No description available.

The corrosion behaviour of cast Al-Mg alloy A535 and its composites containing 10 wt.% and 15 wt.% fly ash, and 10 wt.% hybrid reinforcement (5 wt.% fly ash + 5 wt.% SiC) was investigated using weight-loss and electrochemical corrosion tests, optical microscopy, Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). The tests were conducted in fresh water collected from the South Saskatchewan River and 3.5 wt.% NaCl solution at room temperature. The pH of the salt solution varied from 3 to 9. For comparison, two other aluminum alloys, AA2618 and AA5083-H116, were tested in the same electrolytes. The results of the weight-loss corrosion test showed that unreinforced A535 alloy had a lower corrosion rate in fresh water and seawater environments than the composites at all the tested pH values. The corrosion rate of the composites increased with increasing fly ash content. As expected, the corrosion rates of A535 alloy and the composites tested in fresh water were lower than those in salt solution. The results of the potentiodynamic and cyclic polarization electrochemical tests showed that the corrosion potential (Ecorr) and pitting potential (Epit) of the alloy were more positive than those of the composites. The corrosion and pitting potentials of the composites became more negative (active) with increasing fly ash content. The composites showed more positive (noble) repassivation or protection potential (Erp) than the matrix alloy, with the positivity increasing with fly ash content. Analysis of the electrochemical noise data showed that pitting corrosion was the dominant mode of corrosion for the alloy in 3.5 wt.% NaCl solution. Optical microscopy and SEM revealed that Mg2Si phase and Al-Mg intermetallics corroded preferentially to the matrix. The EDS data indicated that the protective oxide film formed on A535 contained Al2O3 and MgO.

The corrosion behaviour of cast Al-Mg alloy A535 and its composites containing 10 wt.% and 15 wt.% fly ash, and 10 wt.% hybrid reinforcement (5 wt.% fly ash + 5 wt.% SiC) was investigated using weight-loss and electrochemical corrosion tests, optical microscopy, Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray Spectroscopy (EDS). The tests were conducted in fresh water collected from the South Saskatchewan River and 3.5 wt.% NaCl solution at room temperature. The pH of the salt solution varied from 3 to 9. For comparison, two other aluminum alloys, AA2618 and AA5083-H116, were tested in the same electrolytes. The results of the weight-loss corrosion test showed that unreinforced A535 alloy had a lower corrosion rate in fresh water and seawater environments than the composites at all the tested pH values. The corrosion rate of the composites increased with increasing fly ash content. As expected, the corrosion rates of A535 alloy and the composites tested in fresh water were lower than those in salt solution. The results of the potentiodynamic and cyclic polarization electrochemical tests showed that the corrosion potential (Ecorr) and pitting potential (Epit) of the alloy were more positive than those of the composites. The corrosion and pitting potentials of the composites became more negative (active) with increasing fly ash content. The composites showed more positive (noble) repassivation or protection potential (Erp) than the matrix alloy, with the positivity increasing with fly ash content. Analysis of the electrochemical noise data showed that pitting corrosion was the dominant mode of corrosion for the alloy in 3.5 wt.% NaCl solution. Optical microscopy and SEM revealed that Mg2Si phase and Al-Mg intermetallics corroded preferentially to the matrix. The EDS data indicated that the protective oxide film formed on A535 contained Al2O3 and MgO.

The present work deals with the comparison of the properties of metallic biomaterials in terms of their suitability for use as a temporary metal implant. In the work is judged biocompatibility of materials, they are comparing the corrosion rates and the influence of additives in the iron alloy to change biocompatibility and corrosion rate. In a part of this work is suggesting a method of preparing biodegradable metallic samples with different alloying elements and determine the methods, processes and measuring the corrosion rates. Part of this work is the chapter dealing with the function and effect of iron in the human body and any complications that may occur when a surplus caused by the release of part of the implant during its degradation or corrosion products. The outcome of this work is sort of created an iron-based samples in terms of their electrochemical corrosion potential, corrosion rate of samples exposed in various corrosive solutions, spectroscopic elemental analysis and outputs from the microscopic observation of the structures.

No description available.