The aim of my Diploma Thesis is to design and analyse the carrier steel construction of the three-aisled storehouse in location Frýdek-Místek. The object is constructed as spatial frame structure with solid joints which sits hinged on base footings. The hall is of rectangular ground plan sizing 30x46 metres with axial span of transverse links 9,0m + 12,0m + 9,0m and lenght of transverse links 12,0m. The carrying roof construction is made of full-length framed rungs and lattice purlins with parabolic lower belt. A main-aisle roof is saddle with the angle of 5 degrees and its top in height of +9m. The sided-aisle roofs are rack-type with the same angle. The construction sheating is made of polyurethan panel system with trapezium profile. The load consists of its own weight, other usable still and climate load in the form of wind and snow in regards of considered location. The static assessment is performed in SciaEngineer 2012 programme.

L'ADN est en permanence exposé à un grand nombre d'événements dommageables déclenchées par des agents endogènes et exogènes. De nombreux travaux expérimentaux ont fourni des informations cruciales sur les propriétés structurelles et la réparation de certains des lésions de l'ADN. Cependant, il manque une vision mécanistique ou énergétique sur leur formation. La biochimie computationnelle a émergé comme un outil puissant pour comprendre les réactions biochimiques et les propriétés électroniques de systèmes complexes.Dans cette thèse, nous étudions la formation de lésions complexes intra-brin et inter-brin. Ces lésions tandem constituent une puissant menace à l'intégrité du génome, en raison de leur haute fréquence mutagenique. Tout d'abord, nous discutons l'attaque d'une liaison covalente entre un radical pyrimidinique. En comparant avec les bases isolees, nos simulations hybrides Car-Parrinello demontrent que la reactivité de la thymine et de la cytosine radicalaires sont inversees dans l'environnement B-helical. De plus, nos resultats montrent egalement une deformation plus importante pour la lesion G[8-5]C.Nous rationalisons également la plus grande réactivité des cytosines par rapport aux purines vers la formation multi-etapes de lésions complexes inter-brins par condensation avec un site C4' abasique. Ces résultats bases sur des simulations avec solvatation explicite et combines a la théorie de la fonctionnelle de la densité sont en accord avec les données expérimentales. / DNA is continuously exposed to a vast number of damaging events triggered by endogenous and exogenous agents. Numerous experimental studies have provided key information regarding structural properties of some of the DNA lesions and their repair. However, they lack in mechanistic or energetic information pertaining to their formation. Computational Biochemistry has emerged as a powerful tool to understand biochemical reactions and electronic properties of large systems.In this thesis we study the formation of inter- and intra-strand cross-links. These tandem lesions pose a potent threat to genome integrity, because of their high mutagenic frequency. First, we discuss the formation of complex defects which arise from the attack of a pyrimidine radical onto guanine. In comparison with the reactivity of isolated nucleobases, our hybrid Car-Parrinello Molecular Dynamics simulations reveal that the reactivity of hydrogen-abstracted thymine and cytosine is reversed within a B-helix environment. Further, our data also suggest a more severe distortion of the B-helix for G[8-5]C.Second, we rationalize the higher reactivity of cytosine vs. purines toward the multistep formation of inter-strand crosslinks with a C4' oxidized a basic site, which is in qualitative agreement with experiments on isolated nucleobases, using explicit solvent simulations combined to density functional theory.

