Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2014 / Made available in DSpace on 2015-02-05T20:18:07Z (GMT). No. of bitstreams: 1 329721.pdf: 4532649 bytes, checksum: 18cb60d2e542b0328ffc57d72577675e (MD5) Previous issue date: 2014 / O objetivo deste estudo in vitro foi de avaliar a microdureza e a alteração da cor de quatro cimentos resinosos, imersos em seis diferentes substâncias e por diferentes períodos de tempo. Sessenta discos de cimentos resinosos, foram confeccionados (6mm x 2mm), para cada tipo de cimento (Rely - X Veneer (R), Rely-X U200 (U) , Multilink (M) e o Variolink Veneer (V)) e polidos com ponta de borracha de passo único (Optrapol, Ivoclar Vivadent) por 30 s, em seguida armazenados por 24 hrs em água destilada. A subdivisão foi realizado em 6 subgrupos (n=10), de acordo com a solução imersora, a uma temperatura de 37ºC: Grupo R-1(Rely-X Veneer), Grupo M-1 (Multilink), Grupo V-1 (Variolink Veneer) e o Grupo U-1(Rely-X U200), foram armazenadas em água destilada (controle (1)). Grupo R-2, M-2, V-2 e U-2 em coca (2). Grupo R-3, M-3, V-3 e U-3 em vinho (3), Grupo R-4, M-4, V-4 e U-4 em suco cítrico (4), Grupo R-5, M-5, V-5 e U-5 em whisky (5) e Grupo R-6, M-6, V-6 e U-6 embebida energética (6). Os espécimes foram mesurados imediatamente, 24 hrs, 7, 14 e 90 dias, por um microdurometro (HMV 2, Shimadzu - Japão) e a cor avaliada por um espectrofotômetro (Easyshade, Vita). Para a análise estatística dos dados, foi empregada a análise de variância multiplas, (ANOVA) e o teste de tukey ao nível de 95% de confiança. Os maiores valores de microdureza foram obtidos no baseline, seguido de 7, 14 e 90 dias. Apenas não houve diferença estatisticamente significante entre os tempos de 24 horas, 7 e 14 dias(p>0,05). Para os valores de 90 dias, ocorreu uma queda acentuada dos valores para a microdureza. Quando observados os espécimes submersos em água, nota-se alteração no armazenamento de 90 dias, mas sem diferença estatística. O líquido que promoveu o maior índice de alteração de cor foi o vinho nos grupos: R3, M3, V3 e U3. Esses dados prevaleceram em todos os cimentos testados, a partir do 7° dia de armazenamento. O /\E, não foi alterado para os grupos, que foram imersos em água. Os líquidos coca-cola, suco cítrico, whisky e energético, tiveram alteração significativa aos 90 dias de armazenamento. O grupo que apresentou a menor variação após os 14 dias foi o cimento resinoso Rely - X Veneer, porém sem diferença estatística. As substâncias nas quais os cimentos resinosos foram imersos, apresentaram influência na microdureza superficial e na cor para todos os cimentos testados, diminuindo a estabilidade de cor e a dureza em períodos mais longos.<br> / Abstracts: The aim of this in vitro study was to evaluate the microhardness and color change four resin cements immersed in six different substances and for different periods of time. Sixty discs of resin cements were cut (6mm x 2mm), for each type of cement (Rely X -Veneer (R), Rely-X U200 (U), Multilink (M) and Variolink Veneer (V)) and polished rubber tipped single step (Optrapol, Ivoclar Vivadent) for 30 s, then stored for 24 hrs in distilled water. The subdivision was carried out in six subgroups (n = 10) according to imersora solution at a temperature of 370C: R 1-group (Rely-X Veneer)-1 Group M (Multilink), GroupV-1 (Variolink Veneer) and the U-1 group (Rely-X U200) were stored in distilled water(control) (1). Group R-2, M-2, M-2 and U-2 cocaine (2). Group R-3, M-3, M-3 and H-3 'wine(3)-R 4 group, M-4, M-4 and U-4 as citric juice (4)-R 5 group, M-5, M-5 and H-5 whiskey (5)group R-6, F-6, V-6 and U-6 in the energy drink (6). The specimens were immediately mesurados, 24 hrs, 7, 14 and 90 days, by a microhardness (HMV 2, Shimadzu - Japan) and the color measured by a spectrophotometer (Easyshade, Vita). For statistical analysis, we used the multiple analysis of variance (ANOVA) and Tukey's test at 95% confidence.The highest microhardness values were obtained at baseline, followed by 7, 14 and 90 days. As there was no statistically significant difference between the times of 24 hours, 7 and 14 days (p> 0.05). For values of 90 days, there was a sharp decline in values for microhardness. When observing the specimens submerged in water, there is change in storage of 90 days, but no statistical difference. The liquid that promoted the highest rate of color change was the wine groups: R3, M3, V3 and U3. These data prevailed in all cements tested, from the 7th day of storage. The /\E, has not changed for the groups, which were immersed in water. Net cola, citrus juice, whiskey and energetic, had significantly after 90 days of storage change. The group that had the lowest variation after 14 days was the resin cement Rely X - Veneer, but without significant differences.

