Made available in DSpace on 2014-06-11T19:27:48Z (GMT). No. of bitstreams: 0 Previous issue date: 2002-05-14Bitstream added on 2014-06-13T20:36:15Z : No. of bitstreams: 1 jacques_p_me_arafo.pdf: 6578711 bytes, checksum: 7ce3c1075cc06b0164a5b42ddcb9c7d0 (MD5) / A resistência adesiva de um sistema auto-condicionante e um convencional simplificado, Clearfil SE Bond e Single Bond, respectivamente, quando aplicados à dentina superficial tratada com diferentes agentes condicionadores, foi avaliada por meio de ensaios mecânicos de microtração. Superfícies planas de dentina, obtidas removendo-se a superfície oclusal de 30 terceiros molares humanos foram polidas com lixa de granulação 600 antes da aplicação de diferentes agentes condicionadores, SE Primer, ácido fosfórico ou EDTA. O primer acidificado SE Primer foi aplicado sobre a superfície por 20 segundos, seguido de suave secagem com jatos de ar. O ácido fosfórico a 37% foi aplicado por 15 segundos, seguido de lavagem e remoção do excesso de água com papel absorvente e a solução de EDTA 0,5M pH7,2 foi aplicada por 30 segundos, também seguida de lavagem e secagem. Com exceção das superfícies que receberam a aplicação do primer acidificado, as demais foram mantidas úmidas para a posterior aplicação dos sistemas adesivos avaliados. Sobre a superfície coberta pelo sistema adesivo foi construída uma coroa em resina composta Z250 e os dentes foram mantidos em água a 37% por 24h. Após 500 ciclos térmicos em temperaturas de 5o e 55oC, cortes paralelos no sentido mesio-distal e cortes perpendiculares aos primeiros, no sentido vestibulo-lingual, permitiram a obtenção de amostras com área de secção transversal quadrangular de 1,0mm2 em número mínimo de 10 para cada dente. Cada amostra foi colada a um dispositivo especialmente desenvolvido, e este foi acoplado à uma máquina universal de testes operada à velocidade de 0,5mm/min. O lado correspondente à dentina de aproximadamente 50% das superfícies fraturadas após o ensaio mecânico foi analizado em MEV. Os resultados mostraram que o maior valor médio de resistência adesiva foi observado para a associação SE Primer... . / Microtensile bond strength of a self-etching primer and a conventional one-bottle system, Clearfi SE Bond and Single Bond, respectively, bonded to superficial dentin treated with different conditioners was investigated. Flat dentin surfaces obtained by removing the occlusal enamel with a diamond saw were ground with 600-grit SiCs under wet conditions to create the smear layer before the conditioners application. Three different dentin conditioning was performed, SE Primer, phosphoric acid and EDTA. The SE Primer was applied on dentin for 20 seconds followed by slight air-drying. Phosphoric acid (37%) was applied for 15 seconds followed by rinsing. EDTA 0.5M pH7.2 was applied for 30 seconds, also followed by water rinsing. Except for the surfaces that received the SE Primer conditioner, the surfaces were left moist by blot-drying the excess water. The adhesive systems were applied and a 5mm high composite resin (Z250) was built up covering the whole surface. After 24h of storage in water at 37oC the teeth were thermocycled for 500 cycles at preset temperatures of 5o and 55oC. The teeth were sectioned with a diamond saw, perpendicular to the adhesive interface to produce beams with 1.0mm2 of adhesive area. These specimens were then attached to a testing apparatus and a tensile load was applied by a universal machine at a crosshead speed of 0.5mm/min. After the micro-tensile bond test, the dentin side of 50% of the fractured surfaces was examined under a scanning electron microscope. The highest tensile bond strength mean was found for the association of SE Primer and Single Bond, 58.51MPa, followed by the association Clearfil SE Bond and EDTA, 47.81MPa. The remaining associations showed mean tensile bond strength statistically similar, except for the association Single Bond and EDTA, which showed the lowest... (Complete abstract, click electronic address below).