Ziel der Arbeit ist die theoretische Analyse von Kohlenstoff-Clustern der Größe 100 - 500 Atome. Die experimentellen Beobachtungen sind bei dieser geringen Anzahl der Atome schwierig. Anderseits sind Kenntnisse über solche Cluster sehr wichtig, z.B. für die Keimbildung von Diamant auf Substraten, oder für die Kohlenstoff-Nanotechnologie (Fullerene, Nanotubes), oder für strukturelle Defekte in Kohlenstoff-Systemen. Es wurden gekrümmte Grenzflächen im Diamant simuliert. Zuerst mit einem empirischen Potential. Es wurde danach eine Methode entwickelt, bei der die schwach gestörten Gebiete einem empirischen Potential gehorchen, und die stark gestörten Gebiete, wo eine genaue Berechnung erforderlich ist, durch eine quantenmechanische Näherung beschrieben wurden. Somit kann man mit guter Genauigkeit große Systeme, bestehend aus einigen 10 (hoch)4 Atomen, simulieren, bei denen nur lokal quantenmechanische Methoden erforderlich sind. Mit diesem Hybrid-Code wurden weiterhin Diamantkeime auf Silizium gerechnet. Es wurden Aussagen bezüglich der Stabilität des Diamants auf dem Siliziumsubstrat, der kritischen Keimgröße, der Änderungen, die der Keim erfährt, gemacht. Ein anderes Gebiet ist die molekulardynamische Simulation bezüglich der Stabilität und des Transformationsverhaltens von Kohlenstoff-Nanoteilchen. Es wurden als »Rohstoffe» sowohl Diamant- und Graphitkristalle sphärischer, ellipsoidischer oder quadratischer Form benutzt, als auch amorpher Kohlenstoff. Es wurde demonstriert, daß sich Diamant unter höherer Temperatur und Bestrahlung in Kohlenstoffzwiebeln transformiert. Es wurde der innere Kern, bestehend aus zwei Schalen, der Kohlenstoffzwiebel simuliert. Es wurde, nach meinem Wissen, zum ersten Mal gezeigt, daß zwischen den Schalen der Kohlenstoffzwiebel Quer-Verbindungen (cross-links) existieren. Diese waren von den Experimentatoren vermutet worden. Sie bilden die Initiatoren der Diamantkeime der Kohlenstoffzwiebel bei ihrer ohne äußeren Druck möglichen Transformation in Diamant. Die Zentren der Kohlenstoffzwiebeln befinden sich bereits in der Entstehung der Zwiebel unter einem Selbstdruck. Bei den größeren Kohlenstoffzwiebeln beträgt der experimentell bestimmte Abstand zwischen den Schalen von außen nach innen von 3.34 Å bis 2.2 Å. Anlagen: nano1.mpg (91,8 MB); nano2.mpg (131 MB) Nutzung: Referat Informationsvermittlung der SLUB / The scope of this work is the analysis of carbon clusters of about 100 - 500 atoms. The experimental studies are at such small clusters heavy. Knowledges about thus clusters are very important, for example in the field of the nucleation of diamond on substrates, or for the carbon nano-technology (fullerene, nanotubes), or for local defects in carbon systems. There were simulated curved interfaces in diamond. Firstly with an empirical potential. Than I developed a method, in wich the defects and the structure around them are treated by a quantum mechanical algorithm and the rest with a near to ideal structure with an empirical potential. So, it is possible an accurate calculation of great systems of about 10 (high)4 atoms on wich only locally quantum mechanical methods are necessary. With this hybrid-code diamond nuclei on silicon substrate were simulated. The stability of the diamond nuclei on the silicon substrate, the critical radius of the nuclei and the changes of the nuclei during his transformation was investigated. Another field of investigations is the molecular dynamics simulation of free carbon clusters. The initial structures had spherical, ellipsoidical or square form and consists of diamond and graphite or a free form in the case of amorphous carbon. It was demonstrated that diamond transforms at higher temperatures and under irradiation in carbon onions. The genesis of the nucleus of a carbon onion with two shells was here for the first time simulated. The existence of the cross-links between the shells of a carbon onion was demonstrated. These existence was expected from the experimentators. The cross-links are the initiators of the transformation of carbon onions to diamond. The center of carbon onions is under self-pressure, because the distance between the outer shells is about 3.34 Å and between the inner shells about 2.2 Å. Appendix: nano1.mpg (91,8 MB); nano2.mpg (131 MB) Usage: Referat Informationsvermittlung/ SLUB

