An evaluation of solder joints of palladium-based alloys produced by infrared energyDiaz-Siohl, Jesus Alfredo. January 1988 (has links)
Thesis (M.S.)--University of Michigan, Ann Arbor, 1988. / Typescript (photocopy). Includes bibliographical references (leaves 145-149). Also issued in print.
|
2 |
An evaluation of solder joints of palladium-based alloys produced by infrared energyDiaz-Siohl, Jesus Alfredo. January 1988 (has links)
Thesis (M.S.)--University of Michigan, Ann Arbor, 1988. / Typescript (photocopy). eContent provider-neutral record in process. Description based on print version record. Includes bibliographical references (leaves 145-149).
|
3 |
Tensile strength comparison between presoldered and postsoldered joints a thesis submitted in partial fulfillment ... restorative dentistry ... /Monday, J. J. Luc. January 1981 (has links)
Thesis (M.S.)--University of Michigan, 1981.
|
4 |
Tensile strength comparison between presoldered and postsoldered joints a thesis submitted in partial fulfillment ... restorative dentistry ... /Monday, J. J. Luc. January 1981 (has links)
Thesis (M.S.)--University of Michigan, 1981.
|
5 |
Distribuição de tensões e resistência mecânica de infraestruturas de Ni-Cr-Ti sobre implantes após soldagem a laser ou TIG / Stress distribution and mechanical strength of the infrastructures of Ni-Cr-Ti implant after laser or TIG weldingPereira, Brunna Moreira de Farias, 1986- 02 April 2011 (has links)
Orientador: Mauro Antonio de Arruda Nóbilo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T16:32:53Z (GMT). No. of bitstreams: 1
Pereira_BrunnaMoreiradeFarias_M.pdf: 1704488 bytes, checksum: 28150f2bf1280c8cede7a934b8c40a4e (MD5)
Previous issue date: 2011 / Resumo: O objetivo neste estudo foi avaliar, por meio da análise fotoelástica e teste de resistência à flexão, as técnicas de soldagem a Laser e TIG (Tungsten Inert Gas) na confecção de infraestruturas implantossuportadas de NiCrTi. Três grupos foram formados com 5 amostras cada: infraestruturas fundidas em monobloco, soldadas a Laser ou TIG. O modelo fotoelástico foi confeccionado com resina flexível (Polipox® GIII - Indústria e Comércio Ltda. - SP), a partir da moldagem de transferência de uma matriz em aço inoxidável com 4 análogos de implantes de diâmetro regular e hexágono externo. As tensões, causadas pela instalação das infraestruturas com torque de 20Ncm no modelo fotoelástico, foram analisadas num polariscópio circular e registradas por máquina fotográfica (Cyber-Shot DSC-717 - Sony). Posteriormente foi realizado o ensaio de resistência mecânica realizado na máquina de ensaios universais (Model 4411, Instron corp., Canton, MA). As infraestruturas foram parafusadas sobre a matriz metálica e posicionadas na máquina de testes mecânicos que foi ajustada para deslocar 2mm por minuto até a ocorrência de fratura do cantilever. Os resultados obtidos foram tabulados e submetidos à análise de variância (One-Way) e teste de Tukey com 5% de significância. Os resultados mostraram que não houve diferença estatística das tensões cisalhantes máximas com relação às técnicas de soldagem utilizadas e com relação as infraestruturas em monobloco, porém, as maiores tensões foram encontradas ao longo dos implantes do lado direito do modelo. As estruturas em monobloco e soldadas a Laser apresentaram maior resistência à fratura quando comparadas às soldadas a TIG. / Abstract: The aim of this study was to assess by photoelastic analysis and hrough a test of resistance to bending, welding techniques, Laser and TIG (Tungsten Inert Gas) in the manufacturing infrastructure of implant suported NiCrTi. Three groups were formed with 5 samples each: infrastructure framework cast in one piece cast metal and Laser welded and TIG welded. The photoelastic model was made of flexible resin (Polipox® GIII - Industry and Trade Ltda. - SP), from the transfer impression of an array of stainless steel with 4 similar implants in reglular diameter and hexagonal external connection. The tensions caused by the installation infrastructure with 20 Ncm torque on the photoelastic model, were analyzed in a circular polariscope and recorded by camera (Cyber-Shot DSC-717 - Sony). Later, the resistance test was performed on the mechanical universal testing machine (Model 4411, Instron corp., Canton, MA). The infrastructure has been bolted on to metal matrix and positioned in mechanical testing machine which was set to move 2mm per minute until the occurrence of fracture of the cantilever. The results were tabulated and submitted to ANOVA (One-Way and Two-Way) and Tukey's test at 5% significance. The results showed no statistical difference of maximum shear stress between any of the techniques used, however, the highest stresses were found along the right side of the implant model. The one piece frameworks showed higher fracture resistance when compared to the TIG welded. / Mestrado / Protese Dental / Mestre em Clínica Odontológica