Orientador: Milton Carlos Kuga / Resumo: Os objetivos dos estudos foram avaliar os efeitos da cimentação provisória intrarradicular de um pino metálico com cimentos temporários, de composição química diferentes, e analisar a influência da irrigação com agitação ultrassônica passiva (PUI), sobre a resistência de união do cimento resinoso autoadesivo (Relyx U200) na dentina do espaço radicular preparado para pino de fibra de vidro. Noventa raízes unirradiculares de dentes humanos, foram padronizadas com o comprimento de 17,0 mm, a partir do ápice radicular. Os canais radiculares foram instrumentados até o instrumento F5, irrigados a cada troca de instrumento com 5 mL de hipoclorito de sódio a 2,5% e obturados com cimento contendo resina epóxi (AH Plus; Dentsply DeTrey GmbH, Konstanz, GER). Após 7 dias, foi preparado o espaço intrarradicular para pino de fibra de vidro, na extensão de 11mm, a partir da face cervical radicular, com brocas tipo Largo #1 e #2, e dada a conformação final com a broca #2 do sistema White Post DC (FGM, Joinville, SC, BR). No estudo 1, quarenta espécimes foram distribuídos em 4 grupos (n =10), de acordo com o tipo de protocolo de cimentação provisório do pino metálico: G1 (CO), sem a realização prévia da cimentação provisória do pino metálico intrarradicular; G2 (PR), cimentação provisória do pino metálico com o sistema Provy (Dentsply); G3 (RT) cimentação provisória do pino metálico com o sistema Relyx Temp NE (3M) e G4 (TB), cimentação provisória do pino metálico com o sistema Temp Bond NE (... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The aims of this study are to evaluate the effects of temporary intraradicular cementation of a metallic pin with temporary cements made from different chemical composition, and to analyze the influence of agitation with passive ultrasonic irrigation (PUI) on the bond strength of the self-adhesive resin cement (Relyx U200) in the root space dentin prepared for fiberglass pin. Ninety one-root human teeth were standardized with a length of 17.0 mm from the radicular apex. The root canals were instrumented up to instrument F5, irrigated at each instrument change with 5 mL of 2.5% sodium hypochlorite and filled with cement containing epoxy resin (AH Plus; Dentsply DeTrey GmbH, Konstanz, GER). After 7 days, the intraradicular space, 11mm in length, was prepared for the fiberglass pin, from the root cervical face with Largo # 1 and # 2 drills, and given the final conformation with the drill # 2 from White Post DC system (FGM, Joinville, SC, BR). In study 1, forty specimens were distributed into 4 groups (n = 10), according to the type of provisional cementation protocol of the metal pin: G1 (CO), without executing beforehand the provisional cementation of the intraradicular metallic pin; G2 (PR), provisional cementation of the metallic pin with Provy system (Dentsply); G3 (RT) temporary cementation of the metallic pin with Relyx Temp NE (3M) and G4 (TB) system, provisional cementing of the metallic pin with Temp Bond NE system (Sybron Kerr). In all groups, with exception of CO, met... (Complete abstract click electronic access below) / Mestre

O objetivo deste trabalho foi analisar em Microscopia Ótica (MO), Espectroscopia micro-Raman (µR) e Microscopia Eletrônica de Varredura (MEV), a interface adesiva em dentina proporcionada por três sistemas adesivos aplicados in vivo e in vitro. Na condição in vivo, pacientes com primeiros prémolares superiores hígidos indicados para extração, por razões ortodônticas, foram utilizados. Cavidades classe I com 0,5mm além da junção esmalte-dentina foram realizadas, nos dentes, com broca carbide 245 em alta rotação. Foram, então aplicados três sistemas adesivos diferentes foram aplicados, de acordo com as instruções dos respectivos fabricantes: Single Bond (SB-3M), Clearfil SE Bond (CSEB-Kuraray) e One Up Bond-F (OUB-Tokuyama). Aplicados esses, as cavidades foram restauradas incrementalmente com resina composta TPH Spectrum (Dentsply). Em seguida os dentes foram extraídos e armazenados em solução de timol a 0,1%. In Vitro, os mesmos procedimentos foram realizados em pré-molares extraídos. Após os dentes foram levados à uma máquina de cortes e seccionados, com auxílio de um disco de corte em espécimes contendo a interface, com dimensões 2mmx2mmx6mm de comprimento, sendo 2 espécimes para cada dente. Um dos espécimes foi levado a um micrótomo de tecido duro onde fatias com espessura de 5µm foram obtidas e coradas com Tricromo de Goldner. As fatias foram, então, analisadas em um microscópio óptico com aumento de 100 vezes. Nesta técnica a dentina mineralizada se cora de verde, o colágeno não infiltrado de vermelho e o sistema adesivo de beje translúcido. Após o mesmo espécime foi utilizado para análise em espectroscopia micro-Raman. O espécime adjacente foi desidratado em seqüência ascendente de etanol e analisado em microscopia eletrônica de varredura. Os resultados da MO para o sistema SB mostraram a presença de uma grande área corada de vermelho, indicando colágeno exposto ou não devidamente infiltrado pelo sistema adesivo para ambas as situações porém, in vivo, esta camada se mostrou maior. Para o sistema CSEB esta camada se corou de roxa, consistente ao longo de toda interface, indicando também a presença de colágeno disponível para reação com o corante, para ambas as situações. Para o sistema OUB esta camada também se corou de roxa, porém in vivo esta se mostrou mais fina e irregular que in vitro. Em MEV o sistema SB apresentou uma camada híbrida granular e porosa para ambas as situações. In vitro esta se mostrou mais espessa e regular ao longo da interface ao contrário da condição in vivo. Grandes diferenças foram observadas em relação aos tags de resina, onde in vivo, se apresentaram mais finos e curtos. Para o sistema CSEB a camada híbrida se mostrou mais fina quando comparada ao sistema SB porém, mais homogênea e compacta ao longo da interface para ambas as situações. Grandes diferenças foram observadas em relação aos tags de resina onde in vivo foram significativamente em menor número, curtos e finos. Para o sistema OUB in vitro a camada híbrida se apresentou fina porém, homogênea em sua extensão com a presença de longos tags. In vivo a camada híbrida se apresentou bastante fina e até difícil de se detectar. O tags se apresentaram quase inexistes ou muito dobrados devido à pobre polimerização desse sistema. As análises em µR para o sistema SB mostraram uma maior contribuição do sistema adesivo nos dois primeiros micrometros da interface, ao passo que, no restante da mesma, houve pouca contribuição dos monômeros adesivos na proteção do colágeno. Para o sistema CSEB a interface se mostrou bastante fina (1µm), para ambas as condições, porém com contribuição, no complexo hibridizado, dos componentes adesivos, colágeno e mineral. Para o sistema OUB in vitro, os espectros também indicaram a presença de uma interface fina, em torno de 1µm, mas também com contribuição dos componentes adesivos, colágeno e mineral. In vivo, esta não pôde ser detectada pelo Raman por ser inexistente ou ser mais fina que a resolução do Raman (1 µm). Realizada as análises da interface em ambas condições