Ziel der Arbeit ist die theoretische Analyse von Kohlenstoff-Clustern der Größe 100 - 500 Atome. Die experimentellen Beobachtungen sind bei dieser geringen Anzahl der Atome schwierig. Anderseits sind Kenntnisse über solche Cluster sehr wichtig, z.B. für die Keimbildung von Diamant auf Substraten, oder für die Kohlenstoff-Nanotechnologie (Fullerene, Nanotubes), oder für strukturelle Defekte in Kohlenstoff-Systemen. Es wurden gekrümmte Grenzflächen im Diamant simuliert. Zuerst mit einem empirischen Potential. Es wurde danach eine Methode entwickelt, bei der die schwach gestörten Gebiete einem empirischen Potential gehorchen, und die stark gestörten Gebiete, wo eine genaue Berechnung erforderlich ist, durch eine quantenmechanische Näherung beschrieben wurden. Somit kann man mit guter Genauigkeit große Systeme, bestehend aus einigen 10 (hoch)4 Atomen, simulieren, bei denen nur lokal quantenmechanische Methoden erforderlich sind. Mit diesem Hybrid-Code wurden weiterhin Diamantkeime auf Silizium gerechnet. Es wurden Aussagen bezüglich der Stabilität des Diamants auf dem Siliziumsubstrat, der kritischen Keimgröße, der Änderungen, die der Keim erfährt, gemacht. Ein anderes Gebiet ist die molekulardynamische Simulation bezüglich der Stabilität und des Transformationsverhaltens von Kohlenstoff-Nanoteilchen. Es wurden als »Rohstoffe» sowohl Diamant- und Graphitkristalle sphärischer, ellipsoidischer oder quadratischer Form benutzt, als auch amorpher Kohlenstoff. Es wurde demonstriert, daß sich Diamant unter höherer Temperatur und Bestrahlung in Kohlenstoffzwiebeln transformiert. Es wurde der innere Kern, bestehend aus zwei Schalen, der Kohlenstoffzwiebel simuliert. Es wurde, nach meinem Wissen, zum ersten Mal gezeigt, daß zwischen den Schalen der Kohlenstoffzwiebel Quer-Verbindungen (cross-links) existieren. Diese waren von den Experimentatoren vermutet worden. Sie bilden die Initiatoren der Diamantkeime der Kohlenstoffzwiebel bei ihrer ohne äußeren Druck möglichen Transformation in Diamant. Die Zentren der Kohlenstoffzwiebeln befinden sich bereits in der Entstehung der Zwiebel unter einem Selbstdruck. Bei den größeren Kohlenstoffzwiebeln beträgt der experimentell bestimmte Abstand zwischen den Schalen von außen nach innen von 3.34 Å bis 2.2 Å. Anlagen: nano1.mpg (91,8 MB); nano2.mpg (131 MB) Nutzung: Referat Informationsvermittlung der SLUB / The scope of this work is the analysis of carbon clusters of about 100 - 500 atoms. The experimental studies are at such small clusters heavy. Knowledges about thus clusters are very important, for example in the field of the nucleation of diamond on substrates, or for the carbon nano-technology (fullerene, nanotubes), or for local defects in carbon systems. There were simulated curved interfaces in diamond. Firstly with an empirical potential. Than I developed a method, in wich the defects and the structure around them are treated by a quantum mechanical algorithm and the rest with a near to ideal structure with an empirical potential. So, it is possible an accurate calculation of great systems of about 10 (high)4 atoms on wich only locally quantum mechanical methods are necessary. With this hybrid-code diamond nuclei on silicon substrate were simulated. The stability of the diamond nuclei on the silicon substrate, the critical radius of the nuclei and the changes of the nuclei during his transformation was investigated. Another field of investigations is the molecular dynamics simulation of free carbon clusters. The initial structures had spherical, ellipsoidical or square form and consists of diamond and graphite or a free form in the case of amorphous carbon. It was demonstrated that diamond transforms at higher temperatures and under irradiation in carbon onions. The genesis of the nucleus of a carbon onion with two shells was here for the first time simulated. The existence of the cross-links between the shells of a carbon onion was demonstrated. These existence was expected from the experimentators. The cross-links are the initiators of the transformation of carbon onions to diamond. The center of carbon onions is under self-pressure, because the distance between the outer shells is about 3.34 Å and between the inner shells about 2.2 Å. Appendix: nano1.mpg (91,8 MB); nano2.mpg (131 MB) Usage: Referat Informationsvermittlung/ SLUB

Title: Interdisciplinary relations of physics and chemistry in science education Abstract: This master's degree thesis deals with the topic of interdisciplinary relations of chemistry and physics in science education. According to the review, to conveniently integrate physics and chemistry the appropriate topics and approaches were selected. The thesis includes teaching materials and worksheets to the three topics (Evolution of the Universe and the Origin of Elements, Luminescence and Composition and Properties of Matter) that are suitable for integration of physics and chemistry. The teaching material "Evolution of the Universe and the Origin of the Elements" includes a study text for teachers and a shorter study text for pupils. The teaching material "Luminescence" is based on an independent research done by pupils with their own crafted UV-lamp, completed with the facts included in a powerpoint presentation. The teaching material "Composition and Properties of Matter" consists of three parts (The paraffin, The Candle and The Properties of Selected Organic Substances) and is designed for an independent research done by pupils. Listed study materials were checked by teachers during meetings and seminars. The thesis also includes an evaluation of listed study materials by an expert group of high school...

