Made available in DSpace on 2015-03-03T11:52:30Z (GMT). No. of bitstreams: 0 Previous issue date: 2014-02-20Bitstream added on 2015-03-03T12:06:36Z : No. of bitstreams: 1 000795003.pdf: 1118199 bytes, checksum: 98a54dea093e378451b9a2f7d2e032e2 (MD5) / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / Apesar de satisfatórias, as próteses maxilofaciais apresentam limitações quanto à estética, conforto e durabilidade. Por isso estudos com o objetivo de melhorar as propriedades desses materiais são incessantes. É comprovada a eficiência da adição de nanopartículas na proteção de silicones, evitando a degradação da sua cor, no entanto a literatura é escassa quando se refere a outras alterações das propriedades físicas causadas no silicone facial. Assim, o objetivo deste estudo é avaliar a influência da adição de nanopartículas na ruptura, deformação permanente e dureza do Silicone Facial Silastic MDX4-4210. Foram confeccionadas 560 amostras em silicone facial, sendo 280 dessas amostras para o teste de ruptura, 140 para o teste de dureza e 140 para o teste de deformação permanente. As nanopartículas adicionadas na confecção das amostras de silicone foram: óxido de zinco (ZnO); sulfato de bário (BaSO4) e dióxido de titânio (TiO2). Para cada teste (exceção do teste de ruptura, no qual a quantidade de amostras será confeccionada em duplicata), 40 amostras de silicone serão confeccionadas com adição de cada um dos tipos de nanopartículas, totalizando 120 amostras; 10 amostras de silicone com tinta a óleo, sem nanopartículas, e 10 amostras somente de silicone .Para cada tipo de nanopartícula adicionada ao silicone facial, 20 amostras foram confeccionadas na concentração de 1% e 20 na concentração de 2%. Para cada concentração de nanopartículas, metade (10 amostras) foi com adição de tinta a óleo e a outra metade sem tinta a óleo. As amostras foram submetidas aos ensaios de dureza, resistência à ruptura e deformação permanente, e 1008 horas de envelhecimento acelerado. Os dados obtidos foram submetidos à análise estatística, utilizando-se os testes de nested ANOVA e teste de Tukey. Pode-se... / Although satisfactory, the maxillofacial prostheses present aesthetics, comfort and durability limitations. Therefore, studies with the purpose to obtain better properties of these materials are unceasing. The efficiency of adding nanoparticles to silicon protection is well proven in preventing its color degradation, however the literature is scarce when it comes to other physical property changes with infacial silicon.The aim of this study is to evaluate the influence of nanoparticles addition to hardness, rupture resistance and permanent deformation of Facial Silicone Silastic MDX4-4210. 560 samples of facial silicone were made, 280 for rupture resistance test, 140 for hardness test and 140 for permanent deformation test. Nanoparticles added in the preparation of silicone samples were zinc oxide (ZnO), barium sulfate (BaSO4) and titanium dioxide (TiO2). For each test (except the rupture test, in which the samples are duplicated), 40 samples will be made of silicon added to each type of nanoparticles, totaling 120 samples, 10 samples of silicone with oil paint without nanoparticles, and 10 samples only of silicone (control group). For each type of nanoparticle added to the facial silicone, 20 samples were prepared at a concentration of 1% and 20 at a concentration of 2%. For every concentration of nanoparticles, half (10 samples) were added oil paint and the other half without oil paint. Samples were submitted to testing hardness, rupture resistance and permanent deformation, and 1008 hours of accelerated aging. The data were subjected to statistical analysis using nested ANOVA and Tukey tests. It can be verified through the results that the presence of nanoparticles influenced the hardness, tear strength and permanent deformation of the assessed groups. We conclude that all evaluated nanoparticles influenced the hardness, tear strength and permanent... / FAPESP: 12/05270-3