BEZERRA, Daniela da Silva. Efeito de sistema adesivo e de dentifrício fluoretados no desenvolvimento de cárie ao redor de restaurações com e sem fenda marginal em esmalte e dentina : estudo in situ. 2010. 56 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2010. / Submitted by denise santos (denise.santos@ufc.br) on 2011-12-06T13:11:55Z No. of bitstreams: 1 2010_dis_dsbezerra.pdf: 994675 bytes, checksum: 7baa7ae43392863a9549272d083a84cc (MD5) / Approved for entry into archive by Eliene Nascimento(elienegvn@hotmail.com) on 2012-02-01T12:14:40Z (GMT) No. of bitstreams: 1 2010_dis_dsbezerra.pdf: 994675 bytes, checksum: 7baa7ae43392863a9549272d083a84cc (MD5) / Made available in DSpace on 2012-02-01T12:14:40Z (GMT). No. of bitstreams: 1 2010_dis_dsbezerra.pdf: 994675 bytes, checksum: 7baa7ae43392863a9549272d083a84cc (MD5) Previous issue date: 2010 / Secondary caries may be developed between tooth and restoration when marginal gaps are present, however this process could be inhibited by fluoride presence. This research had as the main objective to evaluate, in situ, through a randomized, split-mouth and double-blind, cross-over design, the influence of fluoride from self-etching adhesive systems or dentifrice on the secondary caries development on enamel and root dentine around composite resin restorations with or without marginal gaps. During two phases, of 14 days each, 16 volunteers wore intraoral palatal devices containing 4 human dental slabs composed by a portion of enamel and dentine, restored with Z-250 composite resin. The slabs were randomly divided among 8 experimental groups for each substrate (enamel and dentine) restored with one of the following adhesive: All Bond SETM (no fluoride - NFA) and One Up® Bond F Plus (fluoride - FA) with (G+) or without (G-) the presence of marginal gaps and the use of fluoride dentifrice (FD) or placebo (PD). The restoration procedures were made following the manufacturers instructions and the gap was induced with the use of metallic strips. Each volunteer was instructed to drop on the slabs a 20% sucrose solution 10x/day and use the standardized dentifrice 3x/day. By the end of each clinical phase, the dental slabs were removed and the biofilm was collected for total microorganisms, mutans streptococci and lactobacilli counting, as well as for analysis of fluoride quantity present. The mineral loss was analyzed by microhardness test in a longitudinal cut on enamel and dentine. The lesion depth and presence of the wall lesion were determined by polarized light microscopy. The results were analyzed by ANOVA, following a factorial delineation of 2x2x2. The fluoride from the adhesive did not provide any protection against secondary caries development for enamel and dentine and for none of the studied response variables (p > 0.05). The fluoride from the dentifrice showed a little protection for demineralization in dentin (p<0.05). There was more wall lesion presence, either on enamel or on dentine (p < 0.05), on restorations with gap irrespective of fluoride presence. However, on gap restorations, a bigger depth of lesion was observed only on dentine (p < 0.05). These results suggest that the fluoride from the adhesive was not able to inhibit demineralization around restorations, even in the fluoride dentifrice presence. Nevertheless, the presence of a visible gap affects the secondary caries development, mainly on root dentine, increasing the progression of caries disease. / Cáries secundárias podem desenvolver-se na interface dente-restauração diante da presença de fendas marginais, mas este processo poderia ser inibido pela presença de flúor. Esta pesquisa teve como objetivo avaliar, in situ, através de um delineamento cruzado, aleatorizado, boca dividida e duplo-cego, a influência do flúor proveniente de sistema adesivo autocondicionante ou dentifrício no desenvolvimento de cárie secundária em esmalte e dentina radicular ao redor de restaurações de resina composta com ou sem fenda marginal. Durante duas fases de 14 dias, 16 voluntários utilizaram dispositivos intra-orais palatinos contendo 4 blocos de dente humano compostos por uma porção de esmalte e dentina e restaurados com resina composta FiltekTM Z-250. Os blocos foram aleatoriamente divididos em 8 grupos experimentais para cada substrato (esmalte e dentina) restaurado com um dos seguintes adesivos: All Bond SETM (não fluoretado - ANF) e One Up® Bond F Plus (fluoretado - AF), com a presença de fendas marginais (G+) ou não (G-), e com o uso de dentifrício fluoretado (DF) ou placebo (DP). Os procedimentos restauradores foram realizados seguindo as instruções dos fabricantes e a fenda foi criada com a utilização de matrizes metálicas. Cada voluntário foi instruído a gotejar sobre os blocos uma solução de sacarose a 20%, 10 vezes ao dia e a usar o dentifrício padronizado 3 vezes ao dia. Ao final de cada fase clínica, os blocos dentais foram removidos e o biofilme foi coletado para a contagem de estreptococos do grupo mutans, lactobacilos e microrganismos totais, assim como para a análise da quantidade de flúor presente. A perda mineral foi analisada pelo teste de microdureza em corte longitudinal no esmalte e na dentina. A profundidade da lesão e a presença de lesão da parede foram determinadas por microscopia de luz polarizada. Os resultados foram analisados por análise de variância (ANOVA) seguindo um delineamento fatorial 2x2x2. O flúor do adesivo não ofereceu proteção contra o desenvolvimento de cárie secundária em esmalte e dentina para nenhuma das variáveis de resposta estudadas (p > 0,05). O flúor do dentifrício mostrou leve proteção contra a desmineralização em dentina (p < 0,05). Houve uma maior presença de lesão de parede, tanto em esmalte quanto em dentina (p< 0,05), em restaurações com fenda independente da presença de flúor. No entanto, em restaurações com fenda, uma maior profundidade de lesão foi observada em dentina (p <0,05). Estes resultados sugerem que o flúor do adesivo não foi capaz de inibir a desmineralização ao redor de restaurações mesmo com a presença de flúor no dentifrício. No entanto, a presença de fenda visível afeta o desenvolvimento de cárie secundária, principalmente na dentina radicular, aumentando a progressão da lesão cariosa.