This work deals with studying a molecular mechanism of anticancer effect of a new platinum - based drug. The qualities of still unknow dinuclear platinum komplex (BBR3571-DACH) were parallelly studied together with clinically time-tested and used mononuclear platinum complex DACH. Earlier essays demostrated, that DNA is the critical target for the cytostatic activity of platinum compounds. Altered properties of DNA and binding characteristics of these two platinum compounds were monitored by several different bioanalytical methods (differential pulse polarography, UV-VIS spectrophotometry, fluorescence spectrophotometry, CD spectroscopy and electrophoresis) after modification of DNA by both of platinum complexes. For the compounds BBR3571-DACH and DACH it was determined that the DNA binding is rapid and bifunctional. The stabilizing effect on DNA was significant particularly after modification of DNA by dinuclear komplex, while denaturating effect wasn´t proved at all. The results also indicate that dinuclear platinum complex BBR3571-DACH probably does not participate on formation of long-range cross-links like other early studied polynuclear platinum complexes.

This thesis reports on experimental investigations of the mechanisms inherent in the joint action of short and continuous fibres in high-performance, cement-based composites. Experiments on different levels of observation (macro- meso- and micro-levels) were performed to provide detailed insights into the various effects of adding different types of short fibres (dispersed AR glass, integral AR glass and dispersed carbon fibres) on the strength, deformation, and failure behaviour of textile-reinforced concrete (TRC) subjected to tensile loading. Moreover, visual inspections of the specimens' surfaces and microscopic investigation of the fracture surfaces and the interface zone between fibre and matrix were performed and evaluated. Subsequently, the mathematical descriptions for TRC with short fibres under deformation controlled tensile loading conditions were derived based on a multi-scale rheological-statistical modelling approach. Based on a literature review, the state of the art is presented and discussed to identify key questions that are yet to be answered satisfactorily. This provides the starting point for the investigations presented in this thesis. The experimental program on the macro-level included uniaxial tension tests performed on thin, narrow plates reinforced by: a) only textile reinforcement, b) only short fibres, and c) hybrid reinforcement (both textile reinforcement with the addition of short fibres). Special attention was directed toward the course of the stress-strain relationship, crack pattern development, and fibre failure behaviour. The stress-strain curves resulting from uniaxial tension testing demonstrated clearly the positive influence of all types of short fibre on the mechanical performance of TRC. While the first-crack stress in TRC specimens increased significantly due to the addition of short fibres, an expansion of the strain region, where multiple cracks form, was observed for the stress-strain curves for TRC with added short fibres. The visual inspection of the specimens\' surfaces showed a higher number of cracks and finer crack patterns for given strain levels in the cases when short fibres were added to TRC. Moreover, depending on fibre type, the positive effects of the addition of short fibres on both tensile strength and work-to-fracture of the composite were found to vary significantly. The findings at the micro- and meso-levels of observation provided to a great extent a core of understanding of some particular mechanical behavioural properties of TRC with short fibres at the macro-level of observation. Thus, in addition to the experimental testing performed on composite materials with different parameter combinations, investigations of the action of individual material components, i.e., multifilament-yarns and single short fibres, embedded into cement-based matrices were carried out. It was found that short fibres indeed improve the bond between multifilament-yarns and the surrounding matrix. By their random positioning on the yarn\'s surface, short fibres built new adhesive cross-links which provided extra connecting points to the surrounding matrix. Furthermore, the water-to-binder ratio of the matrix influenced bond quality between fibre and