O objetivo deste trabalho foi avaliar a proporção ideal de dois estabilizantes em compostos elastoméricos, utilizados em pneus que requerem desempenho em longo prazo, submetidos a diferentes tipos de envelhecimento. A resistência ao envelhecimento pode ser alcançada pelo uso de estabilizantes primários e secundários. Para este estudo, os estabilizantes primários selecionados e testados em diferentes quantidades, foram o 6PPD N-1,3 dimetil-butil-N’-fenil-p-fenilenodiamina e o TMQ (2,2,4 - trimetil-quinolina oligomerizada) em uma formulação elastomérica para lateral de pneu de passeio. Nove misturas foram preparadas com 0,5, 1,5 e 2,5 phr (partes por cem de elastômero) de 6PPD, combinado com 0,5; 1,0 e 1,5 phr de TMQ, totalizando 9 amostras. Os compostos foram expostos a três processos de envelhecimento acelerado: termo-oxidativo em estufa, com circulação de ar, a 70°C; fotoquímico em câmara de UV, a 60°C e ao ozônio, 40°C, concentração de 50 pphm. Além disso, as amostras foram envelhecidas naturalmente durante 440 dias. Em intervalos de tempo, pré-determinado, as amostras foram retiradas e as propriedades mecânicas (tensão e alongamento na ruptura e resistência ao rasgamento) foram avaliadas. A cromatografia a gás foi utilizada para quantificar o teor de 6PPD, antes e após os processos de envelhecimento. O envelhecimento natural não apresentou alterações significativas nas propriedades mecânicas, mesmo tendo havido consumo gradativo do 6PPD. As amostras expostas ao envelhecimento termo-oxidativo apresentaram a maior perda das propriedades mecânicas (resistência ao rasgamento e tensão na ruptura) e no teor de 6PPD. Sendo assim, foi o teste mais significativo para definir a melhor combinação dos estabilizantes: 2,5 phr de 6PPD e 1,0 de TMQ. Nos envelhecimentos acelerados em câmara de ozônio e fotoquímico em câmara de UV, teores menores de estabilizantes já garantiram a manutenção das propriedades. Não houve consumo significativo de 6PPD para esses dois envelhecimentos acelerados. / Submitted by Ana Guimarães Pereira (agpereir@ucs.br) on 2015-02-11T12:57:01Z No. of bitstreams: 1 Dissertacao Gelsa Adriana Carpenedo.pdf: 1875191 bytes, checksum: 49a4f9805c5b80c77d6dd289fc885bc3 (MD5) / Made available in DSpace on 2015-02-11T12:57:01Z (GMT). No. of bitstreams: 1 Dissertacao Gelsa Adriana Carpenedo.pdf: 1875191 bytes, checksum: 49a4f9805c5b80c77d6dd289fc885bc3 (MD5) / This study aims at analysing the ideal rate of two stabilizers in elastomeric compounds, used in tires that require a long-term performance, submitted to different kinds of aging. The resistance to the aging can be achieved by using primary and secondary stabilizers. For this study, the primary stabilizers selected and tested in different quantities, have been the 6PPD N-1,3 dimethyl-butyl-N’-phenyl-pphenylenediamine and the TMQ (2,2,4 - trimethyl-oligomerized quinoline) in an elastomeric formulation to the side of tire. Nine mixtures have been prepared with 0,5; 1,5 and 2,5 phr (parts by hundred of elastomer) of 6PPD, combined with 0,5; 1,0 and 1,5 phr of TMQ, totaling nine mixtures. The compounds have been submitted to three accelerated aging processes: thermal-oxidative in heater, with air flow to 70°C; photochemical in UV chamber, to 60°C and to ozone, 40°C, concentration of 50 pphm. In addition, the samples have been aged naturally for 440 days. In predetermined time intervals, the samples have been removed and the mechanical properties (stress at breaking and stretching and resistance to tearing) have been analysed. The gas chromatography has been used to quantify the percentage of 6PPD, before and after the aging processes. The natural aging has not presented significant changes to the mechanical properties, even the fact that there has been gradual consumption of the 6PPD. The samples which have been submitted to the thermal-oxidative aging have presented the highest loss of mechanical properties (resistance to tearing and stress at breaking) and in the percentage of 6PPD. Therefore, it has been the most significant test to define the best combination of the stabilizers: 2,5 phr of 6PPD and 1,0 of TMQ. In the accelerated agings in ozone chamber and photochemical in UV chamber, lower percentages of stabilizers have already ensured the conservation of the properties. There has not been significant consumption of 6PPD for both of these accelerated agings.