experimentais, com os diferentes sistemas adesivos utilizados, conclui-se que: a condição in vivo proporcionou uma interface de menor qualidade para todos os sistemas. O sistema CSEB aparentemente proporcionou uma melhor qualidade de interface e o sistema OUB a pior. O uso dessas três técnicas integradas permitiu uma análise completa, qualitativa e quantitativa da interface adesiva produzida por esses três sistemas, em ambas as condições testadas. / The aim of this research was to analyze in Light Microscopy (LM), micro-Raman Spectroscopy (µR) and Scanning Electron Microscopy (SEM), the dentin-adhesive interface produced by three different bonding systems applied in vivo and in vitro. In in vivo condition patients with the first upper premolars, to be extract for orthodontic reasons, were used. Class I cavities with 0.5mm below the dentin-enamel junction were performed, with carbide bur in high speed. Following, three different bonding systems were applied in accordance with their manufacturer instruction: Single Bond (SB-3M), Clearfil SE Bond (CSEB-KURARAY) and One Up Bond-F (OUBTokuyama), and the cavities restored, incrementally, with composite resin TPH Spectrum (Dentsply). After restoration the teeth were extracted and stored in 0,1% tymol solution. In vitro, the same procedures were performed in extracted upper premolars. Following, the teeth were taken to a cutting machine and cross-sectioned with as diamond saw in specimens with 2mmX2mmx6mm dimensions, being 2 specimens for each tooth. One of the specimen was taken to a hard tissue microtome were 5µm slabs were obtained and stained with Goldner´s Tricrome. The slabs were analyzed in a Light Microscope with 100 times magnification. In this technique, the mineralized dentin is stained green, the collagen is stained red and the bonding system a pale orange. After, the same specimen was used for micro-Raman analysis. The adjacent specimen was dehydrated in ascendant ethanol sequence and analyzed in scanning electron microscopy. The LM results for SB showed the presence of a large area stained red for both conditions, indicating the presence of exposed or non protected collagen by the bonding system. This area was larger in vivo than in vitro. For CSEB this layer war purple stained and consistent along the interface for both situations, indicating, also, collagen available to react with the staining. For OUB this layer was also purple however, in vivo, this layer was thinner and inconsistent than in vitro. In SEM analysis, SB bonding system presented a porous hybrid layer for both situations. In vitro this layer was thicker and regular along the interface and, in vivo, thinner and irregular. Big differences were observed related to the resin tags. In vivo they were thinner and shorter. For CSEB the hybrid layer was thinner when compared with SB however, more homogeneous and compact along the interface for both situations. Big differences were observed related to the resin tags. In vivo, they were significantly in fewer amounts, shorter and thinner. For OUB in vitro, the hybrid layer was thin, however, homogeneous and with long tags. In vivo, the hybrid layer was very thin, almost undetectable. The resin tags were almost non-existent or bended due to poor polymerization of this system. In micro-Raman analysis for SB showed a greater contribution of the bonding system in the first two micrometers of the interface was detected and, in the rest of the interface, there was few contribution of the resin monomers in the collagen protection. For CSEB the interface was thin (1µm), for both conditions, however, with contribution, in the hybridized complex, of the adhesives components, collagen and mineral. For OUB in vitro, the spectras also indicated the presence of a thin interface, among 1µm, but also, with contribution of the bonding components, collagen and mineral. In vivo, the interface could not be detected by the Raman, for being inexistent, or by the fact to be thinner than the Raman resolution (1µm). After all these analysis of the bonding interface, for both conditions, and with these different bonding systems, it can be concluded that: in vivo condition produced a less-quality interface for all the system. CSEB apparently produced a better-quality interface and OUB the worst. The use of these three techniques together allowed a complete analysis, qualitative and quantitative, of the dentin-bonding interface produced by these three bonding systems, for both situations.

Esse estudo in vitro avaliou a resistência adesiva da dentina preparada com laser de Er:YAG ou broca, reidratada com clorexidina ou água deionizada, após armazenamento em saliva artificial e termociclagem. Cento e vinte terceiros molares humanos hígidos foram seccionados no terço médio da coroa, expondo a superfície dentinária (n=10). Os espécimes foram divididos aleatóriamente de acordo com o tratamento [laser de Er:YAG + reidratação com água deionizada (LW), laser de Er:YAG + reidratação com clorexidina a 2% (LC), turbina de alta-rotação com broca #245 + reidratação com água deionizada (TW) e turbina de alta-rotação com broca #245 + reidratação com clorexidina a 2% (TC)]. Após o preparo da dentina, os espécimes foram condicionados com ácido fosfórico 35%, lavados e secos com ar. A reidratação da dentina foi realizada através da aplicação de 1.5!L de água deionizada ou clorexidina 2%. Um sistema adesivo etch and rinse foi aplicado seguido da restauração com resina composta. Em cada grupo os espécimes foram sub-divididos de acordo com o envelhecimento [24 horas de armazenamento em saliva artificial / sem termociclagem (NA); 6 meses de armazenamento em saliva artificial / 12.000 ciclos térmicos (6A); 12 meses de armazenamento em saliva artificial / 24.000 ciclos térmicos(12A)]. Após cada período de envelhecimento, os dentes foram seccionados a fim de se obter 4 palitos com area de ±1.0 mm2, que foram submetidos ao teste de microtração usando uma máquina universal de testes com velocidade de 0.5 mm/min. Para a análise da interface adesiva em MEV foram utilizados 36 terceiros molares hígidos (n = 3) que foram restaurados e envelhecidos como descrito no protocolo empregado para o teste adesivo. ANOVA a dois critérios mostrou que não houve diferença significante para a interação entre os fatores e para o fator envelhecimento. O teste de Tukey 5% mostrou que o grupo LC apresentou os menores valores de resistência adesiva. A análise da interface adesiva através da MEV demonstrou que para os grupos irradiados houve formação de camada híbrida irregular com presença de fendas e o envelhecimento não interferiu na morfologia da interface adesiva. A reidratação com clorexidina influenciou negativamente a resistência adesiva do prepare com laser de Er:YAG. O envelhecimento em saliva artificial e termociclagem não interferiram na resistência adesiva da dentina. / This in vitro study evaluated the bond strength of dentin prepared with Er: YAG laser or turbine, rehydrated with chlorhexidine or deionized water after artificial saliva storage and thermocycling. One hundred twenty human third molars were sectioned in order to expose the dentin surface (n=10). The specimens were equally