Contribuição ao estudo sobre a obtenção do módulo de elasticidade do concreto utilizando modelagem micromecânicaHenrique Barbosa, Anderson 31 January 2010 (has links)
Made available in DSpace on 2014-06-12T17:36:22Z (GMT). No. of bitstreams: 2
arquivo2392_1.pdf: 8231463 bytes, checksum: d531cccb989cd9e0b9a3d23084ea21c0 (MD5)
license.txt: 1748 bytes, checksum: 8a4605be74aa9ea9d79846c1fba20a33 (MD5)
Previous issue date: 2010 / O módulo de elasticidade do concreto é um parâmetro utilizado para verificações
estruturais. Expressões presentes nas normas nacionais e internacionais e apresentadas
por pesquisadores relacionam este parâmetro com a resistência à compressão.
Assumindo o concreto como um material compósito, as suas propriedades elásticas têm
dependência das propriedades elásticas e frações volumétricas das fases constituintes,
especialmente da zona de transição, esta caracterizada por sua maior porosidade em
relação à pasta de cimento. A partir do conhecimento das propriedades elásticas e
frações de volume das fases, modelos como os de Mori-Tanaka e de três fases podem
ser aplicados e apresentam bons resultados quando utilizados para análise do concreto.
Neste trabalho as propriedades da zona de transição foram obtidas aplicando a inversão
do modelo de três fases. Com base nestas informações, a aplicação da modelagem
micromecânica foi avaliada em dois estágios: com e sem a presença da zona de
transição. Comparado aos valores experimentais produzidos, percebe-se boa
concordância dos valores obtidos com a modelagem micromecânica com a consideração
da ITZ, principalmente para idades superiores a 15 dias, além da qualidade das
aproximações de algumas expressões, como as da NBR 6118:2003 e do CEB/90
|
2 |
Atomic force spectroscopy in melanoma and keratinocytes cells. / Espectroscopia de força atômica em células de melanoma e queratinócitosReinoza, Nataly Zaribeth Herrera 21 March 2019 (has links)
In this work, we used atomic force spectroscopy to obtain the elastic modulus of melanoma and keratinocytes fixed cells, with the purpose to determine the initial conditions for studies of confluente cultures of these cells in the future. The cell lines used were HaCaT cells and WM1366 melanoma cell, the last one is derived from a radial growth melanoma and both were analyzed, parental WM1366 cells (WM1366 shSCR cells) and galectin-3 silenced WM1366 cells (WM1366 shGal3). Cells were located and images of them were obtained by AFM contact mode under liquid conditions. Single force curves acquired in the central region of cells were used to determine the elastic modulus by the Hertzian contact model for the pyramidal tip, allowing to establish a comparison patter between cancer and normal cells. It was found that the melanoma cell (21.8 ± 0.5 kPa) exhibit smaller elastic modulus than keratinocytes cells (31.9 ± 0.4 kPa). For WM1366 shGal3 was found a elastic modulus of 16.1 ± 0.6 kPa, therefore, we found that for large indentation depth it is possible to distinguish between the same melanoma cell line, which represents general alterations in the organization of the cytoskeleton induced by the presence or absence of the galectin-3 protein. On the other hand, to detect local elastic modulus variations along the cell and to identify subcellular regions characterized by specific stiffness associated with local structures, we took elasticity maps in which a single force curve is acquired in each probe position. In order to interpret these maps, the cell was sliced into several different heights, curves of each height section were analyzed and represented in histograms, adjusted by the binomial distribution function. It was observed that the gradient of elastic modulus in cells from the nuclear region towards the cell periphery is more pronounced in cells devoid of galectin-3 than parental cells. The increased elastic modulus in the pericellular region of cells devoid of galectin-3 suggests that the organization of the extracellular matrix in these areas is different than those observed around HaCaT and shSCR WM1366 cells. / Neste trabalho, utilizamos espectroscopia de força atômica para obtenção do módulo elástico de células fixadas de melanoma e queratinócitos, com o objetivo de determinar as condições iniciais de estudos a serem realizados futuramente de culturas de células confluentes do mesmo tipo. As linhagem celulares utilizadas foram as células HaCaT e as células de melanoma WM1366, sendo a última derivada de um melanoma de crescimento radial sendo analisadas tanto as células parentais (células WM1366 shSCR) e as células WM1366 silenciadas com galectina-3 (WM1366 shGal3). As células foram localizadas e imageadas no modo AFM contato em meio líquido. Curvas de força adquiridas na região central das células foram utilizadas para determinar o módulo elástico, a partir do modelo de contato hertziano por uma ponta piramidal, permitindo estabelecer um padrão para comparação entre células normais e cancerígenas. Verificou-se que a célula de melanoma exibe menor módulo de elasticidade (21.8 ± 0.5 kPa) do que as células de queratinócitos (31.9 ± 0.4 kPa). Para as células WM1366 shGal3 foi encontrado um módulo elástico de 16.1 ± 0.6 kPa. Portanto, verificou-se que, para grandes profundidades de indentação, é possível distinguir entre a mesma linhagem de melanoma, células que apresentam alterações gerais na organização do citoesqueleto induzidas pela presença ou ausência da proteína galectina-3. Por outro lado, para detectar variações locais do módulo elástico ao longo da célula e identificar regiões subcelulares, caracterizadas por rigidez específica associada a estruturas locais, foram obtidos mapas de elasticidade nos quais uma única curva de força é adquirida em cada posição da sonda. Para interpretar estes mapas, a célula foi dividida em regiões de diferentes alturas e curvas de cada seção de altura foram analisadas e representadas em histogramas, ajustadas pela função de distribuição binomial. Observou-se que o gradiente de módulo de elasticidade em células da região nuclear em direção à periferia celular é mais acentuado em células desprovidas de galectina-3 do que em células parentais. O aumento do módulo de elasticidade na região pericelular das células desprovidas de galectina-3 sugere que a organização da matriz extracelular nestas áreas é diferente das observadas em torno das células HaCaT e shSCR WM1366.