MORAES, Maria Denise Rodrigues. Efeito do envelhecimento de restaurações de cimento de ionômero de vidro na desmineralização do esmalte e dentina : estudo in situ. 2010. 50 f. Dissertação (Mestrado em Odontologia) - Universidade Federal do Ceará. Faculdade de Farmácia, Odontologia e Enfermagem, Fortaleza, 2010. / Submitted by denise santos (denise.santos@ufc.br) on 2011-12-14T14:06:46Z No. of bitstreams: 1 2010_dis_mdrmoraes.pdf: 1564067 bytes, checksum: 603263b0b3fe63d6e904c14de20300c3 (MD5) / Approved for entry into archive by Eliene Nascimento(elienegvn@hotmail.com) on 2012-02-01T14:07:06Z (GMT) No. of bitstreams: 1 2010_dis_mdrmoraes.pdf: 1564067 bytes, checksum: 603263b0b3fe63d6e904c14de20300c3 (MD5) / Made available in DSpace on 2012-02-01T14:07:06Z (GMT). No. of bitstreams: 1 2010_dis_mdrmoraes.pdf: 1564067 bytes, checksum: 603263b0b3fe63d6e904c14de20300c3 (MD5) Previous issue date: 2010 / The beneficial of resin modified glass ionomer cement (RMGIC) restorations in caries inhibition may be questioned due to F-dentifrice use and ageing of the restorations. Objective: To evaluate the effect of an ageing process on caries around cemento-enamel junction restorations in the presence of fluoride from RMGIC or dentifrice. Methods: A randomized double-blind crossover in situ study was performed in 2 phases of 14 days. Sixteen volunteers wore palatal devices containing dental slabs restored with composite resin (CR) or RMGIC, either aged or unaged. The slabs were exposed to a 20% sucrose solution, 10x/day and the volunteers used a non-F or an F-dentifrice 3x/day. The biofilm formed over the slabs was analyzed to determine the counts of total streptococci, mutans streptococci and lactobacilli as well as F-concentration. Results: Enamel demineralisation was determined by cross-sectional microhardness (CSMH) at the margin of the restoration. Kruskal–Wallis and factorial ANOVA, followed by Tukey test, were used to data evaluation (p<0.05). No statistically significant differences were found in the cariogenic microbiota. F-concentration in biofilm was higher for RMGIC restorations. For enamel, higher demineralization around CR restorations was observed regardless dentifrice or ageing process. For dentine, higher demineralization was observed around aged RC restorations without F-dentrifice use. Conclusions: These results suggest that RMGIC restorations provided protection against secondary caries either for enamel and dentine, while ageing process affects caries development in dentine, increasing caries progression. / O benefício de restaurações de cimento de ionômero de vidro modificado por resina (RMGIC) na inibição de cáries pode ser questionado na presença de dentifrício fluoretado e de restaurações envelhecidas. Objetivo: Avaliar o efeito do processo de envelhecimento em cáries ao redor de restaurações na junção amelo-cementária, na presença de flúor proveniente de RMGIC ou dentifrício. Métodos: Um estudo in situ randomizado duplo cego e cruzado foi realizado em duas fazes de 14 dias. Desesseis voluntários utilizaram um dispositivo intraoral contendo blocos de dentes restaurados com resina composta (CR) ou RMGIC, tendo sofrido ou não o processo de envelhecimento. Os blocos foram expostos a uma solução de 20% de sacarose, 10x/dia e os voluntários usaram dentifrício com ou sem flúor 3x/dia. O biofilme formado sobre os blocos foi analizado para determinar a contagem de streptococos totais, estreptococos mutans e lacatobacilos, assim como a concentração de flúor. Resultados: A desmineralização do esmalte foi determinada por meio de microdureza longitudinal na margem da restauração. Foram utilizados os testes de Kruskal–Wallis e ANOVA fatorial, seguidos pelo teste de Tukey (p<0.05). Não foram encontradas diferenças estatisticamente significantes na microbiota cariogência. A concentração do flúor no biofilme foi maior para restaurações de RMGIC. Para o esmalte, independente do uso do dentifrício ou do processo de envelhecimento, houve maior desmineralização ao redor de restaurações de CR. Para a dentina, na ausência do dentifrício fluoretado, houve maior desmineralização ao redor de restaurações de resina composta envelhecidas. Conclusão: Os resultados sugerem que restaurações RMGIC promovem proteção contra cárie em esmalte e dentina, enquanto que o processo de envelhecimento afeta o desenvolvimento de cárie em dentina, aumentando a progressão da cárie.