matrix, i.e., various degrees of matrix-fibre bond were observed. As a result, the mechanical behaviour of the composite varied with w/b: While the good bond of the fibre embedded in a matrix with a low water-to-binder ratio leads to increase in stiffness and strength of the composite, fibres with weak bonding can be considered as defects with respect to stiffness as they lead to a decrease in the value. The thesis further derives the mathematical relationships for TRC with the addition of short fibres under deformation-controlled tensile loading. A physically based rheological model consisting of simple rheological elements was developed based on the experimental results on the micro-scale, using single-fibre pullout tests. Special attention was paid to the gradual de-bonding process and the resulting force-displacement branch. The model adequately reproduced both relevant fibre failure scenarios: fibre fracture and fibre pullout. By means of statistical procedures the combination of these models led to description of the stress-crack opening behaviour of an individual crack bridged by the given number of short fibres. The stress-strain relation for TRC with short fibres subjected to tensile loading was then derived. The concept followed at the macro-level of observation was modelling separately the three main regions of the characteristic stress-strain curve. The regions of crack-free material and crack-widening were considered linear and described based on the corresponding characteristic values of each region. The behaviour of the multiple cracking region was derived by considering an increasing number of cracks in serial interconnection and the contribution of the uncracked matrix in between. The stress transfer, i.e., bridging stress, across the crack was determined based on the contribution of both short fibres and multifilament-yarns. Behaviour of individual cracks was adjusted by varying the number of bridging fibres in different cracks and by varying the yarn bridging stress according to range observed in the pullout experiments. / In der vorliegenden Arbeit wird über Untersuchungen zu den Mechanismen der Wechselwirkungen zwischen Kurz- und Endlosfasern in zement-basierenten Hochleistungskompositen berichtet. Hierzu wurden experimentelle Untersuchungen auf verschiedenen Betrachtungsebenen (Makro-, Meso- und Mikroebene) durchgeführt mit dem Ziel, detaillierte Erkenntnisse zu den Auswirkungen der Zugabe von verschiedenen Arten von Kurzfasern (disperse und integrale AR-Glasfasern, Kohlenstofffasern) hinsichtlich des Festigkeits-, Verformungs- und Bruchverhaltens von Textilbeton (engl.: textile-reinforced concrete = TRC) unter Zugbeanspruchung zu gewinnen. Die Bruchflächen sowie die Gestalt der Interphase zwischen der Bewehrung aus Textilien oder Kurzfasern und der umhüllenden zemengebundenen Matrix wurden mit optischen und elektronenmikroskopischen Verfahren hinsichtlich der Wechselwirkungsphänomene ausgewertet. Die Ergebnisse der experimentellen Arbeiten bildeten den Ausgangspunkt für die mathematischen Beschreibungen für TRC mit Kurzfasern unter verformungsgesteuerter Zugbelastung. Die Formulierungen erfolgten auf Grundlage multiskalarer rheologisch-statistischer Modellansätze. In einer Literatursichtung wurde zunächst der Kenntnisstand zu den Materialien und zum Verhalten von TRC und Faserbeton unter Zugbeanspruchung dargestellt und diskutiert. Die noch zu erforschenden Fragen wurden präzisiert und die Grundlagen für deren Untersuchung geschaffen. Bei den Experimenten auf der Makroebene wurden drei Bewehrungsvarianten betrachtet: a) textile Bewehrung, b) Kurzfaserbewehrung, und c) hybride Bewehrung (Textil und Kurzfasern). An Dehnkörpern wurde die Spannungs-Dehnungsbeziehung unter einachsiger Zugbelastung studiert und dabei das Rissbild und die Phänomene des Faserversagens detailliert beobachtet. Anhand der Spannungs-Dehnungsbeziehungen konnte gezeigt werden, dass die Zugabe von Kurzfasern bei allen untersuchten Kurzfaserarten zu einer erheblichen Verbesserung der Leistungsfähigkeit von Textilbeton führt. Dies zeigte sich unter anderem in einer ausgeprägten Anhebung der Erstrissspannung sowie der Entwicklung von zahlreicheren und damit feineren Rissen, die zu einer Verbesserung der Duktilität führten. Ebenso wurden Steigerungen der Zugfestigkeit und der Energiedissipation festgestellt. In welchem Maß diese Änderungen stattfinden, hängt von