|
3 |
Efeito dos elementos substitucional e intersticial na microestrutura e propriedades mecânicas de ligas Ti-x%pNi, x = 5, 10, 15 e 20 /Cascadan, Daniela. January 2016 (has links)
Orientador: Carlos Roberto Grandini / Banca: Rodrigo José Contieri / Banca: Piter Gargarella / Banca: Aroldo Geraldo Magdalena / Banca: Marcelo Falcão de Oliveira / O Programa de Pós Graduação em Ciência e Tecnologia de Materiais, PosMat, tem caráter institucional e integra as atividades de pesquisa em materiais de diversos campi / Resumo: Ligas de titânio apresentam grande potencial para uso como biomateriais devido à boa biocompatibilidade e propriedades mecânicas. A adição do níquel ao titânio melhora a resistência ao desgaste, à corrosão e propriedades mecânicas deste elemento. O objetivo deste trabalho foi investigar os efeitos da dopagem de oxigênio na estrutura, microestrutura e em algumas propriedades mecânicas selecionadas de ligas do sistema Ti-xNi%p, x= 10, 15 e 20. Neste trabalho as ligas foram preparadas pela fusão dos metais comercialmente puros em forno a arco voltaico. Para comprovar a composição das ligas obtidas foram feitas análises químicas por emissão óptica por plasma induzido e EDS, que forneceu também o mapeamento dos elementos titânio e níquel para verificar a homogeneidade das ligas. Tratamentos térmicos de homogeneização foram realizados como preparação para a conformação mecânica, no caso a laminação a quente, e após para obter uma microestrutura mais estável, livre de tensões. A seguir foram realizadas dopagens com oxigênio, variando a pressão deste gás e a temperatura, originando amostras com quantidades diferentes de oxigênio. A estrutura foi analisada por difração de raios-X e a microestrutura por microscopia óptica, eletrônica de varredura e EDS para analisar a distribuição dos elementos titânio e níquel nas fases. A quantificação de oxigênio e nitrogênio foi feita por fusão sob gás inerte. As propriedades mecânicas mensuradas foram dureza e módulo elástico dinâmico. Os resultad... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Titanium alloys have great potential for use as biomaterials due to the good biocompatibility and mechanical properties. The nickel addition to titanium improves the wear, corrosion and mechanical resistance of this element. The objective of this work was to investigate the effects of oxygen doping on structure, microstructure and on some selected mechanical properties of Ti-xNi wt% (x = 10, 15 and 20) alloys system. In this work, the alloys were prepared by melting of commercially pure metals in arc furnace. To establish the composition of the obtained alloys chemical analyses were made by induced plasma optical emission and EDS, which also provided the titanium and nickel elements mapping to check the homogeneity of alloys. Homogenization heat treatment was performed in preparation for conformation, in the case hot-rolling, and after, to get a more stable microstructure, free of stress. Oxygen doping were made, by varying the pressure of this gas and temperature, resulting in samples with different quantity of oxygen. The structure was analyzed by x-ray diffraction and the microstructure by optical and scanning electron microscopy, and EDS, to analyze the distribution of the elements titanium and nickel in phases. Quantification of oxygen and nitrogen was made by melting under inert gas. The mechanical properties measured were hardness and elastic modulus. The results showed that the samples have the proper concentration of nickel and titanium, and good homogeneity of the e... (Complete abstract click electronic access below) / Doutor
|
4 |
Avaliação da resistência à flexão e do módulo de elasticidade de diferentes materiais restauradores poliméricos tratados ou não termicamente após a fotoativação /Watanabe, Mauricio Umeno. January 2016 (has links)