Submitted by Edileide Reis (leyde-landy@hotmail.com) on 2015-04-15T02:57:53Z No. of bitstreams: 1 PRISCILA COSTA CHAGAS.pdf: 600331 bytes, checksum: 2cfa257e41851f179ef6557ef8576b3d (MD5) / Made available in DSpace on 2015-04-15T02:57:53Z (GMT). No. of bitstreams: 1 PRISCILA COSTA CHAGAS.pdf: 600331 bytes, checksum: 2cfa257e41851f179ef6557ef8576b3d (MD5) Previous issue date: 2013 / O mecanismo de união entre os cimentos resinosos e a zircônia ainda não é bem definido na literatura. Devido à composição da zircônia, existe uma maior dificuldade destes cimentos em estabelecer uma interação química, conferindo um dilema clínico na Odontologia moderna. A adesão química, estabelecida pelos cimentos resinosos, é a maior responsável pela união com a zircônia se comparada aos tratamentos mecânicos; o que torna imprescindível a seleção do tipo de cimento. O objetivo deste trabalho foi realizar uma revisão de literatura referente à adesão dos cimentos resinosos à zircônia, enfatizando suas vantagens, composição, propriedades e tratamentos de superfície. Concluiu-se que, fatores que auxiliam na adesão e mecanismos de retenção micromecânica, são fundamentais para conferir uma união duradoura e resistente. Cimentos resinosos quimicamente ativados parecem ser mais indicados para cimentação em zircônia do que os cimentos duais. Já os cimentos auto-adesivos promovem resistência adesiva adequada à zircônia. Em relação aos tratamentos de superfície mecânicos, o jateamento com óxido de alumínio indica grande eficácia na descontaminação da cerâmica. Entretanto, para garantir uma maior resistência de união, alguns revestimentos podem ser utilizados previamente a silanização, como a aplicação de sílica.

Made available in DSpace on 2014-06-11T19:31:33Z (GMT). No. of bitstreams: 0 Previous issue date: 2000-10-10Bitstream added on 2014-06-13T20:41:58Z : No. of bitstreams: 1 silveira_ff_me_arafo.pdf: 343768 bytes, checksum: e3d592d429f09319f3775639ceb1eefb (MD5) / O objetivo do presente trabalho foi avaliar um novo cimento obturador de canal radicular denominado comercialmente de Sealer Plus, de acordo com as seguintes metodologias. 1. Avaliação histológica em dentes de cães, após período experimental de 90 dias. Foram utilizados 60 canais radiculares de pré-molares de cães com vitalidade, os quais, após preparo biomecânico, foram obturados pela técnica clássica complementada pela condensação lateral utilizando o cimento Sealer Plus, sendo que no Grupo I os canais radiculares receberam um curativo de demora à base de hidróxido de cálcio por 7 dias, no Grupo II um curativo à base da associação corticosteróide-antibiótico pelo mesmo período e no Grupo III não foi empregado o curativo de demora. Decorridos 90 dias da obturação, os animais foram sacrificados por sobredose anestésica, as maxilas e mandíbulas foram removidas e fixadas em formol a 10%, durante 48 horas. Após o processamento histológico de rotina, os cortes foram corados pela hematoxilina e eosina e pelo tricrômico de Mallory. A análise histopatológica evidenciou que o cimento Sealer Plus quanto à compatibilidade tecidual mostrou-se insatisfatório independente da utilização ou não do curativo de demora. 2. Avaliação da infiltração marginal apical in vitro. Foram utilizados 120 incisivos centrais superiores de humanos extraídos e divididos em quatro grupos de 20 dentes cada, e 3 grupos de 10 dentes usados como controle, os quais foram inicialmente instrumentados com limas tipo K até o no 30 no comprimento real do dente... / The scope of this work was to evaluate a new root canal filling Sealer Plus by using the following methods: 1. Histological evaluation of dog teeth. Experimental period of 90 days. In this experiment, 60 premolar with pulp vitality were used and after biomechanical preparation were filled by classic technique using Sealer Plus completed by lateral condensation; in Group I the root canals were filled with calcium hydroxide intracanal dressing during seven days, in Group II antibiotic/corticosteroid dressing during the same period and Group III without intracanal dressing, After a 90- day period, the animals were sacrificed by anesthethic overdose and had their maxillaries and mandibles removed. The removed parts were fixed in 10% formalin for 48 hours. Following a routine histological process, the cuts were stained by hematoxilin, eosin and Mallory Tricromic. The histopathological analysis showed that the Sealer Plus cement were unsatisfactory in relation to the tissue compatibility. 2. Evaluation of the marginal apical infiltration. In this experiment, 120 extracted top-central human incisors in 4 groups of 20 teeth were used and 3 group of 10 teeth used as control groups. The teeth were initially filed with K file up to the number 30 until apical patency and root canal prepared up to the number 50, using sodium hipochloride 0,5%, After that, the root canal were filled with Sealer Plus or Grossman cements, using or no calcium hydroxide intracanal dressing. After the fillings, the teeth were unpermeated in al their extension with nail polishing, except for 1 to 2 mm around the apical forame, submerged in 2% metilen blue colouring under vacuum conditions and fractured in such a way to obtain 2 sections. The colouring penetration was measured by a perilometer and the data, after statistical analysis, there was no difference between the groups.