der Art der Kurzfasern ab. Die Experimente auf der Mikro- und Mesoebene wurden so konzipiert, dass sie die Erkundung der Mechanismen, die den auf der Makroebene beobachteten Phänomenen zugrunde liegen, unterstützten. Auf der Mesoebene wurden Mulitifilamentgarnauszugversuche (mit und ohne Kurzfasern in der Matrix) und auf der Mikroebene Einzelfaserauszugsversuche für alle betrachteten Kurzfasertypen durchgeführt. Es wurde festgestellt, dass die Kurzfasern den Verbund zwischen Matrix und Multifilamentgarn verbessern. Kurzfasern können bei zufälliger Positionierung an der Garnoberfläche zusätzliche Haftbrücken bzw. Verbindungsstellen zu umgebender Matrix bilden. Für die Verbundqualität zwischen Faser und Matrix ist der Wasser-Bindemittel-Wert (W/B-Wert) von entscheidender Bedeutung. Bei einer Matrix mit niedrigem W/B-Wert führt die gute Qualität des Verbunds der eingebetteten Fasern zu einer Erhöhung der Steifigkeit sowie der Festigkeit des Komposites. Bei hohem W/B-Wert haben die Fasern einen schlechten Verbund zur Matrix und müssen überwiegend als Fehl- bzw. Schwachstellen betrachtet werden. Festigkeit und Steifigkeit des Komposits nehmen daher ab. Die Ableitung mathematischer Beziehungen für Textilbeton mit Zugabe von Kurzfasern unter verformungsgesteuerter Zugbelastung erfolgte aufbauend auf den Ergebnissen der experimentellen Untersuchungen auf der Mikroebene. Die Einzelfaserauszugsversuche wurden mit Hilfe eines physikalisch basierten Modelles nachgebildet, das aus einfachen rheologischen Elementen besteht. Phänomene wie die graduelle Ablösung der Faser, Faserbruch und Faserauszug wurden durch eine entsprechende Kombination und Parametrierung der rheologischen Elemente abgebildet. Im Ergebnis wurden zutreffende Kraft-Rissöffnungsbeziehungen modelliert. Auf der Mesoebene wurde ein einzelner Riss modelliert, der sowohl durch Multifilamentgarne als auch Kurzfasern überbrückt werden kann. Der rissüberbrückenden Wirkung der zahlreichen Kurzfasern wurde mit Hilfe statistischer Methoden rechnung getragen, die unterschiedliche Faser-Risswinkel und Einbindelängen berücksichtigen. Die resultierende Spannungs-Rissöffnungskurve umfasst die rissüberbrückende Wirkung von Multifilamentgarnen und Kurzfasern. Auf der Makroebene kann die charakteristische Spannungs-Dehnungsbeziehung von TRC unter Zugbelastung in 3 Bereiche (Zustände I, IIa, IIb) unterteilt werden. Die Kurvenverläufe im Zustand I (ungerissenen) sowie Zustand IIb (abgeschlossenes Rissbild) wurden als linear betrachtet und basierend auf den entsprechenden charakteristischen Werten des jeweiligen Zustands beschrieben. Das Verhalten im Zustand IIa (multiple Rissbildung) wurde durch die Reihenschaltung einer zunehmenden Anzahl von Rissen sowie den Beitrags der ungerissenen Matrix zwischen den Rissen modelliert.

This thesis reports on experimental investigations of the mechanisms inherent in the joint action of short and continuous fibres in high-performance, cement-based composites. Experiments on different levels of observation (macro- meso- and micro-levels) were performed to provide detailed insights into the various effects of adding different types of short fibres (dispersed AR glass, integral AR glass and dispersed carbon fibres) on the strength, deformation, and failure behaviour of textile-reinforced concrete (TRC) subjected to tensile loading. Moreover, visual inspections of the specimens' surfaces and microscopic investigation of the fracture surfaces and the interface zone between fibre and matrix were performed and evaluated. Subsequently, the mathematical descriptions for TRC with short fibres under deformation controlled tensile loading conditions were derived based on a multi-scale rheological-statistical modelling approach. Based on a literature review, the state of the art is presented and discussed to identify key questions that are yet to be answered satisfactorily. This provides the starting point for the investigations presented in this thesis. The experimental program on the macro-level included uniaxial tension tests performed on thin, narrow plates reinforced by: a) only textile reinforcement, b) only short fibres, and c) hybrid reinforcement (both textile reinforcement with the addition of short fibres). Special attention was directed toward the course of the stress-strain relationship, crack pattern development, and fibre failure behaviour. The stress-strain curves resulting from