Orientador: Mirela Sanae Shinohara / Banca: Alberto Carlos Botazzo Delbem / Banca: Eduardo Passos Rocha / Banca: Mario fernando de Goes / Banca: Rodolfo Bruniera Anchieta / Resumo: Objetivo: Resinas compostas para uso direto têm sido frequentemente usadas pelos profissionais para confecção de restaurações indiretas extensas. O objetivo do presente estudo foi avaliar a resistência à flexão (RF) e o módulo de elasticidade (ME) de diferentes materiais restauradores poliméricos diretos, nos tempos de 30min e 24h sem tratamento térmico (TT); e quando submetidos ou não ao TT, sendo armazenados ou não por 180 dias. Materiais e método: Foram confeccionados 200 corpos de prova divididos nos seguintes grupos de acordo com o material: o ormocer microhíbrido Admira Fusion (ADM), a resina tipo "bulk" nanoparticulada Filtek Bulk Fill (BU), a resina composta convencional nanoparticulada Filtek Z350XT (Z350) e resina composta convencional microhíbrida IPS Empress Direct (EMP). Os grupos foram subdivididos (n=10) nos tempos de 30min sem TT, 24h com e sem TT ou 180 dias com e sem TT. Os corpos de prova (10 mm x 2 mm x 2 mm) foram confeccionados usando-se um molde tripartido de aço inox, no qual o material foi inserido em incremento único e fotoativado por 20s de cada lado. No final do período de 24h da fotoativação, o TT foi realizado por 10min em estufa à temperatura controlada de 170⁰C. O armazenamento das amostras de 180 dias foi em água destilada em ambiente escuro a 37⁰C. O teste de resistência à flexão de 3 pontos foi realizado em uma máquina de ensaio Instron à velocidade de 1,0 mm/min. Resultados: Os resultados foram obtidos em MPa (RF) e GPa (ME), sendo depois s... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: Purpose : Direct composite resins are often used by professionals for making extensive indirect restorations. The aim of this investigation was to evaluate flexural strength and elastic modulus of different rest orative polymeri c materials at 30 minutes and 24 hours without heat treatment (HT); and with and without HT at 24 hours and 180 days post cure . Materials and method: 200 samples were prepared and divided accord ing to the material as follows : microhybrid ormocer Admira Fu sion (ADM), nanofilled bulk - fill composite resin Fitek Bu lk Fill (BU), nanofilled universal composite resin Filtek Supreme Ultr a (Z350) and microhybrid universal composite resin IPS Empress Direct (EMP). Groups were subdivided (n=10) at 30 minutes into: wi thout HT (30 min), 24 h with and without HT and 180 days with and without HT. The samples (10 mm x 2 mm x 2 mm) were made in a tri - part stainless steel mold where t he material was inserted and light - cured for 20 seconds on each side. At the end of the 24 h period HT at 170 ⁰ C was performe d for 10 minutes in a dry heat oven. The 180 day storage samples were placed in destilled water at 37 ⁰ C i n the dark. A standard three point bending test was conducted on all samples with a universal testing machine (Instron) at a crosshead speed of 1.0 mm/min. Results: The results were recorded in MPa (flexural strength ) and GPa (elastic modulus) and data were analyzed statistically at a significance level of 5% . All the materials had a significant increase in flexural str ength and elastic modu lus from 30 minutes to 24 hours (p<0. 05). HT promoted an increase in flexural strength for BU and EMP at 24 hours and Z350 at 180 days (p<0,05). Storage di dn't influence flexural strength for BU without HT. HT promoted elastic modulus increase for ormocer ADM at both testing times and for EMP, BU and Z350 at 24 hours (p<0.05). Wit... (Complete abstract electronic access below) / Doutor
|
5 |
Cimentação de laminados cerâmicos: efeito de diferentes modos de fotoativação na estabilidade de cor e nas propriedades mecânicas de sistemas adesivos e cimentos resinosos / Luting of ceramic laminate: effect of different modes of photoactivation in the color stability and mechanical properties of adhesives systems and resin cementsSahyon, Henrico Badaoui Strazzi [UNESP] 12 May 2017 (has links)
Submitted by Henrico Badaoui Strazzi Sahyon null (ico_strazzi@hotmail.com) on 2017-06-07T20:02:14Z
No. of bitstreams: 1
Dissertação Henrico Strazzi corrigida - Pronta Envio Pós Graduação PDF.pdf: 2071858 bytes, checksum: 12b4a6c367fe9ba8eba52de4244b855b (MD5) / Approved for entry into archive by Luiz Galeffi (luizgaleffi@gmail.com) on 2017-06-07T20:19:57Z (GMT) No. of bitstreams: 1
sahyon_hbs_me_araca.pdf: 2071858 bytes, checksum: 12b4a6c367fe9ba8eba52de4244b855b (MD5) / Made available in DSpace on 2017-06-07T20:19:57Z (GMT). No. of bitstreams: 1
sahyon_hbs_me_araca.pdf: 2071858 bytes, checksum: 12b4a6c367fe9ba8eba52de4244b855b (MD5)