Made available in DSpace on 2014-06-11T19:35:02Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-08-01Bitstream added on 2014-06-13T20:06:13Z : No. of bitstreams: 1 000757600.pdf: 2238658 bytes, checksum: e4af2fec93f2c954b6aa895e20cc674a (MD5) / O objetivo deste estudo foi avaliar a taxa de sobrevida, carga para fratura e distribuição de tensões de incisivos centrais e caninos superiores restaurados com facetas cerâmicas variando o desenho do preparo. Trinta incisivos centrais superiores e trinta caninos superiores (N=60) foram selecionados para o estudo. Os espécimes foram embutidos até 3 mm da junção cemento esmalte e o ligamento periodontal simulado usando um material a base de poliéter. Após essa etapa os espécimes foram randomizados em quatro grupos (n=15) de acordo com o desenho do preparo e o tipo de dente: Gr1- Incisivo central com preparo conservador; Gr2- Incisivo central com preparo convencional com chanfro palatino; Gr3- Canino com preparo conservador; Gr4 – Canino com preparo convencional com chanfro palatino. Os espécimes foram restaurados com facetas cerâmicas a base de di-silicato de lítio, obtidas pela técnica da injeção. Os espécimes foram submetidos à 4.106 ciclos mecânicos (45º, 37oC, 100 N, 4 Hz) e avaliados quanto a possíveis falhas a intervalos de 500.000 ciclos. Ao final da ciclagem mecânica os espécimes que sobreviveram foram submetidos ao teste de compressão. Modelos semelhantes aos utilizados no teste laboratorial foram simulados bi-dimensionalmente (Rhinoceros® 4.0) e o comportamento mecânico avaliado (MSC.Patrans 2005r2 e.MSC.Marc 2005r2) através dos valores de Tensão Máxima Principal. As taxas de sobrevida dos corpos de prova foram calculadas pelo teste de Kaplan Meier e Log-rank (α=0.05) e os valores de carga para fratura pelo teste T-Student (α=0.05). Todos os grupos apresentaram taxas de 100 % de sobrevida, não havendo diferença estatística entre eles. O teste T-Student não mostrou diferença estatística para os diferentes desenhos de preparo, mas mostrou diferença para os diferentes dentes submetidos ao mesmo desenho de preparo. O teste de elementos finitos... / The aim of this study was to evaluate the survival rate, load to fracture and tensile distribution of human central incisors and canines restored with ceramic veneers varying the prepare design. Thirty human central incisors and thirty canines (N=60) were selected for the study. The specimens were embedded with acrylic resin up to 3 mm of the cemento/enamel junction and the periodontal ligament was simulated with polyether. After this step the specimens were randomized in four groups (n=15), based on the tooth prepare design and type of teeth: Gr1- Central incisor with a conservative prepare; Gr2- Central incisor with conventional prepare with palatine chamfer; Gr3- Canine with conventional prepare; Gr4 - Canine with conventional prepare with palatal chamfer. The specimens were prepared, molded and models with rock stone type IV were obtained. Ceramic veneers (IPS e.max Press, Ivoclar Vivadent, Schann) were confectioned. The veneers were adhesively cemented on specimens. The specimens were submitted to mechanical cycling (45o, 37oC, 100 N, 4 Hz, 4.000.000 cycles) and evaluated at each 500.000 cycles to detect any kind of failure. Specimens that survive to mechanical cycling were submitted to fracture resistance test. Identical models were draw bi-dimensionally (Rhinoceros® 4.0) and the mechanical behavior were evaluated (MSC.Patrans 2005r2 e.MSC.Marc 2005r2) by Maximum Principal Stress. The survival rate were evaluated by Kaplan-Meier test (α=0.05), while load to fracture values was evaluated by T-Student test (α=0.05). All groups showed same values of survival rate (100%). Same teeth showed same values of fracture load, independently the design of prepare. Different teeth, showed differences in the fracture load, when submitted to same design prepare. The laminate veneer with the palatal chamfer design showed higher Maximum Principal Stress values

Made available in DSpace on 2015-06-17T19:34:04Z (GMT). No. of bitstreams: 0 Previous issue date: 2013-02-20. Added 1 bitstream(s) on 2015-06-18T12:47:30Z : No. of bitstreams: 1 000831085.pdf: 459011 bytes, checksum: 667fcb4731d7d180af7b8334427157eb (MD5) / O objetivo deste estudo foi avaliar a influência da diabetes mellitus na resposta tecidual e na capacidade de mineralização dos cimentos Sealapex®, MTA Angelus® e MTA Fillapex®. Vinte e quatro ratos Wistar foram divididos em dois grupos: diabéticos e não diabéticos. A indução de diabetes foi feita por meio da aplicação do Aloxano. Cada animal recebeu três implantes de tubos de polietileno contendo os materiais a serem testados e mais um tubo vazio como controle. Seis animais de cada grupo receberam injeções dos fluorocromos Calceína (7º dia), Alizarina (14o