uniaxial tension testing demonstrated clearly the positive influence of all types of short fibre on the mechanical performance of TRC. While the first-crack stress in TRC specimens increased significantly due to the addition of short fibres, an expansion of the strain region, where multiple cracks form, was observed for the stress-strain curves for TRC with added short fibres. The visual inspection of the specimens\' surfaces showed a higher number of cracks and finer crack patterns for given strain levels in the cases when short fibres were added to TRC. Moreover, depending on fibre type, the positive effects of the addition of short fibres on both tensile strength and work-to-fracture of the composite were found to vary significantly. The findings at the micro- and meso-levels of observation provided to a great extent a core of understanding of some particular mechanical behavioural properties of TRC with short fibres at the macro-level of observation. Thus, in addition to the experimental testing performed on composite materials with different parameter combinations, investigations of the action of individual material components, i.e., multifilament-yarns and single short fibres, embedded into cement-based matrices were carried out. It was found that short fibres indeed improve the bond between multifilament-yarns and the surrounding matrix. By their random positioning on the yarn\'s surface, short fibres built new adhesive cross-links which provided extra connecting points to the surrounding matrix. Furthermore, the water-to-binder ratio of the matrix influenced bond quality between fibre and matrix, i.e., various degrees of matrix-fibre bond were observed. As a result, the mechanical behaviour of the composite varied with w/b: While the good bond of the fibre embedded in a matrix with a low water-to-binder ratio leads to increase in stiffness and strength of the composite, fibres with weak bonding can be considered as defects with respect to stiffness as they lead to a decrease in the value. The thesis further derives the mathematical relationships for TRC with the addition of short fibres under deformation-controlled tensile loading. A physically based rheological model consisting of simple rheological elements was developed based on the experimental results on the micro-scale, using single-fibre pullout tests. Special attention was paid to the gradual de-bonding process and the resulting force-displacement branch. The model adequately reproduced both relevant fibre failure scenarios: fibre fracture and fibre pullout. By means of statistical procedures the combination of these models led to description of the stress-crack opening behaviour of an individual crack bridged by the given number of short fibres. The stress-strain relation for TRC with short fibres subjected to tensile loading was then derived. The concept followed at the macro-level of observation was modelling separately the three main regions of the characteristic stress-strain curve. The regions of crack-free material and crack-widening were considered linear and described based on the corresponding characteristic values of each region. The behaviour of the multiple cracking region was derived by considering an increasing number of cracks in serial interconnection and the contribution of the uncracked matrix in between. The stress transfer, i.e., bridging stress, across the crack was determined based on the contribution of both short fibres and multifilament-yarns. Behaviour of individual cracks was adjusted by varying the number of bridging fibres in different cracks and by varying the yarn bridging stress according to range observed in the pullout experiments. / In der vorliegenden Arbeit wird über Untersuchungen zu den Mechanismen der Wechselwirkungen zwischen Kurz- und Endlosfasern in zement-basierenten Hochleistungskompositen berichtet. Hierzu wurden experimentelle Untersuchungen auf verschiedenen Betrachtungsebenen (Makro-, Meso- und Mikroebene) durchgeführt mit dem Ziel, detaillierte Erkenntnisse zu den Auswirkungen der Zugabe von verschiedenen Arten von Kurzfasern (disperse und integrale AR-Glasfasern, Kohlenstofffasern) hinsichtlich des Festigkeits-, Verformungs- und Bruchverhaltens von Textilbeton (engl.: textile-reinforced concrete = TRC) unter Zugbeanspruchung zu gewinnen. Die Bruchflächen sowie die Gestalt der Interphase zwischen der Bewehrung aus Textilien oder