Previous issue date: 2017-05-12 / Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES) / Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP) / O objetivo deste estudo in vitro foi avaliar os efeitos de diferentes modos de fotoativação na nanodureza e módulo de elasticidade de sistemas adesivos e cimentos resinosos, assim como o efeito na estabilidade de cor de laminados cerâmicos. Os fatores em estudos foram: dois níveis de fotopolimerizadores (VALO - Ultradent; Radii-Cal – SDI) e três níveis de modo de ativação (sem polimerização prévia do sistema adesivo na superfície dental e no interior do laminado cerâmico; polimerização prévia do sistema adesivo somente na superfície dental; e polimerização prévia do sistema adesivo na superfície dental e no interior do laminado cerâmico). Na análise da estabilidade de cor o terceiro fator estudado foi o tempo de envelhecimento (252, 504 e 756 horas). Foram confeccionados 132 blocos de cerâmica (7x8x0,6mm) de dissilicato de lítio (IPS e-max CAD), os quais foram cimentados sobre o esmalte dentário dos dentes bovinos, distribuídos em 12 grupos de acordo com os materiais restauradores e métodos de procedimentos utilizados. Dois sistemas adesivos e cimentos resinosos foram utilizados (Single Bond Universal/RelyX Veneer- 3M/ESPE e Tetric N Bond/Variolink Veneer – Ivoclar Vivadent). As propriedades mecânicas de nanodureza e módulo de elasticidade foram mensuradas utilizando nanodurômetro (Anton Paar), sob ação de carga de 1000μN (n=3). A estabilidade de cor foi mensurada através do espectrofotômetro de reflexão ultravioleta visível UV-2450 (Shimadzu) antes e após a submissão das amostras em envelhecimento acelerado artificial UVB (n=8). Os dados da estabilidade de cor e propriedades mecânicas foram submetidos a testes estatísticos de normalidade e analisados por ANOVA e teste de Tukey (α=0,05). Os resultados mostraram que, em relação aos protocolos de ativação prévia ou não dos sistemas adesivos, os dois sistemas cimentantes apresentaram comportamentos diferentes dependendo do protocolo utilizado. Para o sistema adesivo Single Bond Universal / RelyX Veneer, a ativação prévia do adesivo contido somente no esmalte dental com a unidade ativadora polywave Valo, apresentou resultados mais satisfatórios. Para o sistema Tetric N Bond / Variolink Veneer, os diferentes protocolos utilizados não demonstraram alteração significante nas propriedades analisadas. De maneira geral, o fotopolimerizador polywave Valo promoveu melhores propriedades mecânicas que o fotopolimerizador singlewave Radii-Cal, para a estabilidade de cor não houve diferença na utilização de diferentes unidades fotoativadoras. / The purpose of this in vitro study was to evaluate the effects of different modes of photoactivation in the nanohardness and elastic modulus of resin cements and adhesives, as well as the effect on the color stability of ceramic laminates. The factors of the studies were: two levels of light curing units (VALO – Ultradent; Radii-Cal – SDI) and three modes of photoactivation (without prior curing of the adhesive system in the tooth surface and inside of the ceramic laminate, prior curing the adhesive system only in the tooth surface, and prior curing of the adhesive system in the tooth surface and within the ceramic laminate). In the analysis of color stability the third factor of the study was the aging time (252, 504 and 756 hours). One hundred and thirty two ceramic blocks (7x8x0.6mm) of lithium dissilicate (IPS e-max CAD) were made, which were cemented on the enamel of bovine teeth, and distributed into 12 groups according to the restorative materials (Single Bond Universal/RelyX Veneer – 3M/ESPE and Excite DSC/Variolink Veneer – Ivoclar Vivadent) and methods of procedures. The mechanical properties of nanohardness and elastic modulus were measured using a nanohardness tester (Anton Paar) under loaf of 1000 μN (n=3). Color stability was measured using a UV-2450 visible UV spectrophotometer (Shimadzu) before and after the submission of the UVB artificial accelerated aging samples (n=8). Data of color stability and mechanical properties were submitted to statistical testes of normality and analyzed by ANOVA and Tukey´s test (α=0.05). The results showed that, in relation to the different behaviors depending of the protocol used. For the Single Bond Universal / RelyX Veneer adhesive system, previous activation adhesive system contained only in the dental enamel with Valo polywave light curing unit showed more satisfactory results. For the Tetric N Bond / Variolink Veneer system, the different protocols did not show significant alteration in the analyzed properties. In general, Valo polywave light curing unit promoted better mechanical properties than Radii-Cal singlewave light curing unit, for color stability there was no difference in the use of different light curing units. / FAPESP: 2015/06355-0