and randomly divided according to treatment [Er:YAG laser + deionized water rehydration (LW), Er:YAG laser + chlorhexidine 2% rehydration (LC), bur on high-speed turbine + deionized water rehydration (BW) and bur on high-speed turbine + chlorhexidine 2% rehydration (BC)]. After dentin preparation, the specimens were etched with 35% phosphoric acid, washed and dried with air. The dentin rehydration method was performed with deionized water or chlorhexidine 2% by applying 1.5!L of each solution. An etch and rinse adhesive system was then applied and the samples were restored with a composite. In each group, the specimens were sub-divided in accordance with the aging method [24 hours artificial saliva storage, no thermocycling (NA); 6 months of artificial saliva storage, 12.000 thermocycling (6A); 12 months of artificial saliva storage, 24.000 thermocycling (12 A)]. After each aging period, each tooth was sectioned in order to obtain 4 sticks with a cross-sectional area of 1.0 mm2, which were submitted to microtensile test using the Universal Test Machine (0.5 mm/min). For the adhesive interface analysis by SEM, 36 healthy third molars (n=3) were restored and aged as the protocol used for the adhesive test. The two-way ANOVA showed no significant differences for the interaction between the factors and for the aging factor. Tukey test 5% showed that the LC group had the lowest bond strength values. The adhesive interface analysis by SEM showed that the irradiated groups presented irregular hybrid layer and cracks and the aging did not affect the adhesive interface morphology. The rehydration with chlorhexidine negatively influenced the bond strength of the preparation with the Er:YAG laser. The artificial saliva aging and thermocycling did not interfere with dentin bond strength.

A utilização de biopolímeros na dentina desmineralizada tem sido analisada com o intuito de melhorar as propriedades mecânicas e estruturais da dentina previamente ao procedimento restaurador. Este estudo in vitro avaliou o efeito da reumificação da dentina com quitosana em diferentes concentrações sobre a resistência adesiva, composição química da dentina e morfologia da interface dentina/resina. Os fatores em estudo foram substrato dentinário em dois níveis: hígido e desmineralizado; e reumidificação da dentina em quatro níveis: quitosana a 2,5%, quitosana a 5,0%, ácido acético a 1,0% (placebo) e ausência de reumidificação (controle). Oitenta dentes bovinos foram seccionados no terço médio da coroa para obtenção dos espécimes de dentina (7,0 X 7,0 mm). Os espécimes foram planificados e polidos, e então foram divididos aleatoriamente em 8 grupos (n=10). Metade dos espécimes foi submetida à indução de cárie artificial pelo método de ciclagem de pH (8h em solução desmineralizante com pH 4.8 e 16 horas em solução remineralizante com pH 7.0) e então, foram subdivididos de acordo com a reumidificação da dentina. Os espécimes foram restaurados e o conjunto dente/restauração foi seccionado a fim de ser obter 6 palitos com área transversal de 1,0±0,2 mm2, que foram submetidos a análise quantitativa (MPa) da resistência de união a microtração. Três espécimes de cada grupo foram desidratados em grau ascendente de etanol e submetidos à análise dos níveis de cálcio e fósforo da superfície dentinária por meio de espectroscopia eletrônica de análise química (EDS) e análise qualitativa da interface adesiva por meio de microscopia eletrônica de varredura (MEV). Os resultados obtidos da análise de microtração foram submetidos a análise de variância (ANOVA) e apresentaram diferença estatisticamente significante para o tipo de substrato dentinário (p=0,00001) e para reumidificação da dentina (p=0,0105). O teste de Tukey encontrou que para o tipo de substrato, a dentina hígida apresentou maior resistência adesiva e que a dentina reumidecida com quitosana a 2,5% apresentou maior resistência adesiva quando comparada a quitosana a 5,0%, ácido acético a 1,0% ou ausência de reumidificação. O teste de Kruskal Wallis encontrou diferença significante para os níveis de cálcio (p=0,036) e fóforo (p=0,019) encontrados na análise de EDS. O teste de Mann-Whitney mostrou que em substrato desmineralizado a reumidificação com ácido acético a 1,0% e quitosana a 2,5% apresentou maiores concentrações de ambos os minerais. As imagens de microscopia eletrônica de varredura mostram partículas de quitosana no interior dos túbulos dentinários, sendo que a reumidificação da dentina desmineralizada com quitosana a 5,0% apresentou maior quantidade de partículas. A reumidificação da dentina com quitosana não influenciou a morfologia da interface dentina/resina, no entanto, a reumidificação da dentina desmineralizada com quitosana a 2,5% gerou alterações na composição química da dentina e proporcionou maior força de adesão. / The use of biopolymers in demineralized dentin has been investigated with the aim of improving the mechanical and structural properties of dentin prior to restorative procedure. The purpose of this study was to evaluate the rewetting of dentin with chitosan at different concentrations, on bond strength, chemical composition and morphology of dentin/resin interface. The factors under evaluation were: dentin substrate at two levels: sound and demineralized; and dentin rewetting at four levels - 2.5% chitosan, 5.0% chitosan, 1.0% acetic acid (placebo) and no rewetting (control). Eighty specimens of bovine dentin (7x7 mm) were randomly assigned into 8 groups (n=10). Half of dentin slabs were submitted to cariogenic challenge (8h in demineralizing solution and 16h in remineralizing solution) and then, were subdivided according to rewetting of dentin. The specimens were restored and each tooth was sectioned in order to obtain 6 sticks with cross-sectional area of 1.0±0.2 mm2, which were submitted to microtensile bond strength test (µTBS). Three specimens of each group were dehydrated in ethanol and submitted to analysis of calcium and phosphorus levels of dentin surface by electron spectroscopy of chemical analysis (EDS) and qualitative analysis of interface under scanning electron microscopy (SEM). For data obtained on microtensile bond strength test, ANOVA showed significant difference between dentin substrates (p=0.00001) and dentin rewetting (p=0.0105). Tukey test showed that for dentin substrate, sound dentin had greater bond strength than demineralized dentin and the rewetting with 2.5% chitosan provided higher bond strength than 5.0% chitosan, 1.0% acetic acid or no rewetting. Kruskal Wallis test found significant difference for calcium (p=0.036) and phosphorus (p=0.019) levels found in EDS analysis. Mann-Whitney test showed that in demineralized dentin, the rewetting with 1.0% acetic acid and 2.5% chitosan had higher concentration of both minerals. SEM analysis showed particles of chitosan within the dentinal tubules, specially when 5.0% chitosan were used. Dentin rewetting with chitosan did not changed the morphology of dentin/resin interface, however, the rewetting of demineralized dentin with 2.5% chitosan modified the chemical composition and provided better substrate for adhesive procedures, resulting in higher bond strength.