Submitted by Ana Guimarães Pereira (agpereir@ucs.br) on 2016-12-02T11:18:53Z No. of bitstreams: 1 Dissertacao Vania Celestin.pdf: 125036 bytes, checksum: d389312dd15b7fa56d359845abb6aeb0 (MD5) / Made available in DSpace on 2016-12-02T11:18:53Z (GMT). No. of bitstreams: 1 Dissertacao Vania Celestin.pdf: 125036 bytes, checksum: d389312dd15b7fa56d359845abb6aeb0 (MD5) Previous issue date: 2016-11-02

Orientadora: Daniela Micheline dos Santos / Coorientador: Marcelo Coelho Goiato / Banca: Marcela Fillié Haddad / Banca: Sandra Helena Penha de Oliveira / Resumo: A prótese bucomaxilofacial implantorretida pode ser suportada por pele ou por mucosa. Subprodutos dos materiais utilizados na confecção destas próteses podem atuar como irritantes ou causadores de reações alérgicas a tais tecidos. A proposta do presente estudo foi avaliar a citotoxicidade de primers e adesivo utilizados na confecção de próteses maxilofaciais retidas por implantes, por meio da análise da proliferação celular e da produção de citocinas pró-inflamatórias e de proteínas de matriz extracelular por queratinócitos humanos. Foram confeccionadas 28 amostras de resina e silicone, em forma de discos (10 x 1 mm), unidas ou não pela aplicação de primer e/ou adesivo. Estas amostras foram distribuídas em 7 grupos: Resina (R), Silicone (S), Resina + Silastic Medhical Adhesive Type A + Silicone (RAS), Resina + DC 1205 primer + Silicone (RDCpS), Resina + Sofreliner primer + Silicone (RSpS), Resina + DC 1205 primer + Silastic Medhical Adhesive Type A + Silicone (RDCpAS) e Resina + Sofreliner primer + Silastic Medhical Adhesive Type A + Silicone (RSpAS). Os extratos dos materiais testados foram preparados colocando-se quatro amostras de cada grupo experimental em tubos de ensaio contendo 9 mL de meio de cultura DMEM (Dulbecco's Modified Eagle's) e incubados a 37°C por 24 horas. Após o período de incubação, a citotoxicidade dos extratos foi avaliada pelo ensaio de MTT em cultura de queratinócitos humanos (HaCaT). Foi avaliada, também, a produção das citocinas IL-1, IL-6 e TNF-α e a quimiocina MIP-1α por meio do ensaio ELISA (Ensaio Imunoabsorbente de Ligação Enzimática). Também foi avaliada a expressão de RNAm para MMP-9, TGF-β e COL-IV por meio da técnica de RT-PCR em tempo real (Reação em Cadeia da Polimerase em Tempo Real). Os dados obtidos foram submetidos à Análise de Variância (ANOVA), seguido... / Abstract: The implant-retained maxillofacial prosthesis can be supported by skin and mucosa. The sub-products produced by the materials used to fabricate these prostheses may act as an irritant factor and cause allergy in these tissues. The aim of this study was to evaluate the cytotoxic effect of primers and adhesive used to bond the acrylic resin and the facial silicone during implant-retained maxillofacial prosthesis fabrication, through the analysis of the cell proliferation, and the production of proinflammatory cytokines and extracellular matrix proteins by keratinocytes. A total of 28 round shape samples (10 x 1 mm) made of resin and silicone bonded or not with primer and adhesive was fabricated. Samples were divided into 7 groups: Resin (R), Silicone (S), Resin + Silastic Medical Adhesive Type A + Silicone (RAS), Resin + DC 1205 primer + Silicone (RDCpS), Resin + Sofreliner primer + Silicone (RSpS), Resin + DC 1205 primer + Silastic Medical Adhesive Type A + Silicone (RDCpAS), and Resin + Sofreliner primer + Silastic Medical Adhesive Type A + Silicone (RSpAS). Extracts of tested materials were prepared setting four samples of each experimental group in Falcon tube with 9mL of medium (Bulbecco's Modified Eagle's) and incubated at 37°C for 24 hours. After incubation period, the extract cytotoxicity was evaluated by an assay of cell survival/proliferation (MTT test) in cultures of human keratinocytes (HaCaT). The levels of IL-1, IL-6 and TNF-α and the chemokine MIP-1α were evaluated by ELISA (Enzyme-Linked Immunoabsorbent Assay). The mRNA expression for MMP-9, TGF-β and collagen type IV were analyzed by the RT-PCR (Real time polymerase chain reaction). Data were submitted to the analysis of variance with Bonferroni post-tests (p<0.05). The results showed increased cell proliferation for the RAS group. The RDCpS group showed the highest... / Mestre