|
6 |
Ensaios pressiométricos de Ménard em maciços compactados para a avaliação de módulos elásticos / Ménard pressuremeter tests in a massive compressed to the evaluation of elastic moduliOLIVEIRA, Devonzir Magalhães de 17 December 2010 (has links)
Made available in DSpace on 2014-07-29T15:18:21Z (GMT). No. of bitstreams: 1
Devonzir Magalhaes.pdf: 2374656 bytes, checksum: be2fa62f68b635119a439a5c539c3894 (MD5)
Previous issue date: 2010-12-17 / The compacting control of earthy materials at engineering works demands great efforts and
the necessity of conducting field and laboratory tests in time and space, conditioned by the
work schedule always tight. It is also known that the embankment supports the efforts of
substantial bodies of water with potential energy, which if, uncontrollably released, will cause
tragedies and imponderable material damages. This work presents the methodology of
execution and analysis of the results of field and laboratory tests performed in two
experimental embankments builted during the definition of the construction s processes of the
Batalha Hydroelectric Power Plant. It was collected disturbed and undisturbed samples at
twelve spot in each embankment, to perform characterization tests, triaxial compression test
and consolidation test. The results of these laboratory tests where compared to the results of
twenty four Pressuremeter Tests (PMT) fulfilled at the same embankment. The interpretation
of the PMT tests was done according to french standards. These tests provided results of
Ménard Pressuremeter Modulus (EM), pressuremeter limit pressure (pl) and creep pressure
(pf), which corresponds to the end of the elastic range of the material. In addition, it was
performed twenty four Standard Penetration Tests in both embankments to obtain the Nspt and
compare with the results of PMT. The studies developed in this research showed that these
tests point out results with less variability that the ones from the laboratories and can be
realized with no difficulties along the soil profile. The results achieved demonstrated that the
PMT can be a very useful tool to reach the modulus of elasticity at any depth of the landfill,
mainly in rolled-fill dams already operating a long time and in places where there are
restrictions to remove samples for laboratory tests. / O controle de compactação de materiais terrosos em obras de engenharia demanda grandes
esforços e a necessidade da realização de ensaios de campo e laboratório, ajustados ao
cronograma sempre apertado das obras. Sabe-se, também, que os aterros compactados de
barragens suportam esforços de grandes massas de água com energia potencial que se
liberadas, incontrolavelmente, causarão tragédias e danos materiais incalculáveis. Este
trabalho apresenta a metodologia de execução e análise dos resultados de ensaios de campo e
laboratório realizados em dois aterros experimentais construídos na fase de definição dos
processos construtivos da barragem da UHE Batalha. Foram coletadas amostras deformadas e
blocos de amostras indeformadas de doze pontos em cada aterro, para caracterização do solo
compactado e realização de ensaios de compressão triaxial e de adensamento. Os resultados
desses ensaios de laboratório foram comparados com os resultados de vinte e quatro ensaios
pressiométricos (PMT) executados nos mesmos aterros. Na interpretação dos ensaios PMT foi
empregada a metodologia das normas francesas. Estes ensaios forneceram resultados do
módulo de elasticidade de Ménard (EM), pressão limite (pl) e pressão de fluência (pf), esta
correspondente ao fim da fase pseudo-elástica do material. Complementarmente foram
realizados vinte e quatro ensaios penetrométricos nos dois aterros para obtenção do NSPT e
comparação com os resultados do PMT. Os estudos desenvolvidos nesta pesquisa mostraram
que estes ensaios apresentaram resultados com menor variabilidade que os ensaios de
laboratório e podem ser realizados sem muitas dificuldades ao longo do perfil de um aterro
compactado. Os resultados alcançados mostraram que o PMT poderá se tornar uma
ferramenta de grande utilidade para obtenção do módulo de elasticidade em quaisquer
profundidades de aterros compactados, principalmente em barragens antigas e em locais
destas onde possam existir restrições para retirada de amostras para ensaios de laboratório.