Kurzfasern und der umhüllenden zemengebundenen Matrix wurden mit optischen und elektronenmikroskopischen Verfahren hinsichtlich der Wechselwirkungsphänomene ausgewertet. Die Ergebnisse der experimentellen Arbeiten bildeten den Ausgangspunkt für die mathematischen Beschreibungen für TRC mit Kurzfasern unter verformungsgesteuerter Zugbelastung. Die Formulierungen erfolgten auf Grundlage multiskalarer rheologisch-statistischer Modellansätze. In einer Literatursichtung wurde zunächst der Kenntnisstand zu den Materialien und zum Verhalten von TRC und Faserbeton unter Zugbeanspruchung dargestellt und diskutiert. Die noch zu erforschenden Fragen wurden präzisiert und die Grundlagen für deren Untersuchung geschaffen. Bei den Experimenten auf der Makroebene wurden drei Bewehrungsvarianten betrachtet: a) textile Bewehrung, b) Kurzfaserbewehrung, und c) hybride Bewehrung (Textil und Kurzfasern). An Dehnkörpern wurde die Spannungs-Dehnungsbeziehung unter einachsiger Zugbelastung studiert und dabei das Rissbild und die Phänomene des Faserversagens detailliert beobachtet. Anhand der Spannungs-Dehnungsbeziehungen konnte gezeigt werden, dass die Zugabe von Kurzfasern bei allen untersuchten Kurzfaserarten zu einer erheblichen Verbesserung der Leistungsfähigkeit von Textilbeton führt. Dies zeigte sich unter anderem in einer ausgeprägten Anhebung der Erstrissspannung sowie der Entwicklung von zahlreicheren und damit feineren Rissen, die zu einer Verbesserung der Duktilität führten. Ebenso wurden Steigerungen der Zugfestigkeit und der Energiedissipation festgestellt. In welchem Maß diese Änderungen stattfinden, hängt von der Art der Kurzfasern ab. Die Experimente auf der Mikro- und Mesoebene wurden so konzipiert, dass sie die Erkundung der Mechanismen, die den auf der Makroebene beobachteten Phänomenen zugrunde liegen, unterstützten. Auf der Mesoebene wurden Mulitifilamentgarnauszugversuche (mit und ohne Kurzfasern in der Matrix) und auf der Mikroebene Einzelfaserauszugsversuche für alle betrachteten Kurzfasertypen durchgeführt. Es wurde festgestellt, dass die Kurzfasern den Verbund zwischen Matrix und Multifilamentgarn verbessern. Kurzfasern können bei zufälliger Positionierung an der Garnoberfläche zusätzliche Haftbrücken bzw. Verbindungsstellen zu umgebender Matrix bilden. Für die Verbundqualität zwischen Faser und Matrix ist der Wasser-Bindemittel-Wert (W/B-Wert) von entscheidender Bedeutung. Bei einer Matrix mit niedrigem W/B-Wert führt die gute Qualität des Verbunds der eingebetteten Fasern zu einer Erhöhung der Steifigkeit sowie der Festigkeit des Komposites. Bei hohem W/B-Wert haben die Fasern einen schlechten Verbund zur Matrix und müssen überwiegend als Fehl- bzw. Schwachstellen betrachtet werden. Festigkeit und Steifigkeit des Komposits nehmen daher ab. Die Ableitung mathematischer Beziehungen für Textilbeton mit Zugabe von Kurzfasern unter verformungsgesteuerter Zugbelastung erfolgte aufbauend auf den Ergebnissen der experimentellen Untersuchungen auf der Mikroebene. Die Einzelfaserauszugsversuche wurden mit Hilfe eines physikalisch basierten Modelles nachgebildet, das aus einfachen rheologischen Elementen besteht. Phänomene wie die graduelle Ablösung der Faser, Faserbruch und Faserauszug wurden durch eine entsprechende Kombination und Parametrierung der rheologischen Elemente abgebildet. Im Ergebnis wurden zutreffende Kraft-Rissöffnungsbeziehungen modelliert. Auf der Mesoebene wurde ein einzelner Riss modelliert, der sowohl durch Multifilamentgarne als auch Kurzfasern überbrückt werden kann. Der rissüberbrückenden Wirkung der zahlreichen Kurzfasern wurde mit Hilfe statistischer Methoden rechnung getragen, die unterschiedliche Faser-Risswinkel und Einbindelängen berücksichtigen. Die resultierende Spannungs-Rissöffnungskurve umfasst die rissüberbrückende Wirkung von Multifilamentgarnen und Kurzfasern. Auf der Makroebene kann die charakteristische Spannungs-Dehnungsbeziehung von TRC unter Zugbelastung in 3 Bereiche (Zustände I, IIa, IIb) unterteilt werden. Die Kurvenverläufe im Zustand I (ungerissenen) sowie Zustand IIb (abgeschlossenes Rissbild) wurden als linear betrachtet und basierend auf den entsprechenden charakteristischen Werten des jeweiligen Zustands beschrieben. Das Verhalten im Zustand IIa (multiple Rissbildung) wurde durch die Reihenschaltung einer zunehmenden Anzahl von Rissen sowie den Beitrags der ungerissenen Matrix zwischen den Rissen modelliert.