examined with SEM. Light irradiance and spectrum characteristics transmitted through ceramic were measured using a power meter and a light spectrometer. Data were submitted to ANOVA and Tukey¿s post-hoc test (p<0.05). The BFS values in MPa (mean ± standard deviation) were HP1 (279.7±12.5); HP2 (230.3±7.1) and HP3 (220.8±8.6). HP1 was significantly higher than HP2 and HP3. The VH values were HP1 (638.1±11.5); HP2 (592.6±6.6) and HP3 (590.4±7.6). HP1 was significantly higher than HP2 and HP3. In conclusion, repeated heat-pressing treatment produce a statistically significant decreased in the biaxial flexural strength and Vickers hardness of the IPS e.max Press glass-ceramic, microstructural alterations and alterations in light transmission throughout ceramic discs / Doutorado / Materiais Dentarios / Doutor em Materiais Dentários

A dissertação apresentada compreende reflexões em torno do pote cerâmico relacionado à prática artística, tanto em meu processo de criação como na produção artística contemporânea. O pote no qual trabalho a minha poética parte da forma clássica da louçaria utilitária doméstica e é suporte para o desenvolvimento de uma prática em que ele se apresenta fora de sua aplicabilidade funcional ou de seu contexto original. A partir da forma da tigela, desenvolvo trabalhos através de múltiplos, uso recursos de impressões serigráficas e tipográficas e outras interferências, como o tricô, na tentativa de trazer outro olhar para o utensílio cerâmico. / The research presented includes discussions on the ceramic pot related to artistic practice, as in my creative process, as also in contemporary artistic production. The pot from my poetic work starts in the classical form of the domestic utilitarian pottery and its a support for the developing of a practice, where its shows outside of their applicability, function or original context. From the shape of the bowl I develop my work across multiples, I use resources of silk screen prints and others typographical interferences as knitting, trying to bring another look at the ceramic utensil.

Vitro-cerâmicas com propriedades ópticas não lineares tem despertado muito interesse em função do baixo custo, facilidade de manufatura e potencialidade de aplicações tecnológicas quando comparado aos monocristais. Vitro-cerâmica para aplicações em óptica não linear tem sido produzidas pela ceramização de vidros. Neste trabalho sintetizamos vidros dos sistemas oxifluoreto 40BaF2.(24-x)LiF.(36-x)NbO2.5.xLiNbO3 (% molar, 0<x<20), e borato de bário xB2O3.(100-x)BaO (% molar, 50<x<68) pelo método convencional de fusão e resfriamento. Posteriormente as amostras sofreram tratamento térmico para provocar uma cristalização controlada. O vidro de oxifluoreto de composição x=10 tem temperatura de fusão em torno de 550°C, e temperaturas características de transição vítrea (Tg), início de cristalização (Tx) e pico de cristalização (Tp) de 263, 355 e 368°C respectivamente. Essa amostra foi tratada termicamente a 290°C por tempos de 12, 24, 36 e 50 horas apresentando mecanismo de cristalização do tipo volumétrico. A evolução da fração cristalizada foi analisada por difratometria de raios-X e absorção no espectro infravermelho e radiação visível. A análise por difração de raios-X não indicou a presença de cristais com propriedades ópticas não lineares como LiNbO3 (LNB). Amostras vítreas do tipo borato de bário tem características ópticas excelentes e razoavelmente estáveis quanto a devitrifição, a ponto de permitir a manufatura de peças de 75 x 75 x 5mm de dimensão (60B2O3 - 40BaO). As temperaturas características para a amostra de composição 57B2O3-43BaO foram: Tg=570°C, Tc= 671°C, Tp = 685°C (± 2°C). As amostras tratadas termicamente a 610 e 620°C apresentaram mecanismo de cristalização do tipo superficial, tendo os filmes cristalinos espessuras de 110 e 220 m. O filme cristalino resultado da cristalização superficial foi caracterizado por difratometria de raios-X e identificado como -BaB2O4 (BBO). A vitro-cerâmica apresentou o fenômeno de geração de segundo harmônio (GSH) quando incidido sobre esta um feixe laser (Nd:YAG) de 1064nm de comprimento de onda e 1.1W de potência. A intensidade do sinal de GSH foi comparada ao sinal de uma lâmina de LiNbO3 monocristalino, de 1.6mm de espessura e cortado na direção z. A vitro-cerâmica apresentou um sinal de intensidade 12,5% da apresentada pela lâmina de LiNbO3. / We synthesized glasses of the oxyfluoride system 40BaF2(24-x)LiF.(36-x)NbO2.5.xLiNbO3 (% mol, 0<x<20) and the barium borate system xB2O3.(100-x)BaO (% moI, 50<x<68) by the conventional melting-quenching method. The samples obtained were thermally treated to provide a controlled crystallization. Among the oxyfluoride glasses, the sample with x=l0mol% showed the best properties. It melts at 550°C, and presents a characteristic temperature of glass transition at 263°C, a temperature of crystallization starting at 355°C and a peak of crystallization at 368°C. It was thermally treated at 290°C for 12, 24, 36 and 50 hours, and exhibited volumetric crystallization as verified under the optical microscope or even at naked eye. The evolution of the crystallization process in this sample was studied by X-ray diffractometry and IR-VIS spectroscopy. However, not any additional phase found was identified as LiNbO3. Among the barium borate glasses, the sample with x=57 mol% showed the best properties. It melts at 904°C, and presents a characteristic temperature of glass transition at 570°C, a temperature of crystallization starting at 671°C and a peak of crystallization at 685 ± 2°C. It was thermally treated at 610 and 620°C, and exhibited surface crystallization by forming layers of crystals with 110 and 220 microns of thickness, respectively. The crystals composition contained in these layers was identified as -Ba2BO4 by X-ray diffractometry. This sample showed second harmonic generation (SHG) when excited by a laser of wavelength of 1064 nm (Nd:YAG) and power of 1.1W. The intensity of the SHG signal detected in such a sample was 12.5% of the full SHG intensity observed from a standard plate of LiNb03 (thickness of 1.6 mm).