|
7 |
Módulo de elasticidade de ossos corticais: revisão e otimização da metodologia para ossos longos / not availableBrandão, Jairo 30 July 1997 (has links)
Neste estudo fez-se um levantamento dos valores publicados para o Módulo de Young de amostras de osso cortical, oriundas de diferentes espécies e de ossos que desempenham diferentes funções. Os valores encontrados estão bastante dispersos e, procurando a causa da dispersão, encontrou-se inúmeros fatores. Destacaram-se os mais citados na literatura: velocidade de aplicação da carga; direção em que se ensaia a amostra; porosidade, mineralização e densidade; tamanho das amostras; posição das amostras no osso e microestrutura do osso. Concluiu-se que para o osso cortical, a maior causa da variabilidade no Módulo de Young se deve à orientação das fibras colágenas. Trabalhos mais recentes afirmam que amostras com estrutura plexiform apresentam maiores valores para o Módulo de Young que amostras com estrutura osteonal. Construiu-se um dispositivo (suporte das amostras) adequando-o à norma ASTMD790M86┓ com a finalidade de otimizar o ensaio de flexão em três pontos. Os aspectos relevantes da construção foram: distância entre os apoios e forma cilíndrica tanto para os apoios como para a cabeça da cruzeta. Na parte experimental, coletou-se 200 amostras de osso cortical de cinco tíbias bovinas, sendo a medida de cada amostra (2x4x40) mm, aproximadamente. Para a coleta e preservação das amostras tomou-se todos os cuidados preconizados como importantes. As amostras foram retiradas das faces anterior, posterior, lateral, medial, antero-lateral, antero-medial, postero-lateral e postero-medial das diáfises das tíbias num trecho situado entre 0,25L e 0,75L, medidos a partir da extremidade distai, onde L é o comprimento total da tíbia. O tamanho das amostras e as dimensões do suporte para o ensaio de flexão seguiram a norma ASTMD790M86┓, indicada para ensaio de plásticos em flexão em três pontos. Com a otimização do ensaio de flexão em três pontos, chegou-se a valores de E compatíveis com os da literatura. Concluiu-se que os valores de E crescem das epífises para a diáfise e que os menores valores aparecem nas faces anterior e posterior das tíbias enquanto que os maiores valores aparecem nas faces lateral e medial. / This study shows a survey of the published values for the Young\'s Modulus of cortical bone samples, from different species and from banes which perform different functions. The values found are very dispersed and, by several factors. The outstanding reasons, in the literature are: strain rate; direction in which the samples is tested; porosity; mineralization and density; sample size; sample position in the bone and the bone\'s microstructure. There is a conclusion that for the cortical bone, the greatest cause of variability in Young\'s Modulus is due to the orientation of the collagen fibers. Recent works state that plexiform samples show greater values for the Young\'s Modulus than osteonal samples. A rack to sustain the samples was built according to the ASTMD970M86┓ Standards to optimize the three point bending test. The relevant aspects in the devices building were: the span between the supports and the supports and cross head cylindrical shapes. In the experimental part, 200 cortical bone samples were collected from 5 bovine tibiae, and each sample sizing (2x4x40) mm, approximately. For the samples collecting and embalming all the important cares were taken. The samples were collected from the anterior, posterior, lateral, medial, anterolateral, antero-medial, postero-lateral and postero-medial faces from diaphysis from tibiae in an area between 0.25L and 0.75L, measured from the distal extremity, where L is the total tibiae length. The sample sizes and the rack dimensions for the bending test followed the ASTMD970M86┓ Standards, indicated for plastic tests in three point bending. With the three point bending optimizing, the E value found were like the ones in literature. We conclude that the E values enhance from the epiphysis to the diaphysis and that smallest values appear in the anterior and posterior tibiae faces, while the greatest values appear in the lateral and medial faces.
|
8 |
Estudo in vitro do efeito de unidades fotoativadoras com diferentes comprimentos de onda na dureza (por meio de micro e ultramicroendentação) e módulo de elasticidade de uma resina composta nanohíbrida / Effect of light sources with different wavelengths in micro and ultramicrohardness and elastic modulus of a nanohybrid composite resin. An in vitro studyAraujo, Jesuina Lamartine Nogueira 04 June 2013 (has links)
Este trabalho avaliou in vitro a dureza e módulo de elasticidade de uma resina composta nanohíbrida (Tetric N-Ceram/Ivoclair-Vivadent) com diferentes cores, fotoativada por duas unidades com diferentes comprimentos de onda em 3 espessuras (1, 2 e 3mm) comparadas à partir da superfície irradiada (0mm). Os espécimes foram divididos em grupos (n=5): microdureza Knoop-KHN, ultramicrodureza-DUH e módulo de elasticidade-ME, cor (A2 e Bleach-M(BM), fotoativador LEDazul (Elipar Freeligth2/3M(750mW/25s/430-480nm(FL) e LEDazul/violeta Bluephase/Ivoclar/Vivadent (1200mW/cm²/15s/380-515nm(B15) e 30s(B30). Os espécimes foram armazenados por 24h/37ºC. Os ensaios de KHN foram realizados no HMV-2000/Shimadzu, com carga de 25gf/40s, e de DUH e ME no DUH 211S/Shimadzu com força de 10mN e tempo de espera de 0s. Foram realizadas 5 endentações na superfície irradiada (0mm) e na base das amostras (1, 2 e 3mm). A análise estatística foi realizada por ANOVA, Tukey e correlação de Pearson (p<0,01%). O teste de Pearson mostrou haver correlação direta entre a KHN e a DUH. A fonte FL promoveu maiores valores de KHN e de DUH para as duas resinas testadas; enquanto que a fonte B15, promoveu o maior valor de ME. Quanto às espessuras, 0 e 1mm apresentaram maiores valores de KHN e de DUH, e menores de ME que as espessuras de 2 e 3mm. A cor A2 apresentou maior valor de KHN e DUH e menor ME que a cor Bleach-M. Assim, de acordo com a metodologia proposta e os resultados apresentados pode-se concluir que apesar de a luz LEDazul/violeta propor uma maior eficácia na polimerização de resinas de cor clara, no tocante às propriedades avaliadas isso não foi verificado. / This study evaluated in vitro the hardness (micro and ultramicro) and elastic modulus of a nanohybrid composite resin (Tetric N-Ceram/Ivoclar-Vivadent) with different colors, light sources and thickness. The specimens were divided into groups (n=5): KHN-Knoop microhardness, DUH-nanohardness and ME-elastic modulus; colors: A2 and Bleach-M (BM); light sources: LEDblue Elipar Free light 2/3M-ESPE (750mW/cm²/ 25s/430-480nm- (FL)), LEDblue/violet Bluephase/Ivoclar-Vivadent (1.200mw/cm²/15s/380-515nm) (B15) and 30s (B30); thickness: 1mm, 2mm and 3mm, compared to the irradiated surface (0mm). Specimens were stored dry for 24hours at 37ºC after photo curing. Assays were performed at KHN in HMV-2000/ Shimadzu with load of 25gf at 40s and DUH/ME in DUH 211S/Shimadzu with force of 10mN and no hold time (0s). 