Made available in DSpace on 2017-07-24T19:22:08Z (GMT). No. of bitstreams: 1 ROBERTOAMARAL.pdf: 3642079 bytes, checksum: 8d0b5d5330120eb300a8c6e7ed3ff428 (MD5) Previous issue date: 2008-03-25 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior / The objective of this study was to evaluate the effect of different modes of application (active vs. inactive) of one step self-etch adhesives under in vitro conditions (resindentin bond strength [BS] and nanoleakage under Scaning Electron Microscopy [SEM]) and in vivo conditions (in non carious class V restorations) in the immediate [IM] and 6 month period [6M]. For the in vitro test, 32 human third molars (20 for BS and 12 for SEM) had their occlusal dentin exposed by wet abrasion with 600-grit SiC paper. The following adhesives Adper Prompt [AP] and Xeno II [XE] were applied under inactive [I] or following vigorous application mode [V] in two coats, which were then ligh-cured for the recommended time. Composite “crowns” were incrementally constructed and the after storage (37C/24 h) the specimens were sectioned in both “x” and “y” direction to obtain bonded sticks (0.8 mm2) to be tested in tension (0.5 mm/min). Half of the specimens were tested I or after 6M of water storage. A threeway ANOVA and Tukey test was used to statistically evaluate the data (0,05). For the clinical study, 120 restorations were placed in non carious cervical lesions in 30 patients, in a way that all four experimental conditions were placed in the same patient. The restorations were evaluated according the modified USPHS. The differences for each adhesive at baseline and 6 months were analysed Fisher’s (0,05) and the performance of each mode of application for each adhesive at each period of evaluation was evaluated by Mc Nemar’s test ( 0,05). In the immediate time, an increase in the BS and lower nanoleakage was observed when both adhesive were applied under A mode. However, after 6 months, the BS were reduced ad a higher nanoleakage occurred for both adhesives regardless the mode of application. Under the in vitro part of the study, 29 patients attended the 6 month recall. Only one AP restoration debonded after 6 months in the inactive mode. Based on the results of the present investigation one can conclude that: 1) although the vigorous application improves the immediate performance of the adhesive systems tested, no improvement was observed after 6 months of water storage. 2) After the short-term evaluation of 6 months no significant difference was observed in none of the USPHS items for the experimental conditions. / O objetivo do presente estudo é avaliar, in vitro (resistência de união [RU] por microtração e análise ultramorfológica pela impregnação de nitrato de prata em microscopia eletrônica de varredura [INP]) e in vivo (avaliação clínica), o efeito da forma de aplicação (inativa vs. ativa) de adesivos autocondicionantes de passo único na dentina nos tempos imediato (baseline) e 6 meses. Para o teste in vitro, trinta e dois terceiros molares humanos (20 para o teste de RU e 12 para MEV) tiveram a dentina exposta com lixas carbeto de silício de granulação 180 e 600 para obter uma smear layer padronizada. Os adesivos (Adper Prompt [AP], e Xeno III [XE]) foram aplicados sobre a superfície dentinária em duas camadas de forma inativa ou sob vigorosa agitação por todo substrato (forma ativa). Após serem restaurados, os dentes foram seccionados em eixos “x” e “y” para obtenção dos corpos-de-prova (cps) com média de (0,8 mm2) e testados sob tração (0,5 mm/min). Metades dos cps obtidos foram testados imediatamente e a outra metade armazenada em água para ser testada após seis meses. Os dados de RU foram submetidos a uma análise de variância de 3 fatores e teste de Tukey (α = 0,05). Para avaliar a efetividade clínica dos sistemas adesivos, 120 lesões cervicais não cariosas foram restauradas em trinta pacientes (n=4), sendo distribuídas aleatoriamente de acordo com cada condição experimental (AP inativa = 30; AP ativa = 30; XE inativa = 30 e XE ativa = 30). As restaurações foram avaliadas de acordo com os critérios USPHS modificado. As diferenças nos índices das duas formas de aplicação testada para cada adesivo após cada tempo (baseline e 6 meses) foram submetidos ao teste exato de Fisher′s (0,05) e a performance dos modos de aplicação para cada adesivo no momento e após 6 meses foi avaliado pelo teste de Mc Nemar′s ( 0,05). Na análise in vitro, os fatores técnica e tempo foram significantes (p < 0,05). No tempo imediato houve um aumento da RU e menor INP para os dois adesivos testados quando foram aplicados de forma ativa, entretanto após 6 meses, houve uma diminuição da RU e aumento da INP para os dois adesivos independentemente da técnica de aplicação. No estudo in vivo, 29 pacientes foram avaliados no período de 6 meses. A única diferença registrada foi à queda de uma restauração para o AP inativa, sendo classificado como critério C (Charlie). Conclui-se que: a RU e uma menor INP pode ser conseguida no período imediato quando os adesivos são aplicados sob vigorosa aplicação, entretanto após 6 meses a técnica de aplicação não se mostrou eficaz e na avaliação clínica nenhuma diferença foi observada no tempo de 6 meses.