Orientador: Marcelo Coelho Goiato / Banca: Daniela Micheline dos Santos / Banca: Mário Alexandre Coelho Sinhoreti / Resumo: Apesar de satisfatórias, as próteses maxilofaciais apresentam limitações quanto à estética, conforto e durabilidade. Por isso estudos com o objetivo de melhorar as propriedades desses materiais são incessantes. É comprovada a eficiência da adição de nanopartículas na proteção de silicones, evitando a degradação da sua cor, no entanto a literatura é escassa quando se refere a outras alterações das propriedades físicas causadas no silicone facial. Assim, o objetivo deste estudo é avaliar a influência da adição de nanopartículas na ruptura, deformação permanente e dureza do Silicone Facial Silastic MDX4-4210. Foram confeccionadas 560 amostras em silicone facial, sendo 280 dessas amostras para o teste de ruptura, 140 para o teste de dureza e 140 para o teste de deformação permanente. As nanopartículas adicionadas na confecção das amostras de silicone foram: óxido de zinco (ZnO); sulfato de bário (BaSO4) e dióxido de titânio (TiO2). Para cada teste (exceção do teste de ruptura, no qual a quantidade de amostras será confeccionada em duplicata), 40 amostras de silicone serão confeccionadas com adição de cada um dos tipos de nanopartículas, totalizando 120 amostras; 10 amostras de silicone com tinta a óleo, sem nanopartículas, e 10 amostras somente de silicone .Para cada tipo de nanopartícula adicionada ao silicone facial, 20 amostras foram confeccionadas na concentração de 1% e 20 na concentração de 2%. Para cada concentração de nanopartículas, metade (10 amostras) foi com adição de tinta a óleo e a outra metade sem tinta a óleo. As amostras foram submetidas aos ensaios de dureza, resistência à ruptura e deformação permanente, e 1008 horas de envelhecimento acelerado. Os dados obtidos foram submetidos à análise estatística, utilizando-se os testes de nested ANOVA e teste de Tukey. Pode-se... / Abstract: Although satisfactory, the maxillofacial prostheses present aesthetics, comfort and durability limitations. Therefore, studies with the purpose to obtain better properties of these materials are unceasing. The efficiency of adding nanoparticles to silicon protection is well proven in preventing its color degradation, however the literature is scarce when it comes to other physical property changes with infacial silicon.The aim of this study is to evaluate the influence of nanoparticles addition to hardness, rupture resistance and permanent deformation of Facial Silicone Silastic MDX4-4210. 560 samples of facial silicone were made, 280 for rupture resistance test, 140 for hardness test and 140 for permanent deformation test. Nanoparticles added in the preparation of silicone samples were zinc oxide (ZnO), barium sulfate (BaSO4) and titanium dioxide (TiO2). For each test (except the rupture test, in which the samples are duplicated), 40 samples will be made of silicon added to each type of nanoparticles, totaling 120 samples, 10 samples of silicone with oil paint without nanoparticles, and 10 samples only of silicone (control group). For each type of nanoparticle added to the facial silicone, 20 samples were prepared at a concentration of 1% and 20 at a concentration of 2%. For every concentration of nanoparticles, half (10 samples) were added oil paint and the other half without oil paint. Samples were submitted to testing hardness, rupture resistance and permanent deformation, and 1008 hours of accelerated aging. The data were subjected to statistical analysis using nested ANOVA and Tukey tests. It can be verified through the results that the presence of nanoparticles influenced the hardness, tear strength and permanent deformation of the assessed groups. We conclude that all evaluated nanoparticles influenced the hardness, tear strength and permanent... / Mestre