dias) e Oxitetraciclina (21o dias) durante a fase experimental. Os tempos operatórios foram 07 e 30 dias, quando os animais foram mortos e os espécimes processados para análise histológica de hematoxilina e eosina, Von Kossa, luz polarizada e fluorescência. Resultados: No 7o dia, observou-se uma resposta inflamatória moderada entre todos os grupos e no 30o dia, verificou-se uma resposta inflamatória leve. Ambos os grupos diabético e não diabético apresentaram, aos 07 e 30 dias, com todos os materiais testados áreas de mineralização e estruturas birrefringentes à luz polarizada. Sealapex® e MTA Fillapex® apresentaram uma maior intensidade de fluorescência do que MTA Angelus® (p <0,05) para todos os fluorocromos no grupo não diabético e somente para alizarina e oxitetraciclina no grupo diabético. Não houve diferença entre o Sealapex® e o MTA Fillapex® para nenhum fluorocromo independente da condição diabética. A intensidade de fluorescência não se alterou com nenhum material nos ratos diabéticos. Conclusão: A diabetes mellitus não interferiu na resposta tecidual e na capacidade de mineralização do Sealapex®, MTA Angelus® ou MTA Fillapex® / Objective: The aim of this study was to evaluate the influence of diabetes mellitus on tissue response and mineralization ability of Sealapex® MTA Angelus® and MTA Fillapex® sealers. Methods: Twenty-four Wistar rats were divided into two groups: diabetics induced by Alloxan and non-diabetics. The materials were placed in the polyethylene tubes and implanted into dorsal connective tissue of rats for 7 and 30 days. Six animals from each group received injection with calcein on day 7, alizarin on day 14 and oxytretacycline hydrochloride on day 21. The animals were killed after 7 and 30 days and the specimens were prepared for histologic analysis with hematoxylin and eosin, Von Kossa technique, and not stained for polarized light or fluorescence. Results: On 7 days, it was observed similar inflammatory reactions among all groups characterized by a moderate inflammatory response and on 30 days, it was found a mild inflammatory response. Both materials groups exhibited positive structures on Von Kossa and Polarized light analysis either on 7 and 30 days. Sealapex® and MTA Fillapex® showed more fluorescence intensity than MTA Angelus® (p<0.05) for all fluorochromes in non-diabetic group and for alizarin and oxytretacycline in diabetic group. It was not observed difference between Sealapex® and MTA Fillapex® for all fluorochromes independently on the diabetic condition. Fluorescence intensity was not changed with any material in diabetic rats. Conclusion: It was concluded that diabetes mellitus did not influence the tissue response or mineralization stimulated by Sealapex® or MTA Angelus® or MTA Fillapex®

Orientador: Marco Antonio Bottino / Co-orientador : Josete Barbosa Cruz Meira / Co-orientador : Luiz Felipe Valandro Soares / Banca: Renata Marques de Melo Marinho / Banca: Alexandre Luiz Souto Borges / Banca: Renata Faria / Banca: Carlos José Soares / Resumo: O objetivo deste estudo foi avaliar a taxa de sobrevida, carga para fratura e distribuição de tensões de incisivos centrais e caninos superiores restaurados com facetas cerâmicas variando o desenho do preparo. Trinta incisivos centrais superiores e trinta caninos superiores (N=60) foram selecionados para o estudo. Os espécimes foram embutidos até 3 mm da junção cemento esmalte e o ligamento periodontal simulado usando um material a base de poliéter. Após essa etapa os espécimes foram randomizados em quatro grupos (n=15) de acordo com o desenho do preparo e o tipo de dente: Gr1- Incisivo central com preparo conservador; Gr2- Incisivo central com preparo convencional com chanfro palatino; Gr3- Canino com preparo conservador; Gr4 - Canino com preparo convencional com chanfro palatino. Os espécimes foram restaurados com facetas cerâmicas a base de di-silicato de lítio, obtidas pela técnica da injeção. Os espécimes foram submetidos à 4.106 ciclos mecânicos (45º, 37oC, 100 N, 4 Hz) e avaliados quanto a possíveis falhas a intervalos de 500.000 ciclos. Ao final da ciclagem mecânica os espécimes que sobreviveram foram submetidos ao teste de compressão. Modelos semelhantes aos utilizados no teste laboratorial foram simulados bi-dimensionalmente (Rhinoceros® 4.0) e o comportamento mecânico avaliado (MSC.Patrans 2005r2 e.MSC.Marc 2005r2) através dos valores de Tensão Máxima Principal. As taxas de sobrevida dos corpos de prova foram calculadas pelo teste de Kaplan Meier e Log-rank (α=0.05) e os valores de carga para fratura pelo teste T-Student (α=0.05). Todos os grupos apresentaram taxas de 100 % de sobrevida, não havendo diferença estatística entre eles. O teste T-Student não mostrou diferença estatística para os diferentes desenhos de preparo, mas mostrou diferença para os diferentes