|
6 |
Análise fotoelástica das tensões e resistência mecânica de infraestruturas de titânio sobre implantes após soldagem a Laser e TIG / Photoelastic analysis of stress and mechanical framework titanium implant after welding and TIGSilva, Maíra Daysê Moreira Serra e 17 August 2018 (has links)
Orientador: Mauro Antonio de Arruda Nóbilo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T15:53:34Z (GMT). No. of bitstreams: 1
Silva_MairaDayseMoreiraSerrae_M.pdf: 4885020 bytes, checksum: 8933e2fbe0ea03e889685d1620189f34 (MD5)
Previous issue date: 2011 / Resumo: Para o sucesso da permanência dos implantes ¿in loco¿ e da reabilitação protética, destaca-se a biomecânica como um fator fundamental. Com o objetivo de obter estruturas metálicas com melhor assentamento e maior resistência mecânica este estudo avaliou, comparativamente, duas técnicas de soldagem a Laser Nd: YAG (neodínio iátrio alumínio garnet), (Desktop Laser ¿ Dentaurum JP Winkelstroter KG, Pforzhein, Alemanha) e Tungstênio Gás Inerte (TIG) (Solda Plasma Micropulsada Micromelt - EDG, São Carlos, SP, Brasil). Por meio de análise fotoelástica e ensaios de resistência à flexão, foi avaliada a distribuição das tensões geradas ao redor de implantes em próteses implantossuportadas, tipo ¿protocolo¿ inferior, bem como a resistência dos cantilevers. Foram confeccionadas 15 infraestruturas em titânio sobre uma matriz metálica, em forma de arco, contendo quatro análogos de implantes do tipo hexágono externo, de diâmetro regular (3,75 X 13mm). Os corpos-de-prova foram separados em três grupos: GI, ou grupo controle, formado por infraestruturas de titânio comercialmente puro (Ti cp) em monobloco; GII, infraestruturas soldadas a Laser e GIII, soldadas a TIG. Para análise das tensões foi confeccionado um modelo fotoelástico (Resina Flexível / Polipox® Indústria e Comércio Ltda), seguido do posicionamento das infraestruturas, e através de um polariscópio circular foram avaliados trinta e nove pontos ao redor dos implantes, após torque de 20Ncm nos parafusos e quantificado as franjas obtendo valores de tensão cisalhante a partir da ¿Lei Ótica das Tensões¿. Em seguida, foi realizado o ensaio mecânico de resistência à flexão em uma máquina de ensaios universais (Instron). Os dados obtidos foram submetidos à análise de variância (um e dois fatores), seguida do teste de Tukey para comparação entre as médias, com nível de significância p?0,05. Os resultados mostraram não haver diferença estatística entre os valores de tensão cisalhante (?) para as duas técnicas de soldagem, porém, as estruturas em monobloco apresentaram menores valores de tensão, com diferença estatística em relação à solda TIG. Quanto ao ensaio mecânico, resultados estatisticamente diferentes entre as técnicas foram obtidos, sendo o grupo I, o de maior resistência mecânica à flexão, seguido pela solda Laser e TIG. Baseados nos resultados obtidos, pode-se concluir que a técnica de fundição é que apresenta maior resistência mecânica à flexão. / Abstract: For the success of the permanence ¿in loco¿ implants and the rehabilitation, biomechanical is a very important factor. Aiming to obtain frameworks with better fit, this study compared one-piece casted frameworks to frameworks obtained by two different soldering techniques: Laser-welding Nd: YAG (neodínio iátrio alumínio garnet), (Desktop Laser - Dentaurum Winkelstroter KG, Pforzhein, Germany) and Tungsten Inert Gas (TIG - Plasma Micropulse Micromelt - EDG, Sao Carlos, SP, Brazil). Thru photoelastic analysis and flexural strength tests, the stress distribution around implants and the mechanical resistance of the frameworks were evaluated. Fifteen commercially pure titanium frameworks were obtained using a steel matrix, with four external-hexagon regular-diameter (3.75 x 13mm) implants (Branemark protocol). The frameworks were divided into three groups: GI, or control group - one-piece casted frameworks; GII - Laser welded frameworks; GIII ¿ TIG welded frameworks. For stress analysis a photoelastic model, reproducing the steel matrix was manufactured with photoelastic flexible resin (Polipox® Industry and Trade Ltd.). Each framework was screwed with 20Ncm torque to the photoelastic models? implants through a circular polariscope, the order of the isochromatic fringes at thirty nine predetermined points around the implants was obtained. Maximum sheer stress was determined for each point through the ¿stress optical law¿. Then, a mechanical testing of flexural strength was performed at the hanging arms? joints of each framework. The data were submitted to ANOVA (One-Way and Two-Way), followed by Tukey test (p ? 0.05). The results showed no statistical difference between shear stress values (?) between the welding techniques, but the casting technique showed lower stress values, with statistical difference compared to TIG welding. As for the mechanical test, statistically different results between the techniques were obtained, GI presented higher ductility, followed by laser welding and TIG. Based on these results, it was concluded that the conventional casting technique is more mechanically resistant than the welding techniques. / Mestrado / Protese Dental / Mestre em Clínica Odontológica