Orientador: Josimeri Hebling / Banca: Ricardo Marins de Carvalho / Banca: Elisa Maria Aparecida Giro / Resumo: A resistência adesiva de um sistema auto-condicionante e um convencional simplificado, Clearfil SE Bond e Single Bond, respectivamente, quando aplicados à dentina superficial tratada com diferentes agentes condicionadores, foi avaliada por meio de ensaios mecânicos de microtração. Superfícies planas de dentina, obtidas removendo-se a superfície oclusal de 30 terceiros molares humanos foram polidas com lixa de granulação 600 antes da aplicação de diferentes agentes condicionadores, SE Primer, ácido fosfórico ou EDTA. O primer acidificado SE Primer foi aplicado sobre a superfície por 20 segundos, seguido de suave secagem com jatos de ar. O ácido fosfórico a 37% foi aplicado por 15 segundos, seguido de lavagem e remoção do excesso de água com papel absorvente e a solução de EDTA 0,5M pH7,2 foi aplicada por 30 segundos, também seguida de lavagem e secagem. Com exceção das superfícies que receberam a aplicação do primer acidificado, as demais foram mantidas úmidas para a posterior aplicação dos sistemas adesivos avaliados. Sobre a superfície coberta pelo sistema adesivo foi construída uma coroa em resina composta Z250 e os dentes foram mantidos em água a 37% por 24h. Após 500 ciclos térmicos em temperaturas de 5o e 55oC, cortes paralelos no sentido mesio-distal e cortes perpendiculares aos primeiros, no sentido vestibulo-lingual, permitiram a obtenção de amostras com área de secção transversal quadrangular de 1,0mm2 em número mínimo de 10 para cada dente. Cada amostra foi colada a um dispositivo especialmente desenvolvido, e este foi acoplado à uma máquina universal de testes operada à velocidade de 0,5mm/min. O lado correspondente à dentina de aproximadamente 50% das superfícies fraturadas após o ensaio mecânico foi analizado em MEV. Os resultados mostraram que o maior valor médio de resistência adesiva foi observado para a associação SE Primer... (Resumo completo, clicar acesso eletrônico abaixo). / Abstract: Microtensile bond strength of a self-etching primer and a conventional one-bottle system, Clearfi SE Bond and Single Bond, respectively, bonded to superficial dentin treated with different conditioners was investigated. Flat dentin surfaces obtained by removing the occlusal enamel with a diamond saw were ground with 600-grit SiCs under wet conditions to create the smear layer before the conditioners application. Three different dentin conditioning was performed, SE Primer, phosphoric acid and EDTA. The SE Primer was applied on dentin for 20 seconds followed by slight air-drying. Phosphoric acid (37%) was applied for 15 seconds followed by rinsing. EDTA 0.5M pH7.2 was applied for 30 seconds, also followed by water rinsing. Except for the surfaces that received the SE Primer conditioner, the surfaces were left moist by blot-drying the excess water. The adhesive systems were applied and a 5mm high composite resin (Z250) was built up covering the whole surface. After 24h of storage in water at 37oC the teeth were thermocycled for 500 cycles at preset temperatures of 5o and 55oC. The teeth were sectioned with a diamond saw, perpendicular to the adhesive interface to produce beams with 1.0mm2 of adhesive area. These specimens were then attached to a testing apparatus and a tensile load was applied by a universal machine at a crosshead speed of 0.5mm/min. After the micro-tensile bond test, the dentin side of 50% of the fractured surfaces was examined under a scanning electron microscope. The highest tensile bond strength mean was found for the association of SE Primer and Single Bond, 58.51MPa, followed by the association Clearfil SE Bond and EDTA, 47.81MPa. The remaining associations showed mean tensile bond strength statistically similar, except for the association Single Bond and EDTA, which showed the lowest... (Complete abstract, click electronic address below). / Mestre

Esse estudo in vitro avaliou a resistência adesiva da dentina preparada com laser de Er:YAG ou broca, reidratada com clorexidina ou água deionizada, após armazenamento em saliva artificial e termociclagem. Cento e vinte terceiros molares humanos hígidos foram seccionados no terço médio da coroa, expondo a superfície dentinária (n=10). Os espécimes foram divididos aleatóriamente de acordo com o tratamento [laser de Er:YAG + reidratação com água deionizada (LW), laser de Er:YAG + reidratação com clorexidina a 2% (LC), turbina de alta-rotação com broca #245 + reidratação com água deionizada (TW) e turbina de alta-rotação com broca #245 + reidratação com clorexidina a 2% (TC)]. Após o preparo da dentina, os espécimes foram condicionados com ácido fosfórico 35%, lavados e secos com ar. A reidratação da dentina foi realizada através da aplicação de 1.5!L de água deionizada ou clorexidina 2%. Um sistema adesivo etch and rinse foi aplicado seguido da restauração com resina composta. Em cada grupo os espécimes foram sub-divididos de acordo com o envelhecimento [24 horas de armazenamento em saliva artificial / sem termociclagem (NA); 6 meses de armazenamento em saliva artificial / 12.000 ciclos térmicos (6A); 12 meses de armazenamento em saliva artificial / 24.000 ciclos térmicos(12A)]. Após cada período de envelhecimento, os dentes foram seccionados a fim de se obter 4 palitos com area de ±1.0 mm2, que foram submetidos ao teste de microtração usando uma máquina universal de testes