5 indentations of each test were made in the surfaces opposites to the photo curing. A statistical analysis was performed by ANOVA, Tukey and Pearson correlation (p<0.01%). Pearsons Test showed a direct correlation between KHN and DUH. Comparison between KHN and ME in the studied resins indicated that the light source FL promoted higher values of KHN and DUH to both resins tested, whereas the B15 light source promoted the higher ME value. Regarding thickness 0mm and 1mm showed higher KHN and DUH and lower ME than 2 and 3mm thickness. A2 color showed higher KHN and DUH and lower ME than BM. Thus, according to the proposed methods and the presented results, the LEDblue/violet was not better for curing the light color of the nanohybrid resin, than LEDblue.
|
9 |
Propriedades dinâmicas do concreto e relações com sua microestrutura / Dynamics properties of concrete and relations with its microstructureGidrão, Gustavo de Miranda Saleme 17 June 2015 (has links)
O módulo de elasticidade do concreto é uma propriedade muito importante para o projeto estrutural. Apesar do comportamento tensão-deformação não linear do concreto, uma estimativa adequada desta propriedade é fundamental para a análise estrutural, avaliação de efeitos de segunda ordem e verificações de deslocamentos. Em especial, o módulo de elasticidade dinâmico é uma propriedade muito importante na análise de vibrações excessivas. Todavia, sua determinação é tipicamente feita a partir do módulo de elasticidade estático. Os códigos normativos usualmente apresentam equações para estimativas do módulo de elasticidade estático a partir da resistência do concreto à compressão, densidade e tipo de agregado utilizado. Logo, outra limitação de tais estimativas é a não consideração de características da zona de transição além do tipo, fração volumétrica e dimensão dos agregados empregados na mistura. Por outro lado, a teoria dos materiais compósitos multifásicos permitiu, nos últimos tempos, o avanço dos modelos de previsão das propriedades do material. Portanto, o entendimento isolado do comportamento da pasta, areia, brita, argamassa e zona de transição é importante para a previsão do comportamento do compósito concreto. Desta forma, utilizou-se do ensaio acústico para a caracterização de variadas dosagens de pasta, argamassa, rocha e concreto. Assim, foi possível investigar a correlação entre as propriedades dinâmicas do compósito concreto e sua microestrutura. Variações de parâmetros como o fator água-cimento, maturidade, presença de superplastificante e tipo de agregado graúdo utilizado na mistura impuseram variados padrões microestruturais, e estes foram avaliados frente às propriedades dinâmicas do material, em especial, ao módulo de elasticidade dinâmico. Também foi possível a constatação da interdependência microestrutural entre o módulo de elasticidade dinâmico, módulo de cisalhamento e coeficiente de amortecimento. Já o coeficiente de Poisson apresentou pouca correlação com as outras propriedades supracitadas. Finalmente fez-se a inferência sobre a precisão das estimativas para módulo de elasticidade dinâmico através das equações empíricas contidas em normas e dos modelos teóricos obtidos via formulação para materiais bifásicos. Uma curva que correlaciona o módulo de elasticidade dinâmico e estático foi proposta para a maturidade referente aos 28 dias. / The modulus of elasticity of concrete is a very important property for structural design. Despite the nonlinear stress-strain behavior of concrete, an appropriate estimate of this property is essential for structural analysis, evaluation of second-order effects and excessive deflexions. In particular, the dynamic modulus of elasticity is an important property in analysis of excessive vibration. However, this value is often estimated from the static modulus. Design codes usually contain equations estimating the static modulus based on compressive strength of concrete, density and type of aggregate used. Another limitation of such estimates is neglecting the characteristics of the transition zone, and the type, size and volume fraction of the aggregates used in the mixture. On the other hand, the theory of multiphase composites materials has allowed in recent times, advances of predictive models of material properties. Therefore, the isolated understanding of paste behavior, sand, gravel, mortar and transition zone is important for predicting concrete composite behavior. In this way, the acoustic test it was utilized for characterization of the various mixes of the paste, mortar, rock and concrete. Thus, it was possible to investigate the correlation between the dynamic properties of the composite concrete and its microstructure. Variations in parameters such as the water-cement ratio, maturity, presence of superplasticizer and type of coarse aggregate used in the mix, imposed various microstructural patterns, and these were evaluated face to the material dynamic properties, in particular to the dynamic modulus of elasticity. Detected a microstructural interdependence between the dynamic modulus of elasticity, shear modulus and damping coefficient It was also. On the other hand, the Poisson ratio, presented low correlation with the other properties mentioned. Finally an inference about the accuracy of estimates for dynamic modulus of elasticity through empirical equations contained in standards and theoretical models obtained by the formulation for biphasic materials was made. A curve that correlates the dynamic and static modulus of elasticity was proposed for the age of 28 days.