|
7 |
Influencia da soldagem laser e ciclos de cocção da porcelana no desajuste marginal de infra-estruturas de proteses fixas em titanio comercialmente puro e titanio-aluminio-vanadio fundidos pelas tecnicas convencional e sobre-modelo refratario / Influence of the laser-welding and ceramic firing cycle over the desadaptation frameworkd margins of commercially pure titanium and titanium-aluminum-vanadium alloy with the conventional casting and refractory dieCorrea, Giovani de Oliveira 07 May 2003 (has links)
Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-04T19:03:33Z (GMT). No. of bitstreams: 1
Correa_GiovanideOliveira_D.pdf: 622152 bytes, checksum: a395604ad381cd7abfdc99e9110c1421 (MD5)
Previous issue date: 2005 / Resumo: A soldagem é uma alternativa para a obtenção de melhor ajuste marginal de retentores metálicos de próteses fixas de três ou mais elementos aos respectivos pilares, em detrimento da fundição tipo monobloco (peça única). No entanto, há a possibilidade de defeitos nas uniões soldadas ou distorções de todo o conjunto. Embora a adaptação não esteja assegurada, as fundições tipo monobloco são vantajosas quanto à economia de tempo, resistência e durabilidade da infra-estrutura. O propósito desse estudo foi a avaliar a soldagem laser na redução do desajuste marginal de infra-estruturas fundidas em titânio comercialmente puro e titânio-alumínio-vanádio; os efeitos do ciclo de cocção da porcelana no desajuste marginal em infra-estruturas de próteses fixas fundidas em monoblocos sobre-modelo refratário, comparando os resultados com a técnica convencional de fundição de próteses fixas. Inicialmente confeccionou-se uma matriz metálica, sendo esta moldada em silicona por adição para a obtenção dos modelos de trabalho. Sobre os modelos foram encerados os padrões simulando infra-estruturas de próteses fixas, correspondendo às fundições convencionais nas duas ligas avaliadas. Para a fundição sobre-modelo, a matriz metálica foi duplicada e modelos em revestimento Rematitan Plus foram obtidos. Sobre os modelos de revestimento foram encerados os padrões simulando as infra-estruturas protéticas, sendo o conjunto padrões/modelo refratário, incluído para a realização das fundições. As infra-estruturas fundidas foram jateadas com óxido de alumínio, ajustadas internamente e acabadas por fresas. Os desajustes marginais foram medidos em microscópio mensurador (Olympus - Japão) com aumento de 50 X. Após a aplicação dos respectivos tratamentos, as infra-estruturas foram submetidas à simulação dos ciclos de cocção (bonder; opaco; corpo e; glaze). As mensurações foram realizadas após todas as fases do estudo, os dados foram tabulados e submetidos a Análise de variância com parcela subdividida e ao teste de Tukey em nível de 5% de significância. Concluiu-se que: a soldagem a laser foi eficaz na redução dos desajustes nas infra-estruturas em ambas as ligas; a etapa bonder interferiu no desajuste nas infra-estruturas / Abstract: Soldering has been an alternative for achieving acceptable marginal fit of metallic crowns of 3-unit fixed frameworks to the respective abutments, in detriment of the single-piece casting. However, defects at the joined areas or distortions of the entire frame are frequent. Although adaptation can not be assured, single-piece casting presents advantages such as time saving, strength and strength of the framework. The purpose of this study was to evaluate: the laser-welding in the decrease of unfitted frameworks margins of commercially pure titanium and titanium-aluminum-vanadium alloy; the effects of the ceramic firing cycle over the unfitted frameworks margins using the method of single-piece casting using a refractory die, comparing the results with the conventional casting technique for fixed prosthodontics. Initially a metallic cast was prepared and duplicated using addition silicone for making working casts. For the conventional technique, the 3-unit simulated frameworks were waxed over the working casts. For the single-piece casting, the metallic cast was duplicated and investment dies were made (Rematitan Plus ¿ c.p. Ti and Ti-6Al-4V). The frameworks were waxed on the investment casts that were invested for the castings. After casting, the frameworks were air-abraded with aluminum oxide particles, adjusted and finished with the aid of wheels. The marginal fit was measured under a measurer microscope (Olympus ¿ Japan) with X50 magnification. After laser welding, frameworks were submitted to firing cycle (bonder, opaque, dentin and glaze). The marginal fit was measured after the studies¿ steps. ANOVA and Tukey¿s tests were used in the statistical analysis of the results (P<0.05). It was concluded that the laser-welding was effective in the decrease of marginal unfit of the frameworks on both alloys; the bonder application did not interfere on the marginal fit of the frameworks / Doutorado / Doutor em Materiais Dentários