com velocidade de 0.5 mm/min. Para a análise da interface adesiva em MEV foram utilizados 36 terceiros molares hígidos (n = 3) que foram restaurados e envelhecidos como descrito no protocolo empregado para o teste adesivo. ANOVA a dois critérios mostrou que não houve diferença significante para a interação entre os fatores e para o fator envelhecimento. O teste de Tukey 5% mostrou que o grupo LC apresentou os menores valores de resistência adesiva. A análise da interface adesiva através da MEV demonstrou que para os grupos irradiados houve formação de camada híbrida irregular com presença de fendas e o envelhecimento não interferiu na morfologia da interface adesiva. A reidratação com clorexidina influenciou negativamente a resistência adesiva do prepare com laser de Er:YAG. O envelhecimento em saliva artificial e termociclagem não interferiram na resistência adesiva da dentina. / This in vitro study evaluated the bond strength of dentin prepared with Er: YAG laser or turbine, rehydrated with chlorhexidine or deionized water after artificial saliva storage and thermocycling. One hundred twenty human third molars were sectioned in order to expose the dentin surface (n=10). The specimens were equally and randomly divided according to treatment [Er:YAG laser + deionized water rehydration (LW), Er:YAG laser + chlorhexidine 2% rehydration (LC), bur on high-speed turbine + deionized water rehydration (BW) and bur on high-speed turbine + chlorhexidine 2% rehydration (BC)]. After dentin preparation, the specimens were etched with 35% phosphoric acid, washed and dried with air. The dentin rehydration method was performed with deionized water or chlorhexidine 2% by applying 1.5!L of each solution. An etch and rinse adhesive system was then applied and the samples were restored with a composite. In each group, the specimens were sub-divided in accordance with the aging method [24 hours artificial saliva storage, no thermocycling (NA); 6 months of artificial saliva storage, 12.000 thermocycling (6A); 12 months of artificial saliva storage, 24.000 thermocycling (12 A)]. After each aging period, each tooth was sectioned in order to obtain 4 sticks with a cross-sectional area of 1.0 mm2, which were submitted to microtensile test using the Universal Test Machine (0.5 mm/min). For the adhesive interface analysis by SEM, 36 healthy third molars (n=3) were restored and aged as the protocol used for the adhesive test. The two-way ANOVA showed no significant differences for the interaction between the factors and for the aging factor. Tukey test 5% showed that the LC group had the lowest bond strength values. The adhesive interface analysis by SEM showed that the irradiated groups presented irregular hybrid layer and cracks and the aging did not affect the adhesive interface morphology. The rehydration with chlorhexidine negatively influenced the bond strength of the preparation with the Er:YAG laser. The artificial saliva aging and thermocycling did not interfere with dentin bond strength.

Submitted by Rosangela Silva (rosangela.silva3@unioeste.br) on 2018-05-28T19:35:21Z No. of bitstreams: 2 Bruna Caroline de Oliveira Lima.pdf: 4552147 bytes, checksum: ed63b8fd6c3f7a7605c22fc5b4d9e51d (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-05-28T19:35:21Z (GMT). No. of bitstreams: 2 Bruna Caroline de Oliveira Lima.pdf: 4552147 bytes, checksum: ed63b8fd6c3f7a7605c22fc5b4d9e51d (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-02-10 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPES / Chlorhexidine in recent years has been used in dentistry for the improvement of the hybrid layer and consequently greater durability of direct aesthetic restorations. Thus, the objective of this work can be applied in vitro or the effect of chlorhexidine (CHX) on the adhesive interfaces, through the microshear bond strength test and the antibacterial activity of CHX incorporated to different adhesive systems, after 24 hours and 30 days of immersion in solution distilled water. We selected 150 crowns of bovine incisors divided into three groups: G1: Single Bond Plus adhesive system; G2: Clearfil SE Bond adhesive system; G3: adhesive system AdheSE Primer and Bond. All groups were subdivided according to the incorporation of CHX (n = 5): no CHX, with CHX prior to incorporated with 0.5%, 1.0% and 2.0% CHX. The micro-shear test was performed with half the CP after 24 hours and with another medium for 30 days. Later, the fracture modes were also found. Antibacterial diffusion tests on agar with Streptococcus mutans were performed with the same groups and subgroups. The Bond Strength variable was evaluated between the groups and solutions by means of the Factor Variance Analysis for repeated measurements. However, the variable size of the bacterial halo was submitted to Kruskall - Wallis non - parametric test, both with a significance level of 95%. The qualitative variability of fractures was evaluated through descriptive statistical analysis. The concentrations of CHX with 0.5 and 1% contributed to the increase of bond strength values and the Clearfil SE Bond system had the highest mean values in the microshear bond strength test. The AdheSE Bond adhesive system presents the best results without antibacterial testing with S.mutans. / A clorexidina nos últimos anos tem sido utilizada na Odontologia para melhoria da camada híbrida e consequentemente maior durabilidade das restaurações