Os elásticos ortodônticos intermaxilares sintéticos vem sendo cada vez mais utilizados, sendo principalmente indicados para pacientes que apresentam hiper-sensibilidade ao látex. Afim de avaliar e comparar o comportamento de elásticos de látex e sintéticos quanto a perda de força ao longo do tempo, este estudo foi realizado tanto in vitro quanto in vivo. Para o estudo in vitro foram avaliados 15 elásticos de cada material, para cada tempo: 0, 1, 3, 12 e 24 horas. No estudo in vivo, pacientes foram avaliados (N=15), utilizando elásticos de ambos os materiais (látex e sintético), nos mesmos tempos do estudo in vitro. Os elásticos foram transferidos para a máquina de ensaios mecânicos (EMIC DL-500 MF). Os valores da força gerada foram registrados após a distensão dos elásticos a uma distância de 25mm. Foi aplicado o teste t pareado para a amostra clínica e independente para a amostra laboratorial. Foi utilizada a análise de variância (ANOVA) para verificar a variação das forças geradas entre os tempos determinados e o teste post-hoc para identificar entre quais tempos houve diferença significativa. Quanto às forças iniciais geradas (zero hora), os valores para os elásticos sintéticos foram bastante semelhantes entre os estudos laboratorial e clínico e ligeiramente superiores aos dos elásticos de látex. Nos tempos subsequentes, as forças geradas pelos elásticos de látex apresentaram valores superiores. Em relação à degradação do material, ao final de 24 horas, maior percentual foi observado para os elásticos sintéticos, tanto in vitro quanto in vivo. A maior queda nos valores das forças liberadas pelos elásticos de ambos os materiais e nos estudos clínico e laboratorial, ocorreu entre os tempos de 0 e 1 hora, seguida de uma queda gradativa e progressiva até o tempo de 24 horas. Os elásticos de látex apresentaram um comportamento mais estável no período estudado em relação aos sintéticos, em ambos os estudos. / Synthetic intermaxillary orthodontic elastics are being increasingly used and they are primarily indicated for patients with hypersensitivity to latex. In order to evaluate and compare the behavior of latex and synthetic elastics, as the loss of strength, over time, this study was conducted both in vitro and in vivo. For the in vitro study, 15 of each elastic material was evaluated for each time: 0, 1, 3, 12 and 24 hours. For the in vivo study, patients were evaluated (N = 15) using both elastic materials (latex and synthetic) at the same times settled in vitro study. The rubber bands were transferred to the testing machine (EMIC DL-500 MF). The values of the force were recorded after stretching the elastic to a length of 25mm. Matched to the clinical and independent for laboratory sample t test was applied. Analysis of variance (ANOVA) was used to check the variation of the forces generated between those determined times and the post-hoc test to identify between which times were marked difference . As regards the initial forces (time zero), the values for synthetic elastic were quite similar between laboratory and clinical studies and slightly higher than the latex elastic. In subsequent times, the forces generated by the latex elastic showed higher values. Regarding the material degradation at the end of 24 hours, the highest percentage was observed for synthetic elastic, both in vitro and in vivo. The largest drop in the values of forces unleashed by the elastic of both materials and the clinical and laboratory studies occurred between times of 0 and 1 hour, followed by a gradual decreases until the time of 24 hours. The latex elastic had a more stable behavior during the period studied compared with synthetic, in both studies.