|
8 |
Estudo da densidade óptica e da resistência à flexão de três pontos em corpos-de-prova fundidos com a liga metálica High Bond (Co-Cr), com secções vertical 90°, diagonal 45° e diagonal 22,5°, soldados pelas técnicas convencional e TIGPereira, Leonardo Viana [UNESP] 06 September 2012 (has links) (PDF)
Made available in DSpace on 2014-06-11T19:28:58Z (GMT). No. of bitstreams: 0
Previous issue date: 2012-09-06Bitstream added on 2014-06-13T19:58:25Z : No. of bitstreams: 1
000738161.pdf: 8215678 bytes, checksum: 0fb4df9ab1185429ce16edda73d5c2b2 (MD5) / O sucesso das próteses sobreimplantes está diretamente relacionado ao grau de adaptação dos componentes protéticos aos implantes. Com a finalidade de se obter um assentamento passivo entre a prótese e os implantes, as estruturas metálicas são confeccionadas inicialmente segmentadas e, posteriormente, soldadas clinicamente para minimizar as distorções do processo de fundição. O sistema TIG (Tungsten Inert Gas) é definido como uma soldagem de arco elétrico, estabelecido entre um eletrodo não consumível à base de tungstênio e a peça a ser soldada. O propósito desse estudo foi, através do uso da densidade óptica e de um teste mecânico de resistência à flexão de 3 pontos, analisando a rigidez do material e a tensão de flexão, verificar o comportamento de dois sistemas de soldas odontológicas: convencional e TIG, realizadas em diferentes angulações (90°, 45° e 22,5°) de secções das porções a serem soldadas, comparando-os a um grupo fundido em monobloco (controle), em uma liga de Co-Cr. Os grupos foram comparados entre si quanto à densidade óptica, rigidez, tensão de flexão. A análise dos resultados obtidos possibilitou as seguintes conclusões: 1. Em relação à análise dos dados da densidade óptica mostrou que o grupo controle apresentou-se mais eficientes, estatisticamente significantes, quando comparadas aos grupos do sistema de solda TIG; não houve diferenças estatisticamente significantes entre as diferentes angulações num mesmo sistema de soldagem, porém quando comparados os sistemas de soldagem numa mesma angulação, o grupo de 22,5°-solda convencional teve resultado melhor, estatisticamente significante, que o 22,5°-solda TIG; 2. Em relação à rigidez (modulo de elasticidade), houve diferença estatisticamente significante apenas quando se comparou os corpos com angulação de 90° com diferentes soldas, tendo resultados maiores com... / The success of the prosthesis over implant is directly related to the adaptation degree of the prosthesis components to implants. Aiming to obtain a passive fit between the prosthesis and the implant, initially the metal structures are segmented and later are clinically welded to minimize the distortions of the casting process. The TIG system (Tungsten Inert Gas) is defined as a welding of an electric arc, established between a non consumable electrode based on tungsten and the part to be welded. The purpose of this study was to use the optical density and a mechanical test of 3 points flexion endurance, to analyze the stiffness of the material and the bending stress and to verify the behavior of two systems of dental welders: conventional and TIG performed at different angles (90º, 45º e 22, 5º) of the sections of the portions to be welded, and compare them to a group fused on monobloc (control) in an alloy of Co-Cr. The groups were compared on optical density, stiffness and bending stress. Analysis of the results made possible the following conclusions: 1. The analysis of the data showed that the optical density of the control group was more efficient, statistically significant, when compared to the groups with TIG welding system; there were no statistical differences between the different angles on the same welding system, although when comparing the welding systems in the same angle, the group of 22,5º- conventional welding had better result than the 22,5º - TIG welding, this difference was statistically significant; 2. There was statistical significant difference regarding the stiffness (modulus of elasticity) only when it was compared the bodies with the 90º angle with different welds, the higher results were with the conventional welding; 3. The results of the...