dentes submetidos ao mesmo desenho de preparo. O teste de elementos finitos... / Abstract: The aim of this study was to evaluate the survival rate, load to fracture and tensile distribution of human central incisors and canines restored with ceramic veneers varying the prepare design. Thirty human central incisors and thirty canines (N=60) were selected for the study. The specimens were embedded with acrylic resin up to 3 mm of the cemento/enamel junction and the periodontal ligament was simulated with polyether. After this step the specimens were randomized in four groups (n=15), based on the tooth prepare design and type of teeth: Gr1- Central incisor with a conservative prepare; Gr2- Central incisor with conventional prepare with palatine chamfer; Gr3- Canine with conventional prepare; Gr4 - Canine with conventional prepare with palatal chamfer. The specimens were prepared, molded and models with rock stone type IV were obtained. Ceramic veneers (IPS e.max Press, Ivoclar Vivadent, Schann) were confectioned. The veneers were adhesively cemented on specimens. The specimens were submitted to mechanical cycling (45o, 37oC, 100 N, 4 Hz, 4.000.000 cycles) and evaluated at each 500.000 cycles to detect any kind of failure. Specimens that survive to mechanical cycling were submitted to fracture resistance test. Identical models were draw bi-dimensionally (Rhinoceros® 4.0) and the mechanical behavior were evaluated (MSC.Patrans 2005r2 e.MSC.Marc 2005r2) by Maximum Principal Stress. The survival rate were evaluated by Kaplan-Meier test (α=0.05), while load to fracture values was evaluated by T-Student test (α=0.05). All groups showed same values of survival rate (100%). Same teeth showed same values of fracture load, independently the design of prepare. Different teeth, showed differences in the fracture load, when submitted to same design prepare. The laminate veneer with the palatal chamfer design showed higher Maximum Principal Stress values / Doutor

Resumo: O objetivo do presente trabalho foi avaliar um novo cimento obturador de canal radicular denominado comercialmente de Sealer Plus, de acordo com as seguintes metodologias. 1. Avaliação histológica em dentes de cães, após período experimental de 90 dias. Foram utilizados 60 canais radiculares de pré-molares de cães com vitalidade, os quais, após preparo biomecânico, foram obturados pela técnica clássica complementada pela condensação lateral utilizando o cimento Sealer Plus, sendo que no Grupo I os canais radiculares receberam um curativo de demora à base de hidróxido de cálcio por 7 dias, no Grupo II um curativo à base da associação corticosteróide-antibiótico pelo mesmo período e no Grupo III não foi empregado o curativo de demora. Decorridos 90 dias da obturação, os animais foram sacrificados por sobredose anestésica, as maxilas e mandíbulas foram removidas e fixadas em formol a 10%, durante 48 horas. Após o processamento histológico de rotina, os cortes foram corados pela hematoxilina e eosina e pelo tricrômico de Mallory. A análise histopatológica evidenciou que o cimento Sealer Plus quanto à compatibilidade tecidual mostrou-se insatisfatório independente da utilização ou não do curativo de demora. 2. Avaliação da infiltração marginal apical in vitro. Foram utilizados 120 incisivos centrais superiores de humanos extraídos e divididos em quatro grupos de 20 dentes cada, e 3 grupos de 10 dentes usados como controle, os quais foram inicialmente instrumentados com limas tipo K até o no 30 no comprimento real do dente... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The scope of this work was to evaluate a new root canal filling Sealer Plus by using the following methods: 1. Histological evaluation of dog teeth. Experimental period of 90 days. In this experiment, 60 premolar with pulp vitality were used and after biomechanical preparation were filled by classic technique using Sealer Plus completed by lateral condensation; in Group I the root canals were filled with calcium hydroxide intracanal dressing during seven days, in Group II antibiotic/corticosteroid dressing during the same period and Group III without intracanal dressing, After a 90- day period, the animals were sacrificed by anesthethic overdose and had their maxillaries and mandibles removed. The removed parts were fixed in 10% formalin for 48 hours. Following a routine histological process, the cuts were stained by hematoxilin, eosin and Mallory Tricromic. The histopathological analysis showed that the Sealer Plus cement were unsatisfactory in relation to the tissue compatibility. 