|
10 |
Cimentação de laminados cerâmicos : efeito de diferentes modos de fotoativação na estabilidade de cor e nas propriedades mecânicas de sistemas adesivos e cimentos resinosos /Sahyon, Henrico Badaoui Strazzi. January 2017 (has links)
Orientador: Paulo Henrique dos Santos / Banca: Wirley Gonçalves Assunção / Banca: Anderson Catelan / Resumo: O objetivo deste estudo in vitro foi avaliar os efeitos de diferentes modos de fotoativação na nanodureza e módulo de elasticidade de sistemas adesivos e cimentos resinosos, assim como o efeito na estabilidade de cor de laminados cerâmicos. Os fatores em estudos foram: dois níveis de fotopolimerizadores (VALO - Ultradent; Radii-Cal - SDI) e três níveis de modo de ativação (sem polimerização prévia do sistema adesivo na superfície dental e no interior do laminado cerâmico; polimerização prévia do sistema adesivo somente na superfície dental; e polimerização prévia do sistema adesivo na superfície dental e no interior do laminado cerâmico). Na análise da estabilidade de cor o terceiro fator estudado foi o tempo de envelhecimento (252, 504 e 756 horas). Foram confeccionados 132 blocos de cerâmica (7x8x0,6mm) de dissilicato de lítio (IPS e-max CAD), os quais foram cimentados sobre o esmalte dentário dos dentes bovinos, distribuídos em 12 grupos de acordo com os materiais restauradores e métodos de procedimentos utilizados. Dois sistemas adesivos e cimentos resinosos foram utilizados (Single Bond Universal/RelyX Veneer- 3M/ESPE e Tetric N Bond/Variolink Veneer - Ivoclar Vivadent). As propriedades mecânicas de nanodureza e módulo de elasticidade foram mensuradas utilizando nanodurômetro (Anton Paar), sob ação de carga de 1000μN (n=3). A estabilidade de cor foi mensurada através do espectrofotômetro de reflexão ultravioleta visível UV-2450 (Shimadzu) antes e após a submissão das amo... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this in vitro study was to evaluate the effects of different modes of photoactivation in the nanohardness and elastic modulus of resin cements and adhesives, as well as the effect on the color stability of ceramic laminates. The factors of the studies were: two levels of light curing units (VALO - Ultradent; Radii-Cal - SDI) and three modes of photoactivation (without prior curing of the adhesive system in the tooth surface and inside of the ceramic laminate, prior curing the adhesive system only in the tooth surface, and prior curing of the adhesive system in the tooth surface and within the ceramic laminate). In the analysis of color stability the third factor of the study was the aging time (252, 504 and 756 hours). One hundred and thirty two ceramic blocks (7x8x0.6mm) of lithium dissilicate (IPS e-max CAD) were made, which were cemented on the enamel of bovine teeth, and distributed into 12 groups according to the restorative materials (Single Bond Universal/RelyX Veneer - 3M/ESPE and Excite DSC/Variolink Veneer - Ivoclar Vivadent) and methods of procedures. The mechanical properties of nanohardness and elastic modulus were measured using a nanohardness tester (Anton Paar) under loaf of 1000 μN (n=3). Color stability was measured using a UV-2450 visible UV spectrophotometer (Shimadzu) before and after the submission of the UVB artificial accelerated aging samples (n=8). Data of color stability and mechanical properties were submitted to statistical testes o... (Complete abstract click electronic access below) / Mestre
|