estéticas diretas. Assim, o objetivo deste trabalho foi avaliar in vitro o efeito da clorexidina (CHX) nas interfaces adesivas, por meio do teste de microcisalhamento e da atividade antibacteriana da CHX incorporada a diferentes sistemas adesivos, após 24 horas e 30 dias de imersão em solução de água destilada. Foram selecionadas 150 coroas de incisivos bovinos divididas em três grupos: G1: sistema adesivo Single Bond Plus; G2: sistema adesivo Clearfil SE Bond; G3: sistema adesivo AdheSE Primer e Bond. Todos os grupos foram subdivididos de acordo com a concentração de CHX (n=5): sem CHX, com CHX previamente ao adesivo e incorporado com CHX a 0,5%, 1,0% e 2,0%. O teste de microcisalhamento foi realizado com metade dos corpos de prova (CP) após 24 horas e com a outra metade após 30 dias. Posteriormente também foram avaliados os modos de fratura. Testes antibacterianos de difusão em ágar com Streptococcus mutans foram realizados aos grupos com CHX. A variável Resistência de União foi avaliada por meio da Análise da Variância fatorial para medidas repetidas. Já a variável tamanho do halo bacteriano foi submetida ao teste não paramétrico de Kruskall – Wallis, ambos com nível de significância de 5%. A variável qualitativa de padrão de fraturas foi avaliada por meio de análise estatística descritiva. Assim pode-se concluir que as concentrações de CHX com 0,5 e 1%, valor de p > 0,05, contribuíram para o aumento dos valores de resistência de união e o sistema adesivo Clearfil SE Bond teve as maiores médias no teste de microcisalhamento. O sistema adesivo AdheSE Bond apresentou os melhores resultados no teste antibacteriano com S.mutans.

Submitted by Neusa Fagundes (neusa.fagundes@unioeste.br) on 2018-08-23T17:52:03Z No. of bitstreams: 2 Márcio_Camargo2018.pdf: 1289257 bytes, checksum: 6b195c00237854a0b325ec5a5c953cac (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) / Made available in DSpace on 2018-08-23T17:52:03Z (GMT). No. of bitstreams: 2 Márcio_Camargo2018.pdf: 1289257 bytes, checksum: 6b195c00237854a0b325ec5a5c953cac (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2018-05-14 / This double-blind randomized clinical trial evaluates the influence of increased application time in two adhesive system two-step etch-and-rinse (Peak® Universal Bond (P); Ultradent Products Ind and Single Link (SL); Angelus Dental Products Industry) applied in non-carious cervical lesions (NCCLs). Methods: A total of 219 restorations were randomly placed in 35 patients according to the following groups: P1 - applied according to the manufacturer’s; P2X – applied for the double time; SL1 and SL2X (the same application mode). The resin composite Amelogen (Ultradent) was placed incrementally. The restorations were evaluated immediately (baseline) and 6 months, using the FDI and USPHS criteria. Statistical analyses were performed using appropriate tests (=0.05). Results: Twenty-four restorations were lost at 6 months (4 for P1, 2 for P2X, 9 for SL1 and 9 for SL2X) (p < 0.05 between groups). Post-operative sensitivity wasn’t observed in any of the recall periods. Thrity-five restorations were considered to have minor discrepancies in marginal adaptation at the 6-month recall using the FDI criteria (8 for P1, 7 for P2X, 12 for SL1 and 8 for SL2X; p > 0.05 between groups). Ten restorations were considered to have minor discrepancies in marginal discoloration at the 6-month recall (2 for P1, 1 for P2X, 3 for SL1 and 2 for SL2X; p > 0.05 between groups). Conclusion: The increased application time of adhesive system two-step etch-and-rinse didn’t improve the clinical behavior of composite restorations placed in NCCLs. In the meantime, clinical behavior may be influenced by the composition of adhesive systems. / Este ensaio clínico controlado randomizado, duplo cego avaliou a influência do aumento do tempo de aplicação em dois sistemas adesivos convencionais de dois passos, Peak® Universal Bond (P) (Ultradent Products Ind) e Single Link (SL) (Angelus Dental Products Industry) aplicados para restaurar lesões cervicais não cariosas (LCNC). Material e Método: No desenho experimental um total de 219 restaurações foram distribuídas aleatoriamente em 35 pacientes de acordo com os seguintes grupos: P1 e SL1 - aplicados de acordo com o fabricante por 10s; P2X e SL2X - aplicados por 20 s. A resina composta Amelogen (Ultradent) foi colocada de forma incremental. As restaurações foram avaliadas imediatamente (baseline), e em 6 meses, utilizando os critérios FDI e USPHS. As análises estatísticas foram realizadas utilizando testes de Friedman e Mc Nemar (α = 0,05). Resultado: Vinte e quatro restaurações foram perdidas aos 6 meses (4 para P1, 2 para P2X, 9 para SL1 e 9 para SL2X) (p<0,05). A sensibilidade pós-operatória não foi relatada durante a avaliação. Trinta e cinco restaurações apresentaram pequenas discrepâncias na adaptação marginal usando os critérios FDI (8 para P1, 7 para P2X, 12 para SL1 e 8 para SL2X; p>0,05 entre os grupos). Oito restaurações apresentaram pequena discrepância no manchamento marginal na avaliação de 6 meses (2 para P1, 1 para P2X, 3 para SL1 e 2 para SL2X; p> 0,05 entre grupos). Conclusão: Aumentar o tempo de aplicação do sistema adesivo convencional de dois passos não melhora o desempenho clínico das restaurações em resina compostas realizadas em LCNCs. Entretanto, este desempenho/performance pode ser influenciado pela composição dos sistemas adesivos.