2. Evaluation of the marginal apical infiltration. In this experiment, 120 extracted top-central human incisors in 4 groups of 20 teeth were used and 3 group of 10 teeth used as control groups. The teeth were initially filed with K file up to the number 30 until apical patency and root canal prepared up to the number 50, using sodium hipochloride 0,5%, After that, the root canal were filled with Sealer Plus or Grossman cements, using or no calcium hydroxide intracanal dressing. After the fillings, the teeth were unpermeated in al their extension with nail polishing, except for 1 to 2 mm around the apical forame, submerged in 2% metilen blue colouring under vacuum conditions and fractured in such a way to obtain 2 sections. The colouring penetration was measured by a perilometer and the data, after statistical analysis, there was no difference between the groups. / Orientador: Léa Assed Bezerra da Silva / Coorientador: Mario Roberto Leonardo / Banca: Mário Tanomaru Filho / Banca: Francisco José de Souza Filho / Banca: Manoel Eduardo de Lima Machado / Doutor

Orientador: Sérgio Eduardo de Paiva Gonçalves / Banca: Rebeca Di Nicoló / Banca: Marta Solange Rampani Duarte / Resumo: A adesão continua a ser um desafio na Odontologia, principalmente em tecidos morfologicamente distintos e valendo-se de sistemas adesivos de mecanismos de ação também distintos. O objetivo deste estudo in vitro foi comparar a resistência adesiva de dois sistemas (autocondicionante e convencional) em dois substratos (esmalte e dentina), associados ou não à tecnologia laser (Nd:YAG). Foram utilizados 120 dentes bovinos, recém-extraídos, embutidos, que tiveram a superfície de esmalte ou dentina exposta por meio de lixas. Uma área de 3mm de diâmetro na região cérvico-vestibular-mediana foi selecionada para adesão, de acordo com os seguintes grupos: a) G1: AF/ esmalte (adesivo autocondicionante em esmalte seguindo especificação do fabricante); b) G2: AF/ dentina (adesivo autocondicionante em dentina seguindo especificação do fabricante); c) G3: AL/ esmalte (adesivo autocondicionante em esmalte + laser Nd:YAG + fotopolimerização); d) G4: AL/ dentina (adesivo autocondicionante em dentina + laser Nd:YAG + fotopolimerização); e) G5: CF/ esmalte (condicionamento ácido + adesivo convencional em esmalte); f) G6: CF/ dentina (condicionamento ácido + adesivo convencional em dentina); g) G7: CL/ esmalte (condicionamento ácido + adesivo convencional em esmalte + laser Nd:YAG + fotopolimerização); h) G8: CL/ dentina (condicionamento ácido + adesivo convencional em dentina + laser Nd:YAG + fotopolimerização). A resina composta Z 250 foi inserida com auxílio de matriz de teflon e fotopolimerizada com luz halógena, seguida da realização do teste de cisalhamento em máquina universal Emic, com carga de100kgf e velocidade de 0,5mm/min. Os valores médios em MPa obtidos para os diferentes grupos foram: G1 (20,291), G2 (14,142), G3 (23,615), G4 (22,235), G5 (20,899), G6 (11,291), G7 (22,102), G8 (15,980). Após aplicação do teste de ANOVA e Tukey 5%, concluiu-se que... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Bonding continues to be a challenge in Dentistry, particularly in morphologically different tissues, and adhesive systems with different action mechanisms are also valid. The aim of this study was to compare the bond strength of two systems (self-etching and conventional) to two substrates (enamel and dentin) either associated with laser technology (Nd:YAG) or not. One hundred and twenty (120) recently extracted, embedded bovine teeth were used, and abrasive papers were used to expose the enamel or dentin surfaces. An area of 3mm in diameter in the cervical-vestibular-median region was selected for bonding, according to the following groups: a) G1: AF/ enamel (self-etching adhesive to enamel in accordance with the manufacturer's specification); b) G2: AF/ dentin (self-etching adhesive to dentin in accordance with the manufacturer's specification); c) G3: AF/ enamel (self-etching adhesive to enamel + laser Nd:YAG + light polymerization ; d) G4: AL/ dentin (self-etching adhesive to dentin + laser Nd:YAG + light polymerization ; e) G5: CF/ enamel (acid etching + conventional adhesive to enamel); f) G6: CF/ dentin (acid etching + conventional adhesive to dentin); g) G7: CL/ enamel (acid etching + conventional adhesive to enamel + laser Nd:YAG + light polymerization ; h) G8: CL/ dentin (acid etching + conventional adhesive to dentin + laser Nd:YAG + light polymerization). Resin composite Z250 was inserted with the aid of a Teflon matrix and light polymerized, followed by the shear test in an EMIC universal machine, with a load of 100 Kgf and speed of 0.5 mm/min. The mean values obtained in Mpa for the different groups were: G1 (20.291), G2 (14.142), G3 (23.615), G4 (22.235), G5 (20.899), G6 (11.291), G7 (22.102), G8 (15.980). After applying the ANOVA and Tukey tests 5%, it was concluded that the application of laser Nd:YAG significantly increased the bond strength under all the experimental... (Complete abstract click electronic access below) / Mestre