|
9 |
Estudo da densidade óptica e da resistência à flexão de três pontos em corpos-de-prova fundidos com a liga metálica High Bond (Co-Cr), com secções vertical 90°, diagonal 45° e diagonal 22,5°, soldados pelas técnicas convencional e TIG /Pereira, Leonardo Viana. January 2012 (has links)
Orientador: Stefan Fiuza de Carvalho Dekon / Banca: Marco Polo Marchese / Banca: Gilberto Aparecido Coclete / Resumo: O sucesso das próteses sobreimplantes está diretamente relacionado ao grau de adaptação dos componentes protéticos aos implantes. Com a finalidade de se obter um assentamento passivo entre a prótese e os implantes, as estruturas metálicas são confeccionadas inicialmente segmentadas e, posteriormente, soldadas clinicamente para minimizar as distorções do processo de fundição. O sistema TIG (Tungsten Inert Gas) é definido como uma soldagem de arco elétrico, estabelecido entre um eletrodo não consumível à base de tungstênio e a peça a ser soldada. O propósito desse estudo foi, através do uso da densidade óptica e de um teste mecânico de resistência à flexão de 3 pontos, analisando a rigidez do material e a tensão de flexão, verificar o comportamento de dois sistemas de soldas odontológicas: convencional e TIG, realizadas em diferentes angulações (90°, 45° e 22,5°) de secções das porções a serem soldadas, comparando-os a um grupo fundido em monobloco (controle), em uma liga de Co-Cr. Os grupos foram comparados entre si quanto à densidade óptica, rigidez, tensão de flexão. A análise dos resultados obtidos possibilitou as seguintes conclusões: 1. Em relação à análise dos dados da densidade óptica mostrou que o grupo controle apresentou-se mais eficientes, estatisticamente significantes, quando comparadas aos grupos do sistema de solda TIG; não houve diferenças estatisticamente significantes entre as diferentes angulações num mesmo sistema de soldagem, porém quando comparados os sistemas de soldagem numa mesma angulação, o grupo de 22,5°-solda convencional teve resultado melhor, estatisticamente significante, que o 22,5°-solda TIG; 2. Em relação à rigidez (modulo de elasticidade), houve diferença estatisticamente significante apenas quando se comparou os corpos com angulação de 90° com diferentes soldas, tendo resultados maiores com ... / Abstract: The success of the prosthesis over implant is directly related to the adaptation degree of the prosthesis components to implants. Aiming to obtain a passive fit between the prosthesis and the implant, initially the metal structures are segmented and later are clinically welded to minimize the distortions of the casting process. The TIG system (Tungsten Inert Gas) is defined as a welding of an electric arc, established between a non consumable electrode based on tungsten and the part to be welded. The purpose of this study was to use the optical density and a mechanical test of 3 points flexion endurance, to analyze the stiffness of the material and the bending stress and to verify the behavior of two systems of dental welders: conventional and TIG performed at different angles (90º, 45º e 22, 5º) of the sections of the portions to be welded, and compare them to a group fused on monobloc (control) in an alloy of Co-Cr. The groups were compared on optical density, stiffness and bending stress. Analysis of the results made possible the following conclusions: 1. The analysis of the data showed that the optical density of the control group was more efficient, statistically significant, when compared to the groups with TIG welding system; there were no statistical differences between the different angles on the same welding system, although when comparing the welding systems in the same angle, the group of 22,5º- conventional welding had better result than the 22,5º - TIG welding, this difference was statistically significant; 2. There was statistical significant difference regarding the stiffness (modulus of elasticity) only when it was compared the bodies with the 90º angle with different welds, the higher results were with the conventional welding; 3. The results of the... / Mestre
|
10 |
Distribuição de tensões e resistência mecânica de infraestruturas de cobalto-cromo sobre implantes após soldagem a Laser e TIG / Stress distribution and mechanical strength of chrome-cobalt framework on implanta after laser or TIG weldingCastro, Gabriela Cassaro de, 1986- 02 October 2011 (has links)