Avaliou-se a taxa de degradação de elásticos ortodônticos de látex de diferentes fabricantes e diâmetros em diversos intervalos de tempo. Grupos de 15 elásticos de força média dos fabricantes AmericanOrthodontics (Sheboygan, Wis, EUA), Tp (La Porte, IN, EUA), Morelli (Sorocaba, SP, Brasil) e Uniden (Sorocaba, SP, Brasil); de diâmetros 3/16, 1/4 e 5/16 foram analisados nos intervalos de 0,1,3,6,12 e 24 horas, totalizando-se 1080 espécimes. Os elásticos foram estirados individualmente à distância de 30mm, respeitando-se o intervalo de um minuto entre cada estiramento. Os materiais foram acondicionados imersos em água deionizada à 37C. Realizou-se leitura das forças na máquina de ensaios Emic DL 500 (Emic Co, Sao Paulo, Brasil) à velocidade de 30 mm/min, com uma célula de 2Kg (Emic Co, Sao Paulo, Brasil). A leitura de cada elástico consumiu aproximadamente um minuto. Teste Kruskal-wallis com correções por Dunns aferiu significância estatística dos resultados. Foram observadas diferenças entre os grupos analisados, exceto às marcas Morelli e Tp. Foram significativas as inferências das variáveis tempo e marca comercial. Em 0 hora, a relação entre as forças geradas foi Morelli>AO>Uniden>Tp para elásticos 3/16 (p=0,0016) e 1/4 (p=0,0016) e, de Morelli>AO>Tp>Uniden para elásticos 5/16 (p=0,0087). Após 24 horas, as porcentagens de degradação dos elásticos foram AO>Morelli>Uniden>Tp no diâmetro 3/16; AO>Tp>Morelli>Uniden no diâmetro 1/4 e Tp>AO>Uniden>Morelli para elásticos de diâmetro 5/16. O comportamento no intervalo de 0-24 horas demonstrou uma queda acentuada no período de 0-3 horas, um ligeiro aumento em 3-6 horas, seguido de uma queda progressiva no intervalo de 6-24 horas. / The purpose of this study was to evaluate the force relaxation of different brands and diameters of latex elastics occurring during different times. Groups of 15 medium forces elastics from manufacturers: American Orthodontics (Sheboygan, Wis, USA), Tp (La Porte, IN, USA), Morelli Orthodontics (Sorocaba, SP, Brazil) and Uniden Orthodontics (Sorocaba, SP, Brazil) with diameters: 3/16, 1/4 and 5/16 inch size were tested at 0,1,3,6,12,24 hours, making a total of 1080 specimens. An apparatus was designed to simulate oral environments during elastics stretching. The forces were read after 1,3,6,12 and 24-hour periods in Emic testing machine (Emic Co, Sao Paulo, Brazil) with 30 mm/min cross-head speed and load cell of 2Kg Emic force (Emic Co, Sao Paulo, Brazil). Kruskal-Wallis and Dunns tests were used to identify statistical signi&#64257;cance. Overall, there were statistically differences among the different manufacturers at all observation intervals, except between Morelli and Tp. Significantly variability were seen in Morelli and Uniden force delivery. The relationships among loads at 0-hour time period were as follows: Morelli>AO>Uniden>Tp for 3/16 (p=.0016) and 1/4 elastics (p=.0016) and Morelli>AO>Tp>Uniden for 5/16 elastics (p=.0087). The forces relaxation over the 24-hour time period were AO>Morelli>Uniden>Tp for 3/16 elastics; AO>Tp>Morelli>Uniden for 1/4; and Tp>AO>Uniden>Morelli for 5/16 elastics.The force decay pattern show a notable drop-off of forces during 0-3 hours, a slight increase in force values from 3-6 hours and a progressive force decay was seen over 6-24 hours.

Fundação de Amparo a Pesquisa do Estado de Minas Gerais / Dynamic analyses of a flexible rotor supported by fluid film radial bearings on elastomeric suspension are performed using the Finite Element Method. The response to the unbalance and the stability behavior are obtained for different types of damping devices configuration and viscoelastic materials. The stiffness and damping coefficients of the hydrodynamic bearings are evaluated through the Short Bearing Theory. The properties of the elastomers, as a function of the frequency at a given temperature, are obtained from tests conducted in the Laboratory of Mechanical Systems of the School of Mechanical Engineering in the Federal University of Uberlândia. Dissipative elastomeric devices have strong influence on the dynamic behavior of the rotor. It is observed that with the suitable choice of the damper, the amplitude of the unbalance response may be reduced. The threshold speed of stability is increased with the use of elastomeric dampers for the most analyzed cases. / Análises dinâmicas de um rotor flexível apoiado por mancais radiais de filme fluido montados em uma suspensão elastomérica são realizadas utilizando o Método dos Elementos Finitos. A resposta ao desbalanceamento e o comportamento da estabilidade são obtidos para várias configurações de dispositivos amortecedores e para diferentes materiais viscoelásticos. Os coeficientes de rigidez e de amortecimento dos mancais hidrodinâmicos são obtidos através da Teoria de Mancais Curtos. As propriedades dos materiais viscoelásticos, determinadas em função da frequência a uma dada temperatura, são obtidas através de ensaios conduzidos no Laboratório de Sistemas Mecânicos da Faculadade de Engenharia Mecânica da Universidade Federal de Uberlândia. Os dispositivos dissipativos elastoméricos possuem forte influência no comportamento dinâmico do rotor. Observa-se que, com a escolha adequada da configuração do amortecedor, a amplitude da resposta ao desbalanceamento pode ser reduzida. A velocidade limite de estabilidade é aumentada com o emprego dos amortecedores elastoméricos para a maioria dos casos analisados. / Doutor em Engenharia Mecânica

A intensa demanda por petróleo aliado às novas descobertas de poços em condições ainda inexploradas, propulsionam a pesquisa e desenvolvimento de novos componentes e materiais para a indústria petrolífera. A alta responsabilidade desses componentes, como Risers e Bend Stiffners, requer, que antes da sua aplicação em campo, seja realizada uma verificação através de ensaios experimentais, desenvolvidos com o objetivo de representar ao máximo todas as condições em campo. No presente trabalho, um sistema de compensação de deslocamento, com molas elastoméricas, foi desenvolvido para simular um comprimento de Riser retirado da amostra devido à inviabilidade de ensaio com o comprimento real. O material foi caracterizado através de ensaios mecânicos normalizados, ensaios específicos à aplicação e modelos em escala. Logo, um conjunto denominado módulo de compensação foi elaborado. O módulo de compensação apresenta a versatilidade da alteração de rigidez, podendo ser realizada através da mudança do número e/ou geometria das molas. Os resultados dos ensaios mostram-se dentro das tolerâncias especificadas, atingindo o objetivo do projeto. / The increasing demand for oil, combined with new wells discoveries in unexplored conditions, drives the research and development of new components and materials for the oil industry. The high responsibility of these components, such as Risers and Bend Stiffners, requires verification before field operation through experimental trials developed to achieve all conditions found during its useful life. In this thesis, a displacement compensation system, with elastomeric springs, was developed to simulate a short sample of riser due the inviability of testing the real length. The material was characterized by standard mechanical tests, specific tests for this application and scale models. Therefore, a group called compensation module was developed. The compensation module presents versatility in stiffness modification which can be achieved by changing the number and / or spring’s geometry. The final test results are according to the expected, within the specified tolerances achieving the project goal.

A falha por descompressão rápida de gás (Rapid Gas Decompression, RGD) de o’rings elastoméricos assume a forma de trincas, bolhas e cisões, apresentandose após a queda da pressão à qual o selo está exposto. A resistência à RGD tem um papel fundamental nas especificações dos materiais elastoméricos para a indústria do petróleo e gás. No presente trabalho foi desenvolvida uma bancada para ensaios de qualificação de o’rings elastoméricos para testes de resistência por RGD seguindo a norma ISO 23936-2. Para avaliar o desempenho da bancada, quatro ensaios foram realizados utilizando o’rings comerciais com e sem certificado para RGD. A análise das curvas de ensaio evidencia que os parâmetros de ensaio foram atingidos satisfatoriamente. Além disso, taxas lineares de descompressão foram atingidas utilizando um método manual, não obstante uma relevante proposta de melhora é apresentada. / Rapid gas decompression (RGD) damage of elastomeric o’ring seals is the structural failure in the form of blistering, internal cracking and splitting caused upon the release of the pressure the seals are exposed to. RGD resistance plays a key role in the specifications of these components for the oil & gas industry. During this work a test bench was developed for qualification of o’rings RGD resistance according to wellknown international standard ISO 23936-2. In order to evaluate the test bench’s performance, four tests were carried out using o’rings with and without RGD qualification certificates. Analysis of test curves show that test parameters were attained satisfactorily. Furthermore, adequate linear decompression processes were achieved using a manual method, nonetheless a relevant improvement is proposed.