Orientador: Mauro Antonio de Arruda Nóbilo / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-17T15:56:25Z (GMT). No. of bitstreams: 1
Castro_GabrielaCassarode_M.pdf: 1780672 bytes, checksum: 8af543ab2352bb5187bc910fb554c95d (MD5)
Previous issue date: 2011 / Resumo: A passividade e a resistência mecânica dos cantiléveres são fatores importantes na avaliação do comportamento biomecânico das próteses implantossuportadas. A proposta neste estudo foi avaliar a influência de três diferentes técnicas de confecção de estruturas implantossuportadas em liga de Co-Cr quanto à passividade e resistência mecânica, por meio de análise fotoelasticidade e teste de resistência à flexão, respectivamente. A partir de uma matriz de aço simulando uma mandíbula edêntula com 4 análogos de implantes hexágono externo com plataforma regular, foi obtido o modelo de trabalho. Sobre este modelo cinco estruturas foram confeccionadas para cada grupo: estruturas em monobloco, soldadas a TIG e a Laser. O modelo fotoelástico foi confeccionado com resina epoxi flexível (GIII, Polipox Indústria e Comércio Ltda, São Paulo). Na análise fotoelástica, as estruturas foram aparafusadas no modelo para a verificação da tensão cisalhante máxima em 34 pontos selecionados ao redor dos implantes e 5 pontos na região mediana do modelo. Foram avaliadas as tensões em todo o modelo fotoelástico, entre as regiões direita, esquerda e central e ainda, entre a região cervical e apical. O teste de resistência à flexão foi realizado em uma máquina de ensaios mecânicos Instron (Instron Co., Canton, Mass.). Os valores foram submetidos à analise de variância para dados com dois fatores de estudo (ANOVA 2-Way), seguidos pelo teste de Tukey para comparação entre as médias. Os resultados não apresentaram diferença significante entre as tensões presentes nos grupos e áreas estudadas. Para o teste mecânico as estruturas em monobloco foram mais resistentes que as soldadas a Laser, que por sua vez, foram mais que as soldadas a TIG. Concluiu-se que as tensões geradas ao redor dos implantes foram semelhantes entre as diferentes técnicas de confecção, e entre todas as regiões analisadas. E as estruturas em monobloco apresentaram melhor resistência, seguida das soldadas a Laser. / Abstract: Passive fitting frameworks and cantilever¿s mechanical strength are important aspects in implant fixed prostheses biomechanical behavior. The proposal of this study was to evaluate the passivity end mechanical strength of tree different Co-Cr alloy framework manufactured technique, by photoelasticity analysis and flexural strength test. In a curved steel matrix, simulating an edentulous mandible, four external hexagon with regular platform implant analogs were positioned. Five frameworks for each group were obtained: one-piece cast, TIG welding and Laser welded frameworks. The photoelastic model was made from flexible epoxy resin (GIII, Polipox Industry e Comerce Ltda, Sao Paulo). To photoelastic analysis, the frameworks were bolted on the model and seventeen points around the implants were selected for right and left regions, to measure the maximum shear stress. At the middle area, 5 points on the medium of the model, was measured. Were evaluated the stress generated around all the implants in the photoelastic model, around implants in selected area (right, left and middle), and the stress on the cervical and apical model¿s area. The frameworks were submitted to flexural strength test in an Instron machine (Instron Co., Canton, MA, USA). The data were statistically analyzed using a 2-way analysis of variance (ANOVA) and Tukey test. The results showed no significant difference between any evaluated groups or areas. In the flexural strength test, one-piece frameworks were more resistant than Laser welded, which were more resistant than the TIG welded. In conclusion, the stresses around the implants were similar among the different framework manufacturing techniques and among all evaluated areas. And one-piece casting framework showed better resistance, followed by Laser welded and TIG welded frameworks. / Mestrado / Protese Dental / Mestre em Clínica Odontológica
|